Process for heat treating ceramics

Abstract
A process for making a heat treated ground ceramic cutting tool and the resultant cutting tool. The process includes the steps of: providing an uncoated ground ceramic cutting tool having at least a portion thereof ground; and heat treating the uncoated ground ceramic cutting tool so as to form the heat treated ground ceramic cutting tool.
Description




FIELD OF THE INVENTION




The invention pertains to a process for making ceramics, as well as a ceramic article of manufacture.




More specifically, the invention pertains to a process for making a ceramic cutting tool that includes silicon nitride-based cutting tools, SiAlON-based cutting tools, alumina-based cutting tools, titanium carbonitride-based cutting tools, and ceramic whisker-reinforced ceramic cutting tools, such as, for example, a whisker-reinforced titanium carbonitride-based ceramic cutting tool and a whisker-reinforced alumina-based ceramic cutting tool.




BACKGROUND OF THE INVENTION




Heretofore, silicon nitride-based cutting inserts, and SiAlON-based cutting inserts, which are ceramic articles of manufacture, have been shown to be useful for many material removal applications. U.S. Pat. No. 4,127,416 to Lumby et al., U.S. Pat. No. 4,563,433 to Yeckley et al ., U.S. Pat. No. 4,711,644 to Yeckley et al., U.S. Pat. No. 5,370,716 to Mehrotra et al., U.S. Pat. No. 5,382,273 to Mehrotra et al., U.S. Pat. No. 5,525,134 to Mehrotra et al., U.S. Pat. No. 4,880,755 to Mehrotra et al., and U.S. Pat. No. 4,913,936 to Mehrotra et al. disclose various SiAlON and silicon nitride compositions which are useful as cutting inserts. These patents are hereby incorporated by reference herein.




Heretofore, whisker-reinforced cutting inserts, which are also ceramic articles of manufacture, have also been shown to be useful for material removal application. These whisker-reinforced cutting inserts include alumina-based materials reinforced with silicon carbide whiskers such as shown and described in U.S. Pat. No. B2 4,789,277 to Rhodes et al., and U.S. Pat. No. 4,961,757 to Rhodes et al. wherein these Rhodes et al. patents are hereby incorporated by reference herein. A whisker-reinforced alumina-based cutting insert with a zirconia addition is also shown and described in U.S. Pat. No. 4,959,332 to Mehrotra et al. wherein this patent is hereby incorporated by reference herein. A whisker-reinforced titanium carbonitride-based cutting insert is shown and described in PCT Patent Application No. PCT/US96/15192 (International Filing Date of Sep. 20, 1996) [International Publication No. WO 97/18177 published on May 22, 1997] for a WHISKER REINFORCED CERAMIC CUTTING TOOL AND COMPOSITION THEREOF [as well as in U.S. patent application Ser. No. 08/874,146 filed Jun. 13, 1997 to Mehrotra] wherein these patent applications are hereby incorporated by reference herein.




While the cutting inserts made from the materials of the above patents and patent application exhibit an acceptable performance in material removal applications such as, for example, milling and turning, there remains as an objective the production of ceramic cutting inserts (e.g., silicon nitride-based cutting inserts, SiAlON-based cutting inserts, alumina-based cutting inserts, titanium carbonitride-based cutting inserts, and whisker-reinforced ceramic cutting inserts) with still better performance characteristics in material removal applications. There also remains as an objective the production of ceramic cutting inserts (e.g., silicon nitride-based cutting inserts, SiAlON-based cutting inserts, alumina-based cutting inserts, titanium carbonitride-based cutting inserts, and whisker-reinforced ceramic cutting inserts) that exhibit a microstructure that results in better physical properties and performance characteristics.




SUMMARY OF THE INVENTION




In one form thereof, the invention is a process for making a heat treated ground ceramic cutting insert comprising the steps of: providing an uncoated ground ceramic cutting insert having at least a portion thereof being ground; and heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert.




In another form thereof, the invention is a heat treated ground ceramic cutting insert produced by the process comprising the steps of: providing an uncoated ground ceramic cutting insert having at least a portion thereof being ground; and heat treating the ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert.




In still another form thereof, the invention is a heat treated ground ceramic article of manufacture formed in the presence of a reaction source wherein the article of manufacture comprises a substrate which has a surface. The substrate presents a microstructure wherein there is a surface region extending inwardly from the surface of the substrate, and there is a bulk region inwardly of the surface region. The bulk region has a bulk composition. The surface region has a surface composition resulting from a reaction with the reaction source wherein the surface composition is different from the bulk composition.




In yet another form thereof, the invention is a process for making a heat treated ground ceramic article of manufacture comprising the steps of: providing an uncoated ground ceramic compact having at least a portion thereof being ground; and heat treating the uncoated ground ceramic compact so as to form the heat treated ground ceramic article of manufacture.











BRIEF DESCRIPTION OF THE DRAWINGS




The following is a brief description of the drawings which form a part of this patent application:





FIG. 1

is an isometric view of a cutting insert of the instant invention;





FIG. 2

is a scanning electron microscope (SEM) photomicrograph which depicts secondary electron images (SEI) at a magnification of 1000× of the rake surface of a ground surface cutting insert of Mixture I;





FIG. 3

is a scanning electron microscope (SEM) photomicrograph which depicts secondary electron images (SEI) at a magnification of 3000× of the rake surface of a ground surface cutting insert of Mixture I;





FIG. 4

is a scanning electron microscope (SEM) photomicrograph which depicts secondary electron images (SEI) at a magnification of 1000× of the rake surface of a ground and heat treated cutting insert of Mixture I;





FIG. 5

is a scanning electron microscope (SEM) photomicrograph which depicts secondary electron images (SEI) at a magnification of 3000× of the rake surface of a ground and heat treated cutting insert of Mixture I;





FIG. 6

is a scanning electron microscope (SEM) photomicrograph which depicts secondary electron images (SEI) at a magnification of 1000× of the rake surface of an unground surface cutting insert flank of Mixture I; and





FIG. 7

is a scanning electron microscope (SEM) photomicrograph which depicts secondary electron images (SEI) at a magnification of 3000× of the rake surface of an unground surface cutting insert flank of Mixture I.











DETAILED DESCRIPTION OF THE INVENTION




Referring to the drawings, there is shown in

FIG. 1

a ceramic cutting insert generally designated


20


. Cutting insert


20


has a rake surface


22


, and flank surfaces


24


. There are cutting edges


26


at the intersections of the rake surface


22


and the flank surfaces. The cutting insert of the instant invention may take on any one of a variety of cutting insert geometries so that applicant does not intend to limit the scope of the instant invention to the geometry of the specific cutting insert illustrated in

FIG. 1

or the geometries set forth in the examples herein.




In regard to the production of the cutting inserts as used in the tests, the powder components were ball milled, dried, and then screened to form the powder mixture. Some powder mixtures to which the instant invention has application are described hereinafter. These powder mixtures included the four silicon nitride-based mixtures (Mixtures I through IV) set forth in Table I below.












