Process for making foamed, sulfur-cured polymer blend compositions

Abstract

A blend of an E/X/Y copolymer, where E is ethylene, X is a vinyl ester, and Y is carbon monoxide or sulfur dioxide, with a polymer of vinyl halide or vinylidene halide is foamed and cured by dispersing in the blend a blowing agent and sulfur or a sulfur-releasing agent and heating the blend containing those additives at 100.degree.-180.degree. C. for a sufficient time to produce curing and foaming. This process can be run either continuously or batchwise in conventional equipment under conventional conditions in the presence of air. Plasticizers and other materials which often interfere with peroxide cures can be present in the process of this invention. The foamed and cured products have excellent physical properties and ozone resistance.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a process for foaming and sulfur-curing blends of an ethylene/vinyl ester/carbon monoxide or ethylene/vinyl ester/sulfur dioxide copolymer with a polyvinyl or polyvinylidene halide, such as, for example, polyvinyl chloride or polyvinylidene chloride.

2. Discussion of Related Art

It is known to foam and cure polymers and polymer blends such as, for example, ethylene/vinyl acetate/carbon monoxide terpolymers or blends of such terpolymers with polyvinyl chloride; see, U.S. Pat. Nos. 4,370,423 and 4,391,923, both to Rys-Sikora. Curing of the foamable polymer compositions of those patents is accomplished by means of free radicals. Those compositions, therefore, contain free radical generators, such as peroxides, peresters, or azides.

It also is known to foam and sulfur-cure diene elastomers such as, for example, natural rubber, SBR, and similar materials. Foams made by such processes are readily available commercially.

Further, it is known to sulfur-cure ethylene/vinyl acetate/carbon monoxide (E/VA/CO) terpolymers, as described in U.S. Pat. No. 4,172,939 to Hoh.

Foaming and curing polymer blends in the manner described in the above-cited Rys-Sikora U.S. Pat. No. 4,391,923 has certain shortcomings. Firstly, free radicals are sensitive to, and are destroyed by, oxygen. As a result, foaming and curing cannot be carried out in the presence of air, for example, in an oven, but normally would be carried out by compression molding, in the absence of air. This, in turn, makes it impossible to produce cured foams by a continuous process, where the composition is at the same time foamed and cured in an oven or a heat tunnel. A second drawback of the free-radical cures is that free radicals are easily consumed by various conventional compounding ingredients, such as, for example, antioxidants, certain extending oils, and plasticizers, and thus quickly become depleted, leaving the composition uncured or only partially cured. Such conventional compounding ingredients are, therefore, often omitted from those compositions.

It is, therefore, desirable to be able to produce foams of such polymer blends by a process which would not suffer from those limitations.

SUMMARY OF THE INVENTION

According to the present invention, there is provided a process for producing, a foamed, cured composition comprising a polymer blend of

(1) 5 to 95 parts of a copolymer (E/X/Y, wherein E is ethylene; X is a vinyl ester; and Y is carbon monoxide or sulfur dioxide; and (2) 95 to 5 parts of a polymer of a vinyl halide or vinylidene halide, the total amount of polymers (1) plus (2) being 100 parts; said process comprising: (A) uniformly dispersing in said polymer blend an effective amount of a blowing agent and at least one curing agent selected from (a) about 0.2 to 5 parts of sulfur and (b) about 0.2 to 15 parts of an agent capable of releasing elemental sulfur under the cure conditions; and (B) heating said blend containing the blowing agent and the curing agent at a temperature of about 100.degree.-180.degree. C., at which both foaming and curing take place, for a sufficient time to obtain substantially complete foaming and curing.

There also is provided a foamed and cured composition produced by the above process.

DETAILED DESCRIPTION OF THE INVENTION

The E/X/Y copolymers used in the present invention either are available commercially or can be made according to published information. The vinyl ester comonomer X can be, for example, vinyl acetate, vinyl propionate, vinyl butyrate etc., but the most commonplace comonomer, vinyl acetate, is preferred. An ethylene/vinyl acetate/carbon monoxide terpolymer is available from the assignee of this invention under the trademark Elvaloy.RTM.. The polymer can be made according to the procedures described in U.S. Pat. No. 3,780,140 to Hammer and U.S. Pat. No. 2,495,286 to Brubaker. Other copolymers, in which X is another vinyl ester, can be prepared in the same manner. Sulfur dioxide-containing copolymers can be made by the process of U.S. Pat. No. 3,684,778 to Hammer.

