Claims
- 1. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of one or more aluminum salt(s) with a titrating agent, thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 8.0 to about 12.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with salts of an element selected from the group consisting of nickel, cobalt, and mixtures thereof, and salts of a heavy metal selected from the group consisting of molybdenum, tungsten, and mixtures thereof, and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 1% w to about 5% w cobalt and/or nickel and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 2. The process of claim 1 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 3. The process of claim 1 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 4. The process of claim 1 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 5. The process of claim 1 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 6. The process of claim 1 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 7. The process of claim 1 wherein step (d) contains salts of nickel and molybdenum.
- 8. The process of claim 7 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 9. The process of claim 1 wherein step (d) contains salts of cobalt and molybdenum.
- 10. The process of claim 9 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 11. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) precipitating an aqueous solution of one or more aluminum salt(s) by adjusting the pH of said solution to a range between about 5.5 and about 10.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing salts of a heavy metal selected from the group consisting of molybdenum, tungsten and mixtures thereof, salts of an element selected from the group consisting of nickel, cobalt and mixtures thereof, and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 1% w to about 5% w nickel and/or cobalt and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 12. The process of claim 11 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 13. The process of claim 11 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 14. The process of claim 11 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 15. The process of claim 11 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 16. The process of claim 11 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 17. The process of claim 11 wherein said solution in step (d) contains salts of nickel and molybdenum.
- 18. The process of claim 17 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 19. The process of claim 12 wherein said solution in step (d) contains salts of cobalt and molybdenum.
- 20. The process of claim 19 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 21. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) precipitating an aqueous solution of one or more aluminum salt(s) by adjusting the pH of said solution to a range between about 5.5 and about 10.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble salts of an element selected for the group consisting of nickel, cobalt and mixtures thereof, dry, water-soluble salts of a heavy metal selected from the group consisting of molybdenum, tungsten and mixtures thereof, and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal, at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 1% w to about 5% w nickel and/or cobalt and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 22. The process of claim 21 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 23. The process of claim 21 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 24. The process of claim 21 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 25. The process of claim 21 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 26. The process of claim 21 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 27. The process of claim 21 wherein said salts in step (d) are salts of nickel and molybdenum.
- 28. The process of claim 27 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 29. The process of claim 21 wherein said salts in step (d) are salts of cobalt and molybdenum.
- 30. The process of claim 29 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 31. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) precipitating an aqueous solution of one or more aluminum salt(s) by adjusting the pH of said solution to a range between about 5.5 and about 10.0 at a temperature in the range between about 20.degree. C. and about 90.degree.C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble salt of a heavy metal selected from the group consisting of molybdenum, tungsten and mixtures thereof, and a mixture of a dry, water-soluble salt selected from the group consisting of nickel, cobalt and mixtures thereof, and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal with the precipitate at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 1% w to about 5% w nickel and/or cobalt and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 32. The process of claim 31 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 33. The process of claim 31 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 34. The process of claim 31 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 35. The process of claim 31 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 36. The process of claim 31 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 37. The process of claim 31 wherein said salts in step (d) salts are salts of nickel and molybdenum.
- 38. The process of claim 31 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 39. The process of claim 31 wherein said salts in step (d) salts are salts of cobalt and molybdenum.
- 40. The process of claim 39 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 41. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt with an aqueous solution of a basic aluminum compound at a pH in the range between about 5.5 and about 10.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing salts of a heavy metal selected from the group consisting of molybdenum, tungsten and mixtures thereof, and salts of an element selected from the group consisting of nickel, cobalt and mixtures thereof, and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 1% w to about 5% w nickel and/or cobalt and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 42. The process of claim 41 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 43. The process of claim 41 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 44. The process of claim 41 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 45. The process of claim 41 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 46. The process of claim 41 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 47. The process of claim 41 wherein said solution in step (d) contains salts of nickel and molybdenum.
- 48. The process of claim 47 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 49. The process of claim 41 wherein said solution in step (d) contains solubilized salts of cobalt and molybdenum.
- 50. The process of claim 49 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 51. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt with an aqueous solution of a basic aluminum compound at a pH in the range between about 5.5 and about 10.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble salts an element selected from the group consisting of nickel, cobalt and mixtures thereof, dry, water-soluble salts of a heavy metal selected from the group consisting of molybdenum, tungsten and mixtures thereof, and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 1% w to about 5% w nickel and/or cobalt and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 52. The process of claim 51 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 53. The process of claim 51 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 54. The process of claim 51 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 55. The process of claim 51 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 56. The process of claim 51 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 57. The process of claim 51 wherein said salts in step (d) are salts of nickel and molybdenum.
- 58. The process of claim 51 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 59. The process of claim 51 wherein said salts in step (d) are salts of cobalt and molybdenum.
- 60. The process of claim 59 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 61. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aequeous solution of an acid aluminum salt with an aqueous solution of a basic aluminum compound at a pH in the range between about 5.5 and about 10.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble salt of heavy metal selected from the group consisting of molybdenum, tungsten and mixtures thereof, and a mixture of a dry, water-soluble salt selected from the group consisting of nickel, cobalt and mixtures thereof and a phosphorus-containing compound in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of heavy metal with the precipitate at a pH in the range between about 4.0 and about 9.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 1% w to about 5% w nickel and/or cobalt and from about 8% w to about 32% w heavy metal,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 62. The process of claim 61 wherein the precipitation is carried out at a pH in the range between about 5.5 and about 8.0.
