Printing sheets

BACKGROUND OF THE INVENTION
This invention relates to printing sheets, more particularly, those for use in offset printing.
Recently, there has been increasing demands for printing various thermoplastic resin films represented by polyester films according as diversified development of printing. It has also been desired to print on special sheet-form materials such as metal foils, metal-deposited paper, metal fiber sheets, ceramics sheets and the like. Generally, these sheet-form materials have been printed by offset printing, gravure printing, flexographic printing, screen printing, relief printing, or the like printing methods. Among the conventional printing methods, offset printing has attracted much attention since it is easy to make plates, it can be performed at low costs, it provides more beautiful printings as compared other printing methods, it can be performed economically when only a small number of sheets are to be printed, and for some other reasons. Development of printing sheets suitable for offset printing has been made accordingly.
The properties that are required for the printing sheets for use in offset printing include sheet running property, anti-blocking property, anti-setoff property, ink-drying property, ink adhesion property, anti-static property, etc. These properties are not satisfied by sheets themselves; the printing sheets are usually subjected to surface treatment before they can be useful as printing sheets suitable for offset printing. For example, polyester films are coated with a coating material containing an inorganic pigment in order to improve ink-drying property, they are subjected to corona discharge treatment in order to improve ink-adhesion property, or the films themselves are molded from resins which comprise copolymers of the ester monomer with other polar monomers or those which are blends of the polyester with other resins composed of polar monomers. For preventing static charges, countermeasure is taken, for example, by kneading an anti-static agent in the resin before molding into sheets or coating the anti-static agent on the surface of the resin sheets.
However, notwithstanding the above-described treatments, the requirements for printing sheets for use in offset printing are not always satisfied completely from the practical viewpoint. Furthermore, it has heretofore been performed to bond an undertaper to the rear side of the printing sheet to obtain printing sheets for use in offset printing in order to overcome disadvantages of the conventional printing sheets such as poor sheet running property, poor anti-blocking property, poor anti-offset of ink, and the like. In this case, however, other problems arise from the viewpoints of operability and economics in that additional steps are necessitated such as a step of bonding in which the undertaper is bonded to the printing sheets, and a step of stripping in which the undertaper is stripped off from the printing sheets after the printing is over, and also that additional cost for the undertaper is incurred.
In addition, as the result of recent development of ultraviolet-curing ink (hereafter, sometimes referred to as "UV ink", for brevity) which dries in a very short time and particularly advantageous in the operability, printing methods using UV ink has prevailed widely. However, when the above-described sheet-form materials are printed with UV ink, no satisfactory adhesion is obtained between the UV ink after curing and the surface of the sheet material, resulting in peeling off of the printed layer. Therefore, it has been desired to develop printing sheets having improved adhesion between the surface thereof and the ink to be applied.
SUMMARY OF THE INVENTION
Therefore, an object of this invention is to provide printing sheets which have all the requirements necessary for printing sheets and also have excellent printing properties, and which can avoid bonding of an undertaper thereto.
Another object of this invention is to provide printing sheets which have excellent adhesion to UV ink.
As the result of extensive research on the requirements to be satisfied by printing sheets, this invention has now been completed, which provides a printing sheet comprising:
(a) a support, and
(b) a surface layer provided on at least one side surface of said support, said surface layer containing at least one compound selected from the group consisting of n-butyl (meth)acrylate based polymers, phenyl (meth)acrylate based homopolymers and copolymers, benzyl (meth)acrylate based homopolymers and copolymers, styrene based homopolymers and copolymers, cinnamic acid, and cinnamic acid derivatives.
In another aspect, this invention provides a printing sheet comprising
(a) a support, and
(b) a surface layer provided on at least one side surface of said support, said surface layer comprising
(i) at least one resin selected from the group consisting of phenyl (meth)acrylate based homopolymers and copolymers, benzyl (meth)acrylate based homopolymers and copolymers, and styrene based homopolymers and copolymers, and
(ii) at least one compound selected from the group consisting of cinnamic acid and cinnamic acid derivatives.
The printing sheets of this invention having a specified surface layer exhibit excellent printability such as reproducibility of letters or images, ink drying property, sheet running property and anti-ink offset and can be used advantageously in various printing methods. Moreover, the printing sheets of this invention are excellent in the ink drying property particularly for oxidation polymerized type ink and therefore they can avoid attachment of undertapers which would otherwise be required for conventional printing sheets for offset printing. Furthermore, the printing sheets of this invention has excellent adhesion to UV curing type ink and makes it possible to apply Uv curing ink to sheet-form materials other than paper such as plastic films when offset printing is used.
