Patent Grant
9797058
This is a §371 US National Stage Application of International Application No. PCT/EP2013/056780 filed on Mar. 28, 2013, claiming the priority of European Patent Application No. 12162441.5 filed on Mar. 30, 2012.
This invention relates to a process for manufacturing a recovery annealed coated steel substrate for packaging applications and a packaging steel product produced thereby.
Packaging steel is generally provided as single or double reduced tin mill products in thicknesses between 0.14 and 0.49 mm. A Single Reduced (SR) tin mill product is cold rolled directly to the finished gauge and then recrystallisation annealed. Recrystallisation is brought about by continuous annealing or batch annealing the cold rolled material. After annealing the material is usually temper rolled, typically by applying a thickness reduction of 1-2%, to improve the properties of the material. A Double Reduced (DR) tin mill product is given a first cold reduction to reach an intermediate gauge, recrystallisation annealed and then given another cold reduction to the final gauge. The resulting DR product is stiffer, harder, and stronger than SR, allowing customers to utilise lighter gauge steel in their application. These uncoated, cold rolled, recrystallisation annealed and optionally temper-rolled SR and DR packaging steels are referred to as blackplate. The first and second cold reduction may be given in the form of a cold rolling reduction in a cold-rolling tandem mill usually comprising a plurality of (usually 4 or 5) rolling stands.
Recovery Annealing (RA) is a cost effective method to produce packaging steels at a strength level comparable to Double Reduced (DR) grades, but with a better formability and notably elongation values. There are three stages in the annealing process, with the first being the recovery phase, which results in softening of the metal through a partial removal of crystal defects (the primary type of which are dislocations) and the decrease of the stored energy introduced during the deformation. Recovery phase covers all annealing phenomena that occur before the appearance of new strain-free grains. The second phase is recrystallisation, where new grains with high angle boundary nucleate and grow at the expense of grains with high stored energy. This is to be avoided in the process and product according to the invention because it leads to a sudden and dramatic decrease of the tensile properties and increase of the elongation values. The third stage is grain growth after recrystallisation.
Unfortunately a drawback of RA is that mechanical properties are usually non-homogeneous along the strip length and also from strip to strip. These variations in mechanical properties are the consequences of too dynamic a response of the grade and/or fluctuations of the temperature of the annealing furnace.
It is an object of the invention to provide better control of the recovery annealing conditions.
It is also an object of the invention to provide recovery annealed material with reproducible properties.
It is also an object of the invention to provide a more cost effective high strength steel for packaging purposes, which has a corrosion resistant outer surface.
One or more of these objects is reached by a process for manufacturing a recovery annealed coated steel substrate for packaging applications, comprising the steps of:
The conversion of the tin layer into an iron-tin alloy layer which contains at least 80 weight percent (wt. %) of FeSn (50 at. % iron and 50 at. % tin) implies that there is no unalloyed tin remaining on the substrate.
The invention is also embodied in a packaging steel product, such as a can, a can lid or a can bottom, comprising a low-carbon, an extra-low-carbon or an ultra-low carbon steel substrate provided on one or both sides with an iron-tin alloy layer which contains at least 80 weight percent (wt. %) of FeSn (50 at. % iron and 50 at. % tin) wherein the iron-tin alloy layer was produced by providing the substrate on the said one or both sides of the substrate with a tin layer followed by an annealing step at a temperature Ta of at least 513° C. for an annealing time ta to form the iron-tin alloy layer and wherein the annealing step simultaneously provides a recovery annealed substrate, followed by fast cooling of the annealed substrate.
Preferred embodiments are provided in the dependent claims.
In the process according to the invention a steel slab or strip suitable for producing a low-carbon, an extra-low-carbon or an ultra-low-carbon hot rolled strip for producing packaging steel by hot rolling at a finishing temperature higher than or equal to the Ar3 transformation point is provided. A low-carbon steel in the context of this invention has a carbon content of at most 0.05%, an extra-low-carbon steel has a carbon content of at most 0.02%, and an ultra-low-carbon has a carbon content of at most 0.003%. In an embodiment of the invention the steel is an interstitial free steel, preferably an ultra-low-carbon. In these steels the interstitial elements carbon and nitrogen are bound to elements like niobium.