TABLE I











Composition (Weight Percent)






of Silicon Nitride-Based Starting Powder Mixtures I-IV

















Silicon




Aluminum




Aluminum








Mixture




Nitride




Nitride




Oxide




Magnesia




Yttria









I




98.0














1.0




1.0






II




85.4




6.2




3.7









4.7






III




63.3




9.3




22.7









4.7






IV




91.6




1.6




1.3









5.5














The powder components set forth in Table I hereinabove are briefly described as follows. For Mixtures I and III, the silicon nitride is Grade SNE10 silicon nitride powder from Ube Industries, Ltd. of Tokyo, Japan. For Mixture II, the silicon nitride is a lower purity nitrided silicon nitride powder available from Herman C. Starck, Inc. of New York, N.Y. (USA). For Mixture IV, the silicon nitride powder is Grade LC10 or M11 available from Herman C. Starck, Inc. For Mixtures I-IV, the aluminum nitride is Grade C AlN powder available from Herman C. Starck, Inc. of New York, N.Y. (USA). For Mixtures I-IV, the alumina is Grade Ceralox HPA 0.5 and is available from Ceralox Corporation of Tucson, Ariz. (USA). For Mixtures I-IV, IV, the yttria powder is fine grade yttria from Herman C. Starck, Inc. of New York, N.Y. (USA). More detailed descriptions of these powders is found in U.S. Pat. No. 5,370,716 to Mehrotra et al., which has already been incorporated by reference herein.




The powder mixtures to which the invention pertains further include silicon carbide whisker-reinforced ceramics, alumina-based ceramics, and titanium carbonitride-based ceramics. Examples of these powder mixtures, which are identified as Mixtures V, VI and VII, are set forth in Table II hereinbelow.












TABLE II











Composition (Weight Percent) of






Silicon Carbide Whisker (SiC


w


)-Reinforced Ceramic,






Alumina-Based Ceramic and






Titanium Carbonitride-Based Ceramic






Starting Powder Mixtures V, VI and VII



















Titanium








Mixture




Zirconia




Alumina




Carbonitride




SiC


w






Other



















V




14.2




Balance




None




1.2




2.3 MgAl


2


O


4


;











0.14 SiO


2


;











0.02 CaO






VI




None




34.4




Balance




19.1




0.3 Y


2


O


3








VII




None




Balance




None




25




500 ppm MgO











as MgAl


2


O


4
















These powder mixtures of Mixtures I through VII can be consolidated by a variety of methods including pressing, sintering, hot isostatic pressing, hot pressing and other methods known in the literature.




As one example, the processing parameters for the powder Mixture I to make the cutting inserts, after the blending of the powder components the powder mixture was uniaxially pressed into green ceramic cutting insert compacts. These green cutting insert ceramic compacts were loaded into a silicon carbide lined graphite pot, and the green cutting insert compacts were surrounded by a protective setting powder. The setting powder was a silicon nitride-based powder with minor amounts of one or more of alumina, yttria, magnesia, carbon, silicon carbide and boron nitride or their reaction products contained therein.




The pot with the green cutting insert compacts therein was loaded into a batch sintering furnace and the green cutting insert compacts were then batch sintered at 1815 degrees Centigrade for 270 minutes in one atmosphere of nitrogen. The resultant product was a sintered ceramic cutting insert compact. After completion of the sintering, the sintered ceramic cutting insert compacts were hot isostatically pressed at 1750 degrees Centigrade at a pressure of 20,000 pounds per square inch (psi) of nitrogen for a duration of 60 minutes. The resulting products were uncoated unground fully dense cutting insert blanks, i.e., as-molded cutting insert blanks with an unground surface. At this point in the processing, these unground as-molded cutting insert blanks correspond to the characterization as “unground surface” cutting inserts (or cutting insert blanks) as found in Table III through Table IX herein. Other methods of powder densification may include sintering (without HIPing), hot pressing, encapsulated HIPing, sintering without a protective powder cover, and other methods known in the literature.




In order to form an uncoated ground ceramic cutting insert, i.e., a cutting insert that corresponds to the characterization “ground surface” cutting insert as found in Table III through Table IX herein, unground surface cutting insert blank was subjected to a grinding process wherein the top surface, the bottom surface, and the periphery were ground to dimension and T land cutting edges were ground.




It should be appreciated that the grinding step may also comprise a honing step or the like. The grinding or honing step may also impact only a portion of the uncoated unground ceramic cutting insert blank so that only a portion of the uncoated ground ceramic cutting insert would be ground or honed. It is intended that in the preferred process the grinding (or honing) step occur on a sintered article which is at least substantially fully dense (i.e., closed porosity).




For fabrication by hot pressing, a plate or disk may be hot pressed to full density, cut (or diced) into desired shapes, and finish ground. Alternatively, near net shape hot pressed cutting insert blanks may be finish ground.




In order to make a heat treated ground ceramic cutting insert, i.e., a cutting insert that corresponds to the characterization “ground & heat treated” cutting insert in Table III through Table IX, the ground ceramic cutting inserts of Mixture I were loaded into a silicon carbide lined graphite pot, and these cutting inserts were surrounded by a protective setting powder. The setting powder was a silicon nitride-based powder with minor amounts of one or more of alumina, yttria, magnesia, carbon, silicon carbide and boron nitride or their reaction products contained therein. The use of the protective setting powder is an optional feature of the process and is presented here only as an example.




The pot with the standard ground cutting inserts therein was loaded into a batch sintering furnace and the standard ground cutting inserts were heat treated at a temperature of 1815 degrees Centigrade for a duration of 270 minutes at a pressure of one atmosphere nitrogen. The duration of the heat treatment may range between about 15 minutes and about 6 hours. The preferred heat treatment temperature range for silicon nitride-based ceramics is between about 1600 degrees Centigrade and about 2200 degrees Centigrade. The preferred heat treatment temperature range for the other ceramic compositions described herein is between about 1300 degrees Centigrade and about 1700 degrees Centigrade.




After completion of the heat treatment, the cutting inserts were furnace cooled. As previously mentioned, the ceramic cutting inserts that result from this heat treatment correspond to the cutting inserts characterized as “ground & heat treated” in Table III through Table IX herein.




Even though the above description pertains to a batch furnace, the process may take place in a continuous furnace.




Although the processing conditions may vary, the post-grinding heat treatment is intended to comprise a heat treatment wherein there may or may not be some liquid phase which forms, and there may or may not necessarily be any further significant densification which occurs due to the post-grinding heat treatment. Also, the post-grinding heat treatment may or may not involve a setting powder and may be accomplished at pressures ranging between sub-atmospheric to about 30,000 psi.




Although the above process to make the heat treated ground cutting inserts included the step of grinding the uncoated ceramic cutting insert blanks (i.e., unground surface cutting insert blanks) prior to the heat treating step, it should be appreciated that some of the grinding steps may occur after completion of the heat treating step. This is especially true for minor grinding steps which may occur after the heat treating step (e.g., on surfaces that are not critical for cutting performance such as holes, and top and bottom surfaces), on some or all surfaces. Still referring to post-heat treatment minor grinding steps, the cutting edges may be lightly ground or polished such that the advantages of the present invention are still retained over standard ground products (i.e., uncoated ground surface ceramic cutting inserts).




While the ground and heat treated cutting inserts described above were the result of the steps of sintering, hot isostatic pressing, grinding and heat treating, the heat treated ground cutting inserts can be made from the steps of sintering, hot isostatic pressing, pre-grinding heat treatment, grinding, and a post-grinding heat treatment.




