The present invention relates generally to methods of immobilizing protein catalysts onto solid surfaces. In another aspect, the invention relates to plastic supports bearing protein catalysts.
Protein catalysts, or enzymes, are useful in promoting reactions in various applications. For certain applications the enzyme must be immobilized on a suitable solid support. Immobilization may be accomplished by a variety of chemically-based approaches including adsorptive, ionic bonding, and covalent bonding techniques. Additionally, the catalyst may be entrapped in a gel or polymer matrix, stabilized in a micellar structure, incorporated into the substance of the matrix itself, or enclosed in a membrane using the so-called membrane-enclosed enzyme catalysis technique.
The immobilization procedures are, as a whole, difficult, expensive, and often only partially effective. For instance, one method requires soaking a polycarbonate membrane for 24 hours in a solution of poly-(L-lysine), rinsing, soaking the membrane in a buffered glutaraldehyde solution for 2 hours, washing, and finally soaking the membrane in a buffered glucose oxidase solution for 24 hours. This method relies on covalent bonding between the poly(L-lysine) layer and the polycarbonate membrane. This method is not effective unless the support medium and the poly(L-lysine) layer are capable of covalent bonding with each other. Another method immobilizes lipases by formation of enzyme-silicone polymer composites. This paper describes problems with binding to hydrophobic polymer surfaces, low catalyst densities in sol-gel entrapment methods, and limited application of crosslinked lipase preparations. To address these issues the paper describes adsorption of proteins onto poly(hydroxymethylsiloxane) [PHOMS], followed by reaction with silanol-terminated PDMS prepolymers, poly(diethylsilicate), and (3-aminopropylethoxysilane) crosslinker to form a solid silicone rubber with encapsulated lipase-PSOMS. Polysiloxanes are relatively expensive, however, and may not be a suitable support for many applications.
The goal in developing new methods of immobilizing enzymes is to enhance the ease, economy, and simplicity of achieving high enzymatic activity that persists for long periods of time at a defined location on a fixed surface or support. To achieve this goal it is desirable to have as high of a catalytic activity of an immobilized enzyme as possible and for the catalytic activity to be relatively stable. It would also be desirable to have a method of immobilizing an enzyme on a polymeric support that would be useful with many kinds of supports and enzymes.
A method of immobilizing a protein catalyst on a polymeric support has steps of (a) applying an adhesive, particularly a one-component adhesive in organic solution, to the polymeric support; (b) applying a layer of a globular protein over the layer of adhesive; (c) binding a crosslinking agent to the protein layer; and (d) binding the protein catalyst by reaction with the crosslinking agent.
In a further embodiment of the invention, a one-component, solvent-based adhesive is applied in the first step.
In still a further embodiment of the invention, the crosslinking agent has a plurality of groups reactive with active hydrogens, particularly hydrogens of amine groups. In a particularly preferred embodiment, the crosslinking agent is or includes a di-aldehyde, especially glutaraldehyde.
The immobilized protein has stable catalytic activity, for dry and moist storage and for ambient and refrigerated storage.
The invention further provides an article having an immobilized protein catalyst on a solid support prepared by the method of the invention.
Depending on the choice of protein catalyst, the immobilized protein catalyst may be used, for example, to enhance absorption of carbon dioxide into liquids, make renewable fuels from biomass, make bioplastics and “smart materials” such as biomaterials that undergo controlled transformations that can be used for sensing, actuating, and controlling chemical and physical functions, destroy contaminants in machining fluids, purify indoor air, or act as a biosensor for a given organic molecule. For instance, immobilized carbonic anhydrase can be used to hydrate carbon dioxide to carbonic acid for sequestering carbon dioxide.
Our invention takes advantage of advances in adhesive chemistry to modify an established technique to produce a simple, economical, four-step process for cost-effective enzyme immobilization.
“A” and “an” as used herein indicate “at least one” of the item is present; a plurality of such items may be present, when possible. “About” when applied to values indicates that the calculation or the measurement allows some slight imprecision in the value (with some approach to exactness in the value; approximately or reasonably close to the value; nearly). If, for some reason, the imprecision provided by “about” is not otherwise understood in the art with this ordinary meaning, then “about” as used herein indicates a possible variation of up to 5% in the value.
The present invention will become more fully understood from the detailed description and the accompanying drawings, wherein:
The following description of the preferred embodiment(s) is merely exemplary in nature and is in no way intended to limit the invention, its application, or uses.
