Patent Application
20090211700
1. Field of the Invention
The present invention relates to a process for laser welding resinous members, an apparatus for the same, and a laser-welded resinous product. More specifically, it relates to a process for integrally bonding transparent resinous members exhibiting transmissivity to laser beams and absorptive resinous members exhibiting absorptivity to laser beams by laser welding, an apparatus for the same, and the resulting laser-welded resinous products.
2. Description of the Related Art
Recently, from the viewpoint of weight saving and cost reduction, it has been carried out extensively to resinify component parts of various fields, such as automobile component parts, thereby making them into resinous molded products. Moreover, from the perspective of producing resinous molded products with high productivity, it is often the case to employ the following measures. A resinous molded product is molded as a plurality of the component parts separately in advance. Then, the resulting independent component parts are bonded with each other.
Laser welding processes have been utilized conventionally in order to bond a resin with another resin. For example, Japanese Unexamined Patent Publication (KOKAI) No. 11-348,132 discloses a laser welding process. In the conventional laser welding process, a transparent resinous member exhibiting transmissivity to a laser beam is overlapped on an absorptive resinous member exhibiting to absorptivity to the laser beam. Thereafter, the transparent resinous member is irradiated with the laser beam. Thus, the transparent resinous member and absorptive resinous member are heated to melt at the surfaces, thereby bonding them integrally.
In the conventional laser welding process, the laser beam is absorbed at the interface of the absorptive resinous member when it transmits through the transparent resinous member and reaches the interface. The laser beam absorbed at the interface is accumulated as energy. As a result, the interface of the absorptive resinous member is heated to melt, and simultaneously the interface of the transparent resinous member is heated to melt by the heat transfer from the interface of the absorptive resinous member. When the interface of the transparent resinous member and the interface of the absorptive resinous member are applied to each other under the circumstance, it is possible to bond them integrally.
However, it is not necessarily possible to obtain a uniform welded state by the above-described conventional laser welding process in certain cases. Let us consider the case of welding a resinous product, a box-shaped container, by the conventional laser welding process with reference to
Moreover,
The present invention has been developed in view of such circumstances. It is therefore an object of the present invention to provide a process for welding a transparent resinous member exhibiting transmissivity to a laser beam to an absorptive resinous member exhibiting absorptivity to the laser beam, process which can equalize the weld strength in the widthwise direction of the weld line at the curved parts thereof. It is a further object of the present invention to provide a welding apparatus for the same. It is a furthermore object of the present invention to provide a laser-welded resinous product in which the weld strength is equalized at the corners.
In order to solve the aforementioned problems, a process for laser welding resinous members according to a first aspect of the present invention comprises the steps of:
overlapping a transparent resinous member on an absorptive resinous material,
irradiating the transparent resinous member with the laser beam, thereby welding an interface between the first weld surface of the transparent resinous member and the second weld surface of the absorptive resinous member as a strip shape, the interface having a weld line welded as a strip shape and comprising linear parts neighboring with each other, a major-curvature-radius curved part intervening between the linear parts and a minor-curvature-radius curved part intervening between the linear parts, wherein energy averaging means averages the energy of the laser beam acting on a side of the major-curvature-radius curved part and the energy of the laser beam acting on a side of the minor-curvature-radius curved part in the second weld surface of the absorptive resinous member.
In the process according to a second aspect of the present invention, the energy averaging means makes a thickness of the major-curvature-radius curved part thinner than that of the minor-curvature-radius curved part in the transparent resinous member.
In the process according to a third aspect of the present invention, the energy averaging means lets the laser beam traverse along a scanning line shifted on a side of the major-curvature-radius curved part with respect to the center line of a strip-shaped width of the weld line.
In the process according to a fourth aspect of the present invention, the energy averaging means functions as an energy-density controlling means for controlling an energy density of the laser beam acting on the major-curvature-radius curved part so as to be relatively greater than an energy density of the laser beam acting on the linear parts or the minor-curvature-radius curved part.