Other methods of manufacture are applicable to the present invention. One additional method of manufacture includes the steps of: sintering, optionally hot isostatic pressing, grinding the cutting insert over its entire surface, and heat treating. Another method of manufacture includes the steps of: sintering, optionally hot isostatic pressing, grinding the cutting insert on the top surface and on the bottom surface and on the K-land, and heat treating. Still another method of manufacture includes the steps of: sintering, grinding the cutting insert over it entire surface, and heat treating the cutting insert. Finally, another method of manufacture includes the steps of: sintering, grinding the top surface and the bottom surface of the cutting insert, heat treating, and then grinding the K-land.




Although the details of the processing may vary, generally speaking the powder mixture of Mixture I may be processed to form an uncoated unground ceramic cutting insert blank according to the teachings of U.S. Pat. No. 5,382,273 to Mehrotra et al. and U.S. Pat. No. 5,525,134 to Mehrotra et al.




The same holds true for the powder mixture of Mixture II in that to form an uncoated unground ceramic cutting insert blank from Mixture II the powder mixture may be processed according to the teachings of U.S. Pat. No. 4,563,433 to Yeckley et al. In regard to the processing of the examples of Mixture II, in the post-sintering heat treatment the parts were set on top of the setting powder which was a boron nitride setting powder in a boron nitride box. The post-sintering heat treatment was at 1770 degrees Centigrade for a duration of two hours at a pressure of one atmosphere nitrogen in a continuous belt furnace.




Likewise for the powder mixture of Mixture III in that to form an uncoated unground ceramic cutting insert blank from Mixture III the powder mixture may be processed according to the teachings of U.S. Patent No. 5,370,716 to Mehrotra et al. In regard to the processing of the examples of Mixture III, in the post-sintering heat treatment the parts were set on top of the setting powder which was a boron nitride setting powder in a boron nitride box. The post-sintering heat treatment was at 1725 degrees Centigrade for a duration of two hours at a pressure of one atmosphere nitrogen in a continuous belt furnace.




The ground and heat treated Mixture III cutting inserts were tested against prior art ground Mixture III cutting inserts in milling and turning.




The milling test was climb milling of Inconel 718 at 3000 sfm, 0.004 ipt, 0.100 inch depth of cut, dry, using four style RNG-45T0320 cutting inserts mounted in a two inch diameter Hertel 4.0060R232 milling cutter where the width of cut was 1.468 inches and the length/pass was 13 inches (actual cut time for each edge per pass=0.050 minutes). The heat treated Mixture III inserts had lifetime of 3.63 passes (average of two reps) and failed by maximum flank wear/chipping, whereas the prior art ground Mixture III inserts had a lifetime of 2.30 passes (average of two reps).




In eccentric bar turning of Inconel 718 using Mixture III RNG-45T0320 style inserts at 500 sfm, 0.006 ipr, and 0.040 depth of cut (flood coolant), the heat treated inserts according to the present invention had an average tool life of 4.1 minutes and the prior art ground inserts had an average tool life of 4.6 minutes.




Although the details of processing may vary, the powder mixture of Mixture IV was processed like that of Mixture I, except that the setting powder was silicon nitride-based with minor additions of one or more of alumina, yttria, and boron nitride, and the post-sintering heat treatment temperature was 1860 degrees Centigrade and the duration of the heat treatment was 130 minutes.




Although the details of the processing may vary, the powder mixture of Mixture V may be processed to form an uncoated unground ceramic cutting insert blank according to the teachings of U.S. Pat. No. 4,959,332 to Mehrotra et al. In regard to the processing of the examples of Mixture V herein, for the post-sintering heat treatment the parts were set on top of the setting powder which was a niobium carbide-based setting powder, and the temperature was 1650 degrees Centigrade for a duration of 60 minutes at a pressure of one atmosphere argon.




The same holds true for the powder mixture of Mixture VI in that to form an uncoated ground ceramic cutting insert blank from Mixture VI the powder mixture may be processed according to the teachings of PCT Patent Application No. PCT/US96/15192 [International Filing Date of Sep. 20, 1996] (as well as U.S. patent application Ser. No.08/874,146 filed Jun. 13, 1997) to Mehrotra for a WHISKER REINFORCED CERAMIC CUTTING TOOL AND COMPOSITION THEREOF. In regard to the processing of the examples of Mixture VI herein, for the post-sintering heat treatment the parts were set on top of the setting powder which was a niobium carbide-based setting powder, and the temperature was 1650 degrees Centigrade for a duration of 60 minutes at a pressure of one atmosphere argon.




Additionally, although the details of processing may vary the powder mixture of Mixture VII may be processed to form an uncoated ground ceramic cutting insert blank according to the teaching of U.S. Pat. No. B2 4,789,277 to Rhodes et al., and U.S. Pat. No. 4,961,757 to Rhodes et al. In regard to the processing of the examples of Mixture VII herein, for the post-sintering heat treatment the parts were set on top of the setting powder which was a niobium carbide-based setting powder, and the temperature was 1650 degrees Centigrade for a duration of 60 minutes at a pressure of one atmosphere argon.




It should be understood based upon the processes described above, that a ground surface will be obtained when a sufficiently thick (i.e., 0.03 inches [0.762 millimeters] to 0.05 inches [1.27 millimeters]) layer is ground away from the ground and heat treated surface.




Table III set forth below presents the crystalline phases (as determined by X-ray diffraction) which exist in the microstructure of the sintered ceramic material made from the powder mixtures of Mixtures I through V when the ceramic material is in one of three conditions, i.e., the unground surface condition, the ground surface condition and the ground and heat treated condition. Along the lines of the above descriptions of these conditions, the use of the characterization “unground surface” in Table III through Table IX hereof means a sintered fully dense cutting insert blank that has not been ground after the initial sintering thereof. The use of the characterization “ground surface” in Table III through Table IX means a sintered fully dense cutting insert that has been ground, but has not been subjected to any post-grinding heat treatment. The use of the characterization “ground & heat treated” in Table III through Table IX means a sintered fully dense cutting insert that has been ground after the initial sintering treatment and then subjected to a post-grinding heat treatment.












TABLE III











Crystalline Phases Present in Mixtures I Through V














Mixture/






Ground &






Condition




Unground Surface




Ground Surface




Heat Treated









I




β-Si


3


N


4


;




β-Si


3


N


4






β-Si


3


N


4


;







Y


2


Si


3


O


3


N


4







Y


2


Si


3


O


3


N


4








II




β′-sialon; 95%




β′-sialon;




β′-sialon;







α′-sialon;




15-20% α′-sialon




95% α′-sialon;







N-YAM





N-YAM






III




β′-sialon;




β′-sialon




β′-sialon;







15R polytype





15R polytype






IV




β′-sialon;




β′-sialon;




β′-sialon;







N-melilite;




B-phase;




N-melilite







N-α-Wollastonite




N-α-Wollastonite






V




Al


2


O


3


;




Al


2


O


3


; t-ZrO


2


;




Al


2


O


3


; t-ZrO


2


;







t-ZrO


2


; m-ZrO


2


;




m-ZrO


2


; SiC;




m-ZrO


2


; SIC;







ZrO




MgAl


2


O


4






MgAl


2


O


4


;









ZrO/ZrC














The designation 15R is a polytype which is a single phase SiAlON of a rhombohedral crystal structure with the formula SiAl


4


O


2


N


4


. This 15R polytype is described in U.S. Pat. No. 4,127,416 to Lumby et al. already incorporated by reference herein. The designation “t-ZrO


2


” means tetragonal zirconia and the designation “m-ZrO


2


” means monoclinic zirconia.




