The invention relates to a process for modifying natural rubber and to modified natural rubber with improved processing performance.
Natural rubber (NR) is obtained from the white latex (latex milk) of particular plants encountered in the tropical climate zone. This latex milk is coagulated to obtain commercially available natural rubber, which finds various uses in large amounts in the rubber-processing industry. For example, in 2005, 8 703 000 t of natural rubber were produced and 8 777 000 t of natural rubber were consumed, of which approximately 70% of the consumption is in the automotive tire sector [source: Römpp, Chemielexikon online, Version 3.1].
The physical and chemical properties of the different natural rubber types are determined by their particular regions of origin and processing or production methods.
An essential criterion in this regard is the production process of the natural rubber latex. This allows the natural rubber types to be divided into two classes, a first class, 1, and a second class, 2.
The rubber types of Class 1 are produced by the conventional process in which the coagulum slabs obtained from latex are processed further directly without comminution. The natural rubber of Class 1 is therefore not subjected to any mechanical stress in the production process and is usually dried at temperatures less than 70° C. As a result, it retains a relatively high molecular weight, which has clear advantages in the dynamic performance of the vulcanizates comprising this natural rubber. A significant disadvantage is, however, the commercial packaging form as “sheets”, which make processibility significantly more difficult. Class 1 includes “Ribbed Smoked Sheets” (RSS), “Air Dried Sheets” (ADS), “UnSmoked Sheets” (USS) and “Pale Crepe”.
The natural rubber of Class 2 is produced by the “crumb process”, wherein the rubber is crushed to crumbs by means of rollers with addition of castor oil, or by mechanical comminution in granulators. The drying, which follows various washing processes, takes place at temperatures up to 130° C. The mechanical process gives rise to lower molecular weights, which have an adverse effect on the dynamic behavior of the corresponding vulcanizates. However, natural rubber of Class 2 is packaged in processing-friendly bales, which ensure significantly improved processibility. Class 2 includes “Standard That Rubber” (STR), “Standard Malaysian Rubber” (SMR) and “Standard Indonesian Rubber” (SIR).
Frequent attempts have been made to influence the properties of the natural rubber according to the criteria desired in each case. As representative examples of further publications on this subject, the following should be mentioned here:
(D1) EP 0 950 485 A1; (D2) DE 199 13 047 B4; and, (D3) EP 1 120 429 A1 (U.S. Pat. No. 6,410,606).
EP 0 950 485 A1 discloses a process for producing natural rubber, and natural rubber thus obtained. Here, before or after a one-stage or multistage drying treatment of the natural rubber, a viscosity stabilizer is added. The usual problems with the drying conditions described in EP 0 950 485 A1 should be alleviated in order to obtain a natural rubber which has a high molecular weight and a low gel content.
The drying treatment results in an amount of gel in the natural rubber of 10% or less and a molecular weight retention of 85% or more.
DE 199 13 047 B4 describes a process for masticating natural rubber in a ramless internal mixer. The purpose of masticating natural rubber is to perform a cleavage of the long hydrocarbon chains in the rubber in order to lower the hardness of the rubber or to make it more easily deformable.
U.S. Pat. No. 6,410,606 discloses a process for producing natural rubber for pressure-sensitive adhesives. To this end, the molecular weight of a non-masticated natural rubber is reduced by using a “peptizer”, while the non-masticated natural rubber is dissolved in an organic solvent.
It is therefore an object of the invention to provide a process for modifying natural rubber, which ensures improved processibility of the natural rubber obtained therefrom in combination with improved dynamic properties of the vulcanizates which comprise the natural rubber thus obtained.
This object is achieved by a process for modifying natural rubber, which is characterized by at least four process steps:
It has been found that, surprisingly, only through these process steps, which have to proceed in the chronological sequence specified, can the natural rubber be modified to the effect that it can ensure better processibility with simultaneously good dynamic properties of the vulcanizates.
