The present invention relates to a process for producing a plastics foil provided with a cured polysiloxane coating on one surface, whereby a tubular, flat laid plastics foil is equipped on both surfaces with a cured polysiloxane coating, comprising steps (a) to (d) listed hereinafter, and then—if the foil has not already previously been opened at least at one side—completely opening it at least at one side along a lateral edge, a plastics foil obtainable by said process and equipped with a cured polysiloxane coating, and the use of such plastics foil as a release foil or protection foil.
Peelable release foils are widely used as removable protection foils for adhesive tapes, self-adhesive labels, or adhesive sanitary and hygiene products, in order to prevent adhesion of these single- or double-side-adhesive products during storage or processing. They have to feature good release effect with respect to adhesives such as pressure-sensitive adhesives or other adhesive materials.
Siliconized release foils are already known from the prior art, for example from EP 1 277 802 A1 or EP 0 769 540 A2.
Siliconized release foils are usually produced by providing single- or multilayer foils with a polysiloxane coating. These foils are first coated with a polysiloxane that has not yet been hardened, and once the coating process has taken place the polysiloxane is then preferably thermally hardened.
However, a disadvantage of a process of this type is that the plastics foils requiring coating have to meet certain minimum mechanical and/or thermomechanical requirements, in order that they withstand the thermal stresses during the curing procedure for the polysiloxane coating. Accordingly, the plastics foils have to have a certain minimum thickness, dependent on the polymer material from which they have been produced, in order that the coating procedure and in particular the curing procedure do not cause any thermal or thermomechanical overloading of the foil to be coated or of the coated foil, with consequent undesired adverse effects on quality or on processes, like for example formation of folds, web shrinkage, web break-offs, or defects in the polysiloxane coating.
However, costs are not the only reason for the provision of a comparatively low thickness of a siliconized release foil for many applications.
There is therefore a need to provide processes which can provide single- or multilayer plastics foils with a curable polysiloxane coating which do not show the above-mentioned disadvantages.
It was therefore an object of the present invention to provide a process for producing a single- or multilayer plastics foil provided with a thermally cured polysiloxane coating on one side, by neither having to use a foil meeting certain minimum mechanical requirements, in particular a certain minimum thickness for the application of the polysiloxane coating, nor having to postpone the reduction of the single- or multilayer plastics foil to a desired thickness until after the application of the polysiloxane coating.
This object is achieved through a preferably continuous process for producing a single- or multilayer plastics foil provided with a thermally hardened polysiloxane coating on one side, in that a preferably tubular, flat laid, optionally already opened and optionally evacuated single- or multilayer plastics foil first
The process of the invention can preferably be carried out continuously. It is moreover also possible that step (e), to the extent that it concerns only the opening or preferably separation, is carried out on the extruded, flat laid, tubular plastics foil before step a).
The process of the invention can provide a single- or multilayer foil made of plastic provided with a cured polysiloxane coating on one of its surfaces, whereby the thickness of the foil can already during siliconization be up to 50% lower than that of a foil which is siliconized by means of conventional coating processes. This is rendered possible by the use of a flat laid, optionally already opened, tubular foil during coating in steps (a) and (c) and during each thermal curing procedure in steps (b) and (d), since during said operations the foil has practically twice the thickness, and therefore has the necessary mechanical and/or thermomechanical robustness. However, a corresponding foil which is half as thick, because the thickness of which corresponds only to the thickness of an inventively used foil, but not to that of the flat laid, tubular foil, lacks the mechanical and/or thermomechanical robustness required therefore. The process of the invention has the advantage that there is no need to reduce the thickness of an already siliconized plastics foil, for example by orientation.
By starting from a preferably tubular plastics foil provided with a cured polysiloxane coating on both surfaces according to the inventive process, a single-side-siliconized foil is obtained by complete opening of the flat laid, tubular plastics foil at least along one lateral edge in the movement direction, and a spreading to full width, which siliconized foil can have a thickness up to 50% lower than that of a foil which has been siliconized successfully by means of conventional coating processes. According to the invention, this complete opening of the flat laid, preferably tubular plastics foil can already take place before the first polysiloxane coating process, i.e. before step a).