DETAILED DESCRIPTION OF THE INVENTION
The term "(meth)acrylate" as used herein refers to methacrylate or acrylate.
The n-butyl (meth)acrylate based polymers which can be used in the surface layer of the printing sheet of this invention include n-butyl (meth)acrylate based resins or oligomers of n-butyl (meth)acrylate. As the n-butyl (meth)acrylate based resin, there can be used copolymers of n-butyl (meth)acrylate with other monomers including vinyl monomers such as acrylate based monomers, methacrylate based monomers, and styrene based monomers as well as homopolymers of n-butyl (meth)acrylate. In the case of the copolymers, the content of n-butyl (meth)acrylate to be copolymerized is not smaller than 30% by weight based on the total weight of the monomers used. The n-butyl (meth)acrylate based oligomers may be homopolymeric oligomers of n-butyl (meth)acrylate or copolymeric oligomers of n-butyl (meth)acrylate with other vinyl monomer. Examples of the vinyl monomers copolymerizable with n-butyl (meth)acrylate which can be used in the preparation of the copolymeric oligomers include methyl (meth)acrylate, (meth)acrylates other than n-butyl methacrylate, acrylates, styrene and butadiene. The proportion of n-butyl (meth)acrylate to the copolymerizable monomer is preferably at least 1:1 by weight. The term "oligomers" as used herein refers to those having average molecular weight of not greater than 5,000, and those having average molecular weight of from 1,000 to 5,000 can be used advantageously.
In this invention, it is preferred that the n-butyl (meth)acrylate based polymers are contained in the surface layer in amounts of from 30 to 100% by weight based on the total weight of the materials constituting the surface layer. When the oligomers are used as the n-butyl (meth)acrylate copolymer, it is preferred that they are contained in the surface layer in amounts of from 30 to 75% by weight, and preferably from 50 to 75% by weight based on the total weight of the surface layer. When the content of the oligomer is greater than 75% by weight, blocking tends to occur upon loading the sheets. On the other hand, the ink drying property is poor with the oligomer in amounts smaller than 30% by weight.
Examples of the cinnamic acid derivatives contained in the surface layer of the printing sheets of this invention include various cinnamic acid derivatives such as cinnamates, for example, ethyl cinnamate and amides of cinnamic acid, for example, amide cinnamate. The homopolymers and copolymers of phenyl (meth)acrylate based monomers, benzyl (meth)acrylate based monomers, and styrene based monomers include respective homopolymers of phenyl (meth)acrylate, benzyl (meth)acrylate and styrene, and copolymers comprising at least one of the monomer components, e.g., copolymers composed of two or three of different kinds of monomers from the above-described monomers, copolymers of the monomer with other monomer copolymerizable therewith such as other methacrylate, acrylate, butadiene, etc. One or more of the polymers can be used in admixture. The term "styrene" as used herein includes various derivatives of styrene such as .alpha.-methylstyrene, vinyltoluene, etc. These compounds are each suitable for printing using particularly UV ink. These compounds have to be contained in the surface layer in amounts of not smaller than 0.5% by weight, and particularly not smaller than 5% by weight when they are contained in the form of polymers.
The thickness of the surface layer on the printing sheets of this invention is preferably from about 1 to 10 .mu.m. For forming the surface layer on the support in this invention, the respective compounds described above, if desired, together with a resin for coating, are dissolved or dispersed in a solvent or water to prepare a coating liquid, which is then coated by conventional methods such as a roll coating method, a blade coating method, a spray coating method, an air-knife coating method, a rod bar coating method and the like, followed by drying. Alternatively, a uniform mixture of the raw materials for forming the surface layer described above is applied to the support by a hot melt coating method and a laminating method, etc. As the resin for coating, there can be used resins commonly used in the coatings or laminates. Suitable examples of such resin include polyester resins, acrylate resins, methacrylate resins, vinyl chloride resins, vinyl acetate resins, and various homopolymer or copolymer resins.