In the process according to a fifth aspect of the present invention, the energy-density controlling means comprises a transparent or reflective liquid crystal device disposed in a path of the laser beam.
In the process according to a sixth aspect of the present invention, the energy-density controlling means comprises a reflector plate disposed in a path of the laser beam, and composed of a plurality of minute mirrors controlled electrically.
In the process according to a seventh aspect of the present invention, the energy-density controlling means a rotary disk disposed in a path of the laser beam, and having a plurality of apertures through which the laser beam passes.
In the process according to an eighth aspect of the present invention, the energy-density controlling means comprises a cylindrical lens disposed in a path of the laser beam, and having an eccentric focus.
In the process according to a ninth aspect of the present invention, the energy-density controlling means gives at least one stress selected from the group consisting of flexural stress, tensile stress and compression stress to an optical fiber for transmitting the laser beam.
In the process according to a tenth aspect of the present invention, the laser beam is emitted from at least one member selected from the group consisting of YAG lasers, laser diodes and fiber lasers.
In the process according to an eleventh aspect of the present invention, the energy-density controlling means comprises a plurality of small-sized oscillators, and a plurality of bundled optical fibers connected with the small-sized oscillators, and controls laser beams emitted from the bundled optical fibers by controlling the small-sized oscillators individually.
In the process according to a twelfth aspect of the present invention, the energy averaging means lets the laser beam exhibit a cross-sectional energy-density distribution which is axially symmetrical to a scanning direction of the laser beam at the linear parts of the weld line, and swings the laser beam about the axial line of the laser beam synchronously with the scanning with the laser beam at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line, thereby lowering an energy density at the minor-curvature-radius curved part than that at the major-curvature-radius curved part. Moreover, in the process according to a thirteenth aspect of the present invention, the energy averaging means lets the laser beam rotate about the axial line of the laser beam by rotating a cylindrical lens or a polarization plate at the linear parts of the weld line, and lets the laser beam swing about the axial line of the laser beam by swinging the cylindrical lens or the polarization plate at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line.
In the process according to a fourteenth aspect of the present invention, the energy averaging means equalizes an energy density of the laser beam at the linear parts of the weld line by rotating the laser beam about the axial line of the laser beam at a high revolving speed, and turns off the high-revolving-speed rotation of the laser beam temporarily at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line so as to swing the laser beam about the axial line of the laser beam synchronously with the scanning with the laser beam, thereby lowering an energy density at the minor-curvature-radius curved part than that at the major-curvature-radius curved part. Moreover, in the process according to a fifteenth aspect of the present invention, the energy averaging means lets the laser beam rotate about the axial line of the laser beam by rotating a cylindrical lens or a polarization plate at the linear parts of the weld line, and lets the laser beam swing about the axial line of the laser beam by swinging the cylindrical lens or the polarization plate at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line.
In the process according to a sixteenth aspect of the present invention, the energy-density controlling means emits a laser beam whose diameter is fully smaller than a strip-shaped width of the weld line.
In the process according to a seventeenth aspect of the present invention, the weld line is scanned with the small-diameter laser beam while vibrating the small-diameter laser beam in a widthwise direction of the weld line.
In the process according to an eighteenth aspect of the present invention, the weld line is scanned with the small-diameter laser beam a plurality of times by traversing the small-diameter laser beam spirally within the weld line.
In the process according to a nineteenth aspect of the present invention, the weld line is scanned with the small-diameter laser beam a plurality of times by traversing the smaller-diameter laser beam parallely within the weld line.
In the process according to a twentieth aspect of the present invention, the energy averaging means lets the laser beam scan the linear parts of the weld line only, thereby making the weld line free from the major-curvature-radius curved part and the minor-curvature-radius curved part.
