The invention relates to a process for producing aqueous polyacrylamide solutions by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water, wherein the process is carried out in a modular, relocatable plant. The plant preferably is deployed at a location at which aqueous polyacrylamide solutions are used, for example on an oilfield or in a mining area.
Water-soluble, high molecular weight homo- and copolymers of acrylamide may be used for various applications such as mining and oilfield applications, water treatment, sewage treatment, papermaking, and agriculture. Examples include its use in the exploration and production of mineral oil, in particular as thickener in aqueous injection fluids for enhanced oil recovery or as rheology modifier for aqueous drilling fluids. Further examples include its use as flocculating agent for tailings and slurries in mining activities.
A common polymerization technology for manufacturing such high molecular weight polyacrylamides is the so called “gel polymerization”. In gel polymerization, an aqueous monomer solution having a relatively high concentration of monomers, for example from 20% by weight to 35% by weight is polymerized by means of suitable polymerization initiators under essentially adiabatic conditions in an unstirred reactor thereby forming a polymer gel. The polymer gels formed are converted to polymer powders by comminuting the gel into smaller pieces by one or more size reduction steps, drying such gel pieces for example in a fluid bed dryer followed by sieving, grinding and packaging. The obtained polyacrylamide powders are thereafter packaged and shipped to customers.
The aqueous polyacrylamide gel obtained from gel polymerization typically comprises from 65% to 80% of water. The residual amount of water in polyacrylamide powders typically is from about 4 to 12% by weight. So, “drying” such polyacrylamide gels does not mean to remove only some residual moisture in course of drying but rather about 0.55 to 0.75 kg of water need to be removed per kg of polymer gel, or—with other words—per kg of polymer powder produced also 1.5 to 2.5 kg of water are “produced”.
It goes without saying that removing such a high amount of water from the polymer gels in course of drying is energy extensive and consequently the operational costs for drying are high. Furthermore, high-performance dryers are necessary as well as equipment for size reduction, sieving and grinding. Consequently, the capital expenditure for the entire post-processing equipment including size reduction, drying, sieving, grinding is significant in relation to the total capital expenditure for the entire plant.
High-molecular weight polyacrylamides are usually used as dilute aqueous solutions. Typical concentrations of polyacrylamides for oilfield and mining applications range from 0.05 wt. % to 0.5 wt. %. Consequently, the polyacrylamide powders manufactured as mentioned above need to be dissolved in aqueous fluids before use. Dissolving high molecular weight polymers in aqueous fluids is time consuming and it is difficult to do so without degrading the polymers and without forming lumps. Suitable equipment for dissolving polyacrylamide powders is necessary on-site.
For oilfield applications, such as enhanced oil recovery or for mining applications large amounts of polyacrylamides need to be available at one location, i.e. at an oilfield or at a mining area. By way of example, even for flooding only a medium size oilfield it may be necessary to inject some thousand m3 of polymer solution per day into the oil-bearing formation and usually the process of polymer flooding continues for months or even years. So, for a polymer concentration of only 0.2 wt. % and an injection rate of 5000 m3/day 10 t of polymer powder are needed per day and need to be dissolved in an aqueous fluid.
It has been suggested not to dry the aqueous polyacrylamide gels after manufacture but directly dissolving said polyacrylamide gels in water thereby obtaining diluted aqueous solutions of polyacrylamides without drying and re-dissolving the dry powder. Working in such a manner saves capital expenditures and operational costs for drying and further post-processing. However, shipping dilute aqueous solutions of polyacrylamides to customers is not an option because transport costs become extremely high as compared to transporting powders. It has therefore been suggested to manufacture aqueous polyacrylamide solutions on-site.
DE 2 059 241 discloses a process for preparing water-soluble polymers, including acrylamide containing polymers, in which an aqueous solution comprising water-soluble monomers and polymerization initiators is filled into transportable containers for polymerization. In the transportable containers, the aqueous solution polymerizes thereby forming polymer gel. The gel may be transported to the end users who can remove the polymer gels and dissolve them in water. The transportable containers may be—for instance—bags, cans, drums, or boxes having a volume from 2 l to 200 l.