If desired, various additives can be added to the surface layer in order to improve anti-blocking property, sheet running property, anti-static property, etc. Examples of the additives which can be used include pigments such as silica, clay, talc, diatomaceous earth, calcium carbonate, calcium sulfate, barium sulfate, aluminum silicate, synthetic zeolite, alumina, zinc oxide, lithopon and satin white, cationic, anionic and nonionic anti-static agents, and the like.
The surface layer of the printing sheets of this invention generally has above-described construction, and the surface layer containing as a major component a resin selected from the group consisting of the homopolymers and copolymers of the phenyl (meth)acrylate based monomers, benzyl (meth)acrylate based monomers, and styrene based monomers, and in addition, cinnamic acid and/or its derivatives, has particularly improved adhesion to UV ink and therefore is advantageous.
Examples of the support which can be used in this invention include paper, synthetic paper, woven fabric, nonwoven fabric, thermoplastic resin sheets (films), ceramic sheets, metal fiber sheets, metal deposited sheets (films), metal foils, metal plates, etc. and multi-layered composite sheets constructed by a combination of these materials. The shape of the support is not limited particularly but it may be in any shape or form such as film, sheet, plate and the like if it is suited for its application to printing machines.
The printing sheets of this invention, which is provided with the above-described surface layer on at least one side surface of the support, have not only good sheet running property and anti-blocking property but also excellent ink-drying property. Further improvement in the ink-drying property can be obtained by adding special metal or metal compound to the surface layer.
The special metal or metal compound which can be used in this invention include simple metals such as aluminum, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, tin and lead, and various compounds of these metals. Of these, cobalt, manganese and lead are preferred. Specific examples thereof include fine powders of the respective metal elements described above, oxides such as manganese dioxide, iron (II) oxide, iron (III) oxide and lead (II) oxide, sulfides such as iron (II) sulfide and lead (II) sulfide, hydroxides such as iron (III) hydroxide and aluminum (III) hydroxide, halides such as iron (II) chloride, cobalt (II) chloride and lead (II) chloride, or various metal salts such as sulfates, nitrates and carbonates of the above-specified metals. In addition, chromates, dichromates, permanganates and the like can also be used in this invention. The metals or metal compounds can be contained in the surface layer in amounts of not smaller than 0.01% by weight, preferably from 0.05 to 10% by weight to obtain desired effects. Two or more of the metals and metal compounds may be used in admixture, if desired.
In the printing sheets of this invention, the anti-static agent may be added to the surface layer as described above to obtain anti-static property. Instead, an anti-static layer can be provided between the support and the surface layer to further improve the anti-static property of the printing sheets. The anti-static layer may be constructed by any material as far as the layer serves as a low resistance layer having a surface resistivity of not higher than 10.sup.12 ohm/cm.sup.2. For example, anti-static agents such as phosphate esters, quaternary ammonium salts, metal materials such as Al, Cu, Fe, etc., conductive materials containing carbon black, and the like can be used.
To form the anti-static layer, various methods can be used, for example, a coating material containing an anti-static agent can be coated on the support. When metals and other conductive materials are used, sheets or foils of a conductive material are laminated on the support. Alternatively, it is also possible to deposit a metal material such as aluminum on the support. The thickness of the anti-static layer may vary depending on the kind of the material used but usually it is preferred to set up in the range of from 1 to 10 .mu.m.
Moreover, an adhesive layer may be provided on the rear side surface (i.e., on the surface on which the surface layer is not provided) of the support using a commonly used adhesive. Furthermore, a releasing film or sheet having a releasing property can be laminated on the adhesive layer, if desired. Thus, the printing sheets of this invention can be used as an adhesive sheet or label which can be tacked at will. This construction ensures wider application of the printing sheets of this invention.
The printing sheets of this invention are particularly suited for offset printing but they also show good printability when used in other printing methods such as gravure printing, flexographic printing, screen printing, relief printing, etc.

EXAMPLES
This invention will be described in greater detail with reference to the following examples and comparative examples which are not construed as limiting this invention in any way.
In the examples and comparative examples, all parts are by weight unless otherwise indicated specifically.
EXAMPLE 1
Polyethylene terephthalate film of 100 .mu.m in thickness was used as a support, and a surface layer of 3 .mu.m in thickness was formed on the support by coating a coating liquid for surface layer having the composition set forth below to form a printing sheet of this invention.
