The present invention relates to a printing process for printing a design onto cork tiles for flooring, wall coverings, and ceilings.
Cork is a natural material that is harvested from the bark of cork oak trees, which are endemic to Southwest Europe and Northwest Africa. Cork is extracted by removing the bark from the trees. Cork is a renewable material in that the cork oak tree regenerates naturally after each extraction of its bark. During a typical lifespan of 150 to 200 years, a cork oak tree can be extracted 15-18 times.
Cork is elastic, highly impermeable, and fire retardant. The characteristics of cork are due to its cellular structure. Cork is composed of small cells of suberin, which are filled with a gas mixture similar to air. The unique structure and materials of cork provide cork with many useful properties. For example, it's high-permeability and elasticity make cork suitable for the most common use as a bottle stopper. The same characteristics also make cork suitable for use as a gasket material, fishing floats and buoys, as well as handles for fishing poles. Cork's cellular form and fire retardant properties also make it suitable for use as acoustic and thermal insulation in-house walls, floors, ceilings, and façades.
Cork is also increasingly used as a flooring and wall covering material. The following properties of cork make it highly suitable for use as a flooring material:
Durable—the elastic properties of cork allow it to bounce back so that furniture indentations are not permanent;
Healthy—cork is anti-microbial, naturally resistant to mold, mildew, and termites, and it does not off-gas or shared microfibers;
Safe—cork is fire resistant and produces less smoke and less toxic material than vinyl flooring during combustion;
Comfortable—a cork floor provides a comfortable cushion underfoot because it gives one compressed, and is also a natural thermal and acoustic insulator.
Because the cork oak tree regenerates the extracted cork bark, the harvesting practice is sustainable. Therefore the use of cork has little negative impact on the environment. Further the manufacturing process for cork flooring generates almost no waste. In fact, cork flooring uses the residuals from the production of cork stoppers. The residuals are finely ground and combined with binders such as, for example, polyurethane. Increasingly, pigments are added to create different colors or patterns. However, the known methods of applying colors or patterns are difficult to use and the appearance of cork floor and wall coverings are still limited.
An object of the invention is to present a new method for applying a color pattern or design to a cork tile used for flooring, wall covering, or ceiling covering.
The term “tile” is used in the specification and claims to include any inlay, piece, sheet, board, or plank or other similarly shaped objects that can be used alone or together with other such inlays, pieces, sheets, boards, or planks to cover a floor, wall, or ceiling. Further, the tile may include click-lock flooring pieces that are connected to each other using interlocking elements, i.e., tongue and groove, or flooring pieces that lie next to each other such as glue-down tiles. The tile may comprise a laminate made of at least one layer of cork material or may be made entirely of cork material.
The object of the present invention is met by a process for applying a color pattern or design to a cork tile, including the steps of providing a release film, printing a design layer on the release film, applying a glue layer on the design layer so that the design layer is between the glue layer and the release film, and laminating the design layer and the glue layer onto a cork top surface of the cork tile using a heated laminating machine, so that the glue layer and the design layer are released from the release film and form the color pattern or design on the cork top surface.
The cork top surface is formed by agglomerating cork granules with a binder and curing at a temperature of 140-180° C. The cork granules of the cork top surface have a particle size of 0.5-1 mm and a density of 500-600 Kg/m3.
In one embodiment, the cork tile includes a backing layer arranged below the cork top surface. The backing layer is formed by agglomerating cork granules with a binder and curing at a temperature of 140° C. or less. The cork granules of the backing layer have a particle size of 1-2 mm and a density of 180-220 kg/m3.
A thickness of the combined design layer and glue layer, which forms the color pattern or design is 20-50 microns.
According to another embodiment, the release film is a PET film.
In a particular embodiment, the step of laminating is performed at a temperature of 100-190° C. and at a pressure of 400-600 bar.
In one embodiment, the heated laminating machine is a heated calendar and includes rolls having a circumference of 520-1500 mm. In an alternative embodiment, the heated laminating machine is a heated machine press.
The glue is an acrylic resin or a silicon dioxide and the design layer includes an ink comprising a polyamine ester with a pigment. The polyamine ester includes a vinyl chloride-acetate copolymer and an ester diluent.
In one embodiment, the step of printing is performed using an engraved cylinder. If multiple colors are printed, a plurality of engraved cylinders are used. As an alternative, inkjet printing and/or electrophotography may be used.
In one embodiment, a release agent is applied to the release film, wherein the step of printing includes printing the design layer on the release film.
According to an embodiment, the cork top surface is mounted on a base layer of the cork tile prior to the step of laminating. The base layer comprises a fiberboard plank or a wood plank.
