Patent Application
20130228278
The present invention relates generally to methods of making laminated film articles, apparatus for making laminated film articles, and more particularly, to apparatus and methods for making laminated film articles having inflatable chambers and channels.
Conventional cushion materials include thermoformed sealed laminate articles to such as Bubble Wrap® cushioning material. However, it is also known to prepare laminated inflatable articles which can be shipped to a packer uninflated, and inflated immediately before use. Such inflatable articles are typically made from two heat sealable films which are fused together in discrete areas to form one or more inflatable chambers.
Conventional methods of making cushion material, such as Bubble Wrap® cushioning material, use a vacuum source to deform polymer film to form bubbles or pockets that can be filled with air (or other gases) to form bubbles. Such products can be made using a heated drum having recesses that are connected to a vacuum source. When vacuum is applied, each of various regions of the heated film in contact with the drum is drawn into a recess on the drum. The heated film is deformed and thinned in the regions drawn into the recess by the vacuum process. One side of the resulting film remains “flat”, while the other side is not flat, but rather is “thermoformed”. A second film, which preferably is a flat film, i.e., not thermoformed, is fused to the “flat side” of the formed film, resulting in a plurality of sealed, air-filled “bubbles.”
The present invention provides a method of making an inflatable article at relatively high speed, by bringing a first film into contact with a second film and heating selected portions of at least one the first and second films to a temperature above a fusion temperature of the first and second films, so that the first and second films are heat sealed to one another to produce a laminated article. The sealing forms a heat seal pattern which provides a plurality of inflatable chambers between the first film and the second film. The first and second films are forwarded at a speed of at least 120 feet per minute while coming into contact with one another. The heating is carried out by contacting the first film with a heated raised surface roller having a release coating thereon. At least the seal layers of one or both of the films are heated to a temperature at or above a temperature at which the one or more of the seal layers will fuse. Preferably, the raised surface roller rotates at a speed which matches the speed at which the first and second films are being forwarded. Preferably, the raised surface roller has a surface roughness of from 50 to 500 rms. Preferably, the first and second films are heat sealed to one another under a combination of heat and pressure.
Preferably, the pressure is produced by means for forming a nip area. The means for forming a nip area includes not only nip rolls, but also gas and fluid impingement, film tensioning against the raised surface roller, and electrostatic nip, as disclosed in U.S. Pat. No. 5,116,444, to John G. Fox, which is hereby incorporated, in its entirety, by reference thereto. Preferably, the means for forming a nip area is a contact roller in a nip relationship with the raised surface roller.
Preferably, the first film is brought into contact with the raised surface roller and heated to the fusion temperature before passing through the nip area. Preferably, the release coating on the raised surface roller comprises a polymer. Preferably, the release coating is a polyinfused coating. Preferably, the polyinfused coating comprises polytetrafluoroethylene. Preferably, the edges of the raised surface of the raised surface roller have a radius of curvature of from 1/256 inch to ⅜ inch.
Preferably, the process further comprises cooling the first and second films after heating the selected portions of the films, the cooling being carried out by a means for cooling. The means for cooling can be, for example, ambient air impingement, refrigerated air impingement, forwarding the film through ambient for a time period long enough to effect cooling, contact with fluid (preferably water), radiative cooling, etc. Preferably, the means for cooling comprises bringing the first film or the second film into contact with a cooling roller. Preferably, the cooling roller has a Shore A hardness of from 40 to 100. Preferably, the cooling roller also has a release coating thereon, as well as a composition which increases the rate of heat transfer through the release coating on the cooling roller.
In the process of the present invention, preferably both the first film and the second film are provided from first and second rolls of film (i.e., rollstocks), respectively. Alternatively, a double-wide flat film (or a double-wide seamless film tubing) on a single roll can be unwound and slit to provide both the first film and the second film. A flat film can be centerfolded, with one side (i.e., “leaf”) being the first film, and the other side being the second film, with the first and second films being connected by the centerfold line before being brought into contact with one another. The double-wide seamless film tubing, prepared by extrusion from an annular die, can likewise be slit open along one edge, in order to provide the equivalent of the centerfolded film described above.
