Patent Application
20070287237
The present invention relates to a printed, self-aligned, top-gate thin film transistor (TFT), in which metal-containing inks can be used for printing the gate metal. In preferred embodiments, the metal-containing ink comprises metal nanoparticles. The present invention advantageously requires little or no high-temperature or laser activation processing after printing the metal ink.
In a conventional top-gate TFT process, alignment between the gate and the source/drain regions is ensured by first patterning the gate material and using it as a mask for dopant implantation and/or activation. This approach poses challenges regarding the choice of the gate metal because it needs to be either reflective to (UV) laser irradiation (e.g., Al) or compatible with thermal dopant activation at temperatures higher than 600° C. (e.g., doped polysilicon or a refractory metal such as Mo, Pd or W).
Conventional printing technologies (e.g., ink-jetting) can be advantageous for manufacturing electronic devices, due to the high throughput of printing processes relative to photolithography. However, high-resolution printing techniques are typically limited with respect to the width of a printed line (about 10 μm or larger), due to the relatively large volume of the drops.
Thus, it would be desirable to develop a process for making TFTs that can form small (e.g., <10 μm) line-width structures such as gates using printing technology, and/or that is not restricted to certain gate materials such as aluminum, refractory metals or doped polysilicon.
One object of the invention is to provide a method of forming a thin film transistor (TFT), comprising: forming a semiconductor thin film layer; printing a doped glass pattern thereon, a gap in the doped glass pattern defining a channel region of the TFT; forming a gate electrode on or over the channel region, the gate electrode comprising a gate dielectric film and a gate conductor thereon; and diffusing a dopant from the doped glass pattern into the semiconductor thin film layer.
Another object of the invention is to provide a thin film transistor (TFT), comprising: semiconductor thin film layer; at least part of a doped glass pattern thereon, wherein at least two portions of the doped glass pattern define a gap over a channel region of the TFT; a gate electrode on or over a channel region of the semiconductor thin film layer, the gate electrode comprising a gate dielectric film and a gate conductor thereon; and dopant-containing regions in the semiconductor thin film layer on opposed sides of the channel region.
Another object of the invention is to provide a method of forming a thin film structure, comprising: forming a semiconductor thin film layer; printing a doped glass pattern thereon, a gap in the doped glass pattern defining a channel region of the TFT; and diffusing a dopant from the doped glass pattern into the semiconductor thin film layer.
Another object of the invention is to provide a thin film structure, comprising: a semiconductor thin film layer; at least part of a doped glass pattern thereon, wherein at least two portions of the doped glass pattern define a gap over a channel region; and dopant-containing regions in the semiconductor thin film layer on opposed sides of the channel region.
In one respect, the present invention recognizes that the space between two lines may be smaller than the minimum width of an inkjet-printed line because the space between lines is mainly determined by ink placement accuracy plus the accuracy and addressability of the mechanical stages of the printer. Therefore, first printing a source/drain pattern which defines the location of subsequently deposited gate metal enables one to fabricate high performance printed top gate TFTs with channel widths <10 μm.
The present invention is therefore directed towards the manufacturing of thin film transistors and circuits thereof on various substrates including, but not limited to, glass (e.g., quartz) sheets or slips, plastic and/or metal foils, sheets or slabs, silicon wafers, etc., all of which may carry one or more buffer layers (such as silicon and/or aluminum oxide). Applications include but are not limited to displays, RF devices, sensors, etc.
FIGS. 1A-E show cross-sectional views at various stages of an exemplary process flow process for making a printed self-aligned top gate device, showing a first dopant drive-in technique.
FIGS. 2A-E show cross-sectional views of another exemplary process flow, including gate oxide formation after the printing of doped glass.
FIGS. 3A-E show cross-sectional views of a process flow that reduces potential out-diffusion from the doped glass during gate dielectric formation and (optional) further processing.
FIGS. 4A-D show cross-sectional views of a process flow for etching the doped glass pattern and forming source/drain contacts and interconnects, using the metal gate as a mask.
FIGS. 5A-E show cross-sectional views of an alternative process flow for forming source/drain contacts and interconnects.
FIGS. 6A-C show cross-sectional views of an alternative process flow in which a dielectric material over the metal gate is used as a mask when etching the doped glass pattern and forming source/drain contacts and interconnects.
FIGS. 7A-D show cross-sectional views of an alternative process flow which uses a printed interlayer dielectric as a mask for etching the doped glass and exposing the doped polysilicon source/drain regions for subsequent contact/interconnect formation.
FIGS. 8A-D show cross-sectional views of a further alternative process flow which uses a printed interlayer dielectric as a mask for non-selectively etching the doped glass and exposing the doped polysilicon source/drain regions for subsequent contact/interconnect formation.
The development of printed refractory metal or Al gates in self-aligned top-gate TFTs poses a significant challenge, which the present invention avoids by first patterning a layer defining the source/drain regions, then activating the dopant (e.g., by annealing at high temperature or by laser activation), and subsequently depositing the gate metal precursor ink. In a preferred embodiment, simple noble metal inks containing silver or gold can be used for printing the gate metal, since no high-temperature or laser activation process step is required afterwards. The present TFTs may be capable of operating at GHz frequencies and may benefit from (1) narrow channel widths, (2) source and drain terminals that are self-aligned to the gate with a small amount of overlap between, and/or (3) high carrier mobility.