These copolymers can also contain a fourth comonomer, which can be, for example, an ethylenically unsaturated carboxylic acid (for example, acrylic or methacrylic acid), an ester of such an acid, acrylonitrile, or an .alpha.-olefin.

The vinyl halide polymer can be, for example, polyvinyl chloride or polyvinyl bromide; and the vinylidene halide polymer can be, for example, polyvinylidene chloride or polyvinylidene bromide. Polyvinyl chloride is commercially available from many sources, including Conoco, Inc., while polyvinylidene chloride is available, for example, from Dow Chemical Co. Other polymers of those types can be made as described, for example, in Encyclopedia of PVC, edited by L. J. Nass. Marcel Dekker, Inc. New York (1976).

The vulcanizing agent that is added to, and dispersed in, the polymer blend is one of those normally employed in the vulcanization of rubber and can be elemental sulfur or a compound that releases sulfur at vulcanization temperatures, i.e., a sulfur donor, or mixtures thereof, which compounds are well known in the industry. Extensive descriptions of sulfur vulcanizing systems that can be used in this invention have been published, for example, in Hofmann, "Vulcanization and Vulcanizing Agents", Palmerton Pub. Co., N.Y. 1967; and Alliger and Sjothun, "Vulcanization of Elastomers", Reinhold Pub. Corp. N.Y., 1964. Representative vulcanizing agents that release sulfur at vulcanization temperatures include thiuram polysulfides, e.g., dipentamethylene thiuram tetrasulfide or hexasulfide, tetramethyl thiuram disulfide; amine disulfides, e.g., di-morpholyl disulfide; sodium polysulfide, and thioplasts. When the temperature of the terpolymer is increased during vulcanization, the sulfur donors liberate part of their loosely bound sulfur which is then consumed in the formation of crosslinks.

Organic accelerators can be, and generally are, used in combination with the vulcanizing agent and dispersed throughout the polymer blend in order to shorten the vulcanization times and lower curing temperatures. Further, the amount of vulcanizing agent can be reduced when a curing accelerator is used. Any conventhonal accelerator or mixtures thereof normally used to vulcanize rubber can be used in the present invention including: the thiazoles; mercapto accelerators such as mercaptobenzothiazole; and sulphenamide accelerators, e.g., derivatives of mercaptobenzothiazole, guanidine accelerators, e.g., diphenylguanidine (DPG) an di-o-tolylguanidine (DOTG); thiurams, such as thiuram monosulfides and thiuram disulfides; and dithiocarbamates. The amount of accelerator used can vary over a wide range and the amount depends on the particular chemical composition, the accelerator and the intended use of the elastomer. Generally, the amount of accelerator used will be about 0.2-4, preferably 0.5-2 parts, per 100 parts of polymer blend.

Fillers, processing aids, plasticizers, and oils can be added if desired. Among the fillers that can be used, carbon black, calcium carbonate, talc, magnesium oxide, and zinc oxide can be mentioned as quite commonplace in the rubber industry. Zinc oxide also serves as an activator for azodicarbonamide when the latter is used as a blowing agent.

Organic plasticizers of the types used in plasticizing polyvinyl chloride can be used in E/VA/CO terpolymer/polyvinyl chloride blends. Suitable plasticizers include, for example, aryl phosphates such as triphenyl phosphate, phthalate esters such as dioctyl phthalate and tributyl phthalate, trimellitate esters such as tri(2-ethylhexyl)trimellitate, and adipate esters such as diisodecyl adipate. Also see "the Technology of Plasticizers" by J. Kern Sears and Jospeh R. Darby, John Wiley and Sons, Pub. (1982). The amount of plasticizer depends on the end use and the stiffness appropriate for the end use, but it preferably should not exceed the level of polyvinyl chloride present in the compositions.

