Claims
- 1. A process of agglomerating a particulate material, comprising:
- commingling said particulate material with at least two binder system components;
- (i) a first component being a binding amount of a water-soluble, binding polymer, said polymer being applied to said particulate material as a dispersion in a non-aqueous dispersion medium; and
- (ii) a second component being a clay, said clay being applied to said particulate material in an amount up to about 12 pounds per tonne of said particulate material.
- 2. The process of claim 1 in which the polymer is contained in the aqueous portion of a water-in oil emulsion.
- 3. The process of claim 1 in which fine particles of polymer are dispersed in the dispersion medium.
- 4. The process of claim 1 wherein said polymer is a poly(acrylamide) based polymer.
- 5. The process of claim 4 wherein said polymer contains repeating units of the following formula: ##STR16## wherein R.sub.2.sup.+ is an alkali metal ion, and f is from 5 to about 90 percent, g is from 5 to about 90 percent, (f)+(g) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 6. The process of claim 5 wherein said polymer is derived from monomer units of acrylamide and sodium acrylate.
- 7. The process of claim 4 wherein said polymer contains repeating units of the following formula: ##STR17## wherein R, R.sub.1 and R.sub.3 are independently hydrogen or methyl, R.sub.2.sup.+ is an alkali metal ion, R.sub.4 is either
- (1) --OR.sub.5 wherein R.sub.5 is an alkyl group having up to 5 carbon atoms;
- (2) ##STR18## wherein R.sub.6 is an alkyl group having up to 8 carbon atoms; (3) ##STR19## wherein R.sub.7 is either methyl, or butyl; (4) phenyl;
- (5) substituted phenyl;
- (6) --CN; or
- (7) ##STR20## and hydrolized tetrapolymers thereof, wherein (a) is from about 5 to about 90 percent, (b) is from 0 to about 90 percent, (c) is from about 0 to about 20 percent, (a)+(b)+(c) equal 100 percent, and (d) is from about 1,000 to about 500,000.
- 8. The process of claim 7 wherein said polymer is derived from monomer units of acrylamide, sodium acrylate and vinyl acetate.
- 9. The process of claim 4 wherein said polymer is derived from monomer units of the formula: ##STR21## wherein R.sub.13 is a hydrogen atom or a methyl group; R.sub.14 is a hydrogen atom, a methyl group or an ethyl group; R.sub.15 is a hydrogen atom, a methyl group, an ethyl group or --R.sub.16 --SO.sub.3 X, wherein R.sub.16 is a divalent hydrocarbon group having 1 to 13 carbon atoms and X is a monovalent cation.
- 10. The process of claim 4 wherein said binding amount of said polymer is applied to said particulate material at an active polymer concentration on said particulate material between about 0.001 percent and about 0.3 percent by weight.
- 11. The process of claim 4 wherein said particulate material is taconite concentrate.
- 12. The process of claim 11 wherein said clay is bentonite.
- 13. A product of the process of claim 1.
- 14. A product of the process of claim 12.
- 15. A process for manufacturing agglomerated mineral ore pellets, comprising:
- (a) commingling:
- (i) a binding amount of a water-soluble, binding polymer dispersed in a non-aqueous dispersion medium onto a taconite mineral ore; and
- (ii) bentonite, said bentonite being applied to said taconite in an amount up to about 12 pounds per tonne of said taconite, thereby forming a composition of said polymer, taconite and bentonite;
- (b) agglomerating said composition to form green balls by a means for balling mineral ore concentrate; and
- (c) firing said green balls by a means for applying sufficient heat to indurate said green balls and form pellets thereby.
- 16. The process of claim 15 wherein said polymer is a poly(acrylamide) based polymer.
- 17. The process of claim 16 wherein said polymer is derived from monomer units of the formula: ##STR22## wherein R.sub.13 is a hydrogen atom or a methyl group; R.sub.14 is a hydrogen atom, a methyl group or an ethyl group; R.sub.15 is a hydrogen atom, a methyl group, an ethyl group or R.sub.16 --SO.sub.3 X, wherein R.sub.16 is a divalent hydrocarbon group having 1 to 13 carbon atoms and X is a monovalent cation, or repeating units of the formula: ##STR23## wherein R.sub.2.sup.+ is an alkali metal ion, and f is from 5 to about 90 percent, g is from 5 to about 90 percent, (f)+(g) equal 100 percent, and (d) is from about 1,000 to about 500,000.
