Patent Application
20070126145
The present disclosure relates to a process and an apparatus for embossing a pattern onto a surface.
Embossing is a process by which a surface of a substrate, e.g., a continuous sheet material or web, is patterned or textured. Embossing is typically accomplished by means of a negative pattern that is pressed onto the substrate surface to form the embossed positive pattern. The negative pattern is formed on a hard material such as a metal layer on an embossing roll, belt, or continuous sleeve. The metal layers are typically fabricated from metals such as nickel, copper, steel, and stainless steel. The negative patterns can be machined into the metal layer, or the metal layer can itself be an electroformed replica of a positive pattern formed on a glass or silicon substrate, that pattern itself produced via standard photolithography techniques. There are other variations on this “mastering” and “submastering” sequence for producing embossing tools that are well known.
To emboss thermoplastic sheet materials, the sheet material is typically first preheated and subsequently pressed with a cooled embossing pattern roll. Preheating the thermoplastic sheet material softens the sheet to allow the pattern to be more accurately set into the sheet and the subsequent cooling step helps retain the pattern. In a continuous process, the sheet material is typically fed into a nip formed between an engraved metal roll having the embossed pattern and a rubber backed backup roll. The metal roll is cooled with a refrigerated solution to remove heat from the sheet and to set in the embossed pattern. The degree of preheating to soften the sheet must be carefully controlled so that no melting or degrading to the sheet will take place. To make the heat removal process as efficient as possible, no more heat should be applied than is needed to satisfactorily emboss the product.
Another variation on the embossing process, used in applications such as holograms, is to use a hot embossing roller and a backing drum to form a high-pressure nip to emboss the surface of the web passing through it. Since there is little flow of plastic material in this process, the web must be extremely flat and uniform in thickness, the rollers very rigid and precise to withstand the high nip forces, and the embossing roll not too hot to prevent sticking of the web and thus smearing of the embossed pattern.
The web may be produced using a conventional extrusion machine and then fed to a separate embossing apparatus. In these types of processes, heating the web to its softening temperature, i.e., deforming temperature, is a rate-limiting step. As a result, process speeds are often limited by the amount of time it takes to heat the web to the desired softening temperature, typically less than about 3 to about 5 feet per minute.
Many attempts have been made to improve the processing speed as well as the accuracy in the reproducibility of the embossed pattern. In U.S. Pat. No. 3,689,346 to Rowland, there is described a method for continuously producing cube-corner type retroreflective sheeting. According to this method, retroreflective sheeting is produced by depositing a curable molding material upon a cube-corner mold and applying a transparent, flexible film material over the molding material, after which the molding material is cured and bonded to the film material. However, the resins specifically described in this patent for use as molding materials are mostly limited to crosslinkable resins such as plastisol type vinyl chloride resin containing a crosslinking acrylic ester monomer.
In U.S. Pat. No. 4,244,683 to Rowland, there is disclosed an apparatus and method (i.e., a so-called progressive pressure forming method) for semi-continuously embossing thermoplastic synthetic resin sheeting to form cube-corner prisms on one surface thereof. In this patent, it is described that prism elements are formed by placing a series of flat embossing molds on one surface of synthetic resin sheeting traveling on an endless belt having a smooth surface, and pressure-forming the sheeting successively in three types of press stations (i.e., a preheating station, a thermoforming station, and a plurality of cooling stations). However, the prism sheeting produced by this method shows seams distinctly owing to the use of juxtaposed flat molds, resulting in a poor appearance of the product. Moreover, this method has the additional disadvantage of being inferior in productivity.
In U.S. Pat. Nos. 4,486,363 and 4,601,861 to Pricone et al., there are disclosed apparatus and methods for continuously embossing cube-corner prisms on one surface of thermoplastic synthetic resin sheeting. According to the embossing methods described in these patents, a portion of an embossing tool comprising an endless belt having a precision embossing pattern is heated to a temperature above the glass transition temperature of the thermoplastic synthetic resin. Thereafter, the thermoplastic synthetic resin sheeting is continuously embossed at a plurality of pressure points and then cooled to a temperature below the glass transition temperature of the thermoplastic synthetic resin in a cooling station.
