The present invention relates to a process for coating a guide.
It is well known that guides made of metal material are used in the field of industrial machinery in order to permit handling one or more parts of the machinery.
A particular type of machine the portions of which are moved sliding on guides is represented by machines for machining and welding elements made of PVC.
Generally, these machining operations require extreme precision, and so, to move parts, arms, tools and the like, ball-bearing guides are used.
In particular, the guides are provided with a seat in which the balls roll without scraping, and so such seat must have a sufficiently smooth and homogeneous surface finish, so as not to create friction.
The PVC is hot welded, i.e. by melting part of the material and juxtaposing the flaps of the elements to be welded.
However, during melting, a small fraction of the PVC tends to decompose, so gaseous chlorine is released which reacts with the water in the air in the form of moisture, producing hydrochloric acid.
As is known, hydrochloric acid is a strong acid and is extremely corrosive, therefore all parts of the machine can undergo corrosion during the course of even short time intervals. Furthermore, the gaseous chlorine which develops determines the corrosion of the steel by pitting, causing the formation of holes that affect the stability of the workpiece.
In order to curb the corrosive effects of the chlorine, the most important parts of the machine from the machining point of view, i.e. tool bits and the like, are made of stainless steel, which is resistant to corrosion, but which has rather high costs compared to common carbon steel.
The remaining parts of the machine, including the guides, are generally made of common steels subsequently treated or coated to make them more resistant to corrosion.
Typical treatments which the machine parts undergo include coating the surfaces with a layer made of a metallic material or resin.
In particular, coating with metallic material is generally done by means of chrome or nickel plating processes, which allow the deposition of a very thin layer of chrome or nickel respectively.
Such coating gives the workpiece greater resistance to corrosion, but also greater surface hardness.
However, the metals used have limited corrosion resistance and after a certain time the coating is damaged by the corrosive action of the hydrochloric acid.
In particular, nickel has a higher corrosion resistance than chromium, as well as better adhesion to the surface to be coated, so nickel plating is far more widely used than chromium plating.
If, on the other hand, the metal guides are coated with resins, the operation is carried out by means of cataphoresis painting.
This process makes it possible to deposit a thin layer of resin on the surface of the metal guide in order to make it resistant to corrosion.
However, the resin layer has a rather rubbery texture, so it is not very suitable for the sliding of the balls, which would end up scraping on the surface of the seat.
Moreover, the resulting resin layer is rather delicate and the scraping of the balls can damage it or even partially remove it, leaving the surface of the guide uncovered.
However, these metal guide coating processes do have a number of drawbacks.
In fact, the nickel or chrome coating of the guides does not guarantee absolute protection from corrosion, but only for a certain period of time, so periodic maintenance of the metal guides is required, so as to restore the coating thereof.
However, in order to do this maintenance work, the machine must be stopped and dismantled, with a significant increase in operating costs related to both labor and machining operations for the restoration of the coating, but also due to operation downtimes.
Moreover, the periodic metal coating restoration operations give rise to a ball sliding seat surface which can become irregular from the point of view of thickness, negatively affecting the correct movement of the machine parts, with negative effects on machining operation precision.
On the other hand, the coating of the guides with resin by means of cathodic painting does not ensure the correct sliding of the balls along the seat, and these tend to scrape, also removing part of the resin and leaving the guide exposed to corrosion.
The main aim of the present invention is to provide a process for coating guides which permits effectively protecting the surface from corrosion.
As part of the described aim, one object of the present invention is to make it possible to reduce operating costs, particularly those associated with special maintenance.
Another object of the present invention is to ensure the correct movement of the sliding parts on the metal guide.
Another object of the present invention is to provide a process for coating a guide, which allows overcoming the aforementioned drawbacks of the prior art within the scope of a simple, rational, easy, efficient to use and cost-effective solution.
The aforementioned objects are achieved by the present process for coating a guide according to claim 1.
Other characteristics and advantages of the present invention will become more evident from the description of a preferred, but not exclusive embodiment of a process for coating a guide, illustrated by way of an indicative, but non-limiting example, in the attached drawings in which:
With particular reference to these illustrations, reference numeral 1 globally indicates a process for coating a guide.
The process for coating a guide according to the invention comprises at least the steps of supplying at least one guide 1 made of metallic material and comprising at least one outer surface 2, 3 provided with at least a first portion 2 adapted to slide at least one carriage 4 and at least a second portion 3 separate from the first portion 2.