- 18. A product of the process of claim 17.
- 19. A process of agglomerating a particulate material, comprising:
- commingling said particulate material with at least two binder system components;
- (i) a first component being a binding amount of a water-soluble, binding poly(acrylamide) or poly(ethylene oxide) based polymer, said polymer being applied to said particulate material as a dry powder; and
- (ii) a second component being a clay, said clay being applied in an amount up to about 12 pounds per tonne of said particulate material.
- 20. The process of claim 19, wherein said first binding polymer is a poly(ethylene oxide) based polymer.
- 21. The process of claim 19, wherein said first binding polymer is a poly(acrylamide) based polymer.
- 22. The process of claim 21 wherein said polymer contains repeating units of the following formula: ##STR24## wherein R.sub.2.sup.+ is an alkali metal ion, and f is from 5 to about 90 percent, g is from 5 to about 90 percent, (f)+(g) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 23. The process of claim 22 wherein said polymer is derived from monomer units of acrylamide and sodium
- 24. The process of claim 21 wherein said polymer contains repeating units of the following formula: ##STR25## wherein R, R.sub.1 and R.sub.3 are independently hydrogen or methyl, R.sub.2.sup.+ is an alkali metal ion, R.sub.4 is either
- (1) --OR.sub.5 wherein R.sub.5 is an alkyl group having up to 5 carbon atoms;
- (2) ##STR26## wherein R.sub.6 is an alkyl group having up to 8 carbon atoms; (3) ##STR27## wherein R.sub.7 is either methyl or ethyl; (4) phenyl;
- (5) substituted phenyl;
- (6) --CN; or
- (7) ##STR28## and hydrolized tetrapolymers thereof, wherein (a) is from about 5 to about 90 percent, (b) is from 0 to about 90 percent, (c) is from about 0 to about 20 percent, (a)+(b)+(c) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 25. The process of claim 24 wherein said polymer is derived from monomer units of acrylamide, sodium acrylate and vinyl acetate.
- 26. The process of claim 21 wherein said polymer is derived from monomer units of the formula: ##STR29## wherein R.sub.13 is a hydrogen atom or a methyl group; R.sub.14 is a hydrogen atom, a methyl group or an ethyl group; R.sub.15 is a hydrogen atom, a methyl group, an ethyl group or --R.sub.16 --SO.sub.3 X, wherein R.sub.16 is a divalent hydrocarbon group having 1 to 13 carbon atoms and X is a monovalent cation.
- 27. The process of claim 26 wherein said binding amount of said polymer is applied to said particulate material mineral ore concentrate at an active polymer concentration in said concentrate between about 0.001 percent and about 0.3 percent by weight of dry concentrate.
- 28. The process of claim 21 wherein said particulate material is taconite concentrate.
- 29. The process of claim 28 wherein said clay is bentonite.
- 30. A product of the process of claim 19.
- 31. A product of the process of claim 29.
- 32. The process of claim 19 wherein said first binder component also includes a polysaccharide polymer.
- 33. The process of claim 32 wherein said polysaccharide polymer is selected from the group consisting of carboxymethyl cellulose, guar gum, hydroxyethyl cellulose, and mixtures thereof.
- 34. A product of the process of claim 33.
- 35. A process of manufacturing agglomerated mineral ore pellets, comprising:
- (a) commingling:
- (i) a binding amount of a water-soluble binding poly(acrylamide) or poly(ethylene oxide) based polymer, said polymer being applied to a taconite mineral ore as a dry powder; and
- (ii) bentonite, said bentonite being applied to said taconite in an amount up to about 12 pounds per tonne of said taconite. thereby forming a composition of said polymer, taconite and bentonite;
- (b) agglomerating said composition to form green balls by a means for balling mineral ore concentrate; and
- (c) firing said green balls by a means for applying sufficient heat to indurate said green balls and form pellets thereby.
- 36. The process of claim 35, wherein said first binder component is a poly(ethylene oxide) based polymer.
- 37. The process of claim 35 wherein said polymer contains repeating units of the following formula: ##STR30## wherein R.sub.2.sup.+ is an alkali metal ion, and f is from 5 to about 90 percent, g is from 5 to about 90 percent, (f)+(g) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 38. The process of claim 37 wherein said polymer is derived from monomer units of acrylamide and sodium acrylate.