It should be appreciated that the present invention is also applicable to cutting inserts made of materials wherein the bulk substrate is α-silicon nitride, α-silicon nitride plus β-silicon nitride, α′-SiAlON, and mixtures of (α and/or β) silicon nitride and (α′ and/or β′) SiAlON. These compositions may have microstructures (other than intergranular phase or phases) which may optionally include additives in an amount up to 30 volume percent of the entire composition wherein these additives comprise the oxides of hafnium and/or zirconium, the carbides, nitrides and/or carbonitrides of titanium, silicon, hafnium and/or zirconium (e.g., titanium carbide, titanium nitride, titanium carbonitride, silicon carbide and hafnium carbide).




Referring now to the test results presented in Table IV set forth hereinafter, Tests Nos. 1 through 7 comprise a variety of tests that used cutting insert of Mixture I wherein the cutting inserts were either in the “unground surface” condition, the “ground surface” condition or the “ground & heat treated” condition. Test No. 8 comprised a milling test using a cutting insert of Mixture IV wherein the cutting inserts were in the “ground surface” and the “ground & heat treated” conditions.




Test No. 1 sets forth the test results of fly cut milling Class 40 Gray Cast Iron (GCI) in the form of blocks with holes therein using a Kennametal KDNR-4-SN4-15CB cutter under the conditions set out in Table IV. The width and length of cut was three inches by twenty-four inches (7.62 centimeters [cm] by 60.96 cm). The end of life (EOL) criteria for all of the tests was by a flank wear of 0.015 inches (0.381 mm). The tool life in minutes as set forth for Test No. 1 in Table IV reflects the actual chip cutting time for the cutting insert. The test results from Test No. 1 show that the tool life as measured in minutes for the ground and heat treated cutting inserts of Mixture I was about two and one-half times as great as that for the ground surface cutting inserts of Mixture I.




Referring to Test No. 2, this data reflect the results of a turning cycle test on Class 40 Gray Cast Iron. The results show for Mixture I that the ground and heat treated cutting insert had improved tool life of about twenty-seven percent (39.2 cycles/30.8 cycles) over the unground surface cutting insert and an improved tool life of about thirty-six percent (39.2 cycles/28.8 cycles) over the ground surface cutting insert.




Referring to Test Nos. 3 and 4 of Table IV, this data reflects the results of the use of a CNGX-434T (0.008 inches×20° K land) style cutting inserts in the turning of Class 30 Gray Cast Iron brake rotors. It is apparent that from Test No. 3 the nose wear for the ground and heat treated cutting insert was about eighteen percent less (2.05×10


−4


inches vs. 2.5×10


−4


inches) than for the ground surface cutting insert. Test No. 4 shows that the average nose wear for the ground and heat treated cutting insert was about the same as for the ground surface cutting insert.




Referring to Test No. 5, a turning cycle test was performed on Class 40 Gray Cast Iron using ground and heat treated cutting inserts and ground surface cutting inserts. The turning cycle test emphasizes interrupted cutting in which sixteen cuts were made per cycle to reduce the bar diameter with a two inch length of cut per cut and a total cutting time per cycle of one minute. The results of these tests reflect the tool life as measured in minutes and where the end of life (EOL) criteria was 0.030 inches of nose wear (i.e., “nw”). The results show that there was a twenty-seven percent improvement in the tool life (12.7 minutes/10.0 minutes) in the turning of gray cast iron, as measured by minutes, between the ground surface cutting insert and the ground and heat treated cutting insert.




Referring to Tests Nos. 6 and 7, these tests pertain to the continuous turning of a round bar of ductile cast iron (80-55-06). The tool life, which comprised actual chip cutting time for the cutting insert, was measured in minutes wherein the EOL criteria was flank wear of 0.015 inches (0.381 mm). Tests Nos. 6 and 7 show that the tool life was about the same for the cutting inserts in a continuous turning test.




Referring to Test No. 8, these results concern the fly cut milling of Class 40 Gray Cast Iron (GCI) in the form of blocks with holes therein using a Kennametal KDNR-4-SN4-15CB cutter under the conditions set out in Table IV with cutting inserts of Mixture IV. The width and length of cut was three inches by twenty-four inches (7.62 centimeters [cm] by 60.96 cm). The end of life (EOL) criteria for all of the tests was by a flank wear of 0.015 inches (0.381 mm). The tool life in minutes as set forth for Test No. 8 in Table IV reflects the actual chip cutting time for the cutting insert. The tool life for the ground and heat treated cutting insert was about twenty percent (1.8 minutes/1.5 minutes) better than that for the ground surface cutting insert of Mixture IV.












TABLE IV











Metalcutting Test Results















Unground




Ground




Ground &







Surface




Surface




Heat Treated









Mixture I/Test









Test No. 1





1.3 minutes




3.2 minutes






Milling Class 40






GCI with holes:






speed = 3000 surface






feet per minute (sfm);






chipload = 0.006 inches






per tooth (ipt);






Depth of Cut






(DOC) = 0.08″;






Insert SNGA433T






(chamfer size = .008″ ×






20 degrees);






Dry






Test No. 2




SNU433T/




SNG433T/




SNG433T/






Turning Cycle




30.8 cycles




28.8 cycles




39.2 cycles






Rectangular Class 40 GCI:






speed = 1600 sfm;






Feed = 0.012 inches per






revolution (ipr);






DOC = 0.1″;






Dry






Test No. 3





2.5 × 10


−4






2.1 × 10


−4








Class 30 GCI





inches nose




inches nose






Brake Disc turning/facing:





wear per part




wear per part






Speed = 2500-3000 sfm;






2.0 × 10


−4








Feed = 0.006-0.024 ipr;






inches nose






Insert CNGX454T;






wear per part






Dry






Test No. 4





2.6 × 10


−4






2.9 × 10


−4








Class 30 GCI





inches nose




inches nose






Brake Disc turning/facing:





wear per part




wear per part






Speed = 2500-3000 sfm;






2.3 × 10


−4








Feed = 0.006-0.024 ipr;






inches nose






Insert CNGX454T;






wear per part






Dry






Test No. 5





10 minutes




12.7 minutes






Turning Cycle






Class 40 GCI:






Speed = 3000 sfm;






Feed = 0.016 ipr;






DOC = 0.07 inches;






Insert CNGX454T;






Dry






Test No. 6





1.4 minutes




1.4 minutes






Turning DCI:






Speed = 2000 sfm;






Feed = 0.02 ipr;






DOC = 0.1 inches;






Insert SNGA433T;






Dry






Test No. 7





1.8 minutes




1.9 minutes






Turning DCI:






Speed = 1500 sfm;






Feed = 0.015 ipr;






DOC = 0.1 inches;






Insert SNGA433T;






Dry






Mixture IV






Test No 8





1.5 minutes




1.8 minutes






Milling Class 40






GCI with holes:






Speed = 3000 sfm;






Chipload = 0.006 ipt;






DOC = 0.08 inches;






Insert SNG432T;






Dry














In addition to conducting tests of the actual cutting insert performance in material removal applications, certain compositions were analyzed to ascertain their physical properties. In this regard, the physical properties of surface roughness, transverse rupture strength, hardness, and surface fracture resistance have been found to be indicative of the performance of a cutting insert. In addition, the microstructure of the cutting insert has been found to, in some cases, influence the performance of the cutting insert.




