Procedure for manufacturing lignocellulosic material products

The present invention concerns a procedure for manufacturing lignocellulosic material products and for improving their strength and water resistance properties using high-molar mass lignin derivatives. Such products are e.g. those of the paper and cardboard industry and those of the industry manufacturing building materials, such as corrugated board, cardboard, kraft-liner, paper cores, wood composites, fibreboard and chipboard, and insulation materials. It is possible to improve by the procedure not only the characteristics of products made of primary fibres but also to enable high-grade products to be made of lower grade raw materials such as reclaimed fibres.
BACKGROUND OF THE INVENTION
In cellulose manufacturing processes in which wood chips are heated in a cooking solution under pressure, about half of the wood is dissolved, forming the so-called waste liquor. One of the main organic components of waste liquor is lignin. In the sulphite process, in which an acid bisulphite/sulphur dioxide solution serves as digesting liquor, lignin is present in the waste liquor in sulphonated form, as so-called lignosulphonates. In this form, lignin is soluble in water also in acid solutions. On the other hand, in alkaline cellulose manufacturing processes, such as the soda process (NaOH as digesting solution), in the kraft process (NaOH, Na.sub.2 S, NaHS as digesting solution) or in the oxygen/alkali process (with NaOH in the presence of oxygen), lignin is present in the form of an Na salt in the waste liquor, and it is water-soluble in alkaline solutions.
It is known in the art that the characteristics of e.g. paper, cardboard and fibre boards can be improved by adding lignin to the fibres, most often in the form of waste liquor. The problem has, however, been the poor retention of said lignin products, that is, poor adhesion to the fibres. For instance, it has been possible to improve the strength properties of corrugated board by adding to the fibre stock 6% by weight, calculated on the dry matter of the stock, thermally processed lignin isolated from sulphite waste liquor (Zellstoff und Papier 24 (1975): 9, 269-70). It is observed, however, in the reference that using lignin cannot be contemplated because the BOD values of the waste liquor become too high owing to its poor retention.
In the Canadian Patent CA 729,140 lignin is used in the form of sulphite waste liquor or black liquor for improving the strength characteristics of paper. Of the dry matter of the black liquor only 26% by weight could be made to adhere to the fibres. All the same, the procedure was considered to be economically advantageous because the concora values of the paper increased from 66.3 points to 87.6 points. A retention of equal degree, about 30% by weight, has also been reached in a Russian study (Bumazh Prom. 11 (1984): 18-19), in which kraft lignin was precipitated with alum onto the paper fibres. The lignin quantity used was over 8% by weight of lignin dry matter, calculated on the dry matter of the fibres. In spite of poor retention, the breaking, punching and rigidity characteristics of the paper could be improved.
The effect of kraft lignin on the strength of fibre board made from waste paper has been compared in an American study (Forest Products J. 28 (1978): 77-82) with the effect of phenol formaldehyde resin. Of the dry matter of the kraft lignin product used, 54.8% by weight was organic matter and 44% by weight was inorganic matter. When pH was adjusted with sulphuric acid to 4.5, only 15 g dry matter out of 100 g were precipitated. Precipitation could be somewhat improved by raising the precipitation temperature to 70.degree. C.; although lignin had to be added 11% by weight, calculated as dry matter related to the dry matter of the fibres, in order to achieve equally good strength characteristics as with 3% by weight phenol formaldehyde addition. Cost calculation analysis revealed that phenolic resin was somewhat more favourable in use than lignin owing to higher lignin addition and oxygen consumption, and to the heating required in precipitating it.
Corrugated board manufactured from reclaimed fibre stock has been impregnated, in Italy, in a sizing press with both NSSC waste liquor and black liquor (Eucepa Conference, Florence, Oct. 6-10, 1986, Proc. Vol. II, 24; 1-31). Subsequent to impregnation, the board was dried at 100.degree.-140.degree. C. The waste liquors originated from poplar and straw cookings. In most of the experiments, the characteristics of the board improved owing to the impregnation. Better results were obtained using the waste liquor at dry matter constant 20-30% by weight than when it was used in dilute solutions, which necessitated performing the impregnation in a plurality of steps. On the other hand, lowering the pH of the waste liquors reduced the strength properties of the board. The board impregnated with waste liquor obtained from straw cooking absorbed more moisture than untreated corrugated board.
Lignin has been chemically modified, particularly for improving its water resistance properties. It has for instance been reacted with amines (Wochenblat fur Papierfabrikation 94 (1966): 4, 107-110), whereafter it has been reacted with formaldehyde (U.S. Pat. No. 3,079,353) or peroxide (SU 520,260). Alakli lignin has, for instance, been sulphonated and used together with starch in order to increase the rigidity of a liner manufactured from waste paper (U.S. Pat. No. 3,644,167). From rice soda black liquor, cyanoethyllignin and aminolignin have been manufactured, and they have been used e.g. in paper sizing (Paperi ja Puu 62 (1980): 10, 589-592, 614). Lignin has also been heat-treated: e.g. lignosulphonates at about 250.degree. to 300.degree. C., with the purpose of converting them into a form insoluble in water (U.S. Pat. No. 2,934,531 and Zellstoff und Papier 18 (1969): 11, 328-332). Using this kind of products it has been possible to improve the characteristics of corrugated board and kraft.