U.S. Pat. No. 4,248,304 discloses a process for recovering oil from subterranean formations wherein a water-in-oil-emulsion of an acrylamide polymer in the presence of an inverting agent is injected into the formation. The water-in-oil emulsion is manufactured in a small chemical plant located near the wells and the manufacturing procedure comprises the steps of forming a water-in-oil emulsion of acrylonitrile, converting a substantially portion of the acrylonitrile to acrylamide using a suitable catalyst, and polymerizing the water-in-oil emulsion of acrylamide in the presence of a free radical polymerization catalyst. The catalyst may be a copper catalyst.
ZA 8303812 discloses a process for preparing polyacrylamides comprising polymerizing acrylamide and optionally suitable comonomers on-site and transferring the polymer formed to its desired place of use on site without drying or concentrating. The polymerization can be carried out as an emulsion polymerization, bead polymerization, or as solution/dispersion polymerization. The polymer may be pumped from the polymerization reactor to the position on site where it is used.
WO 84/00967 A1 discloses an apparatus and method for the continuous production of aqueous polymer solutions, in particular partially hydrolyzed polyacrylamide. The apparatus comprises a polymerization reactor, a hydrolysis reactor and a diluter. The polymerization may be performed on-site and the solutions may be used in secondary or tertiary oil recovery.
U.S. Pat. No. 4,605,689 discloses a method for on-site production of aqueous polyacrylamide solutions for enhanced oil recovery. In a first step an aqueous polyacrylamide gel is provided by polymerizing acrylamide and preferably acrylic acid as comonomer. The polyacrylamide gel obtained is conveyed together with a minor amount of aqueous solvent through at least one static cutting device thereby obtaining a slurry of small gel particles in water, the gel particles are dissolved in the aqueous solvent which forms a homogeneous solution concentrate which is then readily diluted with aqueous solvent thereby obtaining a diluted aqueous polyacrylamide solution.
U.S. Pat. No. 4,845,192 discloses a method of rapidly dissolving particles of gels of water-soluble polymers comprising forming a suspension of such gel particles in water and subjecting said suspension to instantaneous and momentary conditions of high shearing effective to finely slice said particles.
Our older application WO 2017/186567 A1 relates to a process for producing an aqueous polymer solution comprising the steps of providing an aqueous polyacrylamide gel comprising at least 10% by weight of active polymer, cutting the aqueous polyacrylamide gel by means of a water-jet at a pressure of at least 150 bar to reduce the size of the aqueous polyacrylamide gel, and dissolving the aqueous polyacrylamide gel in an aqueous liquid.
Our older application WO 2017/186697 A1 relates to a method of preparing an aqueous polyacrylamide solution, comprising hydrolyzing acrylonitrile in water in presence of a biocatalyst thereby obtaining an acrylamide solution, directly polymerizing the acrylamide solution thereby obtaining a polyacrylamide gel, and directly dissolving the polyacrylamide gel by addition of water thereby obtaining an aqueous polyacrylamide solution. The method may be carried out on-site.
Our older application WO 2017/186685 A1 relates to a method of preparing an aqueous polyacrylamide solution, comprising hydrolyzing acrylonitrile in water in presence of a biocatalyst thereby obtaining an acrylamide solution, directly polymerizing the acrylamide solution thereby obtaining a polyacrylamide gel, and directly dissolving the polyacrylamide gel by addition of water by means of a mixer comprising a rotatable impeller thereby obtaining an aqueous polyacrylamide solution. The method may be carried out on-site.
Our older application WO 2017/186698 A1 relates to a method of preparing an aqueous polyacrylamide solution, comprising hydrolyzing acrylonitrile in water in presence of a biocatalyst thereby obtaining an acrylamide solution, directly polymerizing the acrylamide solution thereby obtaining a polyacrylamide gel, and directly dissolving the polyacrylamide gel by addition of water by means of water-jet cutting, thereby obtaining an aqueous polyacrylamide solution. The method may be carried out on-site.
WO 2016/006556 A1 describes a method for producing a compound using a continuous tank reactor which is provided with two or more reaction tanks for producing the compound and with a reaction liquid feeding pipe that feeds a reaction liquid from an upstream reaction tank to a downstream reaction tank, said method being characterized in that the Reynold's number of the reaction liquid that flows in the reaction liquid feeding pipe is configured to be 1800-22000. The tank reactor may be mounted in a portable container. The compound may be acrylamide produced by conversion from acrylonitrile by means of a biocatalyst.
