Process for continuous xanthation and production of viscose spinning solution

Description

This invention pertains to process and apparatus for continuously xanthating alkali cellulose (AKC) and for converting such alkali cellulose into a spinnable viscose solution.
In many conventional processes for making viscose spinning solution, alkali cellulose is xanthated by contact with carbon disulfide (CS.sub.2) in a batch process. Typically, the alkali cellulose is in crumb or shredded form and is converted into a sticky mass by xanthation.
Numerous efforts have been made to provide a commercially acceptable continuous xanthation process and apparatus therefor. Examples include the processes and apparatus disclosed in U.S. Pat. Nos. 2,762,795-Schlosser et al (xanthation of sheet alkali cellulose passing through a sealed chamber), 2,801,998-Robertson (conventional crumb xanthation followed by later stage involving continuous mixing in wet forms), 2,987,647-Von Kohorn (continuous xanthation of crumb), 3,385,845-Trieber (semi-continuous batch addition and passage through dry xanthation stage followed by a final wet stage), 3,438,969-Meister (xanthation in a kneader-type reactor followed by a vertical column and subsequent vertical solution-forming tower with agitator) and 3,671,279-Yasui et al (continuous kneading and passage of crumb and dough-like material).
Of these, Robertson is most pertinent to the present invention in that it involves a first dry xanthation stage and a second wet or immersion stage. In all of these "staged" processes, however, the CS.sub.2 is fully reacted and the xanthation reaction, with the available CS.sub.2, is taken to completion in the first stage. This procedure neglects the sequential path of the xanthation reaction in which the secondary hydroxyls of the cellulose molecule (the conventionally designated C.sub.2 and C.sub.3 positions) are readily substituted in a matter of minutes while the transfer of the substituted CS.sub.2 to the primary hydroxyl (at the conventionally designated C.sub.6 position) takes much longer. The latter transfer, however, occurs much more readily in a slurry xanthate reaction.
Having in mind certain inherent disadvantages in the continuous or semi-continuous xanthation processes and apparatus heretofore known, and in the processes and apparatus for the subsequent conversion of the xanthate product into a spinning solution, it is the general object of the present invention to provide an improved and more practical process and apparatus for continuously converting either shredded crumbs or continuous strips of alkali cellulose in sheet form into, ultimately, a viscose spinning solution.
A more specific objective of this invention is to provide process and apparatus facilitating in-line continuous xanthation and dissolution of the xanthated product in stages designed to effect maximum overall efficiency and minimum process problems associated with typical batch and semi-batch processes.
These objectives, and others which will be apparent in the course of the subsequent discussion, are met, briefly, by a xanthation system including a vessel containing a CS.sub.2 -alkali hydroxide slurry in which alkali cellulose feed, which has been first partially xanthated in a dry state for a short period of time, is immersed and held for a period of time. Carbon disulfide is also introduced into the vessel at a rate to effect at least partial xanthation of the incoming alkali cellulose feed at its pre-selected feed rate. Slurry is withdrawn from the bottom of the vessel at a rate to maintain a minimum residence time, on the order of 5-10 minutes, of alkali cellulose in the vessel. Means are also included for introducing make-up alkali hydroxide solution to maintain a constant level of liquid slurry in the vessel.
The process is generally carried out at atmospheric pressure with a temperature maintained in the range of 30.degree.-45.degree. C., preferably about 35.degree. C. Slurry taken from the slurry holding vessel is transferred to a screw extruder mixer where further mixing and xanthation occur, with the further addition of carbon disulfide and alkali hydroxide solution as necessary.
The alkali cellulose feed to the slurry vessel (where it is first immersed and reacted) is a shredded partially pre-xanthated alkali cellulose which is delivered through a closed passageway from a closed pre-xanthation chamber into which sufficient carbon disulfide is introduced to effect the desired partial pre-xanthation. Means may also be included for introducing an indefinite length strip of alkali cellulose in sheet form in a continuous manner into such a pre-xanthation chamber with sealing means to prevent escape of gases therefrom at the alkali cellulose entry point. The alkali cellulose is passed continuously through the chamber, where it is partially pre-xanthated (and shredded, if in sheet form), and from there to the slurry xanthation vessel previously described.
The present invention also encompasses continuous mixing and spinning solution-forming means particularly adapted to be used downstream of and in conjunction with the continuous xanthation process and apparatus of this invention. This continuous mixing means comprises generally an elongated passageway preferably including mass dividers or "attritors" near the upstream end thereof to break down the otherwise viscous sticky mass of xanthated alkali cellulose passing therethrough. The elongated passageway also includes, at spaced intervals, means for introducing additional alkali hydroxide solution followed by internal mixers continuously mixing the newly introduced alkali hydroxide solution with the mass in the passageway. At least two such additional solution introducing means and internal mixing means should be spaced at intervals along the passageway. Downstream, a homogenous solution of xanthated alkali cellulose and alkali hydroxide is delivered in form suitable for aging, if required, filtration and spinning into fiber form.