- 63. The process of claim 61 wherein the precipitation is carried out at a temperature between about 50.degree. C. and about 85.degree. C.
- 64. The process of claim 61 wherein the aging pH is in the range between about 9.5 and about 10.5.
- 65. The process of claim 61 wherein step (d) is carried out at a pH in the range between about 4.0 and about 8.0.
- 66. The process of claim 61 wherein said phosphorus-containing compound is selected from the group consisting of phosphoric acid, a phosphate salt and mixtures thereof.
- 67. The process of claim 61 wherein said salts in step (d) are salts of nickel and molybdenum.
- 68. The process of claim 67 wherein said catalyst contains from about 2.5% w to about 4% w nickel and from about 8% w to about 18% w molybdenum.
- 69. The process of claim 61 wherein said salts in step (d) are salts of cobalt and molybdenum.
- 70. The process of claim 69 wherein said catalyst contains from about 2.5% w to about 4% w cobalt and from about 8% w to about 18% w molybdenum.
- 71. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing molybdate or dimolybdate salts and nickel salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 72. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing molybdate or dimolybdate salts and cobalt salts and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 73. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble nickel salts and dry, water-soluble molybdate or dimolybdate salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum, at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 74. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble cobalt salts and dry, water-soluble molybdate or dimolybdate salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum, at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 75. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble molybdate or dimolybdate salt and a mixture of a dry, water-soluble nickel salt and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum with the precipitate at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 76. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble molybdate or dimolybdate salt and a mixture of a dry, water-soluble cobalt salt and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum with the precipitate at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 77. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., which process comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a base at a pH in the range between about 5.5 and about 8.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing molybdate or dimolybdate salts and nickel salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 78. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride with an aqueous solution of a base at a pH in the range between about 5.5 and about 8.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing molybdate or dimolybdate salts and cobalt salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 79. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a base at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble nickel salts and dry, water-soluble molybdate or dimolybdate salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum, at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 80. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a base at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble cobalt salts and dry, water-soluble molybdate or dimolybdate salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum, at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 81. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a base, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble molybdate or dimolybdate salt and a mixture of a dry, water-soluble nickel salt and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum with the precipitate at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 82. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid aluminum salt selected from the group consisting of aluminum sulfate, aluminum nitrate and aluminum chloride, with an aqueous solution of a base, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble molybdate or dimolybdate salt and a mixture of a dry, water-soluble cobalt salt and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum with the precipitate at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 83. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate at a pH in the range between about 5.5 and about 8.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing molybdate or dimolybdate salts and nickel salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 84. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate at a pH in the range between about 5.5 and about 8.0 and a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with one or more solution(s) containing molybdate or dimolybdate salts and cobalt salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. until adsorption of the salts onto the precipitate is sufficient to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 85. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble nickel salts and dry, water-soluble molybdate or dimolybdate salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum, at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 86. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing the precipitate with dry, water-soluble cobalt salts and dry, water-soluble molybdate or dimolybdate salts, and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum, at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 87. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble molybdate or dimolybdate salt and a mixture of a dry, water-soluble nickel salt and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum with the precipitate at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w nickel and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
- 88. A process for hydrotreating hydrocarbon feeds by contacting said feeds at a temperature in the range of from about 300.degree. F. to about 900.degree. F. and a pressure in the range of from about 200 psig to about 3500 psig with a hydrotreating catalyst having a surface area of at least about 300 m.sup.2 /g, at least about 20% of the pore volume in pores having diameters greater than about 350 .ANG. and at least about 20% of the pore volume in pores having diameters less than about 70 .ANG., wherein said catalyst is prepared by a process which comprises:
- (a) titrating an aqueous solution of an acid with an aqueous solution of a basic aluminum compound selected from the group consisting of sodium aluminate and potassium aluminate, at a pH in the range between about 5.5 and about 8.0 at a temperature in the range between about 20.degree. C. and about 90.degree. C., thereby forming a precipitate,
- (b) aging the precipitate at a temperature ranging from about 20.degree. C. to about 90.degree. C. for at least about 15 minutes at a pH ranging from about 9.0 to about 11.0,
- (c) washing the precipitate,
- (d) mixing a dry, water-soluble molybdate or dimolybdate salt and a mixture of a dry, water-soluble cobalt salt and phosphoric acid in an amount of from about 0.2 to about 1.5 moles of phosphorus per mole of molybdenum with the precipitate at a pH in the range between about 4.0 and about 8.0 and a temperature in the range between about 25.degree. C. and about 100.degree. C. to yield a final catalyst having from about 2.5% w to about 4% w cobalt and from about 10% w to about 14% w molybdenum,
- (e) partially drying the product of step (d) to reduce loss on ignition to between about 55% and about 65%,
- (f) extruding the product of step (e), and
- (g) drying and calcining the product of step (f) at a temperature ranging from about 300.degree. C. to about 900.degree. C.
Parent Case Info
This is a division of application Ser. No. 100,661, filed Sept. 24, 1987, now U.S. Pat. No. 4,810,687.
US Referenced Citations (15)
Divisions (1)
|
Number |
Date |
Country |
Parent |
100661 |
Sep 1987 |
|