Claims
- 1. A process for preparing a spherical shape pelletized oxide catalytic composition having a high degree of reproducibility of catalytic activity for oxidizing an unsaturated aldehyde into an unsaturated carboxylic acid, said composition consisting essentially of ( 1) phosphorus, (2) molybdenum, (3) X in which X is at least one element selected from the group consisting of thallium and metals of Groups 1A and II of the periodic table and, optionally (4) Z in which Z is at least one element selected from the group consisting of silicon, chromium, aluminum, germanium, titanium, vanadium, tungsten, bismuth, niobium, boron, gallium, lead, tin, cobalt, palladium, arsenic, zirconium, antimony, iron, nickel, indium, copper, silver, manganese, lanthanum, neodymium, samarium and tellurium at an atomic ratio of P:Mo:X:Z of 0.1-8:12:0.01-10:0-12 and a surface area of 4 to 20m.sup.2 /g and a pore volume of 0.08 to 0.5 ml/g, said catalyst composition being produced by tumbling granulation comprising the steps of:
- feeding the unpelletized, uncalcined catalytic composition into a tumbling granulator;
- granulating the composition at an elevated temperature while spraying a binder selected from the group consisting of water and ammonia water until granules of a predetermined size have formed;
- withdrawing the granules of said predetermined size; and
- calcining said granules.
- 2. The process of claim 1 in which, in said tumbling granulation method, the granules withdrawn from the tumbling granulator are dried prior to being calcined.
- 3. The process of claim 1 in which an inert finely divided carrier diluent is added to said tumbling granulator with said unpelletized, uncalcined catalyst composition.
- 4. The process of claim 1 wherein the catalyst composition fed to the tumbling granulator is in the form of a fine powder having a size of 40 mesh or less.
- 5. The process of claim 1, wherein the atomic ratio of (1) phosphorus: (2) molybdenum: (3) X is 0.2-7:12:0.05-8.
- 6. The process of claim 1, wherein the atomic ratio of (1) phosphorus: (2) molybdenum: (3) X is 0.3-5:12:0.2-6.
- 7. The process of claim 1, wherein the atomic ratio of molybdenum to said element Z is 12:0.1-12.
- 8. The process of claim 1, wherein the atomic ratio of molybdenum to said element Z is 12:0.3-8.
- 9. The process of claim 1, wherein said catalyst composition has a surface area of 4.5 to 15 m.sup.2 /g and a pore volume of 0.09 to 0.35 ml/g.
- 10. The process of claim 1, wherein Z is absent.
Priority Claims (1)
Number |
Date |
Country |
Kind |
49/121418 |
Oct 1974 |
JPX |
|
Parent Case Info
This is a division of application Ser. No. 940,484, filed Sept. 7, 1978 which in turn is a continuation of application Ser. No. 623,616 filed Oct. 20, 1975, both now abandoned.
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
3661801 |
Gutmann et al. |
May 1972 |
|
3795703 |
Niina et al. |
Mar 1974 |
|
3956377 |
Dolhyn et al. |
May 1976 |
|
3976688 |
Akiyama et al. |
Aug 1976 |
|
4077912 |
Dolhyj et al. |
Mar 1978 |
|
Divisions (1)
|
Number |
Date |
Country |
Parent |
940484 |
Sep 1978 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
623616 |
Oct 1975 |
|