WO 2017/167803 A1 discloses a method for producing a polyacrylamide solution having an increased viscosity by preparing an aqueous acrylamide solution by converting acrylonitrile to acrylamide using a biocatalyst, separating the biocatalyst from the aqueous acrylamide solution such that the OD600 of the aqueous acrylamide solution is equal or less than 0.6, and polymerizing the aqueous acrylamide solution thus obtained to polyacrylamide.
WO 97/21827 A1 discloses a process for making a solution of ammonium acrylate by enzymatic hydrolysis of acrylonitrile.
The production of polyacrylamide solution on-site saves equipment and operational costs for drying and re-dissolving of polyacrylamides on the one hand. On the other hand, the need of polyacrylamide solutions at one site can be limited in time. By the way of example, in enhanced oil recovery operations, aqueous solutions of polyacrylamides may be injected into the subterranean formations for months or even a few years, however usually for no longer time. When the polyacrylamide solutions are no longer needed at one site, it is necessary to transport diluted aqueous solutions to another site which generates high transport costs. Deconstructing the plant at the original site and erecting it at another site may also be connected with high costs.
It was an object of the present invention to provide an improved process for manufacturing aqueous solutions of polyacrylamides on-site using a plant capable of becoming relocated easily.
Accordingly, in one embodiment of the present invention, a process for producing an aqueous polyacrylamide solution by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water has been found, wherein the process is conducted in a modular, relocatable plant and the process comprises at least the following steps:
In a preferred embodiment, the process comprises an additional step [0] comprising hydrolyzing acrylonitrile in water in the presence of a biocatalyst capable of converting acrylonitrile to acrylamide in a relocatable bioconversion unit, thereby obtaining an aqueous acrylamide solution, and wherein said aqueous acrylamide solution is used for step [1].
In another embodiment, the present invention relates to a process for producing an aqueous polyacrylamide solution by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water has been found, wherein the process is conducted in a modular, relocatable plant and the process comprises at least the following steps:
In another embodiment, the invention relates to a modular, relocatable plant for manufacturing aqueous polyacrylamide solutions by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water, comprising at least
Preferably, the plant additionally comprises the following units:
In another embodiment, the plant the modular, relocatable plant is deployed at a location at which the polyacrylamide solutions are used, for example on an oilfield or in a mining area.
With regard to the invention, the following can be stated specifically:
By means of the process according to the present invention, it is possible to prepare aqueous solutions of polyacrylamides.
Polyacrylamides
The term “polyacrylamides” as used herein means water-soluble homopolymers of acrylamide, or water-soluble copolymers comprising at least 10%, preferably at least 20%, and more preferably at least 30% by weight of acrylamide and at least one additional water-soluble, monoethylenically unsaturated monomer different from acrylamide, wherein the amounts relate to the total amount of all monomers in the polymer. Copolymers are preferred.
The term “water-soluble monomers” in the context of this invention means that the monomers are to be soluble in the aqueous monomer solution to be used for polymerization in the desired use concentration. It is thus not absolutely necessary that the monomers to be used are miscible with water without any gap; instead, it is sufficient if they meet the minimum requirement mentioned. It is to be noted that the presence of acrylamide in the monomer solution might enhance the solubility of other monomers as compared to water only. In general, the solubility of the water-soluble monomers in water at room temperature should be at least 50 g/I, preferably at least 100 g/I.
Basically, the kind and amount of water-soluble, monoethylenically unsaturated comonomers to be used besides acrylamide is not limited and depends on the desired properties and the desired use of the aqueous solutions of polyacrylamides to be manufactured.
Neutral Comonomers
In one embodiment of the invention, comonomers may be selected from uncharged water-soluble, monoethylenically unsaturated monomers. Examples comprise methacrylamide, N-methyl(meth)acrylamide, N,N′-dimethyl(meth)acrylamide, N-methylol(meth)acrylamide or N-vinylpyrrolidone. Further examples have been mentioned in WO 2015/158517 A1 page 7, lines 9 to 14.
Anionic Comonomers
In a further embodiment of the invention, comonomers may be selected from water-soluble, monoethylenically unsaturated monomers comprising at least one acidic group, or salts thereof. The acidic groups are preferably selected from the group of —COOH, —SO3H and —PO3H2 or salts thereof. Preference is given to monomers comprising COOH groups and/or —SO3H groups or salts thereof. Suitable counterions include especially alkali metal ions such as Li+, Na+ or K+, and also ammonium ions such as NH4+ or ammonium ions having organic radicals. Examples of ammonium ions having organic radicals include [NH(CH3)3]+, [NH2(CH3)2]+, [NH3(CH3)]+, [NH(C2H5)3]+, [NH2(C2H5)2]+, [NH3(C2H5)]+, [NH3(CH2CH2OH)]+, [H3N—CH2CH2—NH3]2+ or [H(H3C)2N—CH2CH2CH2NH3]2+.