Reference will now be made in detail to the preferred embodiments of the invention, examples of which are illustrated in the accompanying drawings. While the invention will be described in conjunction with the preferred embodiments, it will be understood that they are not intended to limit the invention to these embodiments. On the contrary, the invention is intended to cover alternatives, modifications and equivalents that may be included within the spirit and scope of the invention as defined by the appended claims. Furthermore, in the following disclosure numerous specific details are given to provide a thorough understanding of the invention. However, it will be apparent to one skilled in the art that the present invention may be practiced without these specific details. In other instances, well-known methods, procedures, components, and circuits have not been described in detail, to avoid unnecessarily obscuring aspects of the present invention.
For the sake of convenience and simplicity, the terms “coupled to,” “connected to,” and “in communication with” (and variations thereof) refer to direct or indirect coupling, connection or communication, unless the context clearly indicates otherwise. These terms are generally used interchangeably herein, and wherever one such term is used, it also encompasses the other terms, unless the context clearly indicates otherwise. In the present disclosure, the term “deposit” (and grammatical variations thereof) is intended to encompass all forms of deposition, including blanket deposition, coating, and printing, unless the context clearly indicates otherwise. Furthermore, with regard to certain materials, the phrase “consisting essentially of” does not exclude intentionally added dopants, which may give the material to which the dopant is added (or the element or structure formed from such material) certain desired (and potentially quite different) physical and/or electrical properties. The term “(poly)silane” refers to compounds or mixtures of compounds that consist essentially of (1) silicon and/or germanium and (2) hydrogen, and that predominantly contain species having at least 15 silicon and/or germanium atoms. Such species may contain one or more cyclic rings. The term “(cyclo)silane” refers to compounds or mixtures of compounds that consist essentially of (1) silicon and/or germanium and (2) hydrogen, and that may contain one or more cyclic rings and less than 15 silicon and/or germanium atoms. The term “hetero(cyclo)silane” refers to compounds or mixtures of compounds that consist essentially of (1) silicon and/or germanium, (2) hydrogen, and (3) one or more dopant atoms such as B, P, As or Sb that may be substituted by a conventional hydrocarbon, silane or germane substituent and that may contain one or more cyclic rings. Also, a “major surface” of a structure or feature is a surface defined at least in part by the largest axis of the structure or feature (e.g., if the structure is round and has a radius greater than its thickness, the radial surface[s] is/are the major surface of the structure; however, where the structure is square, rectangular or oval, the major surface of the structure is typically a surface defined by the two largest axes, generally the length and width).
Representative cyclosilane compounds of the formula (AHz)k wherein A is Si, z is 1 or 2 (preferably 2) and k is from 3 to 12 (preferably 4 to 8) and an exemplary method for their preparation are described in greater detail in copending application Ser. No. 10/789,317, filed Feb. 27, 2004 (Atty. Docket No. IDR0020), the relevant portions of which are incorporated herein by reference. Representative hetero(cyclo)silane compounds, doped silane intermediates, exemplary methods for their preparation, and techniques for determining and/or controlling the dopant levels in the precursor inks and active films are described in greater detail in copending application Ser. Nos. 10/950,373, 10/949,013 and 10/956,714 (Attorney Docket Nos. IDR0301, IDR0302 and IDR0303), respectively filed on Sep. 24, 2004, Sep. 24, 2004 and Oct. 1, 2004, the relevant portions of which are incorporated herein by reference. Oligo- and polysilane compounds are disclosed in U.S. Provisional Appl. Nos. 60/850,094 and 60/905,403, filed Oct. 6, 2006 and Mar. 5, 2007, respectively (Attorney Docket Nos. IDR0881 and IDR0883), the relevant portions of which are incorporated herein by reference.
Typically, although not necessarily always, liquid-phase semiconductor inks further, comprise a solvent, preferably a cycloalkane (e.g., a mono- or bicycloalkane). Thus, when using an ink comprising or consisting essentially of a Group IVA element source (such as a silane-based precursor to Si or doped Si), forming the semiconductor layer may further comprise drying the liquid-phase precursor ink after deposition. See copending U.S. application Ser. Nos. 10/616,147, 10/789,317 and 10/789,274, respectively filed Jul. 8, 2003, Feb. 27, 2004 and Feb. 27, 2004 (Attorney Docket Nos. KOV-004, IDR0020 and IDR0080, respectively), the relevant portions of each of which are incorporated herein by reference.