Kraft lignin, having average molar mass 25,000-30,000, has been used in manufacturing cardboard, corrugated board and wrapping paper (SU 681,140). As disclosed in said reference, the lignin is added to an aqueous solution containing 2-40% by weight fatty acids and resin acids, and the mixture is heated in an alkali at 80.degree. to 85.degree. C. before use. The dry matter content of the mixture is about 14-18% by weight and the pH is 8-9. The fatty acids and resin acids have probably been added in order to improve the hydrophobic properties. When this mixture was added to a cardboard fibre stock in amount 3% by weight, calculated as dry matter related to the dry matter of the stock, the bursting strength of the cardboard was improved 5% and the tensile strength, 18%.
High-molar mass alkaline kraft lignin has been added 1 to 7% by weight, calculated as dry matter related to the stock dry matter, to a fibre stock used in manufacturing paper and cardboard (SU 374,407). The lignin is added as an alkaline aqueous solution to the stock, and thereafter, 3% by weight of divinylstyrene/rubber latex in emulsion form, containing 75% by weight styrene related to the latex dry matter, is added thereto. Thereafter, the components are precipitated with aluminum sulphate. The rigidity of paper and cardboard could hereby be improved, in comparison with products reinforced with latex alone. The additions are comparatively low, only about 1-7% by weight lignin.
Improved absorptive paper suitable for lamination can be manufactured by adding to the paper in the sizing press, after web formation, high-molar mass lignin, of which at least 50% by weight is over 5000 in molar mass (FI 58,961). The lignin product may consist of lignosulphonates or kraft lignin, and the additions are 0.1 to 10% by weight of the dry paper weight. According to the reference, lignin accelerates the absorption of phenolic resin in the paper but does not affect the tensile strength of the paper.
In the Finnish Patent FI 58788, lignin derivatives are used, of which at least 35% by weight, advantageously 40% by weight, are over 5000 in molar mass. By mixing them with phenol formaldehyde resin and adjusting pH of the bonding agent to be in the range 8-14, preferably 9-13, a waster resistant bonding agent can be manufactured for chipboard, plywood and fibre boards.
As will be evident from the foregoing, the greatest problems in using lignin as a reinforcing agent for various materials has been caused by the poor retention of lignin products, that is, their poor adhesion to fibres.
In the Patent SU 681,140, a lignin product having a given average molar mass (25,000-30,000) has been used. Since lignin is not homogeneous in structure but consists of lignin derivatives differing greatly in molar mass, the value stated for the average molar mass in fact fails to specify the kind of the lignin product used. It may consist of very high-molar mass and very low-molar mass lignin derivatives in varying proportions so that the mean of their molar masses will be 25,000-30,000. It is probably because of the poor adhesion to fibres of low-molar mass lignin derivatives that fatty and resin acids had to be used in addition in this instance in order to improve the hydrophobic properties.
Endeavours have also been made to improve the retention of lignin and the strength and water resistance properties of fibre material chemically by modifying lignin, but the economy of the procedure has suffered in that case.
SUMMARY OF THE INVENTION
With the aid of the procedure of the invention, a decisive improvement is achieved regarding the drawbacks mentioned in the foregoing.
The most significant advantage of the invention is that by applying it, products can be manufactured of various lignocellulosic materials in a sensible way, more advantageously in technical and economical respect than by any other method. Using the procedure now invented, strong bonds, probably hydrogen bonds, are obtained between the lignin derivatives and the lignocellulosic material, owing to which the products possess excellent strength and water resistance properties. Since the retention of lignin in lignocellulosic material is nearly complete applying the method now invented, lignin can be made adherent to the lignocellulosic material up to 100% by weight, calculated as dry matter related to the dry matter of the lignocellulosic material, at the same time improving the properties of the products. Owing to lignin addition, the production of some products can be increased up to 50%. The procedure enables recycled raw materials advantageous in price to be used e.g. instead of virgin fibres. Applying the procedure of the invention, the strength and water resistance properties of products produced from second grade fibres can be improved to be on a level with products based on virgin fibres.
The procedure is also advantageous from the viewpoint of the cellulose mill because the lignin going to fuel can now be utilize. There will be free recovery boiler capacity, and the production of cellulose may therefore be increased without having to invest in a new recovery boiler. The removal from the waste liquor of the high-molar mass lignin enables the waste liquor to be evaporated to higher dry matter content prior to the recovery boiler, without any difficulties with viscosity. Hereby the energy required in the soda boiler for evaporating water will be less because the quantity of feed water is significantly less.
The procedure is furthermore economically advantageous e.g. from the viewpoint of the plant manufacturing lignocellulosic products because to the lignocellulose suspension, mostly used at high dilution, lignin solution, lignin suspension or lignin powder with partly considerably higher dry matter content is added. Hereby, the amount of water to be evaporated per ton of product will be less. In addition, lignin is advantageous in price, e.g. compared with many wet-strengths resins, such as urea-formaldehyde resin or polyethylene-imine.
To the lignosellulosic material products manufactured with the procedure of the invention any additives and components, known per se e.g. plastic raw materials may be added for instance for improving the strength and water resistance or other properties of the products. Thus e.g. resin or resin raw materials, such as phenol formaldehyde resin may be added to the lignocellulosic material in any concentration, for instance less than 10% by weight or less than 5% by weight calculated as dry matter on the mixture of the lignin derivatives and resin, e.g. before or after the addition of the lignin derivatives to the lignocellulosic material.
