Patent Application
20070289486
Conventional printing ink and coating compositions have been formulated to contain water based acrylic and/or polyamide polymers as a pigment binder. For example, U.S. Pat. No. 5,948,419 discloses the use of aqueous emulsion acrylic polymers to formulate nail coatings. To improve the hardness and adhesion performance properties of such nail coatings, the acrylic emulsion is reacted with an organofunctional hydrolyzable silane coupling agent. In another example, U.S. Pat. No. 6,620,880 discloses architectural coatings wherein an improvement in water resistance is achieved by employing coating formulas containing a starch which has been modified by having an acrylic monomer grafted onto it.
Where conventional formulas containing acrylic polymer and/or co-polymer as the pigment binders are used as printing inks and coatings, these formulas typically suffer from a loss in gloss, wet block resistance, shelf life viscosity stability and pH stability. Another disadvantage for ink and coating formulas using acrylic polymers and co-polymers as a pigment binder is that they require the incorporation of an excess of amine in order to maintain the solubility of the acrylate and stabilize the viscosity and pH of the formula. In addition, the unavoidable evaporative losses of amine, can inherently contribute to a pH drift in the formulation, generating odor. Ink formulas using water based polyamide polymers and co-polymers as the pigment binder exhibit similar disadvantages such as the poor repulpability of substrates or materials printed with such ink and higher initial viscosities.
Starches or polysaccharides have been used to formulate water based newsprint inks. For example, U.S. Pat. No. 4,310,356 discloses an aqueous newsprint ink formula containing carbon black pigment, a starch such as corn starch, corn dextrin or potato dextrin and a salt such as calcium chloride, which acts as a viscosity stabilizer. In such ink formula, the salt is employed to offset the viscosity increase over time caused by the starch via a process called “retrogradation” whereby the starch molecules form intermolecular associations. As such, the viscosity of the ink will depend mainly on the amount and type of starch used in the ink formula. In addition, the starch may be cross-linked by cross-linking agents such as urea-formaldehyde, ketone, resorcinol-formaldehyde, melamine-formaldehyde, glyoxals and carbamates to improve the water resistance of the ink. In another example, U.S. Pat. No. 4,310,356 discloses a water based news print ink prepared using pigment and starch. The inks, however, are not fully suitable for printing on corrugated substrates owing to their poor drying, rub resistance, hiding power and foaming properties.
It is an object of the present invention to provide printing ink and coating compositions designed to print on towel, tissue, corrugated substrates and other porous substrates, offering improvements in chemical resistance, solubility, ink strength, pigment loading, pH stability, higher coefficient of friction, and heat resistance. Such printing ink compositions would also offer improved repulpability of substrates or materials printed with such compositions. Another object of the present invention is to eliminate the need for incorporating excess amine in acrylic based formulas to solubilize the acrylate and thus reduce any odor otherwise generated by such amines.
Provided is an aqueous printing ink and coating composition containing a colorant, one or more high molecular weight starches and one or more water soluble acrylic polymers or co-polymers. The aqueous inks are useful for printing on cellulosic substrates, such as towel and tissue substrates, which exhibit improvements in properties including the repulpability of such substrates. Such characteristics include, for instance, the ability to be printed on corrugated substrates and exhibit improvements in gloss, chemical resistance, solubility, the elimination of excess amines to achieve solubility and thereby reduce odor, increased ink strength, pigment loading, pH stability, higher coefficient of friction and heat resistance. The compositions exhibit an ability for printing on corrugated substrates. The printing inks or coatings formulated exploit the synergistic benefits of combining the starch and acrylics without grafting one on the other.
The aqueous printing ink and coating compositions contain colorant, high molecular weight starch and water soluble acrylic polymer and are useful for printing on conventional towel, tissue and corrugated substrates, as well as other porous substrates such as, for instance, paper. They improve the repulpability of substrates or materials printed with such compositions. Furthermore, these inks and coatings contain a lower amount of amine resulting in less odor and a more stable pH.
