Process for preparing alkylene sulfides

BACKGROUND OF THE INVENTION
The present invention relates to a process for preparing alkylene sulfides by an intramolecular dehydration reaction of mercaptoalkanols in a gaseous phase under the presence of catalysts.
Alkylene sulfides, which have superior reactivity, are useful compounds that are extensively used as manufacturing materials for pharmaceuticals, pesticides, and various industrial chemicals as well as being used as a reactant for sulfur-containing polymers.
Concerning processes for manufacturing alkylene sulfides, U.S. Pat. No. 3,687,976 as well as U.K. Pat. No. 1135800 disclose a process wherein ethylene oxide reacts with carbonyl sulfide or carbon disulfide under the presence of catalysts. However, this process has problems with the toxicity of carbonyl sulfide and carbon disulfide as well as with the low yield of alkylene sulfide as a target product.
Further, U.S. Pat. No. 3,622,597 and J. Chem. Soc. (C), p1252-1256, 1969, disclose a process for preparing alkylene sulfides, wherein a mercaptoethanol is subjected to an intramolecular dehydration reaction in a liquid phase under the presence of a catalyst of sulfuric acid series. However, this process suffers from drawbacks wherein the yield of alkylene sulfide as a target product is low because of a large amount of polymerization by-products; and it is expensive to separate the polymerization by-products from the catalyst after the reaction since the reaction is a homogeneous reaction in the liquid phase. Therefore, it is impossible to put this process into practical industrial use.
Moreover, Netherlands Pat. No. 7001172 discloses a process for obtaining alkylene sulfides through the intramolecular dehydration reaction of mercaptoalkanols in a gaseous phase, which is carried out by using solid catalysts such as titanium oxide, zirconium oxide or niobium oxide. It is described that in accordance with this method, alkylene sulfides can be obtained in a high yield from mercaptoalkanols. However, no description is found in the specification concerning catalyst life, which is a very important factor to stably manufacture the target products, alkylene sulfides. According to examinations carried out by the inventors of the present application, in the case of using the catalysts such as titanium oxide, zirconium oxide or niobium oxide, since the acid property of the catalysts is too strong, so-called coking develops during the reaction such that deactivation of the catalysts proceeds quickly. Moreover, in addition to the quick deactivation of the catalysts, MgTiO.sub.3 and SrTiO.sub.3 that are, disclosed in the above Laid-Open Patent Publication, they have extremely low activity in comparison with such a catalyst as titanium oxide. Therefore, it has been shown that this method using these catalysts fails to provide a satisfactory method from the industrial point of view.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a process by which alkylene sulfides are stably and efficiently obtained from mercaptoalkanols in a high yield for a long period.
In order to achieve the above objective, the inventors of the present application have found that, in a process for preparing alkylene sulfides from mercaptoalkanols, by making mercaptoalkanols subject to an intramolecular dehydration reaction in a gaseous phase under the presence of novel catalysts, alkylene sulfides can be stably obtained in a high yield for a long period. The catalysts employed are composite oxides having, as essential ingredients, both of at least one element selected from the group consisting of alkali metals, alkaline earth metals and thallium and at least one element selected from the group consisting of aluminum, boron, silicon and phosphorous.
More specifically, the present invention provides a process for preparing alkylene sulfides of the formula: ##STR1## wherein R.sup.1, R.sup.2, R.sup.3 and R.sup.4 are respectively selected from the group consisting of a hydrogen atom, an alkyl group with 1-4 carbon atoms, a phenyl group, and a benzyl group, which is obtained through the intramolecular dehydration reaction of mercaptoalkanols of the formula: ##STR2## wherein R.sup.1, R.sup.2, R.sup.3 and R.sup.4 are as defined above, in a gaseous phase, the process being characterized by the use of catalysts of the formula:
M.sub.a X.sub.b Y.sub.c O.sub.d (III)
wherein M represents at least one element selected from the group consisting of alkali metals, alkaline earth metals and thallium; X represents at least one element selected from the group consisting of aluminum, boron, silicon and phosphorous; Y represents at least one element selected from the group consisting of lanthanides, IIIA group, IVA group, VA group, IIIB group, IVB group, VB group and VIB group (excluding an element contained in M or X); and O represents oxygen, while subscripts a, b, c and d respectively represent composition ratios of the elements; a and b are numerical values not equal to 0; b=0.2-100 and c=0-50 when a=1; and d is a numerical value determined according to a, b and c.
