The present invention relates to primers for firearms and other munitions. More specifically, a primer made from layered metal oxide and reducing metal, along with a layer of a carbide-containing ceramic is provided.
Cartridges for firearms, as well as other munitions such as larger projectile cartridges and explosives are often ignited by a primer. Presently available primers and detonators are made from a copper or brass alloy cup with a brass anvil and containing lead azide or lead styphnate. When the base of the cup is struck by a firing pin, the priming compound is crushed between the cup's base and the anvil, igniting the primer charge. The burning primer then ignites another flammable substance such as smokeless powder, explosive substances, etc. Lead azide and lead styphnate are hazardous due to their toxicity as well as their highly explosive nature. Additionally, present manufacturing methods are very labor-intensive, with the necessary manual processes raising costs, causing greater difficulty in maintaining quality control.
Energetic materials such as thermite are presently used when highly exothermic reactions are needed. Uses include cutting, welding, purification of metal ores, and enhancing the effects of high explosives. A thermite reaction occurs between a metal oxide and a reducing metal. Examples of metal oxides include La2O3, AgO, ThO2, SrO, ZrO2, UO2, BaO, CeO2, B2O3, SiO2, V2O5, Ta2O5, NiO, Ni2O3, Cr2O3, MoO3, P2O5, SnO2, WO2, WO3, Fe3O4, CoO, Co3O4, Sb2O3, PbO, Fe2O3, Bi2O3, MnO2, Cu2O, and CuO. Example reducing metals include Al, Zr, Th, Ca, Mg, U, B, Ce, Be, Ti, Ta, Hf, and La. The reducing metal may also be in the form of an alloy or intermetallic compound of the above-listed metals.
There is a need for a primer made from materials that do not share the toxicity of lead. There is a further need for a primer made from materials that lend themselves to automated processes. Another need exists for a primer made from energetic materials that lends itself to ignition through a strike by a firing pin, but which otherwise benefits from the stability of thermite.
The above needs are met by a thermite primer. The primer has a substrate having a deposition surface and a rear surface. Alternating layers of metal oxide and reducing metal are deposited upon the substrate. The alternating layers of metal oxide and reducing metal are structured to react with each other in response to an impact applied to the rear face of the substrate. A carbide-containing ceramic layer is disposed within the alternating layers of metal oxide and reducing metal.
The above needs are also met by a cartridge for a firearm. The cartridge comprises a casing having a front end, a back end, and a hollow interior. The cartridge has a bullet secured within the front end of the casing, a propellant disposed within the hollow interior, and a primer secured within the back end of the casing. The primer is in communication with the propellant. The primer comprises a substrate having a deposition surface and a rear surface. The primer further comprises alternating layers of metal oxide and reducing metal deposited upon the substrate. The alternating layers of metal oxide and reducing metal are structured to react with each other in response to an impact applied to the rear surface of the substrate. The primer further comprises a carbide-containing ceramic layer within the alternating layers of metal oxide and reducing metal.
These and other aspects of the invention will become more apparent through the following description and drawings.
Like reference characters denote like elements throughout the drawings.
Referring to
The substrate 12 in the illustrated example is a malleable disk, made from a material such as brass, copper, soft steel, and/or stainless steel, having a deposition surface 20 upon which the layered thermite coating 14 is deposited, and a rear surface 22 (
The layered thermite coating 14 includes alternating layers of metal oxide and reducing metal (with only a small number of layers illustrated for clarity). Examples of metal oxides include La2O3, AgO, ThO2, SrO, ZrO2, UO2, BaO, CeO2, B2O3, SiO2, V2O5, Ta2O5, NiO, Ni2O3, Cr2O3, MoO3, P2O5, SnO2, WO2, WO3, Fe3O4, CoO, Co3O4, Sb2O3, PbO, Fe2O3, Bi2O3, MnO2, Cu2O, and CuO. Example reducing metals include Al, Zr, Th, Ca, Mg, U, B, Ce, Be, Ti, Ta, Hf, and La. The metal oxide and reducing metal are preferably selected to resist abrasion or other damage to a barrel of a firearm with which a cartridge containing the primer is used by avoiding reaction products which could potentially cause such damage. One example of such a combination of metal oxide and reducing metal is cupric oxide and magnesium.
