Patent Grant
10138183
This invention relates to a composition comprising quinone methides useful for stabilizing cyclopentadiene compounds such as, for example, cyclopentadiene and dicyclopentadiene. It relates to a process for inhibiting the polymerization of cyclopentadiene compounds. Application may be possible in all process streams comprising cyclopentadiene compounds.
Cyclopentadiene (=CPD) is a very reactive molecule which dimerizes to dicyclopentadiene (=DCPD) even at low temperatures, via a Diels-Alder reaction. For this reason the dimeric form is also the commercially available form of cyclopentadiene. The monomer can be restored by a retro-Diels-Alder reaction at high temperatures. The reversible dimerization of CPD to DCPD can thus be described as depicted hereinbelow in reaction equation <1> (the forward reaction from CPD to DCPD is the dimerization, which is preferential at low temperatures; the reverse reaction from DCPD to CPD is the cleavage, which is preferential at high temperatures, i.e. T>155° C.):
However, CDP and DCDP have a tendency to polymerize. This can be explained by various mechanisms. These include inter alia the possibility of further Diels-Alder reactions; on the other hand, free-radical polymerizations also take place. It is also possible to imagine mixed polymerization mechanisms. The Diels-Alder polymerization is shown in reaction equation <2>.
This high tendency for CPD and its compounds to polymerize can lead to a variety of problems in all (di)cyclopentadiene-containing process streams as well as with the specific production of cyclopentadiene monomer.
Cyclopentadiene compounds such as cyclopentadiene and dicyclopentadiene are thus present in some process streams, for example in pyrolysis gasoline, as secondary components, and can react with themselves or other vinyl-containing monomers in polymerization reactions. These undesired polymerization reactions occur particularly at high temperatures and can lead to deposits in the plants. The consequence of this is a reduced heat transfer and hence a reduced productivity. If the deposits lead to blockages, unscheduled cleaning of the plant has to be carried out, which leads to interruptions in the manufacturing operation. Every outage adds costs due to repair and cleaning, but in particular also due to the manufacturing outage itself. Avoidance of such outages is therefore a constant objective.
The described problems due to undesired polymerization occur not just in process streams comprising cyclopentadiene compounds as secondary compounds, but also and particularly in the production of cyclopentadiene itself. As previously noted, cyclopentadiene is obtained industrially by cleaving (“cracking”) dicyclopentadiene (in accordance with the high-T reverse reaction in the above reaction equation <1>). The cracking of dicyclopentadiene can take place not only in the liquid phase but also in the gas phase as described by Z. Cai, B. Shen, W. Liu, Z. Xin, and H. Ling (Energy & Fuels 2009, 23, 4077-4081). Particularly the liquid phase version of cracking is prone to the problem of oligomer deposits. Again, reduced heat transfer, reduced productivity and in the extreme case even blockage of plant components can occur, necessitating shutdowns and cleans. Temperatures of not less than 155° C. are needed to crack dicyclopentadiene to cyclopentadiene. These temperatures lead to the very rapid formation of cyclopentadiene oligomers and polymers, which raise the viscosity and thereby make stirring more difficult, and which form deposits and inhibit effective heat transfer, making the reaction more difficult to carry out and entailing yield losses.
Various strategies are described to control the formation of oligomers in the cracking of dicyclopentadiene. The most widely used option is to add an inert solvent as a bottoms diluent. Long-chain hydrocarbons are used for this in particular. The solvent does not prevent the polymerization, but slows it, by reducing the concentration of the reactive component. The advantage of such use of solvent is that the oligomers formed dissolve in the solvent and so do not form deposits, as a result of which the reaction mixture remains workable. Moreover, using a solvent can be used to shorten the period of thermal exposure. This advantage is described by Ammannati et al. (WO2010/020549). Diphenyl ether is used therein as inert solvent. Robota (DE1951320; GB1261565) describes a cracking process wherein a paraffinic hydrocarbon oil is employed as a solvent.
On the other hand, the employment of an inert solvent entails the disadvantage that a portion of the reactor volume is already occupied by the solvent, so the volume-time yield is reduced by the addition of a solvent.
Another conventionally known method to inhibit undesirable polymerizations is offered by the employment of polymerization inhibitors. This possibility is used particularly to inhibit polymerization in process streams comprising various, partly vinylic, monomers, but also DCPD and CPD.
The following classes of inhibitor have been described for this purpose: nitroxides such as TEMPO derivatives, phenyldiamines, hydroxylamines such as diethylhydroxylamine (abbreviated as “DEHA”), nitroaromatics such as 4,6-dinitro-2-sec-butylphenol (abbreviated as “DNBP”), diphenols such as hydroquinone (abbreviated as “HQ”) and p-tert-butylcatechol (abbreviated as “TBC”).
Buccolini et al. (WO2001/047844) describe using a combination of nitroxide compounds, in particular TEMPO derivatives and aromatic amines, in particular diphenylamines and phenylenediamines, to inhibit polymerization reactions in hydrocarbon streams. These hydrocarbon streams comprise butadiene and styrene, but may also comprise cyclopentadiene.
Kazuo et al. (JP62167733A & JP62167734A) describe the admixture of hydroxylamines and TEMPO derivatives, respectively, to a reaction mixture, for example of cyclopentadiene and dicyclopentadiene with 1,3-butadiene, to prevent secondary polymerization reactions.
Ammannati et al. (WO2010/020549) describe a process for producing ethylidenenorbornenes wherein dicyclopentadiene is converted into cyclopentadiene in a first step. Various inert solvents can be used here, for example diphenyl ether, diphenylmethane, decalin or a mixture of di- and triaryl ethers. Polymerization inhibitors such as, for example, 4-oxo-2,2,6,6-tetramethylpiperidine N-oxide (abbreviated as “4-oxo-TEMPO”) and also tert-butylhydroquinone are additionally used.
Cai et al. (Z. Cai, B. Shen, W. Liu, Z. Xin, H. Ling, Energy & Fuels 2009, 23, 4077-4081) describe o-nitrophenol, TBC and DEHA as possible inhibitors. A 3:1 mixture (by weight) of TBC and DEHA is referred to as particularly advantageous.
Cheng et al. (CN101798255) describe polymerization inhibitors useful for removing diolefins from the C5 fraction in a cracking process, specifically in the extraction of 1,3-pentadiene. Sodium nitrite, TBC, DEHA and o-nitrophenol are mentioned as possible polymerization inhibitors.
Ge et al. (CN101104573) describe a process for separating isoprene and cyclopentadiene wherein polymerization inhibitors are employed. The inhibitors employed can be one or more substances selected from o-nitrophenol, TBC, DEHA and dihydroxydihydrocinnamic acid.