The natural rubber used is a latex rubber type which is produced from latex by acid coagulation and can be purchased commercially.
It is essential to the invention here that the natural rubber prior to the modification has been produced by a conventional process in which the coagulum slabs obtained from latex are processed further directly without comminution, and is present in the form of sheets. The natural rubber is preferably an unsmoked natural rubber of the USS type, though it is also possible to use a natural rubber of the ADS type or a combination of both types.
Prior to the modification and also after the modification, the natural rubber has a molecular weight, determined by gel permeation chromatography (GPC), of greater than or equal to 1 000 000 g/mol, preferably of greater than or equal to 1 200 000 g/mol and most preferably of greater than or equal to 1 500 000 g/mol.
The comminution of the natural rubber in the first process step takes place within a period of 1 to 10 min and is effected in a hammer mill and/or in a shredder. This comminutes the natural rubber to particles having a mean average particle size of greater than 1 cm to less than or equal to 15 cm, preferably greater than or equal to 1 cm to less than or equal to 10 cm. The first process step serves to prepare the natural rubber, especially in order to obtain a greater surface area for the second process step and in order to remove relatively large soil particles at this early stage. In addition, in the case of use of different natural rubber types, these are already, as it were, “pre-blended” at this early stage.
The blending and purification of the natural rubber in the second process step are effected in a stirred tank with the aid of a liquid, which is preferably water. The second process step takes place within a period of 1 to 15 min. It should be noted here that the second process step is a continuous process, in which blending and purifying each alternate at indeterminate intervals. The period of 1 to 15 min is therefore based on the total duration of the second process step, not on the individual duration of the blending or the individual duration of the purification.
The second process step preferably serves to minimize variations in the natural rubber types used, and additionally for further blending and purifying, i.e. for removing the soil still present.
The comminution of the natural rubber in the third process step takes place in a hammer mill and/or in a shredder and/or by means of a roller. The natural rubber is comminuted to particles having a mean average particle size of less than or equal to 10 mm, preferably less than or equal to 8 mm.
The third process step serves to further enlarge the surface area, which ensures another improvement in blending and further purification. In addition, this provides good air permeability for the subsequent drying step.
The drying of the natural rubber in the fourth process step takes place in a gaseous medium, which gaseous medium is preferably air. However, other gases, for example nitrogen, are also suitable. The drying takes place at temperatures between 90 and 120° C., preferably between 100 and 118° C. and more preferably at temperatures between 105 and 115° C.
The fourth process step serves to remove the residual moisture of the natural rubber types used by comparatively gentle drying at comparatively low temperature.
It is a further object of the invention to provide a modified natural rubber which features a comparatively high molecular weight and good processibility.
This object is achieved by virtue of the natural rubber being modified by at least four process steps.
The process steps comprise at least comminution of the natural rubber as a first process step, blending and purification of the natural rubber as a second process step, further comminution of the blended and purified natural rubber as a third process step and drying of the natural rubber as a fourth process step.
The natural rubber is a latex rubber type which is formed by acid coagulation of the latex and is commercially purchasable prior to modification.
It is essential to the invention that the natural rubber prior to the modification has been produced by a conventional process in which the coagulum slabs obtained from latex are processed further directly without comminution, and is present in the form of sheets.
Prior to the modification and after the modification, the modified natural rubber has a molecular weight, determined by gel permeation chromatography (GPC), of greater than or equal to 1 000 000 g/mol, preferably of greater than or equal to 1 200 000 g/mol and most preferably of greater than or equal to 1 500 000 g/mol.
In the course of the first process step, the modified natural rubber is comminuted within a period of 1 to 10 min, the comminution being effected in a hammer mill and/or in a shredder. In the course of the first process step, the modified natural rubber is comminuted here to particles having a mean average particle size of greater than 1 cm to less than or equal to 15 cm, preferably greater than or equal to 1 cm to less than or equal to 10 cm.
