Process for preparation of hydrophilic or partially hydrophilic inorganic aerogels

Information

  • Patent Grant
  • 6365638
  • Patent Number
    6,365,638
  • Date Filed
    Wednesday, August 20, 1997
    26 years ago
  • Date Issued
    Tuesday, April 2, 2002
    22 years ago
Abstract
Process for preparation of hydrophilic or partially hydrophilic inorganic aerogels. The invention relates to a process for the preparation of hydrophilic or partially hydrophilic inorganic aerogels, which comprises pyrolyzing a hydrophobic inorganic aerogel in the presence of oxygen at temperatures in the range from 100 to 1000° C.
Description




BACKGROUND OF THE INVENTION




The invention relates to a process for preparation of hydrophilic or partially hydrophilic inorganic aerogels from hydrophobic inorganic aerogels.




1. Field of the Invention




Aerogels, in particular those with porosities of greater than 60% and densities of less than 0.6 g/cm


3


, have extremely low thermal conductivity and are therefore used as thermal insulation material, for example as described in EP-A-0 171 722.




2. Description of the Related Art




Aerogels in the wider sense, ie. in the sense of “gel with air as dispersion medium” are prepared by drying a suitable gel. The term “aerogel” in this sense is taken to mean aerogels in the narrower sense, xerogels and cryogels, a dried gel being termed an aerogel in the narrower sense if the gel liquid is removed to a very large extent at temperatures above the critical temperature and starting at pressures above the critical pressure. If, in contrast, the gel liquid is removed subcritically, for example with formation of a liquid-vapor boundary phase, then the resultant gel is termed a xerogel.




In the present application, the term aerogel is taken to mean aerogels in the wider sense, ie. in the sense of “gel with air as dispersion medium”.




This term is taken to exclude xerogels known from the earlier literature, for example those obtained by precipitation of silica (eg. DE-A-30 25 437 and DD-A296 898), or produced in the form of pyrogenic silica (eg. Aerosil®). In these cases, however, the preparation does not give a homogeneous three-dimensional gel structure which extends across relatively large distances.




Aerogels may fundamentally be divided into inorganic and organic aerogels.




Inorganic aerogels were known as early as 1931 (S. S. Kistler, Nature 1931, 127, 741). Since then, aerogels have been prepared from a wide variety of starting materials. For example, SiO


2


aerogels, Al


2


O


3


aerogels, TiO


2


aerogels, ZrO


2


aerogels, SnO


2


aerogels, Li


2


O aerogels, CeO


2


aerogels, V


2


O


5


aerogels and mixtures of these have been prepared (H. D. Gesser, P. C. Goswami, Chem. Rev. 1989, 89, 765ff). Organic aerogels made from a wide variety of starting materials, for example from melamine formaldehyde, have also been known for some years (R. W. Pekala, J. Mater. Sci. 1989, 24, 3221).




Inorganic aerogels can be prepared by two fundamentally different methods.




Firstly, SiO


2


aerogels, for example, can be prepared by acid hydrolysis and condensation of tetraethyl orthosilicate in ethanol. This gives a gel which can be dried supercritically with retention of the structure. Preparation processes based on this drying technique are known, for example, from EP-A-0 396 076, WO 92/03378 and WO 95/06617.




A fundamental alternative to supercritical drying is provided by a process for subcritical drying of SiO


2


gels, in which the SiO


2


gel can be obtained, f or example, by acid hydrolysis of tetraalkoxysilanes in a suitable organic solvent, using water. After exchanging the solvent for a suitable organic solvent, the resultant gel is reacted with a silylating agent, in a further step. The SiO


2


gel thus obtained can then be dried from an organic solvent in air. Aerogels with densities of less than 0.4 g/cm


3


and porosities of greater than 60% can be attained in this way. The preparation process based on this drying technique is described in detail in WO 94/25149.




The gels described above may moreover be mixed with tetraalkoxysilanes and aged before drying in the aqueous alcoholic solution, in order to increase the strength of the gel structure, for example as disclosed in WO 92/20623.




However, the tetraalkoxysilanes used as starting materials in the processes described above are exceptionally costly. A considerable reduction in costs can be achieved by using water glass as starting material for preparing the SiO


2


gels, for example starting with an aqueous water glass solution and using an ion-exchange resin to prepare a silica which polycondenses on addition of a base to give an SiO


2


gel. After exchanging the aqueous medium for a suitable organic solvent, the resultant gel is then reacted with a chlorine-containing silylating agent, in a further step. The SiO


2


gel thus obtained, modified on its surface with, for example, methylsilyl groups, can then likewise be dried in air from an organic solvent. The preparation process based on this technique is known from DE-A-43 42 548. Alternative processes relating to the preparation of an SiO


2


hydrogel based on water glass followed by subcritical drying are described in the German Patent Applications 195 41 715.1 and 195 41 992.8.




German Patent Application 195 02 453.2 moreover describes the use of chlorine-free silylating agents in the preparation of subcritically dried aerogels.




German Patent Application 195 34 198.8, furthermore, describes an organofunctionalization using organo-functionalized silylating agents in the preparation of subcritically dried aerogels.