After deposition (and generally, at least some drying), a semiconductor layer is generally cured by heating, as described above in copending U.S. patent application Ser. No. 10/789,274 and 10/949,013 (Attorney Docket Nos. IDR0080 and IDR0302, respectively filed on Feb. 27, 2004 and Sep. 24, 2004, the relevant portions of which are incorporated herein by reference) to form an amorphous, hydrogenated (doped) silicon (a-Si:H) layer. When a semiconductor layer originates or is formed from a (poly)silane, (cyclo)silane and/or hetero(cyclo)silane, the curing/heating step may remove unwanted precursor/ink components or byproducts such as volatile carbon-containing species, or reduce the hydrogen content of the a-Si:H layer (which is particularly advantageous if laser crystallization is to be used after semiconductor film formation). When a semiconductor layer originates or is formed from a hetero(cyclo)silane, the curing/heating step may also activate part of the dopant in the hetero(cyclo)silane, but in many embodiments, dopant activation may be more likely to occur during laser crystallization.
Also, a doped semiconductor layer may be deposited by local printing of the liquid semiconductor precursor ink directly onto a structure such as the gate metal (e.g., to form a silicide), dielectric layer (e.g., a gate dielectric) and/or semiconductor layer (see, e.g., copending U.S. patent application Ser. Nos. 10/949,013, 11/084,448 and 11/203,563 [Attorney Docket Nos. IDR0302, IDR0211 and IDR0213, respectively], filed on Sep. 24, 2004, Mar. 18, 2005 and Aug. 11, 2005, respectively, the relevant portions of which are incorporated herein by reference). This approach to forming MOS TFT structures may be cost effective due to (i) the efficient usage of the semiconductor precursor materials and (ii) the combination of semiconductor deposition and patterning into one printing step.
Blanket deposition may comprise, e.g., evaporation, physical vapor deposition, sputtering, or chemical vapor deposition, as is known in the art. Alternatively, blanket deposition may comprise spin-coating an ink comprising, e.g., a (cyclo)silane, (poly)silane or metal nanoparticles (which may be passivated) and a solvent, and curing the ink (see, e.g., U.S. Pat. No. 6,878,184 and U.S. patent application Ser. No. 10/749,876, filed Dec. 31, 2003, the relevant portions of which are incorporated herein by reference). Metals that may be deposited by such methods include elemental metals, such as aluminum, titanium, vanadium, chromium, molybdenum, tungsten, iron, nickel, palladium, platinum, copper, zinc, silver, gold, etc.; conventional alloys of such elements, such as aluminum-copper alloys, aluminum-silicon alloys, aluminum-copper-silicon alloys, titanium-tungsten alloys, Mo—W alloys, aluminum-titanium alloys, etc.; and electrically conductive metal compounds, such as the nitrides and silicides of elemental metals (e.g., titanium nitride, titanium silicide, tantalum nitride, cobalt silicide, molybdenum silicide, tungsten silicide, platinum silicide, etc.). In other embodiments, the blanket depositing step may comprise spin-coating an ink containing the metal-containing material, the metal-containing material may comprise metal nanoparticles and/or organometallic precursors of one or more of the metals disclosed above. Also, whether the metal ink is blanket-deposited or printed, the method may further comprise the step of curing or annealing the metal, organometallic precursor(s) and/or metal nanoparticles before or after the step of laser patterning.
This application describes the design of, and several process flows for fabricating, a printed, self-aligned, top gate TFT. The process flow leverages a printed doped glass in at least one of three ways:
The present invention enables formation of gate line widths of less than 10 um, generally by forming a transistor gate in the space between printed structures. However, as drop volumes are expected to decrease and printing resolution is expected to increase in the future in widely-used printing techniques such as ink-jetting, gravure lithography, and offset lithography, the space between such printed structures is also expected to decrease, and the invention will continue to enable formation of gate widths less than the corresponding minimum width of a conventionally printed structure.
The invention, in its various aspects, will be explained in greater detail below with regard to exemplary embodiments.
Formation of a Self-Aligned Source/Drain Gate Structure
Dopant Drive-In through Gate Dielectric
Referring to FIGS. 1A-E, an exemplary process flow is shown. The exemplary process of FIGS. 1A-E forms the gate dielectric first, before printing a doped glass pattern. The transistor channel (e.g., comprising or consisting essentially of amorphous or polycrystalline silicon) is therefore protected from contamination by dopants from the subsequently deposited doped glass.
Referring to
Substrate 1 generally comprises a conventional mechanical support structure. Suitable electrically inert or inactive substrates may comprise a plate, disc, and/or sheet of a glass, ceramic, dielectric and/or plastic. Alternatively, suitable electrically conductive substrates may comprise a wafer, disc, sheet and/or foil of a semiconductor (e.g. silicon) and/or a metal. In the case where the substrate comprises a metal sheet and/or foil, the device may further comprise an inductor and/or capacitor, and the method may further comprise forming an inductor and/or capacitor from the metal substrate. However, any such electrically conductive substrate should have an insulator layer between it and any electrically active layer or structure thereover (e.g., semiconductor layer 2), except in a location where electrical contact is to be made from the devices on the insulator to a structure formed in the metal substrate (e.g., one or more metal pads of an interposer, inductor and/or capacitor for an EAS or RFID tag; see, e.g., U.S. patent application Ser. Nos. 10/885,283, 11/104,375 and/or 11/243,460 (Attorney Docket Nos. IDR0121, IDR0312 and IDR272), respectively filed on Jul. 6, 2004, Apr. 11, 2005, and Oct. 3, 2005, and/or U.S. Provisional Application Nos. 60/592,596 and 60/617,617 (Attorney Docket Nos. IDR0311 and IDR0271), respectively filed on Jul. 31, 2004, and Oct. 8, 2004). Preferably, the substrate comprises a member selected from the group consisting of a silicon wafer, a glass plate, a ceramic plate or disc, a plastic sheet or disc, metal foil, a metal sheet or disc, and laminated or layered combinations thereof. For example, plastic substrates may further contain a planarization layer thereon to reduce the surface roughness of the substrate, and glass and plastic substrates may further contain a surface energy modifying layer of material thereon to improve the adhesion and/or control the spreading of a material (e.g., an ink) printed or otherwise deposited thereon (see U.S. Provisional Application No. 60/______ [Attorney Docket No. IDR1091], filed on Mar. 20, 2007). In addition, electrically conductive substrates (e.g., metal foils) generally have an insulator layer (e.g., a layer of the corresponding oxide) thereon, except in areas where circuitry formed thereon makes electrical contact with a structure (such as an inductor coil, antenna or capacitor plate) formed from the conductive substrate.
