Process for making high temperature Bi-Sr-Ca-Cu oxide superconductor

Abstract

A description is given of superconducting substances having a content of Bi, Sr, Ca and Cu, and of processes for their preparation from the metal oxides within a range which is specified by the overall composition Bi.sub.a (Sr,Ca).sub.b -Cu.sub.6 O.sub.x, where a=3-24 and b=3.23-24, with an Sr/Ca atomic ratio of 1:9-9:1 and a Bi:(Ca+Sr) atomic ratio of 0.3-1.5. The transition temperature is at least 60 K. The principal phase crystallizes in the orthorhombic system. The pure compounds Bi.sub.4 (Sr,Ca).sub.4 Cu.sub.2 O.apprxeq..sub.12 and Bi.sub.4 (Sr,Ca).sub.6 Cu.sub.4 O.apprxeq..sub.20.

Description

The present invention relates to high-temperature superconducting substances based on bismuth, strontium, calcium and copper.

While it was possible to use the conventional superconducting materials solely at very tow temperatures which required the use of the very expensive coolant helium, the new superconducting oxidic substances operate at substantially higher temperatures which can be achieved with the comparatively cheap coolant nitrogen. This reduces the running costs of superconducting appliances and systems and opens up novel extensive application possibilities.

A substantial disadvantage of many novel oxidic superconductors is however that they contain, as a common component, La or Y or rare earth metals such as, for example, Sm, Lu, Ho or Eu, Some of these metals occur only in small quantities and are expensive owing to their complicated extraction. Disadvantages stemming from the high raw material prices and the limited reserves of the rare earth metals consequently arise for the production of large quantities of oxidic superconductors.

An oxidic superconductor having a transition temperature of 20 K is already known which contains in oxidic form the elements bismuth, strontium and copper in an atomic ratio of 1:1:1. (C. Michel et al., Z. Phys. B 68 (1987) 421). A transition temperature of about 20 K is, however, still not satisfactory for industrial purposes.

There was therefore the object of providing novel superconducting oxidic substances which do not contain any rare earth metals and do not contain lanthanum or yttrium and whose transition temperature is markedly above 20 K.

The invention is based on the discovery that the transition temperature in the system comprising the oxides of Bi, Sr, Ca and Cu is favorably influenced if calcium is also present in addition to strontium and a Bi:(Sr+Ca) atomic ratio of about 0.3-2.2, in particular 0.5-2.2, preferably 0.3-1.5 in the initial mixture of metal oxides is maintained. Particularly preferred is ratio 0.3-1.3.

Novel substances with superconductivity have now been found which contain the metal strontium, calcium, copper and bismuth in oxidic form. These are black crystalline substances with the overall composition

Bi.sub.a (Sr,Ca).sub.b Cu.sub.6 O.sub.x where a=1.8-24, preferably 3-24 b=3.23-24 and x=about 1.5a+b+6 with a Ca/Sr atomic ratio of 9:1-1:9, in particular 9:1-1:3, preferably 3:1-1:3.

The substances have a critical temperature (transition temperature) T.sub.c of at least 60 K and preferably of at least 70 K. They are black and their principal phases crystallize in the orthorhombic system.

Preferred are mixtures with a Bi/Cu atomic ratio of 0.5-2 (ie. a=3-12) and a (Ca+Sr):Cu atomic ratio of 1-2 (ie. b=6-12) and a Bi:(Ca+Sr) atomic ratio of 0.3-2, preferably 0.3-1.3, in particular 0.5-1.

In the substances, the oxygen content found to be somewhat higher than calculated for divalent copper and trivalent bismuth. They therefore probably contain also Cu.sup.+++ ions or Bi.sup.4+ /Bi.sup.5+ ions. For a given a, b and c, an oxygen content (x) which is as high as possible is advantageous for the superconductivity.

In a particular embodiment of the invention, the (Ca+Sr+Cu):Bi atomic ratio in the black crystalline substances is about 1.5.

These substances have the general composition

Bi.sub.2 (Ca,Sr).sub.y Cu.sub.3-y+k O.sub.f, where k denotes a number between -0.05 and +0.05, preferably 0 and y denotes a number between 1 and 2.5, preferably 1.33 to 2.25, in particular 1.33 to 2.1, and f denotes about 6+k.

Here the range y=1.9-2.1 is particularly preferred.

A black crystalline substance furthermore behaves advantageously which has the overall composition Bi.sub.a (Sr,Ca).sub.b Cu.sub.6 O.sub.x,

where a=3-24 and b=3.23 to 24, with a Sr/Ca atomic ratio of 1:9 to 9:1, a Bi:(Sr+Ca) atomic ratio of 0.45 to 1.5, preferably 0.5-1, a transition temperature T.sub.c for the superconductivity of at least 60 K and a principal phase which crystallizes in the orthorhombic system. This also applies to mixtures in which 12<a.ltoreq.24 and b=3.23-24 or a=3-24 and 3.23.ltoreq.b<6 or 12<b.ltoreq.24.

Preferred here are crystalline substances of the overall sonposition

Bi.sub.a (Sr,Ca).sub.b Cu.sub.6 O.sub.x in which a=3-14 and b=4 to 18, in particular 4.9 to 14.