- 39. The process of claim 35 wherein said polymer contains repeating units of the following formula: ##STR31## wherein R, R.sub.1 and R.sub.3 are independently hydrogen or methyl, R.sub.2.sup.+ is an alkali metal ion, R.sub.4 is either
- (1) --OR.sub.5 wherein R.sub.5 is an alkyl group having up to 5 carbon atoms;
- (2) ##STR32## wherein R.sub.6 is an alkyl group having up to 8 carbon atoms; (3) ##STR33## wherein R.sub.7 is either methyl or ethyl; (4) phenyl;
- (5) substituted phenyl;
- (6) --CN; or
- (7) ##STR34## and hydrolized tetrapolymers thereof, wherein (a) is from about 5 to about 90 percent, (b) is from 0 to about 90 percent, (c) is from about 0 to about 20 percent, (a)+(b)+(c) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 40. The process of claim 39 wherein said polymer is derived from monomer units of acrylamide, sodium acrylate and vinyl acetate.
- 41. The process of claim 35 wherein said polymer is derived from monomer units of the formula: ##STR35## wherein R.sub.13 is a hydrogen atom or a methyl group; R.sub.14 is a hydrogen atom, a methyl group or an ethyl group; R.sub.15 is a hydrogen atom, a methyl group, an ethyl group or --R.sub.16 --SO.sub.3 X, wherein R.sub.16 is a divalent hydrocarbon group having 1 to 13 carbon atoms and X is a monovalent cation.
- 42. The process of claim 35 wherein said binding amount of said polymer is applied to said particulate material mineral ore concentrate at an active polymer concentration in said concentrate between about 0.001 percent and about 0.3 percent by weight of dry concentrate.
- 43. The process of claim 37 wherein said particulate material is taconite concentrate.
- 44. The process of claim 43 wherein said clay is bentonite.
- 45. A product of the process of claim 35.
- 46. A product of the process of claim 44.
- 47. A process for manufacturing agglomerated mineral ore flux pellets, comprising:
- (a) commingling:
- (i) a binding amount of a water-soluble, binding polymer dispersed in a non-aqueous dispersion medium onto a taconite mineral ore;
- (ii) bentonite, said bentonite being applied to said taconite in an amount up to about 25 pounds per tonne of said taconite; and
- (iii) an inorganic material, thereby forming a composition of said polymer, bentonite and inorganic material, said composition having a basicity ratio of about 0.60 or higher;
- (b) agglomerating said composition to form green balls by a means for balling mineral ore concentrate; and
- (c) firing said green balls by a means for applying sufficient heat to indurate said green balls and produce pellets thereby.
- 48. The process of claim 47, wherein said polymer is a poly(acrylamide) based polymer.
- 49. The process of claim 48 wherein said polymer contains repeating units of the following formula: ##STR36## wherein R.sub.2.sup.+ is an alkali metal ion, and f is from 5 to about 90 percent, g is from 5 to about 90 percent, (f)+(g) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 50. The process of claim 49 wherein said polymer is derived from monomer units of acrylamide and sodium acrylate.
- 51. The process of claim 48 wherein said polymer contains repeating units of the following formula: ##STR37## wherein R, R.sub.1 and R.sub.3 are independently hydrogen or methyl, R.sub.2.sup.+ is an alkali metal ion, R.sub.4 is either
- (1) --OR.sub.5 wherein R.sub.5 is an alkyl group having up to 5 carbon atoms;
- (2) ##STR38## wherein R.sub.6 is an alkyl group having up to 8 carbon atoms; (3) ##STR39## wherein R.sub.7 is either methyl or ethyl; (4) phenyl;
- (5) substituted phenyl;
- (6) --CN; or
- (7) ##STR40## and hydrolized tetrapolymers thereof, wherein (a) is from about 5 to about 90 percent, (b) is from 0 to about 90 percent, (c) is from about 0 to about 20 percent, (a)+(b)+(c) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 52. The process of claim 51 wherein said polymer is derived from monomer units of acrylamide, sodium acrylate and vinyl acetate.
- 53. The process of claim 48 wherein said bentonite is applied in an amount up to about 20 pounds per tonne of taconite.
- 54. The process of claim 53 wherein said bentonite is applied in an amount up to about 10 pounds per tonne of taconite.
- 55. The process of claim 48 wherein sodium carbonate is commingled with said inorganic material selected to make the flux pellet.