Chen et al. (CN102060649) describe a process for producing cyclopentadiene wherein HQ, 2,6-dinitrocresol and/or TBC or phenothiazine (abbreviated as “PTZ”) are employed.
Hu et al. (CN1253130) describe a process for removing diolefins from a C5 stream wherein DEHA, TBC or o-nitrophenol can be used as stabilizers.
Lartigue-Peyrou et al. (WO1999/015603) describe mixtures of catechol derivatives and aromatic ethers useful for stabilizing unsaturated compounds, including cyclopentadiene and dicyclopentadiene.
Cocuta et al. (RO93489) describe mixtures of sec-butylphenols and phenylenediamines/tert-butylcatechols capable of inhibiting the polymerization of olefins and diolefins.
However, experiments employing pure cyclopentadiene surprisingly show that most of the conventionally known inhibitors which have also been used inter alia for application in the presence of cyclopentadiene have little if any efficacy when used to prevent the polymerization of cyclopentadiene (see Comparative Examples 1 to 6). This applies for example to the substances described in WO2010/020549, WO2001/047844 and JP62167734, which are efficacious as inhibitors for the polymerization reactions of monomers such as butadiene or styrene (see Comparative Examples 13 to 16). As shown in Comparative Examples 1 to 6, however, these substances fail when used for inhibiting the polymerization of cyclopentadiene. DNBP, for example, was found to have no effect with regard to the polymerization of cyclopentadiene. The TEMPO derivatives likewise have only minimal efficacy.
It was accordingly surprisingly found that conventional inhibitors are not very suitable for preventing the polymerization in CPD or DCPD-containing process streams and are mainly or even exclusively effective as inhibitors of free-radical polymerizations observed with vinyl-containing monomers. The fact that certain substances have been described as generally useful for stabilizing olefinically unsaturated monomers cannot be used, therefore to infer their usefulness for inhibiting the polymerization of cyclopentadiene, dicyclopentadiene or other cyclopentadiene compounds.
It is an object of the present invention to provide a polymerization inhibitor having good activity against undesired polymerizations of dicyclopentadiene and cyclopentadiene. The inhibitor should also work at high to very high temperatures and exhibit an improved performance over the inhibitors previously conventionally employed.
It has now been found that this object is achieved, utterly surprisingly, by the employment of certain quinone methides [hereinbelow “Compound of structure (I)”]. They have outstanding inhibitory properties with regard to the polymerization of CPD and DCPD, which is surprising in itself because they have hitherto merely been described for inhibiting the polymerization of vinylic monomers (EP2055691A1; EP0737659A1; EP0737660A1, WO2012/173909). It is further surprising that the inhibitory effect of the quinone methides according to the invention is superior to that of the conventionally known CPD and DCPD polymerization inhibitors. The quinone methides according to the invention may be used neat as well as in diluted form. The cyclopentadiene compound can be in pure form or as a component in a process stream.
The invention relates to a composition (AB) comprising (A) and (B), a process for inhibiting the polymerization of (B) which is characterized in that (A) and (B) are brought into contact, and also to the use of (A) for inhibiting the polymerization of (B), wherein
(A) is at least one compound of structure (I)
where
(B) is at least one cyclopentadiene compound.
Exact experimental descriptions are found in the Examples section.
General Terms
Throughout this description all ranges described include all values and sub-ranges therein, unless otherwise specified.
Additionally, the indefinite article “a” or “an” carries the meaning of “one or more” throughout the description, unless otherwise specified.
The term “cyclopentadiene compound” for the purposes of the present invention describes a compound selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
Cyclopentadiene (CPD) has structure (II).
Dicyclopentadiene (DCPD) has structure (Ill) and possesses two isomeric forms, endo-dicyclopentadiene (endo-DCPD) and exo-dicyclopentadiene (exo-DCPD).
The term “(di)cyclopentadiene” for the purposes of the present invention refers to mixtures of CPD and DCPD.
The expression “polymerization of (B)” describes any polymerization involving (B), preferably an oligomerization/polymerization with itself or vinylic structures.
The term “alkylated cyclopentadiene” for the purposes of the present invention describes compounds of structure (IV).
where, in the compound of structure (IV), at least one of R15, R16, R17, R18, R19, R20 is alkyl having 1 to 18 carbon atoms while the others are each hydrogen. In one preferred embodiment, “alkylated cyclopentadiene” is monoalkylcyclopentadiene or dialkylcyclopentadiene, more preferably monoalkylcyclopentadiene.
The term “monoalkylcyclopentadiene” for the purposes of the present invention describes the compounds of structure (IV) where precisely one of R15, R16, R17, R18, R19, R20 is alkyl having 1 to 18 carbon atoms, preferably alkyl having 1 to 6 carbon atoms, more preferably methyl or ethyl, most preferably methyl, while the others are each hydrogen.
The term “dialkylcyclopentadiene” for the purposes of the present invention describes the compounds of structure (IV) where precisely two of R15, R16, R17, R18, R19, R20 are each independently alkyl of 1 to 18 carbon atoms, preferably alkyl of 1 to 6 carbon atoms, more preferably methyl or ethyl, most preferably methyl, while the others are each hydrogen.
The term “alkylated dicyclopentadiene” for the purposes of the present invention describes any molecule of structure (III) where at least one hydrogen is replaced by alkyl of 1 to 18 carbon atoms, preferably by alkyl of 1 to 6 carbon atoms, more preferably by methyl or ethyl.
The term “alkylated dicyclopentadiene” for the purposes of the present invention describes in one very particularly preferred embodiment any molecule of structure (111) where precisely one hydrogen, precisely two hydrogens, precisely three hydrogens or precisely four hydrogens is/are replaced by alkyl of 1 to 6 carbon atoms, more preferably by methyl or ethyl.
Alkyl of 1 to 18 carbon atoms has for the purposes of the present invention between 1 and 18 saturated carbon atoms and may be linear or branched and may be more particularly selected from methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, iso-butyl, tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1,1-dimethyl propyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, 1-ethylpropyl, n-hexyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, 4-methylpentyl, 1,1-dimethylbutyl, 1,2-dimethylbutyl, 1,3-dimethylbutyl, 2,2-dimethylbutyl, 2,3-dimethylbutyl, 3,3-dimethylbutyl, 1-ethylbutyl, 2-ethylbutyl, 1,1,2-trimethylpropyl, 1,2,2-trimethylpropyl, 1-ethyl-1-methylpropyl, 1-ethyl-2-methylpropyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl. Alkyl of 1 to 12 carbon atoms has for the purposes of the present invention between 1 and 12 saturated carbon atoms and may be linear or branched and may be more particularly selected from methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, iso-butyl, tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, 1-ethylpropyl, n-hexyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, 4-methylpentyl, 1,1-dimethylbutyl, 1,2-dimethylbutyl, 1,3-dimethylbutyl, 2,2-dimethylbutyl, 2,3-dimethylbutyl, 3,3-dimethylbutyl, 1-ethylbutyl, 2-ethylbutyl, 1,1,2-trimethylpropyl, 1,2,2-trimethylpropyl, 1-ethyl-1-methylpropyl, 1-ethyl-2-methylpropyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl.
