Patent Grant
7977444
The present invention relates to a process for obtaining a polymer comprising 1-hexene or higher alpha-olefins derived units, by using a specific class of metallocene compounds, that allows to obtain polymers having high molecular weight in high yields.
Metallocene compounds are well known catalyst components for the polymerization of alpha-olefins. However they are mainly used for the (co)polymerization of ethylene, propylene and 1-butene. Polymerization of 1-hexene and higher alpha olefins by using metallocene catalyst components is discussed in some papers. For example U.S. Pat. No. 6,566,544 discloses in table 10 the polymerization of 1-hexene by using Ind2ZrMe2 and bis(2-phenylindenyl)zirconium dimethyl. The molecular weight of the obtained polymers are quite low. in Macromol. Chem. Phys. 200, 1208-1219 (1999), 1-hexene is polymerized in the presence of iPr(CpFlu)ZrCl2. The polymer obtained has a syndiotactic structure and the molecular mass of the polymer obtained is close to 20000 gmol−1. In Journal of Polymer Science: Part A: Polymer Chemistry, vol 37, 283-292 (1999) a series of metallocene compounds have been tested in 1-hexene polymerization. Rac-[Me2Ge(η5-C5H-2,3,5-Me3)MCl2 (M=Zr or Hf) allows to obtain 1-hexene polymers having a very high molecular weight. However the syntesis of these compounds can be difficult and the polymerization activity can be increased.
WO 01/46278 relates to a polymerization process for producing a copolymer containing from 60 to 94% mol of alpha olefins having from 3 to 6 carbon atoms, and from 6 to 40% mol of alpha olefins having at least one carbon atom more than the first one. In the examples propylene is copolymerized with 1-hexene. These copolymers are obtained with a metallocene compound different from that one used in the present invention, moreover the molecular weight of the obtained copolymers can still be improved. Finally the present invention is directed to a copolymer that contains a smaller amount of propylene or 1-butene.
Thus there is still the need to find a class of metallocene compounds able to give 1-hexene or higher alpha-olefins (co)polymers having an high molecular weight in high yields.
An object of the present invention is a process for preparing a polymer containing derived units of one or more alpha olefins of formula CH2═CHW wherein W is a C3-C10 hydrocarbon radical and optionally from 0 to 81% by mol; preferably from 0 to 70% by mol, more preferably from 0 to 59% by mol, of derived units of propylene or 1-butene, comprising contacting under polymerization conditions one or more alpha olefins of formula CH2═CHW and optionally propylene or 1-butene in the presence of a catalyst system obtainable by contacting:
wherein
M is an atom of a transition metal selected from those belonging to group 3, 4, 5, 6 or to the lanthanide or actinide groups in the Periodic Table of the Elements; preferably M is titanium, zirconium or hafnium;
p is an integer from 0 to 3, preferably p is 2, being equal to the formal oxidation state of the metal M minus 2;
X, same or different, is a hydrogen atom, a halogen atom, or a R, OR, OSO2CF3, OCOR, SR, NR2 or PR2 group, wherein R is a are linear or branched, cyclic or acyclic, C1-C40-alkyl, C2-C40 alkenyl, C2-C40 alkynyl, C6-C40-aryl, C7-C40-alkylaryl or C7-C40-arylalkyl radicals; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R is a linear or branched C1-C20-alkyl radical; or two X can optionally form a substituted or unsubstituted butadienyl radical or a OR′O group wherein R′ is a divalent radical selected from C1-C40 alkylidene, C6-C40 arylidene, C7-C40 alkylarylidene and C7-C40 arylalkylidene radicals; preferably X is a hydrogen atom, a halogen atom or a R group; more preferably X is chlorine or a C1-C10-alkyl radical; such as methyl, or ethyl radicals;
