Claims
- 1. A process for dewatering a grafted diene rubber aqueous latex comprising:
- A. mixing a grafted diene rubber latex, said diene rubber being rubber particles grafted with alkenyl aromatic and alkenyl nitrile monomer, said rubber particles being emulsified in said aqueous latex by an anionic surfactant, with an alkenyl nitrile monomer and optionally an alkenyl aromatic monomer,
- B. dispersing a cationic surfactant into said latex an amount sufficient to deemulsify said rubber particles,
- C. extracting said grafted diene rubber particles into said monomers as a liquid oil phase, said aqueous latex forming a separate water phase, and
- D. separating said water phase from said liquid oil phase, said oil phase having said grafted diene rubber particles evenly dispersed therein and being essentially free of said water phase.
- 2. A process of claim 1 wherein said monomers are styrene and acrylonitrile, said monomers being present in amount of about 250 to 600 parts per 100 parts of grafted rubber solids in said latex.
- 3. A process of claim 2 wherein the ratio of styrene to acrylonitrile used in step (B) is 80:20 to 0:100.
- 4. A process of claim 1 wherein an inorganic acid is added to said latex after the mixing of said monomers in step (A) bringing said latex to a pH of about 1 to 3 followed by the dispersing of said cationic surfactant in an amount sufficient to deemulsify said grafted rubber particles.
- 5. A process of claim 1 wherein said diene rubber is selected from the group consisting of polybutadiene, polychloroprene, polyisoprene and copolymers of butadiene-styrene and butadiene-acrylonitrile.
- 6. A process of claim 1 wherein said grafted rubber particles have a average particle size diameter of about 0.05 to 1.0 microns.
- 7. A process of claim 1 wherein said latex has present about 2 to 75% by weight of said grafted rubber particles.
- 8. A process of claim 1 wherein said grafted rubber particles are grafted with about 10 to 100 parts of said monomers per 100 parts of rubber, the ratio of alkenyl aromatic monomer to alkenyl nitrile monomer being about 85:15 to 15:85.
- 9. A process of claim 1 wherein said liquid oil phase has a viscosity of about 20 to 100 cps such that said water phase is readily separated from said liquid oil phase.
- 10. A process of claim 1 wherein said cationic surfactant is selected from the group consisting of pyridinium salts, imidazolinium salts, quaternary ammonium salts, amine salts or mixtures thereof.
- 11. A process of claim 1 wherein said cationic surfactant is an alkylimidazolium chloride.
- 12. A process of claim 1 wherein said cationic surfactant is an alkylimidazolium sulfate.
- 13. A process of claim 1 wherein said cationic surfactant is a polyalkylene oxide block copolymer amine salt, said amine being selected from the group consisting of mono, di, tri and tetrafunctional amines, said amine salt being a salt of a solubilizing acid.
- 14. A process of claim 13 wherein said polyalkylene oxide block copolymer moiety is --(C.sub.2 4.sub.4 O).sub.x (C.sub.3 H.sub.6 O).sub.y H wherein the molecular weight of the (C.sub.3 H.sub.6 O) block is about 290 to 8700, said (C.sub.2 H.sub.4 O) block is about 44 to 1100 and is present in said block copolymer in an amount of about 5 to 90% by weight, said block copolymer amine moiety having a molecular weight of about 1500 to 40,000.
- 15. A process of claim 13 wherein said solubilizing acid is sulfuric, hydrochloric, acetic and phosphoric or mixtures thereof.
- 16. A process of claim 13 wherein said polyalkenyl oxide block copolymer amine salt is a polyoxyethylene-polyoxypropylene-ethylene diamine, hydrosulfate salt or hydrochloride salt.
- 17. A process of claim 1 wherein said anionic surfactant is selected from the group consisting of alkali and alkaline earth salts of fatty acids, alkyl sulfonic acids and alkylaryl sulfonic acids and mixtures thereof.
- 18. A process for dewatering a grafted diene rubber aqueous latex comprising:
- A. mixing a grafted diene rubber latex, said diene rubber being rubber particles grafted with alkenyl aromatic and alkenyl nitrile monomer, said rubber particles being emulsified in said aqueous latex by an anionic surfactant, with said latex an acrylonitrile monomer and optionally a styrene monomer,
- B. dispersing a cationic surfactant into said latex in an amount sufficient to deemulsify said grafted rubber particles,
- C. extracting and dispersing said grafted diene rubber particles into said monomers uniformly and essentially free of water forming a liquid oil phase, said aqueous latex forming a separate water phase, and
- D. separating said water phase from said liquid oil phase.
Parent Case Info
This application is a continuation-in-part of copending application, Ser. No. 945,983 filed Sept. 27, 1978, now abandoned.
US Referenced Citations (4)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
945983 |
Sep 1978 |
|