The present invention relates to a process for manufacturing an apron board of a high-speed rail equipment cabin, and more particularly to a process for manufacturing an apron board of a high-speed rail equipment cabin using a composite material with high strength and light weight.
The apron board of high-speed rail equipment cabin is an important part of the equipment cabin of standard high-speed train. In practical application, lamination design, material usage and technique design are considered since there are certain requirements on bearing ability, flame retardant ability and impact resistant ability of the apron board; along with the constant update of science and technology, light weight and smooth-going design are used to effectively reduce the resistance of the train during operation, thereby reducing the continuous energy consumption. Under the condition of ensuring comprehensive performance, using of composite materials instead of aluminum alloy materials can reduce the weight of the overall train and enhance the level of light weight performance of the overall train.
In view of the above problems, a main object of the present invention is to provide a process for manufacturing an apron board of a high-speed rail equipment cabin using a composite material with high strength and light weight.
The present invention solves the above technical problems by the following technical solutions: a process for manufacturing an apron board of a high-speed rail equipment cabin using a composite material, wherein the composite material includes:
aramid fiber honeycomb, PET (Polyethylene terephthalate) foam, 3K twill carbon fiber flame retardant prepreg, unidirectional carbon fiber flame retardant prepreg, glass fiber flame retardant prepreg, aramid flame retardant prepreg, and 300 g/m2 single component medium temperature curing blue epoxy adhesive;
the process for manufacturing the apron board of the high-speed rail equipment cabin using the composite material includes steps of:
(1) manufacturing an apron main plate;
(2) manufacturing apron-board trim strips, wherein there are two first apron-board trim strips and two second apron-board trim strips; and
(3) obtaining the apron board of the high-speed rail equipment cabin by the apron main plate, the two first apron-board trim strips and the two second apron-board trim strips,
wherein the two first apron-board trim strips are respectively stuck at two opposite sides of the apron main plate, the two second apron-board trim strips are respectively stuck at another two opposite sides of the apron main plate.
In a specific embodiment of the present invention, the step of manufacturing the apron main plate includes closely pasting multiple layers of raw materials to a mold cavity in sequence from outside to inside in a form of lamination, wherein the multiple layers of raw materials are:
1 layer of 198-200 g/m2 3K twill carbon fiber flame retardant prepreg;
5-8 layers of 300-315 g/m2 glass fiber flame retardant prepreg;
2 layers of 235-240 g/m2 aramid flame retardant prepreg;
2 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive;
2 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 piece of aramid fiber honeycomb with a thickness of 16.4 mm;
1 layer of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of the 300 g/m2 single component medium temperature curing blue epoxy adhesive;
2 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
4 layers of the 300-315 g/m2 glass fiber flame retardant prepreg; and
1 layer of the 198-200 g/m2 3K twill carbon fiber flame retardant prepreg; and then
shaping the apron main plate through a hot press machine with a temperature of 130-150° C., a molding time of 3600-3800 s and a pressure of 4 MPa-6 MPa.
In a specific embodiment of the present invention, the apron-board trim strips are shaped through vacuum bagging, the step of manufacturing the apron-board trim strips includes closely pasting multiple layers of raw materials to a mold cavity in sequence from inside to outside in a form of lamination, wherein the multiple layers of raw materials are:
1-2 layers of 300-315 g/m2 glass fiber flame retardant prepreg;
4-6 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of 235-240 g/m2 aramid flame retardant prepreg;
2 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of the 235-240 g/m2 aramid flame retardant prepreg;
4-6 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg; and
1 layer of 198-200 g/m2 3K twill carbon fiber flame retardant prepreg;
and then installing an air duct, shaping the apron-board trim strips through a hot press machine with a temperature of 130-150° C., a molding time of 3600-3800 s, a pressure of 4 MPa-6 MPa, and an internal pressure of the installed air duct being 1 MPa.
In a specific embodiment of the present invention, a density of the aramid fiber honeycomb is in a range of 48-50 kg/m3.
In a specific embodiment of the present invention, a density of the PET foam is in a range of 59-61 kg/m3.
The positive and progressive results of the present invention are as follows.
The process for manufacturing the apron board of the high-speed rail equipment cabin using the composite material has the following advantages:
(1) By lamination design of the present invention, the apron board obtains very high strength at all angles, and the added aramid design gains high impact resistance.
