Claims
- 1. A process for forming a fine diameter elongate ceramic body, comprising:
- forming a thermoplastic molding composition comprising from about 30 to 60 volume percent of a ceramic powder and from about 40 to 70 volume percent of a binder comprising about 20 to 50 weight percent of an organic acid having a melting point of from about 44.degree. C. to about 88.degree. C. and containing from 12 to 26 carbon atoms per molecule, and about 50 to 80 percent of an isobutylene polymer having an average molecular weight between about 8,700 and 135,000, the ceramic powder being homogeneously dispersed in the thermoplastic binder to form the thermoplastic ceramic molding composition;
- extruding the molding composition at a temperature between about 70.degree. C. to 150.degree. C. to form an elongate ceramic body;
- drawing the elongate ceramic body to a uniform elongation;
- relaxation annealing the drawn body to restore former plasticity; and
- repeating the drawing step to form the fine diameter elongate ceramic body.
- 2. The process of claim 1 before the step of decomposing further comprising the step of supporting the elongate ceramic body.
- 3. A process for forming a fine diameter elongate ceramic body suitable for densifying into a polycrystalline ceramic body having a porosity of less than about 20 percent by volume of the polycrystalline body, comprising:
- forming a thermoplastic molding composition comprising from about 30 to 60 volume percent of a ceramic powder and from about 40 to 70 volume percent of a binder comprising about 20 to 50 weight percent of an organic acid having a melting point of from about 44.degree. C. to about 88.degree. C. and containing from 12 to 26 carbon atoms per molecule, and about 50 to 80 percent of an isobutylene polymer having an average molecular weight between about 8,700 and 135,000, the ceramic powder being homogeneously dispersed in the thermoplastic binder to form the thermoplastic ceramic molding composition;
- extruding the molding composition at a temperature between about 70.degree. C. to 150.degree. C. to form an elongate ceramic body;
- drawing the elongate ceramic body to a uniform elongation;
- relaxation annealing the drawn body to restore former plasticity; and
- repeating the drawing step to form the fine diameter body; and
- decomposing the binder by heating the fine diameter body at a rate of heating that does not produce defects in the fine diameter body and heating up to a temperature that substantially removes the binder, leaving no amount therein that would have a significantly deleterious effect on the body.
Parent Case Info
This application is a Continuation of application Ser. No. 07/414,229, filed Sept. 29, 1989, and now abandoned.
US Referenced Citations (12)
Foreign Referenced Citations (2)
Number |
Date |
Country |
180957 |
Feb 1984 |
JPX |
966945 |
Aug 1964 |
GBX |
Non-Patent Literature Citations (1)
Entry |
"Vistanex.RTM. Polyisobutylene Properties and Applications", Sales brochure Exxon Chemicals, copyright 1974. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
414229 |
Sep 1989 |
|