L is a divalent C1-C40 hydrocarbon radical optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements or a divalent silylene radical containing up to 5 silicon atom; preferably L is a divalent bridging group selected from C1-C40 alkylidene, C3-C40 cycloalkylidene, C6-C40 arylidene, C7-C40 alkylarylidene, or C7-C40 arylalkylidene radicals optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements, and silylene radical containing up to 5 silicon atoms such as SiMe2, SiPh2; preferably L is a group (Z(R″)2)n wherein Z is a carbon or a silicon atom, n is 1 or 2 and R″ is a C1-C20 hydrocarbon radical optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R″ is a linear or branched, cyclic or acyclic, C1-C20-alkyl, C2-C20 alkenyl, C2-C20 alkynyl, C6-C20-aryl, C7-C20-alkylaryl or C7-C20-arylalkyl radicals optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; more preferably the group (Z(R″)2)n is Si(CH3)2, SiPh2, SiPhMe, SiMe(SiMe3), CH2, (CH2)2, and C(CH3)2;
R1 and R2, equal to or different from each other, are C1-C40 hydrocarbon radicals optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably they are linear or branched, cyclic or acyclic, C1-C40-alkyl, C2-C40 alkenyl, C2-C40 alkynyl, C6-C40-aryl, C7-C40-alkylaryl or C7-C40-arylalkyl radicals; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; more preferably R1 and R2 are linear or branched, C1-C20-alkyl radicals; more preferably R1 and R2 are methyl or ethyl radicals;
T, equal to or different from each other, is a moiety of formula (IIa) or (IIb):
wherein the atom marked with the symbol * bonds the atom marked with the same symbol in the compound of formula (I);
R3 is a hydrogen atom or a C1-C40 hydrocarbon radical optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R3 is a linear or branched, cyclic or acyclic, C1-C40-alkyl, C2-C40 alkenyl, C2-C40 alkynyl, C6-C40-aryl, C7-C40-arylalkyl or a C7-C40-alkylaryl radical; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; more preferably R3 is a linear or branched, C1-C20-alkyl C6-C40-aryl, C7-C40-arylalkyl radical; even more preferably R3 is a C6-C20-aryl radical optionally substituted with one or more C1-C10 alkyl groups;
R4 and R6, equal to or different from each other, are hydrogen atoms or C1-C40 hydrocarbon radicals optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R4 and R6, equal to or different from each other, are hydrogen atoms or linear or branched, cyclic or acyclic, C1-C40-alkyl, C2-C40 alkenyl, C2-C40 alkynyl, C6-C40-aryl, C7-C40-alkylaryl or C7-C40-arylalkyl radicals; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R4 and R6 are hydrogen atoms;
R5 is a hydrogen atom or a C1-C40 hydrocarbon radical optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R5 is a linear or branched, cyclic or acyclic, C1-C40-alkyl, C2-C40 alkenyl, C2-C40 alkynyl, C6-C40-aryl, C7-C40-alkylaryl or C7-C40-arylalkyl radicals; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; more preferably R5 is a linear or branched, saturated or unsaturated C1-C20-alkyl radical; even more preferably R5 is a methyl or ethyl radical;
R7 and R8, equal to or different from each other, are hydrogen atoms or C1-C40 hydrocarbon radicals optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; R7 and R8 can optionally form a saturated or unsaturated, 5 or 6 membered rings, said ring can bear C1-C20 alkyl radicals as substituents; preferably R7 and R8 are hydrogen atoms or linear or branched, cyclic or acyclic, C1-C40-alkyl, C2-C40 alkenyl, C2-C40 alkynyl, C6-C40-aryl, C7-C40-alkylaryl or C7-C40-arylalkyl radicals; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements;
preferably R8 is a hydrogen atom or a linear or branched, saturated or unsaturated C1-C20-alkyl radical; more preferably R8 is a methyl or ethyl radical;
preferably R7 is a C1-C40-alkyl, C6-C40-aryl or a C7-C40-arylalkyl; more preferably R7 is a group of formula (III)
wherein R9, R10, R11, R12 and R13, equal to or different from each other, are hydrogen atoms or linear or branched, cyclic or acyclic, C1-C20-alkyl, C2-C20 alkenyl, C2-C20 alkynyl, C6-C20-aryl, C7-C20-alkylaryl or C7-C20-arylalkyl radicals; optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R9, and R12 are a hydrogen atoms; R10, R11 and R13 are preferably hydrogen atoms or linear or branched, cyclic or acyclic, C1-C10-alkyl radicals; more preferably R13 and R10 are linear or branched, cyclic or acyclic, C1-C10-alkyl radicals such as methyl or ethyl radicals and R9, R11, and R12 are hydrogen atoms;
Metallocene compounds of formula (I) are well known in the art, they can be prepared according to known procedure, such as those described in WO 01/44318, WO 03/045964, PCT/EP02/13552 and DE 10324541.3.