The hot rolled steel is cold rolled to produce a single reduced (SR) steel substrate.
On the cold rolled, full-hard substrates, a layer of tin is subsequently deposited. The substrates are called full-hard substrates because the SR-substrate has not undergone a recrystallisation annealing after cold rolling step. So the microstructure of the substrate is still heavily deformed.
After the tinplating the tin-coated steel substrate is annealed at a temperature Ta of at least 513° C. for an annealing time ta to convert the tin layer into an iron-tin alloy layer which contains at least 80 weight percent (wt. %) of FeSn (50 at. % iron and 50 at. % tin), and to simultaneously obtain a recovered microstructure and wherein no recrystallisation of the single reduced substrate takes place (i.e. recovery annealing). After this combined diffusion/recovery annealing the annealed substrate is cooled rapidly.
The temperature Ta and the annealing time ta are relatively high and short, so that the diffusion annealing takes place while simultaneously recovery annealing the substrate. The reduction in tensile strength and yield strength remains limited due to the short annealing time, but the recovery effect generates a significant increase in elongation values. The process parameters are controlled very carefully because the time-temperature process window for diffusion annealing is critical in terms of obtaining the desired amounts of FeSn (50:50) in the diffusion alloy layer. As it is this layer that provides the corrosion protection, the control of these parameters is critical. This degree of control of the T-t-profile also ensures that the recovery process, which is a thermally activated process, is reproducible over the length and width of the strip, and from strip to strip.
The term ‘recovered microstructure’ is understood to mean a heat treated cold rolled microstructure which shows minimal or no recrystallisation, with such eventual recrystallisation being confined to localised areas such as at the edges of the strip. Preferably the microstructure is completely unrecrystallised. The microstructure of the packaging steel is therefore substantially or completely unrecrystallised. This recovered microstructure provides the steel with a significantly increased deformation capability at the expense of a limited decrease in strength.
The inventors found that is necessary to diffusion anneal a tin coated steel substrate at a temperature (Ta) of at least 513° C. to obtain the desired iron-tin coating layer. The diffusion annealing time (ta) at the diffusion annealing temperature Ta is chosen such that the conversion of the tin layer into the iron-tin layer is obtained. The predominant and preferably sole iron-tin alloy component in the iron-tin layer is FeSn (i.e. 50 atomic percent (at. %) iron and 50 at. % tin). It should be noted that the combination of diffusion annealing time and temperature are interchangeable to a certain extent. A high Ta and a short ta will result in the formation of the same iron-tin alloy layer than a lower Ta and a longer ta. The minimum Ta of 513° C. is required, because at lower temperatures the desired (50:50) FeSn layer does not form. Also the diffusion annealing does not have to proceed at a constant temperature, but the temperature profile can also be such that a peak temperature is reached. It is important that the minimum temperature of 513° C. is maintained for a sufficiently long time to achieve the desired amount of FeSn in the iron-tin diffusion layer. So the diffusion annealing may take place at a constant temperature Ta for a certain period of time, or the diffusion annealing may, e.g., involve a peak metal temperature of Ta. In the latter case the diffusion annealing temperature is not constant. It was found to be preferable to use a diffusion annealing temperature Ta of between 513 and 645° C., preferably of between 513 and 625° C. At a lower Ta the recovery process proceeds more slowly. The maximum temperature is limited by the window for forming FeSn and by the recrystallisation temperature of the deformed substrate.
In an embodiment of the invention, the maximum annealing temperature is limited to 625° C., and preferably the maximum annealing temperature is limited to 615° C.
The inventors found the highest FeSn content in the iron-tin alloy layer was obtained when the annealing temperature was chosen to be at least 550° C.