Table V below sets forth the test results of surface roughness measurements in microinches (μinches) of cutting inserts of Mixture I wherein each cutting insert was in one of the three conditions (i.e., unground surface, ground surface, or ground and heat treated). The technique used to measure the surface roughness used a WYKO surface measuring system Model No. NT 2000 equipped with Vision 32 software. The surface roughness measurements were made in the vertical scanning interferometer mode at 10.2 magnifications with the tilt term removed and without filtering. The set up parameters were: size: 736×480, and sampling: 32.296 microinches. The WYKO surface measuring system is made by VEECO WYKO Corporation of Tucson, Ariz. (USA) 85706.












TABLE V











Surface Roughness of Cutting Inserts (Mixture I)















Unground




Ground




Ground & Heat






Parameter/Condition




Surface




Surface




Treated Surface









R


a


(μinches)




43.6-58.8




18.3-22.2




54.8-60.5






R


q


(μinches)




62.4-82.0




23.0-29.2




69.2-76.1






R


z


(μinches)




1113-1492




298-551




603-744






R


t


(μinches)




1436-2378




408-704




 736-1288














Table VI below sets forth the transverse rupture strength (TRS) in thousands of pounds per square inch (ksi) and the standard deviation for the transverse rupture strength, as well as the Weibull Modulus, for transverse rupture bars of Mixture I wherein each transverse rupture bar was in one of the three conditions (i.e., unground surface, ground surface, or ground & heat treated). The technique used to measure the transverse rupture strength comprised a three point bend test.












TABLE VI











Transverse Rupture Strength (ksi)






for Transverse Rupture Bars of Mixture I

















Unground




Ground




Ground &







Test/Condition




Surface




Surface




Heat Treated











TRS (ksi)




113




169




108







Std Deviation (ksi)




 8




 6




 8







Weibull Modulus




 17




 32




 16















These test results show that the ground and heat treated transverse rupture bars had poorer (i.e., less) transverse rupture strength than did the ground surface transverse rupture bars of the same composition. It appears that the reason for this difference in the transverse rupture strength is due to the fact that the ground and heat treated transverse rupture bars had a greater surface roughness than the ground surface transverse rupture bars. Furthermore, the surface of the ground and heat treated transverse rupture bar (Mixture I) showed needle-like grains which were absent from the surface of the ground surface transverse rupture bar (Mixture I).




Table VII below sets forth the critical load in kilograms, which reflects the surface fracture resistance, for cutting inserts of Mixture I wherein each cutting insert was in one of the three conditions (i.e., unground surface, ground surface, or ground & heat treated). The technique used to measure the surface fracture resistance comprised an indentation test using a Rockwell hardness tester equipped with a brale diamond indenter at loads of 18 kilograms, 33 kilograms, 48 kilograms and 70 kilograms. At each load, the specimen was visually examined at 64× to determine the presence or absence of cracks in the surface so as to thereby ascertain the critical load at which cracks first appear in the surface of the cutting insert.












TABLE VII











Fracture Resistance: Critical Load






as Measured in Kilograms






for Cutting Inserts of Mixtures I through VII
















Mixture/




Unground




Ground




Ground &







Condition




Surface




Surface




Heat Treated











I




48




33




70+







II




18




33




48  







III




  70+




33




70  







IV




  70+




33




70+







V




48




33




70+







VI





48




70+







VII





33




70+















The above test results show that for most of the cutting inserts the ground and heat treated cutting inserts displayed the highest critical load. One exception was in the case of Mixture III where the unground surface cutting inserts had a higher (70+kilograms) critical load than the critical load (70 kilograms) of the ground and heat treated cutting inserts. The other exception was in the case of Mixture IV where the critical load of the ground and heat treated cutting insert was the same (i.e., 70+kilograms) as that for the unground surface cutting insert.




Table VIII below presents the finish tolerances for cutting inserts of Mixture I wherein each cutting insert was in one of the three conditions (i.e., unground molded surface, ground surface, or ground & heat treated).












TABLE VIII











Finish Tolerances for Cutting Insert















Unground




Ground




Ground &






IC Tolerance (+/−)




Molded Surface




Surface




Heat Treated









‘G’ 0.001 inches





X




X






‘M’ 0.003 inches




X






‘U’ 0.005 inches




X














This Table VIII above shows that the ground and heat treated cutting inserts met the “GI” tolerance requirements whereas the unground molded cutting inserts only met the “M” and “U” tolerance requirements. The dimensional control of the machined workpieces is much better with the use of “G” tolerance cutting inserts as compared to the use of either “M” tolerance cutting inserts or “U” tolerance cutting inserts.




Table IX sets out the results of hardness testing of cutting inserts made of Mixture I using a Vickers Hardness Test with a load of 50 grams and a load of 100 grams. Low angle polishing of the surface of the material specimens was used to make these hardness measurements close to the surface.




Table IX shows that the ground & heat treated cutting inserts exhibited a higher hardness near the surface of the material (i.e., in a surface region extending about 0.030 inches [0.762 mm] from the surface) than did the ground surface cutting inserts of Mixture I or unground surface cutting inserts of Mixture I. These test results also show that the surface region of the ground and heat treated cutting inserts (of Mixture I) presented a higher hardness than the bulk substrate thereof since the hardness of the bulk substrate of the ground and heat treated cutting inserts equates to the hardness of the ground surface cutting inserts.












TABLE IX











Summary of Average Hardnesses






of Cutting Inserts of Mixture I













Cutting Insert (Condition & Style)




Load (grams)




Average (VHN)









Ground Surface SNG433T




 50




1805 ± 42






Ground Surface SNG433T




100




2385 ± 83






Unground Surface SPG432




 50




2068 ± 26






Unground Surface SPG432




100




2419 ± 30






Ground & Heat Treated SNG433T




 50




2267 ± 55






Ground & Heat Treated SNG433T




100




2643 ± 47














Analyses were performed to ascertain the phases present and surface morphology of the ground surface cutting inserts, the unground surface cutting inserts, and the ground and heat treated cutting inserts. Referring to

FIGS. 2 and 3

, it was found that the surface region of the ground surface cutting insert had grind lines and a relatively flattened structure. An X-ray diffraction analysis showed that the surface region of the ground surface cutting insert comprised only beta silicon nitride.




Referring to

FIGS. 4 and 5

, these photomicrographs show a mixture of ground surfaces and unground surfaces characterized by acicular grain structure. An X-ray diffraction analysis showed that the surface region of the ground and heat treated ground cutting insert has present a beta silicon nitride phase and a Y


2


Si


3


O


3


N


4


phase.




Referring to

FIGS. 6 and 7

, these photomicrographs show unground surfaces characterized by needle-like grain structure. An X-ray diffraction analysis showed that the surface region of the unground surface cutting insert had present a beta silicon nitride phase, and a Y


2


Si


3


O


3


N


4


phase, and a silicon metal phase.




In the heat treatment step of the processing, the setting powder and/or the atmosphere may be tailored to provide controlled surface characteristics for a surface region (i.e., a volume of material extending from the surface inwardly toward the bulk substrate for a specific distance) as compared to the bulk substrate. One may consider the setting powder and/or the atmosphere a reaction source, i.e., a source for the reaction elements. For example, one may be able to achieve a wear resistant surface region in combination with a tougher bulk region. In regard to the setting powder, where it is desired to impart one or more of the following metals and/or their oxides and/or carbides into the surface region of the substrate, one may use a setting powder that contains one or more of the following and/or their reaction products: the oxides of aluminum, hafnium, zirconium, yttrium, magnesium, calcium and the metals of the lanthanide series of the elements; and the nitrides and/or carbides of silicon, titanium, hafnium, aluminum, zirconium, boron, niobium and carbon.