Alternatively, either the first film or the second film can be supplied directly from an extrusion process, with the other film being provided from a rollstock. It is preferred that any film(s) provided from rollstock are stress relaxed by a means for stress relaxation, i.e., a means for annealing. Preferably, the means for stress relaxation is performed immediately upon unwinding the film from the rollstock but before contacting the first and second films together. Preferably, the means for stress relaxation heats the part of all of the film to a temperature above a Vicat softening point of but below a glass transition temperature, so that the film is de-stressed. Stress relief provides the film(s) with enhanced flatness so that the film lies smoothly on the raised surface roller, and so that the films are flat relative to one another in order to improve the uniformity of the desired film-to-film contact during downstream processing.
In one embodiment, the contacting of the first film with the second film is carried out before heating either film, i.e., while forwarding the first film and second film together at the same speed, upstream of the raised surface roller. In another embodiment, a selected portion(s) of the first film is heated before the first and second films come into contact with one another. This can be done by having the first film contact the raised surface roller before the first film contacts the second film, so that film-to-film contact and heat sealing are nearly simultaneous. During heat sealing, preferably heat and pressure are applied simultaneously.
Heating sealing is preferably performed by passing the first and second films together through a nip between a first roll (herein referred to as the “raised surface roller”) and a second roll (herein referred to a the “contact roller”), with at least one of the rolls having a patterned raised surface and at least one of the pair of rolls being heated. The raised surface roller has the patterned raised surface. Preferably the raised surface roller is heated and the contact roller is not heated. Alternatively, if both the first roll as well as the second roll can be provided with a raised surface (and alternatively, both can also be heated), in which case the raised surfaces of the first and second rolls are operatively aligned, so that together they can effect a heat-sealing of the selected portion of the first film to the selected portion of the second film. Preferably, each roll with a raised surface has a continuous raised surface so that the nip between the first and second rolls is maintained throughout rotation of the first and second rolls, without further means to maintain the nip. A continuous nip ensures continuous forwarding of the first and second films. If a roll does not have a raised surface, preferably such roll has a smooth continuous surface to ensure that the nip is maintained throughout rotation of the roll. Alternatively, means can be provided to maintain the nip between irregular rolls and between rolls having discontinuous raised surfaces, such as overlapping raised surfaces, and/or a resilient surface on one or more of the rolls, and/or a roll on a moveable axis with force continuously urging the rolls into contact with one another despite irregularities. Preferably, the first and second films are heat sealed to one another in a repeating pattern which results in one or more sealed areas in combination with one or more unsealed areas.
The numerous features and advantages of the present invention are better understood by those skilled in the art by reference to the accompanying detailed description and the following drawings, in which:
In the process of the present invention, an inflatable article is made from either two discrete films, a tubular film which is slit, or a folded flat film. The films are sealed to one another in selected seal regions, forming a pattern of sealed and unsealed areas, the latter of which define chambers, inflation channels, connecting passageways, an inflation skirt, and optionally one or more inflation manifolds that can be inflated, thereby ultimately (i.e., upon inflation and sealing to entrap the inflation gas or fluid) providing cushioning pockets or bubbles within the laminate. The invention is used to fabricate laminate materials from polymeric resins in a one stage process that eliminates disadvantages associated with multiple stage processes.
In the
The raised surface of raised surface roller 16 heats that portion of film 8 which contacts the raised surface of roller 16. Heat is transferred from the raised surface of roller 16, through a heated portion of film 8, eventually heating through to a corresponding portion of film 10 to be heat sealed to film 8. Upon passing about 180 degrees around raised surface roller 16, heated films 8 and 10 together pass through second nip 19, which subjects heated films 8 and 10 to about the same pressure as is exerted in first nip 17, resulting in a patterned heat seal between films 8 and 10. Preferably, nips 17 and 19 each subject films 8 and 10 to a pressure of from 2 to 10 pounds per linear inch, more preferably 2 to 6 pounds per linear inch, more preferably about 4 pounds per linear inch.