In accordance with the present invention, alkylene sulfides are stably manufactured from mercaptoalkanols with high selectivity for a long period. Moreover, since no secondary reactants are required for the process, few by-products are produced. Thus, the present invention has succeeded in providing a very simple and economical process.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
Suitable mercaptoalkanols to be used as a reactant in the present invention include 2-mercaptoethanol, 1-methyl-2-mercaptoethanol, 1-ethyl-2-mercaptoethanol, 1,2-dimethyl-2-mercaptoethanol and 1-phenyl-2-mercaptoethanol. In accordance with the process of the present invention, the corresponding alkylene sulfides can be obtained depending on the mercaptoalkanols employed.
The catalysts used in the present invention ar composite oxides represented by the aforementioned formula (III). These composite oxides exhibit catalytic performances in a gaseous phase reaction such that alkylene sulfides are stably obtained from mercaptoalkanols in a high yield and with a high selectivity for a long period. In particular, in the case of manufacturing ethylene sulfide which exhibits a remarkably high reactivity among alkylene sulfides, if catalysts of the formula (III) with X containing at least one element selected from the group consisting of boron and phosphorous are used, more preferable results can be obtained.
As to the reason why the catalysts of the present invention exhibit superior performances in the intramolecular dehydration reaction from mercaptoalkanols to alkylene sulfides, it has not been clarified in detail. However, active sites on the surface of the catalysts not only accelerate the intramolecular dehydration reaction of mercaptoalkanols, but also have extremely inactive characteristics toward produced alkylene sulfides; therefore, the consecutive reactions are inhibited. As a result, having less occurrence of coking, the target products can be obtained in a high yield.
Moreover, in these catalysts, special emphasis is placed on the acid and base property on the surface of the catalysts, and generally a remarkable effect has been found especially in their life of the catalysts which have acid sites ranging from +3.3 to +7.0 and base sites ranging from +7.0 to +9.3 in the acid-base strength H.sub.0 that is measured by Hammett's indicator method.
Additionally, the acid-base strength H.sub.0 is measured through the following method:
0.1 g of a catalyst, which has been dried at 250 .degree. C. for two hours, was immersed into 1 ml of anhydrous benzene in a test tube, and ten of these samples were prepared. Then, two or three drops of benzene solutions containing the following indicators were added to the respective samples, and stirred, and then left to rest at room temperature for 24 hours. The benzene solutions used as Hammett's indicators were: dicinnamal acetone (H.sub.0 =-3.0), 4-(phenylazo)diphenylamine (H.sub.0=+1.5), p-dimethyl-aminoazobenzene (H.sub.0 =+3.3), phenylazonaphthylamine (H.sub.0 =4.0), methyl red (H.sub.0 =+4.8), neutral red (H.sub.0 =+6.8), bromthymol blue (H.sub.0 =+7.2), m-nitrophenol (H.sub.0 =+8.3), phenolphthalein (H.sub.0 =+9.3), and 2,4,6-trinitroaniline (H.sub.0 =+12.2). The (H.sub.0) value of the sample at acid site was determined by the smallest (H.sub.0) value among the Hammett's indicators which had been subjected to color changes and which had the (H.sub.0) value of less than +7.0. Similarly, the (H.sub.0) value of the sample at base site was determined by the greatest (H.sub.0) value among the Hammett's indicators which had been subjected to color changes and which had the (H.sub.0) value of more than +7.0.
As for materials for the catalysts, various materials such as metal elements, oxides, hydroxides, halides, nitrates, sulfates, phosphates, and carbonates may be employed.