Examples of monomers comprising —COOH groups include acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid or fumaric acid or salts thereof. Preference is given to acrylic acid or salts thereof.
Examples of monomers comprising —SO3H groups or salts thereof include vinylsulfonic acid, allylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid (ATBS), 2-methacrylamido-2-methylpropanesulfonic acid, 2-acrylamidobutanesulfonic acid, 3-acrylamido-3-methylbutanesulfonic acid or 2-acrylamido-2,4,4-trimethylpentanesulfonic acid. Preference is given to 2-acrylamido-2-methylpropanesulfonic acid (ATBS) or salts thereof.
Examples of monomers comprising—PO3H2 groups or salts thereof include vinylphosphonic acid, allylphosphonic acid, N-(meth)acrylamidoalkylphosphonic acids or (meth)acryloyloxyalkyl-phosphonic acids, preferably vinylphosphonic acid.
Preferred monomers comprising acidic groups comprise acrylic acid and/or ATBS or salts thereof.
Cationic Comonomers
In a further embodiment of the invention, comonomers may be selected from water-soluble, monoethylenically unsaturated monomers comprising cationic groups. Suitable cationic monomers include especially monomers having ammonium groups, especially ammonium derivatives of N-(ω-aminoalkyl)(meth)acrylamides or ω-aminoalkyl (meth)acrylates such as 2-trimethylammonioethyl acrylate chloride H2C═CH—CO—CH2CH2N+(CH3)3Cl− (DMA3Q). Further examples have been mentioned in WO 2015/158517 A1 page 8, lines 15 to 37. Preference is given to DMA3Q.
Associative Comonomers
In a further embodiment of the invention, comonomers may be selected from associative monomers.
Associative monomers impart hydrophobically associating properties to polyacrylamides.
Associative monomers to be used in the context of this invention are water-soluble, monoethylenically unsaturated monomers having at least one hydrophilic group and at least one, preferably terminal, hydrophobic group. Examples of associative monomers have been described for example in WO 2010/133527, WO 2012/069478, WO 2015/086468 or WO 2015/158517.
“Hydrophobically associating copolymers” are understood by a person skilled in the art to mean water-soluble copolymers which, as well as hydrophilic units (in a sufficient amount to assure water solubility), have hydrophobic groups in lateral or terminal positions. In aqueous solution, the hydrophobic groups can associate with one another. Because of this associative interaction, there is an increase in the viscosity of the aqueous polymer solution compared to a polymer of the same kind that merely does not have any associative groups.
Examples of suitable associative monomers comprise monomers having the general formula H2C═C(R1)—R2-R3 (I) wherein R1 is H or methyl, R2 is a linking hydrophilic group and R3 is a terminal hydrophobic group. Further examples comprise having the general formula H2C═C(R1)—R2-R3-R4 (II) wherein R1, R2 and R3 are each as defined above, and R4 is a hydrophilic group.
The linking hydrophilic R2 group may be a group comprising ethylene oxide units, for example a group comprising 5 to 80 ethylene oxide units, which is joined to the H2C═C(R1)— group in a suitable manner, for example by means of a single bond or of a suitable linking group. In another embodiment, the hydrophilic linking group R2 may be a group comprising quaternary ammonium groups.
In one embodiment, the associative monomers are monomers of the general formula H2C═C(R1)—O—(CH2CH2O)k—R3a (III) or H2C═C(R5)—(C═O)—O—(CH2CH2O)k—R3a (IV), wherein R1 has the meaning defined above and k is a number from 10 to 80, for example, 20 to 40. R3a is an aliphatic and/or aromatic, straight-chain or branched hydrocarbyl radical having 8 to 40 carbon atoms, preferably 12 to 32 carbon atoms. Examples of such groups include n-octyl, n-decyl, n-dodecyl, n-tetradecyl, n-hexadecyl or n-octadecyl groups. In a further embodiment, the groups are aromatic groups, especially substituted phenyl radicals, especially distyrylphenyl groups and/or tristyrylphenyl groups.