The thickness of each metal oxide layer and reducing metal layer are determined to ensure that the proportions of metal oxide and reducing metal are such so that both will be substantially consumed by the exothermic reaction. As one example, in the case of a metal oxide layer made from CuO and reducing metal layer made from Mg, the chemical reaction is CuO+Mg→Cu+MgO+heat. The reaction therefore requires one mole of CuO, weighing 79.5454 grams/mole, for every one mole of Mg, weighing 24.305 grams/mole. CuO has a density of 6.315 g/cm3, and magnesium has a density of 1.74 g/cm3. Therefore, the volume of CuO required for every mole is 12.596 cm3. Similarly, the volume of Mg required for every mole is 13.968 cm3. Therefore, within the illustrated example, each layer of metal oxide is about the same thickness or slightly thinner than the corresponding layer of reducing metal. If other metal oxides and reducing metals are selected, then the relative thickness of the metal oxide and reducing metal can be similarly determined.
The illustrated example in
The illustrated example of the thermite coating 14 in
As another example, all layers of metal oxide and reducing metal may be less than about 100 nm thick, and the time required to consume all layers of metal oxide and reducing metal may be increased sufficiently to ignite conventional propellants and explosives by simply increasing the number of layers of metal oxide and reducing metal.
Other examples of the layered thermite coating 14 may include layers 28, 30, 32, 34, or layers 36, 38, 40, 42, 44, 46, 48, 50, that are deposited under different temperatures, so that each layer is deposited under a temperature which is either sufficiently higher or sufficiently lower than the adjacent layers to induce thermal expansion and contraction stresses within the layered thermite coating 14 once temperature is equalized within the layered thermite coating. Such expansion and contraction stresses are anticipated to result in increased sensitivity to ignition through a physical impact.
A passivation layer 18 covers the layered thermite coating 14, protecting the metal oxide and reducing metal within the layered thermite coating 14. One example of a passivation layer 18 is silicon nitride. Alternative passivation layers 18 can be made from reactive metals that self-passivate, for example, aluminum or chromium. When oxide forms on the surface of such metals, the oxide is self-sealing, so that oxide formation stops once the exposed surface of the metal is completely covered with oxide.
The carbide-containing ceramic layer(s) 16 are disposed within the thermite layers 14. In the illustrated examples, one carbide-containing ceramic layers 16 is disposed about ⅓ of the distance to the top of the thermite coating 14. In other examples, a carbide-containing ceramic layer 16 may be located elsewhere in the thermite coating 14, such as a lower portion, a central portion, the top, the bottom, or elsewhere in the upper portion of the thermite coating 14. Some examples may include a plurality of layers carbide-containing ceramic layers 16 which are located in different positions throughout the thermite coating 14. Although one or two layers are illustrated, three or more layers may be utilized. The thickness of the carbide-containing ceramic layer(s) 16 is thicker than the metal oxide or reducing metal layers, and in the illustrated example is between about 100 nm and about 2 μm thick. Other examples of the carbide-containing ceramic layer(s) 16 may be between about 500 nm and about 1 μm thick.
Carbide-containing ceramics are selected for their propensity, when ignited by ignition of the adjacent reducing metal and metal oxide, to project relatively large (as compared to the thermite reaction products) particles into the propellant of a firearm cartridge or other ignitable or detonatable material. Examples include ceramics such as zirconium carbide, titanium carbide, or silicon carbide, as well as aluminum carbide (which is a metal-ceramic composite but will be considered to be a carbide-containing ceramic herein), and combinations thereof. If more than one carbide-containing ceramic layer is present, then the different carbide-containing ceramic layers may be composed of the same carbide-containing ceramic, or different carbide-containing ceramics. Ignition of these carbides (or other suitable carbides) will result in the formation of carbon dioxide through the reaction with oxygen from the cupric oxide. This gas production will aid in propelling the reaction products of the thermite as well as the reaction products of the carbide-containing ceramic into the propellant or other ignitable or detonatable material. The large, hot particles resulting from the reaction of the carbide-containing ceramic with oxygen will burn for a sufficient period of time to ensure reliable ignition of the propellant or other ignitable or detonatable material.
Some examples of the primer compound 10 may include an adhesion layer 17 above and below each carbide-containing ceramic layer 16. In the illustrated example, the adhesion layers 17 are made from titanium or chromium. Nickel may also be used as an adhesion layer in some examples. The illustrated examples of the adhesion layers 17 are about 5 nm to about 10 nm thick.