It is to be noted that it is not mandatory in the procedure of the invention to co-polymerize the lignin derivatives in question with resins. So the lignocellulosic material products may be free of resin.
As regards environmental protection, it is a remarkable advantage of the present invention that when it is applied to the lignin is merely 100% attached to the fibres. Furthermore, the BOD values of the plant's effluents will not increase, as is the case when impure lignin products containing organic acids and other low-molar mass compounds in abundance are used. When using lignin derivatives according to the invention, no toxic low-molar mass sulphur compounds, such as hydrogen sulphide for instance, are released during the manufacturing process, as are for instance set free from sulphate waste liquor in acid conditions.

DESCRIPTION OF THE DRAWING
FIGS. 1 is a graph showing the variation in compressive strength with the molar mass of the lignin derivatives;
FIG. 2 is a graph showing the SCT compression strength, the CCT compression strength and tensile strength as a function of the added lignin; and
FIG. 3 is a graph showing the SCT compression strength as a function of added lignin in sheets produced from reclaimed fibers and sheets produced from Kraft stock.

DESCRIPTION OF THE PREFERRED EMBODIMENT
The invention is described in the following in detail. The high-molar mass lignin derivatives used in the procedure of the invention are isolated e.g. from waste liquor of an alkaline cellulose process or from waste liquor after bleaching by a lignin fractionating method known in itself in the art, such as precipitatior with acid, or by an ultrafiltration process. At least 35% by weight of the high-molar mass lignin derivatives should have molar mass higher than 5000. The molar mass distributions of lignin derivatives can be determined using gel chromatography, as is disclosed in detail in the Finnish Patent No. 58788.
The so-called degree of purity of the lignin has a great significance because when impure lignin products are precipitated onto lignocellulosic materials, the impurities will not adhere to fibres and are discharged into the plant's effluent circulation. Of the lignin derivatives used in the procedure of the invention, over 70% by weight of the total dry matter of the lignin fraction should precipitate from a 1-5% by weight solution with 1M hydrochloric acid at pH 3. The degree of purity of the lignin fraction can be found out with the aid of hydrochloric acid precipitation, since low-molar mass phenolic compounds, and other inorganic and organic impurities, will not be precipitated in such a determination.
The lignin derivatives of the invention may be used in the form of a dilute solution, of an evaporated concentrated solution, of a suspension, or of a powder, e.g. spray-dried. Their dry matter content at the moment of use may therefore vary, depending on the manufacturing process of the product, in the range 0.1 to 100% by weight.
The acid quantity required to lower pH below 7 may be added to the lignin, to the lignocellulosic material or to the lignocellulose/lignin mixture, depending on which is most advantageous in view of the manufacturing process.
It is possible to add to the lignocellulosic material, in addition to lignin, bivalent or trivalent metal salts, such alum, ferric or ferrous sulphate, or ferric chloride. Also organic, commonly known cationic precipitation chemicals, such as polyethylene imine, may be used. The amount of precipitation chemical added depends on the pH of the lignin derivatives and of the lignocellulosic material, and it is usually 0.5-20% by weight, calculated as dry matter related to the dry matter of the lignin/lignocellulose mixture, advantageously about 1-3% by weight.
The amount of high-molar mass lignin derivatives added to the lignocellulosic material varies in general in the range between 1 to 100% by weight, calculated as dry matter related to the lignocellulosic material dry matter, depending on the requirements set for the product.
The lignin derivatives may, as taught by the invention, be added e.g. to finely divided lignocellulosic material, such as to fibres, to chips or to an aqueous suspension made thereof, before the manufacturing process of the product or in conjunction therewith, e.g. on the paper machine or in the sizing press. As taught by the invention, the lignin may also be added to the lignocellulosic material, or on the surface of the product produced, or to be produced, thereof, as a coating or sizing, or it may be added as a bonding agent to the lignocellulosic material between different layers. The lignocellulosic material, or the product manufactured thereof, may also be impregnated with a lignin solution or suspension e.g. when manufacturing insulating materials.
If desired, the lignin derivatives of the invention may also be chemically modified, e.g. by condensation with formaldehyde, by oxidation with air, or by binding amine groups thereto; in most cases, however, fully satisfactory properties are achieved by using the above-mentioned lignin derivatives as such.
The following examples describe the present invention, however without confining it.
EXAMPLE 1
The effect of the properties of lignin on its retention and on the characteristics of liner made from reclaimed fibres
From a kraft process, black liquor was isolated by ultrafiltration, on the basis of molar mass, lignin derivatives of different molar mass distribution and purity level. In Table 1 are stated the characteristics determined for said lignin fractions (R.sub.3, R.sub.4 R.sub.5, R.sub.9, R.sub.10, R.sub.24 and R.sub.32) and for the kraft black liquor after ultrafiltration.
In Table 1, the molar mass distributions (MWD) of the lignin derivatives have been determined according to the method given in the Finnish patent application No. 58788, and they are stated as proportion of lignin derivatives exceeding molar mass 5000, in percent by weight of all lignin derivatives. The proportion of precipitating stated in percent by weight of the total dry matter of the lignin fraction when precipitating lignin from a solution with dry matter content 1-5% by weight with 1M hydrochloric acid at pH 3. Sodium sulphide, sodium and ash content are stated in percent by weight calculated on the dry matter of the lignin fraction.