Preferably, the guide 1 is made of carbon steel, but the possibility of providing a guide 1 made of non-metallic material, such as plastic, cannot be ruled out.
In the embodiment shown in the
In other words, the guide 1 is similar to a rail on which the carriage 4 is mobile and is provided with two opposed end faces 5.
In particular, the guide 1 and the carriage 4 are movable with respect to each other along the main axis A.
In the alternative embodiment shown in
In this case, the carriage 4 follows the path provided by the first portion 2, so it rotates around the main axis A and simultaneously moves with respect to the guide 1 along the main axis itself.
Advantageously, the first portion 2 is shaped to define at least one sliding slot 6 with cross section at least partly circular and concave in which a plurality of balls 7 are sliding which are adapted to move the carriage 4.
It is, in fact, a recirculation ball guide, wherein the balls 7, preferably made of steel, are housed inside the sliding slot 6 and, by means of their rolling, allow the relative movement between the guide 1 and the carriage 4.
In particular, the recirculation of the balls 7 is inside the carriage 4, i.e. the carriage itself is provided with at least one recirculation duct 8 inside which the balls 7 are preloaded which by rolling slide inside the circuit that is determined between the sliding slot 6 and the recirculation duct 8, thus transforming the rolling of the balls 7 into a crossways movement for the movement of the carriage 4 with respect to the guide 1.
The use of a guide 1 of this type provides numerous advantages in terms of high machining precision and high resistance to wear, also due to the fact that the guide 1 and the carriage 4 are never in direct contact with each other.
Usefully, the guide 1 comprises a plurality of first portions 2 each shaped to define a sliding slot 6.
In the particular embodiment shown in the Figures from 1 to 5, the guide 1 is a linear guide which comprises four first portions 2 each shaped to define a respective sliding slot 6 with cross section at least in part circular and concave in each of which is sliding a respective plurality of balls 7 adapted to move the carriage 4.
Consequently, in this particular embodiment, the carriage 4 is provided with four recirculation ducts 8 for the recirculation of the balls 7 which roll on each of the sliding slots 6.
The fact of providing a plurality of sliding slots 6 allows obtaining a more stable carriage 4 trim and a better load distribution.
The guide 1 shown in the illustrations is intended to be mounted on at least one PVC-working machine, such as a welding machine or the like, and the carriage 4 is associated with the parts of the machine itself and is adapted to the movement thereof, so as to perform the machining operations correctly.
Generally, the operations carried out on the PVC, in particular welding, are carried out using hot methods.
Because of the high temperatures, during working operations, the PVC tends to decompose, albeit to a small extent, releasing gaseous chlorine which reacts with the water in the air in the form of moisture, thus producing hydrochloric acid.
Hydrochloric acid is a strong acid and is extremely corrosive, therefore all the parts of the machine can be subject to corrosion in even short periods of time.
Furthermore, the gaseous chlorine which develops from decomposition causes the corrosion of the steel by pitting, causing the formation of holes that affect the stability of the workpiece.
Some parts of the machine are made of special steels, so that they are highly resistant to corrosion and to prevent them being damaged and periodically replaced.
However, these special steels have high costs, so the secondary elements of the machine, including the guide 1, are made from standard steels that are cheaper but are not resistant to the corrosive effect of the hydrochloric acid.
Still according to the invention, the process comprises at least the step of depositing at least a first coating layer 9 on the first portion 2 and on the second portion 3.
As schematically shown in the figures, in the deposition step the first coating layer 9 also deposits on the end faces 5 of the guide 1.
Usefully, the first coating layer 9 is metallic and is aimed at protecting the guide 1 from corrosion.
In particular, the deposition step of the first coating layer 9 is made by nickel-plating and, consequently, such first coating layer 9 is nickel.
The possibility of carrying out the deposition step of the first coating layer 9 by means of a treatment other than nickel plating, such as chrome plating, cannot however be ruled out, so that in this case the first coating layer 9 is made of chrome.
Nickel plating is a surface treatment applicable to objects of any shape and that allows making a nickel surface coating on the machined object, in order to increase its resistance to corrosion.
Nickel, in fact, is a more electronegative metal than the iron contained in the steel of which the guide 1 is composed and consequently it is more resistant to corrosion, including chlorine corrosion.
In particular, nickel plating involves the deposition of metallic nickel to form the first coating layer 9 by means of the reduction of nickel ions and can be performed chemically or electrolytically.