In the course of the second process step, the modified natural rubber is blended and purified in a stirred tank with the aid of a liquid, which is preferably water. In the course of the second process step, the modified natural rubber is blended and purified within a period of 1 to 15 min.
It should be noted here that the second process step is a continuous process in which blending and purification each alternate at indeterminate intervals. The period of 1 to 15 min therefore relates to the total duration of the second process step, not to the individual duration of the blending or the individual duration of the purification.
In the course of the third process step, the modified natural rubber is further comminuted. The further comminution in the course of the third process step takes place in a hammer mill and/or in a shredder and/or by means of a roller. In the course of the third process step, the modified natural rubber is comminuted to particles having a mean average particle size of less than or equal to 10 mm, preferably less than or equal to 8 mm.
In the course of the fourth process step, the modified natural rubber is dried in a gaseous medium, which gaseous medium is preferably air. However, other gases, for example nitrogen, are also suitable. In the course of the fourth process step, the modified natural rubber is dried at temperatures between 90 and 120° C., preferably between 100 and 118° C. and more preferably at temperatures between 105 and 115° C.
In addition, a rubber mixture which comprises a modified natural rubber according to the characterizing part of claim 25 and of the claims dependent thereon is provided.
It is a further object of the invention to use above-described modified natural rubber for producing tires, especially for producing the tread of a tire and/or a body mixture of a tire, and for producing drive belts and conveyor belts.
The invention will now be illustrated in detail by comparative and inventive examples summarized in Tables 1 and 2. The rubber mixture designated “E” here comprises the inventive modified natural rubber, whereas the rubber mixtures designated “V” are comparative mixtures.
For all mixture examples present in the table, the amounts reported are parts by weight based on 100 parts by weight of total rubber (phr).
The mixtures were prepared under customary conditions in two stages in a laboratory tangential mixer. All mixtures were used to produce specimens by vulcanization, and these specimens were used to determine material properties typical of the rubber industry. For the above-described tests on specimens, the following test methods were employed:
a TSS 8, modified in accordance with the invention
It is evident from Table 2 that the modified natural rubber (see E1), by virtue of the packaging form in the form of bales, has improved processibility.
At the same time, it exhibits incorporability of fillers, for example silica and/or carbon black, equivalent to that of V2, V3 and V4, and hence better than that of V1. The viscosity variations, which result from the production, in the Mooney viscosities of the inventive natural rubber, as found in E1, are significantly less than those for the natural rubber of V1. In the industrial process, this leads to significant process reliability, and to improved “batch-to-batch” production. At the same time, the rubber mixture which comprises the inventive modified natural rubber, as a result of the comparatively high molecular weight of 1 600 000 g/mol, exhibits physical properties at a similar level to those of the mixture V1. The natural rubber of the mixture V1 has a comparable molecular weight, but is present in the form of sheets, which is less favorable for processing. The natural rubbers of mixtures V2, V3 and V4 are present in bale form, which is more favorable for processing, but have poorer physical properties owing to their significantly lower molecular weights.
It has been found that, surprisingly, the modified natural rubber, with regard to crosslinking characteristics and mixing properties, does not constitute a compromise between natural rubbers of Class 1 (see V1) and natural rubbers of Class 2 (see V2 to V4), but provides an improvement.
Relevant data which should be mentioned here are as follows:
Consideration of Table 2 shows that the inventive modified natural rubber as was used in the rubber mixture E2 has the specifications mentioned.
It is understood that the foregoing description is that of the preferred embodiments of the invention and that various changes and modifications may be made thereto without departing from the spirit and scope of the invention as defined in the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2008 038 000.8 | Aug 2008 | DE | national |
This application is a continuation application of international patent application PCT/EP 2009/057500, filed Jun. 17, 2009, designating the United States and claiming priority from German application 10 2008 038 000.8, filed Aug. 16, 2008, and the entire content of both applications is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/EP2009/057500 | Jun 2009 | US |
| Child | 12929788 | US |