The polymers, fillers, and plasticizers can be mixed in a batch mixer, such as a Banbury mixer, or a continuous mixer, such as a Farrell continuous mixer, at a suitable temperature, usually about 160.degree.-200.degree. C., preferably 165.degree.-175.degree. C. The temperature should be adequate to facilitate mixing but not so high as to cause polymer discoloration or degradation.

The blowing agent, activator, curing agent, and accelerator can be added to the blend on a roll mill, usually at a roll temperature in the range of 50.degree.-130.degree. C. Usually, these materials are not added all at once but gradually, over a period of several minutes. The roll temperature is chosen so as to avoid both premature curing of the polymer blend and decomposition of the blowing agent during the blending operation. The appropriate temperature thus will depend, among others, on the activities of the blowing and curing systems used as well as on the composition and the softening temperature of the blend.

Curing and foaming are carried out simultaneously within a temperature range of about 100.degree. to 180.degree. C. This can be done, for example, in a circulating oven, a salt bath, a hot air tunnel, or another heating arrangement.

The operation can be either batchwise or continuous. When it is continuous, a completely compounded polymer blend composition containing both the curing and the foaming agents, as well as any accelerators and activators, is continuously extruded into the heating zone at a rate such that both foaming and curing are substantially complete at the time the composition leaves the heating zone; the cured material is cooled to ambient temperature, cut into appropriate lengths, if necessary, and removed to a storage area. In a batch operation, one or a series of compression molds are filled with the completely compounded composition and heated to an appropriate temperature for a suitable time to adequately crosslink the polymer and decompose the blowing agent; the mold is then opened and expansion of the foam occurs.

This invention is now illustrated by the following examples of certain representative embodiments thereof, where all parts, proportions, and percentages are by weight, unless indicated otherwise. "PVC" stands for polyvinyl chloride. All measurements made and results obtained in units other than SI have been converted to SI units.

EXAMPLE 1

A stabilized polymer blend was prepared as follows:

______________________________________Blend Components %______________________________________PVC (Firestone FPC-9300), inh. visc. = 0.96 46.3Mark S17, phosphite chelator (Argus Chem. Co.) 0.5Ba/Cd laurate (Argus Chem. Co.) 1.4Acryloid .RTM. K-120N 1.4acrylic fusion aid (Rohm & Haas)Allied 617A (polyethylene wax) 1.8Epoxidized soybean oil 4.6Calcium carbonate 11.6E/VA/CO (65:25:10) terpolymer, 32.4melt index = 20______________________________________

The blend was made in two steps. First, all ingredients except the E/VA/CO terpolymer were combined in a high speed dry blender (Welex). This dry blend was then added to a Banbury internal mixer, along with the E/VA/CO terpolymer, and was mixed at high speed for 10-15 minutes at a temperature of 190.degree. C. This material is referred to as polymer blend A.

Four foamable and curable compositions designated a, b, c, and d were prepared by intimately mixing all ingredients on a two-roll rubber mill operating at a temperature below the decomposition temperature of the chemical blowing agent, about 120.degree. C. They were then foamed and cured in a press at 165.degree. C. and a force of 188,000N.

Compounding and curing information as well as the physical properties of the resulting foams are summarized in Table 1 below.

TABLE 1______________________________________Components %______________________________________Polymer Blend A 64.3 81.5 85.9 74.1Carbon Black (ASTM-N650) 25.7 6.1 -- 18.1Carbon Black (ASTM-N-762) -- -- 6.4 --Azodicarbonamide 2.6 4.0 3.0 2.5Zinc Oxide 1.3 1.2 2.1 0.8Pentaerythritol; -- 2.0 0.9 1.2particle size 0.075 mmStearic Acid 0.6 0.6 0.2 0.4Zinc Stearate 1.3 1.2 -- 0.7Sulfur 0.6 0.6 0.9 0.4Thiocarbanilide, sulfur 0.2 0.2 -- 0.1cocurativeMercaptobenzothiazole 0.3 0.3 -- 0.2Zinc dibutyl dithiocar- 0.6 0.6 -- 0.4bamateDesical P (80% CaO in 1.9 1.8 -- 1.1hydrocarbon oil),Basic Chemical Co.Tellurium diethyl 0.2 0.2 -- 0.1thiocarbamateTetramethylthiuram mono- -- -- 0.1 --sulfideN--cyclohexyl-2-benzo- -- -- 0.4 --thiazole sulfenamideCure time, min. 7.0 9.0* 7.0 12Density, g/cm.sup.3 0.67 0.26 0.23 0.96Hardness, Durometer A 84 31 29 57(ASTM D2240-81)Bashore rebound, % -- 15 14 13(ASTM D2632-67)______________________________________ *Plus 60 min postcure in oven at 160.degree. C.