Particularly preferred are mixtures in which

a=4 to 14 and b=6 to 14, with a Bi:(Sr+Ca) atomic ratio of 0.45-1.13, in particular 0.5-1.13.

The index for the proportion of oxygen is about x=1.5a+b+6. It is somewhat dependent on the annealing conditions. For high thermal post treatment temperatures, x is less than for low ones. Oxygen can probably be reversibly taken up at particular lattice sites.

Provided the black crystalline substance has an overall composition in the range Bi.sub.a (Sr,Ca).sub.b Cu.sub.6 O.sub.x, where

a=9.8 to 14 and b=9.8 to 14 and the Bi:(Sr+Ca) atomic ratio is 0.89 to 1.13, it contains as the principal component the superconducting phase of the composition Bi.sub.4 (Sr,Ca).sub.4 Cu.sub.2 O.sub.x, further details on the preparation of which are to be found on page 7. In these mixtures too, the Ca:Sr atomic ratio is 9:1-1:9, in particular 3:1-1:3.

The novel substances can be prepared by mixing oxides or oxide precursors of the elements Bi, Sr, Ca and Cu thoroughly and heating the mixture to temperatures of at least 700.degree. C.

During the reaction, the atomic ratio of the metals used does not change in a first approximation. The atomic ratio used therefore corresponds to the required oxide composition.

As oxide precursors, use may generally be made of compounds which react to form the corresponding oxides at the reaction temperature, in particular the hydroxides and nitrates. The acetates, formates, oxalates and carbonates of the said metals may also be used. For example, calcium oxide, strontium carbonate, bismuthic acid, bismuth(III) oxide, bismuth(V) oxide, Cu.sub.2 O and CuO may be used.

The reaction mixture does not have to, or only partially has to, melt. In this case, it is, however, necessary to keep it for a prolonged period at the reaction temperature.

The synthesis temperature is in this case preferably in the range between 700.degree. and 900.degree. C., preferably 750.degree.-850.degree. C.

The reaction time should be at least 4 hours, still better, at least 8 hours. The reaction time is limited in the upward direction only by economic considerations. Reaction times of 100 or 120 hours are possible.

The mixture may also be heated so high that it is melted completely. In this case, cooling can be carried out rapidly to temperatures below the solidification point of the entire mixture, ie. 300.degree.-900.degree. C., preferably 300.degree.-830.degree. C., and the mixture may be kept in this range for a prolonged time (at least one hour, preferably 4 hours).

Advantageously, the melt can be deposited on a substrate and allowed to solidify there. In this manner, compact layers of the superconductor are obtained on a base after the subsequent temperature treatment at 300.degree.-900.degree. C. The substrate (base) should not react with the reaction mixture. Suitable as a material for the substrate are, for example, Al.sub.2 O.sub.3, SiO.sub.2 (quartz), ZrO.sub.2, strontium titanate and barium titanate, and also metals such as steel and Cr/Ni alloys. In this manner, for example, fairly thin layers of 1 .mu.m-5 mm can be prepared.

The melt may also be spun. In this case, filaments or threads are produced which are also superconducting after annealing at 300.degree.-900.degree. C., preferably 300.degree.-830.degree. C.

The actual reaction should take place in a non-reducing atmosphere. Use may be made, for example, of air, pure oxygen, mixtures of O.sub.2 /Ar or O.sub.2 /N.sub.2. It is preferable if the reaction of the oxides is carried out in an atmosphere containing oxygen.

After the reaction is complete, the sample is either removed from the furnace and slowly cooled to room temperature in air or oxygen, or is slowly cooled to room temperature in the furnace. Low cooling rates (not exceeding 100 K/h) have a favorable effect on the superconducting properties of the reaction product.

To make sure that the entire oxide mixture has reacted, it is advantageous to comminute the powder obtained further after cooling and to treat it again thermally. For this post treatment, the temperature is in the range from 300.degree. to 900.degree. C. The duration of the post treatment is at least 1 hour, preferably at least 4 hours. What has been stated for the reaction time applies to the upper limit of the post treatment time. Preferably the hot mixture is cooled to room temperture in an atmosphere containing oxygen.

Preferred lower limits of the post treatment temperature are at least 300.degree. C., in particular 400.degree. C., and preferred upper limit is 750.degree. C., better 600.degree. C., in particular 550.degree. C., and still better 500.degree. C. The possible post reaction should be carried out in air, pure oxygen or in a gas mixture such as O.sub.2 /Ar or O.sub.2 /N.sub.2. Commercially available crucibles or boats of inert materials such as, for example, aluminum oxide, zirconium, platinum and iridium may be used as reaction vessels. Suitable sources of heat are commercially available furnaces such as, for example, chamber, muffle or tubular furnaces.

A further process for preparing the superconducting substances is to mix salts of the said metals in the presence of an aqueous phase, evaporate down the water-containing salt mixture and heat at temperatures of at least 700.degree. C. At least one of the salts used should be water-soluble and the salts should decompose to form oxides in the specified temperature range. The same applies in relation to the reaction time as when the oxides are used.

The salt mixture to be evaporated down can be prepared by dissolving metal oxides in nitric acid and fuming off the nitric acid.

