Claims
- 1. A process for extruding a bubble-free article from a polymeric composition selected from the class consisting of:
- (a) poly(ethylene terephthalate) resin;
- (b) a uniform blend of poly(ethylene terephthalate) resin with a compatible polymer, the amount of the compatible polymer being at most about 10 weight percent of the blend; and
- (c) a uniform blend of a poly(ethylene terephthalate) resin with an incompatible polymer and a compatibilizing agent, the total amount of the incompatible polymer and compatibilizing agent being at most about 20 weight percent of the blend;
- said process comprising:
- (1) premixing an organic diisocyanate with said polymeric composition or individual components of said composition, in any order, the amount of said diisocyanate being sufficient to increase the melt viscosity of said polymeric composition to the desired level without causing excessive crosslinking;
- (2) introducing the premix of step (1) into the feed section of a twin-screw extruder having a cold feed section, a hot plastication zone, a kneading zone maintained at an average temperature of about 280.degree. to 320.degree. C., a venting zone maintained at an average temperature of about 280.degree. to 320.degree. C. and at a pressure of less than about 1.33 kPa, a metering zone maintained at an average temperature of about 260.degree. to 280.degree. C., and an extrusion due maintained at an average temperature of about 255.degree. to 265.degree. C., all the temperatures being wall temperatures; and
- (3) operating the extruder at about 30-120 rpm and at a pressure of about 350 kPa or less to recover the extruded article from the die.
- 2. A process of claim 1 wherein the diisocyanate is methylenebis(p-phenyl isocyanate).
- 3. A process of claim 2 wherein the polymeric composition is poly(ethylene terephthalate).
- 4. A process of claim 1 wherein the polymeric composition is a blend of poly(ethylene terephthalate) with an EPDM elastomer grafted with an unsaturated compound selected from the class consisting of maleic anhydride, maleic acid, fumaric acid, and mono- and diesters of maleic and fumaric acids.
- 5. A process of claim 4 wherein the grafted EPDM elastomer is present in the amount of 4-6% of the total weight of the blend.
- 6. A process of claim 1 wherein the polymeric composition is a blend of poly(ethylene terephthalate) with a compatible polymer, which is present in an amount of at least 3% of the total weight of the blend.
- 7. A process of claim 2 wherein the amount of the diisocyanate is about 0.6-1.1% based on the weight of poly(ethylene terephthalate) resin.
- 8. A process of claim 7 wherein the amount of diisocyanate is 0.7-1% based on the weight of poly(ethylene terephalate) resin.
- 9. A process of claim 8 wherein the amount of diisocyanate is 0.8-0.9% based on the weight of poly(ethylene terephthalate) resin.
- 10. A process of claim 1 wherein the average temperature range within the kneading zone and within the venting zone is about 290.degree.-310.degree. C.
- 11. A process of claim 10 wherein the vent port is maintained at a pressure of about 0.1-0.13 kPa.
- 12. A process of claim 10 wherein the average temperature range within the metering zone is about 270.degree.-280.degree. C.
- 13. A process of claim 10 wherein the feed rate is about one-half of the internal volume per hour.
Parent Case Info
This is a continuation-in-part of application Ser. No. 224,673 filed Jan. 13, 1981 now abandoned.
US Referenced Citations (11)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
224673 |
Jan 1981 |
|