PROCESS FOR HYBRID CARBON CAPTURE AND MINERALIZATION

Abstract

The principal approaches to reducing the effects of global warming seek to slow the increase in atmospheric CO2 levels as a result of fossil fuel combustion for energy production and transportation. A process for hybrid carbon capture and mineralization are disclosed. The process utilizes both flue gas from (e.g., power plants) and reject brine from (e.g., desalination process). The process includes providing flue gas to react with an amine solution to produce carbamate; processing the carbamate in a reactor to regenerate amine and to produce a carbonate; treating reject brine to provide a ready-made brine for carbonation reaction; and processing the carbamate with salt from treating the brine to produce a carbonate.

Description

BACKGROUND

Carbon dioxide (CO₂) considered as one of the main contributor to the greenhouse gases (GHGs and it has a negative effect on the environment. In industry scale, CO₂ is released to the environment as an exhaust stream from different sources including combustion reactions, incineration (flue gas), reformer, etc. Recently, there is a lot of pressure to capture CO₂ waste stream and either store it or convert it to valuable products (carbon capture, sequestration and utilization). On the other hand, demand on fresh water is steadily increasing due to the rapid growth of population. Therefore, water desalination plants is steadily increasing as a reliable technology to produce fresh water in large scale. Reject brine is the waste stream from desalination plants and there are different disposal methods, where surface water discharge (SWD) is mostly used. SWD has a negative environment effect on the marine life in addition to being costly process (e.g., $0.05/m³: $0.30/m³ of brine rejected).

Carbon capture and mineralization has been a challenge. Carbon dioxide absorption in water is a slow reaction with extremely slow kinetics. Such conditions requires a relatively big reactor volume, which in turn will require a high capex or normal reactor size, but with a high residence time resulting in a negative affect on productivity.

SUMMARY

The present disclosure relates generally to a process for hybrid carbon capture and mineralization. According to an embodiment, the process utilizes two waste streams 1) flue gas from, for example, power plants and 2) reject brine from, for example, desalination plants for mineralization process to produce carbonates including CaCO₃, MgCO₃, Na₂CO₃, BaCO₃, and the like. By using this process, the flue gas is treated instead of flaring to the environment, reject brine is utilized rather than being disposed back to environment, and most importantly, valuable products (carbonates) used in building rocks, concrete, cement, and other suitable applications are produced.

Applicant surprisingly found that to overcome the slow reaction kinetics of carbon dioxide capture, an amine solution for absorbing CO₂ is selected to ensure high and fast CO₂ absorption.

In a first non-limiting aspect of the present disclosure, a process for hybrid carbon capture and mineralization is provided. The process includes providing any streaming source of CO₂ to react with an amine solution to produce carbamate; directing the carbamate to a reactor to regenerate amine and to produce carbonates; treating reject brine to make ready the brine for carbonation reaction; and the carbamate reacting with salt from the brine to produce carbonates.

In a further aspect, such streaming sources include, but are not limited to, flue gas from power plants, waste gases from incinerators, waste stream from reformers (methanol, urea, etc.), and waste gases from combustion reactions.

In another aspect, the process for hybrid carbon capture and mineralization can capture carbon from any brine source stream. The brine source streams include, but are not limited to, reject brine from desalination plants, seawater stream, produced water from oil & gas plants, wastewater from GTL plants, alkaline waste, saline groundwater; brackish water.

In an embodiment, the resulting products of the process for hybrid carbon capture and mineralization are carbonates. The process works for a non-limiting variety of elements such as all of group #2 (Ca, Mg, Ba, Be, Sr, and Ra). Further, the process works for all of group #1 (Li, Na, K, Rb, Cs, and Fr), however, the addition of an entrainer is required to alter the pH to avoid the relatively high solubility of group #1 in water. Finally, the process works for some transition metals including, but not limited to, Pb, Fe, Cu, and Cd.