TABLE 1__________________________________________________________________________Characteristics of the examined sulphate lignin fractionsand sulphate waste liquor subsequent to ultrafiltration (% b.w.) MWD Prec. Mean Dens. Visc.Lign. M > 5000 lign. cont. (23.degree. C.) Na.sub.2 S Na Ash (23.degree. C.)fract. % % % g/cm.sup.3 % % % mPa.multidot.s__________________________________________________________________________Waste liquor 21 31 27,0 1,1607 5,3 20,4 49,9 2R.sub.3 30 57 23,0 1,1248 2,4 15,7 36,7 3R.sub.4 32 65 25,5 1,1346 2,0 14,5 33,3 3R.sub.5 35 70 27,8 1,1435 1,6 13,2 31,4 3R.sub.9 40 78 22,1 1,1028 0,6 10,9 25,2 5R.sub.13 46 82 19,7 1,0872 0,2 9,3 20,6 7R.sub.24 49 87 17,0 1,0709 0,02 7,2 13,1 9R.sub.32 54 89 21,1 1,0878 <0,01 7,3 15,9 10__________________________________________________________________________
As a measure measure of the degree of purity of lignin one may take the proportion of precipitable lignin, which varied, as can be seen in Table 1, between 31 and 89% by weight. The impure fractions contained large quantities of sodium sulphide, which is converted into toxic hydrogen sulphide gas when pH is lowered into the alkaline range. This phenomenon is already in itself a bar to using impure, lignin derivatives with high content of low-molar mass compounds in the range below pH 7. By using high-molar mass, pure lignin derivatives this drawback was eliminated. The high-molar mass fraction with higher purity also contained less sodium than the low-molar mass fractions, and this is advantageous in view of the acid and/or alum quantity used in precipitation.
The pH values of the lignin fractions entered in Table 1 were adjusted with sulphuric acid to pH 6.6 and they were added to stock made from reclaimed fibres having consistency 12.2 g/l and pH 6.9. The composition of the stock was: 55% by weight magazines, 30% by weight newsprint and 15% by weight corrugated board. Lignin was added 5% by weight, calculated as dry matter related to the stock dry matter. Subsequent to the lignin addition, 1.5% by weight of alum was added as a 3% solution, calculated as dry matter related to the stock dry matter. In this example, and in those following thereafter, "alum" is understood to mean aluminium sulphate containing crystal water: A1 2 (SO 4 ) 3 .16H 2 O. The retention, or the proportion of lignin that has become adherent to fibres of the original lignin quantity, was determined on the basis of ultraviolet absorption measurements (A 280 nm) of the slurry water and the original lignin solution.
Of the stock, sheets were madeets in the laboratory, having grammages about 150 g/m.sup.2 and thickness about 0.29 mm. From the sheets thus produced, the following characteristics were determined: thickness, density, air permeability (SCAN-P 19:78), compression strength, the so-called SCT (SCAN-P 46-83) and CCT (Corrugated Crush Test, SCAN-P 42:81), tensile strength and tensile index (SCAN-P 16:76, tensile index=tensile strength divided by base weight), and water uptake of the sheets by the so-called drop of water method (Drop of Water, TAPPI RC-70). The characteristics and retentions are stated in Table 2.
TABLE 2__________________________________________________________________________The characteristics of the sheets achieved usingkraft black liquor and various kraft lignin fractions. MWD Prec. Air Comp. str. Tens. Tens. Water >5000 lign. Ret. Dens. perm. CCT SCT str. index Drop % % % kg/m.sup.3 s/100 ml kN/m kN/m kN/m Nm/g s__________________________________________________________________________Without lignin 507 78 1,54 2,19 4,8 35,8 13Waste liquor 21 31 42 505 110 1,91 2,85 5,4 36,5 >300R.sub.3 30 57 77 510 131 1,95 2,85 5,8 38,2 "R.sub.4 32 65 81 522 140 2,01 2,86 6,0 39,0 "R.sub.5 35 70 94 539 158 2,01 3,07 6,1 39,9 "R.sub.9 40 78 95 516 147 1,88 2,90 5,8 40,0 "R.sub.13 46 82 97 525 165 2,02 3,14 5,9 39,9 "R.sub.24 49 87 99 534 181 2,04 3,22 6,0 40,0 "R.sub.32 54 89 98 563 216 2,38 3,66 7,0 42,2 "__________________________________________________________________________
As can be seen from the retention values presented in Table 2, low-molar mass lignin derivatives adhered poorly to the fibres. Retentions over 90% were achieved with fractions of which more than 35% by weight had molar mass higher than 5000 and which had degree of purity (proportion of precipitable lignin, over 70% by weight of the total lignin.
The water resistance properties of the sheets improved in all lignin fractions in comparison with sheets produced from reclaimed fibres alone, the water drop penetrating into the latter in about 10 to 20 seconds. In the case of the sheets containing lignin the measurements were discontinued when 300 seconds had passed.
The properties of the sheets all improved with increasing molar mass and degree of purity of the lignin. Improvement of properties could even be achieved with black liquor alone, but its use, like the use of other impure fractions, is rendered doubtful by poor retention, which would create environmental problems for the mill. A very important characteristic, namely the compression strength (SCT), improved significantly when the molar masses of the lignin derivatives increased .gtoreq.35% by weight M>5000 and the degree of purity rose over 70% by weight (FIG. 1).