Provided water-soluble salts are used, the metal hydroxides or at least on metal hydroxide can also be precipitated by adding a base, for example tetramethylammonium hydroxide. In this manner it is possible to achieve a particularly thorough mixing of the initial products. The precipitated hydroxides form, together with the undissolved constituent, the "insoluble constituent". This may be separated off, dried and then annealed as specified above. Preferably, no low-volatility cations are entrained by the base used and the salts used are derived from readily volatile acids. These are acids whose boiling point is below 150.degree. C.

In this development of the process according to the invention, the atomic ratio of the metal salts used again corresponds to the required atomic ratio of the final product. The oxidic products prepared from the salts can also be thermally post treated as described above.

In the case of copper-rich formulations, crystals of Cu.sub.2 O (red) and CuO (needles) can be removed under the microscope from the black crystalline substance according to the invention after melting, cooling and comminuting. A black crystalline substance is left.

If a Bi:(Sr+Ca):Cu atomic ratio of 2:2:1 is maintained during the preparation, pure black crystals of the composition Bi.sub.4 (Sr,Ca).sub.4 Cu.sub.2 O.sub.x can be obtained whose transition temperature T.sub.c for the superconductivity is at least 60-85 K, generally 70-85 K. In this connection, Ca:Sr atomic ratios of 3:1 to 1:3, in particular 1.4:3-1.8:3 and particularly preferred, of about 1.6:3 are preferred. In superconducting crystals, the index for the oxygen content (x) is about between 12 and 14.

It has now been found that this compound has the lattice constants a=5.39.times.10.sup.-8 cm, b=5.39.times.10.sup.-8 cm and c=24.53.times.10.sup.-8 cm. This compound can be prepared from the required metal oxides, it being necessary to maintain the atomic ratios of the compound. It has further been found that the compound probably also contains pentavalent bismuth.

If the atomic ratio of the formulation is changed slightly, compound with identical lattice constants and somewhat different composition is obtained. Use may be made, in particular, of formulations having a Cu:Bi atomic ratio of 1:1.9-1:2.1, a (Ca+Sr):Cu atomic ratio of 1.9:1-2.1:1, a (Ca+Sr):Bi atomic ratio of 0.9:1-1.1:1 and a Ca:Sr atomic ratio of 9:1-1:9, in particular 3:1-1:3, preferably 1:1-1:3.

It has further been found that, if the corresponding oxide ratios are maintained, a black crystalline substance of the overall composition Bi.sub.4 (Ca,Sr).sub.6 Cu.sub.4 O.apprxeq..sub.20 can be produced which also has a high transition temperature, it may also be obtained from the melt with subsequent thermal treatment with O.sub.2. The crystalline substance so prepared is composed almost exclusively of a principal phase which crystallizes in the orthorhombic system and has the specified composition. Its transition temperature T.sub.c is at least 70 K. The lattice constants of the compound which crystallizes in the orthorhombic system are a=5.395.times.10.sup.-8 cm, b=5.393.times.10.sup.-8 cm and c=30.628.times.10.sup.-8 cm.

A paper entitled "Superconductivity in the Very High T.sub.c Bi--Ca--Sr--Cu--O System:Phase identification" by the authors R. M. Hazen, C. T. Prewitt, R. J. Angel, N. L. Ross, L. W. Finger and C. G. Hadidiacos, D. R. Veblen and P. J. Heaney, P. H. Hor, R. L. Meng, Y. Y. Sun, Y. O. Wang, Y. Y. Xue, Z. J. Huang, L. Gao, J. Bechtold and C. W. Chu, Phys. Rev. Lett. 60 (1988) p. 1174 revealed superconducting phase whose composition is close to Bi.sub.2 Ca.sub.1 Sr.sub.2 Cu.sub.2 O.sub.9 and for which an A-centered orthorhombic unit cell is specified having the dimensions 5.41.times.5.44.times.30.78.times.10.sup.-8 cm.

It has now been found that pure crystals with a somewhat higher transition temperature in which the Ca/Sr atomic ratio is 1:3.5 to 1:6.28, in particular 1:4.5 to 1:5.75, preferably 1:5, can be prepared from an initial mixture with somewhat higher Sr/Ca ratio. Reaction temperatures not exceeding 850.degree. C., slow cooling and post annealing at 700.degree. C. are beneficial for the formation of the compound. Small excesses of CuO and also a higher Sr/Ca ratio are furthermore beneficial.

If the atomic ratios of the formulation are changed slightly, a compound with the lattice constants specified above and a somewhat different composition is again obtained. In particular, formulations having a Cu:Bi atomic ratio of 1:0.9-1.1:1, a (Ca+Sr):Cu atomic ratio of 3:1.9-3:2.1, a (Ca+Sr):Bi atomic ratio of 3:1.9-3:2.1 and a Ca:Sr atomic ratio of 1:1-1:9, in particular 1:3.5-1:6.28 may be used.

As an X-ray structural analysis has shown, the strontium-richer compound just mentioned is made up of layers which are arranged in parallel, which each alternate with one another and which are composed of

a) �Bi.sub.2 O.sub.4 !.sup.2+ and b) �(Ca,Sr).sub.3 Cu.sub.2 O.sub.6 !.sup.2- with a Perowskite structure in which, in the layer, two planes of �CuO.sub.6 ! octahedra which join each other at the corners are present and, in the planes of oxygen atoms which are situated above and below in parallel with each of the two �CuO.sub.4/2 ! planes, the alkaline earth atoms are so arranged that they are each situated at the center of a smallest square composed of 4 oxygen atoms, and the two planes of �CuO.sub.6 ! octahedra have a layer of (Ca,Sr)O in common.