For the purpose of the present invention the term “racemic form” means that the same substituents on the two cyclopentadienyl moieties are on the opposite side with respect to the plane containing the zirconium and the centre of the said cyclopentadienyl moieties. “racemic-like form” means that the bulkier substituents of the two cyclopentadienyl moieties on the metallocene compound are on the opposite side with respect to the plane containing the zirconium and the centre of the said cyclopentadienyl moieties as shown in the following compound:
In one embodiment the compound of formula (I) has the following formula (IV)
wherein M, X, p, L, R1, R2, R7 and R8 have the above described meaning.
In an alternative embodiment the compound of formula (I) has the following formula (V)
wherein
M, X, p, L, R1, R2, R3, R4, R5, R6, R7 and R8 have the above described meaning.
Alumoxanes used as component b) can be obtained by reacting water with an organo-aluminum compound of formula HjAlU3-j or HjAl2U6-j, where the U substituents, same or different, are hydrogen atoms, halogen atoms, C1-C20-alkyl, C3-C20-cyclalkyl, C6-C20-aryl, C7-C20-alkylaryl or C7-C20-arylalkyl radicals, optionally containing silicon or germanium atoms, with the proviso that at least one U is different from halogen, and j ranges from 0 to 1, being also a non-integer number. In this reaction the molar ratio of Al/water is preferably comprised between 1:1 and 100:1.
Alumoxanes used as component b) can be obtained by reacting water with an organo-aluminium compound of formula HjAlU3-j or HjAl2U6-j, where the U substituents, same or different, are hydrogen atoms, halogen atoms, C1-C20-alkyl, C3-C20-cyclalkyl, C6-C20-aryl, C7-C20-alkylaryl or C7-C20-arylalkyl radicals, optionally containing silicon or germanium atoms, with the proviso that at least one U is different from halogen, and j ranges from 0 to 1, being also a non-integer number. In this reaction the molar ratio of Al/water is preferably comprised between 1:1 and 100:1.
The alumoxanes used in the process according to the invention are considered to be linear, branched or cyclic compounds containing at least one group of the type:
wherein the substituents U, same or different, are defined above.
In particular, alumoxanes of the formula:
can be used in the case of linear compounds, wherein n1 is 0 or an integer of from 1 to 40 and the substituents U are defined as above; or alumoxanes of the formula:
can be used in the case of cyclic compounds, wherein n2 is an integer from 2 to 40 and the U substituents are defined as above.
Examples of alumoxanes suitable for use according to the present invention are methylalumoxane (MAO), tetra-(isobutyl)alumoxane (TIBAO), tetra-(2,4,4-trimethyl-pentyl)alumoxane (TIOAO), tetra-(2,3-dimethylbutyl)alumoxane (TDMBAO) and tetra-(2,3,3-trimethylbutyl)alumoxane (TTMBAO).
Particularly interesting cocatalysts are those described in WO 99/21899 and in WO01/21674 in which the alkyl and aryl groups have specific branched patterns.