In steps (a) and (c) of the inventive process, in each case one of the surfaces of the flat laid, preferably tubular foil is coated with at least one uncured, flat laid polysiloxane. It is preferable that in each case the flat laid foil is evacuated, in order to avoid unevenness of the flat laid foil during coating, for example caused by air cushions present in the flat laid foil, and in order to avoid the occurrence of defects in the polysiloxane coating. In each case here, one of the surfaces of the single- or multilayer, flat laid, preferably still tubular foil is provided with at least one preferably liquid, particularly preferably high-viscous, uncured polysiloxane or with a preferably liquid mixture of at least one uncured polysiloxane and optionally of at least one of the additives mentioned hereinafter. The coating is carried out by a full-surface-area coating in each case of the one of the surfaces of the single- or multilayer, flat laid, preferably still tubular foil with at least one polysiloxane or a with a mixture.
In steps (b) and (d) of the inventive process, the polysiloxane coating applied in steps (a) and (c), in each case to one of the surfaces of the flat laid, preferably still tubular foil is in each case cured under drying, preferably through exposure to heat and optionally with UV irradiation. The preferably still tubular foil thus provided with a cured polysiloxane coating on both surfaces can optionally then be cut to the desired dimensions and separated at one or both sides, and preferably stored in the form of a roll.
It is preferable that, before step (c), the flat laid, preferably still tubular foil already provided with a cured polysiloxane coating on one surface is turned about 180°, preferably with the aid of a crossbar system, and then that step (c) is carried out. It is also possible that the flat laid, preferably still tubular foil provided with a cured polysiloxane coating on one surface is placed into intermediate storage in rolled-up form before step (c).
In a preferred embodiment of the inventive process, after step (d), the flat laid, preferably still tubular foil provided with a cured polysiloxane coating on each surface is, in a further step (e), in the movement direction at least along one lateral edge, preferably along both lateral edges, completely opened, or preferably separated, and the resultant full-width flat foil or the resultant two foils is/are then preferably stored in the form of a roll.
The tubular plastics foil used in the process of the invention is preferably a foil which, before the provision of a cured polysiloxane coating, is a single- or multilayer, preferably single-layer tubular foil.
In a preferred embodiment of the inventive process, the plastics foil or at least one layer of the preferably tubular plastics foil, before the provision of the cured polysiloxane coating, is based on at least one optionally biodegradable, thermoplastic polymer, preferably on at least one olefin homo- or copolymer, on at least one thermoplastic homo- or copolyamide, and/or on at least one thermoplastic, biodegradable polymer.
A material preferably suitable for producing said layer is at least one thermoplastic olefin homo- or copolymer of α,β-unsaturated olefins having from 2 to 10 carbon atoms. Suitable olefin homopolymers are preferably those selected from the group consisting of ethylene homopolymers (polyethylenes, PE), preferably LDPE and HDPE, propylene homopolymers (polypropylenes, PP), butylene homopolymers (polybutylenes, PB), and isobutylene homopolymers (polyisobutylenes, PI), or a mixture made of at least two of the polymers mentioned. “LDPE” indicates low-density polyethylene with density in the range from 0.86 to 0.93 g/cm3, featuring a high degree of branching of the molecules. “HDPE” indicates high-density polyethylene with only little branching of the molecular chain, where density can be in the range from 0.94 to 0.97 g/cm3. Suitable olefin copolymers are preferably copolymers of ethylene and/or propylene and of at least one α-olefin having at least 4, preferably from 4 to 10, particularly preferably from 4 to 8, carbon atoms, and very particularly preferably copolymers of ethylene and/or propylene with at least one α-olefin selected from the group consisting of butene, hexene, and octene. The proportion of α-olefin in the olefin copolymer is preferably at most 25% by weight, particularly preferably at most 15% by weight, based in each case on the total weight of the olefin copolymer. Particularly suitable copolymers of ethylene and of at least one α-olefin having at least 4 carbon atoms are LLDPE and/or mPE. “LLDPE” indicates linear low-density ethylene copolymers which are characterized by the presence of a linear main chain with side chains located thereon, and by density in the range of 0.86 and 0.94 g/cm3. “mPE” indicates ethylene copolymers which have been polymerized by means of metallocene catalysts and which preferably have a density in the range of 0.88 and 0.93 g/cm3. Preferred olefin homo- or copolymers for producing the layer (1) are ethylene homo- or copolymers and/or propylene homo- or copolymers. Particular preference is given to an ethylene homopolymer, such as LDPE or HDPE for producing the layer (1).