______________________________________n-Butyl methacrylate resin 20 parts(M.W.: about 180,000)Toluene 80 parts______________________________________
EXAMPLE 2
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________Acrylic resin (Thermolack M-2000, 10 partsproduced by Soken Kagaku Co., Ltd.)n-Butyl methacrylate oligomer 10 parts(M.W.: about 1,000)Toluene 10 parts______________________________________
EXAMPLE 3
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________Acrylic resin (Thermolack M-2000, 10 partsproduced by Soken Kagaku Co., Ltd.)n-Butyl methacrylate/methyl methacrylate 20 partscooligomer (1:1) (M.W.: about 1,000)Toluene 10 parts______________________________________
EXAMPLE 4
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________n-Butyl methacrylate resin 16 parts(M.W.: about 90,000)Methyl methacrylate resin 4 partsSilica (FINESIL X-37, Tokuyama Soda 0.1 partCo., Ltd.)Sodium dodecyl phosphate 0.7 partToluene 80 parts______________________________________
EXAMPLE 5
A printing sheet was prepared in the same manner as in Example 1 except that a polyethylene terephthalate film of 100 .mu.m in thickness on which aluminum had been deposited was used as a support.
EXAMPLE 6
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________n-Butyl methacrylate resin 50 parts(M.W.: 90,000, solid content: 40%)Fine powder of cobalt 0.02 partSolvent (toluene) 50 parts______________________________________
EXAMPLE 7
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________n-Butyl methacrylate resin 50 parts(M.W.: 180,000, Solid content: 40%)Cobalt (II) chloride 0.02 partSolvent (toluene) 50 parts______________________________________
EXAMPLE 8
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following. T1 -n-Butyl methacrylate oligomer 50 parts -(M.W.: about 1,000) -Acrylic resin (Thermolack M-2000, 50 parts -produced by Soken Kagaku Co., Ltd.) -Manganese sulfate 0.01 part -Solvent (toluene) 50 parts -
EXAMPLE 9
A printing sheet was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________n-Butyl methacrylate resin 50 parts(M.W.: 90,000, solid content: 40%)Manganese dioxide 0.01 partSolvent (toluene) 50 parts______________________________________
EXAMPLE 10 to 16
Printing sheets were prepared in the same manner as in Example 6 except that the metals or metal compounds shown in Table 1 were used in place of the fine powder of cobalt in the coating liquid for surface layer.
TABLE 1______________________________________Example Metal or Metal Compound______________________________________10 Manganese Borate11 Vanadium Powder12 Chrome Green13 Cobalt Sulfate14 Tin Powder15 Chrome Yellow16 Lead Borate______________________________________
EXAMPLE 17
Polyethylene terephthalate film of 100 .mu.m in thickness was used as a support, and an anti-static layer of 1 .mu.m in thickness was formed on the support by coating an anti-static coating liquid having the composition set forth below.
______________________________________Acrylic resin based anti-static agent 10 parts(COLCOAT NR3121, Colcoat Co., Ltd.)Methanol 30 parts______________________________________
Then, the same coating liquid for surface layer as used in Example 1 was coated on the thus-formed anti-static layer to form a surface layer.
EXAMPLE 18
A printing sheet of this invention was prepared in the same manner as in Example 17 except that the coating liquid for anti-static layer was prepared by using a polysilioxane based anti-static agent (ANTISTAT CS3900, Toshiba Chemical Co., Ltd.).
COMPARATIVE EXAMPLE 1
A printing sheet for comparison was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________Polyester resin (Vylon #200, 50 partsToyobo Co., Ltd., solid content: 40%)Solvent (toluene) 50 parts______________________________________
COMPARATIVE EXAMPLE 2
A printing sheet for comparison was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________Methyl methacrylate resin (M-2000, 50 partsSoken Kagaku Co., Ltd., solid content: 40%)Solvent (toluene) 50 parts______________________________________
COMPARATIVE EXAMPLE 3
A printing sheet for comparison was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________i-Butyl methacrylate resin 20 partsSolvent (toluene) 80 parts______________________________________
COMPARATIVE EXAMPLE 4
A printing sheet for comparison was prepared in the same manner as in Example 1 except that the coating liquid for surface layer was replaced by the following.
______________________________________Ethyl methacrylate resin 20 partsSolvent (toluene) 80 parts______________________________________
COMPARATIVE EXAMPLE 5
A polyethylene terephthalate film of 100 .mu.m in thickness was used as it is as a support without providing a surface layer to prepare a printing sheet for comparison.