A layered thermite coating 14 can be made by sputtering or physical vapor deposition. In particular, high power impulse magnetron sputtering can rapidly produce the thermite coating 14. As another option, specific manufacturing methods described in U.S. Pat. No. 8,298,358, issued to Kevin R. Coffey et al. on Oct. 30, 2012, and U.S. Pat. No. 8,465,608, issued to Kevin R. Coffey et al. on Jun. 18, 2013, are suited to depositing the alternating metal oxide and reducing metal layers in a manner that resists the formation of oxides between the alternating layers, and the entire disclosure of both patents is expressly incorporated herein by reference. Dr. Coffey's methods permit the interface between alternating metal oxide and reducing metal layers to be either substantially free of metal oxide, or if reducing metal oxides are present, then the reducing metal oxide layer forming the interface will have a thickness of less than about 2 nm. Or a thickness of less than 1 nm. In many examples, the interface will be sufficiently thin so that most of the interface is non-measurable during high-resolution transmission electron microscope detection. Depositing individual layers of the metal oxide and reducing metal under elevated and/or reduced temperatures can optionally be used to create expansion/contraction stresses with respect to other layers within the layered thermite coating 14 as these layers return to room temperature, thereby enhancing the sensitivity of primers 10 to firing pin strikes. If desired, lithography can be used to remove undesired portions of each layer in regions of the substrates 12 where the deposited material is not desired, leaving only that portion which is intended to be coated with the primer composition 10.
A layered thermite coating 14 can also be made using a deposition system using a rotating drum. Such systems are described in the following patents or published applications, the entire disclosure of all of which are expressly incorporated herein by reference: U.S. Pat. No. 8,758,580, which was issued to R. DeVito on Jun. 24, 2014; U.S. Pat. No. 5,897,519, which was issued to J. W. Seeser et al. on Mar. 9, 1999; and EP 0,328,257, which was invented by M. A. Scobey et al. and published on Aug. 16, 1989. The use of a rotating drum system permits the substrates to be rapidly transferred between different chambers for deposition of different layers made from different materials. In one example, some chamber(s) will be used to deposit the reducing metal, other chamber(s) will be used to deposit the metal oxide, and still other chamber(s) will be used to deposit the carbide-containing ceramic. In a four chamber system, other chambers may be used to deposit the adhesion layers above and below the carbide-containing ceramic. One example may utilize between two and four chambers, with two targets per chamber. The atmospheric conditions within each chamber are maintained, and isolated from other portions of the system, by baffles which extend close to the drum while maintaining separation from the substrates. Substrates may thereby be moved between chambers by rotating the drum upon which the substrates are located while maintaining the correct pressure and atmospheric conditions of each chamber throughout the process of depositing multiple layers. Additionally, the pressure of an inert gas, for example, argon in the chamber utilized to deposit reducing metal may be greater than the pressure in the chamber utilized to deposit metal oxide, thus resisting the entry of oxygen into the reducing metal chamber. The need to pump down each chamber between layers of different material is thus avoided, speeding and simplifying the deposition process.
Once all layers of metal oxide 28, 30, reducing metal 32, 34, and carbide-containing ceramic 16 are deposited, the passivation layer 18 may be deposited onto the layered thermite coatings 14 using any of the above-described methods.
Referring to
As another example, the primer compound 10 can be used as the deposited ignitable material within the primer disclosed within US 2020/0400415, which was invented by Timothy Mohler and Daniel Yates and published on Dec. 24, 2020, the entire disclosure of which is expressly incorporated herein by reference.
Although the illustrated examples are for a firearm cartridge, the primer composition 10 can be used for a larger projectile cartridge such as those for artillery, or for other munitions such as hand grenades and other explosives that utilize a primer as part of their detonation mechanism.
The present invention therefore provides a primer made from materials that do not have the toxicity or other safety issues of conventional primers. The primers are easily manufactured by methods that lend themselves to automation. The primer provides at least the reliability of conventional primers while also taking advantage of the stability of thermite. By adjusting the thickness of the thermite layers within the primary and secondary ignition portions, as well as by the optional creation of expansion/contraction stresses, the sensitivity of the primer can be adjusted, and tailored to specific applications. The location and thickness of the carbide-containing ceramic layers can also be tailored to specific applications. The primer is useful not only for firearm cartridges, but also for other projectiles such as artillery, grenades, and other explosives and munitions. One example of the primer will fit within a space designed for a conventional primer.
A variety of modifications to the above-described embodiments will be apparent to those skilled in the art from this disclosure. For example, the shape of the primer may be round, square, rectangular, or have an entirely different shape, with or without a beveled edge, or with the beveled edge on either side of the primer. The primer may fit a conventional or unconventional primer pocket. Thus, the invention may be embodied in other specific forms without departing from the spirit or essential attributes thereof. The particular embodiments disclosed are meant to be illustrative only and not limiting as to the scope of the invention. The appended claims, rather than to the foregoing specification, should be referenced to indicate the scope of the invention.
This application claims the benefit of U.S. provisional patent application Ser. No. 63/150,017, which was filed on Feb. 16, 2021, and entitled “Primer for Firearms and Other Munitions.”
| Number | Date | Country | |
|---|---|---|---|
| 63150017 | Feb 2021 | US |