Another way to control the reaction with the surface to provide controlled surface characteristics is by the use of a gas or gases from the group comprising nitrogen, argon, and carbon monoxide/carbon dioxide. The pressure of these gases may range between sub-atmospheric and about 30,000 psi.




In another example, a Mixture IV β′ sialon composition cutting insert was sintered and ground as described before and then heat treated at 1750 degrees Centigrade for sixty minutes under 15-20 ksi nitrogen isostatic pressure in a setting powder of Si


3


N


4


, Al


2


O


3


, Y


2


O


3


, and optionally BN, and their reaction products. A comparison of x-ray diffraction traces obtained from the ground surface and then from the heat treated surface showed the following:
















PRIOR ART




INVENTION






Ground Surface Phases




Ground and Heat Treated Surface Phases

























β′ sialon




26.6 w/o α′ sialon




34.8 w/o α′ sialon






B phase, YAM,




73.4 w/o β′ sialon




65.2 w/o β′ sialon






wollastonite, and




and minor amounts




and minor amounts






intergranular glass




of melilite,




of melilite, YAM,







B phase and




B phase and







intergranular glass




intergranular glass














These heat treated and ground inserts of Mixture III were tested in metalcutting a modified Waspalloy Jet Engine, seven inch diameter main shaft, under the following rough turning conditions: 676 sfm, 0.008 ipr, 0.180 inch depth of cut, and a four inch length of cut. The ground and heat treated Mixture III material was indexed due to depth of cut notching and produced a workpiece surface finish of 56 RMS while the ground Mixture III material was indexed due to depth of cut notching and chipping and produced a poorer surface finish of 250 RMS.




This test demonstrates that a cutting tool having a β′ sialon bulk microstructure and a α′+β′ sialon surface microstructure can be produced by the present invention. It is also believed that cutting tools having a β silicon nitride bulk microstructure and β′ sialon or a α′+β′ sialon surface microstructure are also produceable by the present invention. To produce these microstructures, it is believed that the setting powder used in the heat treating step should contain, in addition to Si


3


N


4


, up to 50 w/o of AlN and/or Al


2


O


3


, and minor amounts of Y


2


O


3


(or a lanthanide oxide) to help control the α sialon produced in the surface.




Table X set forth below presents the results of the measurement by X-ray fluorescence of the aluminum content on the surface of cutting inserts of Mixture I wherein the cutting inserts were in one of three conditions (i.e., unground surface, ground surface, or ground & heat treated).












TABLE X











Measurement by X-Ray Fluorescence






of the Aluminum Content






on the Surface of Cutting Inserts of Mixture I















Aluminum in Weight Percent







Condition of the




on the Surface as Measured







Cutting Insert




by X-Ray Fluorescence











Ground Surface




less than 10 ppm








(parts per million)







Unground Surface




0.21 to 0.3 







Ground & Heat Treated




1.4 to 1.5















Referring to the results set forth in Table X above, this data shows that as a result of the heat treatment the content of the aluminum on the surface increased. The aluminum was obtained from the setting powder which contained alumina. This increase in aluminum may lead to an alloyed surface region (or layer) that has better properties such as, for example, increased wear resistance, increased hardness, and higher fracture resistance.




In another example, a ground cutting insert of Mixture I was heat treated at 1750 degrees Centigrade for 120 minutes under an isostatic pressure of 1500 psi of nitrogen and a silicon nitride based setting powder containing, as disclosed previously herein for Mixture I, but also containing 10 w/o of titanium nitride. X-ray diffraction and x-ray fluorescence analysis of the heat treated surface, respectively found: the presence of beta silicon nitride, with trace amounts of titanium nitride (TiN) and yttrium silicate (Y


2


SiO


5


) phases; and 5.8 w/o of titanium. It is expected that the addition of titanium nitride (or other materials) in this manner will avoid the problems associated with applying a coating of the same material to the heat treated material; namely, coating adhesion and/or thermal cracks in the coating, while providing a metalcutting performance benefit in certain applications (e.g., milling of class 40 gray cast iron).




Alternatively, the setting powder and/or the reactive atmosphere may help to deplete one or more undesirable (or selected) constituents from the surface region which would then lead to a compositional difference between the surface region and the bulk region. Such a compositional difference may also lead to improved performance, as well as improved properties, for the ground and heat treated cutting inserts as compared to the ground surface cutting inserts.




It seems apparent that applicant has provided an improved method for the production of a ceramic cutting tool including a silicon nitride-based cutting tool, a SiAlON-based cutting tool, an alumina-based cutting tool, a titanium carbonitride-based cutting tool, and a whisker-reinforced ceramic cutting tool. It is also apparent that applicant has provided an improved ceramic cutting tool wherein the cutting tool is a silicon nitride-based cutting tool, a SiAlON-based cutting tool, an alumina-based cutting tool, a titanium carbonitride-based cutting tool, or a whisker-reinforced ceramic cutting tool.




The performance tests reveal that for most cases the ground and heat treated cutting inserts experienced better performance than either the ground surface cutting inserts or the unground cutting inserts in milling and rough turning applications. The physical properties of the ground and heat treated cutting inserts were comparable to those of the ground surface cutting inserts. The microstructure of the ground and heat treated cutting inserts is different from that of either the ground surface cutting insert or the unground cutting inserts.




As an optional feature, the cutting inserts may be coated with a refractory coating (e.g., alumina, titanium nitride, titanium carbide, titanium carbonitride or titanium aluminum nitride). The coating may be applied by physical vapor deposition (PVD) techniques or by chemical vapor deposition (CVD) techniques. In the case where the coating scheme comprises multiple layers, at least one layer may be applied by CVD and at least one layer may be applied by PVD. Applicant expects that coated cutting tools would be suitable for the machining of gray cast iron, ductile iron, steels, and nickel-based alloys.




The patents and other documents identified herein are hereby incorporated by reference herein.




Other embodiments of the invention will be apparent to those skilled in the art from a consideration of the specification or practice of the invention disclosed herein. It is intended that the specification and examples be considered as illustrative only, with the true scope and spirit of the invention being indicated by the following claims.