In the methods described in these patents, the embossing temperature is limited to a temperature higher than the glass transition temperature of the synthetic resin and lower than the glass transition temperature of a carrier film. If the film is heated just above its glass transition, the resin tends to have insufficient fluidity, and hence requires a long pressing time or a plurality of pressure points. Thus, these methods are not considered to be highly productive. Moreover, these methods have the disadvantage that the elements embossed under such temperature conditions show a reduction in shape accuracy owing to elastic deformation. If the film is heated far above its glass transition to assure sufficient fluidity, long pressing times are required for heating and so productivity suffers. Furthermore, since the embossing temperature is limited to a temperature higher than the glass transition temperature of the synthetic resin and lower than the glass transition temperature of a carrier film as described above, the choice of a carrier film is disadvantageously limited when high-melting synthetic resin sheeting made, for example, of a polycarbonate resin is to be embossed. Furthermore, all of the above methods require a plastic film as a raw material supplied to the embossing process, which requires a high-quality extruded film be purchased or manufactured separately, which adds significant cost to the final products.
Disclosed herein are processes and apparatus for producing a film having an embossed surface. In one embodiment, a process for embossing a film comprises heating a resin and forming a flowable melt; directing the flowable melt to a first nip; embossing a first side of the flowable melt and cooling a second side of the flowable melt to form an embossed film; and cooling the embossed film.
In one embodiment, the present invention provides a process for embossing a film, the process comprising heating a resin and forming a flowable melt; directing the flowable melt to a first nip; embossing a portion of a first side of the flowable melt by contacting said portion of the first side of the flowable melt with an embossing tool at a temperature greater than the glass transition temperature of the resin while contacting a corresponding portion of a second side of the flowable melt with a backside roll at a temperature less than the glass transition temperature of the resin to form an embossed film; and cooling the embossed film.
In another embodiment, the process comprises heating a resin and forming a flowable melt; directing a carrier film and the flowable melt to a first nip; embossing a first side of the flowable melt and cooling a second side of the flowable melt in contact with the carrier film to form an embossed film frangibly fused to the carrier film; and cooling the embossed film.
In another embodiment, the present invention provides a process for producing an embossed film comprising heating a resin and forming a flowable melt; directing a carrier film comprising a textured surface and the flowable melt to a first nip; embossing portion of a first side of the flowable melt by contacting said portion of the first side of the flowable melt with an embossing tool at a temperature greater than the glass transition temperature of the resin while maintaining a corresponding portion of a second side of the flowable melt in contact with the textured surface of the carrier film at a temperature less than the glass transition temperature of the resin to form an embossed film frangibly fused to the carrier film, wherein the embossed film comprises an embossed first side and a second side textured with a surface texture provided by the carrier film; cooling the embossed film; and separating the carrier film from the embossed film.
In another embodiment, the present invention provides a process which comprises heating a resin and forming a flowable melt; directing a backing film and the flowable melt to a first nip; embossing portion of a first side of the flowable melt at a temperature greater than the glass transition temperature of the resin while cooling a corresponding portion of a second side of the flowable melt in contact with the backing film to a temperature below the glass transition temperature of the resin to form an embossed film fixedly attached to the backing film; and cooling the embossed film.
In another aspect, the present invention provides an apparatus for producing a film having a surface with an embossed pattern, the apparatus comprising means for heating a resin to form a flowable melt and directing the flowable melt into a first nip formed between an embossing tool and a backside roll; means for maintaining the embossing tool at a temperature greater than a glass transition temperature of the resin; means for maintaining the backside roll at a temperature lower than the glass transition temperature of the resin; and means for pressing the embossing tool and backside roll together to transfer an embossed pattern to a first side of the melt and produce an embossed film.