The preparation method of the catalysts is not necessarily limited to a specific one; various preparation methods that are commonly used may be adopted. For example, those methods include: a method wherein various catalyst materials, which are dissolved or suspended in water and heated and condensed while stirring, are formed after being dried and further calcined to form a catalyst; a method wherein various catalyst materials, which are dissolved or suspended in water and changed into a hydroxide by adding ammonia water thereto, are filtrated and rinsed in water, and then dried to form a catalyst; and a method wherein oxides or hydroxides of various elements are ground and mixed, and after being dried and formed, are calcined to form a catalyst. As for the calcining temperatures of the catalysts, although they depend on the materials to be used and on the calcining time, temperatures of 300.degree. C.-1000.degree. C. are suitable in the air or in an atmosphere of inert gas (such as nitrogen, argon, or helium). Further, the catalysts of the present invention may be used in such a manner wherein they are carried on inert supports, for example, such as diatomaceous earth, caolinite, silicon carbide, or silicon nitride.
In carrying out the gaseous-phase reaction of the present invention, any type of reactor may be employed among the fixed bed flowing type, the fluidized bed type and the moving bed type.
Moreover, mercaptoalkanol a reactant may be supplied into the reactor, either diluted or not diluted. In the case of supplying it in a diluted state, an inactive gas such as nitrogen, helium or argon may be used as a diluent gas. Here, the concentration of the reactant is preferably set to not less than 5% by volume since an extremely low concentration of the reactant causes a decrease in productivity. Generally, the reaction is conducted under reduced or normal pressure; but, the reaction may be conducted under a pressurized atmosphere.
The space velocity of the reactant gas, although it varies depending on the composition of the reactant gas, the reaction temperature and the reaction pressure, is set in the range of 10-10000 h.sup.-1 during the reaction. The reaction temperature is in the range of 180.degree. C.-350.degree. C., preferably 200.degree. C.-320.degree. C. If the reaction temperature is below 180.degree. C., the catalyst activity will be too low to get a sufficient yield. On the contrary, if the reaction temperature is above 350.degree. C., secondary reactions will occur preferentially so that the selectivity of the target alkylene sulfides becomes low.
The following description will discuss the present invention in detail by reference to experimental examples and comparative examples. Here, the conversion of mercaptoalkanols, the selectivity of alkylene sulfides and the yield are determined according to the following definitions.
The conversion of mercaptoalkanols (%)=(the number of moles of mercaptoalkanols consumed through the reaction/the number of moles of mercaptoalkanols supplied) .times.100.
The selectivity of alkylene sulfides (%)=(the number of moles of alkylene sulfides produced/the number of moles of mercaptoalkanols consumed).times.100.
The yield of alkylene sulfides (%)=(the number of moles of alkylene sulfides produced/the number of moles of mercaptoalkanols supplied).times.100.

EXAMPLE 1
To a solution prepared by dissolution of 1.2 grams of cesium nitrate and 3.9 grams of boric acid in 250 ml of water was added 34 grams of silica gel. The mixture was heated and condensed, and then dried at 130.degree. C. for 11 hours. The resulting solid matter was calcined at 600.degree. C. in the air for 3 hours; thus, a catalyst with a composition represented by Cs.sub.1 B.sub.10 Si.sub.90 in the atomic ratio excluding oxygen was obtained. The catalyst having the composition of Cs.sub.1 B.sub.10 Si.sub.90 thus obtained was crushed into powder of 4-9 mesh and loaded into a reaction tube. Then, the reaction tube was immersed into a melt salt bath at 270.degree. C., and a reactant gas was introduced into the reaction tube at a space velocity of 3000 .sup.-1. The reactant gas had a composition ratio of 2-mercaptoethanol:nitrogen=10:90 in the volume ratio. The reaction conditions are shown in Tables 1 and 2.
The products of the reaction were analyzed by gas chromatography, and the results shown in Table 3 were obtained.
In the following examples 2 through 18, each catalyst was prepared by each method as shown below. Here, reactions and analyses were performed in the same manner as Example 1 except that: the kind of mercaptoalkanol, as a reactant; the concentration of a reactant gas; the space velocity; the reaction temperature; and the reaction pressure were all changed as indicated in Tables 1 and 2. Consequently, the results shown in Tables 3 were obtained.