A laser welding apparatus according to a twenty-first aspect of the present invention comprises:
means for irradiating a transparent resinous member overlapped on an absorptive resinous member with a laser beam,
whereby welding an interface between the first weld surface of the transparent resinous member and the second weld surface of the absorptive resinous member as a strip shape, the interface having a weld line welded as a strip shape and comprising linear parts neighboring with each other, a major-curvature-radius curved part intervening between the linear parts and a minor-curvature-radius curved part intervening between the linear parts; and
energy averaging means for averaging the energy of the laser beam acting on a side of the major-curvature-radius curved part and the energy of the laser beam acting on a side of the minor-curvature-radius curved part in the second weld surface of the absorptive resinous member.
A laser-welded resinous product according to a twenty-second aspect of the present invention comprises:
a transparent resinous member having a first predetermined shape, and comprising a part including a strip-shaped first weld surface, at least the part formed of a transparent resin allowing a laser beam to transmit therein;
an absorptive resinous member overlapped on the transparent resinous member, having a second predetermined shape, and comprising a part including a strip-shaped second weld surface to be welded to the first weld surface, at least the part formed of an absorptive resin which absorbs the laser beam;
the transparent resinous member and the absorptive resinous member being welded at an interface between the first weld surface of the transparent resinous member and the second weld surface of the absorptive resinous member as a strip shape by irradiating the transparent resinous member with the laser beam, the interface having a weld line welded as a strip shape and comprising linear parts neighboring with each other, a major-curvature-radius curved part intervening between the linear parts and a minor-curvature-radius curved part intervening between the linear parts; and
exhibiting weld strength on a side of the major-curvature-radius curved part substantially equal to weld strength on a side of the minor-curvature-radius curved part.
In the process according to the first aspect of the present invention, the weld line at which the transparent resinous member and the absorptive resinous member are welded as a strip shape comprises the linear parts neighboring with each other, the major-curvature-radius curved part intervening between the linear parts and the minor-curvature-radius curved part intervening between the linear parts; and the energy averaging means averages the energy of the laser beam acting on a side of the major-curvature-radius curved part and the energy of the laser beam acting on a side of the minor-curvature-radius curved part in the second weld surface of the absorptive resinous member. Therefore, it is possible to equalize the weld strength at the major-curvature-radius curved part of the weld line with the weld strength at the minor-curvature-radius curved part thereof.
As described above, the process according to the first aspect of the present invention can equalize the weld strength at the corners of the weld line, composed of the linear parts, the major-curvature-radius curved part and the minor-curvature-radius curved part, in the widthwise direction thereof when welding the overlapped transparent resinous member and absorptive resinous member by the laser beam. Therefore, it is possible to appropriately apply the process according to the first aspect of the invention to welding resinous products, such as cases for in-vehicle computers, hybrid inverter cases and lamp cases having corners, which are required to be highly airtight.
In the process according to the second aspect of the present invention, the energy averaging means makes a thickness of the major-curvature-radius curved part thinner that of the minor-curvature-radius curved part in the transparent resinous member. Accordingly, it is possible to irradiate the major-curvature-radius curved part as well with the laser beam of sufficient energy. Consequently, it is possible to equalize the weld strength at the major-curvature-radius curved part of the weld line with the weld strength at the minor-curvature-radius curved part thereof.
In the process according to the third aspect of the present invention, the energy averaging means lets the laser beam scan along a scanning line shifted on a side of the major-curvature-radius curved part with respect to the center line of a strip-shaped width of the weld line. Accordingly, it is possible to irradiate the major-curvature-radius curved part as well with the laser beam of sufficient energy. Consequently, it is possible to equalize the weld strength at the major-curvature-radius curved part of the weld line with the weld strength at the minor-curvature-radius curved part thereof.
In the process according to the fourth aspect of the present invention, the energy averaging means functions as an energy-density controlling means for controlling an energy density of the laser beam acting on the major-curvature-radius curved part so as to be relatively greater than an energy density of the laser beam acting on the linear parts or the minor-curvature-radius curved part. Accordingly, it is possible to cause an energy-density deviation in the cross section of the laser beam. That is, it is possible to place the higher-energy-density side of the laser beam on a side of the major-curvature-radius curved part of the weld line, and to place the lower-energy-density side of the laser beam on a side of the minor-curvature-radius curved part thereof. Therefore, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners.