The oxygen positions between the two octahedral layers are (depending on the conditions of preparation of the superconductor), not occupied or only partially occupied. Prolonged heating at 900.degree. C. results in loss of oxygen, while prolonged heating at 400.degree. C. in an oxygen atmosphere results in a partial filling of said oxygen positions. The oxygen occupation in the �Bi.sub.2 O.sub.4 !.sup.2+ layers is also altered by the thermal treatment. Up to two O atoms can be removed for each Bi.sub.2 O.sub.4. Bismuth is then trivalent. At the same time the color of the crystals changes from black to brown. A high oxygen content (black mass) which can be established ideally at approx. -600.degree. C. is beneficial.

The X-ray structural analysis carried out on a single crystal having the Ca:Sr atomic ratio of 1:4 has revealed that only strontium atoms are present in the outer (Ca,Sr)O planes of the layer containing copper. On the other hand, the Ca/Sr atomic ratio in the inner (Ca,Sr)O plane of the layer containing copper is 1:1. Depending on the Ca/Sr ratio used in the formulation, this ratio may be 0.7:1-2.1:1, in particular 0.8:1 to 1.2:1. The structural arrangement of this compound is shown in FIG. 1.

In addition to the compound just described and having a Perowskite structure in which, in the layer containing copper, 2 planes of �CuO.sub.6 ! octahedra which are joined to each other at the corners are present, and to the compound Bi.sub.4 (Ca,Sr).sub.4 Cu.sub.2 O.sub.x having a Perowskite structure in which, in the layer containing copper, only one plane of �CuO.sub.6 ! octahedra joined to each other at the corners is present, compounds exist in which the layer containing Cu is made up of more than 2 planes of �CuO.sub.6 ! octahedra which join each other at the corners.

Using the generally specified processes, it is possible to prepare black superconducting compounds which crystallize in the orthorhombic system and have a transition temperature T.sub.c of at least 70 K and a content of Bi, Ca, Sr and Cu, and which have an overall composition of Bi.sub.4 (Ca,Sr).sub.4+2n -Cu.sub.2+2n O about 16+4n, where n=2, 3, 4 or 5. In these compounds, the Ca/Sr atomic ratio is 1:9 to 9:1. The lattice constants of the compounds are a=5.39.times.10.sup.-8 cm, b=5.39.times.10.sup.-8 cm and c=(24.5+n.times.6.1).times.10.sup.-8 cm.

X-Ray structural analyses indicate that the specified compounds are made up of layers which are arranged in parallel, which each alternate with one another and which are composed of

a) �Bi.sub.2 O.sub.4 !.sup.2+ and b) �(Ca,Sr).sub.2+n Cu.sub.1+n O.sub.4+2n !.sup.-2 having a Perowskite structure in which, in this layer, 1+n planes of �CuO.sub.6 ! octahedra which are joined to each other at the corners are present and the alkaline earth atoms in the 2+n planes of the oxygen positions, which are parallel to, but not in, the �CuO.sub.4/2 ! planes are so arranged that they are each situated at the center of a smallest square composed of 4 oxygen atoms and the planes of �CuO.sub.6 ! octahedra are joined by n common layers of (Ca,Sr)O.

Here, too, the oxygen positions between the two layers of octahedra, ie. in the (Ca,Sr)O plane are not occupied or only partially occupied. A corresponding remark applies to the �Bi.sub.2 O.sub.4 !.sup.2+ layers. The degree of occupation also depends on the thermal treatment of the crystalline substance first produced and the reaction gas used. A post-treatment as disclosed on page 6 expedient.

The Sr/Ca atomic ratio in the two outer (Ca,Sr)O planes of the layer containing copper is at least 10. These planes are therefore very strontium-rich. On the other hand, the Ca/Sr atomic ratio in the n inner (Ca,Sr)O planes of the layer containing copper depends substantially on the initial Ca/Sr ratio and may therefore be 1:10 to 10:1, in particular 1:3 to 3:1, preferably 1:1. The Ca/Sr ratio in all n inner (Ca, Sr)O planes is probably the same.

Surprisingly, superconducting substances can be obtained in the process according to the invention from laboratory chemicals having a purity of only about 99.5%.

If the atomic ratios of the formulation are changed slightly for the three-layer compound (n=2), a substance is again obtained which has a very high proportion of the compound with the specified layer structure and the specified lattice constants, but somewhat different composition. For example, formulations having a Cu:Bi atomic ratio of 3:1.9-3:2.1, a (Ca+Sr):Cu atomic ratio of 8:5.8-8:6.2, a (Ca+Sr):Bi atomic ratio of 2.1:1-1.9:1 and a Ca:Sr atomic ratio of 1:1-1:5, in particular 1:1.9-1:2.1 may be used.