In a preferred embodiment of the inventive process, the preferably tubular foil is, before the provision of the cured polysiloxane coating, composed only of one layer, which is based on at least one olefin homo- or copolymer, preferably on an olefin homopolymer, particularly preferably on HDPE, on LDPE or on polypropylene.
Another material suitable for producing the, or a, layer of the preferably tubular plastics foil is at least one thermoplastic homo- and/or copolyamide. The layer can preferably be produced by using thermoplastic homo- or copolyamides selected from the group consisting of thermoplastic aliphatic, semiaromatic, or aromatic homo- or copolyamides. These homo- or copolyamides can be produced from diamines, such as aliphatic diamines having from 2 to 10 carbon atoms, in particular hexamethylenediamine and/or aromatic diamines having from 6 to 10 carbon atoms, in particular p-phenylenediamine, and from dicarboxylic acids such as aliphatic or aromatic dicarboxylic acids having from 6 to 14 carbon atoms, e.g. adipic acid, terephthalic acid, or isoterephthalic acid. It is moreover possible to produce homo- or copolyamides from lactams having from 4 to 10 carbon atoms, for example from ε-caprolactam. Polyamides used in the invention are preferably PA 6, PA 12, PA 66, PA 6I, PA 6T, or corresponding copolymers, or mixtures of at least two of the polyamides mentioned.
In another preferred embodiment of the inventive process, it is also possible to use a multilayer plastics foil as preferably tubular foil before the provision of the cured polysiloxane coating. This foil can have an internal layer based on at least one homo- or copolyamide with, on each surface, a layer based on at least one olefin homo- or copolymer, preferably on at least one olefin homopolymer, particularly preferably on at least one propylene homopolymer, and, if necessary, adhesion-promoter layers.
It is also possible to use at least one thermoplastic biodegradable polymer for producing the, or a, layer of the plastics film used in the invention.
According to the present invention, the expression “biodegradable polymer” means a natural, semisynthetic, or synthetic polymer in various forms, e.g. in the form of a, or the single, layer of a tubular foil which, with exposure to microorganisms and/or to enzymes, can be decomposed to give water, carbon dioxide, and biomass in accordance with DIN EN 13432, and which according to the disintegration test is biodegraded to an extent of at least 90%, preferably of at least 95%, particularly preferably of ≧99%, after 12 weeks of aerobic composting.
Preferably for producing the preferably tubular plastics foil at least one thermoplastic biodegradable polymer selected from the group comprising lactic acid homo- and copolymers, preferably polylactides, particularly preferably DL-lactide, L-lactide, and D-lactide, polyhydroxyalkanoates, cellulose, cellulose derivatives, thermoplastic starch, polyesters, preferably polyesters derived from lactones having from 4 to 10 carbon atoms, particularly preferably polycaprolactones, at least partially hydrolyzed polyvinyl acetates, ethylene-vinyl alcohol copolymers, copolymers of at least two monomers of the polymers mentioned, and mixtures of at least two of the polymers can be used. At least partially hydrolyzed polyvinyl acetates can be obtained by complete or incomplete hydrolysis of corresponding polyvinyl acetates (PVAc), and comprise not only partially hydrolyzed polyvinyl acetates with a degree of hydrolysis of from 50 to 98 mol % but also fully hydrolyzed polyvinyl acetates, i.e. polyvinyl alcohols (PVOH) with a degree of hydrolysis ≧98%. Ethylene-vinyl alcohol copolymers (EVOH) can be obtained through hydrolysis of corresponding ethylene-vinyl acetate copolymers (EVAc), and preferably comprise ethylene-vinyl alcohol copolymers (EVOH) with a degree of hydrolysis ≧98% and a proportion of ethylene of from 0.01 to 20 mol %, preferably from 0.1 to 10 mol %.