The above described and other features are exemplified by the following figures and detailed description.
Referring now to the figures wherein like elements are numbered alike:
Disclosed herein are processes for producing a film having an embossed pattern formed in one surface. The processes generally include heating a resin to form a flowable melt, and directing the flowable melt into a first nip between an embossing tool maintained at a temperature greater than a glass transition temperature of the resin and a backside roll maintained at a temperature lower than the glass transition temperature of the resin. The flowable melt is pressed against the embossing tool and the backside roll forming a self-supporting film by cooling a surface of the melt in contact with the backside roll to a temperature less than the glass transition temperature of the resin, and embossing a pattern onto the other surface of the melt in contact with the embossing tool. The other surface in contact with the embossing tool is at a temperature greater than the glass temperature of the resin and as such, maintains the resin in a flowable state. The film maintains engagement with the embossing tool as it exits the first nip, may pass through additional nip rollers and/or sonic welders, is cooled, and is subsequently separated from the embossing tool.
The processes for producing the embossed film are versatile and can be practiced with or without a carrier film. When employed, the carrier film is preferably engaged with the backside roll and fed into the first nip. Advantageously, carrier films can be used to provide a desired finish to the backside surface (the non-embossed surface) of the product embossed film. For example, if a smooth polished finish to the backside surface is desired, the surface of the carrier film that contacts the second surface of the flowable melt preferably has a smooth surface. To produce a textured finish such as for light diffusion applications, the surface of the carrier film that contacts the second surface of the flowable melt preferably has a textured surface sufficient to impart the desired light diffusion properties. As used herein, the terms “texturing”, “textured surface”, and “textured finish” refers to the possibly imperfect replication of a surface that is not smooth. For example a tool having a surface characteristic to be replicated, for example a random surface roughness, when contacted with a flowable melt is said to provide a film having a “textured surface” when less than 90 percent of the surface characteristics of the tool are replicated in the surface of the product film. In contrast, the term “embossing” refers to the precise replication of the pattern on the embossing tool in the surface being embossed. Typically the surface characteristics of the embossing tool are replicated in the embossed surface with greater than 90 percent fidelity, and more typically with greater than 95 percent fidelity. The surface characteristics of the embossing tool to be replicated in the embossed surface are illustrated by surface characteristics such as random roughness and specific functional microstructures. Specific functional microstructures are illustrated by light-diffusing microstructures, prismatic microstructures, optical lens microstructures, microfluidic device microstructures, and like microstructures.
In one embodiment, the present invention provides an embossed film comprising functional microstructures selected from the group consisting of hemispherical functional microstructures, lenticular functional microstructures, prismatic functional microstructures, and corner-cube (retroreflective) functional microstructures. Films comprising functional microstructures typically comprise an embossed surface having precise geometry and tolerances. In one embodiment, the present invention provides an embossed film comprising functional microstructures, said microstructures being from about 1 to about 100 microns in size. In one embodiment, the embossed film provided by the present invention has a surface characteristic corresponding to a surface roughness of less than about 50 nm. In yet another embodiment, the embossed film provided by the present invention has a surface characteristic corresponding to a surface roughness of less than about 10 nm. In still yet another embodiment, the embossed film provided by the present invention has a surface characteristic corresponding to sharp corners, for example prism tips, having a radius of less than about 1 micron. It should be noted that conventional embossing techniques give relatively poor control of fidelity in the transfer of surface characteristics from the embossing tool to the embossed film. A lack of fidelity in the embossing process can lead to, for example, functional microstructures having rounded tips on the surface of the embossed film replicated using an embossing tool having sharp edged structures. In one embodiment, the present invention provides an embossed film comprising prismatic microstructures. In a specific embodiment, the present invention provides an embossed film comprising prismatic microstructures having a 25-50 micron pitch and approximately 90 degree peaks. In one embodiment, the prismatic microstructures are from about 12 to about to about 25 microns tall, have a tip radius of less than about 2 microns, and have a surface roughness of less than about 10 nm on flat portions of the prismatic microstructures.