Alkyl of 1 to 6 carbon atoms has for the purposes of the present invention between 1 and 6 saturated carbon atoms and may be linear or branched and may be more particularly selected from methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, iso-butyl, tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, 1-ethylpropyl, n-hexyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, 4-methylpentyl, 1,1-dimethylbutyl, 1,2-dimethylbutyl, 1,3-dimethylbutyl, 2,2-dimethylbutyl, 2,3-dimethylbutyl, 3,3-dimethylbutyl, 1-ethylbutyl, 2-ethylbutyl, 1,1,2-trimethylpropyl, 1,2,2-trimethylpropyl, 1-ethyl-1-methylpropyl, 1-ethyl-2-methylpropyl.
Alkyl of 1 to 4 carbon atoms has for the purposes of the present invention between 1 and 4 saturated carbon atoms and may be linear or branched and may be more particularly selected from methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, iso-butyl, tert-butyl.
Alkyl of 1 to 3 carbon atoms has for the purposes of the present invention between 1 and 3 saturated carbon atoms and may be linear or branched and may be more particularly selected from methyl, ethyl, n-propyl, iso-propyl.
Cycloalkyl of 3 to 15 carbon atoms is for the purposes of the present invention more particularly selected from cyclopropyl, cyclobutyl, cyclopropylmethyl, cyclopentyl, cyclobutylmethyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl, cyclododecyl, cyclotridecyl, cyclotetradecyl, cyclopentadecyl.
Cycloalkyl of 3 to 12 carbon atoms is for the purposes of the present invention more particularly selected from cyclopropyl, cyclobutyl, cyclopropylmethyl, cyclopentyl, cyclobutylmethyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl, cyclododecyl.
Aryl of 6 to 15 carbon atoms is more particularly selected from phenyl, 1-naphthyl, 2-naphthyl, 9-anthryl, 9-phenanthryl.
Aryl of 6 to 10 carbon atoms is for the purposes of the present invention more particularly selected from phenyl, 1-naphthyl, 2-naphthyl.
Phenylalkyl of 7 to 15 carbon atoms comprises for the purposes of the present invention branched or unbranched alkyl with an attached phenyl ring, and is more particularly selected from benzyl, phenylethyl, α-methylbenzyl, 3-phenylpropyl, phenyl-2-methylethyl, phenyl-1-methylethyl, α,α-dimethylbenzyl, butylphenyl, hexylphenyl, octylphenyl, nonyiphenyl, preferably benzyl.
Alkylamino of 1 to 4 carbon atoms for the purposes of the present invention refers more particularly to an amino moiety comprising an alkyl group of 1 to 4 carbon atoms, and is preferably selected from methylamino, ethylamino, propylamino, isopropylamino and butylamino.
Dialkylamino for the purposes of the present invention is more particularly an amino moiety which bears two alkyl groups, and is more particularly dialkylamino of 2 to 8 carbon atoms.
Dialkylamino of 2 to 8 carbon atoms for the purposes of the present invention refers more particularly to an amino moiety comprising two alkyl groups of 1 to 4 carbon atoms, wherein these alkyl groups of 1 to 4 carbon atoms can be the same or different, and is preferably selected from dimethylamino, diethylamino, dipropylamino, dibutylamino, methylethylamino and methylbutylamino.
“High-boiling hydrocarbon cuts” for the purposes of the present invention denotes aliphatic or aromatic hydrocarbon cuts having fixed boiling ranges, in particular aromatic hydrocarbons having a boiling point (at atmospheric pressure) in the range from 155° C. to 300° C., these preferably contain one or more substances selected from the group consisting of n-propylbenzene, 1-methyl-4-ethylbenzene, 1-methyl-3-ethylbenzene, mesitylene, 1-methyl-2-ethylbenzene, 1,2,4-trimethylbenzene, 1,2,3-trimethylbenzene, indane, 1,3-diethylbenzene, 1-methyl-4-propylbenzene, 1-methyl-3-propylbenzene, 1,2,4,5-tetramethylbenzene, 1,2,3,5-tetramethylbenzene and naphthalene.
Process According to the Invention
The expression “process according to the invention” is synonymous with “process for inhibiting the polymerization of (B)”.
The invention provides a process for inhibiting the polymerization of (B), said process being characterized in that (A) and (B) are brought into contact, wherein
(A) is at least one compound of structure (I)
(B) is at least one cyclopentadiene compound.
In one preferred embodiment of the process according to the invention, R1 and R2 in the compound of structure (I) are each independently selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl and tert-butyl; and
In one more preferred embodiment of the process according to the invention, R1 and R2 are each independently selected from the group consisting of methyl and tert-butyl in the compound of structure (I); and R3 is —CN, —COOH, —COOR4, —S—R11, —R12, —C≡C—R13 or halogen; wherein
In one still more preferred embodiment of the process according to the invention R1 and R2 are each tert-butyl in the compound of structure (I); and
In a first very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is CN, the compound of structure (I) then having structure (V) (hereinafter also abbreviated as “QM-1”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a second very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is phenyl, the compound of structure (I) then having structure (VI) (hereinafter also abbreviated as “QM-2”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a third very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is 3,5-di-tert-butyl-4-hydroxyphenyl, the compound of structure (I) then having structure (VII) (hereinafter also abbreviated as “QM-3”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fourth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is 2-furyl, the compound of structure (I) then having structure (VIII) (hereinafter also abbreviated as “QM-4”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fifth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OR10, wherein
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a sixth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH3, the compound of structure (I) then having structure (X) (hereinafter also abbreviated as “QM-5”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a seventh very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH3, the compound of structure (I) then having structure (XI) (hereinafter also abbreviated as “QM-6”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In an eighth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH3, the compound of structure (I) then having structure (XII) (hereinafter also abbreviated as “QM-7”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a ninth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH(CH3)2, the compound of structure (I) then having structure (XIII) (hereinafter also abbreviated as “QM-8.”