In another embodiment, the associative monomers are monomers of the general formula H2C═C(R1)—O—(CH2)n—O—(CH2CH2O)x—(CH2—CH(R5)O)y—(CH2CH2O)zH (V), wherein R1 is defined as above and the R5 radicals are each independently selected from hydrocarbyl radicals comprising at least 2 carbon atoms, preferably from ethyl or propyl groups. In formula (V) n is a natural number from 2 to 6, for example 4, x is a number from 10 to 50, preferably from 12 to 40, and for example, from 20 to 30 and y is a number from 5 to 30, preferably 8 to 25. In formula (V), z is a number from 0 to 5, for example 1 to 4, i.e. the terminal block of ethylene oxide units is thus merely optionally present. In an embodiment of the invention, it is possible to use at least two monomers (V), wherein the R1 and R6 radicals and indices n, x and y are each the same, but in one of the monomers z=0 while z>0 in the other, preferably 1 to 4.
In another embodiment, the associative monomers are cationic monomers. Examples of cationic associative monomers have been disclosed in WO 2015/158517 A1, page 11, line 20 to page 12, lines 14 to 42. In one embodiment, the cationic monomers having the general formula H2C═C(R1)—C(═O)O—(CH2)k—N+(CH3)(CH3)(R6) X− (VI) or H2C═C(R1)—C(═O)N(R1)—(CH2)k—N+ (CH3)(CH3)(R6) X− (VII) may be used, wherein R1 has the meaning as defined above, k is 2 or 3, R6 is a hydrocarbyl group, preferably an aliphatic hydrocarbyl group, having 8 to 18 carbon atoms, and X− is a negatively charged counterion, preferably Cl− and/or Br−.
Further Comonomers
Besides water-soluble monoethylenically unsaturated monomers, also water-soluble, ethylenically unsaturated monomers having more than one ethylenic group may be used. Monomers of this kind can be used in special cases in order to achieve easy crosslinking of the acrylamide polymers. The amount thereof should generally not exceed 2% by weight, preferably 1% by weight and especially 0.5% by weight, based on the sum total of all the monomers. More preferably, the monomers to be used in the present invention are only monoethylenically unsaturated monomers.
Composition of Polyacrylamides
The specific composition of the polyacrylamides to be manufactured according the process of the present invention may be selected according to the desired use of the polyacrylamides.
Preferred polyacrylamides comprise, besides at least 10% by weight of acrylamide, at least one water-soluble, monoethylenically unsaturated comonomer, preferably at least one comonomer selected from the group of acrylic acid or salts thereof, ATBS or salts thereof, associative monomers, in particular those of formula (V) or DMA3Q, more preferably at least one comonomer selected from acrylic acid or salts thereof, ATBS or salts thereof, associative monomers, in particular those of formula (V).
In one embodiment, the polyacrylamides comprise 20% to 90% by weight of acrylamide and 10% to 80% by weight of acrylic acid and/or salts thereof, wherein the amounts of the monomers relate to the total of all monomers in the polymer.
In one embodiment, the polyacrylamides comprise 20% to 40% by weight of acrylamide and 60% to 80% by weight of acrylic acid and/or salts thereof.
In one embodiment, the polyacrylamides comprise 55% to 75% by weight of acrylamide and 25% to 45% by weight of acrylic acid and/or salts thereof.
In one embodiment, the polyacrylamides comprise 45% to 75% by weight of acrylamide and 25% to 55% by weight of ATBS and/or salts thereof.
In one embodiment, the polyacrylamides comprise 30% to 80% by weight of acrylamide, 10% to 40% by weight of acrylic acid and/or salts thereof, and 10% to 40% by weight of ATBS and/or salts thereof.
In one embodiment, the polyacrylamides comprise 45% to 75% by weight of acrylamide, 0.1 to 5%, preferably 0.1 to 2% by weight of at least one associative monomer of the general formulas (I) or (II) mentioned above and 10 to 54.9% by weight of acrylic acid and/or ATBS and/or salts thereof. Preferably, the associative monomer(s) have the general formula (V) including the preferred embodiments mentioned above.
In one embodiment, the polyacrylamides comprise 60% to 75% by weight of acrylamide, 0.1 to 5%, preferably 0.1 to 2% by weight of at least one associative monomer of the general formula (V) mentioned above, including the preferred embodiments, and 20 to 39.9% by weight of acrylic acid or salts thereof.