In the process according to the fifth aspect of the present invention, the energy-density controlling means comprises a transparent or reflective liquid crystal device disposed in a path of the laser beam. Therefore, it is possible to cause an energy-density deviation in the cross section of the laser beam.
In the process according to the sixth aspect of the present invention, the energy-density controlling means comprises a reflector plate disposed in a path of the laser beam, and composed of a plurality of minute mirrors controlled electrically. Therefore, it is possible to cause an energy-density deviation in the cross section of the laser beam.
In the process according to the seventh aspect of the present invention, the energy-density controlling means comprises a rotary disk disposed in a path of the laser beam, and having a plurality of apertures through which the laser beam passes. Therefore, it is possible to cause an energy-density deviation in the cross section of the laser beam.
In the process according to the eighth aspect of the present invention, the energy-density controlling means comprises a cylindrical lens disposed in a path of the laser beam, and having an eccentric focus. Therefore, it is possible to cause an energy-density deviation in the cross section of the laser beam.
In the process according to the ninth aspect of the present invention, the energy-density controlling means gives at least one stress selected from the group consisting of flexural stress, tensile stress and compression stress to an optical fiber for transmitting the laser beam. Therefore, it is possible to cause an energy-density deviation in the cross section of the laser beam.
In the process according to the tenth aspect of the present invention, the laser beam is emitted from at least one member selected from the group consisting of YAG lasers, laser diodes and fiber lasers. Therefore, it is possible to apply desirable stress to the optical fiber.
In the process according to the eleventh aspect of the present invention, the energy-density controlling means comprises a plurality of small-sized oscillators, and a plurality of bundled optical fibers connected with the small-sized oscillators, and controls laser beams emitted from the bundled optical fibers by controlling the small-sized oscillators individually. Therefore, it is possible to cause an energy-density deviation in the cross section of the resulting bundled laser beams.
In the process according to the twelfth aspect of the present invention, the energy averaging means lets the laser beam exhibit a cross-sectional energy-density distribution (or deviation) which is axially symmetrical to a scanning direction of the laser beam at the linear parts of the weld line, and swings the laser beam about the axial line of the laser beam synchronously with the scanning with the laser beam at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line, thereby lowering an energy density at the minor-curvature-radius curved part than that at the major-curvature-radius curved part. Accordingly, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners. Moreover, in the process according to the thirteenth aspect of the present invention, the energy averaging means lets the laser beam rotate about the axial line of the laser beam by rotating a cylindrical lens or a polarization plate at the linear parts of the weld line, and lets the laser beam swing about the axial line of the laser beam by swinging the cylindrical lens or the polarization plate at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line. Consequently, it is possible to rotate the laser beam about the axial line of the laser beam synchronously with the rotation of the cylindrical lens or polarization plate at the linear parts of the weld line, and to swing the laser beam about the axial line of the laser beam synchronously with the swing of the cylindrical lens or polarization plate at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line.
In the process according to the fourteenth aspect of the present invention, the energy averaging means equalizes an energy density of the laser beam at the linear parts of the weld line by rotating the laser beam about the axial line of the laser beam at a high revolving speed, and turns off the high-revolving-speed rotation of the laser beam temporarily at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line so as to swing the laser beam about the axial line of the laser beam synchronously with the scanning with the laser beam, thereby lowering an energy density at the minor-curvature-radius curved part than that at the major-curvature-radius curved part. Accordingly, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners. Moreover, in the process according to the fifteenth aspect of the present invention, the energy averaging means lets the laser beam rotate about the axial line of the laser beam by rotating a cylindrical lens or a polarization plate at the linear parts of the weld line, and lets the laser beam swing about the axial line of the laser beam by swinging the cylindrical lens or the polarization plate at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line. Consequently, it is possible to rotate the laser beam about the axial line of the laser beam synchronously with the rotation of the cylindrical lens or polarization plate at the linear parts of the weld line, and to swing the laser beam about the axial line of the laser beam synchronously with the swing of the cylindrical lens or polarization plate at the major-curvature-radius curved part and minor-curvature-radius curved part of the weld line.