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a tenth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH3, the compound of structure (I) then having structure (XIV) (hereinafter also abbreviated as “QM-9”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In an eleventh very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH2CH3, the compound of structure (I) then having structure (XV) (hereinafter also abbreviated as “QM-10”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a twelfth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH2CH2CH3, the compound of structure (I) then having structure (XVI) (hereinafter abbreviated as “QM-11”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a thirteenth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —C≡C-phenyl, the compound of structure (I) then having structure (XVII) (hereinafter abbreviated as “QM-12”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fourteenth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —COOH, the compound of structure (I) then having structure (XVIII) (hereinafter abbreviated as “QM-13”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fifteenth very particularly preferred embodiment of the process according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —SCH2CH2CH2CH3, the compound of structure (I) then having structure (XIX) (hereinafter abbreviated as “QM-14”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
(A) may be used in the process according to the invention in gaseous form, as a solid material (as a powder, for example) or as a liquid, in particular as a solid material (as a powder, for example) or as a liquid, preferably as a liquid. (A) used as a liquid in the process according to the invention is more particularly used as a melt or in the form of a solution in (C), where “(C)” has the meaning “at least one solvent”.
Any material may be useful as a solvent in the process according to the invention provided (A) is soluble therein in the desired concentration range and it is both compatible with (A) and does not have a disruptive effect on the process according to the invention, and may be an apolar solvent, preferably an apolar aromatic or aliphatic solvent. It may be more preferable for the solvent in the process according to the invention to be selected from the group consisting of benzene, mono- or polyalkylated aromatics, alkanes having a carbon number of 6 to 15, cycloalkanes having a carbon number of 6 to 15, high-boiling hydrocarbon cuts, ethers having a carbon number of 6 to 15 and esters having a carbon number of 6 to 15. It may be still more preferable for the solvent in the process according to the invention to be selected from the group consisting of benzene, toluene, ethylbenzene, xylene, styrene and high-boiling aromatic hydrocarbon cuts. It may be particularly preferable for the solvent in the process according to the invention to be selected from the group consisting of toluene, ethylbenzene, xylene and styrene. Alternatively, the cyclopentadiene compound itself can also serve as the solvent in the process according to the invention.
When (A) is used in the process according to the invention in the form of a solution in (C), the total weight of all compounds of structure (I) in said solution (AC) preferably has an (m/m) ratio to the total weight of all solvents in said solution (AC) in the range from 1:1000 to 100:1, more preferably in the range from 1:100 to 10:1 and still more preferably in the range from 1:10 to 3:1.
(B) may be present in the process according to the invention in gaseous form, as a liquid or as a solid material, in particular in gaseous form or as a liquid, preferably as a liquid. (B) as a liquid is still more preferably in the form of a melt or solution. It may be particularly preferable for (B) to be in the form of a solution. Such a solution in a first very particularly preferred embodiment is a process stream as obtained in cracking processes. (B) may typically be present in such a process stream at from 0.0001 wt % to 15 wt %.
In an alternative second very particularly preferred embodiment, the solution may be a process stream as generated in the production of DCPD and/or CPD itself. (B) is typically present in such a process stream at between 15 and 100 wt %, preferably between 70 and 100 wt % and still more preferably between 70 and 99.99 wt %.
The expression “bringing (A) and (B) into contact” for the purposes of the invention is to be understood as meaning in particular that (A) is admixed to (B) or (B) is admixed to (A). Admixing (A) to (B) or (B) to (A) can be effected according to conventionally known methods.
(A) may be admixed with advantage in the process according to the invention into any feedstream or outflow line of a distillation column, into the in- and outflow line of a heat exchanger or into the in- and outflow line of a vaporizer (“reboiler”) or into the in- and outflow line of a condenser or into the in- and outflow line of a reactor. (A) may also be added in the process according to the invention to storage tanks containing a process stream comprising (B). (A) may be admixed to (B) not only before but also during a process, for example a production or purification process.
An effective amount of (A) is admixed in the process according to the invention. The term “effective amount of (A)” in the context of this invention may be understood as meaning the amount of (A) needed to delay/prevent the undesired polymerization of (B). This effective amount depends on the conditions under which the cyclopentadiene compound, or mixture of two or more cyclopentadiene compounds, is stored or handled and can readily be determined from case to case by a person skilled in the art. For example, the cracking of dicyclopentadiene requires by reason of the higher temperatures a higher amount of (A) than the storing of (B) at for instance room temperature.
(A) may preferably be used in the process according to the invention in such an amount that the total concentration of all compounds of structure (I) is between 10 ppb on a mass to mass basis (m/m) and 100,000 ppm (m/m), more preferably between 1 ppm (m/m) and 50,000 ppm (m/m), even more preferably between 10 ppm and 10,000 ppm (m/m), most preferably between 100 ppm and 5000 ppm (m/m), each based on the total weight of all cyclopentadiene compounds.
The temperature at which the process according to the invention may be carried out is not subject to any in-principle limitation; on the contrary, it is a feature of the present invention that the process according to the invention can be carried out not only at low but also at high temperatures, in particular in the range from 0° C. to 250° C., preferably 0° C. to 200° C.
The process according to the invention may utilize a polymerization inhibitor (D) as well as (A). Polymerization inhibitors of this type are conventionally known, examples being nitroxides such as, for instance, oxo-TEMPO or 4-hydroxy-TEMPO, phenylenediamines, hydroxylamines such as diethylhydroxylamine (DEHA), nitro- or nitrosoaromatics such as DNBP, (di)phenols such as hydroquinone, TBC or 2,6-di-tert-butylphenol, benzoquinones, phenothiazines such as PTZ.