In a preferred embodiment a process for producing a coated substrate for packaging is provided wherein the time at Ta is at most 4 seconds, preferably at most 2 seconds, and more preferably wherein there is no dwell time at Ta. In the latter case the diffusion annealing takes place by heating the substrate to the peak metal temperature of Ta after which the substrate is cooled. The short dwell time at Ta allows the production of the iron-tin alloy layer in an appropriately modified conventional tinplating line. Careful control of these parameters ensures a reproducible recovery annealing process.
The mechanical properties of recovery annealed steel depend on the composition of the grade, the cold rolling reduction and the difference between the recovery annealing temperature and the recrystallisation temperature. Therefore, the final mechanical properties can be controlled in principle by limiting the release of the stored energy by choosing the right annealing cycle. More particularly, between steel sheets made from the same grade and having the same processing history (hot rolling, cold rolling reduction) and equivalent annealing cycles the release of the stored energy can be estimated using the following formula:
M=(Ta+273)(log ta+20)×10−3
where Ta is in ° C. Steel sheets with a similar M coefficient will have similar mechanical properties. By selecting the correct values for Ta and ta the desired properties of the recovery annealed substrate and the iron-tin alloy layer can be determined.
In a preferred embodiment the iron-tin alloy layer contains at least 85 wt. % of FeSn, preferably at least 90 wt. %, more preferably at least 95 wt. %. The FeSn layer is a layer fully covering the substrate surface. The higher the fraction of FeSn, the better the corrosion protection of the substrate will be. Although ideally the iron-tin alloy layer consists of FeSn only, it appears to be difficult to prevent the presence of very small fractions of other compounds such as α-Sn, β-Sn, Fe3Sn or oxides. However, these small fractions of other compounds have been found to have no impact on the product performance in any way. It must be noted that there are no other FexSny-layers present but the FeSn layer on the substrate. There is also no unalloyed tin remaining on the substrate.
The time at Ta may not exceed a critical time to avoid the onset of recrystallisation. In a preferred embodiment a process for producing a coated substrate for packaging is provided wherein the time at Ta is at most 4 seconds, preferably at most 2 seconds, and more preferably wherein there is no dwell time at Ta. In the latter case the diffusion annealing takes place by heating the substrate to the peak metal temperature of Ta after which the substrate is cooled. The short dwell time at Ta allows the production of the iron-tin alloy layer with a recovered substrate in an appropriately modified conventional tinplating line and, in addition, the recrystallisation of the deformed substrate is prevented.
In an embodiment of the invention the iron-tin alloy layer or layers are provided with a chromium metal—chromium oxide coating layer produced by a trivalent chromium electroplating process as described in the co-pending application (EP12162415.9).
In an embodiment of the invention a process is provided wherein the annealing is performed in a reducing gas atmosphere, such as HNX, while keeping the coated substrate in a reducing or inert gas atmosphere prior to cooling using non-oxidising or mildly oxidising cooling medium, so as to obtain a robust, stable surface oxide.
In an embodiment of the invention the fast cooling after diffusion/recovery annealing is achieved by means of quenching with water, wherein the water used for quenching has a temperature between room temperature and its boiling temperature. It is important to maintain a homogeneous cooling rate over the strip width during cooling to eliminate the risks of the strip getting deformed due to cooling buckling. This can be achieved by applying cooling water through a (submerged) spray system that aims to create an even cooling pattern on the strip surface. To ensure a homogeneous cooling rate during spraying it is preferred to use cooling water with a temperature between room temperature and 60° C. to prevent that the water reaches boiling temperatures upon contact with the hot steel strip. The latter can result in the onset of localized (unstable) film boiling effects that can lead to uneven cooling rates over the surface of the steel strip, potentially leading to the formation of cooling buckles.