EXAMPLE 2
A solution was prepared by dissolution of 4.2 grams of sodium nitrate and 367.8 grams of aluminum nitrate in 2000 ml of water. Then, a 28% solution of ammonia water was added to the solution with stirring carried out for two hours while maintaining the pH of the solution in the range from 8 to 10. After cooling-off, filtration, and water rinse processes, white powder was obtained. The powder was dried for 14 hours at 120.degree. C., and then calcined at 700.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Na.sub.1 Al.sub.20 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 3
To a solution prepared by dissolution of 7.6 grams of rubidium nitrate and 0.5 grams of sodium nitrate in 170 ml of water was consecutively added 6.5 grams of an 85% solution of phosphoric acid and 34 grams of silica. The mixture was heated and condensed, and then dried at 140.degree. C. for 12 hours.
The resulting solid matter was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Rb.sub.0.9 Na.sub.0.1 P.sub.1 Si.sub.10 in the atomic ratio excluding oxygen was obtained.
EXAMPLES 4 AND 5
4.2 grams of sodium hydroxide (purity 95%), 8.1 grams of a 85% solution of orthophosphoric acid, and 30 grams of silicon carbide (whisker) as a support were suspended in 200 ml of water, and the mixture was heated and condensed at 80.degree. C. with sufficient stirring. The resulting solid matter, after having been dried at 120.degree. C. in the air for 12 hours, was calcined at 600.degree. C. in the air for two hours; consequently, a catalyst with a composition represented by Na.sub.1 P.sub.0.7 in the atomic ratio excluding support element and oxygen was obtained.
EXAMPLE 6
To a solution prepared by dissolution of 10.1 grams of potassium nitrate and 11.9 grams of diammonium hydrogen phosphate in 200 ml of water was added 30 grams of silica gel. The mixture was heated and condensed, and then dried at 120.degree. C. for 12 hours. The resulting solid matter was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by K.sub.1 P.sub.0.9 Si.sub.5 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 7
To a solution prepared by dissolution of 8.2 grams of boric acid and 2.1 grams of thallium nitrate in 200 ml of hot water having a temperature of 80.degree. C. were added 5.9 grams of barium hydroxide octahydrate and 70.8 grams of niobium pentoxide in powder. The mixture was heated and condensed, and then sufficiently dried at 120.degree. C. The resulting solid matter was calcined at 600.degree. C. in the air for two hours; consequently, a catalyst with a composition represented by Tl.sub.0.3 Ba.sub.0.7 B.sub.5 Nb.sub.20 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 8
A solution prepared by dissolution of 6.2 grams of potassium hydroxide (purity 90%) and 30.9 grams of boric acid in 300 ml of hot water having a temperature of 80.degree. C. was added to 56.5 grams of yttrium oxide in powder. The mixture was heated and condensed, and then sufficiently dried at 120.degree. C. in the air. The resulting solid matter was calcined at 650.degree. C. in the air for six hours; consequently, a catalyst with a composition represented by K.sub.1 B.sub.5 Y.sub.5 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 9
A mixture was prepared by mixing 2.9 grams of cerium(IV) oxide and 40 grams of titanium oxide, both in powder. To the mixture was added a mixed solution prepared by dissolution of 16.9 grams of potassium nitrate and 22.0 grams of diammonium hydrogen phosphate in 300 ml of water. The mixture was heated and condensed, and then sufficiently dried at 120.degree. C. The resulting solid matter was calcined at 600.degree. C. in the air for two hours; consequently, a catalyst with a composition represented by K.sub.1 P.sub.1 Ce.sub.0.1 Ti.sub.3 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 10
A solution was prepared by dissolution of 86.6 grams of lanthanum nitrate hexahydrate and 3.9 grams of cesium nitrate in 500 ml of water. To the solution was added 26.5 grams of diammonium hydrogen phosphate, and the mixture was heated and condensed with sufficient stirring, and then sufficiently dried at 120.degree. C. The resulting solid matter was calcined at 750.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Cs.sub.1 P.sub.10 La.sub.10 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 11