To form a simulated wood grain or stone surface, the step of laminating optionally includes using an embossed roll or an embossed plate according to one embodiment of the present invention.
If a finishing coat or polymer layer is applied to the color pattern or design, the finishing coat or polymer layer may be embossed.
The various features of novelty which characterize the invention are pointed out with particularity in the claims annexed to and forming a part of the disclosure. For a better understanding of the invention, its operating advantages, specific objects attained by its use, reference should be had to the drawings and descriptive matter in which there are illustrated and described preferred embodiments of the invention.
As a release film 28 is unwound from the supply reel 18, the release film 28 passes the release agent applicator 26, which applies a release agent to the release film. In one embodiment, the release film 28 is a Polyethylene terephthalate (PET) film. However, any known or hereafter developed release film may be used. The printer 22 is arranged downstream of the release agent applicator 26 and prints a design or pattern of a coloring agent such as ink or toner onto the release film after the release agent is applied. In a preferred embodiment, the printing is performed using ink applied by one or more engraved cylinders, i.e., one cylinder for each color of ink to be printed. Instead of using an engraved cylinder, printing may alternatively include other printing machines such as for example inkjet printing or electro-photography printing. The ink may include a polyamine ester, such as one made from a vinyl chloride-acetate copolymer and an ester diluent. The ink also will include a pigment (titanium dioxide for white-collar, and organic pigment for other colors). Instead of ink, other coloring agents such as, for example, toner can also be used. A glue applicator 24 downstream of the printer 22 applies a glue coating on the ink layer. In a preferred embodiment, the glue comprises an acrylic resin or silicon dioxide. However, other glues may alternatively by used.
The ink and the glue are dried on the release film and, after the glue and ink have dried, the release film with the glue and the ink is led through rolls 12, 14 of the calendar 10. The rolls 12, 14 apply pressure of 400-600 bar at a temperature of 100-190° C. so that the glue and the ink are released from the release film and laminated onto the cork tile 16. In one embodiment, the temperature and pressure cause the glue and the ink to mix together and form one composite layer on the cork tile. In another embodiment, the glue and ink remain as separate layers. In both cases, the pressure and temperature allow the glue to become tacky so that the glue adheres to the cork tile 16. After passing through the rolls 12, 14, the take-up reel 20 downstream of the calendar 10 collects the release film.
In the embodiment of
In step S12, a backing layer is formed by the same agglomeration process, but with cork grains having a particle size of 1-2 mm, and a density between 180-220 kg/m3. The backing layer can be cured at a temperature of 140° C. or less. The backing layer is used as an underlayer at a bottom of the cork tile. The backing layer of the cork tile has a thickness of 1-4 mm.
In step S14 the cork top surface and the backing are applied to a fiberboard plank using water-based adhesives with a specificity D3 or higher on heated plate presses to form the cork tile 16. Although fiberboard planks are used in the preferred embodiment, any known or hereafter developed base layer for flooring or wall covering may be used. As an example, wood or another cork layer may be used instead of the fiberboard planks.
In step S16, and ink layer and glue layer are laminated onto the assembled cork tile, as described in more detail below. After the glue and ink layers are transferred to the cork tile, a finish layer such as urethane or polymers may is applied in step S18. For residential applications, the finish layer may include water-based or acrylic varnishes. For commercial applications, high wear resistance polymers, which are free of polyvinyl chloride (PVC), such as PET, polyurethane (PU), polyethylene (PE), and polystyrene (PS). These polymers may have different compositions to achieve specific performance characteristics.
The final product may be embossed, step S20. The embossing may be performed before or after the step of applying the finish. The embossing may be accomplished using embossing rolls, i.e., in the calendar 10 of the embodiments of
After the design layer is printed, a glue layer is applied on the ink layer, step S104. The glue comprises an acrylic resin or silicon dioxide. The glue layer and design layer are dried and then laminated onto the cork tile, step S106. The lamination can be accomplished using a calendar or a machine press as described above. In both cases, the lamination is accomplished with a pressure of 400-600 bar and at a temperature of 100-190° C.
Thus, while there have shown and described and pointed out fundamental novel features of the invention as applied to a preferred embodiment thereof, it will be understood that various omissions and substitutions and changes in the form and details of the devices illustrated, and in their operation, may be made by those skilled in the art without departing from the spirit of the invention. For example, it is expressly intended that all combinations of those elements, which perform substantially the same function in substantially the same way to achieve the same results, are within the scope of the invention. Moreover, it should be recognized that structures and/or elements shown and/or described in connection with any disclosed form or embodiment of the invention may be incorporated in any other disclosed or described or suggested form or embodiment as a general matter of design choice. It is the intention, therefore, to be limited only as indicated by the scope of the claims appended hereto.