PRINTABILITY TEST
The printing sheets of Examples 1 to 18 and Comparative Examples 1 to 5 were subjected to printability tests performed using IGT printability tester manufactured by Kumagai Riki Co., Ltd. and TSP 300 Black produced by Toyo Ink Mfg. Co., Ltd. as ink. The results obtained are shown in Table 2.
TABLE 2______________________________________ Sheet Repro- Ink Drying Ink RunningSample ducibility Property Setoff Property______________________________________1 Good Good Fair Good2 Good Good Fair Good3 Good Good Fair Good4 Good Good Fair Good5 Good Good Fair Good6 Good Excellent Good Good7 Good Excellent Good Good8 Good Excellent Good Good9 Good Excellent Good Good10 Good Excellent Good Good11 Good Excellent Good Good12 Good Excellent Good Good13 Good Excellent Good Good14 Good Excellent Good Good15 Good Excellent Good Good16 Good Excellent Good Good17 Good Good Fair Excellent18 Good Good Fair ExcellentC.E. 1 Good Poor Poor Fair2 Good Poor Poor Poor3 Good Poor Poor Poor4 Good Fair Fair Poor5 Good Poor Poor Fair______________________________________
Notes:
(1) Reproducibility: Judged by visual observation.
"Good" indicates a state in which scratching or thinning of ink seldom occurs and the reproducibility of letters or images is acceptable and "poor" indicates a state in which the reproducibility is unacceptable.
(2) Ink drying property: 1 hour after printing printed sheet was rubbed with finger, and judged by visual observation.
"Excellent" indicates a state in which no stain was observed on the finger. "Good" means a state in which the finger was stained very slightly. "Fair" shows a state in which ink adhered to the finger notably. "Poor" indicates a state in which ink adhered to the finger considerably and the surface of the printed matter was stained.
(3) Ink Setoff: Immediately after printing, an unused printing sheet was superimposed on the printed sheet and after the ink dried, transfer of ink to the rear surface of the superimposed printing sheet was judged by visual observation.
"Good" indicates a state in which there was no problem. "Fair" indicates a state in which slight ink setoff was observed. "Poor" stands for a state in which ink setoff was observed clearly, which was practically unacceptable.
(4) Sheet running property: Continuous printing with a printing machine was conducted.
"Excellent" means a state in which no obstruction (such as double sheet feeding, jamming, unalignment of printing sheets at the mounting portion, etc.) was observed. "Good" indicates a state in which obstruction was observed only a little. "Fair" indicates a state in which obstruction involving the stoppage of the printing machine was observed. "Poor" means a state in which obstruction occurred frequently and practically unacceptable.
Table 2 clearly shows that the printing sheets of this invention are superior in printability to those of comparison.
EXAMPLE 19
On a polyethylene terephthalate film (PET 100G, Fuji Photo Film Co., Ltd.) of 100 .mu.m in thickness was coated with a coating liquid for surface layer having the composition set forth below to a thickness of 3 .mu.m to form a surface layer, followed by drying to obtain a printing sheet of this invention.
______________________________________Methyl methacrylate/styrene (1:1) copolymer 10 parts(M.W.: about 30,000, solid content: 40%)Toluene 10 parts______________________________________
EXAMPLE 20
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Methyl methacrylate/phenyl methacrylate 10 parts(1:1) copolymer (M.W.: about 30,000,solid content: 40%)Toluene 10 parts______________________________________
EXAMPLE 21
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Methyl methacrylate/benzyl methacrylate 10 parts(1:1) copolymer (M.W.: about 30,000,solid content: 40%)Toluene 10 parts______________________________________
EXAMPLE 22
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Methyl methacrylate resin (M-2000, 10 partsSoken Kagaku Co., Ltd., solid content: 10%)Cinnamic acid 0.05 partToluene 10 parts______________________________________
EXAMPLE 23
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Polyester based resin (Vylon #200, 10 partsToyobo Co., Ltd., solid content: 40%)Cinnamic acid 0.05 partToluene 40 parts______________________________________
EXAMPLE 24
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Polyphenyl methacrylate 10 parts(M.W.: about 15,000, solid content: 40%)Toluene 10 parts______________________________________
EXAMPLE 25
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Polybenzyl methacrylate 10 parts(M.W.: about 15,000, solid content: 40%)Toluene 10 parts______________________________________
EXAMPLE 26
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Polyphenyl methacrylate 10 parts(M.W.: about 15,000, solid content: 40%)Cinnamic acid 0.05 partToluene/MEK = 1/1 10 parts______________________________________
EXAMPLE 27
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Polybenzyl methacrylate 10 parts(M.W.: about 15,000, solid content: 40%)Cinnamic acid 0.05 partToluene/MEK = 1/1 10 parts______________________________________
EXAMPLE 28
A printing sheet was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Methyl methacrylate/styrene (1:1) copolymer 10 parts(M.W.: about 30,000, solid content: 40%)Cinnamic acid 0.05 partSilica (FINESIL X37, Tokuyama Soda Co., Ltd.) 0.01 partToluene 10 parts______________________________________
COMPARATIVE EXAMPLE 6
The same polyethylene terephthalate film as used in Example 19 as a support was used as it is as a printing sheet for comparison.