A support, which may be selected from any useful material including polymeric, cardboard, glass, metal, and foam core materials, of a desired design or shape is used to support the protein catalyst. The support may be selected, for example, from any polymeric material appropriate for the conditions under which the catalyst will be used. In general, supports formed from polyethylene, polypropylene, polybutadiene, polyamide, polycarbonate, vinyl polymers, polypropylene glycol, polyesters such as poly(ethylene terephthalate), phenolic polymers, epoxy polymers, polyurethanes, and so on. Useful vinyl polymers may be homopolymers and copolymers of, for example, α,β-ethylenically unsaturated monocarboxylic acids containing 3 to 5 carbon atoms and α,β-ethylenically unsaturated dicarboxylic acids containing 4 to 6 carbon atoms, and derivatives of these such as esters and amides; vinyl esters, vinyl ethers, vinyl ketones, and aromatic or heterocyclic aliphatic vinyl compounds. Suitable examples of vinyl polymers include, without limitation, poly(methyl methacrylate), other acrylic polymers, poly(vinyl chloride), poly (vinyl acetate), styrene polymers and copolymers, and so on.
The support may have a shape adapted to the needs of a particular application for which the immobilized catalyst will be employed. For example, the supports can be discs, sheets, rods, cones, spheres, cylinders, membranes and so forth.
An adhesive is applied to the surface of the support. It is preferred to use a one-component, solvent-based adhesive. Such adhesives are known and readily available commercially. Such adhesives include PVC and acrylic adhesives such as described in “Adhesive Compositions,” Encyclopedia of Polymer Science and Technology (2d ed.) Vol. 1, pages 569-74, incorporated herein by reference and those described, for example, in Haraguchi et al., U.S. Pat. No. 5,280,061 and the documents mentioned therein, all of which are incorporated herein by reference. One suitable adhesive that is commercially available is 3M PhotoMount Spray Adhesive®, which readily adheres to different kinds of materials, including plastics such as polypropylene, and binds the globular protein layer thereto.
It is desirable for the adhesive to be diluted in solvent so that it is easier to apply a thin layer to the support surface. The adhesive may be diluted in an appropriate organic solvent, for example and without limitation hexane, heptane, toluene, xylene, methylene chloride, carbon tetrachloride, trichloromethane, Aromatic 100, tetrahydrofuran, acetone, 2-propanol, methanol, and acetronitrile. It is preferred to apply the adhesive by dip coating the support, although it is possible to apply the adhesive by other means, such as spraying, brushing, roll coating, and so on.
After applying the adhesive, it is preferred to evaporate any solvent in the adhesive layer. The drying step may be carried out at room temperature in air.
A globular protein layer is then applied onto the adhesive layer. The globular protein layer and the crosslinker are selected to provide appropriate interaction with the enzyme being immobilized. Globular proteins include albumins, globulins, histones, and protamines. It is particularly preferred to use an albumin, especially ovalbumin, which is derived from avian eggs, a readily available source.
The globular protein layer may be applied by immersing the support with adhesive layer into a buffered solution of the protein. The pH of the solution is preferably substantially neutral, although pH may differ somewhat from 7.0 depending on the globular protein selected. The solution may be diluted to apply a layer of appropriate thickness. A more dilute solution will deposit a thinner protein layer. The protein layer need only be thick enough so that the crosslinker is anchored to the support densely enough to achieve the desired surface concentration of enzyme. In general, a solution that is about 0.5% to about 5.0% is sufficiently concentrated. More concentrated solutions would also work, but would make a thicker layer of the globular protein on the support.
The support with adhesive layer may be dipped one or more times in the globular protein solution for a desired time, preferably from about 1 to about 5 seconds. The globular protein may be kept chilled, e.g. at 4° C., if needed to prevent denaturation and/or contamination with microbes. The deposited globular protein layer may then be allowed to dry.
A crosslinking agent is attached to the globular protein layer to provide a site for immobilizing the enzyme. The crosslinking agent has at least two groups, one group that can attach to the globular protein layer and a second group that can attach to the enzyme. In general, the globular protein layer and/or enzyme may be bound through reaction of an amine group, acid group, phenolic group, sufhydryl group, or imidazole group, so that the crosslinking agent may have functionality such as aldehyde groups, isocyanate groups, oxirane groups, thio groups, sulfhydryl groups, amine groups, and photoreactive crosslinkers. Known crosslinking agents include, without limitation, polyaldehydes such as glutaraldehyde; polyisocyanates such as 1,6-diisocyanatohexane (hexamethylene diisocyanate or HMDI), 1,4-butylene diisocyanate, lysine diisocyanate, 1,4-methylene bis-(cyclohexyl isocyanate), toluene diisocyanate (toluene diisocyanate or TDI), isophorone diisocyanate (IPDI), α,α,α′,α′-tetramethyl xylylene diisocyanate (TMXDI) and 4,4′-dibenzyl diisocyanate; bisdiazobenzidine; hexamethylene diisothicyanate; hexamethylene diamine; polyepoxides such as polyoxyethylene-bis(glycidyl ether); N,N′-ethylene bismaleimide; N,N′-polymethylene bisiodoacetamide; 4-azidobenzoic acid (3-sulfo-N-succinimidyl) ester sodium salt; 1,4-bis[3-(2-pyridyldithio)propionamido]butane; bis[2-(N-succinimidyl-oxycarbonyloxy)ethyl]sulfone; bis[2-(4-azidosalicylamido)ethyl]disulfide; dimethyl 3,3′-dithiopropionimidate dihydrochloride; ethylene glycol disuccinate di(N-succinimidyl) ester; and sebacic acid bis(N-succinimidyl)ester. The crosslinking agent is selected so that the bonding to the globular protein layer and the bonding of the protein catalyst both take place under conditions that avoid denaturing the protein catalyst.