Composition According to the Invention
The invention also provides a composition (AB), comprising (A) and (B),
wherein
In one preferred embodiment of the composition (AB) according to the invention, R1 and R2 in the compound of structure (I) are each independently selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl and tert-butyl; and R3 is —CN, —COOH, —COOR4, —COR5, —OCOR6, —CONR7R8, —PO(OR9)2, —O—R10, —S—R11, —R12—C≡C—R13 or halogen;
In one more preferred embodiment of the composition (AB) according to the invention, R1 and R2 in the compound of structure (I) are each independently selected from the group consisting of methyl and tert-butyl; and
In one still more preferred embodiment of the composition (AB) according to the invention, R1 and R2 are each tert-butyl in the compound of structure (I); and R3 is —CN, —COOH, —O—R10, s-R11, —R12 or —C≡C—R13;
In a first very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is CN, the compound of structure (I) then having structure (V) (hereinafter also abbreviated as “QM-1”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a second very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is phenyl, the compound of structure (I) then having structure (VI) (hereinafter also abbreviated as “QM-2”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a third very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is 3,5-di-tert-butyl-4-hydroxyphenyl, the compound of structure (I) then having structure (VII) (hereinafter also abbreviated as “QM-3”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fourth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is 2-fu the compound of structure (I) then having structure (VIII) (hereinafter also abbreviated as “QM-4”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fifth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OR10, wherein R10 is methyl, ethyl, iso-propyl, n-propyl, n-butyl, sec-butyl, iso-butyl, tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, 1-ethylpropyl, n-hexyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, 4-methylpentyl, 1,1-dimethylbutyl, 1,2-dimethylbutyl, 1,3-dimethylbutyl, 2,2-dimethylbutyl, 2,3-dimethylbutyl, 3,3-dimethylbutyl, 1-ethylbutyl, 2-ethylbutyl, 1,1,2-trimethylpropyl, 1,2,2-trimethylpropyl, 1-ethyl-1-methylpropyl or 1-ethyl-2-methylpropyl, preferably methyl, ethyl, iso-propyl, n-propyl, n-butyl, sec-butyl, tert-butyl, n-pentyl or n-hexyl, more preferably methyl, ethyl, n-propyl, iso-propyl, n-butyl, n-pentyl or n-hexyl;
the compound of structure (I) then having structure (IX)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a sixth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH3, the compound of structure (I) then having structure (X) (hereinafter also abbreviated as “QM-5”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a seventh very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (1) has R1 and R2 being tert-butyl and R3 is —OCH2CH3, the compound of structure (I) then having structure (XI) (hereinafter also abbreviated as “QM-6”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In an eighth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH3, the compound of structure (I) then having structure (XII) (hereinafter also abbreviated as “QM-7”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a ninth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH(CH3)2, the compound of structure (I) then having structure (XIII) (hereinafter also abbreviated as “QM-8”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a tenth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH3, the compound of structure (I) then having structure (XIV) (hereinafter also abbreviated as “QM-9”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In an eleventh very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH2CH3, the compound of structure (I) then having structure (XV) (hereinafter also abbreviated as “QM-10”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a twelfth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH2CH2CH3, the compound of structure (I) then having structure (XVI) (hereinafter abbreviated as “QM-11”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a thirteenth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure has (I) has R1 and R2 being tert-butyl and R3 is —C≡C-phenyl, the compound of structure (I) then having structure (XVII) (hereinafter abbreviated as “QM-12”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fourteenth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —COOH, the compound of structure (I) then having structure (XVIII) (hereinafter abbreviated as “QM-13”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fifteenth very particularly preferred embodiment of the composition (AB) according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —SCH2CH2CH2CH3, the compound of structure (I) then having structure (XIX) (hereinafter abbreviated as “QM-14”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In composition (AB) according to the invention, the total concentration of all compounds of structure (I) in said composition (AB) may preferably be between 10 ppb (m/m) and 100,000 ppm (m/m), more preferably between 1 ppm (m/m) and 50,000 ppm (m/m), even more preferably between 10 ppm and 10,000 ppm (m/m), most preferably between 100 ppm and 5000 ppm (m/m), each based on the total weight of all cyclopentadiene compounds in said composition (AB).
Composition (AB) according to the invention in a further preferred embodiment may additionally also comprise (C), where “(C)” has the meaning “at least one solvent”.
Any material may be useful as a solvent in the composition (AB) according to the invention provided (A) is soluble therein in the desired concentration range and it is both compatible with (A) and does not have a disruptive effect on the process according to the invention, and is in particular an apolar solvent, preferably an apolar aromatic or aliphatic solvent. It is more preferable for the solvent in the composition (AB) according to the invention to be selected from the group consisting of benzene, mono- or polyalkylated aromatics, alkanes having a carbon number of 6 to 15, cycloalkanes having a carbon number of 6 to 15, high-boiling hydrocarbon cuts, ethers having a carbon number of 6 to 15 and esters having a carbon number of 6 to 15. It is still more preferable for the solvent in the composition (AB) according to the invention to be selected from the group consisting of benzene, toluene, ethylbenzene, xylene, styrene and high-boiling aromatic hydrocarbon cuts. It is particularly preferable for the solvent in the composition (AB) according to the invention to be selected from the group consisting of toluene, ethylbenzene, xylene and styrene. Alternatively, the cyclopentadiene compound itself may also serve as solvent in the composition (AB) according to the invention.
When composition (AB) according to the invention also comprises (C), the (m/m) ratio of the total weight of all compounds of structure (I) which are comprised by composition (AB) to the total weight of all solvents comprised by composition (AB) in composition (AB) may preferably be in the range from 1:1000 to 100:1, more preferably in the range from 1:100 to 10:1 and still more preferably in the range from 1:10 to 3:1.
Use According to the Invention
The expression “use according to the invention” is synonymous with “use of (A) for inhibiting the polymerization of (B)”.
The invention also provides for the use of (A) for inhibiting the polymerization of (B), wherein
(A) is at least one compound of structure (I)
wherein
In one preferred embodiment of the use according to the invention, R1 and R2 in the compound of structure (I) are each independently selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl and tert-butyl; and R3 is —CN, —COOH, —COOR4, —COR5, —OCOR6, —CONR7R8, —PO(OR9)2, —O—R10, —S—R11, —R12—C≡C—R13 or halogen;
In one more preferred embodiment of the use according to the invention, R1 and R2 in the compound of structure (I) are each independently selected from the group consisting of methyl and tert-butyl; and
R3 is —CN, —COOH, —COOR4, —S—R11, —R12, —C≡C—R13 or halogen;
In one still more preferred embodiment of the use according to the invention, R1 and R2 are each tert-butyl in the compound of structure (I); and R3 is —CN, —COOH, —O—R10, —S—R11, —R12 or —C≡C—R13;
In a first very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is CN, the compound of structure (I) then having structure (V) (hereinafter also abbreviated as “QM-1”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a second very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is phenyl, the compound of structure (I) then having structure (VI) (hereinafter also abbreviated as “QM-2”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a third very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is 3,5-di-tert-butyl-4-hydroxyphenyl, the compound of structure (I) then having structure (VII) (hereinafter also abbreviated as “QM-3”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fourth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is 2-furyl, the compound of structure (I) then having structure (VIII) (hereinafter also abbreviated as “QM-4”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fifth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OR10, where R10 is methyl, ethyl, iso-propyl, n-propyl, n-butyl, sec-butyl, iso-butyl, tert-butyl, n-pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, 1-ethylpropyl, n-hexyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, 4-methylpentyl, 1,1-dimethylbutyl, 1,2-dimethylbutyl, 1,3-dimethylbutyl, 2,2-dimethylbutyl, 2,3-dimethylbutyl, 3,3-dimethylbutyl, 1-ethylbutyl, 2-ethylbutyl, 1,1,2-trimethylpropyl, 1,2,2-trimethylpropyl, 1-ethyl-1-methylpropyl or 1-ethyl-2-methylpropyl, preferably methyl, ethyl, iso-propyl, n-propyl, n-butyl, sec-butyl, tert-butyl, n-pentyl or n-hexyl, more preferably methyl, ethyl, n-propyl, iso-propyl, n-butyl, n-pentyl or n-hexyl;
the compound of structure (I) then having structure (IX)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a sixth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3=—OCH3, the compound of structure (I) then having structure (X) (hereinafter also abbreviated as “QM-5”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a seventh very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH3, the compound of structure (I) then having structure (XI) (hereinafter also abbreviated as “QM-6”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In an eighth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH3, the compound of structure (I) then having structure (XII) (hereinafter also abbreviated as “QM-7”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a ninth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH(CH3)2, the compound of structure (I) then having structure (XIII) (hereinafter also abbreviated as “QM-8”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a tenth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH3, the compound of structure (I) then having structure (XIV) (hereinafter also abbreviated as “QM-9”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In an eleventh very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH2CH3, the compound of structure (I) then having structure (XV) (hereinafter also abbreviated as “QM-10”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a twelfth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —OCH2CH2CH2CH2CH2CH3, the compound of structure (I) then having structure (XVI) (hereinafter abbreviated as “QM-11”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a thirteenth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —C≡C-phenyl, the compound of structure (I) then having structure (XVII) (hereinafter abbreviated as “QM-12”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fourteenth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —COOH, the compound of structure (I) then having structure (XVIII) (hereinafter abbreviated as “QM-13”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
In a fifteenth very particularly preferred embodiment of the use according to the invention, the compound of structure (I) has R1 and R2 being tert-butyl and R3 is —SCH2CH2CH2CH3, the compound of structure (I) then having structure (XIX) (hereinafter abbreviated as “QM-14”)
and the cyclopentadiene compound is selected from the group consisting of cyclopentadiene, dicyclopentadiene, alkylated cyclopentadiene and alkylated dicyclopentadiene, more preferably selected from the group consisting of cyclopentadiene and dicyclopentadiene.