Non-limiting examples of aluminum compounds that can be reacted with water to give suitable alumoxanes (b), described in WO 99/21899 and WO01/21674, are:
tris(2,3,3-trimethyl-butyl)aluminum, tris(2,3-dimethyl-hexyl)aluminum, tris(2,3-dimethyl-butyl)aluminum, tris(2,3-dimethyl-pentyl)aluminum, tris(2,3-dimethyl-heptyl)aluminum, tris(2-methyl-3-ethyl-pentyl)aluminum, tris(2-methyl-3-ethyl-hexyl)aluminum, tris(2-methyl-3-ethyl-heptyl)aluminum, tris(2-methyl-3-propyl-hexyl)aluminum, tris(2-ethyl-3-methyl-butyl)aluminum, tris(2-ethyl-3-methyl-pentyl)aluminum, tris(2,3-diethyl-pentyl)aluminum, tris(2-propyl-3-methyl-butyl)aluminum, tris(2-isopropyl-3-methyl-butyl)aluminum, tris(2-isobutyl-3-methyl-pentyl)aluminum, tris(2,3,3-trimethyl-pentyl)aluminum, tris(2,3,3-trimethyl-hexyl)aluminum, tris(2-ethyl-3,3-dimethyl-butyl)aluminum, tris(2-ethyl-3,3-dimethyl-pentyl)aluminum, tris(2-isopropyl-3,3-dimethyl-butyl)aluminum, tris(2-trimethylsilyl-propyl)aluminum, tris(2-methyl-3-phenyl-butyl)aluminum, tris(2-ethyl-3-phenyl-butyl)aluminum, tris(2,3-dimethyl-3-phenyl-butyl)aluminum, tris(2-phenyl-propyl)aluminum, tris[2-(4-fluoro-phenyl)-propyl]aluminum, tris[2-(4-chloro-phenyl)-propyl]aluminum, tris[2-(3-isopropyl-phenyl)-propyl]aluminum, tris(2-phenyl-butyl)aluminum, tris(3-methyl-2-phenyl-butyl)aluminum, tris(2-phenyl-pentyl)aluminum, tris[2-(pentafluorophenyl)-propyl]aluminum, tris[2,2-diphenyl-ethyl]aluminum and tris[2-phenyl-2-methyl-propyl]aluminum, as well as the corresponding compounds wherein one of the hydrocarbyl groups is replaced with a hydrogen atom, and those wherein one or two of the hydrocarbyl groups are replaced with an isobutyl group.
Amongst the above aluminum compounds, trimethylaluminium (TMA), triisobutylaluminium (TIBA), tris(2,4,4-trimethyl-pentyl)aluminum (TIOA), tris(2,3-dimethylbutyl)aluminum (TDMBA) and tris(2,3,3-trimethylbutyl)aluminum (TTMBA) are preferred.
Non-limiting examples of compounds able to form an alkylmetallocene cation are compounds of formula D+E−, wherein D+ is a Brønsted acid, able to donate a proton and to react irreversibly with a substituent X of the metallocene of formula (I) and E− is a compatible anion, which is able to stabilize the active catalytic species originating from the reaction of the two compounds, and which is sufficiently labile to be removed by an olefinic monomer. Preferably, the anion E− comprises one or more boron atoms. More preferably, the anion E− is an anion of the formula BAr4(−), wherein the substituents Ar which can be identical or different are aryl radicals such as phenyl, pentafluorophenyl or bis(trifluoromethyl)phenyl. Tetrakis-pentafluorophenyl borate is particularly preferred compound, as described in WO 91/02012. Moreover, compounds of formula BAr3 can be conveniently used. Compounds of this type are described, for example, in the International patent application WO 92/00333. Other examples of compounds able to form an alkylmetallocene cation are compounds of formula BAr3P wherein P is a substituted or unsubstituted pyrrol radical. These compounds are described in WO01/62764. Compounds containing boron atoms can be conveniently supported according to the description of DE-A-19962814 and DE-A-19962910. All these compounds containing boron atoms can be used in a molar ratio between boron and the metal of the metallocene comprised between about 1:1 and about 10:1; preferably 1:1 and 2.1; more preferably about 1:1.