In one embodiment, the polyacrylamides comprise 45% to 55% by weight of acrylamide, 0.1 to 5%, preferably 0.1 to 2% by weight of at least one associative monomer of the general formula (V) mentioned above, including the preferred embodiments, and 40 to 54.9% by weight of acrylic acid or salts thereof.
In one embodiment, the polyacrylamides comprise 60% to 99% by weight of acrylamide and 1% to 40% by weight of DMA3Q.
In one embodiment, the polyacrylamides comprise 10% to 50% by weight of acrylamide and 50% to 90% by weight of DMA3Q.
In one embodiment, the polyacrylamides comprise 90 to 99.5% by weight of acrylamide, 0.5 to 2% by weight of at least one associative monomer, and 0% to 9.5% by weight of and anionic monomer, for example ATBS or a cationic monomer, for example DM3AQ. Preferably, the associative monomer(s) have the general formula (V) including the preferred embodiments mentioned above.
In all embodiments mentioned above, the amount of the monomers relates to the total of all monomers in the polyacrylamide. Further water-soluble, monoethylenically unsaturated monomers may be present besides those specifically mentioned, however, the embodiments each include also one embodiment in which besides the monomers specifically mentioned no further monomers are present, i.e. the total amount of the monomers specifically mentioned is 100% by weight.
The weight average molecular weight Mw of the polyacrylamides to be manufactured usually ranges from 1*106 g/mol to 50*106 g/mol, preferably from 1.5*106 g/mol to 40*106 g/mol, more preferably from 2*106 g/mol to 30*106 g/mol, and for example from 5*106 g/mol to 25*106 g/mol.
Modular Plant Comprising Relocatable Units
The plant according to the present invention is a modular, relocatable plant comprising several relocatable units. Each relocatable unit bundles certain functions of the plant. Examples of such relocatable units comprise units for storing and optionally cooling the monomers and other raw materials, hydrolyzing acrylonitrile, mixing monomers, polymerization and gel dissolution. Details will be provided below. For performing the process according to the present invention individual units are connected with each other in a suitable manner thereby obtaining a production line.
“Relocatable unit” means that the unit is not permanently fixed with the ground but is transportable to another location. It is transportable basically as a whole and that is it not necessary to disassemble the entire unit into individual parts for transport. Transport may happen on trucks, railcars or ships.
Such a modular composition of the plant enables an easy relocation of the plant from one location to another location. As will be detailed below, the plant may be deployed at sites at which aqueous polyacrylamide solutions are needed or close to such sites. When there is no longer a need for aqueous polyacrylamide solutions at such a site the plant may become relocated to another site at which there is a need for polyacrylamide solutions.
In one embodiment, such modular, relocatable units are containerized units which may be transported in the same manner as closed intermodal containers for example on trucks, railcars or ships. Intermodal containers are large standardized (according to ISO 668) shipping containers, in particular designed and built for intermodal freight transport. Such containers are also known as ISO containers. Such ISO containers may have external dimensions of a height of ˜2.59 m, a width of ˜2.44 m and a length of ˜6.05 m. Larger ISO containers have external dimensions of a height of ˜2.59 m, a width of ˜2.44 m and a length of ˜12.19 m.
In another embodiment, the relocatable units may be fixed on trucks or on trailers. With other words, for such relocatable units not a container or something similar is deployed at the site of the modular plant, but the entire truck or the trailer including the unit in its loading spaces is deployed. The trucks or trailers advantageously also function as platform for the units on the ground. Also, two or more different units may be mounted together on a truck or trailer.
The modular, relocatable plant for preparing polyacrylamide solutions according to the present invention basically may be deployed at any location. From such a location, the polyacrylamide solutions may be transported to the locations at which the polyacrylamide solutions are used.
However, preferably the plant is deployed at a location at which the polyacrylamide solutions are used or at least a location close to such a location of use.
In one embodiment, the modular, relocatable plant may be deployed at an oil and/or gas well to be treated with aqueous polyacrylamide solutions or close to such an oil and/or gas well.
Examples comprise oil wells which into which aqueous polyacrylamide solutions are injected in course of enhanced oil operations, production wells whose productivity is enhanced by injection of fracturing fluids comprising polyacrylamides as friction reducers, or wells which are drilled and aqueous polyacrylamide solutions are used for making the drilling fluid. In another embodiment, the plant may be deployed in between a plurality of such oil and/or gas wells or at one of them and the aqueous polyacrylamide solution is distributed to all injection wells, for example by means of pipelines.