EP-A-0 606 638 discloses, furthermore, the preparation of SiO


2


aerogels containing carbon particles by heating organically modified SiO


2


aerogels in the presence of at least one pyrolyzable hydrocarbon gas and/or at least one inert gas. The organic groups on the surface of the aerogels and/or those of the hydrocarbon gas are oxidized here in an oxygen-free atmosphere to give elemental carbon.




Depending on the solvent used in the supercritical drying, the aerogels obtained by supercritical drying are hydrophilic because of OH groups on the internal surface (supercritical drying from CO


2


) or hydrophobic in the short term because of alkoxy groups on the internal surface (supercritical drying from alcohols). However, in the long term a reaction of the alkoxy groups with water from the surroundings takes place and leads to formation of hydroxide groups on the internal surface, again giving a hydrophilic aerogel.




The formation of a hydrophilic aerogel can be avoided by a hydrophobicization step during the supercritical drying. For this, a hydrophobicizing agent, for example Me


2


Si(OMe)


2


, can be used, as disclosed in EP-A-0 396 076, for example. The methylsilyl groups on the internal surface make the resultant aerogels permanently hydrophobic.




As a result of the preparation process (silylation before drying), subcritically dried aerogels are permanently hydrophobic. Since the subcritical drying of aerogels requires unreactive, hydrophobic internal gel surfaces, direct preparation of hydrophilic, subcritically dried aerogels is impossible.




For many applications, however, a hydrophilic or partially hydrophilic internal surface of the aerogels is precisely what is essential or advantageous.




It was therefore an object of the present invention to provide a process for preparation of hydrophilic or partially hydrophilic inorganic aerogels, but without having to accept the disadvantage of supercritical drying, with its disproportionately high technical complexity.




This object is achieved by means of a process in which a hydrophobic inorganic, preferably subcritically dried, aerogel is pyrolyzed in the presence of oxygen at temperatures in the range from 100 to 1000° C.




BRIEF SUMMARY OF THE INVENTION




Not Applicable




DETAILED DESCRIPTION OF THE INVENTION




For the purposes of the present application, the term “the presence of oxygen” is taken to mean that a sufficient amount of oxygen is present to oxidize the surface groups of the aerogels, it being possible for this amount to be present in any formulation known to the person skilled in the art (e.g.: air, oxygen-air mixture and/or oxygen-inert gas mixture).




For the purposes of the present application, the term “inorganic aerogel” is taken to mean an aerogel whose preparation has been based on inorganic materials.




The term “aerogels based on inorganic materials” is taken, in particular, to include those aerogels which have been modified, for example, by silylation.




Preference is given to aerogels having hydrophobic surface groups, said aerogels consisting predominantly of SiO


2


, Al


2


O


3


, TiO


2


, ZrO


2


, or mixtures of these. Such aerogels having hydrophobic surface groups can be prepared by any process known to the person skilled in the art. Particular preference is given to hydrophobic SiO


2


-containing aerogels, in particular SiO


2


aerogels.




In a preferred embodiment, the aerogel is pyrolyzed at temperatures from 100 to 1000° C., particularly preferably at from 150 to 800° C., in particular at from 250 to 650° C., in a gentle flow of air.




The duration of the pyrolysis is essentially determined by the surface modification and the density of the material of the aerogels. The duration of the pyrolysis is preferably less than 10 hours, particularly preferably less than 1 hour.




If partially hydrophilic aerogels are to be prepared, the temperature and the duration of the pyrolysis should be adjusted so that only an appropriate proportion of the organic surface groups pyrolyzes.




If the aerogels have different organic groups on their internal surface, the different decomposition temperature of the individual organic groups can be used to pyrolyze the appropriate groups in a controlled fashion and in accordance with the desired degree of hydrophilicity. In the case of aerogels having both phenyl and methyl groups on their internal surface, for example, properties which are partly hydrophilic can then be achieved by pyrolysis at 450° C., which substitutes hydroxide groups for the methyl groups on the surface of a corresponding aerogel, but not for the phenyl groups which are present.











The novel preparation of the hydrophilic aerogels is described below using working examples, but without being restricted by these.




EXAMPLE 1




1 l of a sodium water glass solution (with a content of 7% by weight of SiO


2


and an Na


2


O:SiO


2


ratio of 1:3.3) was stirred with 0.5 l of an acid ion-exchange resin (stryene-divinylbenzene copolymer having sulfonic acid groups, commercially available under the name ®Duolite C20), until the pH of the aqueous solution was 2.3. The ion-exchange resin was then filtered off, and the aqueous solution was adjusted to pH 4.7, using 1 molar NaOH solution. The resultant gel was then aged for a further 3 hours at 85° C., and the water was then exchanged for acetone, using 3 l of acetone. The acetone-containing gel was then silylated with trimethylchlorosilane (5% by weight of trimethylchlorosilane per gram of wet gel). The gel was dried in air (3 hours at 40° C. then 2 hours at 50° C. and 12 hours at 150° C.).




The resultant transparent aerogel had a density of 0.2 g/cm


3


; its BET specific surface area was 480 m


2


/g and it was permanently hydrophobic.




