Patent Application
20110067800
The present invention relates to a process and apparatus for producing an elastomeric compound.
More particularly, the present invention relates to a process for producing an elastomeric compound comprising at least one mixing step carried out in at least one batch mixing device, and at least one mixing step carried out in at least one continuous mixing device, the resulting elastomeric compound being primarily, but not exclusively, intended for use in the manufacturing of tires.
Moreover, the present invention also relates to a plant for producing an elastomeric compound comprising at least one batch mixing device, and at least one continuous mixing device.
Conventionally, the production of elastomeric compounds is performed batchwise by means of batch mixing devices, e.g. internal mixers such as, for example, Banbury® mixers, having two counter-rotating rotors which exert an intensive mixing action to masticate the elastomeric polymer(s) and to incorporate and thoroughly disperse therein the other components usually present in the elastomeric compounds such as, for example, reinforcing fillers, lubricating aids, curatives and other. additives.
The production of elastomeric compounds using internal mixers shows many drawbacks, particularly a poor heat dissipation and thus a scarce temperature control, mainly due to an unfavourable ratio between material volume and mixer surface area. To improve dispersion in the elastomeric polymer(s), the various components, and particularly the reinforcing fillers, are usually incorporated into the elastomeric polymer(s) in batches distributed in a plurality of mixing operations separated by cooling and storage steps. Usually, the temperature sensitive components, such as crosslinking agents and accelerators, are added only during the final mixing step, after the cooling of the elastomeric compounds below a predetermined temperature (usually below 110° C.) to avoid premature crosslinking (“scorching” phenomena).
Therefore, the production of elastomeric compounds using batch mixing devices, although still remaining the most widely used production process in the rubber industry, is time and energy consuming and does not guarantee an effective control on the properties of the resulting elastomeric compounds, particularly as regards dispersion homogeneity of reinforcing fillers into the elastomeric polymer(s). Variation in the added amounts of individual components, timing of addition and discharge from the mixers, initial temperature of the raw materials, and fluctuations of shear forces inside the material during mixing, all contribute to batch-to-batch variation.
To overcome the limitations of the batchwise processes above disclosed, many attempts have been performed by the rubber industry to set up production processes, based on extrusion techniques analogous to those commonly employed in the processing of thermoplastic polymer materials. Production processes carried out by means of an extruder should improve uniformity of the properties of the obtained elastomeric compounds, better thermal management resulting from improved surface-to-mass ratios, and possible development of highly automated operations. For an overview on this subject see the article “A tale of continuous development” by H. Ellwood, published in European Rubber Journal, March 1987, pages 26-28.
U.S. Pat. No. 4,897,236 discloses a process and an apparatus for continuously producing a rubber mixture, wherein the ingredients of the mixture are fed, masticated and homogenized in a twin-screw extruder. The resulting mixture is divided into a first and a second portion. The first portion is discharged, while the second portion is recycled for further homogenization and for mixing with fresh batches of the ingredients being fed to the extruder. The recycled portion is circulated to and returned from a cooled, annular chamber exterior to the extruder chamber, said annular chamber having outflow and inflow passages communicating with the interior of the extruder. That partial recycling of the rubber mixture should compensate for fluctuations in the metering of the ingredients and for local inhomogeneities which may occur. Moreover, the intensive cooling of the recycled portion in the annular chamber should correct a rising processing temperature, and should improve the dispersing action because of increased shearing stresses consequent to the temperature decrease.
U.S. Pat. No. 5,626,420 discloses a continuous mixing process and apparatus, wherein base elastomer(s) and other components are continuously dosed and introduced into a mixing chamber formed of a stator and a rotor rotating therein, preferably a single screw extruder. The introduced components advance within the mixing chamber along zones of propulsion and mixing. To improve dispersion and homogenization of the rubber components, the filling rate of the mixing chamber in at least certain mixing zones is lower than 1. To properly introduce the components, and particularly the rubber base, into the mixing chamber, force feeding means are used, such as volumetric pumps (e.g. gear pumps). To obtain precise dosage of the different components, it may be desirable to add the components in a mixing zone where the filling rate is equal to 1, located between two mixing zones having a filling rate lower than 1.