Non limiting examples of compounds of formula D+E− are:
Triethylammoniumtetra(phenyl)borate,
Tributylammoniumtetra(phenyl)borate,
Trimethylammoniumtetra(tolyl)borate,
Tributylammoniumtetra(tolyl)borate,
Tributylammoniumtetra(pentafluorophenyl)borate,
Tributylammoniumtetra(pentafluorophenyl)aluminate,
Tripropylammoniumtetra(dimethylphenyl)borate,
Tributylammoniumtetra(trifluoromethylphenyl)borate,
Tributylammoniumtetra(4-fluorophenyl)borate,
N,N-Dimethylbenzylammonium-tetrakispentafluorophenylborate,
N,N-Dimethylhexylamonium-tetrakispentafluorophenylborate,
N,N-Dimethylaniliniumtetra(phenyl)borate,
N,N-Diethylaniliniumtetra(phenyl)borate,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)aluminate,
N,N-Dimethylbenzylammonium-tetrakispentafluorophenylborate,
N,N-Dimethylhexylamonium-tetrakispentafluorophenylborate,
Di(propyl)ammoniumtetrakis(pentafluorophenyl)borate,
Di(cyclohexyl)ammoniumtetrakis(pentafluorophenyl)borate,
Triphenylphosphoniumtetrakis(phenyl)borate,
Triethylphosphoniumtetrakis(phenyl)borate,
Diphenylphosphoniumtetrakis(phenyl)borate,
Tri(methylphenyl)phosphoniumtetrakis(phenyl)borate,
Tri(dimethylphenyl)phosphoniumtetrakis(phenyl)borate,
Triphenylcarbeniumtetrakis(pentafluorophenyl)borate,
Triphenylcarbeniumtetrakis(pentafluorophenyl)aluminate,
Triphenylcarbeniumtetrakis(phenyl)aluminate,
Ferroceniumtetrakis(pentafluorophenyl)borate,
Ferroceniumtetrakis(pentafluorophenyl)aluminate.
Triphenylcarbeniumtetrakis(pentafluorophenyl)borate, and
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate.
Organic aluminum compounds used as compound iii) are those of formula HjAlU3-j or HjAl2U6-j as described above.
The polymerization process of the present invention can be carried out in liquid phase, optionally in the presence of an inert hydrocarbon solvent. Said hydrocarbon solvent can be either aromatic (such as toluene) or aliphatic (such as propane, hexane, heptane, isobutane, cyclohexane and 2,2,4-trimethylpentane). Preferably, the polymerization process of the present invention is carried out by using the alpha olefin of formula CH2═CHW wherein W is a C3-C10 hydrocarbon radical such as 1-hexene or 1-octene as polymerization medium, i.e. the same olefin that is going to be polymerizated for example 1-hexene is used as polymerization medium when a 1-hexene based polymer is the wished polymer.
The polymerization temperature preferably ranges from 0° C. to 250° C.; preferably comprised between 20° C. and 150° C. and, more particularly between 40° C. and 90° C.;
The molecular weight distribution can be varied by using mixtures of different metallocene compounds or by carrying out the polymerization in several stages which differ as to the polymerization temperature and/or the concentrations of the molecular weight regulators and/or the monomers concentration. Moreover by carrying out the polymerization process by using a combination of two different metallocene compounds of formula (I) a polymer endowed with a broad melting is produced.
With the process of the present invention isotactic polymers endowed with high molecular weights can be obtained in high yields.