(2) The mould pressing technique is applied to the apron main plate, and the vacuum bagging technique is applied to the apron-board trim strips to improve the strength thereof. Different techniques are applied to different product parts.
(3) Through the hot mould pressing process, the resin is low in content, which greatly reduces the weight of the apron main plate.
(4) The present invention brings not only elegant and nice appearance but also strong performance. The weight of the apron board made from the composite material is 35%-40% lower than the apron board made from the aluminum alloy material, which leads to a good prospect of application.
Some preferred embodiments are described with accompanying drawings to explain technical solutions of the present invention in detail as follows.
A process for manufacturing an apron board of a high-speed rail equipment cabin using a composite material includes steps of:
(1) manufacturing an apron main plate 3;
(2) manufacturing apron-board trim strips 1, 2, wherein there are two apron-board trim strips 1 and two apron-board trim strips 2; and
(3) obtaining the apron board of the high-speed rail equipment cabin by the apron main plate 3, the two apron-board trim strips 1 and the two apron-board trim strips 2,
wherein the two apron-board trim strips 1 are respectively stuck at two opposite sides of the apron main plate, the two apron-board trim strips 2 are respectively stuck at another two opposite sides of the apron main plate.
The step of manufacturing the apron main plate includes closely pasting multiple layers of raw materials to a mold cavity in sequence from outside to inside in a form of lamination, wherein the multiple layers of raw materials are:
1 layer of 198-200 g/m2 3K twill carbon fiber flame retardant prepreg;
5-8 layers of 300-315 g/m2 glass fiber flame retardant prepreg;
2 layers of 235-240 g/m2 aramid flame retardant prepreg;
2 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive;
2 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 piece of aramid fiber honeycomb with a thickness of 16.4 mm;
1 layer of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of the 300 g/m2 single component medium temperature curing blue epoxy adhesive;
2 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
4 layers of the 300-315 g/m2 glass fiber flame retardant prepreg; and
1 layer of the 198-200 g/m2 3K twill carbon fiber flame retardant,
and then shaping the apron main plate through a hot press machine with a temperature of 130-150° C., a molding time of 3600-3800 s and a pressure of 4 MPa-6 MPa.
The apron-board trim strips are shaped through vacuum bagging, the step of manufacturing the apron-board trim strips includes closely pasting multiple layers of raw materials to a mold cavity in sequence from inside to outside in a form of lamination, wherein the multiple layers of raw materials are:
1-2 layers of 300-315 g/m2 glass fiber flame retardant prepreg;
4-6 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of 235-240 g/m2 aramid flame retardant prepreg;
2 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg;
1 layer of the 235-240 g/m2 aramid flame retardant prepreg;
4-6 layers of the 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg; and
1 layer of 198-200 g/m2 3K twill carbon fiber flame retardant prepreg,
and then installing an air duct, shaping the apron-board trim strips through a hot press machine with a temperature of 130-150° C., a molding time of 3600-3800 s, a pressure of 4-6 MPa, and an internal pressure of the installed air duct being 1 MPa.
The present invention is further explained with accompanying embodiments as follows.
Step One: The Manufacturing of an Apron Main Plate with Mould Pressing Technique:
According to lamination design, 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg, 6 layers of 300 g/m2 glass fiber flame retardant prepreg, 3 layers of 235 g/m2 aramid flame retardant prepreg, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 piece of aramid fiber honeycomb with a thickness of 16.4 mm, 1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive, 2 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg, 4 layers of 300 g/m2 glass fiber flame retardant prepreg, and 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg are laminated in sequence from outside to inside, all layers are pasted in a mould cavity closely with a temperature of 130° C., a molding time of 3600 s and a pressure of 4 MPa.
Step two: The manufacturing of the two apron-board trim strips 1 and the two apron-board trim strips 2 through vacuum bagging; 1 layer of 300 g/m2 glass fiber flame retardant prepreg, 6 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 235 g/m2 aramid flame retardant prepreg, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 235 g/m2 aramid flame retardant prepreg, 6 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, and 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg are laminated in sequence from inside to outside; all layers are pasted closely in a mould cavity; after installation of an air duct, the apron-board trim strips are shaped through a hot press machine with a temperature of 130° C., a molding time of 3600 s, a pressure of 4 MPa, and an internal pressure of the installed air duct being 1 MPa.