EXAMPLE 2

The stabilized and plasticized polymer blend used in this example was prepared in the manner described in Example 1 from the following components and is referred to as polymer blend B.

______________________________________Polymer Blend B %______________________________________PVC (Firestone FPC-9300), inh. visc. = 0.96 43.82Phosphite chelator (Argus Chem. Co.) 0.22Ba/Cd laurate (Argus Chem. Co.) 1.10Epoxidized soybean oil 2.19Stearic acid 0.09Dioctyl phthalate 35.06E/VA/CO (65:25:10) terpolymer, 15.34melt index = 20______________________________________

The composition was prepared in two stages using a two-roll rubber mill. The ingredients of part I of the formulation shown in Table 2, below, were blended at a temperature of 150.degree. C. The mill was then allowed to cool to 110.degree. C. and the ingredients of part II of the formulation shown in Table 2 were blended in at that temperature. The curing conditions and physical properties of foams resulting from these compositions also are shown in Table 2.

TABLE 2______________________________________ a b______________________________________Part IPolymer Blend B 67.10 66.73Calcium Carbonate 16.77 16.68Satintone Special Clay 6.71 6.67(Engelhardt)Zinc Oxide 2.68 2.67Stearic Acid 1.34 1.33Part IIAzodicarbonamide 3.35 3.33Sulfur 0.94 0.93N--cyclohexyl-2-benzo- 0.67 0.67thiazole sulfenamideMercaptobenzothi- 0.34 0.33azoleTetramethyl- 0.13 0.13thiuram monosulfidePentaerythritol -- 0.50______________________________________ ______________________________________Cure conditions and foam properties Composition a Composition b______________________________________press cure time at 6 -- 6 5 6165.degree. C., min.post-cure time in -- 6* 10 5 --oven at 170.degree. C., min.density g/cm.sup.3 0.81 0.72 0.63 0.31 0.21Shore A hardness 50 40 49 20 10______________________________________ *Sample was cut from uncured sheet produced on roll mill and placed directly in an oven at 170.degree. C. to afford a cured, free blown (no compression) foam.

EXAMPLE 3

This example illustrates the preparation of a filled, sulfur-cured, low density, closed cell foam by extrusion and continuous oven cure.

The stabilized polymer blend used in this example had the following composition:

______________________________________Polymer Blend C Parts______________________________________PVC (Conoco grade 5305, inherent 40viscosity, 0.75)Mark XX (liquid phosphite chelator, 1.5Argus)Mark XI (Ba/Cd laurate stabilizer, Argus) 3Epoxidized soybean oil 6(Rohm & Haas)Allied 6A (polyethylene processing aid, 6Allied)E/VA/CO (66:24:10) Terpolymer 60(melt index 35)______________________________________

All of the ingredients in Blend C, except the E/VA/CO terpolymer, were first blended in a high speed mixer (Welex) in 3000 g batches. The dry blend was then placed in a lined drum along with the terpolymer, and the blend was tumble-blended on a drum tumbler. The resulting blend was melt-extruded using a 28 mm single screw extruder operated at 220 rpm with the barrel temperature set at 180.degree.-200.degree. C. and the die temperature at about 220.degree.-230.degree. C.