U.S. Pat. No. 6,726,352 discloses a method for processing a rubber mixture or compound for tire manufacturing including the steps of determining variation tolerances with respect to reference values for process parameters, detecting values of the process parameters, comparing detected values of the process parameters with the reference values and the variation tolerances, attributing an evaluation to a semi-finished product depending on compliance or non-compliance of the detected values with the reference values and the variation tolerances, classifying the semi-finished product on a basis of the attributed evaluation, and establishing successive steps for processing the semi-finished product depending on the classification of the semi-finished product. The processing includes at least one mixing cycle and an extrusion cycle for obtaining the semi-finished product. Said mixing cycle is advantageously carried out in at least one mixer comprising a pair of rotors which operate tangentially relative to each other or are interpenetrating such as, for example a Banbury® or a Intermix®. The cycles are controlled by the process parameters detected during execution of the cycles.
In the Applicant's view, one of the most critical aspects in the production of elastomeric compounds by means of continuous mixing devices, e.g. extruders, is the feeding system of all the components of the elastomeric compounds into the continuous mixing devices. In fact, said components must be worked (e.g. granulated, pelletized, subdivided, ect.) and precisely dosed to be fed into the continuous mixing devices. For these reasons, a complex feeding system should be provided, which causes an increase in the overall production process in time, as well as an increase of the production costs.
On the other hand, the Applicant has noted that the dispersion of the components which are usually added to the elastomeric compounds, in particular the dispersion of the reinforcing fillers using batch mixing devices, may be unsatisfactory.
However, increasing the number of mixing steps in batch mixing devices in order to improve the components dispersion in the elastomeric compounds, generally, may cause a lot of drawbacks such as, for example, damages to the elastomeric polymer(s), worsening of the mechanical properties of the elastomeric compounds, premature crosslinking (“scorching” phenomena) of the elastomeric compounds.
The Applicant has faced the problem of providing a more efficient process for producing elastomeric compounds which reduces the number of mixing steps to which the elastomeric compounds are usually subjected when the process is carried out using batch mixing devices, as well as to reduce or even to avoid the drawbacks which may occur when the process is carried out by using continuous mixing devices.
In particular, the Applicant has faced the problem of providing a process for producing an elastomeric compound wherein an improved dispersion of said components, in particular of the reinforcing fillers, may be obtained, without negatively affecting the mechanical properties (both static and dynamic) of the obtained elastomeric compound.
The Applicant has now surprisingly found that the above reported properties may be obtained by producing an elastomeric compound with at least one mixing step carried out in at least one batch mixing device and at least one mixing step carried out in at least one continuous mixing device.
Moreover, the Applicant has found that said process allows to reduce the mixing time so increasing the productivity and reducing the production costs.
For the aim of the present description and of the claims which follow, the term “batch mixing device” means a mixing device into which the components of the elastomeric compound are periodically fed in predefined amounts (batches) and mixed for a predetermined time so as to obtain the elastomeric compound. At the end of the mixing step, the obtained elastomeric compound is completely discharged from the mixing device.
For the aim of the present description and of the claims which follow, the term “continuous mixing device” means a mixing device into which the components of the elastomeric compound are continuously fed (apart from possible stopping of the mixing device due to maintenance, or change of elastomeric compound recipe) and from which the elastomeric compound is discharged in a continuous stream, in contrast to the periodic charge/discharge of a batch mixing device.
According to a first aspect the present invention relates to a process for producing an elastomeric compound, comprising:
The Applicant has found that said second elastomeric compound shows a significantly improved dispersion of said at least one reinforcing filler with respect to said first elastomeric compound, together with substantially unaffected or even improved mechanical properties (both static and dynamic).
According to one preferred embodiment, said process may be carried out continuously or discontinuously.
When said process is carried out continuously, the first elastomeric compound is directly fed to said at least one continuous mixing device without being stored.
When said process is carried out discontinuously, said first elastomeric compound is fed to said at least one continuous mixing device after having being stored.
According to a further aspect, the present invention relates to a plant for producing an elastomeric compound, comprising:
According to a further aspect, the present invention relates to a process for manufacturing a tire comprising:
The present invention, in at least one of the abovementioned aspects, may show one or more of the preferred characteristics hereinafter disclosed.
According to one preferred embodiment, said batch mixing device is selected from internal mixers, open mixers. Internal mixers are particularly preferred.
Usually, said batch mixing device comprises a pair of rotors which operate tangentially relative to each other or are inter-penetrating.
Usually, said batch mixing device comprises a mixing chamber internally housing a pair of rotors turning in opposite directions, so as to mix up the components introduced into the mixing chamber from the top thereof.
For this purpose, said batch mixing device is usually provided with a pneumatic or hydraulic cylinder located in the upper part of the mixing chamber and a piston movable upwards to open the mixing chamber, thereby allowing the introduction of the components via special loading hoppers, and downwards so as to exert a pressure on the material processed by the rotors and located above them.