In combination with providing a desired finish to the backside surface, the carrier film also serves to hold the embossed film against the tool, and to protect the film from processing defects such as stick-ripple, particle contamination, and the like. Feeding the carrier film into the first nip prevents formation of stick ripple pattern in the embossed film since sticking of the melt to the backside roll is prevented. The carrier film can be later stripped from the embossed film prior to rolling or may be left on the embossed film during rolling.
In another embodiment, a backing film can be employed. The backing film is preferably a material that will permanently adhere to the embossed film formed from the flowable melt as the embossed film is produced. That is, after processing, the backing film cannot be removed without damaging the embossed film. The backing film may be comprised of the same material as the resin used to form the embossed film or a different material. If the backing film uses the same material as the embossed film, it is preferred that a thickness of the backing film is chosen to be greater than a thickness of the embossed film formed from the flowable melt. In this manner, a higher thermal mass is provided to the backing film and melting of the backing film during processing can be prevented. For similar reasons, if the backing film is selected from a material that has a glass transition temperature less than the resin used to form the embossed film, a careful balance between thickness as well as processing speed is required to prevent melting or softening of the backing film during processing.
Suitable resins for practicing the process of the present invention include various thermoplastic or thermoset materials. Suitable resins which may be used to form the flowable melt used in the present invention include, but are not limited to, amorphous materials, crystalline materials, semi-crystalline materials, reaction products, and combinations comprising at least one of the foregoing materials. For example, the resin may comprise one or more of the following materials: polyvinyl chloride, polyolefins (including, but not limited to, linear and cyclic polyolefins and including polyethylene, chlorinated polyethylene, polypropylene, and the like), polyesters (including, but not limited to, polyethylene terephthalate, polybutylene terephthalate, polycyclohexylmethylene terephthalate, and the like), polyamides, polysulfones (including, but not limited to, hydrogenated polysulfones, and the like), polyimides, polyether imides, polyether sulfones, polyphenylene sulfides, polyether ketones, polyether ether ketones, ABS resins, polystyrenes (including, but not limited to, hydrogenated polystyrenes, syndiotactic and atactic polystyrenes, polycyclohexyl ethylene, styrene-co-acrylonitrile, styrene-co-maleic anhydride, and the like), polybutadiene, polyacrylates (including, but not limited to, polymethylmethacrylate, methyl methacrylate-polyimide copolymers, and the like), polyacrylonitrile, polyacetals, polycarbonates, polyphenylene ethers (including, but not limited to, those derived from 2,6-dimethylphenol and copolymers with 2,3,6-trimethylphenol, and the like), ethylene-vinyl acetate copolymers, polyvinyl acetate, liquid crystalline polymers, ethylene-tetrafluoroethylene copolymer, aromatic polyesters, polyvinyl fluoride, polyvinylidene fluoride, and polyvinylidene chloride. Other examples of suitable resins include, but are not intended to be limited to, epoxies, phenolics, alkyds, polyesters, polyimides, polyurethanes, mineral filled silicones, bis-maleimides, cyanate esters, vinyls, and benzocyclobutene resins. Additionally, the resin may comprise blends, copolymers, mixtures, reaction products, and composites comprising at least one of the foregoing resins. In one embodiment, the resin employed to produce the flowable melt is a polycarbonate. In a particular embodiment, the resin employed is bisphenol A polycarbonate.