Claims
  • 1. A process for making a heat treated ground ceramic cutting insert comprising the steps of:providing an uncoated ground ceramic cutting insert having at least a portion thereof being ground; and heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert, and wherein the heat treatment occurs in a nitrogen atmosphere at a pressure of one atmosphere and at a temperature of between about 1815 degrees Centigrade and 1860 degrees Centigrade for a duration of between about 130 minutes and about 270 minutes.
  • 2. The process according to claim 1 wherein:the heat treatment occurs in an atmosphere comprising one or more of nitrogen and argon and carbon monoxide; the heat treatment occurs at a pressure ranging from sub-atmospheric to about 30,000 psi; the heat treatment occurs at a temperature ranging between about 1300 degrees Centigrade and about 2200 degrees Centigrade; and the heat treatment occurs for a time between about fifteen minutes and about six hours.
  • 3. The process according to claim 1 further including the step of coating the heat treated ground ceramic cutting insert.
  • 4. The process according to claim 3 wherein the coating is selected from one or more compounds of the group consisting of alumina, titanium nitride, titanium carbonitride, titanium carbide and titanium aluminum nitride.
  • 5. The process according to claim 1 further including the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; hot isostatically pressing the sintered unground ceramic cutting insert compact so as to form an uncoated unground ceramic cutting insert blank; and grinding at least a portion of the uncoated unground ceramic cutting insert blank so as to form the uncoated ground ceramic cutting insert.
  • 6. The process according to claim 5 wherein after the hot isostatically pressing step, the uncoated unground ceramic cutting insert is subjected to an additional sintering step.
  • 7. The process according to claim 1 further including the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; and grinding at least a portion of the sintered unground ceramic cutting insert compact so as to form the uncoated ground ceramic cutting insert.
  • 8. The process according to claim 1 further including the steps of:forming a green ceramic cutting insert compact from a powder mixture; uniaxially hot pressing the green ceramic cutting insert compact so as to form a hot pressed unground ceramic cutting insert compact; and grinding at least a portion of the hot pressed unground ceramic cutting insert compact so as to form the uncoated ground ceramic cutting insert.
  • 9. The process according to claim 8 wherein the powder mixture comprises alumina and silicon carbide whiskers.
  • 10. The process according to claim 9 wherein the powder mixture further includes zirconia.
  • 11. The process according to claim 9 wherein the powder mixture further includes titanium carbonitride.
  • 12. A process for making a heat treated ground ceramic cutting insert comprising the steps of:providing an uncoated ground ceramic cutting insert having at least a portion thereof being ground; and heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert, and wherein the heat treatment occurs in an argon atmosphere at a pressure of about one atmosphere and at a temperature of about 1650 degrees Centigrade for a duration of about 60 minutes.
  • 13. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; grinding at least a portion of the sintered unground ceramic cutting insert compact so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert, and wherein the powder mixture comprises between about 60 weight percent and about 98 weight percent silicon nitride, up to about 25 weight percent aluminum nitride, up to about 25 weight percent alumina, up to about 2 weight percent magnesia, and up to about 7 weight percent yttria.
  • 14. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; hot isostatically pressing the sintered unground ceramic cutting insert compact so as to form an uncoated unground ceramic cutting insert blank; grinding at least a portion of the uncoated unground ceramic cutting insert blank so as to form the uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; and wherein the powder mixture comprises about 98 weight percent silicon nitride, about 1 weight percent magnesia and about 1 weight percent yttria.
  • 15. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; grinding at least a portion of the sintered unground ceramic cutting insert compact so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert, and wherein the powder mixture comprises about 85.4 weight percent silicon nitride, about 6.2 weight percent aluminum nitride, about 3.7 weight percent alumina, and about 4.7 weight percent yttria.
  • 16. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; grinding at least a portion of the sintered unground ceramic cutting insert compact so as to form an uncoated ground ceramic cutting insert; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert, and wherein the powder mixture comprises about 63.3 weight percent silicon nitride, about 9.3 weight percent aluminum nitride, about 22.7 weight percent alumina, and about 4.7 weight percent yttria.
  • 17. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; hot isostatically pressing the sintered unground ceramic cutting insert compact so as to form an uncoated unground ceramic cutting insert blank; grinding at least a portion of the uncoated unground ceramic cutting insert blank so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; and wherein the powder mixture comprises about 91.6 weight percent silicon nitride, about 1.6 weight percent aluminum nitride, about 1.3 weight percent alumina, and about 5.5 weight percent yttria.
  • 18. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; hot isostatically pressing the sintered unground ceramic cutting insert compact so as to form an uncoated unground ceramic cutting insert blank; grinding at least a portion of the uncoated unground ceramic cutting insert blank so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; and wherein the powder mixture is silicon nitride-based, and prior to the sintering step, the green ceramic cutting insert compact is in contact with a setting powder; and the setting powder includes one or more of the following and/or their reaction products: the oxides of aluminum, hafnium, zirconium, yttrium, magnesium, calcium and the metals of the lanthanide series of the elements; and nitrides and/or carbides of silicon, titanium, hafnium, aluminum, zirconium, boron, niobium and carbon.
  • 19. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; hot isostatically pressing the sintered unground ceramic cutting insert compact so as to form an uncoated unground ceramic cutting insert blank; grinding at least a portion of the uncoated unground ceramic cutting insert blank so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; and wherein the powder mixture including up to thirty volume percent of at least one component selected from the group of hafnia, zirconia, and the nitrides, carbides and/or carbonitrides of titanium, silicon, hafnium, and zirconium and their mixtures.
  • 20. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; uniaxially hot pressing the green ceramic cutting insert compact so as to form a hot pressed unground ceramic cutting insert compact; grinding at least a portion of the hot pressed unground ceramic cutting insert compact so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; and wherein the powder mixture comprises alumina and silicon carbide whiskers, the powder mixture comprises about 34.4 weight percent alumina, about 19.1 weight percent silicon carbide whiskers, about 0.3 weight percent yttria, and the balance titanium carbonitride.
  • 21. The process according to claim 20 wherein the titanium carbonitride has the formula TiCxNy, and equals about 0.5 and y equals about 0.5.
  • 22. A process for making a heat treated ground ceramic cutting insert comprising the steps of:forming a green ceramic cutting insert compact from a powder mixture; sintering the green ceramic cutting insert compact so as to form a sintered unground ceramic cutting insert compact; grinding at least a portion of the sintered unground ceramic cutting insert compact so as to form an uncoated ground ceramic cutting insert having at least a portion being ground; heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert, and wherein the powder mixture comprises about 14.2 weight percent zirconia; about 2.3 weight percent MgAl2O4; about 1.2 weight percent silicon carbide whiskers; about 0.14 silicon dioxide; about 0.02 calcium oxide; and the balance alumina.
  • 23. A process for making a heat treated ground ceramic cutting insert comprising the steps of:providing an uncoated ground ceramic cutting insert having at least a portion thereof being ground; and heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; and grinding at least a portion of the uncoated heat treated ground cutting insert.
  • 24. A process for making a heat treated ground ceramic cutting insert comprising the steps of:providing an uncoated ground ceramic cutting insert having at least a portion thereof being ground; and heat treating the uncoated ground ceramic cutting insert so as to form the heat treated ground ceramic cutting insert; wherein the uncoated ground cutting insert during the heat treating is in contact with a setting powder; and the setting powder includes one or more of the following and/or their reaction products: the oxides of aluminum, hafnium, zirconium, yttrium, magnesia, calcium, and the metals of the lanthanide series of the periodic table; and nitrides and/or carbides of silicon, titanium, hafnium, aluminum, zirconium, boron, niobium and carbon; and wherein during said heat treating said uncoated ground cutting insert reacting with said setting powder wherein the composition of surface of the uncoated ground ceramic cutting insert has been modified.
Parent Case Info

This application is a divisional of U.S patent application Ser. No. 09/576,833 filed May 22, 2000, now U.S. Pat. No. 6,610,113, which is a CIP of U.S patent application Ser. No. 09/393,004 filed Sep. 9, 1999, now abandoned.

