Claims
- 1. A process for making uniformly sized polymer particles having a selected final particle size within the range of 1-50 .mu.m which comprises the steps of
- a) combining a free-radical-polymerizable, water-insoluble monomer or mixture of such monomers with an aqueous dispersion of seed polymer particles, at a rate such that an amount of monomer or mixture of monomers equal to the total initial weight of the seed polymer particles is combined with the dispersion over a period of from about 45 to about 120 minutes, in the presence of a dispersion stabilizer and an oil-soluble, free-radical polymerization initiator at a temperature at least as high as that at which the initiator is activated, until sufficient monomer or mixture of monomers has been combined to grow the particles to a selected intermediate size,
- b) maintaining the temperature of the combined monomer and particles at least as high as that at which the initiator is activated, until sufficient monomer or mixture of monomers has been combined to grow the particles to a selected size, and
- c) continuing to maintain the temperature of the combined monomer and particles at least as high as that at which the initiator is activated until all the monomer is polymerized,
- these steps being repeated until the selected intermediate size is equal to the selected final particle size.
- 2. The process of claim 1 wherein the rate at which the monomer or mixture of monomers and the dispersion are combined is such that the amount of monomer or mixture of monomers equal to the total initial weight of the seed polymer particles is combined with the dispersion over a period of from about 60 to about 90 minutes.
- 3. The process of claim 1 wherein the rate of addition of the monomer or mixture of monomers is such that the free monomer or mixture of monomers present does not exceed about 10%, by weight, of the instantaneous polymerparticle weight.
- 4. The process of claim 1 wherein the selected intermediate size is from about 1.1 to about 10 times the initial volume of the seed polymer particle.
- 5. The process of claim 1 wherein the selected intermediate size is from about 1.5 to about 7 times the initial volume of the seed polymer particle.
- 6. The process of claim 1 wherein the selected intermediate size is from about 2 to about 5 times the initial volume of the seed polymer particle.
- 7. The process of claim 1 wherein the seed polymer particles are emulsionpolymerized particles having an initial diameter of from about 0.01 to about 2 .mu.m.
- 8. The process of claim 1 wherein the seed polymer particles are emulsionpolymerized particles having an initial diameter of from about 0.05 to about 0.5 .mu.m.
- 9. The process of claim 1 wherein the seed polymer particles are particles produced by applying steps a) through c) to emulsion-polymerized particles one or more times.
- 10. The process of claim 1 wherein the stabilizing agent is selected from anionic surfactants and nonionic surfactants.
- 11. The process of claim 10 wherein the stabilizing agent additionally includes a water-soluble polymer.
- 12. The process of claim 1 wherein the initiator has a one-hour half-life temperature of from about 60.degree. to about 100.degree. C.
- 13. The process of claim 12 wherein the initiator is a peroxide initiator.
- 14. The process of claim 12 wherein the initiator is an azo initiator.
- 15. The process of claim 13 wherein the initiator is benzoyl peroxide.
- 16. The process of claim 1 wherein the monomer or mixture of monomers is one or more vinylaromatic monomers.
- 17. The process of claim 16 wherein the monomer is styrene.
- 18. The process of claim 16 wherein the monomer or mixture of monomers includes a crosslinking monomer.
- 19. The process of claim 1 wherein the monomer or mixture of monomers is combined with the polymer particles in the presence of a porogen.
- 20. The process of claim 19 wherein the porogen is toluene.
- 21. The process of claim 19 wherein the porogen is xylene.
- 22. The process of claim 19 wherein the porogen is methyl isobutyl carbinol.
Parent Case Info
This is a continuation-in-part of U.S. patent application Ser. No. 497,377 filed Mar. 22, 1990, now abandoned. This invention relates to a polymerization process, and more particularly to a process for polymerizing water-insoluble monomers in the presence of pre-formed, uniformly sized polymer particles.
US Referenced Citations (14)
Foreign Referenced Citations (1)
Number |
Date |
Country |
0190886 |
Aug 1986 |
EPX |
Non-Patent Literature Citations (4)
Entry |
Almog et al., "Effect of Initiator on the Molecular Weight Distribution in Dispersion Poly'n of Styrene", J. Polym. Sci. (Chem.) 18, 1 (1980). |
Almog et al., "Studies of Particle-Size Distribution . . . of Stabilizers in Dispersion Polymerization", J. Polym Sci. (Chem.) 20, 417 (1982). |
Almog et al, "Dispersion Polymerization of Styrene: Effect of Surfactant", J. Polym. Sci. (Chem.) 19, 115 (1981). |
Almog et al., "Monodisperse Polymeric Spheres in the Micron Size Range by a Single-Step Process", Br. Polym. J. Dec. 131 (1982). |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
497377 |
Mar 1990 |
|