In an embodiment of the invention the annealing process comprises i) the use of a heating unit able to generate a heating rate preferably exceeding 300° C./s, like an inductive heating unit, in a hydrogen containing atmosphere such as HNX, and/or ii) followed by a heat soak which is kept at the annealing temperature to homogenise the temperature distribution across the width of the strip, and/or iii) wherein the cooling is preferably performed in an reducing gas atmosphere such as a HNX atmosphere, and/or iv) the cooling is preferably performed by means of water quenching, by using (submerged) spraying nozzles, wherein the water used for quenching has a minimal dissolved oxygen content and has a temperature between room temperature and 60° C., while keeping the substrate with the iron-tin alloy layer(s) shielded from oxygen by maintaining an inert or reducing gas atmosphere, such as HNX gas, prior to quenching.
In an embodiment of the invention the coating weight of the tin layer or layers onto one or both sides of the substrate is at least 100 and/or at most 600 mg/m2 of substrate surface.
In an embodiment of the invention the steel comprises (in weight. %):
In a preferred embodiment of the invention the carbon content is at most 0.02%, preferably at most 0.003%, and/or the niobium content is at least 0.02 and/or at most 0.08%, and/or the manganese content is at least 0.2 and/or at most 0.4%. Preferably the niobium content is at least 0.03 and/or at most 0.06%.
By choosing a carbon content of 0.003 or lower and a suitably high niobium content, the steel becomes interstitial free, meaning that the carbon and nitrogen in the steel become attached to niobium. This results in a steel of which the properties are not affected by the ageing phenomenon. Interstitial atoms, such as carbon and nitrogen, have a marked effect on the deformation behaviour of steel. Discontinuous yielding in steel is strongly related to interstitials and may result in Luders bands, which are detrimental to surface appearance, and may also promote premature breakage during forming or non-uniform springback after deformation. In order to combat the detrimental effects of interstitial species, interstitial-free steels are essentially devoid of solute carbon and nitrogen. These “interstitial-free” steels predominantly rely upon the solid state precipitation of carbides, nitrides, and carbosulfides to reduce the solute interstitial content. Additionally, the total carbon and nitrogen contents are reduced to extremely low levels, typically less than 0.003 weight percent carbon and less than 0.006 weight percent nitrogen through modern steelmaking techniques.
In an embodiment the coated substrate is further provided with an organic coating, consisting of either a thermoset organic coating, or a thermoplastic single layer coating, or a thermoplastic multi-layer polymer coating.
In a preferred embodiment the thermoplastic polymer coating is a polymer coating system comprising one or more layers comprising the use of thermoplastic resins such as polyesters or polyolefins, but can also include acrylic resins, polyamides, polyvinyl chloride, fluorocarbon resins, polycarbonates, styrene type resins, ABS resins, chlorinated polyethers, ionomers, urethane resins and functionalised polymers. For clarification:
Mixtures of two or more resins can be used. Further, the resin may be mixed with anti-oxidant, heat stabiliser, UV absorbent, plasticiser, pigment, nucleating agent, antistatic agent, release agent, anti-blocking agent, etc. The use of such thermoplastic polymer coating systems have shown to provide excellent performance in can-making and use of the can, such as shelf-life.
According to a second aspect a packaging steel is provided that comprises a low-carbon, an extra-low-carbon or an ultra-low carbon steel substrate provided on one or both sides with an iron-tin alloy layer which contains at least 80 weight percent (wt. %) of FeSn (50 at. % iron and 50 at. % tin) wherein the iron-tin alloy layer was produced by providing the substrate on the said one or both substrates with a tin layer followed by an annealing step at a temperature Ta of at least 513° C. for an annealing time ta to form the iron-tin alloy layer and wherein the annealing step simultaneously provides a recovery annealed substrate, followed by fast cooling of the annealed substrate.
This steel is both provided with a corrosion resistant coating in the form of the iron/tin alloy layer and a good strength/elongation ratio as a result of the recovery annealed full hard cold rolled (SR) steel substrate.
In an embodiment of the invention a packaging steel product is provided wherein the steel substrate comprises (in weight percent):
In a preferred embodiment a packaging steel product is provided wherein:
Preferably the carbon content of the steel according to the invention has a carbon content of at most 0.003%. More preferably the steel substrate is an interstitial free steel.