In another preferred embodiment of the inventive process, a single-layer plastics foil, preferably a tubular foil, is used before the application of the curable polysiloxane coating, which foil is based on at least one biodegradable polymer, preferably on at least one polylactide.
According to the inventive process, the flat laid, single- or multilayer, preferably still tubular or optionally already opened plastics foil is provided with a cured polysiloxane coating on both surfaces.
For the purposes of the present invention, the expression “polysiloxane” means compounds having polymer chains composed of silicon atoms and oxygen atoms in alternation. A polysiloxane is based on n repeating siloxane units (—[Si(R2)—O]—)n which in each case mutually independently have disubstitution with two organic moieties R, where R is in each case preferably R1 or OR1, and each R1 is an alkyl moiety or an aryl moiety. It is preferable that the hardened polysiloxane coating is based on a repeating dialkylsiloxane unit or on a repeating alkylaryl siloxane unit. These units can be classified as a function of the number of Si—O bonds in an individual siloxane unit, based in each case on a tetravalent silicon atom, as terminal monofunctional siloxanes (M) having one Si—O bond, difunctional siloxanes (D) having two Si—O bonds, trifunctional siloxanes (T) having three Si—O bonds, and tetrafunctional siloxanes (Q) having four Si—O bonds. it is preferable that the polysiloxane coating of the invention has a crosslinked ring- or chain-type structure, particularly a crosslinked chain-type structure, linked via (D), (T), and/or (Q) units to give a two- or three-dimensional network. The number n of repeating siloxane units [Si(R2)—O]—)n in the polysiloxane chain is called the degree of polymerization of the polysiloxane.
According to the inventive process the cured polysiloxane coating is preferably based on at least one cured, i.e. crosslinked polysiloxane selected from the group consisting of addition-crosslinked, preferably metal-catalyzed addition-crosslinked, condensation-crosslinked, free-radical-crosslinked, and/or cationically crosslinked polysiloxanes.
A particularly preferred polysiloxane coating is based on at least one cured polysiloxane which has been cured thermally, optionally by exposure to UV radiation. Preferably, the polysiloxane coating is based on at least one cured polysiloxane selected from the group comprising polydialkylsiloxanes, preferably polydimethylsiloxanes, and polyalkylarylsiloxanes, preferably polymethylphenylsiloxanes, in each case cured. Thermally cured polysiloxanes can be obtained through thermal hydrosilylation of polysiloxanes having silane functions with a compound having at least one carbon double bond.
If necessary, it is possible to add to the polysiloxane coating, as well as to at least one layer of the preferably inventively used tubular foil independently from each other additives selected from the group comprising antiblocking agents, antistatic agents, antifogging agents, antimicrobial ingredients, dyes, color pigments, stabilizers, preferably heat stabilizers, process stabilizers, processing aids, flame retardants, nucleating agents, crystallization aids, preferably crystal-nucleating agents, lubricants, optical brighteners, flexibilizers, sealants, plasticizers, antiblocking agents, fillers, peeling additives, waxes, wetting agents, compounds with surface activity, preferably surfactants, and dispersing agents. However, the release effect of the polysiloxane coating must not be impaired thereby.
Optionally, the polysiloxane coating as well as optionally at least one layer of the plastics foil, can, if necessary, independently from each other comprise at least 0.01-30% by weight, preferably at least 0.1-20% by weight, based on the total weight of the respective layer, of at least one of the above-mentioned additives.
The single- or multilayer, tubular plastics foil used in the process of the invention can be produced, before the application of the curable polysiloxane coating, by known production methods, particularly preferably by blown-film extrusion or blown-film coextrusion, whereby the thickness of the tubular plastics film is already established by the, preferably only once blowing-up ratio of the extruded tubular film.
