Patent Grant
7074727
The present invention relates generally to semiconductor fabrication processes and more particularly to a process for repairing degradation of dielectric properties of low-k organosilicate dielectric material.
As semiconductor devices are scaled down to smaller feature sizes, interconnect delay becomes a significant performance barrier for high-speed signal conduction. The use of dielectric materials with a lower dielectric constant (k) can significantly improve performance measures by reducing signal propagation time delay, cross talk, and power consumption in semiconductor devices having a multilevel interconnect architecture. The most-used dielectric material for semiconductor fabrication has been silicon oxide (SiO2), which has a dielectric constant in the range of k=3.9 to 4.5, depending on its method of formation. Dielectric materials with k less than 3.9 are classified as ‘low-k dielectrics’. Some low-k dielectrics are organosilicates formed by doping silicon oxide with carbon-containing compounds. One such low-k dielectric material is methylsilsesquioxane (MSQ), which is a polymer having an inorganic backbone of alternating silicon and oxygen atoms with methyl (CH3) groups attached to the silicon by a silicon-carbon (Si—C) bond. MSQ typically has a dielectric constant in the range k=2.6–2.8.
Well-known steps in the fabrication of a semiconductor device include forming a layer of dielectric material on a silicon wafer or on previous levels of the device, applying a layer of photoresist material to the surface of dielectric material, exposing areas of the photoresist layer to light through a pattern mask, dissolving the exposed areas of photoresist with a developer solution to reveal the underlying areas of dielectric material, etching the revealed areas of dielectric material, removing the remaining photoresist layer, and filling the etched dielectric material with metal.
The steps of etching the dielectric material and removing the photoresist layer may be performed with an O2-containing plasma, which can degrade the dielectric properties of the dielectric material through oxidation. This damage to the material is believed to occur when Si—C bonds are broken and hydrophilic hydroxyl (OH) groups replace the hydrophobic methyl groups in the MSQ. The polarity of the dielectric material is thus changed and the damaged dielectric more easily absorbs moisture, resulting in an increase of both leakage current and dielectric constant. Subsequent heating of the damaged dielectric material can release moisture, interfering with the process of filling the etched cavities with metal. Semiconductor devices fabricated with such damaged dielectric material exhibit reduced performance measures and increased fabrication defects compared to devices fabricated with undamaged dielectric material.
Degradation of the dielectric properties of MSQ through substitution of hydroxyl groups for methyl groups may occur in other processing steps as well, such as creating nanopores in the dielectric layer by forming it from a composite of MSQ and triblock copolymer, e.g., poly(ethylene oxide-b-propylene oxide-b-ethylene oxide), and calcinating the block polymer to generate pores. Another processing step, chemical-mechanical polishing, can also produce increased leakage current and dielectric constant in MSQ. The kinematic mechanical abrasion and a chemical reaction with polishing additives such as tetramethylammonium hydroxide can break the Si—C bonds, resulting in moisture uptake and dielectric degradation.
Experiments have shown that treating the damaged dielectric material with trimethylchlorosilane (TMCS) ((CH3)3Si—Cl) reduces the leakage current and dielectric constant of the material. This is thought to result from a reaction in which the TMCS replaces a hydrophilic hydroxyl group with hydrophobic trimethylsiloxane ((CH3)3SiO), causing a decrease in the moisture uptake of the treated dielectric. Treatment with hexamethyldisilazane (HMDS) ((CH3)3Si—NH—Si(CH3)3) has also been shown to reduce leakage current and dielectric constant. This is thought to result from a reaction in which two hydroxyl groups are replaced with trimethylsiloxane. These are relatively inefficient chemical replacement reactions, however, which require high pressures or long treatment times to achieve their results. Furthermore, while replacing the hydrophilic hydroxyl groups with hydrophobic methyl groups, these treatments have not been shown to restore the silicon-carbon bonds and, as a result, the polarity of the damaged dielectric material.
Alternatively, the damaged dielectric material can be treated with hydrocarbon, fluorocarbon, or organo-substituted silane gases (e.g., (CH3)xSiH(4-X), where x is 1 to 4). This treatment has been shown to reduce defects in metal fillings deposited on the treated dielectric material. However, the effect of this treatment on the dielectric properties of the damaged dielectric material has not been demonstrated.
In view of the foregoing disadvantages inherent in restoring degraded dielectric properties of low-k dielectric material, aspects of the present invention can be found in a process of treating the material with a series of reagents. Processes employing the present invention are more efficient and may require lower pressures and shorter treatment times than prior treatment processes.
More specifically, aspects of the invention can be found in a process for treating low-k organosilicate dielectric material including the steps of exposing the material to a halogenation reagent, an alkylation reagent, and a termination reagent. Further aspects of the invention can be found in performing steps of the method in the same chamber as a process that breaks at least one silicon-carbon bond in the dielectric material.
Other aspects of the invention can be found in the following process for fabricating an insulating layer on an integrated circuit structure. A layer of low-k organosilicate dielectric material is formed on the integrated circuit structure. A resist mask is formed on the dielectric material, the material is etched, and the resist mask is removed. The dielectric material is exposed to a halogenation reagent, an alkylation reagent, and a termination reagent.
Other aspects of the invention can be found in a semiconductor device with a methylsilsesquioxane dielectric that has had one or more of its methyl groups replaced by end group molecules. The chemical formula of the end group molecules is R1OR2, where R1 is an alkyl with a carbon chain of five or fewer carbon atoms (a C1–C5 lower alkyl) and R2 is either trimethylsilyl (Si(CH3)3) or a C1–C5 lower alkyl.