Raised surface roller 16 comprises raised surfaces 24, recesses 25, and recessed surfaces 26. Raised surface roller 16 is a heat transfer roller. Raised surface roller 16 preferably has a diameter of 12 inches and is preferably heated by circulating hot oil therethrough so that the surface is maintained at a temperature of from 280° F. to 350° F., with the edges of its raised surfaces being rounded over to a radius of 1/64 inch.
In order to carry out the process at relatively high speed, e.g., a speed of at least 120 feet per minute, preferably from 150 to 300 feet per minute, but up to as high as 500 feet per minute, it has been found to be important to provide the manufacturing apparatus with several features. First, the raised surface roller should be provided with a release coating or layer. The release coating reduces adherence with film 12 while film 12 contacts raised surface roller 16, and particularly when film 12 releases from roller 16. At least a portion of release coating 28 is infused with one or more polymers. The polymer infused can be any conventional polymer used for reducing adherence to polymer films, for example, Teflon® polytetrafluoroethylene. Raised surface roller 16 can be infused by any conventional infusion process. As used herein, the phrase “release coating” is inclusive of all release coatings and layers, including polyinfused coatings, applied coatings such as brushed and sprayed coatings which cure on the roll, and even a release tape adhered to the roll.
A preferred release coating composition comprises Teflon® polytetrafluoroethylene. More particularly, raised surface roller 16 has an infused Teflon® polytetrafluoroethylene coating thereon (i.e., a polyinfused coating, which was a SF-2R coating {less preferably, an SFX coating}) prepared by General Magnaplate, at 1331 US 1, Linden, N.J., 07036, with the raised surface(s) being above the background by a distance of ¼ inch (0.64 cm).
Preferably, the raised surface of roller 16 is also textured to reduce adherence to polymer films. More particularly, the raised surface of raised surface roller 16 is provided with a surface roughness of from 50 to 500 root mean square (i.e., “rms”), preferably 100 to 300 rms, more preferably about 250 rms. This degree of roughness improves the release qualities of raised surface roller 16, enabling faster process speeds and a high quality product which is undamaged by licking back on roll 16.
Films 8 and 10 preferably contact raised surface roller 16 for a distance of about 180 degrees. The edges of the raised surfaces should be rounded off to a radius large enough that the film readily releases without snagging on an edge due to its “sharpness” relative to the softened film, and to prevent damage to the hot films during passage through a nip between the raised surface roller and the contact roller and especially when passing through a nip between the raised surface roller and the cooling roller. Preferably, the radius of curvature on the edges of the raised surface is from 1/256 inch to ⅜ inch, more preferably from 1/128 inch to 1/16 inch, more preferably from 1/100 inch to 1/32 inch, and more preferably about 1/64 inch, i.e., about 0.04 cm.
Contact roller 15 applies pressure to films 8 and 10 as they pass through nip 17. The present invention is not limited to contact roller 15, but rather encompasses other contact surfaces formed on other apparatus, such as a planer surfaces, curved surfaces, or portion of a clamp, as will be understood by persons familiar with film processing technology in view of the present disclosure. Preferably, contact roller 15 has an elastic outer coating 13 comprising rubber. Preferably, elastic outer coating 13 provides roller 15 has a Shore A. hardness of from 50 to 110, more preferably from 55 to 85, more preferably from 60 to 80, more preferably about 70. Alternatively, contact roller 15 has a release coating thereon, which preferably comprises polytetrafluoroethylene.
Contact roller 15 applies pressure to films 8 and 10 as they pass through nip 17. The present invention is not limited to contact roller 15, but rather encompasses other contact surfaces formed on other apparatus, such as a planer surfaces, curved surfaces, or portion of a clamp, as will be understood by persons familiar with film processing technology in view of the present disclosure.