EXAMPLE 2
The effect of pH adjustment on the characteristics of liner produced from reclaimed fibres
The high-molar mass kraft lignin fraction with 74% by weight having molar mass higher than 5000 and having degree of purity 89% by weight was isolated from kraft black liquor by ultrafiltration. The pH of the fraction as such was 12.6.
The fraction was divided into 8 parts, their pH values being lowered with sulphuric acid to be in the range pH 3 to 10. In the solutions having pH below 6.5, part of the lignin was present in precipitated form as a suspension. The dry matter content of all solutions/suspension was 3.0% by weight.
From waste paper a stock was produced which had a consistency of 4 g/l. The stock was divided into batches and their pH was adjusted to 7, 5 and 3, respectively. The above-mentioned lignin-water suspensions were added to the stock batches so that the lignin addition was 30% by weight, calculated as dry matter related to the stock dry matter.
Thereafter, 3% alum was added as a 2% by weight aqueous solution, calculated as dry matter related to the stock dry matter.
From the lignin/stock mixture liner sheets were produced which had base weight were 140-150 g/m.sup.2 and thickness about 0.25 mm. The characteristics of the sheets are stated in Table 3.
TABLE 3__________________________________________________________________________The effect of the pH values of reclaimed fibre stock, kraftlignin and lignin/fibre mixture on the characteristics of liner sheets. Fibre/ Comp. str. Tens.Stock Lign. lign./al Dens. Air perm. SCT CCT str. Cobb.sub.60 valuepH pH mixt. pH kg/m.sup.3 s/100 ml kN/m kN/m Nm/g index g/m.sup.2__________________________________________________________________________Without lignin 505 126 2,81 1,77 36,2 1517 12,6 12 546 304 2,74 1,85 38,5 102" 9 7 536 208 3,03 1,95 41,7 56" 8 7 480 208 2,94 1,70 41,0 54" 6,5 6 566 320 3,02 2,02 41,7 21" 5 5 682 382 3,58 2,11 40,3 22" 4 5 615 487 3,79 2,14 42,2 21" 3 4 579 525 3,75 2,19 41,8 255 12,6 10 526 193 2,92 1,72 40,0 197" 10 7 520 188 2,95 1,77 39,3 94" 8 6 532 213 3,07 1,96 39,7 25" 6,6 6 540 233 3,31 2,02 42,6 22" 5 5 733 302 3,48 2,97 37,4 17" 4 4 549 314 3,69 2,08 42,6 173 12,6 9 596 182 2,93 2,12 38,7 182" 10 6 541 217 3,14 1,96 39,1 30" 8 5 566 254 3,52 2,03 41,7 18" 6,6 4 602 332 3,69 2,09 39,9 19" 5 4 581 308 3,50 2,06 37,4 28" 4 4 634 279 3,68 2,11 37,9 19__________________________________________________________________________
As can be seen in Table 3, the characteristics of the sheets, in particular the SCT, CCT and Cobb values, improved considerably when the pH of the slurry/lignin/alum mixture fell below 7.
EXAMPLE 3
The effect of the order of adding lignin, acid and precipitation chemical
The pH of the high-molar mass kraft lignin fraction as in Example 2 was adjusted with sulphuric acid to be pH 5. The dry matter content of the lignin solution was 3% by weight. The sulphuric acid quantity required for said pH adjustment was added, in another experiment, directly to stock made from reclaimed fibres, having a consistency of 8 g/l and pH 6.8. In this case, lignin was added to the stock in the form of a solution having pH 12.6. The lignin addition was about 30% by weight, calculated as dry matter related to the stock dry matter. For precipitation chemical, alum was used in the experiments, this being added in the form of a 3% by weight solution at 2% by weight, calculated as dry matter related to the fibre stock dry matter.
In the experiments the order of adding kraft lignin, sulphuric acid and alum to the fibre stock was varied. From the lignin/stock mixtures sheets were produced which had base weight 140-150 g/m.sup.2 and thickness 0.25 mm. The lignin retention and the characteristics of the sheets are stated in Table 4.
TABLE 4__________________________________________________________________________The effect of order of adding lignin (SA), acid (H.sub.2 SO.sub.4) andprecipitationchemical (alum) on the characteristics of sheets. Cases in whichsulphuricacid was added to the lignin in advance are marked (SA + H.sub.2 SO.sub.4) AirOrder of perm. Comp. str. Tens. Cobb.sub.60addition Mixt. Ret. Dens. s/100 SCT CCT str. ind. value.sup.1)to stock pH % kg/m.sup.3 ml kN/m kN/m Nm/g g/m.sup.2__________________________________________________________________________Stock 6,8 -- 505 126 2,81 1,77 36,2 151withoutlignin1) (SA + H.sub.2 SO.sub.4) 6,3 99 585 539 3,77 2,18 40,2 182) Alum1) Alum 6,1 99 601 594 3,88 2,24 39,9 192) (SA + H.sub.2 SO.sub.4)1) H.sub.2 SO.sub.4 5,7 99 584 496 3,97 2,18 43,9 172) SA3) Alum1) Alum 5,7 99 571 544 3,92 2,39 44,0 172) SA3) H.sub.2 SO.sub.41) H.sub.2 SO.sub.4 5,6 99 588 584 3,97 2,22 43,6 182) Alum3) SA1) SA 5,7 97 599 531 3,97 2,36 45,2 112) H.sub.2 SO.sub.43) Alum__________________________________________________________________________ .sup.1) SCANP 12:64, states the water quantity (in g/m.sup.2) meter, whic the paper or cardboard surface absorbs in 60 seconds from a water column cm in height covering it.