Further aspects of the invention are found in a treatment for low-k organosilicate dielectrics whose dielectric properties have been degraded by a previous step in the semiconductor fabrication process. Steps of the treatment include exposing the damaged dielectric to a halogenation reagent, an alkylation reagent, and a termination reagent.
The foregoing has outlined rather broadly the features and technical advantages of the present invention in order that the detailed description of the invention that follows may be better understood. Additional features and advantages of the invention will be described hereinafter which form the subject of the claims of the invention.
It should be appreciated by those skilled in the art that the conception and specific embodiment disclosed may readily be utilized as a basis for modifying or designing other structures or processes for carrying out the same purposes of the present invention. It should also be realized by those skilled in the art that such equivalent constructions do not depart from the spirit and scope of the invention as set forth in the appended claims.
For a more complete understanding of the present invention, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawing, in which like reference numbers indicate like features and wherein:
The making and using of the presently preferred embodiments are discussed in detail below. It should be appreciated, however, that the present invention provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative of specific ways to make and use the invention, and do not limit the scope of the invention.
The present invention will be described with respect to preferred embodiments in a specific context, namely an organosilicate low-k dielectric whose dielectric properties have been degraded through oxidation by exposure to O2 plasma. The invention may also be applied, however, to such dielectrics that have had silicon-carbon bonds broken by other steps in the semiconductor fabrication process.
With reference now to
A proposed reaction through which the organosilicate low-k dielectric material may be damaged by O2 plasma is illustrated in
The displacement of hydrophobic methyl groups by hydrophilic hydroxyl groups also promotes moisture uptake, as shown in
Further problems with the damaged dielectric material arise during subsequent processing steps, such as annealing, in which the material is heated.
The first step of a repair process embodying the present invention is the exposure of the degraded dielectric material to a halogenation reagent. One example of such a halogenation reaction is shown in
Thionyl chloride is only one of the halogenation reagents that may be used in this embodiment of the present invention. Other reagents that cause the hydroxyl group to be replaced with chlorine include PCl3, PClS, POCl3, and Cl2. Halogenation reagents that cause the hydroxyl group to be replaced with bromine include SOBr2, PBr3, PBr5, and Br2.
The reagents SOCl2, PCl3, PCl5, POCl3, SOBr2, PBr3 and PBr5 are used in liquid form. An inert gas, such as N2 or Ar2, at a pressure that can range from about 10 militorr to about 10 Torr, but that is preferably about 0.2 Torr, is used to carry the vapor from the liquid reagent into the reaction chamber. Heating the reservoir of liquid reagent will increase the vapor pressure of the reagent. The reagents Cl2 and Br2 are used in gaseous form, at a pressure that can range from about 10 militorr to about 10 Torr, but that is preferably about 0.2 Torr. The flow rate of the halogenation reagent into the chamber can range from about 5 standard cubic centimeters per minute (seem) to about 500 sccm, but is typically about 250 sccm. The halogenation step is performed at a temperature in the range between about 25° C. and about 300° C., but preferably at a temperature of about 150° C. In the flow rate, pressure and temperature ranges listed above, this step of the treatment typically takes about 5 minutes to replace all the hydroxyl groups in the damaged dielectric material with halogen atoms.
The second step of a repair process embodying the present invention is the exposure of the halogenated dielectric material to an alkylation reagent.
While ethylene is employed as the alkylation reagent in the embodiment of the invention illustrated in
The final step of a repair process embodying the present invention is the exposure of the second product of the repair process to a termination reagent, an embodiment of which is illustrated in
The termination reagent TMCS is shown in
The steps of a process embodying the present invention are preferably carried out in situ with the preceding step in the fabrication process that damages the dielectric material. This is because the damaged dielectric material, the halogenation reagents and the intermediate products of the halogenation reaction are moisture sensitive. By performing the processing in a cluster tool with multiple chambers, the environment can be controlled during and between processing steps in order to control exposure to moisture. A vacuum system can be used to carry away the gaseous byproducts of the reaction. Alternatively, however, the semiconductor wafer being treated can be transported from one processing site to another in a sealed chamber to prevent moisture uptake.
Processes embodying the present invention employ more efficient chemical replacement reactions than previous treatments for degraded organosilicate low-k dielectrics. However, one skilled in the chemical arts will be aware that supplying heat or energy to an endothermic reaction system can speed up the rate of the reaction. Energy generators such as hot plates, microwave generators, and light emission sources can be used to supply heat or energy to a chemical reaction. Thus, to further shorten the time required to perform a process according to the present invention, an energy generator can be placed in the reaction chamber where the process is performed.
In summary, a process according to the present invention operates using more efficient chemical replacement reactions to restore the dielectric properties of organosilicate low-k dielectric material that have been degraded by previous semiconductor fabrication processing steps. Such a treatment replaces the hydroxyl groups in the degraded dielectric material with end groups of the form R1OR2, wherein R1 is a C1–C5 lower alkyl and R2 is either trimethylsilyl (Si(CH3)3) or a C11–C5 lower alkyl. As a result of the treatment, it appears that Si—OH bonds in the damaged dielectric material are replaced with Si—C bonds, and the hydrophobic property of the material is restored to prevent moisture uptake.
Although the present invention and its advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the invention as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure of the present invention, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present invention. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4921321 | Weidman | May 1990 | A |
| 5468890 | Herzig et al. | Nov 1995 | A |
| 6346490 | Catabay et al. | Feb 2002 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20050010000 A1 | Jan 2005 | US |