To a solution prepared by dissolution of 5.3 grams of strontium nitrate and 2.1 grams of sodium nitrate in 300 ml of water was added 61.6 grams of zirconium oxide in powder with sufficient stirring. Then, 4.0 grams of diammonium hydrogen phosphate was added to the mixture, and it was heated and condensed, and then sufficiently dried at 130.degree. C. The resulting powder was calcined at 650.degree. C. in the air for three hours; consequently, a catalyst whose composition was represented by Na.sub.0.5 Sr.sub.0.5 P.sub.0.6 Zr.sub.10 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 12
A mixture prepared by mixing and grinding 16.5 grams of sodium tungstic acid dihydrate and 30 grams of silica gel in a mortar was further kneaded with 100 ml of water. The resulting slurry was sufficiently dried at 130.degree. C., and then calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Na.sub.1 Si.sub.5 W.sub.0.5 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 13
To a solution prepared by dissolution of 88.0 grams of diammonium hydrogen phosphate in 800 ml of water was added 74.1 grams of calcium hydroxide, and the mixture was evaporated and dried hard, thereby resulting in a solid matter. The solid matter was calcined at 600 .degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Ca.sub.1 P.sub.0.66 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 14
To a solution prepared by dissolution of 321.7 grams of lithium nitrate and 205.3 grams of diammonium hydrogen phosphate in 300 ml of water was added 28% ammonia water to adjust the pH of the solution to 8-10 with stirring carried out for two hours. Then, the mixture was cooled off, filtered and rinsed in water, thereby resulting in white powder. The white powder was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Li.sub.1 P.sub.0.33 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 15
To a solution prepared by dissolution of 43.4 grams of strontium nitrate in 200 ml of water was added 50 grams of aluminum phosphate. The solution was heated and condensed, and then dried at 130.degree. C. for ten hours. The resulting solid matter was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Sr.sub.1 Al.sub.2 P.sub.2 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 16
A mixture was prepared by mixing and grinding in a mortar 3.5 grams of gallium oxide in powder and 50 grams of kaolin powder as a support. Then, to the mixture was added a solution prepared by dissolution of 9 grams of sodium dihydrogen phosphate in 300 ml of water, and the mixture was heated and condensed. The resulting solid matter was sufficiently dried at 120.degree. C., and then calcined at 500.degree. C. in the air for six hours; consequently, a catalyst with a composition represented by Na.sub.1 P.sub.1 Ga.sub.0.5 in the atomic ratio excluding support atoms and oxygen was obtained.
EXAMPLE 17
A mixture was prepared by sufficiently mixing and grinding in a mortar 5.4 grams of boric acid, 3.9 grams of barium hydroxide octahydrate, 40 grams of titanium oxide in powder, and 13.1 grams of germanium oxide in powder. After adding 200 ml of 50.degree. C. warm water thereto, the mixture was heated and condensed. The resulting solid matter was sufficiently dried at 120.degree. C., and then calcined at 750.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Ba.sub.1 B.sub.7 Ge.sub.10 Ti.sub.40 in the atomic ratio excluding oxygen was obtained.
EXAMPLE 18
A solution was prepared by dissolution of 10.5 grams of dipotassium hydrogen phosphate in 200 ml of water. After adding thereto 1.7 grams of antimony(III) oxide in powder and 30.6 grams of alumina powder, the mixture was heated and condensed. The resulting solid matter was sufficiently dried at 120.degree. C. and then calcined at 800.degree. C. in the air for four hours; consequently, a catalyst with a composition represented K.sub.1 P.sub.0.5 Al.sub.5 Sb.sub.0.2 in the atomic ratio excluding oxygen was obtained.