According to a preferred embodiment, the preferably tubular foil used in the inventive process is, before the application of the curable polysiloxane coating, produced and used in the form of a single- or multilayer tubular plastics foil. This tubular foil can preferably be embossed after production directly, without prior storage. Optionally, the foil can be opened at least at one side before or after embossing.
By embossing it is possible, in-line or off-line, to provide a preferably tubular inventively used plastics foil having only on one side or right through going an embossed structure, preferably by means of structuring or embossing calendars comprising a screen equipment for applying a screen pattern, preferably a roll system for applying a screen pattern. Preferably, this type of calendar has counterrotating rolls arranged at a certain distance vertically above one another. For the embossing process, the flat laid, preferably still tubular plastics foil is carried to the rolls and passed through the slit, the width of which being variably adjustable. The roll system for applying a screen pattern preferably has a first roll with a comparatively hard surface, particularly preferably a steel roll, and a second roll with a less hard surface, preferably made of a resilient material, particularly preferably of rubber or ebonite.
Before the application of, or between the two applications of, the curable polysiloxane coating, the flat laid foil used in an inventive process, preferably being tubular or optionally already opened at least on one side, can preferably be rolled up and optionally stored in rolled-up form. Preferably during the first roll-up process the preferably tubular foil is laid flat simultaneously. The rolled-up tubular foil is in turn unrolled for the first or the further application of the curable polysiloxane coating, i.e. for step (a) and, respectively, (c) of the inventive process.
Preferably, the total thickness of the full-width flat foil provided with a cured polysiloxane coating on one of the surfaces, or of the two foils each provided with a cured polysiloxane coating on one surface, these being respectively obtained after step (e) of the process, optionally after any still necessary longitudinal-side opening of the tubular plastics foil, is ≦45 μm, preferably ≦35 μm, particularly preferably ≦25 μm.
If according to the inventive process a single-layer, tubular film based on LDPE is used, the thickness of the final product, i.e. of the foil having a cured polysiloxane coating on one of its surfaces, can preferably be ≦45 μm.
If according to the inventive process a single-layer, tubular film based on HDPE is used, the thickness of the final product, i.e. of the foil having a cured polysiloxane coating on one of its surfaces, preferably can be ≦35 μm.
If according to the inventive process a tubular foil is used which foil has three layers and the internal layer of which is based on at least one homo- or copolyamide, and each of the two surface layers is based on at least one olefin homo- or copolymer, preferably on at least one olefin copolymer, particularly preferably on at least one propylene copolymer, the thickness of the final product, i.e. of the foil having a cured polysiloxane coating on one of its surfaces, can preferably be ≦25 μm.
The thickness of the polysiloxane coating of a foil obtained by the inventive process is preferably ≦5 μm, particularly preferably ≦3 μm, very particularly preferably in the range from 0.1 μm to ≦3 μm, in particular in the range from 0.2 μm to ≦1.5 μm.
A further object of the present invention is a foil having a cured polysiloxane coating on one of its surfaces and obtainable by an inventive process.
The foil having on one surface a cured polysiloxane coating and obtainable by an inventive process has an excellent suitability as peelable release foil or peelable protective foil.
The peelable release foil or peelable protective foil obtained by an inventive process can have been embossed.
The peelable release foil or peelable protective foil obtained by an inventive process can be a printed and/or colored and/or transparent foil.
A further object of the present invention is also the use of a foil obtainable according to the inventive process as peelable release foil or peelable protective foil, preferably as peelable release foil or peelable protective foil, preferably for self-adhesive labels, for adhesive tapes, for stickers or for adhesive hygiene products, preferably in sanitary towels and panty inserts.
The inventive process can preferably be carried out in an equipment arrangement described hereinafter:
The said equipment arrangement comprises at least
The equipment arrangement used can also comprise a cutting apparatus (6), preferably in the form of blades, for the complete opening, preferably complete separation, at least along one lateral edge, preferably along both lateral edges in the movement direction, of the flat laid foil coated with a cured polysiloxane coating on both of its surfaces, and preferably still tubular or optionally opened only on one side. It is preferable that the equipment arrangement used provides—if necessary—one or two rollers by means of which the full-width flat foil obtained after complete opening along one lateral edge of the flat laid foil, or the two foils obtained after complete opening along both lateral edges, is/are rolled up, and can therefore be stored in rolled-up form.