(A) may be used in the use according to the invention in gaseous form, as a solid material (as a powder, for example) or as a liquid, in particular as a solid material (as a powder, for example) or as a liquid, preferably as a liquid. (A) used as a liquid in the use according to the invention is more particularly used as a melt or in the form of a solution in (C), where “(C)” has the meaning “at least one solvent”.
Any material may be useful as a solvent in the use according to the invention provided (A) is soluble therein in the desired concentration range and it is both compatible with (A) and does not have a disruptive effect on the use according to the invention, and is in particular an apolar solvent, preferably an apolar aromatic or aliphatic solvent. It is more preferable for the solvent in the use according to the invention to be selected from the group consisting of benzene, mono- or polyalkylated aromatics, alkanes having a carbon number of 6 to 15, cycloalkanes having a carbon number of 6 to 15, ethers having a carbon number of 6 to 15, high-boiling hydrocarbon cuts and esters having a carbon number of 6 to 15. It is still more preferable for the solvent in the use according to the invention to be selected from the group consisting of benzene, toluene, ethylbenzene, xylene, styrene and high-boiling aromatic hydrocarbon cuts. It is particularly preferable for the solvent in the use according to the invention to be selected from the group consisting of toluene, ethylbenzene, xylene and styrene. Alternatively, the cyclopentadiene compound itself can also serve as solvent in the use according to the invention.
When (A) is used in the use according to the invention in the form of a solution in (C), the total weight of all compounds of structure (I) in solution (AC) preferably has an (m/m) ratio to the total weight of all solvents in solution (AC) in the range from 1:1000 to 100:1, more preferably in the range from 1:100 to 10:1 and still more preferably in the range from 1:10 to 3:1.
(B) may be present in the use according to the invention in gaseous form, as a liquid or as a solid material, in particular in gaseous form or as a liquid, preferably as a liquid. (B) as a liquid is still more preferably in the form of a melt or solution. It is particularly preferable for (B) to be in the form of a solution. Such a solution in a first very particularly preferred embodiment of the use according to the invention is a process stream as obtained in cracking processes. (B) is typically present in such a process stream at from 0.0001 wt % to 15 wt %.
In an alternative second very particularly preferred embodiment of the use according to the invention, the solution may be a process stream as generated in the production of DCPD and/or CPD itself. (B) is typically present in such a process stream at between 15 and 100 wt %, preferably between 70 and 100 wt % and still more preferably between 70 and 99.99 wt %.
The use according to the invention typically comprises bringing (A) and (B) into contact, which for the purposes of the invention is to be understood as meaning in particular that (A) is admixed to (B) or (B) is admixed to (A).
Admixing (A) to (B) or (B) to (A) can be conducted according to conventionally known methods.
(A) can be admixed with advantage in the use according to the invention into any feedstream or outflow line of a distillation column, into the in- and outflow line of a heat exchanger or into the in- and outflow line of a vaporizer (“reboiler”) or into the in- and outflow line of a condenser or into the in- and outflow line of a reactor. (A) can also be added in the use according to the invention to storage tanks containing a process stream comprising (B). (A) can be admixed to (B) not only before but also during a process, for example a production or purification process.
An effective amount of (A) is admixed in the use according to the invention. The term “effective amount of (A)” in the context of this invention is to be understood as meaning the amount of (A) needed to delay/prevent the undesired polymerization of (B). This effective amount depends on the conditions under which the cyclopentadiene compound, or mixture of two or more cyclopentadiene compounds, is stored or handled and may readily be determined from case to case by a person skilled in the art. For example, the cracking of dicyclopentadiene requires by reason of the higher temperatures a higher amount of (A) than the storing of (B) at for instance room temperature.
(A) is preferably used in the use according to the invention in such an amount that the total concentration of all compounds of structure (I) is between 10 ppb (m/m) and 100,000 ppm (m/m), more preferably between 1 ppm (m/m) and 50,000 ppm (m/m), even more preferably between 10 ppm and 10 000 ppm (m/m) most preferably between 100 ppm and 5000 ppm (m/m), each based on the total weight of all cyclopentadiene compounds.
The temperature at which the use according to the invention can be carried out is not subject to any in-principle limitation; on the contrary, it is a feature of the present invention that the use according to the invention can be carried out not only at low but also at high temperatures, in particular in the range from 0° C. to 250° C., preferably 0° C. to 200° C.
The use according to the invention may utilize a polymerization inhibitor (D) as well as (A). Polymerization inhibitors of this type are conventionally known, examples being nitroxides such as, for instance, oxo-TEMPO or 4-hydroxy-TEMPO, phenylenediamines, hydroxylamines such as diethylhydroxylamine (DEHA), nitro- or nitrosoaromatics such as DNBP, (di)phenols such as hydroquinone, TBC or 2,6-di-tert-butylphenol, benzoquinones, phenothiazines such as PTZ.
Having generally described this invention, a further understanding can be obtained by reference to certain specific examples, which are provided herein for purposes of illustration only, and are not intended to be limiting unless otherwise specified.
The examples which follow shall further elucidate the invention without the invention being limited to these embodiments.
