The invention relates to a pressure sensing technique, and more particularly, to a pressure sensor and a manufacturing method thereof.
In recent, the pressure-sensitive layer in the pressure sensor is mostly formed by mixing conductive particles in a resin. The pressure-sensitive layer is functioned by pressure resulting in thinning thickness thereof so as to reduce output resistance. However, since the conductivity of conductive particles lacks directionality, not only does resistance change occur to regions subjected to pressure, regions not subjected to pressure are also readily affected, such that pressure resolution is worsened. Therefore, how to alleviate the above issues of the pressure sensor to achieve excellent resolution is an important research topic.
The invention provides a pressure sensor that can effectively enhance pressure resolution.
The invention further provides a pressure sensor that can also effectively enhance pressure resolution.
The invention further provides a manufacturing method of a pressure sensor that can manufacture a pressure sensor having high pressure resolution.
A pressure sensor of the invention includes a thin-film transistor array and a pressure-sensitive layer covering the thin-film transistor array. In particular, the pressure-sensitive layer includes a plurality of one-dimensional materials arranged on the same plane and a plurality of insulating layers, and the one-dimensional materials and the insulating layers are alternately stacked.
Another pressure sensor of the invention includes a thin-film transistor array and a pressure-sensitive layer covering the thin-film transistor array. In particular, the pressure-sensitive layer includes a plurality of two-dimensional materials and a plurality of insulating layers, and the two-dimensional materials and the insulating layers are alternately stacked.
In the above embodiments of the invention, the pressure-sensitive layer may be inductive resistive.
In an embodiment of the invention, the diameter of the one-dimensional material may be 5 nm to 100 nm.
In an embodiment of the invention, the aspect ratio of the one-dimensional material may be greater than 100.
In an embodiment of the invention, the one-dimensional material may include a metal nanowire, a carbon nanotube, or a metal oxide semiconductor.
In an embodiment of the invention, a metal of the metal nanowire may include gold, silver, or copper.
In an embodiment of the invention, a metal oxide of the metal oxide semiconductor may include zinc oxide, titanium oxide, tungsten oxide, molybdenum oxide, vanadium oxide, copper oxide, nickel oxide, cobalt oxide, iron oxide, or tin oxide.
In another embodiment of the invention, the two-dimensional material may include graphene oxide or molybdenum disulfide.
A manufacturing method of the pressure sensor of the invention includes forming a thin-film transistor array and forming a pressure-sensitive layer on the thin-film transistor array by 3D printing. The pressure-sensitive layer includes a plurality of insulating layers and a plurality of one-dimensional materials arranged on the same plane that are alternately stacked, or the pressure-sensitive layer includes a plurality of insulating layers and a plurality of two-dimensional materials that are alternately stacked.
Based on the above, in the pressure sensor of the invention, by disposing alternately stacked insulating layers and one- or two-dimensional materials arranged on the same plane in the pressure-sensitive layer, the conductive structure in the pressure-sensitive layer may be a conductive layer having directionality, and therefore the pressure resolution of the pressure sensor is enhanced.
In order to make the aforementioned features and advantages of the disclosure more comprehensible, embodiments accompanied with figures are described in detail below.
The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
Please refer to
Hereinafter, the detailed structure of the pressure sensor of
Please refer first to
In the present embodiment, the diameter of the one-dimensional material is generally 5 nm to 100 nm, preferably 20 nm to 80 nm, and more preferably 40 nm to 60 nm. Moreover, in terms of good conductivity, the length of the one-dimensional material is not particularly limited provided the aspect ratio of the one-dimensional material is greater than 100. For instance, the one-dimensional material may include a metal nanowire, a carbon nanotube, or a metal oxide semiconductor. The metal of the metal nanowire may include gold, silver, or copper, but is not limited thereto. The metal oxide of the metal oxide semiconductor may include zinc oxide, titanium oxide, tungsten oxide, molybdenum oxide, vanadium oxide, copper oxide, nickel oxide, cobalt oxide, iron oxide, or tin oxide, but is not limited thereto.
In
When pressure is not applied, as shown in
Moreover, the one-dimensional materials 206 may also be replaced by two-dimensional materials (not shown) such that a pressure-sensitive layer is formed by the alternate stacking of the two-dimensional materials and the insulating layers 208. The two-dimensional materials may include, for instance, graphene oxide or molybdenum disulfide (MoS2), but is not limited thereto. The structure of the two-dimensional materials may also be alternately stacked with the insulating layers 208 to prevent contact of the two-dimensional materials between the layers. Therefore, the embodiment thereof is similar to that of the one-dimensional materials and is therefore not repeated herein.
Hereinafter, the manufacturing method of the pressure sensor according to another embodiment of the invention is described. Please refer to
First, step 300 is performed to form a TFT (thin-film transistor) array, and the method of forming the TFT array may adopt any known manufacturing method.
Then, step 302 is performed to form a pressure-sensitive layer on the TFT array by 3D printing, wherein the pressure-sensitive layer includes insulating layers and one-dimensional materials arranged on the same plane, and the insulating layers and the one-dimensional materials are alternately stacked. In other embodiment, the pressure-sensitive layer includes insulating layers and two-dimensional materials, and the insulating layers and the two-dimensional materials are alternately stacked. The one-dimensional materials and the two-dimensional materials are as described in each of the embodiments above and are therefore not repeated herein. When the pressure-sensitive layer is a one-dimensional material, the insulating layers and the one-dimensional materials are alternately formed on the TFT array, and therefore the one-dimensional materials between the layers do not come in contact in the absence of pressure, and current is transferred between the one-dimensional materials only after the pressure-sensitive layer is subjected to a certain amount of pressure to change (reduce) the resistance of the pressure sensor.
When the pressure-sensitive layer includes two-dimensional materials, the insulating layers and the two-dimensional materials are similarly alternately formed on the TFT array, and the results thereof are the same as those of the pressure-sensitive layer formed by one-dimensional materials.
Moreover, in addition to the 3D printing, the method of forming the pressure-sensitive layer may also adopt a manufacturing method suitable for roll-to-roll such as screen printing or gravure printing.
Based on the above, in the pressure sensor of the invention, by alternately stacking the plurality of one-dimensional materials arranged on the same plane and the insulating layers or alternately stacking the plurality of two-dimensional materials and the insulating layers in the pressure-sensitive layer, the pressure resolution of the pressure sensor may be enhanced. The reason is that, current transfer between the one-dimensional materials or two-dimensional materials has directionality, and therefore in comparison to conventional pressure sensor in which the pressure-sensitive layer contains conductive particles, the invention may provide better pressure resolution.
Although the invention has been described with reference to the above embodiments, it will be apparent to one of ordinary skill in the art that modifications to the described embodiments may be made without departing from the spirit of the invention. Accordingly, the scope of the invention is defined by the attached claims not by the above detailed descriptions.