Advantageously, the nickel plating step is carried out by means of chemical nickel plating, which allows the deposition of the first coating layer 9 to be obtained by the direct action of reducing substances on the nickel ions to be deposited, although the possibility of making nickel plating by means of electrolytic nickel plating cannot be ruled out.
The first coating layer 9 obtained by means of chemical nickel plating is characterized by a very low porosity, so it has a sealing effect that prevents the penetration of the gaseous chlorine, which does not thus come into contact with the steel of which the guide 1 is made, protecting it from the corrosive effect of chlorine.
Moreover, chemical nickel plating allows obtaining a first coating layer 9 with a very smooth and regular surface finish and an extremely uniform thickness irrespectively of the shape and material of the guide 1, thus avoiding any grinding after the nickel plating step and ensuring the correct operation of the guide itself.
In particular, the fact of obtaining the first coating layer 9 with a remarkably regular surface finish is particularly important for the correct operation of the guide 1, as it ensures the rolling of the balls 7 inside the sliding slot 6, without the risk of scraping and the onset of friction.
Furthermore, the distance between the carriage 4 and the outer surface 2, 3 of the guide 1 is extremely small and the machine provides for a system of zero setting of the plays that minimize such distance.
Consequently, the fact that the first coating layer 9 has an extremely regular thickness allows the machine to be moved without the risk of the carriage 4 scraping on the outer surface 2, 3 of the guide 1.
Moreover, precisely because of the minimum distances between the guide 1 and the carriage 4, the thickness of the first coating layer 9 must be as small as possible, compatibly with the protective effect of the material.
In particular, the thickness of the first coating layer 9 is between 1 μm and 20 μm, that is, they are extremely small dimensions that allow ensuring the correct related movement between guide 1 and carriage 4.
Preferably, first coating layer 9 has a thickness equal to 10 μm, although the possibility of having a different thickness cannot be ruled out.
It is important to underline that within the scope of the present discussion, the representation of the first coating layer 9 has been carried out as an example and that such first coating layer has been represented with a considerably greater thickness than the real value in order to make it easily distinguishable.
Chemical nickel plating is a chemical reduction process carried out in a nickel plating tank 10 in which a nickel plating bath 11 is prepared in which the guide 1 to be treated is soaked.
Such nickel plating bath 11 consists of an aqueous solution containing nickel in the form of salt, in particular nickel chloride (NiCl2), together with a reducing agent, which is generally identifiable in the hypophosphite ion (H2PO2) which is inserted in the nickel plating bath itself in the form of sodium hypophosphite (NaH2PO2).
The use of a different nickel agent or the supply of nickel in the form of a salt different to that mentioned cannot however be ruled out.
During the nickel plating step of the guide 1, the hypophosphite ions are catalytically oxidized to phosphite ions, generating gaseous hydrogen, and causing the simultaneous reduction of the nickel cations to metallic nickel, which deposits on the first portion 2 and on the second portion 3, thus forming the first coating layer 9.
Still according to the invention, the process comprises at least one step of painting by cataphoresis of the guide 1 adapted to deposit at least a second coating layer 12 onto the first portion 2 and onto the second portion 3 on top of the first coating layer 9.
As in the nickel-plating step, in the cataphoresis painting step as well, the second coating layer 12 is also deposited on the end faces 5 of the guide 1, as well as on the outer surface 2, 3.
Painting by cataphoresis is a surface coating process which permits obtaining a second coating layer 12 with an extremely uniform thickness.
In particular, the second coating layer 12 has a thickness comprised between 15 μm and 35 μm.
Preferably, the second coating layer 12 has a thickness equal to 25 μm, although the possibility of having a different thickness cannot be ruled out.
As discussed above, it should be noticed that within the scope of the present discussion the representation of the second coating layer 12 was carried out as an example and that such second coating layer was represented with a significantly greater thickness than the real value in order to make it distinguishable.
Advantageously, the second coating layer 12 is made in at least one of an epoxy resin and an acrylic resin, i.e. polymeric materials characterized by high resistance to the action of acids, so they make it possible to protect the guide 1 from the corrosive action of hydrochloric acid.
In general, “cataphoresis” means the movement of positively charged particles soaked in a fluid by the effect of an electric field applied by means of a pair of electrodes.
In particular, painting by cataphoresis is carried out by electrochemical deposition of epoxy resin or acrylic resin which, within the polymer chain, comprise groups with considerable polarity, which therefore make them susceptible to the action of the electric field.
In practice, painting by cataphoresis is carried out in at least one cataphoresis tank 13 inside which at least one painting bath 14 is prepared, consisting of an aqueous solution wherein the epoxy resin or the acrylic resin is dispersed, which, being polar, is at least partly soluble in water, as well as in dyes and additives.