Heating the resin to form the flowable melt is preferably performed in an extruder assembly. The general operation of extruder assemblies is known to those skilled in the art. That is, in a typical extrusion operation, the resin is subjected to heat, pressure, and shear sufficient to form flowable melt. The flowable melt is then forced through an extrusion die. In a preferred embodiment, the melt is extruded from the extrusion die in the shape of a film, i.e., a planar form, and is discharged directly into the first nip. More preferably, the direction of the melt as it is dropped into the first nip is biased toward the embossing tool such that the film-shaped melt first contacts the embossing roll. The amount of biasing is preferably about the thickness target of the desired film. A distance between the opening of the extrusion die and the nip surface that the melt first contacts is preferably effective to maintain the flow properties of the melt, so that the melt, as it enters the first nip flows into complete conformance with the embossing pattern and that it remains in conformance until it is sufficiently cooled to below its glass transition temperature. Too great a distance will lead to premature cooling of the flowable melt resulting in incomplete duplication (replication) of the embossed pattern present on the embossing tool into the film surface. In addition the distance between the opening of the extrusion die and the nip surface that the melt first contacts must be controlled in order to avoid coating anomalies. Typically, the distance is less than or equal to about 4 inches.
The embossing tool may be a continuous embossing belt or an embossing roll having the embossing pattern (surface characteristics) on its outer surface. Where the embossing tool is an embossing roll, the embossing roll is preferably a steel drum which may internally heated or cooled as needed such that the temperature at the interface between the embossing tool and the first side of the flowable melt is greater than the glass transition temperature of the resin used to form the flowable melt. In one embodiment, the embossing tool is heated or cooled using a fluid medium such as steam, water, air, oil, or the like. In one embodiment, the embossing tool comprises electrical heating elements. In an alternate embodiment, the embossing tool is heated by externally applied radiant energy, for example light from a sunlamp configured to irradiate a portion of the surface of the embossing tool. In one embodiment, the embossing tool is an embossing roll having a double shell design with a spiral wrap for the most efficient passage of a fluid heating medium. In an alternate embodiment, the embossing tool is an embossing roll drum may be rotated about its axis in a single revolution passing a location where it is heated by an infrared lamp or other radiant heating device to a temperature above the glass transition temperature of the resin to be processed. In one embodiment, the embossing roll is heated with externally with a source of radiant energy in combination with internally heating or cooling of the embossing roll. In one embodiment, the embossing tool is such that the embossing pattern to be replicated in the surface of the flowable melt is contained on the surface of a metal or plastic sleeve that fits over the outer surface of a tool component. For example, the embossing tool may be a metal or plastic sleeve which fits over the outer surface of an embossing roll, the metal or plastic sleeve comprising a surface pattern which contacts the flowable melt. In one embodiment, the embossing tool is a continuous embossing belt. In one embodiment, the embossing belt supported by a heating roller and a cooling roller having parallel axes. The heating roller is preferably maintained at a temperature greater than the glass transition temperature of the resin. The cooling roller is preferably maintained below the glass transition temperature. The temperature of the heating and cooling rollers can be controlled by internal heating and/or radiant heating as previously described, e.g., steam, hot oil, infrared lamps, and the like. The rollers are rotated to impart movement to the belt, e.g., the rollers may be driven by chains to advance the belt in the appropriate direction, or the like. The width and circumference of the belt will depend in part upon the width of the flowable melt to be embossed, the desired embossing speed, and thickness of the belt. In the case where the film is stripped off of the belt before it makes contact with the second drum, the second drum may be heated to aid in raising the belt temperature before it returns to the embossing nip.
In one embodiment, the backside roll is preferably a steel drum comprising a highly polished surface for producing a film with a highly polished backside surface. In an alternate embodiment, the backside roll comprises an outer coating of a resilient elastomeric material comprising a surface pattern to be replicated in the product embossed film. In such circumstances, the product embossed film comprises a having a textured backside surface. Suitable resilient elastomeric materials are preferably abrasion resistant and capable of withstanding the processing temperatures. In one embodiment, the elastomeric coating is a silicone rubber with a thickness of about 0.25 inches (about 6.35 millimeters) to about 0.5 inches (about 12.7 millimeters) and a durometer hardness based on Shore A scale of from about 20 to about 100 in one embodiment, and in an alternate embodiment from about 60 to about 100.