In another embodiment, potential amines include, but are not limited to, primary amines (MEA, DGA), secondary amine (DEA, DIPA), tertiary amine (MDEA, TEA), amino acids, aromatic amines (aniline, etc.), cyclic aromatic amines (pyridine, piperazine, pyrimidine, triazole, tetrazole, pirrole, imidazole, etc.), cyclic amines (Piperidine, pirrolidine, etc.), sterically hindered amines (PZ, AMP, DETA, AEEA, MAPA, DETA, TETA, TEPA), PZ derivatives (1-MPZ, 1-EPZ, DMPZ, HEP, TEDA), immobilized amines on metal oxides (Ti, Ni, Si, Zn, Zr, etc.), metal oxides, binary and ternary metal oxides, physical solvents (K₂CO₃, etc.), ionic liquids, deep eutectic solvents, blended amines (bi-blend, tri-blend and tetra-blend), ammonia, and alkali.

An advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization can succeed through the use of amine solution with a neutral pH. Similar processes require alkaline media to precipitate carbonates and use of alkaline media such as NaOH, CaO, Ca(OH)₂, MgO, Mg(OH)₂ significantly increase the relative cost of the process and negatively impact any return on investment from carbon capture and mineralization. The use of an amine solution produces carbamate and, with the addition of brine, a carbonate precipitates. Then, the amine is “chemically regenerated” and can be reused for more process for hybrid carbon capture and mineralization.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization results in a fast reaction time and increased kinetics for CO₂ absorption.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization does not use an alkaline source for the precipitation process.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization precipitates carbonate at neutral pH.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization chemically regenerates the reusable amine solution.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization eliminates any thermal energy requirements for amine solvent regeneration.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization eliminates the need for a stripper column in the CO₂ capture process, meaning there is a lower capex and shorter payback period.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization reduces and/or eliminates the stripper column high corrosion rate at the bottom section where the carbon dioxide was in relatively higher concentration and the temperature (average of 125° C.).

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization eliminates the need for anti-corrosion technology in CO₂ capture plant.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization ensures a relatively high CO₂ loading capacity.

A further advantage of one or more embodiments provided by the present disclosure is that the process for hybrid carbon capture and mineralization works at nearly room temperature conditions (atmospheric pressure and room temperature).

Additional features and advantages are described herein, and will be apparent from the following Detailed Description and the figures.

BRIEF DESCRIPTION OF THE FIGURES

The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the office upon request and payment of the necessary fee.

FIG. 1 shows a Novel Absorption-Mineralization Process Flow Diagram.

FIG. 2 shows a Group #2 Reaction Mechanism.

FIG. 3 shows Rich Amine Regeneration Mechanism.

FIG. 4 shows Carbon Capture, Sequestration and Utilization Reaction Experimental Steps.

FIG. 5 shows FT-IR spectra of CaCO₃.

FIG. 6 shows XRD spectra of CaCO³.

FIG. 7 shows FT-IR spectra of BaCO₃.

FIG. 8 shows XRD spectra of BaCO₃.

FIG. 9 shows FT-IR spectra of MgCO₃.

FIG. 10 shows FT-IR spectra of Na₂CO₃.

FIG. 11 shows XRD spectra of Na₂CO₃.

DETAILED DESCRIPTION

The present disclosure provides a process for hybrid carbon capture and mineralization. The process utilizes two waste streams including flue gas from power plants and other suitable sources and reject brine from desalination plants and other suitable sources for mineralization process to produce carbonates (e.g., CaCO₃, MgCO₃, Na₂CO₃, BaCO₃, the like, and suitable combinations thereof). The process treats both flue gas and reject brine in the same process to produce commercially-valuable products (i.e., carbonates). The process also includes a step of regenerating amine.

The process—as illustrated in FIG. 1—includes the following steps according to an embodiment: during step (1), flue gas reacts with an amine solution to produce carbamate; a circulated amine solution along with a makeup amine (e.g., to make up any amine loss during the whole process) enters to react with flue gas; and the resulting rich amine solution is directed to a reactor to regenerate amine and to produce carbonates. During step (2), reject brine is treated to make ready the brine (i.e., salt source stream) for carbonation reaction. During step (3), the rich amine solution (i.e., carbamate) reacts with salt from the brine to produce carbonates and regenerates the rich amine solution; this step ends with precipitation of carbonates from the liquid phase. During step (4), the solid carbonates are separated from the amine solution; the solid carbonates are washed with amine solutions and dried to produce anhydride carbonates.

The process for hybrid carbon capture and mineralization can treat both flue gas (which is otherwise released to the environment) and reject brine (which is otherwise disposed to the environment), thus benefiting the environment in both ways. Further, both waste streams are utilized by the present process to produce commercially valuable products of carbonates, which are commonly used in concrete, cement and other suitable building blocks and applications.