With the process of the present invention polymers containing derived units of one or more alpha olefins of formula CH2═CHW wherein W is a C3-C10 hydrocarbon radical and optionally from 0 to 81% by mol of derived units of propylene or 1-butene can be obtained. Examples of alpha olefins of formula CH2═CHW are 1-pentene; 1-hexene; 1-octene and 1-decene. Preferably 1-hexene and 1-octene are used; more preferably 1-hexene is used.
When said alpha olefins of formula CH2═CHW are copolimerized with propylene or 1-butene preferably the obtained copolymer has a content of derived units of propylene or 1-butene ranging from 0.1% by mol to 59% by mol; more preferably the content of propylene or 1-butene ranges from 10% by mol to 50% by mol, even more preferably it ranges from 19% by mol to 40% by mol.
The obtained copolymer is endowed with the following properties:
In said copolymer the alpha olefin of formula CH2═CHW is preferably 1-hexene and 1-octene.
The copolymers, other than the above properties, are further endowed with a very low Shore A (measured according to ISO 868), in particular the shore A is lower than 30; preferably lower than 25; more preferably lower than 20; and furthermore the tensile modulus is lower than 20 MPa (measured according to ASTM 5026,4092 e 4065); preferably lower than 15MPa; more preferably lower than 11 MPa.
A further preferred range of content of derived units of propylene and 1-butene is from 19% by mol to 59% by mol; even more preferably from 30% by mol to 59% by mol.
The process of the present invention is particularly suitable for preparing homopolymers of alpha olefins of formula CH2═CHW wherein W is a C3-C10 hydrocarbon radical, in particular homopolymers of 1-hexene or 1-octene; preferably homopolymer of 1-hexene are produced.
The homopolymer prepared according to the present invention can be used for application known in the art such as masterbaches or in adhesive formulations.
Even if the homopolymer of the present invention are not exemplified, their preparation can be easily achieved by the skilled man once it is know the process for preparing the copolymers. In fact it is sufficient to avoid to add the comonomer in the processes exemplified above for obtaining the wished homopolymer.
The copolymers obtainable with the process of the present invention described above, can have the same uses of the homopolymer and furthermore they can be used as compatibilizer. For example they can improve the dispersion of a rubber phase in an crystalline matrix, due to the presence of the comonomer that help to compatibilize the two phases, so that a material having an improved izod impact value can be obtained.
The following examples are given to illustrate and not to limit the invention.
General Procedures and Characterizations
All chemicals were handled under nitrogen using standard Schlenk techniques. Methylalumoxane (MAO) was received from Albemarle as a 30% wt/vol toluene solution and used as such.
Pure triisobutylaluminum (TIBA) was used as such.
Isododecane was purified over aluminum oxide to reach a water content below 10 ppm.
A 101 g/L TIBA/isododecane solution was obtained by mixing the above components.
The melting points of the polymers (Tm) were measured by Differential Scanning Calorimetry (D.S.C.) on a Perkin Elmer DSC-7 instrument, according to the standard method. A weighted sample (5-7 mg) obtained from the polymerization was sealed into aluminum pans and heated to 180° C. at 10° C./minute. The sample was kept at 180° C. for 5 minutes to allow a complete melting of all the crystallites, then cooled to 20° C. at 10° C./minute. After standing 2 minutes at 20° C., the sample was heated for the second time to 180° C. at 10° C./min. In this second heating run, the peak temperature was taken as the melting temperature (Tm) and the area of the peak as melting enthalpy (ΔHf).
