Patent Application
20120135268
1. Technical Field
The exemplary disclosure generally relates to a process for joining a metal part and a ceramic part, especially to a process for joining a stainless steel part and a silicon nitride ceramic part, and a composite article made by the process.
2. Description of Related Art
It is important to be able join stainless steel parts and silicon nitride ceramic parts. However, due to distinct physical and chemical properties, it can be difficult to join stainless steel and silicon nitride ceramic using traditional bonding methods such as braze welding, fusion welding, solid diffusion bonding.
Therefore, there is room for improvement within the art.
Many aspects of the embodiments can be better understood with reference to the following drawings. The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the exemplary process for joining stainless steel part and silicon nitride ceramic part, and composite article made by the process. Moreover, in the drawings like reference numerals designate corresponding parts throughout the several views. Wherever possible, the same reference numbers are used throughout the drawings to refer to the same or like elements of an embodiment.
The process according to the present disclosure is generally implemented by a spark plasma sintering (SPS) device as illustrated in
Referring to
A ceramic part 20 made of silicon nitride ceramic, a metal part 30 made of stainless steel, and an intermediate member in provided. The intermediate member includes two foils, a molybdenum (Mo) foil 40 and an Fe foil 50. The intermediate member is used as a joining medium between the surfaces of the ceramic part 20 and the metal part 30. the Mo foil 40 has a thickness of about 0.2˜0.4 mm. the Fe foil 50 has a thickness of about 0.2 to about 0.4 mm.
A clamping mold 70 is used to hold the SiN ceramic part 20, the stainless steel part 30, the Mo foil 40 and the Fe foil 50. The clamping mold 70 includes a pressing board 72, a corresponding supporting board 74 and a receiving board 76. The receiving board 76 defines a cavity 762 running through the upper/bottom surface to receive the SiN ceramic part 20, the stainless steel part 30, the Mo foil 40 and the Fe foil 50. The pressing board 72 and the corresponding supporting board 74 extend towards the cavity 762 from opposing directions and can be moved relative to the cavity 762 by a driving system such as hydraulic pressure system. The SiN ceramic part 20, the Mo foil 40, the Fe foil 50 and the stainless steel part 30 are placed into the cavity 762 and clamped by the pressing board 72 and the corresponding supporting board 74. The Mo foil 40 and the Fe foil 50 are inserted between the SiN ceramic part 20 and the stainless steel part 30. The SiN foil 40 abuts against the SiN ceramic part 20, the Fe foil 50 abuts against the stainless steel part 30. The pressing board 72 and the corresponding supporting board 74 from two opposite sides, brings the surfaces of the parts to be joined into tight contact, for compressing the SiN ceramic part 20, the Mo foil 40, the Fe foil 50 and the stainless steel part 30.
A clamping mold 70 made of electro-conductive material, such as graphite, is provided as shown in
An hot press sintering device 100 including a chamber 101 is provided. The clamping mold 70 is placed into the chamber 101. The vacuum level inside the chamber 101 is set to about 10−3 Pa to about 9×10−3 Pa. Argon (Ar) is fed into the chamber 101 to maintain the chamber 101 pressure in a range of about 0.3-0.6 MPa. The pressing board 72 and the corresponding supporting board 74 press toward each other at about 5 Mpa to firmly clamp the SiN ceramic part 20 and the stainless steel part 30. Then, the chamber 101 is heated at a rate of about 1-20 degrees Celsius per minute (° C./min). When the temperature of the chamber 101 reaches to about 300° C., the clamping pressure applied by the boards 72, 74 steadily increases, until the temperature of the chamber 101 reaches to about 1000-1200° C., and the clamping pressure reaches to about 10-40 Mpa. The pressure and heat are maintained in their respective peak ranges for about 20-50 min, so that the Mo foil 40 and the Fe foil 50 will interact with each other, and the Mo foil 40 interacts with the SiN ceramic part 20, and the Fe foil 50 interacts with the stainless steel part 30. Accordingly, the SiN ceramic part 20 and the stainless steel part 30 are connected by the Mo foil 40 and the Fe foil 50 to form a composite article 10. The composite article 10 is removed after the chamber 101 is cooled.
Owing to the present process, a final, permanent joint, of great strength is obtained. The process requires a short hold time and a low vacuum level of the sintering chamber 13, thus saving significant time and energy.
Referring to
The composite article 10 manufactured by the present process includes the ceramic part 20, the metal part 30 and a multi-layered joining layer 80 connecting the ceramic part 20 to the metal part 30. The joining layer 80 is formed by placing the Mo 40 and the Fe foil 50 between the ceramic part 20 and the metal part 30, and then heating and pressing the ceramic part 20 and the metal part 30 as previously described. The various layers of the joining layer 80 result from differing reactions between the metal part 30, the Mo foil 40, the Fe foil 50, and the ceramic part 20.
In particular, the joining layer 80 includes:
a) a first transition layer 81: The first transition layer 81 mainly includes compounds comprised Mo element and C element. The compounds result from chemical reactions between adjacent portions of the ceramic part 20 and the Mo foil 40;
b) a Mo layer 82: The Mo layer 82 results from portions of the Mo foil 40 that do not react with either the ceramic part 20 or the Fe foil 50;
c) a second transition layer 83: The second transition layer 83 is located between the Mo layer 82 and the Fe layer 84. The second transition layer 83 mainly includes chemical compounds comprising Mo element and Fe element, and Mo with Fe solid solutions. The compounds and solutions result from chemical reactions between adjacent portions to the Mo foil 40 and Fe foil 50;
d) an Fe layer 84: The Fe layer 84 results from portions of the Fe foil 50 that do not react with either the Mo foil 40 or the metal part 30;
e) a third transition layer 85: The third transition layer 85 is located between the Fe layer 84 and the metal layer 30 and connects the Fe layer 84 and the ceramic layer 30. The third transition layer 85 mainly includes Fe solid solutions, The compounds and resulting from chemical reactions between adjacent portions of the Fe foil 50 and the metal part 30.
The thermal expansion rate of the joining layer 80 gradually changes from a value close to that of the ceramic part 20 (in the area of 81) to a value close to that of metal part 30 (in the area of 85). This results in a composite article 10 well suited to temperature changes due to the gradual, rather than abrupt, changes in its internal thermal expansion rates.
The joining part 80 of the composite article 100 has no cracks or apertures, and has a smooth surface. The metal/ceramic interface of the composite article 100 has a shear strength of about 80 to about 150 MPa. In addition, it has a tensile strength of about 60 MPa to about 100 MPa.
It is to be understood, however, that even through numerous characteristics and advantages of the exemplary disclosure have been set forth in the foregoing description, together with details of the system and function of the disclosure, the disclosure is illustrative only, and changes may be made in detail, especially in matters of shape, size, and arrangement of parts within the principles of the disclosure to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201010565691.1 | Nov 2010 | CN | national |
This application is related to co-pending U.S. Patent Applications (Attorney Docket No. US36183), entitled “PROCESS FOR JOINING STAINLESS STEEL PART AND TITANIUM CARBIDE CERAMIC PART AND COMPOSITE ARTICLES MADE BY SAME”. Such applications have the same assignee as the present application. The above-identified applications are incorporated herein by reference.