The high molecular weight starches, or polysaccharides, suitable for use in the present invention are derived from an abundance of renewable natural products such as corn, potatoes, wheat, maize, rice, sago, sorghum and tapioca; also included are starch degradation products such as dextrin, thin boiling starches, maltodextrins and polysaccharides such as polymers of sugar. Additional starches suitable for use in the present invention are described, for example, in U.S. Pat. No. 6,620,880. As used herein, the term “high molecular weight” means a number average of at least about 100,000, preferably at least about 200,000, and most preferably at least about 250,000. A single starch or a combination of starches may be employed. A particularly preferred source of high molecular weight starch is LPR41 polysaccharide, a dispersion of starch from corn in polyethylene glycol and water, available from Lorama Chemicals.
The amount of high molecular weight starch to be used will vary with factors such as, for example, the type of starch, the type and amount of colorant, the type and amount of acrylic, and other solids. The term “solids” as used herein refers to the starch, acrylic, colorant and any other non-volatile ingredients which optionally may be added to the composition. In general, the amount of high molecular weight starch, such as waxy corn starch, is about 5 to 26 wt. %, based on the total weight % of the composition, although higher or lower amounts may also be applicable in some compositions. The preferred amount of starch is about 10.0 to 15.0 wt. %.
The binder polymer or polymers are obtained from mono-ethylenically unsaturated monomers and known colloquially as “acrylics”. They are usually copolymers of at least two alkyl esters of one or more mono-ethylenically unsaturated carboxylic acids, such as for instance methyl methacrylate/butyl acrylate copolymer, but may also be homopolymers. Any water soluble acrylic polymer which has previously been used as a binder polymer can be employed, such as, for example, acrylic polymers and co-polymers, styrene acrylic emulsions, acrylic amide copolymers and co-polymers and/or acrylic colloidal dispersions. The amount of polymer will vary with factors such as, for example, the type and amount of starch, the type of polymer, the type and amount of colorant and other solids. In general, the preferred amount of polymer or co-polymer is about 7.0 to 25.0 wt. %. The more preferred amount is about 8.0 to 15.0 wt. %. It is noted that if lower amounts of polymer or co-polymer are used, the amount of starch, colorant and/or other solids should be increased proportionately to obtain adequate color density and printability.
The colorant suitable for use in the present invention may be a carbon black or any other inorganic pigment, an organic pigment, a dye or mixtures of pigments and/or dyes. The colorant may be in the form of a dry powder, dispersion, flush or any other conventional form. Suitable pigments include but are not limited to organic or inorganic pigments. Usable organic pigments include a pigment or a blended combination of the following non-limiting examples: Pigment Yellows #12, 13, 14, 17, 74, 83; Pigment Reds #2, 22, 23, 48:1, 48:2, 52, 53, 57:1, 122, 166, 170, 266; Pigment Orange #5, 16, 34, 36; Blue #15:3, 15:4; Violet #3, 27; and/or Pigment Green #7. Inorganic pigments may be one of the following non-limiting pigments: iron oxides, Pigment White #6, 7 and/or Pigment Black #7. Other organic and inorganic pigments appropriate for the colors desired can also be used. The amount of colorant used is generally about 2 to 20 wt. %, and more preferably about 5 to 13 wt. %.
Further additives which may be employed as desired to impart various properties to the printing ink and coating compositions of the present invention include surface tension modifiers, defoamers, wax or wax substance such as polyethylene wax, preservatives, biocides, dispersants, thickeners and cross-linking agents. Any of the known additives typically employed in aqueous inks and coatings can be used.
Any printable porous substrate can be printed with the composition described above by any known conventional technique. The ink is particularly useful in connection with corrugated paper or paperboard products, other cellulosic substrates, and paper products which may be subjected to recycling.