The permanently hydrophobic aerogel thus prepared was pyrolyzed at 600° C. in a gentle flow of air in a tube furnace, for 1 hour. The resultant transparent aerogel had a density of 0.21 g/cm


3


, a BET specific surface area of 450 m


2


/g, a thermal conductivity λ of 20 mW/mK, and was hydrophilic.




EXAMPLE 2




1 l of a sodium water glass solution (with a content of 7% by weight of SiO


2


and an Na


2


O:SiO


2


ratio of 1:3.3) was stirred with 0.5 l of an acid ion-exchange resin (stryene-divinylbenzene copolymer having sulfonic acid groups, commercially available under the name ®Duolite C20), until the pH of the aqueous solution was 2.3. The ion-exchange resin was then filtered off, and the aqueous solution was adjusted to pH 4.7, using 1 molar NaOH solution. The resultant gel was then aged for a further 3 hours at 85° C., and the water was then exchanged for acetone, using 3 l of acetone. The acetone-containing gel was then silylated with a mixture of trimethylchlorosilane and diphenylmethylchlorosilane (2% by weight of trimethylchlorosilane per gram of wet gel and 2% by weight of diphenylmethylchlorosilane per gram of wet gel). The gel was dried in air (3 hours at 40° C. then 2 hours at 50° C. and 12 hours at 150° C.).




The resultant transparent aerogel had a density of 0.15 g/cm


3


; its BET specific surface area was 480 m


2


/g and it was permanently hydrophobic.




The permanently hydrophobic aerogel thus prepared was pyrolyzed at 450° C. in a gentle flow of air in a tube furnace, for 20 minutes. The resultant transparent aerogel had a density of 0.17 g/cm


3


, a BET specific surface area of 450 m


2


/g, a thermal conductivity λ of 22 mW/mK, and was only partially hydrophilic.




The thermal conductivity was measured using a hot wire method (see, for example, O. Nielsson, G. Rüschenpöhler, J. GroB, J. Fricke, High Temperatures—High Pressures, Vol. 21, 267-274 (1989)).



Claims
  • 1. A process for preparation of hydrophilic or partially hydrophilic inorganic aerogels which comprises pyrolyzing, in the presence of oxygen and at temperatures in the range from 250 to 1000° C., a hydrophobic inorganic aerogel having hydrophobic surface groups, said aerogel having been modified by silylation wherein the inorganic aerogel is selected from the group consisting of SiO2, Al2O3, TiO2, ZrO2 or mixtures thereof.
  • 2. The process as claimed in claim 1, wherein said hydrophobic aerogel is a subcritically dried aerogel.
  • 3. The process as claimed in claim 1, wherein said hydrophobic inorganic aerogel is pyrolyzed at a temperature in the range of from 250 to 800° C.
  • 4. The process as claimed in at least one of claim 1, wherein the pyrolysis is carried out in air.
  • 5. The process as claimed in at least one of claim 1, wherein the pyrolysis is carried out in a gentle flow of air.
  • 6. The process as claimed in claim 1 wherein the pyrolysis is carried out in less than 10 hours.
  • 7. The process as claimed in claim 1 wherein the pyrolysis is carried out in less than one hour.
Priority Claims (1)
Number Date Country Kind
195 06 141 Feb 1995 DE
CROSS REFERENCE TO RELATED APPLICATIONS

This application is filed under 35 C.F.R. 371 based on PCT/EP96/00741, filed Feb. 22, 1996.

PCT Information
Filing Document Filing Date Country Kind
PCT/EP96/00741 WO 00
Publishing Document Publishing Date Country Kind
WO96/26890 9/6/1996 WO A
US Referenced Citations (16)
Number Name Date Kind
4327065 von Dardel et al. Apr 1982 A
4667417 Graser et al. May 1987 A
4954327 Blount Sep 1990 A
4971779 Paine, Jr. et al. Nov 1990 A
5122291 Wolff et al. Jun 1992 A
5141806 Koontz Aug 1992 A
5270027 Balducci et al. Dec 1993 A
5275796 Tillotson et al. Jan 1994 A
5565142 Deshpande et al. Oct 1996 A
5587107 Schwertfeger et al. Dec 1996 A
5647962 Jansen et al. Jul 1997 A
5705535 Jansen et al. Jan 1998 A
5759506 Jansen et al. Jun 1998 A
5789075 Frank et al. Aug 1998 A
5795556 Jansen et al. Aug 1998 A
5811031 Jansen et al. Sep 1998 A
Foreign Referenced Citations (6)
Number Date Country
43 00 598 Jul 1994 DE
0018955 Nov 1980 EP
0537851 Apr 1993 EP
0658513 Jun 1995 EP
WO 9203378 Mar 1992 WO
WO 9506617 Mar 1995 WO
Non-Patent Literature Citations (2)
Entry
Hawley's Condensed Chemical Dictionary, Eleventh Edition, Edited by sax and Lewis, Sr. (Van Nostrand Reinhold Co., NY, NY, copyright 1987) pp. 985, Oct. 1989.*
G. Poelz et al., Nuclear Intruments and Methods, 195, No. 3, (1982) pp. 491-503, 1982.