Patent Application
20160111571
1. Technical Field
The disclosure generally relates to flexible low moisture vapor transmission rate (low MVTR) sealing tapes and, more particularly, to a desiccated flexible low MVTR sealing tape for sealing the edge of photovoltaic modules wherein one surface of the tape is primed for bonding to a fluoropolymer-based member. The disclosure also relates to a photovoltaic cell, module, or array that includes the primed tape and different methods for manufacturing and using the primed tape.
2. Background Information
A photovoltaic module generally includes two silicone layers, a bottom contact, and a top contact grid sealed between top and back substrates or sheets using a clear laminating adhesive such as EVA (ethylene vinyl acetate) or PVB (polyvinyl butyral). A low MVTR edge seal is used about the perimeter between the top and back substrates to seal the interior of the module against moisture and moisture vapor. Clear fluoropolymer films, such as those sold by Dupont or 3M, are used as the top layer of some photovoltaic modules. The fluoropolymer-based films protect the modules from damage and increase their useful life.
One type of low MVTR edge tape is a desiccated butyl sealing tape. Bonding a low MVTR desiccated butyl edge tape to a flexible fluoropolymer-based top sheet in a photovoltaic module can be problematic due to the top sheet chemical structure which is predominately fluoropolymer based. In order to achieve a good bond, which fails in a cohesive manner in a typical peel test to the fluoropolymer substrate, requires some type of primer to make the butyl tape bond to the substrate. Problems exist with primers in their application. Typically they can be solvent borne coatings with non-VOC compliant solvents making up a large portion of the system. Many users shy away from the solvent borne coatings for health and safety reasons. Another issue with the use of primers is the time that is required to allow the coating to dry can sometimes be excessive.
The disclosure provides an edge sealing tape for photovoltaic modules wherein one side of the edge sealing tape carries a primer suitable for bonding the edge sealing tape to the top sheet. In one exemplary configuration, the edge sealing tape is a polyisobutylene-based material such as butyl and carries a primer disposed between one side of the edge sealing tape and a release liner wherein the primer is configured to bond with a fluoropolymer-based top sheet such that the edge sealing tape cohesively fails after the primer bonds the tape to the top sheet.
The disclosure also provides a photovoltaic module that incorporates the primed tape described above.
The disclosure also provides a method for forming the edge sealing tape described above. The method generally includes the steps of casting the primer onto a release layer and then flashing off the solvent with heat. The resulting primer film assembly is slit to the desired width and wound for use. The primer film assembly is then fed through an extrusion process and a desiccated low MVTR pressure sensitive adhesive material is applied to the primer film assembly so that the primer and the desiccated low MVTR material are in intimate contact with one another to form a desiccated low MVTR pressure sensitive tape. The desiccated low MVTR material may be a polyisobutylene-based material such as butyl. This intimate contact occurs while the desiccated low MVTR material is at an elevated temperature during the extrusion process and, as such, there is excellent bonding between the desiccated low MVTR material and the primer.
The disclosure also provides a method for using the primed edge sealing tape with a top sheet and a bottom sheet to form a sealed photovoltaic unit. When the low MVTR pressure sensitive tape is removed from the release film, the primer is carried on an exterior side of the tape such that the primer may be placed in contact with the fluoropolymer top sheet to secure bonding between the tape and the top sheet.
The disclosure also provides an alternative method wherein the primer film is connected to the low MVTR adhesive material after the low MVTR material is connected to one of the substrates or sheets of the photovoltaic module.
The drawings are not to scale and are schematic. Similar reference numbers refer to similar structures through the specification.
Tape 10 of
As shown in
An alternative method to connect the primer to the sealing body is to extrude the sealing body 12 and then coat the primer on the top of the sealing body 12. Drawbacks with this method are that the solvent of the primer contacts the sealing body and degrades the sealing body such as by softening the sealing body or by degrading the sealing body and, when the solvent is water-based, consuming desiccant. Another drawback is that winding the assembly before solvent is gone causes solvent to permeate the package of tape.
Another desirable alternative method is shown in
When the final photovoltaic is laminated, the top sheet 22 is adhered to the desiccated low MVTR pressure sensitive adhesive tape 10 such that when it is peeled apart the desiccated low MVTR PSA tape 10 will tear and leave a residue of material 46 on the fluoropolymer top sheet 22 in cohesive failure. This is opposed to a system that does not have the primer film applied to the desiccated low MVTR PSA tape which when peeled from the fluoropolymer top sheet will leave no residue on the substrate.
The MVTR is tested as described in ASTM F1249 which is incorporated herein by reference and a low MVTR is considered to be less than 1 gram per square meter per day for a 60 mil thick test sample when tested at 100% relative humidity at 37.5 degrees C.
Although isobutylene based polymers such as polyisobutylene and butyl rubber are preferred for sealing body 12 due to their low MVTR, other polymers may be used instead of or in addition to isobutylene based polymers. Isobutylene-based polymers will be defined as polymers comprising at least 80 mole percent repeat units from isobutylene. Examples of other polymers include ethylene-propylene polymer, ethylene-propylene diene polymer (EPDM), ethylene-vinyl acetate, acrylic rubber, neoprene rubber, chlorosulfonated polyethylene, urethane, epoxy, natural rubber, polymer from conjugated dienes such as synthetic polyisoprene polybutadiene, nitrile rubber, or styrene-butadiene rubber, and amorphous polyolefins (e.g., homopolymer or copolymer of propene along with other monoolefins or diolefins having from 2 to 10 carbon atoms and having less than 20 wt. % crystallinity as polymers and being other than EPDM and ethylene-propylene polymer). Polyisobutylenes desirably have a number average molecular weight of about 2,000 to 1,400,000 or more, and more desirably from 10,000 to 800,000. The polyisobutylenes are desirably polymers of essentially isobutylene with initiator fragments and/or chain transfer or chain terminator fragments. Butyl rubber is a polymer comprising from about 80 to about 98 or 99 wt. % isobutylene and from about 1 to about 20 wt. % of other monomers such as dienes with from 4 to 12 carbon atoms (e.g., isoprene), and/or aromatic vinyl monomers with from 8 to 16 carbon atoms such as styrene, para-methylstyrene, etc. If para-methylstyrene is a comonomer, desirably the polymer is halogenated (e.g., brominated). Butyl rubber desirably has a number average molecular weight from about 250,000 to about 600,000, more desirably from about 350,000 to about 450,000. The other polymers desirably have number average molecular weights from about 10,000 to 1,000,000 or 2,000,000. Amorphous polyalphaolefins desirably have a number average molecular weight from about 10,000 to about 40,000, more desirably from about 10,000 to about 25,000. If butyl rubber is present in the core, it is desirably from about 5 to about 70 wt. % of the polymers of the core. Amorphous polyalphaolefins are often used in combination with polyisobutylene and/or butyl rubber. The weight ratio of amorphous polyalphaolefins to polyisobutylene and/or butyl rubber is desirably from 1:8 to 8:1 and more desirably from 1:4 to 4:1.
In the foregoing description, certain terms have been used for brevity, clearness, and understanding. No unnecessary limitations are to be implied therefrom beyond the requirement of the prior art because such terms are used for descriptive purposes and are intended to be broadly construed. Moreover, the description and illustration of the invention is an example and the invention is not limited to the exact details shown or described. Throughout the description and claims of this specification the words “comprise” and “include” as well as variations of those words, such as “comprises,” “includes,” “comprising,” and “including” are not intended to exclude additives, components, integers, or steps.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2013/047344 | 6/24/2013 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 61663388 | Jun 2012 | US |