This invention may be better understood by reference to the subsequent detailed description thereof, taken in conjunction with the appended claims and the figures, wherein:
FIG. 1 is a diagrammatical illustration of the basic elements of the dry and slurry xanthation and viscose spinning solution forming apparatus of the present invention in its preferred embodiment; and
FIG. 2 is a diagrammatical illustration of one type of pre-xanthation and shredding stage preferably used in combining the xanthation process and apparatus of this invention with a continuous sheet steeping process for producing alkali cellulose.

The xanthate reaction, that is the reaction between CS.sub.2 and AKC, can take place in the gas-solid phase or in the solution phase (that is, CS.sub.2 introduced into a slurry of AKC, NaOH and water). There are advantages to be gained in both quality and speed of reaction by using both reaction mechanisms. In the initial stages of the reaction it is advantageous, both for final quality, and speed of complete xanthation and mixing, to utilize the gas-solid reaction, keeping the AKC "dry" i.e., undissolved. In less than five minutes, the CS.sub.2 can be substituted on the C.sub.2 and C.sub.3 hydroxyls (the secondary hydroxyls) in the dry pre-xanthation stage. Subsequently the reaction of xanthation and solution (including transfer of the CS.sub.2 to the C.sub.6 or primary hydroxyl position to complete the xanthation process) proceeds at a much higher rate if it is carried out in solution or slurry. In the process and apparatus of the present invention, maximum advantage is taken of both of these reaction possibilities.
Turning more specifically to FIG. 1, there is shown a process and apparatus wherein shredded alkali cellulose or crumb 1 is fed into the top of a cylindrical column 2. The AKC is advanced vertically down the column by means of an advancing screw 3. Approximately 5 feet down the column, CS.sub.2 is introduced through several spray heads 4 placed around the column. The height of AKC above the CS.sub.2 spray heads 4 serves to seal off CS.sub.2 preventing it from escaping upward out of the apparatus as the AKC will absorb and react with all the CS.sub.2 introduced. The xanthate reaction is thereby initiated in this region. The AKC-CS.sub.2 mixture continues downward in the column for approximately five feet more while the xanthate reaction is progressing. Its total residence time in this part of the reactor is on the order of 3-20 minutes and 5-35% of the total required CS.sub.2 is introduced in this dry stage. The reacting mass is then introduced into a larger diameter column called the primary reactor 5. A second advancing screw 6 insures the uniform advancement of the mass downward. However, this screw is designed to turn at a moderate speed and to insure thorough blending and mixing throughout the reactor. At the head of this reactor additional CS.sub.2 is added by injectors 7 and directly thereafter a water solution of alkali hydroxide, usually Na0H, is introduced through injectors 8. The AKC has by this time become partially xanthated and the solubility in weak alkali has increased to the point that partial dissolution takes place. The dissolved and partially reacted AKC forms a slurry in which the xanthate reaction continues and dissolution of the AKC-xanthate continues as it forms.
The CS.sub.2 added in the crumb or shredded AKC column, and in the primary reactor constitutes a large portion, if not all, of the total CS.sub.2 charge required. In some cases a third portion of CS.sub.2 may be added through injection to the secondary reactor, to be described later.
Near the top of the primary reactor there may be introduced a recirculated stream of nearly dissolved, and completely xanthated slurry through recycle line 10 from the end of the secondary reactor also including recycle slurry pump SP.sub.1. The purpose of this recirculation is to take advantage of the fact that partially xanthated AKC dissolves more readily and uniformly in viscose solution than in a water solution of Na0H or K0H.
From the primary reactor the slurry is continuously pumped, by slurry pump 11, into the secondary reactor. The rate of pumping is of course equal to the rate necessary to remove cellulose from the AKC column 2 as it is introduced. The dwell time in the primary reactor 5 is approximately 10 minutes. The secondary reactor 12 follows the same general design as the primary reactor. However, the vessel is larger, in order to achieve a dwell time of up to 60 minutes. NaOH and H.sub.2 O are introduced through inlet lines 13 at the top of the reactor 12, to further the progress of dissolution. A third portion of the total CS.sub.2 charge may in some cases also be added here through injectors 9 although in most instances the total CS.sub.2 required will have been added in the AKC column 2 and in the primary reactor 5. The advancing screw 14 in secondary reactor 12, as in the primary reactor, is designed to insure uniform advance and thorough blending of the chemical mass. From the outlet of this reactor some viscose slurry may be recirculated to the beginning of the primary reactor through recycle line 10 as discussed above.
From the secondary reactor the slurry is pumped by SP.sub.2 continuously through a series of attrition mixing chambers 15-16. The viscose slurry is passed alternately through attrition mills 16 and then mixed by high speed blending propellers 17. Fractions of the total caustic solution charge are added through inlet lines 18 in various cells 15.
It is well known that the most efficacious way to bring viscose into final solution is to do most of the mixing and kneading while the slurry is thick and pasty. After a homogenous, essentially dissolved, concentrated solution is achieved the final addition of water and caustic are added to bring the solution to the desired final composition. In this way maximum homogeneity is achieved with a minimum of undissolved gels, in minimum solution time.
