Claims
- 1. In a hydrocarbon conversion process for converting a sulfur-containing hydrocarbon feedstock which comprises (1) contacting said feedstock with solid particles capable of promoting the conversion of said feedstock at hydrocarbon conversion conditions in at least one reaction zone to produce at least one hydrocarbon product and to cause deactivating sulfur-containing carbonaceous material to be formed on said solid particles thereby forming deposit-containing particles; (2) contacting said deposit-containing particles with an oxygen-containing vaporous medium at conditions to combust at least a portion of said carbonaceous deposit material in at least one regeneration zone to thereby regenerate at least a portion of the hydrocarbon conversion catalytic activity of said solid particles and to form a regeneration zone flue gas containing sulfur trioxide; and (3) repeating steps (1) and (2) periodically, the improvement which comprises, using, in intimate admixture with said solid particles, a minor amount of discrete entities having a composition different from said solid particles and comprising at least one metal-containing spinel including a first metal and at least two different second metals having valences higher than the valence of said first metal, one of said second metals being aluminum and the other of said second metals being trivalent and selected from the group consisting of iron, chromium, vanadium, manganese, gallium, boron, cobalt and mixtures thereof, the atomic ratio of said first metal to said second metals in said spinel is at least about 0.17 and said spinel having a surface area in the range of about 25 m.sup.2 /gm. to about 600 m.sup.2 /gm., said discrete entities being present in an amount sufficient to reduce the amount of sulfur oxides in said flue gas.
- 2. The process of claim 1 wherein said conversion comprises hydrocarbon cracking in the substantial absence of added molecular hydrogen, said solid particles and discrete entities being fluidizable and circulating between said reaction zone and said regeneration zone.
- 3. The process of claim 2 wherein said hydrocarbon feedstock contains about 0.1% to about 5.0% by weight of sulfur.
- 4. The process of claim 2 wherein said discrete entities contains at least about 70% by weight of said spinel.
- 5. The process of claim 2 wherein at least one of said solid particles and discrete entities further comprise a minor, catalytically effective amount of at least one additional metal component capable of promoting the conversion of sulfur dioxide to sulfur trioxide at the conditions of step (2).
- 6. The process of claim 5 wherein said spinel comprises alkaline earth metal-containing spinel, and the atomic ratio of said first metal to said second metals in said spinel is at least about 0.25.
- 7. The process of claim 2 wherein said solid particles are separate from said discrete entities and the relative amounts of said solid particles and said discrete entities are in the range of about 80 parts to about 99 parts and about 1 part to about 20 parts by weight, respectively.
- 8. The process of claim 2 wherein said solid particles comprise at least one crystalline aluminosilicate capable of promoting hydrocarbon cracking at the conditions of step (1).
- 9. The process of claim 2 wherein said spinel includes magnesium as said first metal.
- 10. The process of claim 2 wherein said discrete entities contain at least about 90% by weight of said spinel.
- 11. The process of claim 1 wherein said other second metal is iron.
- 12. The process of claim 1 wherein said other second metal is chromium.
- 13. The process of claim 1 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 14. The process of claim 2 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 15. The process of claim 7 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 16. The process of claim 9 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 17. The process of claim 1 wherein said solid particles and said discrete entities are both present in combined particles.
- 18. In a hydrocarbon conversion process for converting a sulfur-containing hydrocarbon feedstock which comprises (1) contacting said feedstock with solid particles capable of promoting the conversion of said feedstock at hydrocarbon conversion conditions in at least one reaction zone to produce at least one hydrocarbon product and to cause deactivating sulfur-containing carbonaceous material to be formed on said solid particles thereby forming deposit-containing particles; (2) contacting said deposit-containing particles with an oxygen-containing vaporous medium at conditions to combust at least a portion of said carbonaceous deposit material in at least one regeneration zone to thereby regenerate at least a portion of the hydrocarbon conversion catalytic activity of said solid particles and to form a regeneration zone flue gas containing sulfur trioxide; and (3) repeating steps (1) and (2) periodically, the improvement which comprises, using, in intimate admixture with said solid particles, a minor amount of discrete entities having a composition different from said solid particles and comprising a major amount of at least one metal-containing spinel including a first metal and at least two different second metals having valences higher than the valence of said first metal, one of said second metals being aluminum and the other of said second metals being trivalent and selected from the group consisting of iron, chromium, vanadium, manganese, gallium, boron, cobalt and mixtures thereof, the atomic ratio of said first metal to said second metals in said spinel is at least about 0.17, said discrete entities being present in an amount sufficient to reduce the amount of sulfur oxides in said flue gas.
- 19. The process of claim 18 wherein said conversion comprises hydrocarbon cracking in the substantial absence of added molecular hydrogen, said solid particles and discrete entities being fluidizable and circulating between said reaction zone and said regeneration zone.
- 20. The process of claim 19 wherein said hydrocarbon feedstock contains about 0.1% to about 5.0% by weight of sulfur.
- 21. The process of claim 19 wherein said discrete entities contains at least about 70% by weight of said spinel.
- 22. The process of claim 19 wherein at least one of said solid particles and discrete entities further comprise a minor, catalytically effective amount of at least one additional metal component capable of promoting the conversion of sulfur dioxide to sulfur trioxide at the conditions of step (2).
- 23. The process of claim 22 wherein said spinel comprises alkaline earth metal-containing spinel, and the atomic ratio of said first metal to said second metals in said spinel is at least about 0.25.
- 24. The process of claim 19 wherein said solid particles are separate from said discrete entities and the relative amounts of said solid particles and said discrete entities are in the range of about 80 parts to about 99 parts and about 1 part to about 20 parts by weight, respectively.
- 25. The process of claim 19 wherein said solid particles comprise at least one crystalline aluminosilicate capable of promoting hydrocarbon cracking at the conditions of step (1).
- 26. The process of claim 19 wherein said spinel includes magnesium as said first metal.
- 27. The process of claim 19 wherein said discrete entities contain at least about 90% by weight of said spinel.
- 28. The process of claim 18 wherein said other second metal is iron.
- 29. The process of claim 18 wherein said other second metal is chromium.
- 30. The process of claim 18 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 31. The process of claim 19 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 32. The process of claim 26 wherein said discrete entities further comprise about 0.1% to about 25% by weight of free magnesia, calculated as MgO.
- 33. The process of claim 18 wherein said solid particles and said discrete entities are both present in combined particles.
RELATED APPLICATIONS
This application is a continuation of co-pending application Ser. No. 494,604, filed May 16, 1983, now U.S. Pat. No. 4,495,304 which, in turn, is a continuation-in-part of co-pending application Ser. No. 301,678, filed Sept. 14, 1981, now abandoned, which, in turn, is a continuation-in-part of co-pending application Ser. No. 173,315, filed July 29, 1980, now abandoned.
US Referenced Citations (4)
Number |
Name |
Date |
Kind |
4071436 |
Blanton, Jr. et al. |
Jan 1978 |
|
4102777 |
Wheelock |
Jul 1978 |
|
4153535 |
Vasalos et al. |
May 1979 |
|
4469589 |
Yoo et al. |
Sep 1984 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
494604 |
May 1983 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
301678 |
Sep 1981 |
|
Parent |
173315 |
Jul 1980 |
|