Claims
- 1. An elastic film formed from a water insoluble gel of a neutralized sulfonated polymer, said gel having a viscosity of at least 50,000 cps.
- 2. A film according to claim 1, wherein said neutralized sulfonated polymer, is an EPDM terpolymer having about 10 to 200 meq. of sulfonate groups per 100 grams of sulfonated polymer.
- 3. A high strength grease formed from a water insoluble gel of a neutralized sulfonated elastomeric polymer, said gel having a viscosity of at least 50,000 cps.
- 4. A grease according to claim 3 wherein said neutralized elastomer polymer is a neutralized sulfonated EPDM terpolymer having about 10 to 200 meq. of sulfonate groups per 100 grams of sulfonated polymer.
- 5. A grouting material formed from a water insoluble gel of a neutralized sulfonated elastomeric polymer said gel having a viscosity of at least 50,000 cps.
- 6. A grouting material according to claim 5, wherein said neutralized elastomer polymer is a neutralized sulfonated EPDM terpolymer having about 10 to 200 meq. of sulfonate groups per 100 grams of sulfonated polymer.
- 7. A substrate stabilization process which comprises the impregnation in and depositing on a surface of a substrate a layer of a polymeric solution of a neutralized sulfonated polymer dissolved in a mixed solvent system of an organic liquid and a polar cosolvent, said organic liquid being selected from the group consisting of aromatic hydrocarbons, cyclic aliphatic ethers, aliphatic ethers and organic aliphatic esters and mixtures thereof, said solvent system containing less than 15 wt.% of polar cosolvent, a viscosity of said solvent system being less than about 1000 cps. said solution containing about 0.1 to about 20 wt.% of said neutralized sulfonated polymer, said neutralized sulfonated polymer having about 10 to about 200 meq of neutralized sulfonate groups; and depositing sufficient water onto said layer of said polymer solution to transform said polymeric solution into an water insoluble elastomeric layer.
- 8. A process according to claim 1, wherein said substrate is sand or a soil formation.
- 9. A coating process which comprises the impregnation in and depositing on a surface of a substrate a layer of a polymeric solution of a neutralized sulfonated EPDM terpolymer dissolved in a mixed solvent system of an organic liquid and a polar cosolvent, said organic liquid being selected from the group consisting of aromatic hydrocarbons, cyclic aliphatic ether, aliphathic ethers and organic aliphathic esters and mixture thereof, said solvent system containing less than 15 wt.% of polar cosolvent, a viscosity of said solvent system being less than about 1000 cps. said solution containing about 0.1 to about 20 wt.% of said neutralized sulfonated EPDM terpolymer, said neutralized sulfonated EPDM terpolymer having about 10 to about 200 meq. of neutralized sulfonate groups and depositing sufficient water onto said layer of said polymer solution to transform said polymeric solution into an water insoluble elastomeric layer.
- 10. A coating process which comprises the step of depositing onto the surface of water a polymeric solution of a neutralized sulfonated EPDM terpolymer dissolved in a mixed solvent system of an organic liquid and a polar cosolvent, said organic liquid being selected from the group consisting of aromatic hydrocarbons, cyclic aliphatic ethers, aliphathic ethers and organic aliphathic esters and mixtures thereof, said solvent system containing less than 15 wt.% of polar cosolvent, a viscosity of said solvent system being less than about 100 cps. said solution containing about 0.1 to about 20 wt.% of said neutralized sulfonated EPDM terpolymers, terpolymer having about 10 to about 20 meq. of neutralized sulfonate groups, said water interacting with said polymeric solution thereby transforming said polymeric solution into an water insoluble elastomeric film on said surface of said water.
- 11. A process according to claim 7, wherein said elastomeric film is reverted to said polymeric solution by the further addition of said cosolvent.
- 12. A process according to claim 9, wherein said elastomeric film is reverted to said polymeric solution by the further addition of said cosolvent.
- 13. A process according to claim 10, wherein said elastomeric film is reverted to said polymeric solution by the further addition of said cosolvent.
- 14. A water insoluble elastic film according to claim 1, wherein said film is formed on an aqueous substrate.
Parent Case Info
This is a CIP of Ser. No. 136,837, filed Apr. 3, 1980, now U.S. Pat. No. 4,322,329, which is a CIP of Ser. No. 106,027, filed Dec. 21, 1979 now U.S. Pat. No. 4,282,130.
US Referenced Citations (6)
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
136837 |
Apr 1980 |
|
Parent |
106027 |
Dec 1979 |
|