As can be seen in Table 4, good retentions were achieved independent of the order in which lignin, acid and alum were added, and the characteristics of the sheets improved in all instances in comparison with reclaimed fibre alone.
EXAMPLE 4
The effect of lignin quantity added on the characteristics of reclaimed fibre liner
To stock produced from reclaimed fibres, having pH about 7 and consistency about 10 g/l, was added high-molar mass lignin of which 54% had molar mass higher than 5000, at 0, 0.5, 2.5, 5, 7, 10, 15, 20, 30, 40, 50 and 60% by weight as dry matter, calculated on the stock dry matter. The dry matter content of the lignin solution was 3% and its pH had been adjusted to be below 7 before addition to the fibre stock. After the lignin addition, alum as 3% solution was added 1.5-2% by weight, calculated as dry matter related to the stocky dry matter. The stock/lignin/alum mixtures had pH values varying between 5 and 6. The retention was between 94 and 100% in all cases. The grammages of the sheets were about 150 g/m.sup.2 and the thickness about 0.25 mm; the other characteristics are seen in Table 5.
TABLE 5__________________________________________________________________________The effect of high-molar mass lignin addition quantity on thecharacteristics of liner sheets produced from reclaimed fibres.SA Dens. Air perm. Comp. str. Tens. str. Tens. index Cobb.sub.60 Wateradded % kg/m.sup.3 s/100 ml SCT kN/m CCT kN/m kN/m Nm/g g/m.sup.2 Drop__________________________________________________________________________ 0% 500 94 2,47 1,58 5,01 34,8 159 95 0,5 498 86 2,69 1,84 5,10 35,2 23 2,5 521 96 2,76 1,86 5,33 36,2 77 5 527 146 2,92 1,92 5,72 38,6 27 >300 7 520 95 2,82 1,88 5,74 37,5 >30010 543 164 3,00 1,93 5,30 36,1 25 "15 548 207 3,23 2,03 5,76 39,2 24 "20 574 244 3,49 2,16 5,80 39,5 24 "25 593 274 3,73 2,37 6,30 41,2 "30 592 537 3,73 2,20 6,01 40,9 20 "40 595 373 3,98 2,43 5,91 39,4 22 "50 602 396 3,96 2,36 5,92 40,8 32 "60 614 477 3,97 2,26 5,72 40,9 19 "__________________________________________________________________________
The results are also shown in FIG. 2, in which the SCT compression strength, CCT compression strength and tensile strength values are calculated as percent improvement over the with sheets without lignin. As is seen in FIG. 2, the SCT values are bettered up to 60%. The Cobb.sub.60 values, i.e., the amount of water absorbed by the cardboard in 60 seconds, were reduced from 159 to about 22 g/m.about.2.about., or by 86% when the lignin additions were over 20%.
When comparing the results with the characteristics of sheets made from virgin fibres, e.g. from a kraft stock, one may note that by adding high-molar mass lignin to reclaimed fibres more than 20% by weight, sheets can be produced on which the SCT values are equal to or better than the values of sheets manufactured from a kraft stock (FIG. 3).
EXAMPLE 5
The effect of the dry matter content of lignin on its adhesion to fibres
As is seen in Table 6, eleven kraft lignin solutions in the dry matter range 0.1 to 20% by weight were prepared. All solutions had pH 5, and the high-molar mass kraft lignin fraction was the same as in Example 2. Part of the kraft lignin was freeze-dried into a finely divided powder. Prior to drying, the pH of the lignin was adjusted to be 5.
The lignin quantity added was 30% by weight as dry matter calculated on the dry matter of stock produced from waste paper. The stock had consistency 8.5 g/l and pH about 7. The alum quantity added after the lignin addition was 2.0% by weight calculated as dry matter related to the stock dry matter, and it was added in the form of a 3% by weight aqueous solution. The retentions that were determined are stated in Table 6.
TABLE 6______________________________________The effect of the dry matter content of high-molar mass kraft lignin on its retention.Dry matter Consistency of slurry/cont. of lignin Retention lignin/alum mixture,% % g/l______________________________________ 0,10 98,4 3,1 0,15 97,1 4,1 0,20 96,0 4,9 0,40 97,8 6,8 0,60 98,5 7,7 0,80 98,5 8,4 1,0 98,8 8,8 3,0 98,8 10,2 5,0 98,9 10,510,0 99,0 10,720,0 99,9 10,9Powder (about 100%) 93,7 11,0______________________________________
As can be seen in the table, good retentions were achieved within the entire dry matter range 0.1 to 100%. Selection of appropriate dry matter content is therefore in the first place dependent on the production process used and on whether it is desired to reduce the consumption of water per ton of product, whereby for instance the drying costs will be lower.