A hydraulic system located on the bottom of the mixing chamber allows discharging of the elastomeric compound at the end of the mixing cycle by opening a suitable outlet.
Specific examples of internal mixers which may be advantageously used according to the present invention are those known under the tradename of Banbury® or Intermix®, depending on whether the rotors operate tangentially relative to each other or are inter-penetrating. Banbury® mixer is particularly preferred.
Specific examples of open mixers which may be advantageously used according to the present invention are: open mill mixer, Z-blade mixer. Open mill mixer is particularly preferred.
According to one preferred embodiment, the mixing in said at least one batch mixing device may be carried out at a rotor speed of about 20 rpm to about 60 rpm, preferably of about 30 rpm to about 50 rpm.
According to a further preferred embodiment, the mixing in said at least one batch mixing device, may be carried using a fill factor of the mixing chamber (the fill factor is the portion of the total free volume of the mixing chamber occupied by the material to be mixed) not higher than about 80%, preferably of about 55% to about 70%. If a too high fill factor is selected, lack of free volume prevents material movement and cross-blending and adequate mixing becomes impossible. Likewise, if only a very small fill factor is selected, it is difficult to ensure adequate mixing, with high shearing forces, and adequate homogenisation of the material in the mixing chamber.
According to one preferred embodiment, said at least one continuous mixing device has at least two co-rotating screws.
Said rotating screws may comprise high-shear mixing elements such as kneaders; elements that enable redistribution of the materials such as toothed elements, gears or pins; flow restrictors such as blisters, adjustable or fixed throttling arrangements, or screw flights with low flight depth. These elements may be arranged on two or more shafts that rotate about their axes in the same-sense (co-rotating), or in the opposite sense (counter-rotating) with respect to each other. The screw shaft may be parallel, convergent, or divergent. The rotating speeds of said shafts may be the same or different. The screw shafts may be placed apart at different distances from each other so as to enable the assembly of elements on each shaft to intermesh to various extents or not intermesh at all. The choice of orientation of each of the mixing elements (including whether the elements will be left handed or right handed) is made based on the degree of back mixing and/or pressure gradient and temperature/shear history required along the extruder length. Some variations in the design of kneaders include single cam, double or multi lobe designs. The number of teeth on the gear or toothed mixer may also vary.
Preferably, said at least two co-rotating screws are at least partially intermeshed. More preferably, said at least two co-rotating screws are substantially fully intermeshed.
According to a further preferred embodiment, said continuous mixing device is a mixing extruder.
Preferably, said mixing extruder comprises:
According to a further preferred embodiment, said mixing extruder may be selected, for example, from: co-rotating twin-screw extruders; co-rotating multi-screw extruders comprising more than two screws such as, for example, ring extruders; planetary roller extruders. Co-rotating twin-screw extruders, or ring extruders, are particularly preferred. Ring extruders are even more preferred.
According to a further preferred embodiment, said at least one mixing extruder is a self-wipening co-rotating intermeshing multi-screw extruder.
According to a further preferred embodiment, said at least one mixing extruder is a self-wipening co-rotating intermeshing twin-screw extruder.
Usually, the self-wipening co-rotating intermeshing multi-screw or twin-screw extruders comprise mixing elements of one rotating screw which are substantially fully intermeshed with the mixing elements of the adjacent rotating screw thus allowing the self-wipening of the extruder.
The use of said co-rotating substantially fully intermeshing multi-screw or twin-screw extruder may allow to obtain a very good dispersion of the components, in particular of the reinforcing fillers, in the second elastomeric compounds.
According to one preferred embodiment, the mixing in said at least one continuous mixing device may be carried out at a screw speed of about 10 rpm to about 600 rpm, preferably of about 40 rpm to about 400 rpm.
It has to be noted that said screw speed may allow to obtain a very good dispersion of the components, in particular of the reinforcing fillers, in the second elastomeric compound, as well as to avoid premature crosslinking (“scorching” phenomena) of the second elastomeric compound which may occur if a too high screw speed is used.
According to a further embodiment, the process of the present invention may comprise cooling said first elastomeric compound before feeding it to said at least one continuous mixing device. Preferably, said first elastomeric compound may be cooled to a temperature from about 15° C. to about 40° C., more preferably from about 20° C. to about 25° C.
According to a further embodiment, said mixing apparatus includes at least one conveying extruder.
According to one preferred embodiment, said first elastomeric compound is fed to said at least one conveying extruder before being fed to said at least one continuous mixing device.
According to one preferred embodiment, said at least one conveying extruder comprises:
For the purposes of the present invention and of the claims which follow, the term “conveying element” means an element which does not substantially exert a mixing action but merely exerts a conveying of the elastomeric compound through the extruder length. Typical conveying elements may be selected, for example, from elements that mainly promote axial movement of the material such as helical screws.