Strip shape problems are not expected to occur with an IF-steel after the recovery annealing process. The strip flatness is affected by internal-stresses which in turn originate from a non-homogenous microstructure due to a variation of the annealing temperature. The variation of mechanical properties is sluggish for a Nb-IF grade. With a variation in annealing temperature the change in mechanical properties is relatively small (e.g. 35 MPa for a change in temperature of 50° C.) whereas for LC steel a difference of about 70 MPa is expected for Rp and Rm, for a recovery annealed low-C steel. So LC-steels are more critical to produce than IF-grades.
However, if the strip shape or surface texture (e.g. roughness) would require some minor corrections or if the product needs to be supplied in a condition that the yield point is suppressed, then the invention is also embodied in a process wherein the coated and annealed substrate is temper rolled or subjected to tension levelling wherein the reduction of the substrate is between 0.5 and 3% temper rolling reduction or the equivalent reduction in tension levelling. Interstitial free steels do not age as a result of the absence of free interstitials, and therefore the only reason to temper roll interstitial free steels would be for shape correction or surface texture. Temper rolling can also be performed after the substrate was coated with the thermoset organic coating, or a thermoplastic single layer coating, or a thermoplastic multi-layer polymer coating. A temper rolled single reduced substrate is not considered a DR substrate.
The invention will now be further explained by means of the following, non-limitative examples.
At a selected annealing time, the recovery annealing window is between the recrystallisation start temperature and the temperature from which the material is considered to behave as full-hard. The temperature from which the steel is considered to behave as a full-hard material is estimated to be at 200° C. below the recrystallisation start temperature. The recrystallisation start temperature for Nb40 has been determined to be 710° C. from an analysis of the microstructure and the mechanical properties in which FH specimens were treated at different temperatures for 60 s. Therefore the recovery annealing range for grade Nb40 is estimated to lie between 710° C. and 510° C. In principle, each temperature above 510° C. can be used to obtain a recovery annealed Nb40 steel. However, the minimum temperature to obtain the desired iron-tin alloy layer is at least 513° C. To keep the annealing times low, it is preferable to anneal at a temperature of at least 550° C. Experiments were also performed at the highest allowable temperature of 625° C. for 4 s. According to the formula above these conditions correspond to an annealing at 576° C. for 60 s in a standard continuous annealing line.
The annealing parameters used were: Heating rate to Ta: 300 C°/s, Ta between 550 and 625° C., ta between 4 and 60 s, cooling rate after annealing 100° C./s (Table 3).
The Nb40 grade is an IF grade. Therefore strip shape problems are not expected to occur after the recovery annealing process.
| Number | Date | Country | Kind |
|---|---|---|---|
| 12162441 | Mar 2012 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2013/056780 | 3/28/2013 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2013/144320 | 10/3/2013 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2357126 | Nachtman | Aug 1944 | A |
| 3174917 | Lesney et al. | Mar 1965 | A |
| 4726208 | Saunders | Feb 1988 | A |
| 6533876 | Cornelissen et al. | Mar 2003 | B1 |
| Number | Date | Country |
|---|---|---|
| 1483247 | Mar 1969 | DE |
| 1123189 | Aug 1968 | GB |
| 2082776 | Apr 1997 | RU |
| 2208485 | Jul 2003 | RU |
| 2381293 | Feb 2010 | RU |
| 2012045791 | Apr 2012 | WO |
| 2013144321 | Oct 2013 | WO |
| Entry |
|---|
| International Search Report dated Jun. 25, 2013 from International Application PCT/EP2013/056780 to Tata Steel Ijmuiden BV filed Mar. 28, 2013. |
| Search Report completed Mar. 9, 2017 for RU 2014143507/02(070206) to Tata Steel Ijmuiden BV filed Mar. 28, 2013. |
| Russian Office Action dated Apr. 28, 2017 for RU Application No. 2014143507/02(070206) to Tata Steel Ijmuiden BV filed Mar. 28, 2013. |
| Number | Date | Country | |
|---|---|---|---|
| 20150044500 A1 | Feb 2015 | US |