EXAMPLE 6
The effect of the alum quantity on retention and on the characteristics of liner
High-molae mass kraft lignin as in Example 2 was added as a 3% aqueous solution to stock produced from waste paper, at 30% by weight, calculated calculated as dry matter related to the stock dry matter. The pH of the lignin solution had been adjusted to about pH 5 with sulphuric acid before addition. The pH of the stock was adjusted to pH 5.3 prior to lignin addition. The alum addition varied in the range 0 to 10% by weight (on the stock dry matter).l Liner sheets were produced in the laboratory, with base weight about 150 g/m.sup.2 and thickness about 0.25 mm. The retentions and the characteristics of the liner are stated in Table 7.
TABLE 7__________________________________________________________________________The effect of alum quantity added on retentionand on the characteristics of liner sheet.Alum Ret. Dens. Air perm. Comp. str. Tens. str. Tens. index Cobb.sub.60added % % kg/m.sup.3 s100 ml SCT kN/m CCT kN/m kN/m Nm/g value gm.sup.2__________________________________________________________________________Without 500 94 2,47 1,58 5,01 34,8 159lignin0 97,9 621 226 3,08 1,78 4,76 33,8 600,5 98,2 560 283 3,08 1,80 4,88 38,7 261 99,0 583 281 4,06 1,93 5,00 37,6 191,5 99,0 587 286 3,09 1,92 4,81 37,6 182 99,4 563 286 3,14 1,77 4,77 37,0 222,5 99,3 601 279 3,15 1,74 4,28 34,0 473 99,3 597 313 3,40 2,11 5,08 36,9 245 98,0 597 328 3,49 1,89 5,15 36,3 227 98,2 619 286 3,52 1,87 5,48 38,3 2110 98,8 605 300 3,51 2,02 5,10 36,2 24__________________________________________________________________________
As can be seen in Table 7, alum addition is not indispensable, but even with a small alum addition both the retentions and the characteristics of the sheets alrady improve.
EXAMPLE 7
The effect of precipitation chemicals on lignin retention
Salts of bivalent and trivalent metals, alum, FeCl.sub.3, Fe.sub.2 (SO.sub.4).sub.3, FeSO.sub.4, polyaluminiumchloride (PAC), and cationic precipitation chemical, polyethylene imine (Polymin SK, BASF) were used for precipitation chemical for precipitating the high-molar mass lignin fraction onto reclaimed fibres. The quantity of lignin added was 30% by weight as dry matter, calculated on the slurry dry matter. The degree of purity of the lignin fraction was 89% by weight, and 79% by weight thereof has molar mass higher than 5000. pH of the lignin solution had been adjusted to pH 5 with sulphuric acid prior to precipitation, and its dry matter content was 3.0%. The precipitation chemicals were added as a 3% solution at 2% by weight of the stock dry matter, taking into account the crystal water in the chemical, if any. The effect of the chemicals on adhesion of the lignin to the fibres is indicated by the retention values, Table 8.
TABLE 8______________________________________The effect of precipitation chemicals on lignin retentionPrecipitation Lignin pH of stock/lignin/chemical retention, % prec. chem. mixture______________________________________-- 92,3 6,7H.sub.2 SO.sub.4 99,5 3,5Al.sub.2 (SO.sub.4).sub.3.16H.sub.2 O 99,9 4,8FeCl.sub.3.6H.sub.2 O 98,1 4,6Fe.sub.2 (SO.sub.4).sub.3 99,6 5,0FeSO.sub.4.7H.sub.2 O 99,7 5,8PAC 99,7 5,5Polymin SK 99,7 6,3______________________________________
As can be seen in Table 8, it is possible, using various precipitation chemicals, to increase the retention close to 100% without substantially increasing the acidicity; this is often desirable considering the characteristics of the product, e.g. its sizability and printability. Achieving high retention is also important in view of the plant effluents.
EXAMPLE 8
Use of hogh-molar mass bleaching lignin in reinforcement of liner
From waste liquor from the alkali extraction step following after chlorination, originating from bleaching alkali-digested cellulose, a high-molar mass lignin fraction was isolated which had a molar mass of 37% by weight of M>5000, pH about 8 and dry matter content 17% by weight. Before precipitation, the lignin fraction was diluted to 3% by weight and its pH was adjusted to be below 3.
To a stock produced from reclaimed fibres, having pH 7, 30% by weight lignin fraction and 5% by weight polyimine were added, both calculated as dry matter related to the stock dry matter. Sheets with a grammage of 130 g/m.sup.2 and thickness about 0.22 mm were produced in the laboratory. The characteristics determined from the sheets are stated in Table 9.
TABLE 9__________________________________________________________________________The effect of high-molar mass lignin fraction isolated from bleachingwasteliquor on the characteristics of sheets produced from reclaimed fibres. Density Porosity Compr. str. Cobb.sub.60 Water kg/m.sup.3 s/100 ml SCT kN/m CCT kN/m value g/m.sup.2 Drop s__________________________________________________________________________Without 531 184 2,35 1,34 215 13ligninBleaching 605 480 3,04 1,66 146 >300lign.__________________________________________________________________________
As can be seen in Table 9, good characteristics were also achieved by using high-molecular lignin isolated from bleaching waste liquor.