COMPARATIVE EXAMPLE 7
A printing sheet for comparison was prepared in the same manner as in Example 19 except that the coating liquid for surface layer was replaced by the following.
______________________________________Methyl methacrylate resin (M-2000, 10 partsSoken Kagaku Co., Ltd., solid content: 40%)Toluene 10 parts______________________________________
PRINTABILITY TEST
The printing sheets obtained in Examples 19 to 28 and Comparative Examples 6 and 7 were printed using IGT printability tester manufactured by Kumagai Riki Co., Ltd. and UV curing ink (FLASH DRY Kon-ai XG, produced by Toyo Ink Mfg. Co., Ltd) as ink. Then, the ink was cured by irradiating UV light using three 5.6 kw UV lamps at a distance of 14 cm for 3 seconds. The reproducibility and adhesion properties were evaluated. The results obtained are shown in Table 3.
TABLE 3______________________________________ Repro- Ink AdhesionExample ducibility Nail Tape______________________________________19 Good Good Fair20 Good Good Fair21 Good Good Fair22 Good Good Fair23 Good Good Fair24 Good Good Fair25 Good Good Fair26 Good Good Good27 Good Good Good28 Good Good GoodC.Ex. 6 Good Poor PoorC.Ex. 7 Good Fair Poor______________________________________
Notes:
(i) Reproducibility: Judged by visual observation. "Good" indicates a state in which scratching or thinning of ink seldom occurs and the reproducibility of letters or images is acceptable and "poor" indicates a state in which the reproducibility is unacceptable.
(ii) Ink Adhesion (Nail): The printed portions were scratched with nail.
"Good" indicates a state in which substantially no ink was removed. "Fair" indicates a state in which a little ink was removed. "Poor" stands for a state in which ink was removed readily.
(iii) Ink Adhesion (Tape): An adhesive regenerated cellulose (Cellophane.RTM.) tape was affixed to the printed portion of the printing sheet and peeled off quickly. "Good" indicates a state in which substantially no ink was removed. "Fair" indicates a state in which a small amount of ink was removed. "Poor" means a state in which a considerable amount of ink was removed.
Table 3 clearly shows that the printing sheets of this invention are superior in the ink adhesion property to those of comparison.
OPERATIONAL SUITABILITY TEST
The printing sheets obtained in Example 19 to 28 were subjected to operational suitability tests using an offset printing machine (HEIDERBERG MO). After continuous printing of 10,000 sheets, practically no problem was observed in the sheet running property, reproducibility, ink adhesion and the like.
As described above, the printing sheets of this invention are excellent also in UV ink adhesion and exhibit good printability.
While the emobodiments of the present invention, as herein disclosed, constitute a preferred form, it is to be understood that other forms might be adopted.

Number	Name	Date
4092457	Fujita et al.	May 1978
4603079	Nishizaki et al.	Jul 1986
4701367	Malhotra	Oct 1987
4707463	Ikeda	Nov 1987

Number	Date	Country
00233703	Jan 1987	EPX
3627973 A1	Feb 1988	DEX
0055193	Mar 1987	JPX
1166066	Oct 1969	GBX
2166689 A	May 1986	GBX

Printing sheets

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

US Referenced Citations (4)

Foreign Referenced Citations (5)