It is also important to provide the cooling roller downstream of and in nip relationship with the raised surface roller, with a release coating or layer, as described above. Preferably, the cooling roller is maintained at a temperature below the fusing temperatures of films, using conventional cooling techniques. The cooling roller solidifies the heated portions of the first and second films. The present invention is not limited to one cooling roller 18, but rather further encompasses the use of two or more cooling rollers in the process, i.e., downstream of the heated raised surface roller 16. Moreover, any suitable means for cooling could be used in place of one or more cooling rollers, such as cooled planer surfaces, cooled curved surfaces, cooled clamping surfaces of any shape, cool fluids and gases, etc., as will be understood by persons of skill in the art of film manufacture and processing.
The cooling roller lowers the temperature of the selected heated portions of the laminate, in order to cool the heat seals so that they become strong enough to undergo further processing without being damaged or weakened. Moreover, the means for cooling is preferably immediately downstream of the heating means (i.e., the raised surface roller), in order to reduce heat seepage from the still-hot seals to unheated portions of film, to prevent unheated portions of laminated article from becoming hot enough to fuse the films in an area intended to serve as an inflation chamber or inflation passageway.
Preferably, films 8 and 10 make a partial wrap of about 90 degrees around heat transfer roller 18 (i.e., a cooling roller), which has a diameter of 12 inches and which has cooling water passing therethrough, the cooling water having a temperature of from 100° F. to 150° F. Preferably, cooling roller 18 has a ¼ inch thick (about 0.64 cm thick) release and heat-transfer coating thereon (not illustrated). The coating is made from a composition designated as “Thermosil® 70 Brown”, which was provided and applied to a metal roller by United Silicone of Lancaster, N.Y. The coating contained silicone rubber to provide cooling roller 74 with a Shore A hardness of from 50 to 110, preferably 55-85, more preferably 60-80, and still more preferably about 70. The Thermosil® 70 Brown to composition also contained one or more fillers to increase the heat conductivity to improve the ability of cooling roller 18 to cool the still hot films, now sealed together to result in inflatable article 20, which was thereafter rolled up to form a roll for shipment and subsequent inflation and sealing, to result in a cushioning article.
Although cooling step 6 can be passive (e.g., in that the heat seals are simply allowed to cool by giving off heat to the ambient environment), it is preferably active in order to quickly cool the heat seals immediately after formation, so that the heat seal is not damaged or weakened by continued processing. Preferred cooling means are as described above.
The process can be further assisted by an apparatus capable of adjusting the temperature of films to maximize film fabrication speeds. Optionally, one or more transfer rollers (not illustrated) can be used between roll 6 and raised surface roller 16, as well as between roll 12 and raised surface roller 16. The transfer rolls can be at ambient temperature or optionally can be heated or cooled in order to preheat or cool the film(s) before contact with raised surface roll 16 or one another. Preheating of film from a rollstock can assist in fast heat sealing. Cooling of a films provided via extrusion (vs. rollstock) can assist in downstream processing by quickly bringing the film down to (or below) a temperature suitable for passage through nip 17 and formation of the heat seal.
The present invention is inclusive of the heat-sealing of two monolayer films to one another, heat sealing a multilayer film to a monolayer film, and heat sealing two multilayer films to one another.
The methods and apparatus of the present invention can be operated at a higher output than conventional processes, including for example film outputs of more than 250 feet in length of film per minute. In addition, the methods produce larger width films than conventional processes, including for example, widths greater than 36 inches. The increase in film width and in rate of film produced thereby permits an increase in the surface area of laminated material produced more efficiently and at lower cost compared to conventional methods.
The methods of the present invention have an advantage over conventional methods of making protective laminates and bubble film because the present methods do not require thermoforming of the structure of the laminate material during the heat sealing process by vacuum stretching the films. However, the present invention is not limited to methods that do not distort and/or deform the films, but rather encompasses conventional vacuum stretching techniques as will be understood by persons familiar with film processing technology in view of the present disclosure.
Raised surfaces 24 and recessed surfaces 26 form a patterned heat seal 27 in laminate material 20 as explained more fully above with reference to
In an alternative embodiment of the present invention (not illustrated), contact roller 15 has raised surfaces that correspond to raised surfaces 24. Contact roller 15 has recesses and recessed surfaces that correspond with recesses 25 and recessed surfaces 26.