General Description—Screening Test; Examples 1-11
The following apparatus was set up: A 250 mL multi-neck flask was fitted with a reflux condenser, a nitrogen supply and a sampler.
A 100 g quantity of dicyclopentadiene (purity: 98%) was melted and weighed into the 250 mL flask.
Nitrogen was passed over the dicyclopentadiene, and 50 mg (500 ppm) of the in-test inhibitor shown in Table 1 are added.
While the flow of nitrogen over the dicyclopentadiene was continued, the flask was immersed in a preheated oil bath at 170° C. As the flask was immersed, the reaction started.
Beginning with the immersion of the flask, 0.5-1 mL samples were taken every 30 minutes with a glass syringe. The samples were diluted in a 1:9 weight ratio in ethylbenzene and measured using an evaporative light scattering (ELS) detector.
The ELS detector (Polymerlabs; model: PL-ELS 1000) was connected to an HPLC system which was operated without separation column. Ethylbenzene was used as the mobile phase at a flow rate of 1 mL/min. The injection volume of the diluted sample is 20 μL.
The ELS detector was set to the following parameters:
The peak area detected was a measure of the oligomer/polymer content of the sample. The oligomer/polymer contents determined are not absolute. The peak area was proportional to the oligomer/polymer content in the measured region, so the results of the various inhibitors are comparable.
The results after 120 min and 240 min are summarized below in Table 1—and all measured values are depicted in graphical form in
Example 1 is the blank (without admixture of an inhibitor). Examples 2 to 6 are comparative examples, not in accordance with the invention, which were carried out with conventionally known cyclopentadiene polymerization inhibitors 4-hydroxy-TEMPO (4-HT; Example 2), 4-butoxy-TEMPO (4-BT; Example 3), tert-butylcatechol (TBC; Example 4) and dinitro-sec-butylphenol (DNBP; Example 5), hydroquinone monomethyl ether (MeHQ; Example 6). Examples 7 to 11 are examples in accordance with the invention which were carried out with the compounds QM-1 (Example 7), QM-2 (Example 8), QM-5 (Example 9), QM-7 (Example 10) and QM-11 (Example 11).
Results Regarding Examples 1-11:
The curve slopes up continuously over the measurement period of 4 hours, i.e. the polymer content increased continuously. Peak area was 1100 when measured after two hours, slightly more than doubling to 2300 after four hours.
The curve in
Polymerization was slowed greatly compared with the blank, the TEMPO derivatives and/or DNBP. Peak area even after four hours is just 640.
DNBP is a good retarder with “normal” polymerization-prone vinyl-containing monomers, e.g. styrene (see Example 16, not in accordance with the invention). DNBP is likewise reputed to intervene in the Diels-Alder mechanism. DNBP should therefore have been expected to do well in this test. Yet, when used in the test, DNBP was found to have no effect in relation to the polymerization of cyclopentadiene or dicyclopentadiene. Polymerization proceeded in the presence of DNBP in exactly the same way as without any admixture. Detected peak area after two and/or four hours corresponded to that of the blank value (Example 1).
MeHQ was used as stabilizer in some of the processes described in the literature. Yet tested with (di-)cyclopentadiene it showed no effect.
The quinone methides tested are good retarders—as good as DNBP—with “normal” polymerization-prone vinyl-containing monomers, e.g. styrene. Based on conventional wisdom as reported in the literature DNBP v. quinone methides in styrene—quinone methides would therefore not be expected to show any activity.
It was all the more astonishing that the quinone methides used have a very substantial slowing effect on the polymerization of cyclopentadiene/dicyclopentadiene. The effect was greater than that of any other of the inhibitors tested.
Comparative Test with Styrene Monomer; Examples 12-21:
Commercially available stabilized styrene was freed of the stabilizer tert-butyl-1,2-hydroxybenzene (TBC) in an inert nitrogen atmosphere at a reduced pressure of 95 mbar and a pot temperature of 75° C. The experimental apparatus, which consisted of a multi-neck flask equipped with a thermometer, a reflux condenser, a septum and a KPG stirrer, was thoroughly purged with nitrogen to obtain an oxygen-free atmosphere. 300 g of the unstabilized styrene were introduced into the multi-neck flask and admixed with 100 ppm of an inhibitor as per Table 2. A constant supply of nitrogen into the styrene solution through a glass frit ensured an inert nitrogen atmosphere throughout the entire duration of the experiment. The styrene solution was vigorously stirred.
At the start of the experiment, the flask was immersed in a preheated oil bath at 110° C. to such an extent that the stabilized styrene solution is completely immersed. After the three-neck flask had been immersed in the heated oil bath, about 3 g of the styrene solution were removed via the septum at regular intervals, accurately weighed and introduced into 50 ml of methanol. The methanol mixture was stirred at room temperature for half an hour. The methanol worked to precipitate the polystyrene formed during the experiment. This polystyrene was separated off by filtration through a glass filter crucible. The filter residue was washed with 20 ml of methanol and then dried at 110° C. for not less than 5 hours. The polystyrene remaining behind in the glass filter crucible was then weighed. The value found and the initial weight were used to determine the percentage fraction of polymer. This polymer content was plotted against the reaction time (cf. also further values depicted in
Evaluation of Examples 12-21
It is apparent from the table that the TEMPO derivatives (Examples 13 and 14) were effective inhibitors of the polymerization of styrene—for a short time. Thereafter, they were spent and virtually devoid of any further activity. Corresponding results were found in (di)cyclopentadiene (Examples 2 and 3).
TBC (Example 15), however, had virtually no effect in the styrene test, but was found to have fairly good activity in (di)cyclopentadiene (Example 4).
With DNBP (Example 16), the effect was exactly the other way round. While its performance in styrene was virtually equivalent to or even better than that of the quinone methides QM-2, QM-5, QM-7, QM-8 (Examples 18-21), DNBP had no effect in (di)cyclopentadiene (Example 5). Yet all the quinone methides were very active in (di)cyclopentadiene (Examples 7-11). In contrast to the other quinone methides, QM-1 proved to be a potent inhibitor in styrene, but was quick to lose its activity (Example 17). In (di)cyclopentadiene, by contrast, it surprisingly shows very good, sustained activity (Example 7).
Comparing the results of the tests with (di)cyclopentadiene and styrene suggests that different mechanisms are involved in the polymerization of the two unsaturated monomers. The effectiveness of inhibitors cannot be predicted as to between monomers.
The values obtained with QM-1 and QM-5 are shown for comparison in
General Description—Use in Cyclopentadiene Production; Examples 22 and 23
A 500 ml multi-neck flask was volumetrically calibrated and marked at 400 mL. Continuous metered addition of fresh dicyclopentadiene was provided. The flask was fitted with a heatable column packed with glass Raschig rings. The oil bath was temperature regulated to 180° C.