Forming the semiconductor thin film layer 2 may include printing a semiconductor precursor ink on substrate 1 to form a pattern, drying the ink, curing the ink (e.g., by heating and or annealing the dried ink for a length of time sufficient to cross-link, oligomerize and/or polymerize a silane therein, and/or increase an average molecular weight, increase a viscosity and/or reduce a volatility of the composition), then partially or substantially completely crystallizing the semiconductor film pattern to form a polycrystalline film. Alternatively, where applicable, one may simply print an amorphous film, without crystallizing it. The semiconductor thin film layer 2 generally comprises one or more Group IV elements, preferably polysilicon or silicon-germanium. Typical semiconductor layer 2 thicknesses may be from about 10, 30, 75 or 100 nm to about 200, 500 or 1000 nm, or any range of values therein. The film thickness may be chosen to optimize the electrical properties of the transistor.
In various embodiments, semiconductor layer 2 comprises or consists essentially of a lightly doped inorganic semiconductor material, such as one or more Group IVA elements (e.g., silicon and/or germanium), a so-called “III-V” material (e.g., GaAs), a II-VI (or chalcogenide) semiconductor, etc., further containing a dopant (such as B, P, As or Sb) in a concentration of from ˜1016 to ˜5×1018 atoms/cm3. Exemplary lightly doped semiconductor films are disclosed in copending U.S. application Ser. No. 10/949,013, filed Sep. 24, 2004 (Attorney Docket No. IDR0302), the relevant portions of which are incorporated herein by reference. In one embodiment, the semiconductor (transistor channel) layer 2 may be lightly doped (e.g., having a dopant concentration of from about 1016 to about 5×1018 atoms/cm3). When formed from a silane-based and/or nanoparticle ink, the lightly doped semiconductor layer 2 may have a concentration profile (e.g., dopant concentration as a function of semiconductor layer thickness) in an amorphous state that is substantially uniform throughout substantially the entire thickness of the semiconductor layer.
Referring to
The gap 5 between the printed doped glass film regions defines the position of the gate metal. The width and/or spacing of the gap may range from 0.1-100 μm (preferably 1-10 μm, and in some embodiments, 1-5 μm). Upon high-temperature annealing, the dopant from the doped glass migrates through the gate dielectric into the polysilicon film, defining the source/drain regions 5. The temperature for diffusing the dopant from the doped glass through the gate dielectric is preferably lower than 1100° C., but at least about 700° C., for a length of time sufficient to dope the source/drain terminals, but leave channel region 7 undoped.
Preferably, the process of printing the doped glass utilizes a tool that can simultaneously deposit N- and P-type doped glass in different areas of the circuit. One embodiment utilizes, for instance, an inkjet printer with at least two inkjet heads on the same gantry, which are separated by a distance matching or corresponding to the distance (e.g. a multiple of such distance) between the areas of N- and P-type transistors in the circuit. The two inkjet (IJ) heads may correspondingly be connected to reservoirs of N- and P-type doped glass precursor (e.g., an ink comprising a doped spin-on glass precursor or other formulation) and may dispense N- and P-type doped glass in different areas of the circuit in the same printing pass.