The term “nip” as used herein refers to a contact area between two rollers. First film 8 and second film 10 are in contact as they pass though nip 17. As first and second films 8 and 12 pass through nip 17, heat and/or pressure are applied to selected portions of first and second films 8 and 10, fusing the films together to form patterned heat seals schematically illustrated as 27 in
First and second films 8 and 10 can be monolayer films, or multilayer films. If multilayer, they can be coextruded through annular or slot dies, extrusion coated, and can be produced by cast or blown film processes. In one embodiment, first and second films 8 and 10 are toughened by crosslinking via chemical cross-linking or irradiation techniques known to those of skill in the art.
The process and apparatus illustrated in
The films referred to herein preferably comprise a polyolefin, such as for example a low density polyethylene, a homogeneous ethylene/alpha-olefin copolymer (preferably a metallocene-catalyzed ethylene/alpha-olefin copolymer), a medium density polyethylene, a high density polyethylene, a polyethylene terapthalate, polypropylene, nylon, polyvinylidene chloride (especially methyl acrylate and vinyl chloride copolymers of vinylidene chloride), polyvinyl alcohol, polyamide, or combinations thereof.
Preferably, laminate materials 20 are as thin as possible, in order to minimize the amount of resin necessary to fabricate laminate materials 20, but at the same time are thick enough to provide adequate durability. Preferably, each of first and second films 8 and 10 has a gauge thickness of from about 0.1 to about 20 mils. More preferably, each film layer has a total gauge thickness from about 0.5 to about 10 mils, more preferably from about 0.8 to about 4 mils, and even more preferably from about 1.0 to about 3 mils.
If desired or necessary, various additives are also included with the films. For example, additives comprise pigments, colorants, fillers, antioxidants, flame retardants, anti-bacterial agents, anti-static agents, stabilizers, fragrances, odor masking agents, anti-blocking agents, slip agents, and the like. Thus, the present invention encompasses employing suitable film constituents.
Preferably first and second films 8 and 10 are hot blown films having an A/B/C/B/A structure which has a total thickness of 1.5 mils. The A layers together make up 86 percent of the total thickness, each of the B layers making up 2% of the total thickness, and the C layer making up 10% of the total thickness. The C layer is an O2-barrier layer of 100% Caplon® B100WP polyamide 6 having a viscosity of Fav=100, obtained from Allied Chemical. Each of the B layers are tie layers made of 100% Plexar® PX165 anhydride modified ethylene copolymer from Qunatum Chemical. Each of the A layers are a blend of 45% by weight HCX002 linear low density polyethylene having a density of 0.941 g/cc and a melt index of 4, obtained from Mobil, 45% by weight LF 10218 low density polyethylene having a density of 0.918 g/cc and a melt index of 2, obtained from Nova, and 10% by weight SLX9103 metallocene-catalyzed ethylene/alpha-olefin copolymer, obtained from Exxon.
The laminates formed according to the present invention will resist popping when pressure is applied to a localized area because channels of air between chambers provide a cushioning effect. The laminates also show excellent creep resistance and cushioning properties due to inter-passage of air between bubbles.
The various terms and phrases utilized throughout this document are to be given their ordinary meaning as understood by those of skill in the art, except and to the extent that any term or phrase used herein is referred to and/or elaborated upon in U.S. Pat. No. 5,837,335, to Babrowicz, entitled High Shrink Multilayer Film which Maintains Optics upon Shrinking, issued Nov. 17, 1998, which is hereby incorporated in its entirety by reference thereto, and which supplements the ordinary meaning of all terms, phrases, and other descriptions set forth herein.
In the figures and specification, there have been disclosed preferred embodiments of the invention. All sub-ranges of all ranges disclosed are included in the invention and are hereby expressly disclosed. While specific terms are employed, they are used in a generic and descriptive sense only, and not for the purpose of limiting the scope of the invention being set forth in the following claims.
Those skilled in the art will appreciate that numerous changes and modifications may be made to the embodiments described herein, and that such changes and modifications may be made without departing from the spirit of the invention.