The present process provides a number of advantages including, for example: 1) it provides an economical process for CO₂ capture, sequestration and utilization; 2) it is scalable and it can be designed to fit small-, mid- or large-scale plants; 3) it can be adaptable to any suitable gas stream and/or any suitable brine source stream; 4) a variety of different and suitable amine solutions may be used in the process; 4) it can be easily adapted to any suitable current or new co-generation plant; 5) it can work with any suitable alkaline waste streams; 6) it can work for any suitable CO₂ source stream; 7) it can work for any suitable brine source stream.

The present process provides a number of desirable features related to CO₂ capture, for example: 1) it chemically regenerates the rich amine solution to provide a lean amine solution to the process; 2) it does not require any thermal energy for amine regeneration; 3) it does not require a stripper column in CO₂ capture process; 4) it does not require an anti-corrosion of CO₂ capture plant; 5) it works well at nearly room temperature; and 6) it does not require an external alkaline source.

Further, the present process for hybrid carbon capture and mineralization is economically favorable as the starting materials are two waste streams and the end products do not need further treatment with a lifelong market demand.

It should be understood that various changes and modifications to the presently preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modifications can be made without departing from the spirit and scope of the present subject matter and without diminishing its intended advantages. It is therefore intended that such changes and modifications be covered by the appended claims.

EXAMPLES

The following non-limiting examples are experimental examples supporting one or more embodiments provided by the present disclosure.

Example 1. Reaction for Ca-, Mg- and Ba-salts

FIG. 2 shows examples of Group #2 Reaction Mechanism.

In a two-neck round bottom flask, 10 g of piperazine was added to 80 g of deionized water under continuous stirring, at room temperature. Upon complete dissolution of the amine, the pH, measured by pH-meter, was raised to 11-12. CO₂ gas (purity 4N) was purged via rubber septum into the solution with a pressure of 1 bar and continuous stirring (600 rpm). The pH gradually dropped between 7-6. After approximately 15 minutes, the pH became stable and 10 g of CaCl₂) (or MgCb, or BaCb) was added to the mixture.

Immediately, the solution turned from clear to milky and a white fine precipitate started crushing out. After 30 minutes from the addition of the salt, the purging of CO₂ was stopped. The solution was filtered under vacuum. The filtrate was washed with deionized water and left to dry in the oven overnight. The resulting white solid, with yields ranging from 20 to 90%, was characterized by FT-IR, SEM, XRD, and EDS. All the used characterization techniques confirmed the formation of carbonate.

Example 2. Reaction for Na-Salts (Group #1)

In a two-neck round bottom flask, 10 g of piperazine was added to 80 g of deionized water under continuous stirring at room temperature. Upon complete dissolution of the amine, the pH, measured by pH-meter, raised to 11-12. CO₂ gas (purity 4N) was purged via rubber septum into the solution with a pressure of 1 bar and continuous stirring (600 rpm). The pH gradually dropped between 7-6. After approximately 15 minutes, the pH became stable and 80 g of acetone was added to the mixture. Once the two liquids mixed completely, 10 g of NaCl was added.

Slowly, the solution turned from clear to milky and a white fine precipitate started crushing out. After 3 minutes from the addition of the salt, the purging of CO₂ was stopped. The solution was filtered under vacuum. The filtrate was washed with acetone and left to dry in the oven overnight. The resulting white solid was characterized by FT-IR, SEM, XRD, and EDS. All the used characterization techniques confirmed the formation of carbonate.

Example 3. Regeneration Reaction

FIG. 3 shows an example of a Rich Amine Regeneration Mechanism.

FIG. 4 shows an example of Carbon Capture, Sequestration and Utilization Reaction Experimental Steps.

The spent solution obtained from the aforementioned reaction was added to a two-neck round bottom flask under continuous stirring. The initial pH was in the range of 5-6. The pH was adjusted up to a value of 11 with the addition of cone NaOH solution. In another embodiment, a makeup amine also can be used. At this point, CO₂ gas (purity 4N) was purged via rubber septum into the solution with pressure of 1 bar and continuous stirring. The pH gradually dropped between 7-6.