The superconducting substances obtained can be used in power engineering (for cables and wires, transformers, and energy storage devices in the form of coils with current flowing through them), in magnetic technology (for example, nuclear spin tomographs and to produce holding magnets for suspension railways), in computer technology (thin films, connections on printed circuit boards, Josephson switching devices) and for electronic components (detectors, antennas, transistors, electronic sensors, for example SQUIDs, galvanometers, modulators, bolometers and SLUGs). The use of superconduction in metrology is dealt with in a paper "Die Anwendung der Supraleitung in der MeBtechnik" by Prof. F. Baumann, Karlsrube, published in series of papers by the VDI-Bildungswerk (1976).

It has further been found that several measures are advantageous for raising the proportion of a phase having T.sub.c .apprxeq.110 K,

A beneficial requirement is that the overall composition of the reaction mixture in the triangular coordinate system (ignoring the oxygen component) lies between four points ABCD which define a parallelogram, where

A=Bi.sub.0.19 E.sub.0.35 Cu.sub.0.46, B=Bi.sub.0.14 E.sub.0.4 Cu.sub.0.46, C=Bi.sub.0.3 E.sub.0.38 Cu.sub.0.32, D=Bi.sub.0.25 E.sub.0.43 Cu.sub.0.32 and E denotes the sum of the alkaline earths Ca+Sr. The calcium/strontium atomic ratio is 0.85:1-1.2:1, in particular 0.95:1-1.1:1. Preferably it is 1:1. Preferably, the overall composition lies between the corner points Bi.sub.0.2 E.sub.0.4 Cu.sub.0.4 and Bi.sub.0.25 E.sub.0.4 Cu.sub.0.35 which define a straight line intersection. With a Ca/Sr atomic ratio of 1:1, this corresponds to the corner points BiSrCaCu.sub.2 O.sub.x and BiSr.sub.0.8 Ca.sub.0.8 Cu.sub.1.4 O.sub.x.

It is furthermore advantageous to carry out the sintering process at as high temperatures as possible. However, in this process, the formulation should not melt. The duration of the sintering process is advantageously at least 50 hours. preferably at least 80 hours. It is beneficial to sinter in an oxygen-containing atmosphere, in particular air. If sintering is carried out in pure nitrogen, the formulation begins to melt about 40 K earlier.

A further advantageous measure is to cool down the formulation after sintering to temperatures of 550.degree.-650.degree. C,. preferably 580.degree.-620.degree., in particular 590.degree.-610.degree. C., to leave it for some time at this temperature, to heat it up again to the sintering temperature and to repeat this process at least 2.times.. This process can be repeated 2-20 times. The proportion of the superconducting phase then decreases again. It is preferable to repeat the cycle 2-6 times, in particular 2-3 times. The time for cooling from the sintering temperature to 550.degree.-650.degree. C., holding in the range 550.degree.-650.degree. C. and heating up again to the sintering temperature should be at least 30 minutes in each case, or better, at least 45 minutes. For the time of cooling to 550.degree.-650.degree. C. and holding at 550.degree.-650.degree. C., a time is preferred of at least one hour, in particular 1-3 hours, in each case. A further increase in these times appears to offer no more advantages.

The invention is explained in more detail by the examples.

EXAMPLE 1

1 mol of Bi.sub.2 O.sub.3, 2 mol of SrO, 2 mol of CaO and 2 mol of CuO are comminuted in an agate mortar, very intimately mixed and transferred to an Al.sub.2 O.sub.3 boat.

The specimen is rapidly heated in a suitable laboratory furnace to 950.degree. C,. and the specimen melts Specimens quenched directly from 950.degree. C. to room temperature exhibit an X-ray diffraction diagram according to Table 1 and also do not exhibit any superconduction.

If the specimen is cooled from 950.degree. C. to 700.degree. C. and kept at this temperature for one hour and then rapidly cooled to room temperature, the fragments of the melt cake so obtained exhibit a critical temperature of T.sub.c =70 K with measurements in a SQUID magnetometer.

The X-ray diffraction diagram of this specimen exhibits the appearance of a further crystalline phase (Table 2).

If the specimen is cooled from 700.degree. C. to 500.degree. C. and again annealed there for one hour, the powder diagram exhibits the phase which appeared at 700.degree. C. as the main product (Table 3). This specimen also exhibits a critical temperature of approx. 70 K (SQUID magnetometer).

EXAMPLE 2

3 mol of SrCO.sub.3, 1.5 mol of Bi.sub.2 O.sub.3, 3 mol of CaCO.sub.3 and 6 mol of CuO are comminuted in an agate mortar, mixed thoroughly and transferred to an Al.sub.2 O.sub.3 crucible.

The specimen is heated in air to 800.degree. C. in 6 hours in a suitable laboratory furnace and kept there for 6 hours. The specimen is then cooled to 400.degree. C. in 2 hours, kept at this temperature for a further 3 hours, then cooled to 100.degree. C. in 2 hours and removed from the furnace.

The black material so prepared exhibits a transition temperature of T.sub.c =75 K with measurements in a SQUID magnetometer (FIG. 2).