The guide 1 is soaked in the painting bath 14 and connected to a negative pole 15 of an electric generator 16, while a positive pole 17 is soaked in the painting bath itself.
The electric field and the electrochemical phenomena that occur inside the painting bath 14 cause the resin macromolecules to migrate towards the guide 1 and deposit on the outer surface 2, 3, forming the second coating layer 12.
Furthermore, the possibility cannot be ruled out of the guide 1 undergoing a drying step in the oven at the end of the cataphoresis painting step, which permits carrying out the polymerization of the second coating layer 12, which is particularly useful when using a thermosetting resin, such as, e.g., epoxy resin.
Finally, according to the invention, the process comprises at least one removal step of the second coating layer 12 from the first portion 2.
The resins of which the second coating layer 12 is composed have a rather rubbery texture, which does not allow the correct rolling inside the sliding slot 6 of the balls 7, which therefore tend to scrape on the resin, which being soft generates considerable friction.
Moreover, the scraping of the balls 7 tends to detach the second coating layer 12, creating accumulations of resin inside the sliding slot 6 that would prevent the correct movement of the carriage 4 with respect to the guide 1.
Consequently, the removal step of the second coating layer 12 from the first portion 2 causes the balls 7 to rest on the first coating layer 9, which has a smooth and homogeneous surface finish and allows the balls themselves to roll without scraping.
Usefully, the second coating layer 12 is removed only from the first portion 2, while it is maintained on the second portion 3, in order to protect the uncovered parts of the guide 1 from the corrosive action of the hydrochloric acid and gaseous chlorine.
Despite the removal of the second coating layer 12, the first portion 2 remains protected against corrosion by the first coating layer 9.
Furthermore, the rolling of the balls 7 carries out a self-cleaning action of the system, as the rolling friction that occurs during the rolling of the balls themselves performs a micro-abrasion action on any deposits of oxides or dirt, keeping the sliding slot 6 in optimal working conditions.
Advantageously, the removal step is performed manually by using at least one tool 18 which is shaped in a manner at least partly complementary to the first portion 2.
In this way, therefore, it is possible to remove the second coating layer 12 in a precise manner without the risk of damaging the surface finish of the first coating layer 9.
Usefully, the tool 18 is provided with at least one removal portion 19 having a shape which is at least partly circular and convex, adapted to allow the second coating layer 12 to be removed from the first portion 2, as well as at least one grip portion 20 adapted to be gripped by the operator.
The shape of the removal portion 19 is such as to allow the resin to be removed in a single pass and, being convex, allows the material to be removed avoiding the formation of accumulations, so as to optimize the processing times.
In combination or as an alternative to manual removal, the removal step of the second coating layer 12 is performed automatically by using at least one laser device pointing towards the first portion 2.
The use of the laser applied to the first portion 2 effectively removes the second coating layer 12.
It is also possible to use in combination manual removal and automatic removal in order to make removal by means of the tool 18 less difficult, obtaining a qualitatively high result.
It is emphasized that
In particular, the guide 1 is provided with only one first portion 2 and, consequently, with only one sliding slot 6 inside which the balls 7 slide.
The sliding slot 6 has a helical shape and this allows the carriage 4 to move in rotation around the main axis A and in translation along the same axis.
Given the shape of the guide 1, the carriage 4 is provided with a single recirculation duct 8 inside which the balls 7 re-circulate.
It has in practice been found that the described invention achieves the intended objects.
In this regard, it is underlined that the particular solution of providing a process for coating a guide allows effectively protecting the surface from corrosion.
Furthermore, the particular solution of providing a nickel plating step followed by a cataphoresis painting step allows protecting the guide from corrosion for a considerably long time, thus reducing the frequency of maintenance and associated costs.
In particular, the process allows considerably limiting corrosion due to chlorine and to the attack of acids, thus reducing the frequency and related costs of special maintenance. Moreover, the particular solution of carrying out the nickel plating step by means of chemical nickel plating allows obtaining an extremely smooth and regular surface finish of the first coating layer, so that there is no need for grinding or further treatments, thus reducing operating costs.
Furthermore, the particular solution of providing the removal step of the second coating layer from the first portion allows ensuring the correct rolling of the balls housed inside a ball-bearing carriage that moves along the guide.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102017000141347 | Dec 2017 | IT | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2018/059669 | 12/5/2018 | WO | 00 |