Polymer C was further compounded as follows:

______________________________________ a b______________________________________Polymer Blend C 894 894Hydrated amorphous 44.7 44.7silica (Hardwick)Calcium carbonate 268.2 268.2Dimethylnaphthalene/ 89.4 89.4formaldehyde resinCalcium stearate 8.94 8.94Stearic Acid 4.5 4.5Titanium dioxide 44.7 44.7Adipic acid 4.5 4.5Zinc Oxide 22.4 22.4Chlorinated paraffin 44.7 44.7oil (Diamond Shamrock)Calcium oxide 22.4 22.4Magnesium carbonate 89.4 89.4Diethylene glycol 8.94 8.94TE 80 (Processing aid, 8.94 8.94Technical Processing Co.)Isodecyl diphenyl 44.7 89.4phosphate______________________________________

Polymer Blend C, in pelletized form, was charged to a Banbury mixer and melted, whereupon the other ingredients listed above were added, and mixing was continued at 165.degree. C. for 10 minutes. Each blend was then discharged and rolled into a sheet on a roll mill. These materials are referred to as Banbury compounds.

The Banbury compounds were blended with a blowing agent, a blowing agent accelerator, and sulfur curing agents on a roll mill set at 80.degree. C.

The milled compound was taken off the roll as sheets which were cut into strips and fed into a 3.75 cm Royale single screw extruder equipped with a vacuum screw with an L/D ratio of 15 and a streamlined 1.25 cm diameter circular hole die and extruded at a melt temperature of about 100.degree. C. The smooth extruded rod was cured in a tunnel with two heating zones, 140.degree. C. and 154.degree. C. with a residence time of 8 minutes in each zone. A soft foam with a smooth outer skin and having a density of 0.16 gm/cm.sup.3 was obtained.

EXAMPLE 4

The formulations shown here exhibit greatly improved ozone resistance over nitrile rubber/PVC foams:

TABLE 2______________________________________ g %______________________________________Part IEVACO (65.5:23.5:11) terpolymer 66.0 23.8PVC (Inherent viscosity 0.93) 27.2 9.9Ba/Cd Laurate 0.8 0.3Phosphite Chelator (Argus Chem. Co.) 0.3 0.1Epoxidized soybean oil 2.7 1.0Polyethylene Wax (Allied 617A) 5.1 1.8Stearic Acid 2.1 0.8Acrylic Processing Aid 0.8 0.3(Acryloid .RTM. K120, Rohm & Haas)Titanium dioxide 70.0 25.3Hydrated Alumina 30.0 10.8Carbon Black (ASTM N550 FEF) 10.0 3.6Zinc Oxide 4.0 1.4Tricresyl Phosphate 15.0 5.4Dioctyl Phthalate 20.0 7.2Part IISurface-Treated Urea (Uniroyal) 1.5 0.5Azodicarbonamide 18.0 6.5Sulfur 1.4 0.5N--cyclohexyl-2-benzo- 1.0 0.4thiazole sulfenamideMercaptobenzothiazole 0.5 0.2Tetramethylthiuram monosulfide 0.5 0.2 276.9 100.0______________________________________

PVC, stabilizers, and processing aids (Ba/Cd laurate through Acryloid.RTM.K120 in Table 2) were combined in a high intensity mixer (Welex); then the other ingredients of Part I were combined in a Banbury mixer at 180.degree. C. for 10-15 minutes.

On a roll mill, Part I and Part II were combined at a maximum temperature of about 120.degree. C.

Foams were made by compression molding at 165.degree. C. for 3-5 minutes followed by an oven cure of 9-10 minutes at 170.degree. C.

Ozone Degradation

Samples of a commercial nitrile rubber-PVC foam were compared with the above E/VA/CO-PVC foam in a static ozone exposure test. Ozone concentration was 3 ppm at 37.8.degree. C. Samples 2.5 cm wide, 1.25 cm thick, and 15 cm long were attached at one end and bent over a 5 cm mandrel; a weight was affixed to the free end. Samples were observed after exposure to the ozone, and both failure and failure time were recorded. Samples were checked daily except on weekends. Therefore, a time range is recorded for time to break.