EXAMPLE 3

0.2 mol of Bi.sub.2 O.sub.3, 0.6 mol of SrO, 0.2 mol of CaO and 0.6 mol of CuO are comminuted, mixed and rapidly heated to 830.degree. C. in a corundum crucible. This temperature is maintained for 2 hours and subsequent annealing is then carried out in air at 800.degree. C. for 3 hours. The formulation is quenched from 800.degree. C. to room temperature by removing it from the furnace and allowing it to cool in air.

A compound is obtained of the approximate composition Bi.sub.4 (Ca,Sr).sub.8 Cu.sub.6 O.sub.20. The Sr/Ca atomic ratio is 4:1. The transition temperature T.sub.c is 70-82 K.

EXAMPLE 4

0.01 mol of CaO, 0.01 mol of Bi.sub.2 O.sub.3, 0.01 mol of SrO and 0.01 mol of CuO are mixed in an agate mortar, comminuted and transferred to a corundum boat. The formulation is heated rapidly in air to 1000.degree. C. in a laboratory furnace and kept at this temperature for 30 minutes. The crystalline substance melts in this process. It is then allowed to cool in the furnace to room temperature. The black stalk-like solidified melt cake is comminuted in a mortar, heated again (to 800.degree. C. in 2 hours in an oxygen atmosphere), then kept for 3 hours at 800.degree. C. and cooled to room temperature in 3 hours.

A subsequent measurement of the susceptibility in a SQUID magnetometer reveals a transition temperature of 77 K. The compound has the overall composition Bi.sub.4 (Ca,Sr).sub.4 Cu.sub.2 O.-+..sub.14.

EXAMPLE 5

0.02 mol of CaO, 0.01 mol of Bi.sub.2 O.sub.3, 0.02 mol of SrO and 0.04 mol of CuO are mixed in an agate mortar, comminuted and transferred to a corundum boat. The formulation is heated in one hour to 1000.degree. C. in air in a laboratory furnace and kept at this temperature for 30 minutes. In this process a melt is formed. Cooling is then carried out to 500.degree. C. in 2 hours and the formulation is removed from the furnace at this temperature. A subsequent measurement of the susceptibility in a SQUID magnetometer reveals a transition temperature of about 80 K.

According to radiographic investigations, the main product is Bi.sub.6 (Sr,Ca).sub.6 Cu.sub.4 O.apprxeq..sub.20.

EXAMPLE 6

2 mol of Bi.sub.2 O.sub.3, 4 mol of SrCO.sub.3, 4mol of CaO and 8 mol of CuO are comminuted in an agate mortar, mixed thoroughly and transferred to an Al.sub.2 O.sub.3 crucible. The specimen is rapidly heated in air to 800.degree.-820.degree. C., kept there for 20 hours and rapidly cooled to room temperature. The annealed powder is comminuted and treated thermally and mechanically a further two times as described above.

The black powder is then pressed into tablets under a pressure of 300 MPa (3 kbar), these are placed on MgO sheets and variously treated thermally (in air) as described below:

a) Heating to 870.degree. C. for 3 hours annealing at 870.degree. C. for 80 hours cooling to room temperature (=RT) in 2 min ("quenching") conductivity measurement: T.sub.c (R=O)=57 K SQUID measurement: 12% superconducting component at 4 K (measured at B=100 gauss; 1 gauss=10.sup.-4 Wb/m.sup.2) b) Heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 80 hours cooling to 600.degree. C. in 3 hours quenching from 600.degree. C. to RT (2 min) conductivity: T.sub.c (R=O)=63 K SQUID measurement: c) Heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 80 hours cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 3 hours cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 3 hours cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours conductivity measurement: T.sub.c (R=O)=107 K SQUID measurement: 30% superconducting component at 4 K (measured at 100 gauss) d) Heating to 864.degree. C. in 3 hours annealing at 864.degree. C. for 50 hours following temperature cycle run six times: cooling to 600.degree. C. in 1 hour annealing at 600.degree. C. for 1 hour heating to 864.degree. C. in 1 hour annealing at 864.degree. C. for 1 hour then: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours conductivity measurement: T.sub.c (R=O)=102 K SQUID measurement: 25% superconducting component at 4 K (measured at B=100 gauss) e) Heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 80 hours following temperature cycle run twelve times: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 3 hours then: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours conductivity: T.sub.c (R=O)=105 K SQUID measurement: 26% superconducting component at 4 K (measured at B=100 gauss) f) Heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 80 hours following temperature cycle run three times: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 3 hours then: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours conductivity: T.sub.c (R=O)=98 K SQUID measurement: 35% superconducting component at 4 K measured with 100 gauss 50% superconducting component measured with 10 gauss 1 gauss=10.sup.-4 Wb/m.sup.2.