- 56. A process for manufacturing agglomerated mineral ore flux pellets, comprising:
- (a) commingling:
- (i) a binding amount of a water-soluble, binding polymer, said polymer applied as a dry powder onto a taconite mineral ore;
- (ii) bentonite, said bentonite being applied to said taconite in an amount up to about 25 pounds per tonne of said taconite; and
- (iii) an inorganic material, thereby forming a composition of said polymer, bentonite and inorganic material, said composition having a basicity ratio of about 0.60 or higher;
- (b) agglomerating said composition to form green balls by a means for balling said mineral ore concentrate; and
- (c) firing said green balls by a means for applying sufficient heat to indurate said green balls and produce pellets thereby.
- 57. The process of claim 56, wherein said polymer is a poly(acrylamide) base polymer.
- 58. The process of claim 57 wherein said polymer contains repeating units of the following formula: ##STR41## wherein R.sub.2.sup.+ is an alkali metal ion, and f is from 5 to about 90 percent, g is from 5 to about 90 percent, (f)+(g) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 59. The process of claim 58 wherein said polymer is derived from monomer units of acrylamide and sodium acrylate.
- 60. The process of claim 57 wherein said polymer contains repeating units of the following formula: ##STR42## wherein R, R.sub.1 and R.sub.3 are independently hydrogen or methyl, R.sub.2.sup.+ is an alkali metal ion, R.sub.4 is either
- (1) --OR.sub.5 wherein R.sub.5 is an alkyl group having up to 5 carbon atoms;
- (2) ##STR43## wherein R.sub.6 is an alkyl group having up to 8 carbon atoms; (3) ##STR44## wherein R.sub.7 is either methyl or ethyl; (4) phenyl;
- (5) substituted phenyl;
- (6) --CN; or
- (7) ##STR45## and hydrolized tetrapolymers thereof, wherein (a) is from about 5 to about 90 percent, (b) is from 0 to about 90 percent, (c) is from about 0 to about 20 percent, (a)+(b)+(c) equal 100 percent, and (d) is an integer of from about 1,000 to about 500,000.
- 61. The process of claim 60 wherein said polymer is derived from monomer units of acrylamide, sodium acrylate and vinyl acetate.
- 62. The process of claim 57 wherein said bentonite is applied in an amount up to about 20 pounds per tonne of taconite.
- 63. The process of claim 62 wherein said bentonite is applied in an amount up to about 10 pounds per tonne of taconite.
- 64. The process of claim 57 wherein sodium carbonate is commingled with said inorganic material selected to make the flux pellet.
- 65. A product of the process of claim 48.
- 66. A product of the process of claim 57.
Parent Case Info
This application is a continuation-in part application of U.S. Ser. No. 903,968, filed Sept. 5, 1986, which was a continuation-in-part application of U.S. Ser. No. 736,237, filed May 21, 1985, now abandoned. This application is also a continuation-in-part application of U.S. Ser. No. 875,250, filed June 17, 1986, which was a continuation of U.S. Ser. No. 773,700, filed Sept. 9, 1985, now abandoned.
US Referenced Citations (13)
Foreign Referenced Citations (10)
Number |
Date |
Country |
0533975 |
Dec 1956 |
CAX |
0890342 |
Jan 1972 |
CAX |
265133 |
Jun 1970 |
SUX |
277808 |
Aug 1970 |
SUX |
648626 |
Feb 1979 |
SUX |
662021 |
May 1979 |
SUX |
901313 |
Jan 1982 |
SUX |
954464 |
Aug 1982 |
SUX |
996485 |
Jan 1983 |
SUX |
1063850 |
Dec 1983 |
SUX |
Non-Patent Literature Citations (5)
Entry |
Kramer, 29th An. Min. Symp. (1968) 145:51. |
Armstrong, Aus. I.M.M. Conf. (1973) 543:6. |
Dokuchayev, et al., "Utilization of Surface-Active Agents in Pelletization of Iron Ore Concentrates", Metallurgy and Mining Institute, Bulletin of Scientific and Technical Information, Production of Sbornik, No. 3, pp. 5-8 (1972) (English translation). |
Bereschnoy et al., Pelletizing Fine Grained Iron Ore Concentrates, Moscow, Nedra Publishers (1971). |
Pozihidayeva et al., "Selection of a Binder Additive for the Manufacture of Pellets", Izvestiya VUZ-ov. Ferrous Metallurgy No. 2, pp. 13-15 (1984); (English translation). |
Continuations (1)
|
Number |
Date |
Country |
Parent |
773700 |
Sep 1985 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
903968 |
Sep 1986 |
|
Parent |
736237 |
May 1985 |
|