The combination of high molecular weight starches and acrylic polymers imparts desired physical and chemical properties to the printing ink and coating such as improvements in chemical resistance, re-solubility, repulpability, ink strength and pigment loading, pH stability, higher coefficient of friction and heat resistance. In addition, such compositions eliminate the need to employ an excess of amine for acrylic based compositions and thereby reduces any odor otherwise generated from such amines. As used herein, the “repulpability” of a printed material or substrate is determined by measuring/evaluating the reusability of an unwanted or discarded printed material or substrate (e.g. paper fibers) after the maximum amount of colorant (e.g. pigment) has been extracted from such printed material or substrate.
The ink and coating compositions of the present invention are further illustrated by the following non-limiting examples in which all parts and percentages are by weight, unless otherwise indicated.
Three corrugated printing ink compositions designated as A, B and C were prepared using the components and parts by weight shown below in Table I:
The three printing ink compositions prepared in Example I were tested for viscosity and pH stability, mileage and color strength. After the initial pH was noted, stability was determined by heating the ink to 115°-120° F. (ca. 46-48° C.) and agitated at 4000 rpm for 4.5 hours, and then allowed to cool to room temperature overnight. The dilution data is reflective of the amount of ink which will be consumed for a specific length of paper.
The results of each test are described below in Table II.
Three coating compositions designated as D, E and F were prepared using the following components shown below in Table III:
The following two coating compositions were prepared:
Composition G (Comparative):
Comparative composition G had a pH of 8.8 and a viscosity (Signature #3 cup) of 16 seconds whereas composition H had a pH of 8.1 and a viscosity of 24 seconds.
The compositions were coated on corrugated board and evaluated. The results are shown in Table IV below.
In the water drop test, one drop of water was applied to the surface of dried print, and thereafter a single wipe made with an absorbent substance and both the absorbent and print examined for any sign of bleeding. To determine hot rub resistance, two printed corrugated samples were placed face to face on a Sutherland Rub Tester and rubbed against each other at 450° F. (ca. 232° C.) and then visually examined for signs of marring. Slide angle represents the degree of elevation when two face to face printed boards began to slide and is a method of measuring the coefficient of static friction by resistance. To determine hot block resistance, a print about four inches long was folded so that the test material was face to face and then a heated element was pressed against the folded board, after which the ability to unfold after cooling evaluated. In the wet block test, two squares of printed board were sprayed evenly with water, placed face to face and after being allowed to sit overnight under a one pound weight, the squares are pulled apart and the damage assessed.
Four towel and tissue printing ink compositions designated as I, J, K and L were prepared according to the present invention using the varnish shown below in Table V:
Inks were then prepared by combining 85% varnish of Table V with 15% of the following colorants:
For comparison purposes, four towel and tissue printing ink compositions designated M, N, O and P were prepared by combining 87.5 parts of a polyamide resin-containing varnish with 12.5 parts of the same colorants.
The eight ink compositions prepared in Example V were tested for chemical rub resistance, and repulpability. To determine rub resistance, prints on paper were immersed in a commercial household cleaner sold under the trademark “Formula 409” for 1 minute, then blotted and examined for bleeding (none bleed) then the print was subjected to 3-4 cycles on a Sutherland Rub Tester and the resistance to ink run-off rated on a scale of 1 to 10 with 1 being the best.
The results of these test are described below in Table VII.
(1)Repulpability was determined by blending and mixing a printed tissue sample with sodium hypochlorite-containing water. Hot aqueous KOH (pH 12) is added and mixed with the blend. Sodium bisulfite or KOH was added as necessary to realize a pH between 6 and 7. The resulting
The preparation of Ink A is repeated substituting the same amount of Zeina B860 (National Starch) for the LPR41 starch.
The preparation of Ink A is repeated substituting one half of the PLR41 starch with Zeina B860 starch (National Starch).
Now that the preferred embodiments of the present invention have been described in detail, various modifications and improvements thereon will become readily apparent to one of ordinary skill in the art. Therefore, the spirit and scope of the invention are to be limited only by the appended claims and not by the foregoing specification.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US05/43971 | 12/2/2005 | WO | 7/12/2007 |
| Number | Date | Country | |
|---|---|---|---|
| 60633124 | Dec 2004 | US |