EXAMPLE 7

4.3 mol of Bi.sub.2 O.sub.3, 7 mol of SrCO.sub.3, 7 mol of CaO and 12 mol of CuO are comminuted in an agate mortar, mixed and transferred to an Al.sub.2 O.sub.3 crucible. The specimen is rapidly heated in air to 800.degree.-820.degree. C., kept there for 20 hours, rapidly cooled to RT and coeeinuted (agate mortar). The annealing comminuting is repeated a further two times. Then the powder is pressed into tablets under a pressure of 300 MPa (3 kbar) and treated thermally on MgO sheets as described below:

a) Heating to 866.degree. C. in 3 hours annealing at 866.degree. C. for 65 hours following temperature cycle traversed six times cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 866.degree. C. in 3 hours annealing at 866.degree. C. for 3 hours then: cooling to 600.degree. C. for 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours T.sub.c (R=O)=66 K b) Heating to 866.degree. C. in 3 hours annealing at 866.degree. C. for 53 hours following temperature cycle run six times: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 866.degree. C. in 3 hours annealing at 866.degree. C. for 3 hours then: cooling to 600.degree. C. for 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours T.sub.c (R=O)=95 K 24% superconducting component at 4 K (measured with B=100 gauss) c) Heating to 868.degree. C. in 3 hours annealing at 868.degree. C. for 34 hours following temperature cycle run nine times: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 868.degree. C. in 3 hours annealing at 868.degree. C. for 3 hours then: cooling to 600.degree. C. for 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours T.sub.c (R=O)=60 K

EXAMPLE 8

2 mol of Bi.sub.2 O.sub.3, 4 mol of SrCO.sub.3, 4 mol of CaO and 12 mol of CuO are processed into tablets by the method specified in Example 6. These are thermally treated in various rays (in air):

a) Heating to 863.degree. C. for 3 hours annealing at 863.degree. C. for 50 hours following cycle traversed six times: cooling to 600.degree. C. in 1 hour annealing at 600.degree. C. for 1 hour heating to 863.degree. C. in 1 hour annealing at 863.degree. C. for 1 hour then: cooling to 600.degree. C. in 1 hour annealing at 600.degree. C. for 1 hour cooling to RT in 1 hour T.sub.c (R=O)=66 K b) Heating to 868.degree. C. in 3 hours annealing at 868.degree. C. for 34 hours following cycle traversed eight times: cooling to 600.degree. C. in 1 hour annealing at 600.degree. C. for 1 hour heating to 868.degree. C. in 1 hour annealing at 868.degree. C. for 1 hour then: cooling to 600.degree. C. in 1 hour annealing at 600.degree. C. for 1 hour cooling to RT in 1 hour T.sub.c (R=O)=64 K

EXAMPLE 9

1 mol of Bi.sub.2 O.sub.3, 2 mol of SrCO.sub.3, 2 mol of CaO and 3 mol of CuO are processed into tablets by the method specified in Example 6. These are thermally treated in the following way (in air):

Heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 80 hours following cycle traversed twice cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours heating to 870.degree. C. in 3 hours annealing at 870.degree. C. for 3 hours then: cooling to 600.degree. C. in 3 hours annealing at 600.degree. C. for 3 hours cooling to RT in 3 hours T.sub.c (R=O)=65 K 20% superconducting component at 4 K (measured at 100 gauss) TABLE 1______________________________________NO 2 THETA D INTEG.I (%)______________________________________1 7.125 12.4060 6.62 16.709 5.3057 0.53 21.674 4.1002 27.74 23.487 3.7877 0.75 25.718 3.4640 20.76 29.222 3.0560 100.07 29.600 3.0179 26.98 30.455 2.9351 3.99 31.937 2.8022 5.210 33.154 2.7021 14.811 34.884 2.5719 7.312 35.620 2.5204 0.613 36.532 2.4596 8.514 37.193 2.4173 6.215 37.854 2.3767 1.016 40.085 2.2494 1.117 41.047 2.1989 0.618 41.962 2.1530 15.419 44.368 2.0417 2.720 44.706 2.0270 8.921 50.234 1.8162 0.922 52.027 1.7577 16.823 53.693 1.7070 2.224 54.214 1.6919 1.325 54.972 1.6703 1.326 57.077 1.6136 9.0______________________________________ TABLE 2______________________________________NO 2 THETA D INTEG.I (%)______________________________________1 4.122 21.4351 3.62 4.302 20.5386 2.33 5.698 15.5105 1.64 7.107 12.4381 4.35 7.682 11.5074 1.66 21.611 4.1121 29.57 22.809 3.8986 21.98 24.713 3.6025 8.39 25.713 3.4646 26.010 26.101 3.4140 1.511 27.278 3.2693 35.612 28.947 3.0844 100.013 29.637 3.0142 47.514 30.149 2.9642 2.115 30.676 2.9144 45.516 31.950 2.8011 17.417 33.057 2.7098 84.918 34.875 2.5728 38.719 35.781 2.5094 1.320 36.497 2.4618 9.821 37.210 2.4183 12.822 39.964 2.2559 1.823 42.093 2.1466 3.924 44.719 2.0265 99.425 46.642 1.9473 3.826 47.382 1.9186 31.627 50.234 1.8162 14.128 52.881 1.7313 1.529 53.697 1.7069 4.730 54.224 1.6916 2.431 54.917 1.6719 3.632 56.343 1.6329 1.933 56.797 1.6209 3.634 57.524 1.6021 0.935 58.423 1.5796 1.6______________________________________ TABLE 3______________________________________NO 2 THETA D-space INTEG.I (%)______________________________________1 7.231 12.21443 6.12 14.363 6.16182 8.23 16.783 5.27810 8.34 19.324 4.58947 14.15 21.703 4.09147 8.56 23.570 3.77145 6.47 24.696 3.60198 6.18 25.753 3.45652 61.29 27.327 3.26082 6.210 28.700 3.10796 10.311 29.002 3.07624 48.612 29.675 3.00800 100.013 30.202 2.95671 9.614 30.553 2.92351 8.615 31.856 2.80687 13.616 32.057 2.78974 6.217 32.674 2.73843 6.318 32.917 2.71878 25.619 33.216 2.69494 53.020 34.491 2.59820 9.721 34.737 2.58039 8.722 35.681 2.51426 8.323 35.990 2.49334 7.924 36.376 2.46778 10.625 37.231 2.41303 7.226 42.002 2.14932 13.227 44.645 2.02803 14.228 47.340 1.91868 9.729 47.662 1.90646 19.730 51.393 1.77645 7.231 51.789 1.76380 12.632 52.047 1.75566 7.233 53.148 1.72185 6.834 54.943 1.66978 8.535 56.669 1.62296 8.336 56.861 1.61791 6.537 57.072 1.61243 10.538 57.408 1.60379 6.039 57.713 1.59604 6.640 60.004 1.54048 8.8______________________________________