EXAMPLE 9
Addition of lignin to a fibre web (Coating)
Using high-molar mass kraft lignin with 79% by weight of it exceeding M 5000, six aqueous solutions were prepared having 3% by weight dry matter content, and pH 3. The pH of five solutions was adjusted with sulphuric acid to, respectively, pH 3, 4, 5, 7 and 9. The first three were partly in suspension form. The lignin-water solutions/suspensions were added as a kind of coating to reclaimed fibre sheets, from which most of the water had been drained through the wire. The addition was 30% by weight, calculated as dry matter related to the dry matter of the fibres. For precipitation chemical, alum was used as a 3% solution, the addition being 2% by weight calculated as dry matter related to the dry matter of the fibres. The results are given in Table 10.
TABLE 10__________________________________________________________________________Addition of lignin as a coating and its effecton the characteristics of reclaimed fibre liner. Air Compr. str. Tens. Tens. Cobb.sub.60Lign. Dens. perm. SCT CCT str. ind. valuepH kg/m.sup.3 s/100 ml kN/m kN/m kN/m kN/m g/m.sup.2__________________________________________________________________________3 458 321 3,92 2,35 5,6 35,9 584 653 448 3,71 2,37 5,7 37,3 585 641 485 3,98 2,58 6,3 44,6 317 473 131 2,24 1,25 4,5 39,2 1639 479 150 2,12 1,27 4,4 38,4 16113 531 184 2,35 1,34 4,6 35,7 215Without 507 174 2,69 1,70 5,1 35,2 199lignin__________________________________________________________________________
As can be seen in Table 10, by adding on the surface of sheets a lignin solution with pH adjusted to be below 7, the characteristics of liner produced from reclaimed fibres could be significantly improve in comparison with liner to which no lignin had been added.
EXAMPLE 10
The effect of lignin addition quantity on the characteristics of fiber produced from kraft stock
To a kraft stock with a pH of 8.55 and a consistency of 18 g/l before precipitation, 0 to 50% by weight of high-molar mass kraft lignin as in Example 2 was added at 0 to 50% by weight dry matter, calculated on the stock dry matter, its pH being adjusted to pH 5 before precipitation. For precipitation chemical, alum as a 3% by weight solution was used, added to the fibres at 2% by weight, calculated as dry matter related to the stock dry matter. The grammage of the liner sheets that were produced was about 150 g/m.sup.2 and thickness about 0.26 mm. The other characteristics, determined at 50% relative humidity, unless otherwise stated, were as follows:
TABLE 11__________________________________________________________________________The effect of high-molar mass kraft lignin onthe characteristics of liner produced from kraft stock. Air Comp. str. Tens. Tens. Cobb.sub.60 85%-humid.Lign. Dens. perm. SCT CCT str. ind. value SCTadded kg/m.sup.3 s/100 ml kN/m kN/m kN/m Nm/g g/m.sup.2 kN/m__________________________________________________________________________ 0 550 5,4 3,10 1,83 6,93 48,5 34 1,64 5 579 6,5 3,44 1,95 7,54 51,6 32 1,8610 574 6,0 3,52 1,99 7,91 53,4 27 1,9020 565 5,3 3,45 1,90 7,74 52,7 25 1,9030 578 6,2 3,47 2,00 7,79 52,6 27 1,8940 596 7,8 3,51 2,11 8,08 54,2 26 1,9450 593 9,7 3,65 2,19 8,19 54,6 26 1,96__________________________________________________________________________
As can be seen in Table 11, also virgin fibres can be reinforced with high-molar mass lignin. The SCT values have here increased by 20%, both at 50% and 85% relative humidity of air. The quantity of lignin added, calculated at 5% by weight dry matter related to the stock dry matter, implies that when for instance the added quantity is 50% by weight, the composition of the stock/lignin mixture is 33% by weight lignin dry matter and 67% by weight stock dry matter.
EXAMPLE 11
Production of fibreboards
To a fibre suspension which had consistency 10 g/l, high-molar mass kraft lignin was added, as a 5% solution, at 1 and 2.5% by weight. The lignin was precipitated onto the fibres with alum, added as a 3% solution at 1% by weight, calculated as dry matter related to the dry matter of the fibres.
The production conditions of fibre boards were as follows: hot pressing temperature 205.degree. C., pressure 0.5 Nm/mm.sup.2, and pressing time 6 to 7 minutes. The sheets were post-hardened at 160.degree. C. for 4 hours.
The characteristics of the boards are given in Table 12, where also the characteristics of fibre boards made with phenolic resin are stated.
TABLE 12______________________________________The characteristics of fibre boards Quant. Flexur. Tens. Water added str. str. uptake SwellingBonding agent % N/mm.sup.2 N/mm.sup.2 24 h, % 24 h, %______________________________________Phenolic resin 1 501 2,22 27,2 16,8High-molar mass 1 612 2,56 23,6 15,3kraft ligninD:o 2,5 546 265 26,6 16,7______________________________________
As can be seen in Table 12, the results achieved with high-molar mass kraft lignin are better than those with phenolic resin. Thus, the strength characteristics of fibreboards could be improved in an economically advantageous way.

Number	Name	Date
2849314	Goss	Aug 1958
3159528	Goss	Dec 1964
3236720	Tousignant et al.	Feb 1966
3615788	Limbert et al.	Oct 1971
4357454	Holmberg	Nov 1982

Procedure for manufacturing lignocellulosic material products

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Parent Case Info

PCT Information

US Referenced Citations (5)

Foreign Referenced Citations (1)

Continuations (1)