Slowly, the solution turned from clear to milky and a white fine precipitate started crushing out. After 30 minute the purging of CO₂ was stopped. The solution was filtered under vacuum. The filtrate was washed with deionized water and left to dry in the oven overnight. The resulting white solid was characterized by FT-IR, SEM, and EDS. All the used characterization techniques confirmed the formation of carbonate arising from the unreacted salt already present in the spent solution.

TABLE 1
Summary of tested salts, regenerated amine, and product yield.
				Regenerated
			Product	Amine Solution
Brine Feed	Yield %	Product	(gm)	(gm)
CaCl2	93.25	CaCO3	8.41	87.93
MgCl2	31.62	MgCO3	2.8	89.43
BaCl2	69.34	BaCO3	7.92	82.84
NaCl	22.88	Na2CO3	4.15	—

Example 4. Product Characterization of CaCO₃

FIG. 5 (top figure) shows FT-IR for the experimentally produced CaCO₃ and (bottom figure) FT-IR from the literature reference for comparison.

FIG. 6 shows the XRD for the experimentally produced CaCO₃.

The isolated solids have been preliminary characterized by Attenuated total reflection (ATR) FT-IR and X-ray powder diffraction (XRD).

The FT-IR spectrum for CaCO₃ matches with the literature, revealing a mineral morphology like calcite. The XRD analysis confirmed the presence of calcite and valerite (see FIGS. 5 and 6).

Example 5. Product Characterization of BaCO₃

FIG. 7 (top figure) shows FT-IR for the experimentally produced BaO₃ and (bottom figure) FT-IR from the literature reference for comparison.

FIG. 8 shows the XRD for the experimentally produced BaCO₃.

The FT-IR spectrum for BaCO₃ matches with the literature. The XRD analysis confirmed the presence of BaCO₃ as whiterite (See FIGS. 7 and 8).

Example 6. Product Characterization of MgCO₃

FIG. 9 (top figure) shows FT-IR for the experimentally produced MgCO₃ and (bottom figure) shows the FT-IR from the literature reference for comparison.

The FT-IR spectrum for MgCO₃ matches with the literature. The XRD analysis did not match with any known morphology for MgCO₃, however, the Energy-dispersive X-ray spectroscopy (SED) confirmed the presence of hydrated MgCO₃.

Example 7. Product Characterization of Na₂CO₃

FIG. 10 (top figure) FT-IR for the experimentally produced Na₂CO₃ and (bottom figure) shows FT-IR from the literature reference for comparison.

FIG. 11 shows the XRD for the experimentally produced Na₂CO₃.

The FT-IR spectrum for Na₂CO₃ matches with the literature (FIG. 10). The XRD analysis confirmed the presence of Na₂CO₃, as natrite, together with the presence of NaCl, that can be removed by further washing the sample with water:acetone mix (FIG. 11).

Example 8. Proof of Concept

Regarding outputs, the solid product is Carbonate, not bicarbonate or other product, as characterized by the XRD analysis as well as FT-IR, EDS and SEM. The FT-IR analysis is compared with literature and confirmed carbonate formation.

The reaction yield is the amount of product obtained in a chemical reaction. For benchmark comparison, one can compare against the conventional/standard process:

Na₂CO_3(aq)+Ca²⁺ or Mg²⁺+CaCO₃ or MgCO₃

TABLE 2
Yield comparison
	Benchmark Yield from
Product	conventional recess	Yield from Novel Process
CaCO3	Average of 90% Calera Process	93.25%

Example 9. Scale-Up

The proof of concept was conducted on a lab scale (100 ml reactor volume). Increasing the scale of such a process requires will require additional and gradual scaling up of the reactor volume, while increasing the maturity of the process as reflected in the below Table 3.

TABLE 3
Scale-Up Criteria
Scale	Reactor Volume	Location	Timeline
Small	100 ml-1000 ml	ROG-Applied Chemistry Lab	By 2020
Mid	5000	ml	RDC- Applied Chemistry Lab	By 2022
Large	1000	L	To be decided	To be decided

For each level of scale, different parameters are be checked and optimized for scale adaptions including: reaction conditions (temperature, pressure, and rotation speed); reactant ratios; amine type and concentration; regenerated amine solution activity; filtration, washing and drying time and type; product yield, stability and quality; detailed techno-economics study (payback, ROI, NPV, breakthrough point, etc.); and frequent updates to the products market need and value.

