Patent Grant
8900406
The present invention relates to procedures for obtaining nanofibrillated cellulose, and more particularly, to obtaining nanofibrillated cellulose from recovered paper.
Different documents describing different procedures for obtaining nanofibrillated cellulose are known in the state of the art.
In U.S. Pat. No. 4,483,743, nanofibrillated cellulose is obtained from a liquid suspension of virgin cellulose that is subjected to a warming-up pre-treatment of 50° C. to 80° C., being processed by passing it through a high pressure homogeniser.
WIPO publication WO2011/051882 A1 describes a procedure for obtaining nanofibrillated cellulose obtained from cotton, cereals, hard and soft woods that are subjected to a pre-treatment with enzymes, being processed by a twin-screw extruder.
In WIPO publication WO2010/149711 A2, the raw material from which nanofibrillated cellulose is obtained is recycled white paper, colour paper of different colours or bleached papers, which are subjected to a previous treatment comprising the use of a paper shredder with an interchangeable hammer mill suitable for the preparation of hemp, cereal straw and other lignocellulosic materials, related to the separation of foreign (opposite) material (wood, metal, stone, plastics, etc.) and a cleaning system, including the elimination of powder.
Finally, WIPO publication WO2011/055148 describes an apparatus and a method for processing cellulose fibres, which leaves the source of cellulosic material very open, not using just paper, using some pre-treatments similar to those from the above patent.
However, none of the above patents describes a procedure for obtaining nanofibrillated cellulose starting from recovered paper, obtaining nanofibrillated cellulose having similar features to that obtained from virgin cellulose.
In view of the foregoing, it is an object of the present invention to develop a procedure for obtaining nanofibrillated cellulose that, starting from recycled material (e.g., recovered paper, or recovered paper pulp or recovered cellulose), obtains cellulose with similar features to that obtained from virgin cellulose.
The present invention is characterised by both the starting raw material and the technical features of some of the stages, such that the overall features allow obtaining nanofibrillated cellulose from recovered paper.
The distinguishing feature with respect to the state of the art, is not just the fact of starting from recovered paper, or from recovered paper pulp or from recovered cellulose, but also the stages that said raw material has had to be subjected to in order to obtain nanofibrillated cellulose with similar features to that obtained from virgin cellulose.
For that purpose, the raw material undergoes a procedure comprising a chemical pre-treatment stage, and a second mechanical treatment stage.
The chemical pre-treatment stage has two objectives, on the one hand the weakening of cellulose fibre and, on the other hand, the elimination of inorganic fillers that can act as promoters of agglomeration of fibres, i.e., purification is undertaken by removing mineral fillers without attacking the fibres through the elimination of carbonates, among other mineral fillers.
Among all the products tested and sought it is believed that the product that cleans all the fibres of the original cellulosic material of most of the mineral filler is acetic acid, the raw material being immersed in an acetic acid dilution for a while and subjected to a stirring process.
The second stage consists of a mechanical treatment in which some shear forces are applied in order to longitudinally and completely separate the cellulose fibres already weakened in the previous step.
The application of shear forces for longitudinally separating the fibres can take place through a mixer or similar equipment for creating enough shearing on the cellulose pulp.
According to an embodiment of the present invention, a procedure for obtaining nanofibrillated cellulose, starting from a raw material including recycled or recovered paper or recovered paper pulp or recovered cellulose, comprises the following stages:
These and other objects, aspects and advantages of the present invention will be better appreciated in view of the following detailed description of preferred embodiments.
For a preferred embodiment of the invention, the acetic acid dilution in which the raw material (recovered paper, or recovered paper pulp or recovered cellulose pulp) is immersed will be a 10% to 50% by volume dilution, and even lower or higher dilutions can be used, depending on the time the raw material is immersed in the dilution. The lower the dilution, the higher the immersion time, and vice versa.
The time the raw material remains immersed in the acetic acid dilution will be inverse to the concentration of acetic acid in the dilution, noting just as a reference and not a limiting value that, for a 35% by volume acetic acid dilution, the suitable time of immersion for the raw material will be approximately 20 minutes.
The acetic acid dilution in which the raw material is immersed and the time required are not necessarily limiting, and can readily be adjusted according to convenience and taking into account the inverse relation of the two. More preferred values for a particular process can be determined after characterising the cellulose obtained by analysing the physical-chemical features.
Regarding the mechanical processing for the longitudinal separation of fibres, it can take place through the application of shear forces, which in turn can be applied, among other methods, by means of a mixer or similar equipment capable of creating enough shearing on cellulose pulp. The speed of the mixer will be in the range of 20 to 600 revolutions per minute (RPM).
The obtained pulp humidity will be in the range of 30% to 50%, while the temperature at which the process is performed will be from 25° C. to 95° C.
Sufficiently described the nature of the present invention, as well as how to put it into practice, it is noted that, within its essence, it may be brought to the practice in other embodiments that differ in detail from the one shown by way of example, and which will also reach the protection that is sought, provided that its fundamental principle is not altered, changed or modified.
In general, the foregoing description is provided for exemplary and illustrative purposes; the present invention is not necessarily limited thereto. Rather, those skilled in the art will appreciate that additional modifications, as well as adaptations for particular circumstances, will fall within the scope of the invention as herein shown and described and of the claims appended hereto.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201230663 | May 2012 | ES | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4483743 | Turbak et al. | Nov 1984 | A |
| 5964983 | Dinand et al. | Oct 1999 | A |
| Number | Date | Country |
|---|---|---|
| 2010149711 | Dec 2010 | WO |
| 2011051882 | May 2011 | WO |
| 2011055148 | May 2011 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20130292070 A1 | Nov 2013 | US |