In the process according to the sixteenth aspect of the present invention, the energy averaging means emits a laser beam whose diameter is fully smaller than a strip-shaped width of the weld line. Therefore, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners.
In the process according to the seventeenth aspect of the present invention, the weld line is scanned with the small-diameter laser beam while vibrating the small-diameter laser beam in a widthwise direction of the weld line. Therefore, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners.
In the process according to the eighteenth aspect of the present invention, the weld line is scanned with the small-diameter laser beam a plurality of times by traversing the small-diameter laser beam spirally within the weld line. Therefore, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners.
In the process according to the nineteenth aspect of the present invention, the weld line is scanned with the small-diameter laser beam a plurality of times by traversing the smaller-diameter laser beam parallely within the weld line. Therefore, it is possible to equalize the weld strength in the widthwise direction of the weld line at the corners.
In the process according to the twentieth aspect of the present invention, the energy averaging means lets the laser beam scan the linear parts of the weld line only, thereby making the weld line free from the major-curvature-radius curved part and the minor-curvature-radius curved part. Therefore, it is possible to equalize the weld strength at all locations in the weld line.
In the laser-welding apparatus according to the twenty-first aspect of the present invention, the irradiating means laser welds the transparent resinous member and the absorptive resinous member as a strip shape so that the weld line comprises the linear parts neighboring with each other, the major-curvature-radius curved part intervening between the linear parts and the minor-curvature-radius curved part intervening between the linear parts; and the energy averaging means averages the energy of the laser beam acting on a side of the major-curvature-radius curved part and the energy of the laser beam acting on a side of the minor-curvature-radius curved part in the second weld surface of the absorptive resinous member. Therefore, it is possible to equalize the weld strength at the major-curvature-radius curved part of the weld line with the weld strength at the minor-curvature-radius curved part thereof.
In the production of the laser-welded resinous product according to the twenty-second aspect of the present invention, the energy of the laser beam acting on the major-curvature-radius curved part and the energy of the laser beam acting on the minor-curvature-radius curved part are averaged in the second weld surface of the absorptive resinous member by the energy averaging means according to the present laser welding process or laser welding apparatus. Therefore, the laser-weld resinous product is provided with the major-curvature-radius curved part whose weld strength is equalized with that of the minor-curvature-radius curved part substantially.
A more complete appreciation of the present invention and many of its advantages will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings and detailed specification, all of which forms a part of the disclosure.
Having generally described the present invention, a further understanding can be obtained by reference to the specific preferred embodiments which are provided herein for the purpose of illustration only and not intended to limit the scope of the appended claims.
A process according to the present invention is for laser welding resinous members, and comprises the steps of:
overlapping a transparent resinous member on an absorptive resinous material,
irradiating the transparent resinous member with the laser beam, thereby welding an interface between the first weld surface of the transparent resinous member and the second weld surface of the absorptive resinous member as a strip shape, the interface having a weld line welded as a strip shape and comprising linear parts neighboring with each other, a major-curvature-radius curved part intervening between the linear parts and a minor-curvature-radius curved part intervening between the linear parts, wherein energy averaging means averages the energy of the laser beam acting on a side of the major-curvature-radius curved part and the energy of the laser beam acting on a side of the minor-curvature-radius curved part in the second weld surface of the absorptive resinous member.
In the present laser-welding process, it is possible to name the following as the means for averaging the energy of the laser beam:
(1) controlling the thickness of the transparent resinous member;
(2) controlling the locus of scanning with the laser beam;
(3) varying the way of scanning the linear parts of the weld line with that of scanning the curved parts thereof by controlling the energy density in the cross section of the laser beam;
(4) irradiating the strip-shaped weld line with a small-diameter laser beam so as to mark it out; and
(5) making the weld line of linear parts only.
These means will be hereinafter described in detail with reference to the drawings.