Heretofore, it has not been practicable to take advantage of this principle as batch xanthate and mixing processes were not well adapted to use the techniques required.
In this process, xanthation and mixing is achieved in about 90 minutes or less by a continuous process requiring little direct labor. Furthermore, the viscose is expected to be of better quality and spinability than any heretofore achieved commercially. This process has been shown in its preferred form with vertical columns and advancing screws. However, horizontal vessels with equivalent advancing mechanisms may also be used.
Turning now to FIG. 2, there is shown a prexanthation stage in which a continuous sheet of AKC is partially xanthated and shredded prior to passage to the xanthation process and apparatus shown in FIG. 1. More specifically, a continuous sheet of mercerized alkali cellulose 21 is fed continuously by means of feed rolls 22 into an enclosed chamber 23. Chamber 23 may be connected to a carbon absorption-type CS.sub.2 recovery system conventionally used in the viscose process for recovering dilute mixtures of CS.sub.2 gas from air. If desired this chamber may contain a nitrogen atmosphere.
The advancing sheet of AKC is fed over "kiss" rolls 24 whereby CS.sub.2 is picked up from a feeding system 25 and imparted to the AKC sheet. The sheet is then passed through disintegrator 26 and the shredded crumbs 27 are fed into the AKC column 2 of FIG. 1. Alternatively, instead of using "kiss" rolls, a spray of CS.sub.2 may be injected onto the sheet from each side. CS.sub.2 injectors 4 (of FIG. 1) may be omitted if the dry pre-xanthation is accomplished in a chamber such as that shown in FIG. 2.
The following examples typify proposed conditions and expected results in the possible practice of the present invention.
EXAMPLE 1
The feed to the continuous xanthator is an alkali cellulose, by weight:
33% cellulose,
15% Na0H,
52% h.sub.2 o.
this AKC is pre-shredded, and is fed to initial xanthate and seal column 2 at a rate of 150 pounds per minute. The following total amounts of materials are added throughout the reaction:
14 pounds CS.sub.2 per minute
380 pounds H.sub.2 O per minute
11 pounds Na0H per minute
to produce a final desired viscose which has the composition:
28.0% CS.sub.2, based on dry cellulose weight,
9.0% cellulose, based on viscose weight,
6.0% NaOH, based on viscose weight,
82.5% H.sub.2 O, based on viscose weight.
Portions of CS.sub.2 are added at the points indicated as follows:
______________________________________Point CS.sub.2 (pounds added per min)______________________________________4 FIG. 1 4.77 FIG. 1 4.79 FIG. 1 4.6______________________________________
Portions of H.sub.2 O and NaOH are also added at the places and in amounts as follows:
______________________________________ (pounds added) (pounds added)Point NaOH per minute H.sub.2 O per minute______________________________________8 FIG. 1 5.5 48.413 FIG. 1 5.5 48.418a FIG. 1 0.0 94.418b FIG. 1 0.0 94.418c FIG. 1 0.0 94.4______________________________________
The dwell times, and operating temperatures for the various stages of the process, as shown in FIG. 1, are given in the table below:
______________________________________Reaction Stage Dwell Timeor Position (minutes) Temperature(.degree. C.)______________________________________Incoming AKC FIG. 1 40Reactor 2 FIG. 1 15 40 - 35Reactor 5 FIG. 1 10 35Reactor 12 FIG. 1 35 35Attritor-Mixer 30 3016a, 16b, 16c,18a, 18b, 18c______________________________________
EXAMPLE 2
The alkali cellulose feed in this example comes from a continuous sheet double-steep-mercerizing system.
AKC feed to xanthator - mixing process (FIGS. 1-2)
10% naOH,
33% cellulose,
57% H.sub.2 O.
The final desired viscose is, as in Example 1:
28% CS.sub.2, based on dry cellulose weight,
9% cellulose, based on viscose weight,
6% NaOH, based on viscose weight,
82.5% H.sub.2 O, based on viscose weight.
Total chemicals added through the xanthate-mixing process:
14.0 pounds CS.sub.2, per minute
18.3 pounds NaOH, per minute
373.0 pounds H.sub.2 O, per minute
Portions of CS.sub.2 are introduced at the placed indicated as follows:
______________________________________Point CS.sub.2 (pounds added per minute)______________________________________24 FIG. 2 47 FIG. 1 59 FIG. 1 5______________________________________
Portions of NaOH and H.sub.2 O are added at the places and in the amounts indicated, as follows:
______________________________________ (pounds added) (pounds added)Point NaOH per minute H.sub.2 O per minute______________________________________8 FIG. 1 9.2 82.513 FIG. 1 9.1 82.518a FIG. 1 0.0 69.018b FIG. 1 0.0 69.018c FIG. 1 0.0 70.0______________________________________
The dwell times and operating temperatures for this example are as follows:
______________________________________Reaction Stage Dwell Timeor Position (minutes) Temperature(.degree. C.)______________________________________Chamber 23 FIG. 2 1 35Reactor 2 FIG. 1 15 35Reactor 5 FIG. 1 10 35Reactor 12 FIG. 1 35 35Attritor-Mixter 30 3516, 18 FIG. 1______________________________________
In each example, the temperature of the entering AKC may be varied from 30.degree. to 60.degree. C., depending upon method of mercerization. The preferred temperature in the primary and secondary reactors is 35.degree. C., but may vary between 30.degree.-45.degree. C.
While this invention has been described with reference to xanthation in the presence of an alkali hydroxide solution generally, normally this solution is sodium hydroxide. Potassium hydroxide may also be used.
Various other such minor modifications and variations of the present invention will be apparent to those skilled in the art. While this invention has been described, for purposes of definiteness and specificity as required by the statute, with respect to specific embodiments and examples, it should be understood that it is not limited thereto and that the appended claims are therefore intended to be construed to encompass those various modifications and variations which may be made in this invention without departing from the true spirit and scope thereof.