In the field of mining, the modular, relocatable plant may be a location at or close to a tailings ponds in which mineral tailings are dewatered using aqueous polyacrylamide solutions. In one embodiment of the invention, it may be a location for the treatment of red mud, a by-product of the Bayer process for manufacturing aluminium.
In other embodiments, the location may be at a paper production site, at sewage works or at seawater desalination plants or at sites for manufacturing agricultural formulations.
The distance between the location of the modular, relocatable plant and the location at which polyacrylamide is used is not specifically limited. However, in order to limit the costs of transporting the aqueous polyacrylamide solutions the location of the plant and the location of using the polyacrylamide should not be too far apart from each other. By the way of example, the distance between location of the modular, relocatable plant and the location(s) of using polyacrylamide solutions may range from 0.1 to 500 km, for example from 0.1 to 100 km, from 0.2 to 10 km or from 0.5 to 5 km.
Provision of Acrylamide
Acrylamide may be synthesized by partial hydrolysis of acrylonitrile using suitable catalysts. It is known in the art to use copper catalysts or other metal containing catalysts and it is also known to use biocatalysts capable of converting acrylonitrile to acrylamide. Pure acrylamide is a solid, however, typically acrylamide—whether made by bio catalysis or copper catalysis—is provided as aqueous solution, for example as aqueous solution comprising about 50% by wt. of acrylamide.
Acrylamide obtained by means of biocatalysts (often referred to as “bio acrylamide”) can be distinguished from acrylamide obtained by means of copper catalysts or other metal containing catalysts because the latter still comprises at least traces of copper or other metals. Acrylamide obtained by means of biocatalysts may still comprise traces of the biocatalyst.
For the process according to the present invention, preferably an aqueous acrylamide solution is used which has been obtained by hydrolyzing acrylonitrile in water in presence of a biocatalyst capable of converting acrylonitrile to acrylamide. As will be detailed below, using biocatalysts for hydrolyzing acrylonitrile has significant advantages for the present invention.
In one embodiment of the invention, aqueous solutions of bio acrylamide for use in the process according to the present invention may be manufactured at another location, and shipped to the location of the modular, relocatable plant according to the present invention.
Such other location of manufacture may be at a fixed chemical plant or a modular, relocatable plant for the manufacture of bio-acrylamide at another location than the plant according to the present invention. A modular, relocatable plant for the manufacture of bio acrylamide may be located closer—as compared to a fixed chemical plant—to the modular, relocatable plant according to the present invention, for example in a mining area or at an oilfield, thereby minimizing transport costs. From such a location one or more than one modular plants for the manufacture of aqueous polyacrylamide solutions according to the present invention may be served with bio acrylamide. In one embodiment, the site of manufacture of bio acrylamide may be apart 1 to 200 km from the modular, relocatable plant according to the present invention.
In a preferred embodiment of the present invention the manufacture of bio acrylamide is also performed by the modular, relocatable plant according to the present invention by means of a suitable bioconversion unit (hereinafter designated as process step [0]).
Manufacturing bio acrylamide by the modular, relocatable plant saves significant transport costs. Acrylonitrile is a liquid and may be transported as pure compound to the location of the plant. The molecular weight of acrylamide is ˜34% higher than that of acrylonitrile and acrylamide is typically provided as ˜50% aqueous solution. So, for a 50% aqueous solution of acrylamide the mass to be transported is about 2.5-fold as much as compared to transporting pure acrylonitrile. Transporting pure, solid acrylamide means transporting only ˜34% more mass as compared to transporting pure acrylonitrile, however, additional equipment for handling and dissolving the solid acrylamide is necessary at the location of the plant.
Step [0]—Hydrolysis of Acrylonitrile
As already outlined above, step [0] is only optional for the process according to the present invention, however, in a preferred embodiment of the invention, the process according to the invention includes step [0]. In course of step [0] acrylonitrile is hydrolyzed in water in presence of a biocatalyst capable of converting acrylonitrile to acrylamide thereby obtaining an aqueous acrylamide solution.