Molecular weight parameters were measured using a Waters 150C ALC/GPC instrument (Waters, Milford, Mass., USA) equipped with four mixed-gel columns PLgel 20 μm Mixed-A LS (Polymer Laboratories, Church Stretton, United Kingdom). The dimensions of the columns were 300×7.8 mm. The solvent used was TCB and the flow rate was kept at 1.0 mL/min. Solution concentrations were 0.1 g/dL in 1,2,4 trichlorobenzene (TCB). 0.1 g/L of 2,6- di-t-butyl-4-methyl phenol (BHT) was added to prevent degradation and the injection volume was 300 μL. All the measurements were carried out at 135° C. GPC calibration is complex, as no well-characterized narrow molecular weight distribution standard reference materials are available for 1-hexene polymers. Thus, a universal calibration curve was obtained using 12 polystyrene standard samples with molecular weights ranging from 580 to 13,200,000. It was assumed that the K values of the Mark-Houwink relationship were: KPS=1.21×10−4, dL/g and KPH=1.78×10−4 dL/g for polystyrene and poly-1-hexene respectively, for the copolymers the same KPH has been used. The Mark-Houwink exponents a were assumed to be 0.706 for polystyrene and 0.725 for poly-1-hexene and copolymers. Even though, in this approach, the molecular parameters obtained were only an estimate of the hydrodynamic volume of each chain, they allowed a relative comparison to be made.
The intrinsic viscosity (I.V.) was measured in tetrahydronaphtalene (THN) at 135° C. rac dimethylsilandiylbis-6-[2,5-dimethyl-3-(2′-methyl-phenyl)cyclopentadienyl-[1,2-b]-thiophene]zirconium dichloride (A-1) was prepared according to WO01/44318.
Preparation of Catalyst Systems
Preparation of Catalyst System C-1 A-1/MAO:TIBA 2:1 (400)
9.8 cc of TIBA/isododecane solution (101 g/L) were mixed with 1.91 cc of MAO/toluene solution (Albemarle -30% wt) to obtain a MAO/TIBA molar ratio of 2:1. The solution was stirred for 1 hour at room temperature. Then, 26 mg of A-1 were dissolved in the solution.
The orange solution did not show any trace of residual solid.
The final solution was diluted with 4 cc of isododecane to reach a concentration of 100 g/L.
Polymerization Tests
1-hexene Copolymerisation
An amount of purified liquid 1-hexene as indicated in table 1 was transferred reactor at room temperature in a 250 glass vessel under nitrogen atmosphere. The reactor had been maintained under slight positive nitrogen atmosphere at all time. Consequently the temperature was increased to the polymerization temperature indicated in table 2 and an over pressure of 1 bar-g of propylene or 1-butene was fed in the autoclave. The catalyst solution, (ageing indicated in table 2), was fed into the liquid, under a nitrogen flow. The pressure was increased adding propylene until reaching the polymerisation pressure indicated in table 2. The polymerization was conducted for 60 minutes, then stopped by flashing the monomers. The polymer was precipitated by adding acetone to the polymer solution. The recovered polymer was dried at 50° C. under vacuum. Polymerization and polymer data are reported in table 1.
1-hexene/propylene Copolymerisation
4 mmol of Al(i-Bu)3 (as a 1M solution in hexane) and 1000 g of 1-hexene were charged at room temperature in a 4-L jacketed stainless-steel autoclave, previously purified by washing with an Al(i-Bu)3 solution in hexane and dried at 50° C. in a stream of nitrogen. The autoclave was then thermostated at the polymerisation temperature, 70° C., and then the solution containing the catalyst/cocatalyst solution indicated in table 3 prepared 12 hours before was injected in the autoclave by means of nitrogen pressure through the stainless-steel vial. The monomer was fed until a pressure indicated in table 3 and the polymerisation carried out at constant temperature for 1 hour. The pressure into the autoclave is decreased until 20 bar-g and the polymerization solution is discharged into a heated steel tank containing water at 70° C. The tank heating is switched off and a flow of nitrogen at 0.5 bar-g is fed. After cooling at room temperature, the steel tank is opened and the wet polymer collected and dried at 70° C. under reduced pressure. The polymerisation conditions and the characterisation data of the obtained polymers are reported in Table 2.