The embossing tool can be forced against or maintained in close proximity to the backside roll by means of pneumatic or hydraulic cylinders and lever mechanisms. Varying the pressure to the cylinders and varying the width of the space between the embossing tool and the backside roll may be used to control the force applied to the flowable melt in contact with the embossing tool and can be used to control the speed the replication process. The rotation speed of the rolls is preferably optimized to maintain the film properties. Maximum speed is desired in certain embodiments to ensure that pressure is applied before the melt cools.
As previously described, the process includes maintaining the embossing roll or portion of the embossing belt that first contacts the melt at a temperature greater than the glass transition temperature of the resin and maintaining the backside roll at a temperature less than the glass transition temperature. The term “glass transition temperature” refers to the temperature at which the resin first begins to flow. In this manner a portion of one side (first side) of the flowable melt is in contact with the embossing tool at a temperature greater than the glass transition temperature of the resin while a corresponding portion of the other side (second side) of the flowable melt is in contact with the backside roll at a temperature less that the glass transition temperature of the flowable melt as the flowable melt passes through the first nip. Preferably, the temperature of the embossing roll or the portion of the belt that first contacts the melt is greater than or equal to about 10° C. higher than the glass transition temperature (Tg) of the resin, with a temperature greater than or equal to about 50° C. higher than the Tg more preferred, and a temperature greater than or equal to about 100° C. higher than the Tg even more preferred.
In combination with the temperature of the embossing roll or portion of the belt, it is in certain embodiments preferred that the backside roll has a temperature less than the glass transition temperature of the resin to be embossed. In certain embodiments the temperature of the backside roll is about 5° C. less than Tg of the resin, with a temperature of about 10° C. less than the Tg more is at times preferred, and a temperature of about 25° C. less than the Tg is at times even more preferred. While not wanting to be bound by theory, it is believed that by maintaining the backside roll at a temperature below the glass transition temperature of the resin and the embossing tool at a temperature greater than the glass transition temperature, a temperature gradient across the thickness of the melt (film) is established. Thus a portion of one surface of the melt is cooled below the glass transition temperature of the resin as it contacts the backside roll to form a self-supporting film whereas a corresponding portion of the other surface of the melt that contacts the embossing tool is at a temperature greater than the glass transition temperature of the resin maintaining its flow properties as it passes through the first nip. As a result, a high degree of dimensional accuracy on reproducing the embossed pattern onto the film is achieved. Moreover, it is anticipated that distortion and shrinkage can thus be minimized thereby improving replication of the embossed pattern into the film surface.
As the film exits the first nip, the embossed film maintains engagement with the embossing tool and may be further pressed into the embossed pattern by additional nip rollers in contact with the embossing roll. Suitable nip rollers include a rubber roll, a metal roll, a synthetic resin roll, and other roller types as well as combinations comprising at least one of the foregoing rollers. Optionally, one or more sonic welders may be utilized, especially in applications where a carrier film or backing film is used. In certain embodiments, the sonic welders may be of the type operated by a 120 volt 60 Hertz power supply capable of vibrating at 20,000 cycles per second with horns that move through 0.010 inches. In one embodiment, the sonic welders are disposed in contact with the film after the film exits the first nip. In one embodiment, the sonic welder contacts the film after the first nip as it maintains engagement with the embossing tool.
The resulting embossed film is then rapidly cooled at a cooling station to a temperature lower than the Tg of the resin, preferably greater than or equal to about 5° C. less than the Tg, and more preferably greater than or equal to about 25° C. less than the Tg. The cooling means in the cooling station may comprise, for example, blowing nozzles (e.g., for blowing a cooling medium upon one surface or both surfaces), the use of one or more chilling rollers, immersion of the film into a water bath, and the like.
