The present invention belongs to the field of recycling and more specifically to dry processing and recycling of steel slag, removing the metal fraction of the slag in such an innovative process and through the metal-free material.
Through the process of the present invention, one can produce granules of ore shot and steel shot, sealing blocks, apparent blocks, building blocks, interlocking floors in all models, caissons, guides, masonry mortar, adhesive mortar, floor on floor mortar, pumpable mortars, grouts, colored grouts, flexible grouts, epoxy grouts, epoxy mass for production of floors, grouts of several strengths replacing natural lower aggregates such as sand, crushed stone by steel slag in their particle sizes with the addition of cement at 0.1% to 40%. The product obtained by the process of the present invention is particularly used in replacement of 100% of the conventional cement produced by a cement produced from steel slag, applying additives from 0.1% to 30% additives, depending on the application of each product.
All literary processes described to date for the process to control expansion of steel slag are to develop a route from the wet process, ie, via a discontinuous process and which demands high availability of time and space to hydration by water of steel slag, which makes it unfeasible, ecologically and financially.
The present invention aims to provide a process for recycling and transforming steel slag by a dry route, generating basic raw materials for obtaining, for example the following products:
1. Interlocking floors of low, medium and high mechanical strength applicable to conditions of light, medium and heavy traffic in order to provide mechanical strength that meets current standards.
2. Apparent and structural sealing blocks, normal finishing and fine finishing for internal and external environments.
3. Mortars of type AC I, AC II, AC III, adhesive mortar, “floor on floor” mortar, pumpable mortars and designed mortars.
4. Flexible grout, colored grouts and epoxy grouts.
5. Epoxy mass for the production of floors
6. Grout for structures, anchoring of equipment, recovery and all possible applications for this product.
7. Feedstock rich in CaO and MgO for the manufacture of cement, using steel slag, is this composition of cement mortars and grouts, tiles, blocks and grouts.
8. Metallic iron the following particle sizes:
Moreover, the process aims to obtain results as:
1. The removal of metal, for inhibiting expandability.
2. Obtaining raw materials of higher strength of steel slag and with different particle sizes for fine aggregate, and
3. Obtaining raw materials of lower strength but high in calcium and magnesium oxide, to obtain fines for cement replacement.
In case of removal of metal, the steel slag, mainly composed by adding silica (SiO2), limestone and other components of a lower percentage, is intended to perform the final purification of the steel, which can reach temperatures of 1350 and 1400° C., so that the components undergo sintering process and is incorporated into metallic iron steel slag.
In addition, metallic iron may be incorporated in different particle sizes and in different oxidation states, ranging from metal iron (Fe°) to iron monoxide (FeO) and iron oxide (Fe2O3). The presence of iron in different oxidation states, mainly iron monoxide (FeO—Fe+2), will give an extremely magnetic character to the slag, which will compete with the magnetism of metallic iron. Thus, it is used an innovative process of separation of metallic iron (as shown in the flow chart of the drawings).
Within the context of
Regarding the extraction of raw materials for added strength, the process according to the present invention has 100% economic sustainability, in which the main goal is to get all the basic raw materials for manufacture of floors, blocks, mortars, grouts and especially replacement of cement, from steel slag, after removal of the metal components.
Once done the process of disintegration, release and clearance of grains of the slag, non-magnetic fraction is used to render the grains for different applications, so you may need to meet the following additional steps depending on each intended application:
It is important to remember that at the process of separation of metallic components involving several stages of crushing, screening, magnetic separation at different particle size stages and final release of the slag, are automatically generated the basic raw materials for manufacture of floors, blocks, mortar and grouts.
In relation to obtaining raw materials of lower strength, the item of greater economic sustainability of the project is to obtain compounds rich in CaO and MgO, which can produce raw material for cement replacement, considering that this component is the item major cost in the production of products to be developed.
In this same concept of recovering processing of metallic iron there is generated a component rich in CaO and MgO for the production of cement replacement, whereby it may be necessary to fulfill the following process steps:
Laboratory tests were performed, and the obtained parameters to adjust the recovery process of metallic material and obtaining of raw matter. In the tests performed, the following steps occur:
28. Mechanical strength and weathering test (weather degradation);
Once identified the raw material of lower mechanical strength rich in CaO and MgO, the raw material was comminuted to −325 mesh, then the additive of cement replacement by inserting special additives (slag activators), and implementation of test for different traces for different applications.
In more detail, it may be noted that the invention provides a process with a dry route for the control of expansion factors (CaO, MgO and metallic iron), contained in the steel slag.
During processing, it was found that the slag, when heated in a controlled manner (residence time of 30 seconds at +1300° C.), actives binding properties of the slag, as well as facilitates removal of friable material (free CaO and MgO), elements which, under normal conditions, react with water to form expandable hydroxides (CaOH2 and MgOH2).
The main steps involved in the process and treatment of steel slag are feeding scum, primary crushing, drying, secondary crushing, metal separation, particle size classification, dust collectors and storage of aggregates.
These steps can be described in greater detail as follows:
Feeding of slag: occurs by means of a vibratory feeder in which the slag in the primary crusher is measured;
Primary crushing: through the mill, the size of gross slag is reduced;
Drying: crushed slag is exposed at a controlled manner to determined temperature and time;
Secondary crushing: the friable material is separated into mill, whose principle of operation is the impact.
Magnetic Separation: after the grinding, fractionated slag is found with reduced content of calcium oxide (CaO) and magnesium oxide (MgO), so that all material is led to Magnetic Separation system.
Magnetic separation according to the invention takes place by means of randomly designed magnets with different intensities (Gauss) to capture particulate matter of different particle sizes.
After clearing the Metallic iron and part of the oxides (which cause expansion), the material is transported to the screening system.
Size classification: After the classification in vibrating screen, there is obtained a controlled steel aggregate with permitted levels of Cao, MgO and iron oxides, which do not react when mixed with water and cement, eliminating the expansion.
Dust collectors: it is further provided a step of sleeve filtering that collects fine friable materials, arising from the dryer, the mill and the size classification system.
Storage of aggregates: The steel crushed stone classified as superfine, fine, medium and coarse size is stored in a covered location and is ready to be used in the production of artifacts.
The steel aggregate, after being treated by the process of the present invention replaces, with huge environmental gains, natural fine aggregates commonly used in the production of artifacts, such as crushed stone and sand.
The steel crushed stone can be used in the production of concrete artifacts such as interlocking floors, sealing blocks, building blocks, caissons, guides, curb, concrete, as well as adhesive mortars, floor on floor mortar, pumpable mortar, grout, colored grouts, flexible grouts, epoxy grouts, epoxy masses.
In turn, the fines produced during processing of slag have a cement function, and can be used in addition to the conventional cement, or in some cases by additives, or used to replace 100% of the conventional cement, by a cement produced by steel slag, applying additives from 0.1% to 30% of additives depending on the application and degree of strength of each product.
With a demonstrative purpose, analytical results are shown below, which demonstrate the control of expandability of the slag processed according to the present invention.
It is therefore a process of recycling and transforming of steel slag by a dry route of great importance to the objective pursued, fully meeting the proposed objectives and fulfilling at a practical and efficient manner the intended functions, providing advantages inherent to its applicability, with specific and innovative characteristics and provided with fundamental requirements of novelty and inventive activity, required to obtain patent protection.