The shore A (ISO 868) of copolymers of examples 6 and 7 has been measured, the results are reported in table 3. The tensile modulus of a sample of copolymers obtained in examples 6 and 7 has been measured according to ASTM 5026, 4092 and 4065 as follows:
Specimens for tensile test are cut from compression moulding plaques. Specimen sizes are approx. 40 mm long overall, 20 mm inter-clamp length, 6 mm width and thickness was 1 mm. Specimen is clamped in the SEIKO DMS 6100 tensile DMTA.
The applied frequency is 1 Hz.
Specimens are heated from −80° C. to +140° C. with 2° C./min as heating rate; specimens are re-clamped at the low temperature.
The results are reported in table 3
| Number | Date | Country | Kind |
|---|---|---|---|
| 04101020 | Mar 2004 | EP | regional |
| 04104350 | Sep 2004 | EP | regional |
This application is the U.S. national phase of International Application PCT/EP2005/002480, filed Mar. 8, 2005, claiming priority to European Patent Application 04101020.8 filed Mar. 12, 2004, and European Patent Application 04104350.6 filed Sep. 9, 2004, and the benefit under 35 U.S.C. 119(e) of U.S. Provisional Application No. 60/554,110, filed Mar. 17, 2004 and U.S. Provisional Application No. 60/610,065 filed Sep. 15, 2004; the disclosures of International Application PCT/EP2005/002480, European Patent Applications 04101020.8 and 04104350.6 and U.S. Provisional Application Nos. 60/554,110 and 60/610,065, each as filed, are incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2005/002480 | 3/8/2005 | WO | 00 | 9/12/2006 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2005/095473 | 10/13/2005 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5043515 | Slaugh et al. | Aug 1991 | A |
| 5066631 | Sangokoya et al. | Nov 1991 | A |
| 5145819 | Winter et al. | Sep 1992 | A |
| 5239022 | Winter et al. | Aug 1993 | A |
| 5243001 | Winter et al. | Sep 1993 | A |
| 5324800 | Welborn, Jr. et al. | Jun 1994 | A |
| 5556928 | Devore et al. | Sep 1996 | A |
| 5847177 | Sangokoya et al. | Dec 1998 | A |
| 6232421 | Fujita et al. | May 2001 | B1 |
| RE37384 | Winter et al. | Sep 2001 | E |
| 6444607 | Gonioukh et al. | Sep 2002 | B1 |
| 6566544 | Waymouth et al. | May 2003 | B1 |
| 6664208 | Fujita et al. | Dec 2003 | B1 |
| 6953829 | Kratzer et al. | Oct 2005 | B2 |
| 7101940 | Schottek et al. | Sep 2006 | B2 |
| 20060252637 | Okumura | Nov 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 2220243 | Sep 1997 | CA |
| 19962814 | Jun 2001 | DE |
| 19962910 | Jul 2001 | DE |
| 10324541 | Dec 2004 | DE |
| 129368 | Dec 1984 | EP |
| 172961 | Mar 1986 | EP |
| 480390 | Apr 1992 | EP |
| 485820 | May 1992 | EP |
| 485822 | May 1992 | EP |
| 485823 | May 1992 | EP |
| 604908 | Jul 1994 | EP |
| 1327636 | Jul 2003 | EP |
| 999725 | Jul 1965 | GB |
| 9102012 | Feb 1991 | WO |
| 9200333 | Jan 1992 | WO |
| 9622995 | Aug 1996 | WO |
| 9818801 | May 1998 | WO |
| 9822486 | May 1998 | WO |
| 9921899 | May 1999 | WO |
| 9924446 | May 1999 | WO |
| 9958539 | Nov 1999 | WO |
| 0121674 | Mar 2001 | WO |
| 0144318 | Jun 2001 | WO |
| 0146278 | Jun 2001 | WO |
| 0147939 | Jul 2001 | WO |
| 0162764 | Aug 2001 | WO |
| 03045964 | Jun 2003 | WO |
| 2004050713 | Jun 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20080281061 A1 | Nov 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60554110 | Mar 2004 | US | |
| 60610065 | Sep 2004 | US |