According to a further preferred embodiment, the conveying in said at least one conveying extruder may be carried out at a conveying element speed from about 10 rpm to about 60 rpm, preferably from about 20 rpm to about 35 rpm.
The feeding to said at least one conveying extruder may allow to control the feeding rate of said first elastomeric compound to said at least one continuous mixing device.
Preferably, said at least one conveying extruder is selected from single helical screw extruders, dump extruders having counter-rotating two helical screws.
According to a further embodiment, said mixing apparatus includes at least one open mixer.
According to a further embodiment, said mixing apparatus includes at least one internal mixer and at least one open mixer, said open mixer being preferably placed downstream to said at least one internal mixer.
According to a further embodiment, the process of the present invention, may comprise feeding said second elastomeric compound to at least one further batch mixing device. Said at least one further batch mixing device may be selected from those above disclosed.
According to a further embodiment, the process of the present invention, may comprise feeding said second elastomeric compound to at least one further continuous mixing device. Said at least one further continuous mixing device may be selected from those above disclosed.
According to a further embodiment, said at least one continuous mixing device may be placed upstream of a device for manufacturing a semi-finished product by using said second elastomeric compound.
The device for manufacturing a semi-finished product may be selected from those known in the art such as, for example, calendering devices, extruders.
According to a further embodiment, said at least one continuous mixing device may be equipped with a roller die. In this case, a semi-finished product is directly obtained from said at least one continuous mixing device.
Accordingly to a further embodiment, said at least one continuous mixing device may be equipped with an extrusion die. In this case, a semi-finished product is directly obtained from said at least one continuous mixing device.
Said semi-finished product may be, for example, one of the different structural elements of a tire such as, for example: carcass ply, belt layer, bead filler, sidewall, tread band, liner, underliner, antiabrasive layer. According to processes known in the art, said structural elements may be subsequently assembled using a suitable manufacturing apparatus to give a finished tire.
On the other hand, alternative processes for manufacturing a tire without using semi-finished products, are known in the art.
In this regards, in case of tire structural elements being substantially constituted by elastomeric compound such as, for example, bead filler, sidewall, tread band, liner, underliner, antiabrasive layer, a continuous elongated strip-like element is laid down on a support bearing the tire being manufactured, said continuous elongated strip-like element being arranged so as to form a plurality of consecutive coils in side by side and/or superposed relationship, to obtain a tire in its final configuration. Alternatively, in case of tire structural elements being substantially constituted by elastomeric compound and at least one thread-like reinforcing element such as, for example, carcass ply, belt layer, said continuous elongated strip-like element is associated with at least one thread-like reinforcing element in order to produce semi-finished products in the form of rubberized wire or of strip-like element comprising at least one thread-like reinforcing element, which are further laid down on a support bearing the tire being manufactured, in side-by side and/or superposed relationship, to obtain a tire in its final configuration. Said support may be a rigid support and may have a toroidal shape. Processes of this type may be disclosed, for example, in European Patent Applications EP 928 680 or EP 928 702, or in International Patent Application WO 01/36185.
Said support may be selected, for example, from the following devices:
According to a further embodiment, said at least one continuous mixing device may form said second elastomeric compound as a continuous elongated strip-like element which is further deposited on a support as above reported, said continuous mixing device being preferably equipped with a roller die or an extrusion die. Alternatively, said continuous elongated strip-like element may be associated with at least one reinforcing thread-like reinforcing element.
Said continuous elongated strip-like element, comprising said second elastomeric compound, may have a flattened cross-section such as, for example, rectangular, elliptic, or lenticular, or tapered shape. Cross-section dimensions of said continuous elongated strip-like element are considerably lower than the cross-section dimensions of the structural element to be manufactured. By way of example, the continuous elongated strip-like element may have a width indicatively ranging from about 3 mm to about 15 mm and a thickness indicatively ranging from about 0.5 mm to about 1.2 mm.
According to one preferred embodiment, all the components of the elastomeric compound may be fed to said at least one mixing apparatus.
In particular, besides said at least one elastomeric polymer and said at least one reinforcing filler, at least one of the following components may be added to the elastomeric compound:
The above list of components is given only to illustrate some examples of the most common components usually used in elastomeric compounds, particularly in elastomeric compound for tires manufacturing, and shall not be intended as limiting of the scope of the present invention.