______________________________________ Hours to Break______________________________________Nitrile-PVC foam 47-119Nitrile-PVC foam 23-47E/VA/CO-PVC foam No break after 1879 hours. Test terminated.______________________________________

EXAMPLE 5

The following blends were prepared

______________________________________ Parts______________________________________Part IPVC (Firestone FPC-9300) 26.8Ba/Cd Laurate (Argus Chem Co.) 0.8Phosphite Chelator 0.3(Argus Chem Co.)Epoxidized soybean oil 2.6Dioctyl phthalate 8.0Polyethylene wax (Allied 6A) 1.0Stearic Acid 0.1Acryloid .RTM. K-120N (Rohm & Haas) 0.8E/VA/CO (65:25:10) terpolymer 59.5Talc 70Clay 40Zinc Oxide 4Stearic Acid 2Part IIAzodicarbonamide 18Surface-treated urea (Uniroyal) 1.52-Mercaptobenzothiazole 0.5Sulfur 1.4N--Cyclohexyl-2-benzothiazole 1sulfenamideTetramethylthiuram monosulfide 0.2Carbon Black (ASTM N-650) 1______________________________________

PROCEDURE

Part I ingredients were blended in a Banbury internal mixer for 10 min. at 160.degree. C. Ingredients of Part II were blended with the Part I blend on a two-roll rubber mill at 50.degree. C.

The above composition was fed to a single screw extruder operating at 88.degree. C., exiting through a ribbon die into a 6-meter air-heated tunnel with an air temperature of 175.degree. C. The rate of feed was controlled so that the total residence time in the tunnel was 7.5 min. The resulting closed-cell foam had a density of 0.39 g/cm.sup.3.

Claims

1. A foamable and curable composition comprising a polymer blend of

(1) 5 to 95 parts of an E/X/Y copolymer, wherein

E is ethylene;

X is a vinyl ester; and

Y is carbon monoxide or sulfur dioxide; and

(2) 95 to 5 parts of a polymer of a vinyl halide or vinylidene halide, the total amount of polymers (1) plus (2) being 100 parts;

(3) an effective amount of a blowing agent; and

(4) at least one curing agent selected from

(a) about 0.2 to 5 parts of sulfur and

(b) about 0.2 to 15 parts of an agent capable of releasing elemental sulfur under the cure conditions, at a temperature of about 100.degree.-180.degree. C.

2. A composition of claim 1, wherein the E/X/Y copolymer is an ethylene/vinyl acetate/carbon monoxide terpolymer.

3. A composition of claim 2, wherein the polymer blended with the ethylene/vinyl acetate/carbon monoxide terpolymer is polyvinyl chloride.

4. A composition of claim 3 wherein the curing agent is sulfur.

5. A composition of claim 1, which also contains a vulcanization accelerator.

6. A composition of claim 5, wherein the vulcanization accelerator is a conventional rubber vulcanization accelerator.

7. A composition of claim 6 wherein the amount of the vulcanization accelerator is 0.2-4 parts per 100 parts by weight of polymer blend.

8. A composition of claim 7 wherein the amount of the vulcanization accelerator is 0.5-2 parts per 100 parts by weight of polymer blend.

9. A foamed and cured composition obtained by foaming and curing a composition of claim 1.

10. A foamed and cured composition obtained by foaming and curing a composition of claim 3.

11. A foamed and cured composition obtained by a process comprising

(A) uniformly dispersing an effective amount of a blowing agent and at least one curing agent selected from:

(a) about 0.2 to 5 parts of sulfur, and

(b) about 0.2 to 15 parts of an agent capable of releasing sulfur under the cure conditions in a polymer blend of:

(1) 5 to 95 parts of an E/X/Y copolymer, wherein

E is ethylene;

X is a vinyl ester; and

Y is carbon monoxide or sulfur dioxide; and

(2) 95 to 5 parts of a polymer of a vinyl halide or vinylidene halide, the total amount of polymers (1) plus (2) being 100 parts, all the parts being by weight; and

(B) heating said blend containing the blowing agent and the curing agent at a temperature of about 100.degree.-180.degree. C., at which both foaming and curing take place, for a sufficient time to obtain substantially complete foaming and curing.