Technical-grade DCPD (93%) was used in the continuous runs.
The entire dicyclopentadiene to be used was admixed with 5000 ppm of the in-test inhibitor. A slow stream of nitrogen was passed continuously over 100 g of dicyclopentadiene (with inhibitor).
The multi-neck flask was then immersed in the preheated oil bath. Once a pot temperature of 160° C. was reached, 30 ml per hour of dicyclopentadiene (with inhibitor) were metered continuously into the pot. The pot begins to boil at a temperature of about 164° C. and the dicyclopentadiene was cleaved into cyclopentadiene, which distilled over through the column. The cyclopentadiene produced was collected in a receiver cooled to −3° C.
Once insufficient cyclopentadiene was formed under the given temperatures, the pot level rises. When a pot level of 400 mL was reached, the metered addition was terminated and remaining dicyclopentadiene and cyclopentadiene formed was distilled out of the pot. The results are shown in Table 3.
The table reveals that the addition of QM-5 had a distinct prolongating effect on the run time in the production of dicyclopentadiene and cyclopentadiene. Instead of for 38 h, the apparatus could be operated for 43.5 h without pot exchange. In addition, the cyclopentadiene yield, based on the entire feed of dicyclopentadiene, went up from 76.8% to 79.3%.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2013 204 950 | Mar 2013 | DE | national |
This application is a divisional of U.S. application Ser. No. 14/217,588 filed on Mar. 18, 2014, claiming priority to German Application No. 102013204950.1, filed Mar. 20, 2013, the disclosure of which is incorporated herein by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3061586 | Thompson | Oct 1962 | A |
| 3530193 | Starnes, Jr. | Sep 1970 | A |
| 4003800 | Bacha et al. | Jan 1977 | A |
| 4040911 | Bacha et al. | Aug 1977 | A |
| 4654451 | Miller et al. | Mar 1987 | A |
| 5616774 | Evans et al. | Apr 1997 | A |
| 5670692 | Nesvadba et al. | Sep 1997 | A |
| 7030279 | Tanielyan et al. | Apr 2006 | B1 |
| 7045647 | Benage | May 2006 | B2 |
| 7046647 | Oba et al. | May 2006 | B2 |
| 8128804 | Weyler et al. | Mar 2012 | B2 |
| 8212081 | Rinker et al. | Jul 2012 | B2 |
| 20030205452 | Merrill | Nov 2003 | A1 |
| 20040034247 | Eldin | Feb 2004 | A1 |
| 20050027150 | Eldin et al. | Feb 2005 | A1 |
| 20050256312 | Osterholt et al. | Nov 2005 | A1 |
| 20060020089 | Merrill | Jan 2006 | A1 |
| 20060283699 | Ma et al. | Dec 2006 | A1 |
| 20070208204 | Meyer et al. | Sep 2007 | A1 |
| 20090114878 | Weyler | May 2009 | A1 |
| 20100267992 | Rinker et al. | Oct 2010 | A1 |
| 20120101295 | Weyler et al. | Apr 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 642 560 | May 2009 | CA |
| 1699311 | Nov 2005 | CN |
| 1907927 | Feb 2007 | CN |
| 101104573 | Jan 2008 | CN |
| 101423449 | May 2009 | CN |
| 694 19 662 | Jan 2000 | DE |
| 696 09 110 | Mar 2001 | DE |
| 0 626 377 | Nov 1994 | EP |
| 0 737 659 | Jul 2000 | EP |
| 0 737 660 | Aug 2002 | EP |
| 2 055 691 | May 2009 | EP |
| 61-165338 | Jul 1986 | JP |
| 61-165338 | Jul 1986 | JP |
| 9-176215 | Jul 1997 | JP |
| 2003-515656 | May 2003 | JP |
| 2004-511569 | Apr 2004 | JP |
| 2004-513985 | May 2004 | JP |
| 2011-256142 | Dec 2011 | JP |
| WO 9948896 | Sep 1999 | WO |
| WO 0140404 | Jun 2001 | WO |
| WO0147844 | Jul 2001 | WO |
| WO 0147844 | Jul 2001 | WO |
| WO 0233025 | Apr 2002 | WO |
| WO 0233026 | Apr 2002 | WO |
| WO 2004026995 | Apr 2004 | WO |
| WO 2008067012 | Jun 2008 | WO |
| WO 2010078096 | Jul 2010 | WO |
| Entry |
|---|
| Office Action dated May 31, 2017 in Malaysian Patent Application No. PI 2014000772. |
| European Search Report dated Feb. 9, 2009 in EP 08 16 5122 (with English translation of category of cited documents). |
| C.M. Orlando, “Quinone Methide Chemistry. The Benzylic Oxidative Methoxylation of 2, 6-Di-tert-butyl-p-cresol”, J. Org. Chem. vol. 35, No. 11, XP-002514061 , 1970, pp. 3714-3717. |
| Von Eugen Muller, et al., “Instabile Aroxyle”, Justus Liebigs Annalen Der Chemie, Verlag Chemie GMBH, Weinheim, De, vol. 645, XP-009096429, Jan. 1, 1961, pp. 66-78. |
| A. A. Yassin, et al. , “The Mechanisms of Retardation and Inhibition in Radical Polymerizations by Quinones”, European Polymer Journal, vol. 9, No. 7, XP-023321771, Jul. 1, 1973, pp. 657-667. |
| Taiwanese Office Action dated Jun. 20, 2013 in Taiwanese Patent Application No. 097141190 (English translation only). |
| Japanese Office Action dated Jun. 24, 2013 in Patent Application No. 2008-282889 (German Translation only). |
| R.E. Winkler, et al., “Inhibition of the Thermal Polymerization of Styrene by N-Phenyl-N′-Isopropyl-p-Phenylenediamine”, J. Polym. Sci. Polym. Chem. Ed., vol. 26, 1988, pp. 2853-2858. |
| European Search Report dated Jul. 2, 2014 in Patent Application No. 14160170.8 with English Translation of Category of Cited Documents. |
| Written Opinion and Search Report dated Mar. 20, 2015 in Patent Application No. 10201400699R. |
| Maria M. Toteva, et al., “The generation and reactions of quinone methides” Advances in Physical Organic Chemistry, vol. 45, Jan. 1, 2011, pp. 39-91. |
| Palmova et al., 2001, Experimental and Modeling Studies of Oligomerization and Copolymerization of Dicyclopentadien, Chemical Engineering Science, vol. 56, pp. 927-935. |
| Number | Date | Country | |
|---|---|---|---|
| 20160237008 A1 | Aug 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14217588 | Mar 2014 | US |
| Child | 15137900 | US |