The examples hereinafter serve to illustrate the invention, but are not to be interpreted as restrictive.
A single-layer tubular plastics foil produced by blown-film extrusion, composed of LDPE with thickness of 35 μm is laid flat under evacuation and is coated with a liquid uncured polysiloxane on one of its surfaces. After thermal curing of said coating in a dryer unit, the single-side-coated, flat laid tubular foil is turned about 180°, and its second, still uncoated surface is likewise coated with a liquid uncured polysiloxane. Said second coating is also thermally cured in a dryer unit. The thickness of each of the polysiloxane coatings is 2 μm. The resultant flat laid, tubular foil coated on each surface with a cured polysiloxane is in each case completely separated in the movement direction along each lateral edge, thus providing two LDPE foils each single-side-coated with a cured polysiloxane. The total thickness of each of these foils is 37 μm.
A single-layer tubular foil produced by blown-film extrusion, made with HDPE with a total thickness of 30 μm is laid flat with evacuation and coated with a liquid uncured polysiloxane on one of its surfaces. After thermal curing of said coating in a dryer unit, the single-side-coated, flat laid tubular foil is turned about 180°, and its second, still uncoated surface is likewise coated with a liquid uncured polysiloxane. Said second coating is also thermally cured in a dryer unit. The thickness of each of the polysiloxane coatings is 1.5 μm. The resultant flat laid, tubular foil coated on each of its surfaces with a cured polysiloxane is completely separated in the movement direction along one lateral edge, thus providing, after the HDPE foil has been laid flat at the full width, a foil coated on one of its surfaces with a cured polysiloxane and having a total thickness of 31.5 μm.
A three-layer tubular foil produced by blown-film coextrusion, composed of an internal layer made of a copolyamide and having on each surface a layer (1) based on a propylene copolymer, has a total thickness of 21 μm. Said foil is laid flat under evacuation, and coated with a liquid uncured polysiloxane on one of its surfaces. After thermal curing of said coating in a dryer unit, the single-side-coated, flat laid tubular foil is turned about 180°, and its second, still uncoated surface is likewise coated with a liquid uncured polysiloxane. Said second coating is also thermally cured in a dryer unit. The thickness of each of the polysiloxane coatings is 1.5 μm. The resultant flat laid, tubular foil coated on each surface with a cured polysiloxane is completely separated in the movement direction along each lateral edge, thus giving two plastic foils each being single-side-coated with a cured polysiloxane. The total thickness of each of these foils is 22.5 μm.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2010 036 022 | Aug 2010 | DE | national |
This application is a Continuation of PCT/EP2011/004377, filed Aug. 31, 2011, which claims foreign priority benefit under 35 U.S.C. §119 of German Patent Application 10 2010 036 022.8 filed Aug. 31, 2010, the contents of all of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5672428 | Muschelweicz et al. | Sep 1997 | A |
| 6737119 | Kim et al. | May 2004 | B1 |
| 20090081430 | Husemann et al. | Mar 2009 | A1 |
| 20090134547 | Bauer et al. | May 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 28 01 038 | Jul 1979 | DE |
| 0 071 349 | Feb 1983 | EP |
| 0 769 540 | Apr 1997 | EP |
| 1 277 802 | Jan 2003 | EP |
| 1 557 451 | Jul 2005 | EP |
| 1 734 093 | Dec 2006 | EP |
| 2001 225416 | Aug 2001 | JP |
| 2009 233953 | Oct 2009 | JP |
| 2007141327 | Dec 2007 | WO |
| Entry |
|---|
| International Search Report Dated Feb. 2, 2012, Mailed Feb. 15, 2012. |
| Translation of International Search Report Dated Feb. 2, 2012, Mailed Feb. 15, 2012. |
| Number | Date | Country | |
|---|---|---|---|
| 20130189436 A1 | Jul 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/EP2011/004377 | Aug 2011 | US |
| Child | 13780344 | US |