Claims

1. A process for preparing a superconducting compound having essentially the overall composition

Bi.sub.4 (Ca,Sr).sub.4+2n Cu.sub.2+2n O.sub.x

where n is 2 and x, which varies with the conditions of said process, is greater than 16 but not greater than 16+4n,

said process comprising:

preparing an initial mixture containing the oxides or oxide precursors of bismuth, calcium, strontium, and copper in the atomic ratios necessary to form said superconducting compound,

heating the resulting mixture to a temperature within the range of between 700.degree. C. and 900.degree. C. so that the mixture is not melted or is only partially melted, and keeping the mixture in this temperature range for at least 100 hours,

cooling the mixture, and

obtaining a superconducting compound having a principal phase which crystallizes in the orthorhombic system and a transition temperature T.sub.c for the superconductivity of at least 70K.

2. A process for preparing a superconducting substance having essentially the overall composition

Bi.sub.a (Sr, Ca).sub.b Cu.sub.6 O.sub.x

wherein

a=3 to 12,

b=6 to 12, and

x varies with the conditions of the process, with an atomic ratio Sr/Ca of 1:9 to 9:1, an atomic ratio Bi:(Sr+Ca) of 0.3 to 1.3,

said superconducting substance having a principal phase which crystallizes in the orthorhombic system and a transition temperature T.sub.c for the superconductivity of at least 70 K, said process comprising:

preparing an initial mixture containing the oxides or oxide precursors of bismuth, calcium, strontium, and copper in the atomic ratios necessary to form said superconducting substance,

heating the resulting mixture to a temperature in the range of between 700.degree. C. and 900.degree. C. so that the mixture is not melted or is only partially melted, and keeping the mixture in this temperature range for at least 100 hours, and cooling the mixture.

3. The process as claimed in claim 2, wherein salts of bismuth, calcium, strontium and copper, of which at least one is water-soluble, are mixed in the presence of an aqueous phase, the mixture is evaporated down and heated.

4. The process as claimed in claim 3, wherein at least one metal hydroxide is precipitated by adding a base to the mixture of the salts in the presence of an aqueous phase, and the insoluble component is separated off, dried and heated.

5. The process as claimed in claim 3, wherein the salts used are derived from readily volatile acids.

6. The process as claimed in claim 2, wherein the initial mixture is heated to a temperature of at least 800.degree. C., but so that the mixture is not melted, in an atmosphere containing oxygen.

7. The process as claimed in claim 2, wherein the heating is carried out in an oxygen-containing atmosphere.

8. The process as claimed in claim 2, wherein, after the heating process, the resulting product is subjected to a post treatment by heating in the temperature range of 300.degree. to 750.degree. C.

9. The process as claimed in claim 8, wherein said post treatment is carried out in the temperature range of 400.degree. to 600.degree. C.

10. The process as claimed in claim 8, wherein the post treatment is carried out in an oxygen-containing gas.

11. The process as claimed in claim 2, wherein the mixture is annealed after said heating step.

12. The process as claimed in claim 11, wherein the annealed mixture is comminuted, mixed, and again heated in a temperature range of 300.degree. to 900.degree. C.

13. The process as claimed in claim 2, wherein the heating or the cooling, or both the heating and cooling, are carried out in an oxygen-containing atmosphere.

14. The process as claimed in claim 2, wherein the mixture is heated for 120 hours.

15. The process as claimed in claim 2, wherein said superconducting substance is a compound and has essentially the overall composition

Bi.sub.4 (Ca,Sr).sub.4+2n Cu.sub.2+2n O.sub.x

where n is 2, 3, 4, or 5, and x, which varies with the conditions of said process, is greater than 16 but not greater than 16+4n.

16. The process as claimed in claim 15, wherein the initial mixture is heated to a temperature of at least 800.degree. C., so that the mixture is not melted in an atmosphere containing oxygen.

17. The process as claimed in claim 15, wherein said superconducting substance is a compound having lattice constants a=5.41.times.10.sup.-8 cm, b=5.47.times.10.sup.-8 cm, and c=(24.5+n.times.6.3).times.10.sup.-8 cm, where n is as defined in claim 15.

18. The process as claimed in claim 15, wherein the heating is carried out in an oxygen-containing atmosphere.