When all the components of the elastomeric compound are fed to a batch mixing device, e.g. an internal mixer such as a Banbury® mixer, the mixing may be preferably carried out in at least two different steps, the first step being a non-productive step wherein all the components except those able to promote the crosslinking (for example, sulfur and accelerators) are fed to said batch mixing device, the second step being a productive step wherein the elastomeric compound obtained from said first step as well as the components able to promote crosslinking are fed to said batch mixing device. The so obtained elastomeric compound, i.e. first elastomeric compound, is subsequently fed to a continuous mixing device, e.g. an extruder, so as to obtain a second elastomeric compound.
Alternatively, all the components of the elastomeric compound, except from the components able to promote crosslinking, are fed to a batch mixing device, e.g. an internal mixer such as a Banbury® mixer, to obtain a first elastomeric compound which is subsequently fed to a continuous mixing device, e.g. an extruder, so as to obtain a second elastomeric compound. The so obtained second elastomeric compound, as well as the components able to promote crosslinking, are subsequently fed to a further batch mixing device, e.g. an internal mixer such as a Banbury® mixer, which is placed downstream said continuous mixing device, e.g. an extruder.
Alternatively, all the components of the elastomeric compound, except from the components able to promote crosslinking, are fed to a batch mixing device, e.g. an internal mixer such as a Banbury® mixer, to obtain a first elastomeric compound. The so obtained first elastomeric compound, as well as the components able to promote crosslinking, are subsequently fed to a continuous mixing device, e.g. an extruder, so as to obtain a second elastomeric compound.
When an open mixer is used as a batch mixing device, preferably, all the components of the elastomeric compound are fed to said open mixer so as to obtain a first elastomeric compound which is subsequently fed to a continuous mixing device, e.g. an extruder, so as to obtain a second elastomeric compound.
The process according to the present invention may be employed to produce an elastomeric compound comprising any kind of elastomeric polymers, particularly of elastomeric polymers, as well as any kind of reinforcing fillers, usually used in the tires manufacturing.
Preferably, the elastomeric polymers may be selected, for example, from: diene elastomeric polymers and mono-olefin elastomeric polymers, or mixtures thereof.
Diene elastomeric may be selected, for example, from elastomeric polymers or copolymers with an unsaturated chain having a glass transition temperature (Tg) generally below 20° C., preferably in the range from about 0° C. to about −110° C. These polymers or copolymers may be of natural origin or may be obtained by solution polymerization, emulsion polymerization or gas-phase polymerization of one or more conjugated diolefins, optionally blended with at least one comonomer selected from monovinylarenes and/or polar comonomers. Preferably, the obtained polymers or copolymers contain said at least one comonomer selected from monovinylarenes and/or polar comonomers in an amount of not more than 60% by weight. Examples of diene elastomeric polymers are: cis-1,4-polyisoprene (either natural or synthetic, preferably natural rubber), 3,4-polyisoprene, poly-1,3-butadiene (in particular, high vinyl poly-1,3-butadiene having a content of 1,2-polymerized units from about 15% to about 85% by weight), polychloroprene, optionally halogenated isoprene/isobutene copolymers, 1,3-butadiene/acrylonitrile copolymers, 1,3-butadiene/styrene copolymers, 1,3-butadiene/isoprene copolymers, isoprene/styrene copolymers, isoprene/1,3-butadiene/styrene terpolymers; or mixtures thereof.
As to mono-olefin elastomeric polymers, they may be selected, for example, from: copolymers of ethylene with at least one alpha-olefin having from 3 to 12 carbon atoms, and optionally with a diene having from 4 to 12 carbon atoms; polyisobutene; copolymers of isobutene with at least one diene. Particularly preferred are: ethylene/propylene copolymers (EPR); ethylene/propylene/diene terpolymers (EPDM); polyisobutene; butyl rubbers; halobutyl rubbers; or mixtures thereof.
Preferably, said at least one reinforcing filler may be selected, for example, from: carbon black, silica, alumina, aluminosilicates, calcium carbonate, kaolin, or mixtures thereof.
When a reinforcing filler comprising silica is present, the elastomeric compound may advantageously incorporate a coupling agent capable of interacting with the silica and of linking it to the elastomeric polymer(s) during the vulcanization. Among the coupling agents that are particularly preferred are bis(3-triethoxysilylpropyl)-tetrasulphide, or bis(3-triethoxysilylpropyl)disulphide. Said coupling agents may be used as such or as a suitable mixture with an inert filler (for example, carbon black) so as to facilitate their incorporation into the elastomeric compound.