In the present laser welding process, a transparent resinous member in which a laser beam transmits is overlapped on an absorptive resinous member which absorbs the laser beam; and the transparent resinous member is irradiated with the laser beam to melt the surface of the absorptive resinous member by generating heat, thereby welding the transparent resinous member and the absorptive resinous member together. Therefore, the absorptive resinous member absorbs most of the energy of the laser beam, but the transparent resinous member absorbs a part thereof as well. The absorption not only depends on the type of resins making the transparent resinous member and absorptive resinous member, but also on the laser-beam transmission length in the transparent resinous member, that is, the thickness of the transparent resinous member. The above-described disadvantageous phenomenon, the energy of the laser beam being less at the major-curvature-radius curved part of a weld line than at the minor-curvature-radius curved part thereof, occurs when the thickness of the transparent resinous member is constant (i.e., the energy of the laser beam which transmits through the transparent resinous member and reaches the absorptive resinous member is constant). Accordingly, as illustrated in
The thickness t1 on the major-curvature-radius side of the transparent resinous member 3, and the thickness t2 on the minor-curvature-radius side thereof will be hereinafter calculated. Note that the thickness t1 and thickness t2 allow to equalize the molten state on the major-curvature-radius side in the interface of the absorptive resinous member 4 with that on the minor-curvature-radius side therein.
A
T
=K×{exp−1(αt)}×A (a)
Therefore, “AT1” an energy density of the laser beam which transmits through a thickness “t1” can be expressed by the following equation (b).
A
T1
=K×{exp−1(αt1)}×A (b)
Likewise, “AT2,” an energy density of the laser beam which transmits through a thickness “t2” can be expressed by the following equation (c).
A
T2
=K×{exp−1(αt2)}×A (c)
Moreover, “T,” a time (sec) required for the laser beam to travel along the curved part of the weld can be expressed by the following equation (d). Accordingly, “ΔE,” an energy (J/mm2) acquired by a minute segment of the curved part of the weld line along the locus of the center of the laser beam can be expressed by the following equation (e).
T={(2πR/4)/i V}=πR/2V (d)
ΔE=AT×T=K×{exp−1(αt)}×A×(1/V) (e)
Similarly, “ΔE1,” an energy (J/mm2) acquired by a minute segment of the major-curvature-radius curved part of the weld line, and “ΔE2,” an energy (J/mm2) acquired by a minute segment of the minor-curvature-radius curved part thereof can be expressed by the following equations (f) and (g), respectively.
ΔE1=K×{exp−1(αt1)}×A×[R/{R1+(d/2)})×(1/V1) (f)
ΔE2=K×{exp−1(αt2)}×A×[R1/{R2−(d/2)}]×(1/V2) (g)
In order to establish an equally molten state on the major-curvature-radius curved part and on the minor-curvature-radius curved part, the energy acquired by a minute segment of the major-curvature-radius curved part of the weld line can be equal to the energy acquired by a minute segment of the minor-curvature-radius curved part thereof. Accordingly, the “t1′ and “t2” can be determined so that “ΔE1”=ΔE2.”
When scanning a weld line 2 with a laser beam 1 having such an energy-intensity distribution so as to coincide the center of the laser beam 1 with the widthwise center of the weld line 2 as illustrated in
(3)-1 Controlling Energy Density in Cross Section of Laser Beam
As described above, the intensity of a laser beam is not uniform in the cross section of the laser beam. However, the energy-intensity distribution of a laser beam is usually symmetric with respect to the axial line of the laser beam. However, when the energy-intensity distribution of a laser beam is made asymmetric with respect to the axial line of the laser beam in the cross section of the laser beam, and when the energy density of the laser beam is controlled in the cross section of the laser beam so that the energy density is made relatively larger at the major-curvature-radius curved part of a weld line than that at the linear parts or minor-curvature-radius curved part thereof, it is possible to equalize the weld strength at the major-curvature-radius curved part with that at the minor-diameter-curvature curved part thereof.
As for a method of controlling the energy density of a laser beam, it is possible to dispose a liquid crystal device or reflector mirror in a path of the laser beam.