Examples of precursors for the doped glass include conventional spin-on-dopant (SOD) formulations and customized versions with increased viscosity (e.g., “customized” by replacing or diluting the solvent in the conventional formulation with a similar or compatible solvent of higher viscosity), doped molecular silicon ink formulations which can be oxidized at low temperatures (e.g. ≦400° C.) after deposition (e.g. cyclic, linear or branched silane oligomers or polymers with dopant substituents, such as cyclo-Si5H9PR2, wherein R is lower [C1-C4] alkyl, phenyl or C1-C4-alkyl substituted phenyl) or dopant precursors in the formulation (e.g. tert-butyl phosphine), oxidized doped molecular silicon ink formulations (e.g. oxidized versions of cyclic, linear or branched silane oligomers or polymers (e.g., cyclo-Si5O5H10) with dopant precursors in the formulation (e.g. mono-, di- or tri-tert-butylphosphine or oxidized analogs thereof) or dopant substituents thereon, and glass forming formulations (e.g., so-called sol-gel formulations) containing phosphorous and boron compounds (e.g., organophosphates such as di-n-butylphosphate, etc.) and -borates (e.g. tri-t-butylborate, etc.). Suitable dielectrics also include compounds and/or polymers containing phosphorous and oxygen (which may further include silicon, carbon, hydrogen and/or nitrogen), boron (which may further include silicon, carbon, hydrogen, oxygen and/or nitrogen), arsenic and/or antimony (either of which may further include silicon, carbon, hydrogen and/or oxygen), etc. Exemplary phosphorous-containing dielectric precursors include:
Exemplary boron-containing dielectric precursors include:
Exemplary arsenic and/or antimony-containing dielectric precursors include:
Thus, the source and drain terminals 6 in
In various embodiments, the gate has a length of at least 0.1 microns, 0.5 microns, 1 micron, or 2 microns. In one implementation, the minimum gate length is about 5 microns. In the present disclosure, and consistent with gate dimensions as are known in the art, the gate length corresponds to the gap width or spacing. The gate may have a width of from about 1 μm to about 1000 μm or any range of values therein (e.g., from about 2 μm to about 200 μm, or from about 5 μm to about 100 μm, etc.), and a thickness of from about 10 nm to about 10,000 nm or any range of values therein (e.g., from about 50 or 100 to about 5000 nm, or from about 200 to about 2000 nm, etc.). The source and drain terminals 6 may have a thickness of from 10 to 1000 nm or any range of values therein (e.g., from 100, 200, or 250 Å to 10,000, 1000, or 500 Å), generally not to exceed the thickness of semiconductor layer 2.
Referring now to
Printing of the gate metal precursor may include ink-jetting, gravure printing, offset lithography, etc. Furthermore (or alternatively), patterning the gate metal may include coating or printing the gate metal precursor and locally exposing it to laser radiation such that it changes its solubility characteristics in the exposed areas (see, e.g., U.S. patent application Ser. No. 10/722,255, 10/749,876, and 11/203,563 [Attorney Docket Nos. KOV-015, KOV-012, and IDR0213], filed Nov. 24, 2003, Dec. 31, 2003 and Aug. 11, 2005, the relevant portions of which are incorporated herein by reference). Upon washing away the unexposed area, the irradiated gate metal precursor stays behind to form the gate metal, optionally after an additional curing or annealing step (so-called “negative” patterning and developing). Alternatively, “positive” patterning and developing may be employed, in which the area exposed to radiation is washed away. These embodiments (including the positive patterning embodiment) may provide advantages for the patterning of high-resolution metal gates which may not be directly achievable with direct printing methods. In general, the gate conductor comprises a metal. However, with respect to the gate, “metal” includes doped polysilicon.
A metal-containing ink (and, for that matter, any other printable ink disclosed herein) may be printed by essentially any conventional printing technology. For example, printing may comprise inkjet printing (“inkjetting”), screen printing, gravure printing, offset printing, flexography (flexographic printing), spray-coating, slit coating, extrusion coating, meniscus coating, microspotting, pen-coating, stenciling, stamping, syringe dispensing and/or pump dispensing the metal-containing ink in a predefined pattern. The ink may comprise or consist essentially of the metal precursor material and a solvent. The metal precursors that are generally compatible with printing or (selectively) plating may comprise organometallic compounds or nanoparticles (e.g., nanocrystals) of a metal such as titanium, copper, silver, chromium, molybdenum, tungsten, cobalt, nickel, gold, palladium, platinum, zinc, iron, etc., or metal alloys thereof, preferably silver or gold (or a metal alloy thereof). Such nanoparticles or nanocrystals may be conventionally passivated (e.g., with one or more surfactants), provided with one or more surface ligands (e.g., alkyl, aralkyl, alcohol, alkoxy, mercaptan, alkylthio, carboxylic acid and/or carboxylate groups bound thereto, or H atoms adsorbed thereon), or remain unpassivated. Plating may comprise, in one example, laser writing or printing a seed layer of metal (e.g., Pd; see U.S. Provisional Application No. 60/______ [Attorney Docket No. IDR1262], filed on May 30, 2007, the relevant portions of which are incorporated herein by reference) using nanoparticles and/or an organometallic compound of the metal, then selectively depositing (e.g., by electroless or electroplating) a bulk conductor (e.g., Co, Ni, Cu, etc.) onto the laser-written or printed seed layer. Alternatively, the ink may comprise or consist essentially of a conventional paste comprising a powder of one or more such metals or alloys thereof in a conventional binder.
The metal-containing ink may be dried by conventional and/or otherwise known processes. For example, metal precursor inks may be dried by heating the substrate containing the printed metal precursor ink thereon at a temperature and for a length of time effective to remove the solvent and/or binder. Suitable temperatures for removing solvents from a printed ink may range from about 50° C. to about 150° C., or any range of temperatures therein (e.g., from about 80 or 100° C. to about 120° C.). Suitable lengths of time for removing solvents from a printed ink at such temperatures may ranges from about 1 seconds to about 10 minutes, or any range of times therein (e.g., from about 10 or 30 seconds to about 5 minutes, or about 1 minute to 3 minutes, etc.). Such heating may take place on a conventional hotplate or in a conventional furnace or oven, optionally in an inert or reducing atmosphere.