The present invention will now be illustrated in further detail by means of illustrative embodiments, with reference to the attached figures wherein:
a is a lateral view of the two screws of a self-wipening co-rotating intermeshing twin-screw extruder;
b are views in cross-section of the two screws of a self-wipening co-rotating intermeshing twin-screw extruder.
With reference to
Preferably, all the remaining components of the elastomeric compound (e.g. vulcanizing agents, activators, accelerators, or the other additives optionally present) may be fed to the internal mixer (101).
Alternatively, the mixing into said internal mixer (101) may be carried out in at least two steps.
After the mixing has been carried out, the obtained first elastomeric compound (104) is fed to the mixing extruder (106) (e.g. a self-wipening co-rotating intermeshing twin-screw extruder) through a feed hopper (105).
The mixing extruder (106) of
Usually, the mixing extruder (106) may optionally be provided with a degassing unit (110) to allow the exit of the gases which may develop during the mixing of the elastomeric compound. Alternatively, more than one degassing unit may be present along the mixing extruder (106) (not represented in
After the mixing have been carried out, a second elastomeric compound (108) is discharged from the mixing extruder (106), e.g. in the form of a continuous ribbon, by pumping it through a roller die (107), for example by means of a gear pump (not represented in
Alternatively, the second elastomeric compound (108) may be obtained in the form of a subdivided product by pumping it through an extruder die (not represented in
According to said embodiment, the second elastomeric compound (108) is fed to a further internal mixer (201) (e.g. a Banbury® mixer). The feeding to said further internal mixer (201) may be particularly useful when not all the components of the elastomeric compound are fed to the internal mixer (101). In this case, for example, the vulcanizing agents, and/or the activators, and/or the accelerators may be fed to said further internal mixer (201).
According to the particular embodiment of
Alternatively, the second elastomeric compound (108) may be directly fed, without being cooled, to said further internal mixer (201) (not represented in
Alternatively, the second elastomeric compound (108) may be obtained in the form of a subdivided product as disclosed above and subsequently fed to said further internal mixer (201) (not represented in
In the particular embodiment of
According to said embodiment, the first elastomeric compound (104) is fed to a conveying extruder (301) (e.g. a single helical screw extruder) through a feed hopper (302).
The feeding to said one conveying extruder (301) may allow to control the feeding rate of said first elastomeric compound (104) to said mixing extruder (106). According to the particular embodiment of
According to the particular embodiment of
Alternatively, said conveying extruder (301), instead of said roller die (303), may be equipped with:
Alternatively, said conveying extruder (301) may be replaced with an open mill mixer (not represented in
Alternatively, an open mill mixer may be placed between said internal mixer (101) and said conveying extruder (301) (not represented in
According to the particular embodiment of
Alternatively, the first elastomeric compound (104), at the exit from the conveying extruder (301), after being cooled by passing it through a cooling device (401), may be obtained in the form of a subdivided product by means of a cutting device (e.g. a mill provided with rotatably blades) before being fed to the mixing extruder (106) (not represented in
According to the particular embodiment of
According to the particular embodiment of
Alternatively, the second elastomeric compound (108) may be directly fed, without being cooled, to said further internal mixer (501) (not represented in
Alternatively, the second elastomeric compound (108) may be obtained in the form of a subdivided product as disclosed above and subsequently fed to said further internal mixer (501).
According to the particular embodiment of
The second elastomeric compound is discharged from the extruder (601) in the form of a sheet (603) (e.g. in the form of a semi-finished product useful in tire manufacturing), by pumping it through an extrusion die (not represented in
Alternatively, the second elastomeric compound (108) is discharged from the extruder (601) in the form of a sheet (603) (e.g. in the form of a semi-finished product useful in tire manufacturing), by pumping it through a roller die (not represented in
Usually, the obtained sheet (603) (e.g. in the form of a semi-finished product useful in tire manufacturing) is subsequently subjected to a cooling treatment, usually by means of water and/or forced air. The sheet (603) thus treated is then usually arranged on benches or on bobbins waiting for further processing.
Alternatively, a continuous elongated strip-like element (not represented in
According to the particular embodiment of
The second elastomeric compound (108) is discharged from the extruder (601a) in the form of a sheet (603) (e.g. in the form of a semi-finished product useful in tire manufacturing), by pumping it through an extrusion die (not represented in
According to the particular embodiment of
Alternatively, the second elastomeric compound (108) is discharged from the mixing extruder (106) in the form of a sheet (603) (e.g. in the form of a semi-finished product useful in tire manufacturing), by pumping it through an extrusion die (not represented in
a is a lateral view of the two screws (900) of a self-wipening co-rotating intermeshing twin-screw extruder.
b are views in cross-section of the screws (901) of a self-wipening co-rotating intermeshing twin-screw extruder according to the present invention.