Moreover, when using the laser beam 1 by reflecting it as shown in
The above-described liquid crystal devices and rotary disk can be disposed in a part of the laser-beam path. For instance, it is possible to dispose them between an oscillator and a beam expander, or between a beam expander and a galvano-mirror.
As for another method of controlling the energy density of a laser beam, it is possible to use a cylindrical lens which makes the after-control energy-density distribution of the laser beam asymmetric as depicted with a contour map shown in
In the case of YAG lasers or semiconductor lasers which use optical fibers for the transmission system, flexural stress, partial compression stress or tensile stress is given to the optical fibers which connect laser-emitting media with a collimator lens, thereby varying the energy-density distribution of laser beams transmitting in the optical fibers. Thus, it is possible to control the energy-density distribution of emitting laser beams.
It is preferable to use a large number of oscillators, such as light-emitting diodes, which are extremely small and produce laser light with a lesser power, as means for controlling the energy density of a laser beam. For example, in an apparatus which transmits a laser beam by bundling a plurality of fine optical fibers connected with such small-sized oscillators, it is possible to form an energy-density distribution in the bundled laser beams by controlling the output of the individual small-sized oscillators in response to the shape of the curved part of a weld line.
(3)-2 Scanning with Laser Beam Exhibiting Energy-Density Distribution
So far, methods for forming a deviation in the energy-density distribution in the cross section of a laser beam have been described. When welding the curved parts of a weld line with a laser beam exhibiting such an energy-density distribution, it is advisable to scan a weld line with the laser beam in the following manner.
At the linear parts of the weld line, the weld line is scanned with the laser beam so that the energy-density distribution of the laser beam is axially symmetric with respect to the travelling direction of the laser beam. At the curved parts of the weld line, the laser beam is swung synchronously with the scanning of the weld line so that the energy density of the laser beam is always the lowest at the minor-curvature-radius curved part of the weld line.
For example, let us consider the case that the energy density of a laser beam is distributed as illustrated in
In addition to the method which uses a liquid crystal device as the energy-density controlling means, it is possible to suitably apply the scanning with such a laser beam to the method which uses a rotary disk, and to the method which gives stress to an optical fiber.
Moreover, when using a laser beam exhibiting a deviated energy-density distribution, it is preferable as well to rotate the laser beam at a high revolving speed so as to equalize the energy-density distribution at the linear parts of a weld line; and to swing the laser beam about the axial line of the laser beam synchronously with the scanning of the curved parts of the weld line so as to always irradiate the major-curvature-radius curved part with a higher energy-density side of the laser beam as described above.
When the liquid crystal device shown in
Heretofore, the methods of welding the transparent resinous material to the absorptive resinous member by irradiating the weld line with a laser beam has been described, in methods which the weld line is irradiated with a laser beam whose diameter is equal to the width of the weld line. However, the following method is available in order to equalize the laser-beam energy density at the major-curvature-radius curved part of the weld line with the laser-beam energy density at the minor-curvature-radius curved part thereof. Specifically, the transparent resinous member can be welded to the absorptive resinous member uniformly over the entire width of the weld line by scanning the weld line with a laser beam whose spot diameter is reduced fully smaller than the width of the weld line.
So far, welding processes for welded resinous products whose weld line comprises linear parts and curved parts have been described in detail. However, depending on jigs and the shape of resinous members to be welded, a weld line can be free from curved parts, and can be made of linear parts only.
The present laser welding apparatus comprises:
means for irradiating a transparent resinous member overlapped on an absorptive resinous member with a laser beam,
whereby welding an interface between the first weld surface of the transparent resinous member and the second weld surface of the absorptive resinous member as a strip shape, the interface having a weld line welded as a strip shape and comprising linear parts neighboring with each other, a major-curvature-radius curved part intervening between the linear parts and a minor-curvature-radius curved part intervening between the linear parts; and
energy averaging means for averaging the energy of the laser beam acting on a side of the major-curvature-radius curved part and the energy of the laser beam acting on a side of the minor-curvature-radius curved part in the second weld surface of the absorptive resinous member.