The dried metal precursor from the ink may be further annealed at a temperature and for a length of time sufficient to improve its electrical and/or physical properties (e.g., conductivity, morphology, electromigration and/or etch resistance, stress and/or surface strain, etc.) and/or its adhesion to the underlying gate oxide. When the metal-containing ink is globally (blanket) deposited or printed, annealing is generally conducted to form a metal film on which a resist may be deposited for subsequent (laser) patterning (e.g., using conventional photolithography or laser resist processing, and/or other conventional processing. including developing, etching and/or stripping the resist). Also, when directly laser writing a metal precursor ink results in a patterned metal and/or metal precursor, annealing is generally performed to form a metal layer with improved conductivity, adhesion etc. Such annealing may comprise either annealing already-fused metal nanoparticles, or converting a patterned metal precursor layer into a patterned metal (which may include a metal silicide or doped polysilicon). Suitable annealing temperatures generally range from about 100° C. to about 500° C., or any range of temperatures therein (e.g., from about 150° C. to about 400° C.), although a temperature of up to 700° C. may be advantageous for formation of a metal silicide. Suitable lengths of time for annealing may range from about 1 minute to about 2 hours, preferably from about 10 minutes to about 1 hour, or any range of times therein (e.g., from about 10 to about 30 minutes). Annealing may be conducted in a conventional furnace or oven, optionally in an inert or reducing atmosphere. Thus, the present method may further comprise the step of annealing the laser patterned metal gate sufficiently to improve its electrical, physical and/or adhesive properties.
In one embodiment, the gate metal precursor ink may de-wet from the printed doped glass pattern, which effectively confines it to the gap defined by the doped glass pattern. The doped glass pattern may be treated (e.g., by plasma exposure, coating with a fluorinated layer or other material having similar de-wetting properties, etc.) before deposition of the gate metal precursor ink to ensure de-wetting. Similarly, the gate metal precursor ink and/or the doped glass precursor may contain additives which ensure de-wetting of the gate metal precursor ink from the doped glass pattern. In an alternative embodiment, the gate metal precursor wets the printed doped glass pattern so that it extends beyond the area of the gap between portions of the doped glass pattern, and at least partially covers the doped glass pattern. This embodiment may be advantageous for decreasing the gate-induced drain leakage in the device.
An exemplary process flow for making thin film transistors in accordance with the present invention may therefore include the following steps:
Oxide Formation after Printing Doped Glass
FIGS. 2A-E show an alternative process flow that advantageously combines gate dielectric formation by thermal oxidation of polysilicon with drive in of the dopants from the doped glass either in situ or in one process step. One important aspect of this second exemplary process, however, is to achieve gate oxide growth before significant dopant diffusion sets in.
A silicon film 12 is generally formed on substrate 11 by the same process as in
Referring to
Silicon oxidation in the exposed gate areas of the poly-Si film 12 can be accomplished by heating the film in a suitable atmosphere (air, O2, ozone, N2O, wet or dry steam, or a combination thereof) to a temperature higher than 600° C. The maximum temperature is preferably lower than 1000° C., more preferably lower than 900° C., to reduce, inhibit or prevent dopant diffusion from the doped glass into the channel region 17.
Alternatively, liquid phase deposition of SiO2 (or other metal oxide[s]) may include growing an oxide layer in the exposed gate areas by hydrolysis of a saturated aqueous solution of hexafluorosilicic acid (H2SiF6) in the presence of boric acid at relatively moderate temperatures. This approach avoids the relatively high temperatures for thermal growth of an oxide layer (e.g., from silicon) and thereby reduces or eliminates the risk of dopant diffusing from the doped glass pattern into the channel region 17, potentially shorting the transistor.