TABLE 1______________________________________Exam- Catalyst Composition Acid-Base Strength H.sub.0ple M.sub.a X.sub.b Y.sub.c Acid Site Base Site______________________________________ 1 Cs.sub.1 B.sub.10 Si.sub.90 -- +3.3 +7.2 2 Na.sub.1 Al.sub.20 -- +4.0 +7.2 3 Na.sub.0.1 Rb.sub.0.9 P.sub.1 Si.sub.10 -- +4.0 +8.3 4 Na.sub.1 P.sub.0.7 -- +6.8 +8.3 5 Na.sub.1 P.sub.0.7 -- +6.8 +8.3 6 K.sub.1 P.sub.0.9 Si.sub.5 -- +4.8 +8.3 7 Tl.sub.0.3 Ba.sub.0.7 B.sub.5 Nb.sub.20 +3.3 +7.2 8 K.sub.1 B.sub.5 Y.sub.5 +4.0 +7.2 9 K.sub.1 P.sub.1 Ce.sub.0.1 Ti.sub.3 +4.0 +7.210 Cs.sub.1 P.sub.10 La.sub.10 +4.8 +8.311 Na.sub.0.5 Sr.sub.0.5 P.sub.0.6 Zr.sub.10 +4.0 +8.312 Na.sub.1 Si.sub.5 W.sub.0.5 +4.8 +8.313 Ca.sub.1 P.sub.0.66 -- +6.8 +9.314 Li.sub.1 P.sub.0.33 -- +4.8 +9.315 Sr.sub.1 Al.sub.2 P.sub.2 -- +6.8 +8.316 Na.sub.1 P.sub.1 Ga.sub.0.5 +4.0 +8.317 Ba.sub.1 B.sub.7 Ge.sub.10 Ti.sub.40 +4.8 +8.318 K.sub.1 P.sub.0.5 Al.sub.5 Sb.sub.0.2 +6.8 +9.3______________________________________
TABLE 2______________________________________Ex- Space Reactant Pres-am- Velocity Temp. Ratio sureple Reactant (h.sup.-1) (.degree.C.) (Vol. %) (mmHg)______________________________________ 1 2-mercaptoethanol 3000 270 10 760 2 1,2-dimethyl- 2000 250 20 760 2-mercaptoethanol 3 2-mercaptoethanol 4000 270 10 760 4 2-mercaptoethanol 3000 270 10 760 5 2-mercaptoethanol 400 300 100 80 6 2-mercaptoethanol 2000 250 10 760 7 1-methyl- 2000 270 10 760 2-mercaptoethanol 8 2-mercaptoethanol 4000 300 20 760 9 2-mercaptoethanol 2500 300 20 76010 2-mercaptoethanol 2000 230 10 76011 1-methyl- 200 200 100 150 2-mercaptoethanol12 1-methyl- 1500 300 10 760 2-mercaptoethanol13 2-mercaptoethanol 300 300 100 8014 1-phenyl- 7000 300 5 1000 2-mercaptoethanol15 1,2-dimethyl- 200 270 100 80 2-mercaptoethanol16 2-mercaptoethanol 2000 300 10 76017 2-mercaptoethanol 2500 270 10 76018 2-mercaptoethanol 2000 300 10 760______________________________________
TABLE 3______________________________________ Elapsed Conver- Selec-Exam- Time sion tivity Yieldple Product (hr) (%) (%) (%)______________________________________ 1 ethylene sulfide 1 87.4 95.1 83.1 200 84.0 95.1 79.9 2 2,3-dimethyl 1 87.2 93.1 81.2 ethylene sulfide 50 84.9 95.6 81.1 3 ethylene sulfide 1 86.3 95.4 82.3 100 86.2 96.1 82.8 4 ethylene sulfide 2 95.1 93.2 88.6 200 93.7 93.4 87.5 5 ethylene sulfide 2 93.6 97.1 90.9 200 90.8 97.5 88.5 6 ethylene sulfide 2 97.1 98.3 95.4 200 96.5 98.7 95.2 7 2-methyl 1 84.4 92.2 77.8 ethylene sulfide 100 83.0 91.9 76.3 8 ethylene sulfide 2 93.6 94.7 88.6 100 91.5 95.3 87.2 9 ethylene sulfide 2 93.8 92.6 86.9 200 93.5 92.8 86.810 ethylene sulfide 2 87.2 93.3 81.4 100 82.9 92.5 76.711 2-methyl 2 95.9 96.2 92.3 ethylene sulfide 100 95.5 95.8 91.512 2-methyl 2 88.8 91.6 81.3 ethylene sulfide 50 85.9 92.3 79.313 ethylene sulfide 1 90.6 94.6 85.7 100 90.0 94.3 84.914 2-phenyl 1 84.8 97.7 82.8 ethylene sulfide 100 83.2 97.9 81.515 2,3-dimethyl 1 89.4 91.6 81.9 ethylene sulfide 100 87.1 93.3 81.316 ethylene sulfide 1 92.3 91.1 84.1 100 89.9 93.7 84.217 ethylene sulfide 1 87.6 94.1 82.4 100 85.9 93.7 80.518 ethylene sulfide 1 96.3 92.4 89.0 100 93.0 91.9 85.5______________________________________
COMPARATIVE EXAMPLES 1-4
Concerning each of the catalysts prepared in accordance with the following comparative examples 1-4, reactions and analyses were performed in the same manner as Example 1 except that: the kind of mercaptoalkanol, as a reactant; the concentration of a reactant gas; the space velocity; the reaction temperature; and the reaction pressure were changed as indicated in Table 4. Consequently, the results shown in Table 5 were obtained.