In the present laser welding apparatus, the laser beam is not limited in particular. It is possible to use laser beams which have been used extensively for cutting or welding metals, or for photochemical reactions. For example, it is possible to use laser beams emitted from YAG lasers, semiconductor lasers, solid-state lasers, or gas lasers whose representative is carbon dioxide lasers.
Moreover, it is advisable to combine the present laser welding apparatus with industrial robots. With such a combination, it is possible to carry out such a control that the linear parts and curved parts are scanned while giving them an individually required energy only.
The present laser-welded resinous product comprises:
a transparent resinous member having a first predetermined shape, and comprising a part including a strip-shaped first weld surface, at least the part formed of a transparent resin allowing a laser beam to transmit therein;
an absorptive resinous member overlapped on the transparent resinous member, having a second predetermined shape, and comprising a part including a strip-shaped second weld surface to be welded to the first weld surface, at least the part formed of an absorptive resin which absorbs the laser beam;
exhibiting weld strength on a side of the major-curvature-radius curved part substantially equal to weld strength on a side of the minor-curvature-radius curved part.
In the present laser-welded resinous product, the resinous material for the transparent resinous member is not limited in particular as far as it exhibits thermoplasticity and allows laser beams, the heat source, to transmit therein by predetermined transmissivity or more. For instance, it is possible to name polyamides (PA) such as nylon 6 (PA6) and nylon 66 (PA66), polyethylene (PE), polypropylene (PP), stylene-acrylonitrile copolyrners, polyethylene terephthalate (PET), polystyrene (PS), acrylonitrile-butadiene-styrene (ABS), polymethyl methacrylate (PMMA), polycarbonate (PC) and polybutylene terephthalate (PBT). Note that these resinous materials can be colored to use, if necessary.
Moreover, the resinous material for the absorptive resinous member is not limited in particular as far as it exhibits thermoplasticity, and does not allow laser beams, the heat source, to transmit therein but can absorb it. For example, it is possible to name those admixtures of polyamides (PA) such as nylon 6 (PA6) and nylon 66 (PA66), polyethylene (PE), polypropylene (PP), stylene-acrylonitrile copolymers, polyethylene terephthalate (PET), polystyrene (PS), acrylonitrile-butadiene-styrene (ABS), polymethyl methacrylate (PMMA), polycarbonate (PC), polybutylene terephthalate (PBT) and polyphenylene sulfide (PPS) with carbon black or an ordinary coloring agent such as dyes and pigments. In addition, the carbon black admixed with the resinous materials as a laser-energy adsorbent can desirably be admixed in an amount of more than 0.1% by weight with respect to the resinous materials. When the admixing amount of the carbon black is 0.1% by weight or less with respect to the resinous materials, the resulting admixtures cannot fully adsorb the energy of laser beams. On the other hand, when the carbon black is admixed in an amount of more than 2% by weight with respect to the resinous materials, it is not preferable because such an admixing amount results in blow holes or cavities. Note that the admixing amount can further preferably fall in a range of from 0.2 to 1% by weight with respect to the resinous materials.
The present laser-welded resinous product is produced by welding the transparent resinous member and absorptive resinous member, which are molded into a predetermined shape from the aforementioned resinous materials, with a laser beam, and the weld strength is uniform at the curved parts of the weld line. Hence, it can make welded products with high airtightness.
The present invention has been detailed so far with reference to the preferred embodiments. However, the present invention is not limited to such preferred embodiments at all. It is needless to say that the present invention can be performed in various modes, provided that they do not deviate from the subject of the present invention.
Having now fully described the present invention, it will be apparent to one of ordinary skill in the art that many changes and modifications can be made thereto without departing from the spirit or scope of the present invention as set forth herein including the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-166478 | Nov 2003 | JP | national |
This is a division of application Ser. No. 10/862,436, filed Jun. 8, 2004 which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10862436 | Jun 2004 | US |
| Child | 12379301 | US |