The present invention will be further illustrated below by means of a number of preparation examples, which are given for purely indicative purposes and without any limitation of this invention.
Preparation of the Elastomeric Compounds
The receipt of the prepared elastomeric compounds was given in Table 1 (the amounts of the various components are given in phr).
The above reported elastomeric compounds were prepared as follows.
1st Step
All the components listed in Table 1, except sulfur and accelerators (DPG80 and CBS), were mixed together in a Banbury® mixer (model F270), operating at the following working conditions:
2nd Step
The elastomeric compound obtained in 1st step, was cooled to room temperature (23° C.) and was subsequently fed to the same Banbury® mixer above disclosed and a further mixing was carried out operating at the following working conditions:
3rd Step
The elastomeric compound obtained in 2nd step, cooled to room temperature (23° C.), as well as the sulfur and the accelerators (DPG80 and CBS), were fed to the same Banbury® mixer above disclosed and a further mixing was carried out operating at the following working conditions:
The elastomeric compound discharged from the Banbury® mixer was subsequently cooled to room temperature (23° C.).
The obtained elastomeric compound was tested to evaluate the following properties: Mooney viscosity (ML 1+4), mechanical properties (both static and dynamic), as well as filler dispersion: the obtained results were given in Table 2.
The elastomeric compound was produced by using a plant according to
To this aim, the elastomeric compound obtained according to Example 1, was directly fed (without cooling) to a conveying extruder (i.e. a single screw extruder), operating at the following working conditions:
The elastomeric compound discharged from the conveying extruder was cooled to room temperature (23° C.) and subsequently fed to a self-wipening co-rotating intermeshing twin screw extruder Maris TM92HT having a nominal screw diameter of 92 mm and a L/D ratio of 32, operating at the following working conditions:
The elastomeric compound discharged from the self-wipening co-rotating intermeshing twin screw extruder was subsequently cooled to room temperature (23° C.).
The obtained elastomeric compound was tested to evaluate the following properties: Mooney viscosity (ML 1+4), mechanical properties (both static and dynamic), as well as filler dispersion: the obtained results were given in Table 2.
The elastomeric compound was produced by using a plant according to
To this aim, all the components reported in Table 1, except from sulfur and accelerators (DPG80 and CBS), were mixed together in a Banbury® mixer (model F270), operating at the following working conditions:
To this aim, the elastomeric compound discharged from the Banbury® mixer was directly fed (without cooling) to a conveying extruder (i.e. a single screw extruder), operating at the following working conditions:
The elastomeric compound discharged from the conveying extruder, was cooled to room temperature (23° C.) and subsequently fed to a self-wipening co-rotating intermeshing twin-screw extruder Maris TM92HT having a nominal screw diameter of 92 mm and a L/D ratio of 32, operating at the following working conditions:
The elastomeric compound discharged from the self-wipening co-rotating intermeshing twin-screw extruder, was cooled to room temperature (23° C.) and subsequently fed a further Banbury® mixer, onto which sulfur and accelerators (DPG80 and CBS) were added, operating at the following working conditions:
The elastomeric compound discharged from the further Banbury® mixer was subsequently cooled to room temperature (23° C.).
The obtained elastomeric compound was tested to evaluate the following properties: Mooney viscosity (ML 1+4), mechanical properties (both static and dynamic), as well as filler dispersion: the obtained results were given in Table 2.
Mooney Viscosity
The Mooney viscosity ML(1+4) at 100° C. was measured, according to Standard ISO 289-1:1994, on the non-crosslinked elastomeric compounds obtained as described above.
Mechanical Properties
The modulus (100% Modulus and 300% Modulus), the stress at break, as well as the elongation at break, were measured according to Standard ISO 37:2005 on samples of the abovementioned elastomeric compounds vulcanized at 170° C., for 10 min. The results obtained are given in Table 2.
The hardness in IRHD degrees (at 23° C.) according to Standard ISO 48:1994 were measured on samples of the abovementioned elastomeric compounds vulcanized at 170° C., for 10 min. The results obtained are given in Table 2.
Table 2 also shows the dynamic mechanical properties, measured using an Instron dynamic device in the traction-compression mode according to the following methods. A test piece of the crosslinked elastomeric compounds (vulcanized at 170° C., for 10 min) having a cylindrical form (length=25 mm; diameter=12 mm), compression-preloaded up to a 7.5% longitudinal deformation with respect to the initial length, and kept at the prefixed temperature (23° C. and 70° C.) for the whole duration of the test, was submitted to a dynamic sinusoidal strain having an amplitude of ±3.5% with respect to the length under pre-load, with a 10 Hz frequency. The dynamic mechanical properties are expressed in terms of dynamic elastic modulus (E′) and Tan delta (loss factor) values. The Tan delta value is calculated as a ratio between viscous modulus (E″) and elastic modulus (E′).