COMPARATIVE EXAMPLE 1
A mixture prepared by addition of 50 grams of commercial niobium pentoxide to 100 ml of water was heated and condensed, and then sufficiently dried at 150.degree. C. The resulting solid matter was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Nb.sub.1 in the atomic ratio excluding oxygen was obtained.
COMPARATIVE EXAMPLE 2
A mixture prepared by addition of 50 grams of titanium oxide (rutile type) in powder to 100 ml of water was heated and condensed, and then dried at 150.degree. C. The resulting solid matter was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Ti.sub.1 in the atomic ratio excluding oxygen was obtained.
COMPARATIVE EXAMPLE 3
A mixture prepared by addition of 50 grams of commercial strontium titanate to 100 ml of water was heated and condensed, and then dried at 150.degree. C. The resulting solid matter was calcined at 500.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by Sr.sub.1 Ti.sub.1 in the atomic ratio excluding oxygen was obtained.
COMPARATIVE EXAMPLE 4
To a solution prepared by dissolution of 8.8 grams of diammonium hydrogen phosphate in 130 ml of water was added 40 grams of silica gel. The mixture was heated and condensed, and then dried at 140.degree. C. for ten hours. The resulting solid matter was calcined at 600.degree. C. in the air for three hours; consequently, a catalyst with a composition represented by P.sub.1 Si.sub.10 in the atomic ratio excluding oxygen was obtained.
TABLE 4__________________________________________________________________________ Acid-Base Space React-Catalyst Compo- Stren. (H.sub.0) Veloc- ant Pres-sition Acid Base ity Temp ratio sure* M.sub.a X.sub.b Y.sub.c Site Site Reactant (h.sup.-1) (.degree.C.) (V %) (mmHg)__________________________________________________________________________1 -- -- Nb.sub.1 +1.5 -- 2-mercapto 2000 275 20 760 ethanol2 -- -- Ti.sub.1 +3.3 -- 2-mercapto 2000 270 10 760 ethanol3 Sr.sub.1 -- Ti.sub.1 +6.8 +7.2 2-mercapto 2000 270 10 760 ethanol4 -- P.sub.1 S.sub.10 -- -3.0 -- 2-mercapto 2000 250 20 760 ethanol__________________________________________________________________________ *Comparative Example
TABLE 5______________________________________Compar-ative Elapsed Conver- Selec-Exam- Time sion tivity Yieldple Product (hr) (%) (%) (%)______________________________________1 ethylene sulfide 1 95.1 70.0 66.6 30 48.5 67.8 32.92 ethylene sulfide 1 86.7 71.1 61.6 30 36.4 73.9 26.83 ethylene sulfide 1 16.2 76.3 12.4 30 10.8 73.9 8.04 ethylene sulfide 1 93.4 3.2 3.0______________________________________
The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiment is therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.

Number	Date	Country	Kind
3-316657	Nov 1991	JPX
3-316658	Nov 1991	JPX

Number	Name	Date	Kind
3622597	Fletcher	Nov 1971
3687976	Wright	Aug 1972

Number	Date	Country
6512117	Mar 1966	NLX
7001172	Jun 1970	NLX
1092610	Nov 1967	GBX
1135800	Dec 1968	GBX

Process for preparing alkylene sulfides

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (2)

US Referenced Citations (2)

Foreign Referenced Citations (4)

Non-Patent Literature Citations (1)