US Referenced Citations (98)
Number Name Date Kind
4011108 Hellman et al. Mar 1977 A
4038092 Baumgartner et al. Jul 1977 A
4127416 Lumby et al. Nov 1978 A
4227842 Samanta et al. Oct 1980 A
4264548 Ezis Apr 1981 A
4264550 Ezis Apr 1981 A
4286905 Samanta Sep 1981 A
4296065 Ishii et al. Oct 1981 A
4388085 Sarin et al. Jun 1983 A
4401617 Ezis et al. Aug 1983 A
4406667 Sarin et al. Sep 1983 A
4406668 Sarin et al. Sep 1983 A
4409003 Sarin et al. Oct 1983 A
4409004 Sarin et al. Oct 1983 A
4416670 Sarin et al. Nov 1983 A
4421525 Sarin et al. Dec 1983 A
4431431 Sarin et al. Feb 1984 A
4433979 Sarin et al. Feb 1984 A
4434238 Ezis et al. Feb 1984 A
4440547 Sarin et al. Apr 1984 A
4440707 Shimamori et al. Apr 1984 A
4441894 Sarin et al. Apr 1984 A
4449989 Sarin et al. May 1984 A
4497228 Sarin et al. Feb 1985 A
4563433 Yeckley et al. Jan 1986 A
4575449 Lueth Mar 1986 A
4607017 Wolfe et al. Aug 1986 A
4609633 Fukuhara et al. Sep 1986 A
4632910 Lee et al. Dec 1986 A
4640693 Bhat et al. Feb 1987 A
4650498 Buljan Mar 1987 A
4652276 Burden Mar 1987 A
4670024 Bhat et al. Jun 1987 A
4711644 Yeckley et al. Dec 1987 A
4743571 Steinmann et al. May 1988 A
4745022 Miyake et al. May 1988 A
4769350 Nishioka et al. Sep 1988 A
4789277 Rhodes et al. Dec 1988 A
4843039 Akesson et al. Jun 1989 A
4848984 Ezis et al. Jul 1989 A
4880755 Mehrotra Nov 1989 A
4881950 Bhat et al. Nov 1989 A
4892792 Sarin et al. Jan 1990 A
4913936 Mehrotra et al. Apr 1990 A
4946630 Ezis Aug 1990 A
4959331 Mehrotra et al. Sep 1990 A
4959332 Mehrotra et al. Sep 1990 A
4960735 Mehrotra et al. Oct 1990 A
4961757 Rhodes et al. Oct 1990 A
4965231 Mehrotra et al. Oct 1990 A
5024976 Mehrotra et al. Jun 1991 A
5034022 Bhat et al. Jul 1991 A
5049531 Nakanishi et al. Sep 1991 A
5066553 Yoshimura et al. Nov 1991 A
5079198 Edler et al. Jan 1992 A
5110770 Brandt et al. May 1992 A
5122485 Akimune Jun 1992 A
5171723 Moriguchi et al. Dec 1992 A
5198165 Akimune et al. Mar 1993 A
5234643 Matsumoto Aug 1993 A
5250477 Baldoni, II et al. Oct 1993 A
5264297 Jindal et al. Nov 1993 A
5294575 Matsumoto Mar 1994 A
5296008 Moriguchi et al. Mar 1994 A
5308561 Leimer et al. May 1994 A
5316856 Suzuki et al. May 1994 A
5326733 Mizuno et al. Jul 1994 A
5352641 Matsui et al. Oct 1994 A
5370716 Mehrotra et al. Dec 1994 A
5382273 Mehrotra et al. Jan 1995 A
5384081 Wotting et al. Jan 1995 A
5384292 Matsui et al. Jan 1995 A
5405592 Edler et al. Apr 1995 A
5411923 Suzuki et al. May 1995 A
5424256 Yoshimura et al. Jun 1995 A
5432132 Dasgupta et al. Jul 1995 A
5439855 Rosenthal Aug 1995 A
5445776 Honma et al. Aug 1995 A
5449649 Li et al. Sep 1995 A
5453232 Hida et al. Sep 1995 A
5455000 Seyferth et al. Oct 1995 A
5472919 Mitomo et al. Dec 1995 A
5502011 Yamamoto et al. Mar 1996 A
5525134 Mehrotra et al. Jun 1996 A
5541143 Hirosaki et al. Jul 1996 A
5545362 Hirosaki et al. Aug 1996 A
5545597 Yeckley Aug 1996 A
5571760 Pujari et al. Nov 1996 A
5628590 Beeghly et al. May 1997 A
RE35538 Akesson et al. Jun 1997 E
5668069 Sato et al. Sep 1997 A
5683481 Chatterjee et al. Nov 1997 A
5691261 Takahashi et al. Nov 1997 A
5705449 Hirao et al. Jan 1998 A
5720917 Matsuura et al. Feb 1998 A
5759481 Pujari et al. Jun 1998 A
5858181 Jindal et al. Jan 1999 A
6204213 Mehrotra et al. Mar 2001 B1
Foreign Referenced Citations (17)
Number Date Country
3938644 May 1990 DE
3939989 Jul 1990 DE
4000777 Aug 1990 DE
0107919 May 1984 EP
0298936 Jan 1989 EP
0497355 Aug 1992 EP
0499861 Aug 1992 EP
0589997 Apr 1994 EP
0615963 Sep 1994 EP
0472256 Aug 1995 EP
6252192 Mar 1987 JP
0354143 Mar 1991 JP
3193666 Aug 1991 JP
4-136174 May 1992 JP
9114017 Sep 1991 WO
WO 9718177 May 1997 WO
WO 9735817 Oct 1997 WO
Non-Patent Literature Citations (9)
Entry
Sivasankaran et al., “Wear of Ceramic Tools in MachiningCast Iron”, pp. 293-301, no date.
Beeghly et al., “Application-Specialized Ceramics: A Silicon Nitride for Machining Gray Cast Iron”, pp. 91-99; ASM Confenrence: Tool Materials, Scottsdale, AZ (Feb. 1987).
Janardhana Reddy et al., “Comparative Studies of Ceramic and Tungsten Carbide Tools for Machining Grey Cast Iron,” pp. 161-171; Conference: Advanced Ceramics; India (Mar., 1990).
Tennenhouse et al., “Interaction of Silicon Nitride and Metal Surfaces”, J. Am. Ceramic Soc.68 (1)C30-C31 (1995), no month.
Agranov et al., “Wear Behavior of Hot Pressed Silicon Nitride in Cutting of Cast Iron”, Ind. Ceramics vol. 8, No. 4 pp. 192-197 (1988), no month.
Bhola et al., “Ceramic Cutting Tool Inserts”, Key Engineering Materials, vols. 122-124 (1996), pp. 235-246, no month.
Nishioka et al., “Mechanical Properties of Si3N4 Ceramics with ZrO2-addition under High Temperature and Observation of the Micro-Structure”, date unknown.
Falk et al., “Microstructure and Short Term Oxidation of Hot-Pressed Si3N4/ZrO2(+Y2O3) Ceramics”, J. Am.Ceramic Soc. 75 (1) (1992) pp. 28-35, no month.
Knutson-Wedel, Si3N4 Ceramic Formed by HIP Using Additions of ZrO2, Ceramics Today—Tomorrow's Ceramics, Materials Science Monographs, 66B, Elsevier Science Publishers B.V. (1991), no month pp. 1347-1356.
Continuation in Parts (1)
Number Date Country
Parent 09/393004 Sep 1999 US
Child 09/576833 US