The gate dielectric film 13 in the present electronic device may comprise any of the materials for the gate dielectric film described herein. The gate dielectric film 13 may have a width and length slightly less than the corresponding dimensions of the subsequently formed gate metal layer when it is wet etched, but the two layers will have substantially the same width and length when dry etched. The gate dielectric film 13 may have a thickness of from 20 Å to 1000 Å or any range of values therein (e.g., from 30 to 300 or 400 Å, or from 50 to 200 Å, etc.). Alternatively, a thicker gate dielectric layer (e.g., in the range of from 500 to 2000 Å, and in one implementation, on the order of about 150 Å) can be used, preferably using a material having a higher dielectric constant than silicon dioxide or aluminum oxide. In one embodiment, the gate dielectric film 13 has a thickness greater than the thickness of the heavily doped source and drain terminals, largely to minimize the possibility that source and drain terminals may form an electrical connection to gate metal layer. However, for high speed transistors, generally a thin gate dielectric film is preferred. Typically, after the gate oxide 13 is formed, referring now to
Thereafter, referring to
Passivation of the Doped Glass Layer
FIGS. 3A-C show a further alternative process flow that reduces the problem of potential out-diffusion from the doped glasses during gate dielectric formation by depositing a barrier and/or passivation layer 25 or generating a similar deactivated layer 25 on the doped glass. Thus, in a further embodiment, a thin dopant-depleted layer 25 is formed on top of the printed doped glass pattern 24. This layer is intended to prevent dopant diffusion into the channel region 27 during dopant activation. The formation of this layer can be accomplished in various ways (e.g., depositing an essentially undoped glass [acting as a buffer] or a silicon nitride film). Films which effectively getter typical dopants (e.g. phosphorus or boron) may also be used. Alternatively, a surface layer depleted of dopant may be generated by exposing the patterned doped glass film to hot water or water vapor, which extracts some of the dopant from the exposed surface(s) but leaves sufficient dopant in the bulk of the glass (particularly adjacent to the interface with underlying silicon 22) to be useful for source/drain doping. Furthermore, the thin passivation and/or dopant-depleted layer 25 may be formed by exposing the patterned glass film to conditions which change its surface characteristics, such as to prevent significant dopant diffusion into the channel, e.g. by exposing it to ozone, N2O, water, etc.
Referring now to
Referring now to
In some cases, out-diffusion of dopant into the channel region 27 prior to oxidation may be desirable due to the enhanced oxidation rate of the doped material. This enhanced oxidation rate would give a thicker gate oxide 23 at the edge of the channel 27. This thicker dielectric reduces the electric field at the edge of drain 26, thereby reducing gate induced drain leakage (GIDL).
Referring now to
Formation of Source/Drain Contacts and Interconnections
The following process flows for the formation of source/drain contacts and interconnects can be used with any of the device structures and/or processes described above.
Gate as Mask for Source/Drain Contact Etch
FIGS. 4A-D show an exemplary embodiment of a process for forming source/drain contacts and an interlayer dielectric (ILD) on the basic TFT structures of
Source/drain regions 112/114 and channel 116 are formed on substrate 100 similarly to source/drain regions 6 and channel 7 of
As shown in
After etching and an optional cleaning step (not indicated), referring now to
To ensure good contact, the structure of
After printing the interconnect metal 150/152 (which may also be formed by more conventional processes, such as sputtering and photolithography, but printing is preferred), and referring now to
Printing the interlayer dielectric 160 may comprise ink-jetting, gravure, offset printing, etc., similar to the other printable inks disclosed herein. Alternatively, patterning the interlayer dielectric may comprise printing or depositing an interlayer dielectric (e.g. UV- and/or IR-sensitized polyimide), and exposing it to radiation (e.g. IR, visible, or UV radiation) to change its solubility characteristic(s) in the irradiated areas. Exposing this layer to a suitable etchant or solvent (e.g., a developer) may remove the exposed (positive) or unexposed (negative) area of the interlayer dielectric forming via holes.
In an alternative embodiment, a sacrificial material may first be printed in locations corresponding to the locations of the later formed via holes in the interlayer dielectric. Then, an interlayer dielectric precursor as outlined above is printed or globally (blanket) deposited. Upon curing the interlayer dielectric precursor, the sacrificial material in the via areas may decompose, forming the via holes. Other means of removing the sacrificial material from the via hole are envisioned (e.g., selective etching, etc.). The circuit is completed by printing an interconnect metal connecting the respective contact pads in the open via-holes (see, e.g., FIGS. 7B-C and 8B-C). The same techniques and materials as outlined above can be utilized.
Conductors in communication with one of the source/drain terminals or the gate terminal may also be coupled to or continuous with another one of the conductors. For example, in a diode-configured transistor, a conductor may be in electrical communication with one source/drain terminal and the gate. In a capacitor-configured transistor, a conductor may be in electrical communication with both source/drain terminals. Alternatively, a thin dielectric layer may be formed over a source/drain terminal, and a conductor capacitively coupled to the underlying source/drain terminal may be formed thereover.
ILD as a Mask for Source/Drain Contact Etch
FIGS. 5A-E show structures formed during an alternative process for making the present TFT. Referring to
Similar to the process of FIGS. 4A-E, the process of FIGS. 5A-E utilizes a gate 240 which is essentially confined to the area between printed doped glass regions 230 (as is gate dielectric 210) and does not cover the doped glass pattern 230. However, in this embodiment, a first interlayer dielectric 245 is deposited to protect the gate metal 240 and gate dielectric 220 during the etch of the doped glass pattern 230 to expose the source/drain regions 212/214 or contacts thereon (not shown).
In
Printing the first interlayer dielectric 245 may comprise inkjetting, gravure, offset printing, etc. Alternatively, patterning the interlayer dielectric may comprise printing or depositing an interlayer dielectric (e.g. UV- and/or IR-sensitized polyimide), and exposing it to radiation (e.g., IR, visible, or UV radiation) to change its solubility characteristic(s) in the irradiated areas. Exposing this layer to a suitable etchant or solvent (e.g., developer) will remove the exposed (positive) or unexposed (negative) area of the interlayer dielectric forming via holes.