Step Three: The Performing of CNC (Computer Numerical Control) Engraving and Gluing.
Step four: Weighing, wherein a weight of the apron board using the composite material is less 51% than a weight of an aluminum alloy apron board of a real high-speed rail, a loading capacity of the apron board using the composite material is over 2500 Pa per unit area.
Step One: The Manufacturing of an Apron Main Plate with Mould Pressing Technique:
According to lamination design, 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg, 7 layers of 300 g/m2 glass fiber flame retardant prepreg, 2 layers of 235 g/m2 aramid retardant prepreg, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 piece of aramid honeycomb with a thickness of 16.4 mm, 1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive, 2 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg, 4 layers of 300 g/m2 glass fiber flame retardant prepreg and 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg are laminated in sequence from outside to inside, all layers are pasted in a mould cavity closely with a temperature of 140° C., a molding time of 3600 s and a pressure of 4 MPa.
Step two: The manufacturing of the two apron-board trim strips 1 and the two apron-board trim strips 2 through vacuum bagging; 2 layers of 300 g/m2 glass fiber flame retardant prepreg, 4 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 235 g/m2 aramid flame retardant prepreg, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 235 g/m2 aramid flame retardant prepreg, 6 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, and 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg are laminated in sequence from inside to outside; all layers are pasted closely in a mould cavity; after installation of an air duct, the apron-board trim strips are shaped through a hot press machine with a temperature of 140° C., a molding time of 3600 s, a pressure of 5 MPa, and an internal pressure of the installed air duct being 1 MPa.
Step Three: The Performing of CNC (Computer Numerical Control) Engraving and Gluing.
Step four: Weighing, wherein a weight of the apron board using the composite material is less 52% than a weight of an aluminum alloy apron board of a real high-speed rail, a loading capacity of the apron board using the composite material is over 2500 Pa per unit area.
Step One: The Manufacturing of an Apron Main Plate with Mould Pressing Technique:
According to lamination design, 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg, 6 layers of 300 g/m2 glass fiber flame retardant prepreg, 3 layers of 235 g/m2 aramid flame retardant prepreg, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 piece of aramid honeycomb with a thickness of 16.4 mm, 1 layer of 300 g/m2 single component medium temperature curing blue epoxy adhesive, 2 layers of 100-150 g/m2 unidirectional carbon fiber flame retardant prepreg, 4 layers of 300 g/m2 glass fiber flame retardant prepreg and 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg are laminated in sequence from outside to inside, all layers are pasted in a mould cavity closely with a temperature of 150° C., a molding time of 3600 s and a pressure of 4 MPa.
Step two: The manufacturing of the two apron-board trim strips 1 and the two apron-board trim strips 2 through vacuum bagging; 1 layer of 300 g/m2 glass fiber flame retardant prepreg, 4 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 235 g/m2 aramid flame retardant prepreg, 2 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, 1 layer of 235 g/m2 aramid flame retardant prepreg, 8 layers of 150 g/m2 unidirectional carbon fiber flame retardant prepreg, and 1 layer of 200 g/m2 3K twill carbon fiber flame retardant prepreg are laminated in sequence from inside to outside; all layers are pasted closely in a mould cavity; after installation of an air duct, the apron-board trim strips are shaped through a hot press machine with a temperature of 150° C., a molding time of 3600 s, a pressure of 6 MPa, and an internal pressure of the installed air duct is 1 MPa.
Step Three: The Performing of CNC (Computer Numerical Control) Engraving and Gluing.
Step four: Weighing, wherein a weight of the apron board using the composite material is less 51% than a weight of an aluminum alloy apron board of a real high-speed rail, a loading capacity of the apron board using the composite material is over 2500 Pa per unit area.
The basic principle, main features and advantages of the present invention have been shown and described above. It should be understood by those skilled in the art that the present invention is not limited by the foregoing embodiments. The foregoing embodiments and descriptions describe only the principle of the present invention. Without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications which fall within the scope of the claimed invention. The scope of the present invention is defined by the appended claims and their equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201510947266.1 | Dec 2015 | CN | national |
This is a U.S. National Stage under 35 U.S.C 371 of the International Application PCT/CN2016/096333, filed Aug. 23, 2016, which claims priority under 35 U.S.C. 119(a-d) to CN 201510947266.1, filed Dec. 16, 2015.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2016/096333 | 8/23/2016 | WO | 00 |