Once the film has cooled to the desired temperature, the film is then separated from the embossing tool and passed to a winding station or the like. The film may be separated from the embossing tool by a common means, such as a stripping roll.
In the embodiment schematically shown in
As the melt passes through the first nip 18, a temperature gradient across the thickness of the melt is established. The portion of the melt in contact with the backside roll 22 solidifies to form a self-supporting film, i.e., the temperature of the resin portion contacting the backside roll 22 is below the glass transition temperature of the resin. In contrast, the portion of the melt in contact with the embossing roll 20 is at a temperature greater than the glass temperature of the resin, and as such, maintains its flow properties so that the embossing roll 20 reproducibly imprints the embossed pattern into the softened surface of the melt in contact therewith.
The embossed film maintains engagement with the embossing roll 20 and may be further pressed with the embossed pattern by nip roller 24 in contact with the embossing roll 20. Additional nip rollers, sonic welders, and the like, may also be added depending on the intended embossing application.
The embossed film is then cooled at a cooling station 26 by any number of methods. Such methods include moving the film over one or more chilled rollers, delivering the film to a water bath, cooling by air or other gases, and the like. After passing through the cooling station 26, the embossed film 29 is separated from the embossing roll 20 at stripping roller 28.
In
The laminate is then cooled at cooling station 26 and removed from engagement with the embossing roll 20 at stripper roller 28. Once separated from the embossing roll 20, the carrier film 36 may then be stripped from the embossed film 29 by engaging the carrier film with stripper roller 40 as shown, or alternatively, can be left on the embossed film. Once the carrier film is removed from the embossed film 29, the surface of the embossed film that was frangibly fused to the carrier film 36, i.e., the non-embossed surface, will have a mirror image of the surface of the carrier film. In this manner, the amount of texture present on the non-embossed surface can be controlled for those applications where it is desired, e.g., light diffusion applications, high gloss, and the like.
Optionally, the carrier film 36 may include a release coating for controlling the gloss to the non-embossed surface of the film or for facilitating the ease in which the carrier film 36 is separated from the embossed film 29. The release coat is preferably a silicone based liquid coating applied to the carrier film by a coating process such as a gravure printing process, by direct or reverse roll coating, or the like. The carrier film 36, individually or in combination with the release coat, may also include a transfer film that is transferred to the back of the embossed film during processing. The transfer film may be fabricated from the same or different material than the resin used to form the embossed film, or may comprise one or more layers depending on the desired application.
In
In
In
In
The present disclosure provides processes for embossing one surface of a film and optionally texturing the other surface. Advantageously, the processes eliminate the step of separately forming a continuous sheet material and feeding the sheet material into a separate embossing apparatus, which is a significant reduction in cost. Significant reductions in process times can also be achieved by directly extruding the flowable melt into the embossing apparatus. In this manner, the processing speeds for the embossing process may be optimized to more closely match typical extrusion speeds. Moreover, by maintaining the embossing tool at a temperature greater than the glass transition temperature of the resin and the backside roll at a temperature less than the glass transition temperature, the embossed pattern is accurately reproduced with minimal shrinkage and distortion effects. The processes can be practiced with or without a carrier film. In one embodiment, utilizing the carrier film provides the user with control over the surface texture of the non-embossed surface. Still further, the process provided by the present invention can advantageously be used for permanently attaching a backing film to an embossed film. In these processes, the flowable melt can be used to partially fill or completely fill the embossed pattern.
The method of the present invention is further illustrated by the following example using the apparatus shown in
While the invention has been described with reference to an exemplary embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims.
This application is a continuation-in-part of application Ser. No. 10/635,065, filed Aug. 5, 2003. This application claims priority to and benefit from the foregoing disclosure.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10635065 | Aug 2003 | US |
| Child | 11671764 | Feb 2007 | US |