Claims

1. In a process for xanthating alkali cellulose by contacting said alkali cellulose with carbon disulfide, the improvement consisting of continuously feeding alkali cellulose at a predetermined rate first in dry form to a vessel where it is brought into contact for 3-20 minutes with 5-35% of the CS.sub.2 necessary to provide partial xanthation of the cellulose and then, prior to completion of reaction between said CS.sub.2 and said dry cellulose, passing said cellulose on to a vessel containing an alkali hydroxide slurry, immersing said cellulose therein while continuously introducing carbon disulfide into said vessel at a controlled rate, continuously feeding alkali hydroxide solution into said vessel at a controlled rate, and continuously withdrawing a portion of said slurry from the bottom of said vessel at a rate, selected to maintain a preselected minimum residence time of alkali cellulose in said vessel, then passing said withdrawn slurry through a screw extruder mixer, introducing further carbon disulfide and alkali hydroxide solution thereto, as required, to effect further xanthation therein.
2. An improved process, as recited in claim 1, wherein said minimum residence time in said slurry vessel is 5-10 minutes, the temperature of said slurry is about 35.degree. C. and the pressure in said vessel is about 1.0 atmospheres.
3. In improved process, as recited in claim 1, wherein a portion of the xanthated alkali cellulose product from said screw extruder mixer is recirculated to said slurry-containing vessel.
4. An improved process, as recited in claim 1, wherein said alkali hydroxide is sodium hydroxide and said alkali cellulose is sodium cellulose.
5. An improved process, as recited in claim 1, wherein said dry partially xanthated alkali cellulose is in strip form and passes through a closed passageway from a sealed chamber to said slurry-containing vessel.
6. An improved process, as recited in claim 5, wherein said alkali cellulose strip is shredded after it passes through said sealed chamber and before it enters said slurry-containing vessel.
7. An improved process, as recited in claim 1, wherein said alkali cellulose is shredded and passes downwardly into a vessel containing gaseous carbon disulfide, said incoming alkali cellulose capturing and preventing said carbon disulfide from escaping from the top of said vessel.

US Referenced Citations (1)

Number	Name	Date	Kind
2801998	Robertson	Aug 1957

Process for continuous xanthation and production of viscose spinning solution

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US