Claims
- 1. A process for the preparation of an oriented electrical steel sheet having a high magnetic flux density comprising;
- providing a steel slab having a composition consisting essentially of 0.8 to 4.8% by weight Si, 0.012 to 0.050% by weight of acid soluble Al; up to 0.01 by weight of N, balance Fe and unavoidable impurities;
- heating said steel slab to a temperature of 1270.degree. C. or less;
- subjecting the heated slab to hot rolling to provide a hot rolled sheet;
- cold rolling the hot rolled sheet at least once or at least twice with intermediate annealing to provide a cold rolled sheet of final thickness;
- primary recrystallization annealing of the cold rolled sheet;
- said process further comprising:
- performing said primary recrystallization annealing to provide the cold rolled sheet with a selected crystal grain structure;
- nitriding the primary recrystallization annealed sheet for a short period of time in a temperature range of 800.degree. C. or less for precipitating nitride of Si.sub.3 N.sub.4 or (Si,Mn)N, whereby growth of crystal grains does not substantially occur during said nitriding;
- after completion of said nitriding, coating said nitrided sheet with an annealing separation agent;
- after coating said nitrided sheet, holding the coated nitrided sheet at a temperature range of 700.degree. C. to 800.degree. C. for at least four hours during temperature raising to final annealing temperature whereby said Si.sub.3 N.sub.4 or (Si,Mn)N nitride formed by the nitriding dissolves and re-precipitates allowing said nitride to transform to a thermally stable nitride of AlN or (Al,Si)N and said stable nitride of AlN or (Al,Si)N is uniformly distributed in the thickness direction of the steel sheet and growth of crystal grains does not substantially occur during said holding at 700.degree. C. to 800.degree. C. for at least four hours; and
- after said holding at 700.degree. C. to 800.degree. C. for at least four hours, heating said nitrided steel sheet to the final annealing temperature of about 1200.degree. C. and holding said nitrided steel sheet at the final annealing temperature in a 100% H.sub.2 atmosphere for purification.
- 2. A process for the preparation of an oriented electrical steel sheet having high magnetic flux density as claimed in claim 1 further comprising annealing said hot rolled sheet after hot rolling and prior to cold rolling.
- 3. A process for the preparation of an oriented electrical steel sheet having high magnetic flux density as claimed in claim 1 further comprising maintaining a partial pressure of nitrogen of 10% or more during said holding of said nitrided sheet at the temperature of 700.degree. C. to 800.degree. C. whereby the nitride formed by said nitriding dissolves and reprecipitates.
Priority Claims (1)
Number |
Date |
Country |
Kind |
3-000749 |
Jan 1991 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 07/819,371 filed on Jan. 6, 1992, now abandoned.
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
4929286 |
Komatsu et al. |
May 1990 |
|
5049205 |
Takahashi et al. |
Sep 1991 |
|
5082509 |
Ushigami et al. |
Jan 1992 |
|
Foreign Referenced Citations (8)
Number |
Date |
Country |
0219611 |
Apr 1987 |
EPX |
0318051 |
May 1989 |
EPX |
0339474 |
Nov 1989 |
EPX |
2262703 |
Sep 1975 |
FRX |
B30-3651 |
May 1955 |
JPX |
B40-15644 |
Jul 1965 |
JPX |
46-937 |
Jan 1971 |
JPX |
B51-13469 |
Apr 1976 |
JPX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
819371 |
Jan 1992 |
|