Subsequently, as shown in
Thus, depending on the etch time, the etchant may remove only relatively narrow portions of the doped glass pattern 230, exposing only a small boundary or area of the source/drain regions 214/216. In this case, all materials mentioned above are suitable for the first interlayer dielectric 245, as long as its thickness is sufficient to protect the gate metal and dielectric given its potentially low etch selectivity relative to the doped glass 230.
Alternatively, and referring now to
Subsequently, the doped glass pattern 230 (see
Referring now to
Printing and forming the interconnect metal may include printing a suitable interconnect metal precursor (e.g. metal nanoparticles or organometallic compound(s), silicide precursor ink(s), etc.) and converting it to the interconnect metal, largely as described herein. Alternatively, a precursor for a seed layer can be printed on the contact areas and converted to a seed layer, then the interconnect metal (e.g., Ag, Au, Cu, Pd, Pt, etc.) can be electroplated or electrolessly plated on the seed layer. The seed layer may require an activation step before the plating process.
Alternatively, patterning of the interconnect metal may include coating or printing the interconnect metal precursor and locally exposing it to laser radiation such that the solubility characteristics of the printed interconnect metal precursor changes in the exposed areas. Upon washing away either the exposed or unexposed area (preferably the unexposed area), the irradiated interconnect metal precursor stays behind to form the interconnect metal, optionally after an additional curing or annealing step. This embodiment may provide advantages for the patterning of high-resolution metal interconnect which may not directly be achievable with direct printing methods.
To ensure good contact, the structure may furthermore be annealed to form a silicide at the interface or throughout the entire film thickness of the contact areas between the interconnect metal and the silicon. Thus, in such an embodiment, the interlayer dielectric protecting the gate metal 240 during the etch of the doped glass pattern 230 is compatible with the silicidation temperature.
Referring now to
A Printed ILD as a Mask for Doped Glass Etching
The process flows of
Referring to
Subsequently, and as shown in
In either case, the etch time is chosen such that most (but not the entire) doped glass layer is removed from over the source/drain regions 312/314. Specifically, a small amount of doped glass 332 adjacent to the gate metal 340 and gate dielectric film 320, covered by the first interlayer dielectric 350 or 350′, remains.
After etching and an optional cleaning step (not shown), an interconnect metal 360/362 can be printed on the exposed source/drain regions 312/314, as shown in
After printing the interconnect metal 360/362, as shown in
In certain embodiments of the present process (not necessarily limited to
Alternatively, a semiconductor layer (e.g., having characteristics of the transistor channel 7, 17, 27, 116, 210, or 310, such a dopant level or concentration) may be formed by printing or coating the substrate with a doped or undoped semiconductor ink while simultaneously irradiating the ink/substrate. In one implementation, the process comprises spin-coating the ink containing a semiconductor precursor onto a substrate, while irradiating the ink with ultraviolet light during a substantial part of the spin-coating step. This technique (which, in the latter implementation, is sometimes known as “UV spin-coating”) is described in greater detail in co-pending U.S. patent application Ser. No. 10/789,274 (Attorney Docket No. IDR0080), filed on Feb. 27, 2004, the relevant portions of which are incorporated herein by reference. In another implementation, printing (which may include simultaneous or immediately subsequent UV irradiation) comprises inkjetting or gravure, flexographic, screen or offset printing a doped or undoped semiconductor ink in locations on the substrate corresponding to active transistor regions (or other deposition technique for depositing material in selected areas of the substrate). In either case, the semiconductor layer generally has an amorphous morphology following deposition (with optional substantially simultaneous irradiation) and curing, and before further processing, it is generally crystallized (e.g., by heating or by laser irradiation; see, e.g., U.S. patent application Ser. Nos. 10/950,373 and 10/949,013 [Attorney Docket Nos. IDR0301 and IDR0302], each of which was filed on Sep. 24, 2004, the relevant portions of which are incorporated herein by reference). In many cases, such crystallization will also activate at least some of the dopant.
The present invention advantageously provides a low cost method for making printed self-aligned top-gate TFTs having reliable, commercially acceptable electrical characteristics (e.g., on/off speeds and ratios, carrier mobilities, Vt's, etc.). The invention advantageously provides (1) results similar to structures formed by more conventional approaches, but at a much lower cost and at a much higher throughput (on the order of hours to days, as opposed to weeks to months) than conventional process technology, and (2) TFTs with higher resolution patterning capability and similar or higher throughput as compared to conventional graphic arts printing technology (e.g., inkjetting).
The foregoing descriptions of specific embodiments of the present invention have been presented for purposes of illustration and description. They are not intended to be exhaustive or to limit the invention to the precise forms disclosed, and obviously many modifications and variations are possible in light of the above teaching. The embodiments were chosen and described in order to best explain the principles of the invention and its practical application, to thereby enable others skilled in the art to best utilize the invention and various embodiments with various modifications as are suited to the particular use contemplated. It is intended that the scope of the invention be defined by the Claims appended hereto and their equivalents.
This application claims the benefit of U.S. Provisional Application No. 60/813,161, filed Jun. 12, 2006 (Attorney Docket No. IDR0811), which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 60813161 | Jun 2006 | US |