The versatile process for hybrid carbon capture and mineralization is an economical process for CO₂ capture, sequestration, and utilization; scale-adapted and can be designed to fit small, mid and large-scale plants; can be adapted for different gas stream; can be adapted for any brine source stream; succeed using many amine solvents; can be easily adapted to a current and new co-generation plant, where CO₂ source is available from (flue gas) and reject brine stream is coming from desalination plants; and can succeed in alkaline waste streams.

Claims

1. A process for hybrid carbon capture and mineralization, the process comprising: providing flue gas to react with an amine solution to produce carbamate;processing the carbamate to regenerate amine and to produce carbonates;treating reject brine to provide ready-made brine for carbonation reaction; andprocessing the carbamate with salt from treating reject brine to produce a carbonate.

2. The process of claim 1 further comprising providing a makeup amine to make up any amine loss during the process.

3. The process of claim 1 further comprising precipitation of a solid carbonate from the liquid phase.

4. The process of claim 3 further comprising separating the solid carbonate from the amine solution.

5. The process of claim 4 further comprising washing the solid carbonate with an amine solution and drying the washed solid carbonate to produce an anhydride carbonate.

6. The process of claim 1, wherein the carbonate product comprises an alkaline-earth metal of Group #2 (Ca, Mg, Ba, Be, Sr, and Ra) and a carbonate ion.

7. The process of claim 1, wherein the carbonate comprises an alkali metal of Group #1 (Li, Na, K, Rb, Cs, and Fr) and a carbonate ion, wherein the addition of an entrainer is required.

8. The process of claim 1, wherein the carbonate comprises a transition metal (Pb, Fe, Cu, and Cd) and a carbonate ion.

9. The process of claim 7, wherein the entrainer is from an organic family such as acetone, ethanol, methanol, and isopropanol.

10. The process of claim 6, wherein the carbonate is at least one of CaCO3, MgCO3, Na2CO3, and BaCO3.

11. A process for hybrid carbon capture and mineralization, the process comprising: adding 10 g of piperazine to 80 g of deionized water under continuous stirring at room temperature to make a solution,measuring and raising the pH to 11-12,purging CO2 gas via a rubber septum into the solution,dropping the pH to between 7-6,letting the solution stand for approximately 15 minutes,verifying the pH of the solution is stable,adding 10 g of at least one of CaCl2), MgCb, and BaCb to the solution,ceasing purging after 30 minutes from the addition of the salt,filtering the solution under vacuum filtration,washing the filtrate with deionized water, anddrying in the oven overnight.

12. The process of claim 11, wherein the purging of occurred under 1 bar of pressure and continuous stirring at 600 rpm.

13. The process of claim 11, wherein the purging is done with purity 4N CO2.

14. The process of claim 11, wherein after verifying the pH of the solution is stable, the process comprises: adding 80 g of acetone to the solution,mixing the acetone and the solution completely,adding 10 g of NaCl,ceasing purging after 30 minutes from the addition of the salt,filtering the solution under vacuum filtration,washing the filtrate with acetone, anddrying in the oven overnight.

15. The process of claim 14, wherein the purging of occurred under 1 bar of pressure and continuous stirring at 600 rpm.

16. The process of claim 14, wherein the purging is done with purity 4N CO2.

17. A process for hybrid carbon capture and mineralization, the process comprising: regenerating an amine solution, wherein the regenerating comprises: adjusting pH of a spent solution resulting from the process of claims 11 and 14 to a pH of 11,purging CO2 gas via a rubber septum into the solution,dropping the pH to between 7-6,letting the solution stand for approximately 15 minutes,verifying the pH of the solution is stable,adding 10 g of at least one of CaCl2), MgCb, and BaCb to the solution,ceasing purging after 30 minutes from the addition of the salt,filtering the solution under vacuum filtration,washing the filtrate with deionized water, anddrying in the oven overnight.

18. The process of claim 17, wherein the adjusting pH of a spent solution resulting from the process of claims 11 and 14 to a pH of 11 is done by the addition of at least one of a cone NaOH solution and a makeup amine.

19. The process of claim 17, wherein the purging of occurred under 1 bar of pressure and continuous stirring at 600 rpm.

20. The process of claim 14, wherein the purging is done with purity 4N CO2.