The crosslinker may be applied by any known method. For example, the coated support may be immersed for an hour or two in a solution of the crosslinker in an aqueous buffer. The solution should be of an appropriate concentration to allow a layer of crosslinker to adhere to the globular protein surface. Again, the pH of the solution may be substantially neutral. The deposited crosslinker layer may then be rinsed with deionized water and allowed to dry.
Many different protein catalysts are known and commercially available. Among those that may be used are carbonic anhydrase (which catalyzes the hydration of carbon dioxide to carbonic acid), papain, alpha-amylase, ribonuclease, trypsin, alpha-chymotrypsin, aminoacylase, aldolase, alcohol dehydrogenase, glutamate dehydrogenase, glucose oxidase, tyrosinase, catalase, peroxidase, carboxypepsidase A, alkaline phosphatase, lysozyme, subtilisin, and others. A combination of protein catalysts may be used.
The protein catalyst may be applied from a solution of the protein catalyst in an aqueous buffer, e.g. a phosphate buffer. The conditions are appropriate to avoid denaturing the enzyme or protein layer. The solution may be chilled, for example to 4° C., to avoid denaturation and/or biological contamination. The time necessary to attain the desired catalytic activity for a given protein catalyst may be determined in a straightforward manner by measuring the catalytic activity at timed intervals.
The invention is further described in the following example. The example is merely illustrative and does not in any way limit the scope of the invention as described and claimed. All parts are parts by weight unless otherwise noted.
A polypropylene disk 0.25 inches in diameter, 0.0625 inches thick was dipped for several seconds in an adhesive solution prepared from 1 part by volume of 3M PhotoMount Spray Adhesive® diluted in 3 parts by volume toluene, then further diluted in 3 parts by volume hexane. The disk was removed from the adhesive and allowed to dry. The dried disk was then dipped in a freshly prepared mixture of about 1 part by volume ovalbumin and 10 parts by volume of 50 mM phosphate buffer, pH 7.0. The ovalbumin adhered readily to the adhesive layer. The disk was then air dried. Next, the disk was immersed for 2 hours in a solution held at 4° C. of glutaraldehyde, 1% by weight, in 50 mM phosphate buffer, pH 7.0. The disk was then washed three times with distilled water and air dried. Finally, the disk was incubated with carbonic anhydrase by immersing the disk in a 10 mg/ml solution of carbonic anhydrase in the 50 mM phosphate buffer for 2 hours at 4° C. The disk was then removed and rinsed with the phosphate buffer.
The immobilized protein has excellent stability. Carbonic anhydrase disks prepared in this way could be stored dry or moist, chilled or at room temperature with minimal loss of activity. Referring now to the figures,
The immobilized carbonic anhydrase can be used to hydrate carbon dioxide to carbonic acid for sequestering carbon dioxide. The catalytic support may be prepared by immersing a polymeric membrane, such as a polypropylene membrane, beads, fabrics, fibers, membranes, particulates, porous surfaces, rods, tubes, or supports of other shape in an adhesive solution prepared from 1 part by volume of 3M PhotoMount Spray Adhesive® diluted in 3 parts by volume toluene, then further diluted in 3 parts by volume hexane. The adhesive is dried, then dipped in a freshly prepared mixture of about 1 part ovalbumin and 10 parts of a phosphate buffer solution to add a layer of globular protein. The protein layer is then treated with a crosslinker such a glutaraldehyde, 1% by weight in phosphate buffer solution, and finally carbonic anhydrase is attached by the crosslinker from a solution of carbonic anhydrase in phosphate buffer. The support bearing the immobilized carbonic anhydrase may then be placed into an aqueous medium where it is exposed to carbon dioxide in order to facilitate hydration of the carbon dioxide to carbonic acid.