Filler Dispersion
The filler dispersion (i.e. silica dispersion) was measured according to Standard ISO 11345:2006.
To this aim a test piece of the crosslinked elastomeric compounds (vulcanized at 170° C., for 10 min) having the following dimension: 4 mm×4 mm, was used to evaluate both the silica dispersion (X value) and the silica distribution (Y value) by using a DisperGrader Model 1000NT with 100× magnification, (TECH PRO Corp.). This model has several scales available for comparison. The scale that was selected for these test was the RCB scale. This scale is typically used for measurement of elastomeric compounds filled with reinforcing carbon black.
Ten reference pictures are used for determining the silica dispersion (X value). An algorithm has been derived using these reference pictures and is then applied to an unknown sample. The DisperGrader then analyzes an unknown sample and automatically assigns a dispersion value (X value) to the unknown sample. Higher dispersion values (X values) represent better dispersion. Visual comparison is seen on a computer monitor. The unknown specimen is shown on one half of the screen and the reference picture is displayed simultaneously adjacent to it. The numerical value of dispersion value (X value) is shown on the screen and output to a separate computer for further analysis.
The Y value is not based on visual comparison against photographic standards, but based on the actual size and number of large agglomerates. A high rating values means that there are no agglomerates present in the tested areas that are higher than 23 μm in average diameter.
The data reported in the above Table 2, show that the crosslinked elastomeric compounds obtained according to the present invention (Examples 2 and 3) have improved stress at break, the remaining properties, being not negatively affected, with respect to the crosslinked elastomeric compound obtained according to the prior art (Example 1).
Moreover, the data reported in the above Table 2, show that crosslinked elastomeric compounds obtained according to the present invention (Examples 2 and 3) have an improved silica dispersion with respect to the crosslinked elastomeric compound obtained according to the prior art (Example 1).
Preparation of the Elastomeric Compounds
The receipt of the prepared elastomeric compounds was given in Table 3 (the amounts of the various components are given in phr).
The above reported elastomeric compounds were prepared as follows.
1st Step
All the components listed on Table 3, except sulfur, retardant (PVI), hexamethoxymethylmelamine (HMMM) and accelerator (DCBS), were mixed together in a Banbury® mixer (model F270), operating at the following working conditions:
2nd Step
The elastomeric compound obtained in 1st step was cooled to room temperature (23° C.) and subsequently fed to the same Banbury® mixer above disclosed and a further mixing was carried out operating at the following working conditions:
The obtained elastomeric compound was subsequently cooled to room temperature (23° C.).
The obtained elastomeric compound was tested to evaluate the following properties: Mooney viscosity (ML 1+4), mechanical properties (both static and dynamic), as well as filler dispersion: the obtained results were given in Table 4.
The elastomeric compound was produced by using a plant according to
To this aim, the elastomeric compound obtained according to Example 4, was directly fed (without cooling) to a conveying extruder (i.e. a single screw extruder), operating at the following working conditions:
The elastomeric compound discharged from the conveying extruder, was cooled to room temperature (23° C.) and subsequently fed to a self-wipening co-rotating intermeshing twin screw extruder Maris TM92HT having a nominal screw diameter of 92 mm and a L/D ratio of 32, operating at the following working conditions:
The elastomeric compound discharged from the self-wipening co-rotating intermeshing twin screw extruder was subsequently cooled to room temperature (23° C.).
The obtained elastomeric compound was tested to evaluate the following properties: Mooney viscosity (ML 1+4), mechanical properties (both static and dynamic), as well as filler dispersion: the obtained results were given in Table 4.
The Mooney viscosity ML(1+4), the mechanical properties, as well as the filler dispersion (i.e. carbon black), were measured as reported above.
The data reported in the above Table 4, shows that the crosslinked elastomeric compounds obtained according to the present invention (Example 5) has improved stress at break, the remaining properties, being not negatively affected, with respect to the elastomeric compound obtained according to the prior art (Example 4).
Moreover, the data reported in the above Table 4, show that crosslinked elastomeric compound obtained according to the present invention (Example 5) has a significant improved carbon black dispersion with respect to the crosslinked elastomeric composition obtained according to the prior art (Example 4).
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2007/009798 | 11/13/2007 | WO | 00 | 5/12/2010 |