Provision of Acrylonitrile
Acrylonitrile for step [0] may be stored in one or more than one relocatable storage units. The storage unit comprises a storage vessel. The volume of the storage vessel is not specifically limited and may range from 50 m3 to 150 m3, for example it may be about 100 m3. Preferably, the storage vessel should be double walled and should be horizontal. Such a construction avoids installing a pit for the collection of any leakage thereby ensuring an easier and quicker relocation of the storage unit. Double-walled vessels may be placed on every good bearing soil. The storage unit furthermore comprises means for charging and discharging the vessel, means for controlling the pressure in the vessel, for example a valve for settling low-pressure or overpressure,
and means for controlling the temperature of the acrylonitrile which preferably should not exceed 25° C. It furthermore may comprise means for measurement and control to the extent necessary.
Examples of relocatable storage units comprise relocatable cuboid, storage tanks, preferably double-walled tanks. Further, any considerable form, shape and size of container is suitable and applicable for the storage and/or provision of acrylonitrile in the sense of the present invention. Particularly, standard iso-tanks are applicable for the storage and/or provision of acrylonitrile.
Other examples comprise tank containers having a cuboid frame, preferably a frame according to the ISO 668 norm mentioned above and one or more storage vessels mounted into the frame. Such normed tank containers may be stacked and transported on trucks, railcars or ships in the same manner closed intermodal containers.
Basically, temperature control may be performed by any kind of temperature controlling unit. Temperature control may require—depending on the climatic conditions prevailing at the site of the modular plant—cooling or heating the contents of the storage units. Regarding the monomers, temperature control typically means cooling, because it should be avoided that the monomers become too hot. In one embodiment, an internal heat exchanger may be used for cooling or heating, i.e. a heat exchanger mounted inside of the storage vessel. The coolant is provided to the heat exchanger by a suitable cooling or heating unit mounted outside of the storage vessel. In another embodiment of the invention, for temperature control an external temperature control cycle, for example a cooling cycle is used, which comprises a pump which pumps the monomer from the storage vessel through a heat exchanger and back into the storage vessel.
The temperature control cycle may be a separate, relocatable temperature control unit comprising pump and heat exchanger and which is connected with the storage vessel by pipes or flexible tubes.
In another embodiment, the temperature control cycle may be integrated into relocatable storage unit. It may—for example—be located at one end of the unit besides the storage vessel.
Acrylonitrile may be provided to the site of the modular plant by road tankers, ISOtanks or rail cars and pumped into the relocatable storage vessel(s).
The acrylonitrile may be removed from the relocatable storage vessel through a bottom valve by means of gravity or it may be pumped, for example from the upper side using a suitable pump.
Biocatalysts
As biocatalyst for performing step [0], nitrile hydratase enzymes can be used, which are capable of catalyzing the hydrolysis of acrylonitrile to acrylamide. Typically, nitrile hydratase enzymes can be produced by a variety of microorganisms, for instance microorganisms of the genus Bacillus, Bacteridium, Micrococcus, Brevibacterium, Corynebacterium, Pseudomonas, Acinetobacter, Xanthobacter, Streptomyces, Rhizobium, Klebsiella, Enterobacter, Escherichia Coli, Erwinia, Aeromonas, Citrobacter, Achromobacter, Agrobacterium, Pseudonocardia and Rhodococcus. WO 2005/054456 discloses the synthesis of nitrile hydratase within microorganisms and therein it is described that various strains of Rhodococcus rhodochrous species have been found to very effectively produce nitrile hydratase enzymes, in particular Rhodococcus rhodochrous NCIMB 41164. Such microorganisms, suitable as biocatalyst for the enzymatic conversion of acrylonitrile to acrylamide, which are known for a person skilled in the art, are able to be applied in a relocatable bioconversion unit according to the present invention. Additionally, the specific methods of culturing (or cultivation, or fermentation) and/or storing the microorganism as well as the respective sequences of polynucleotides which are encoding the enzyme, particularly the nitrile hydratase, are known in the art, e.g. WO 2005/054456, WO 2016/050816, and are applicable in context of the present invention. Within the present invention nitrile hydratase and amidase producing microorganisms may be used for converting a nitrile compound into the corresponding amide compound as it is described for example in WO 2016/050816.
The terms “nitrile hydratase (NHase) producing microorganism” or “microorganism” or “biocatalysts” or the like, have the meaning to be able to produce (i.e. they encode and express) the enzyme nitrile hydratase (also referred to as, e.g., NHase) either per se (naturally) or they have been genetically modified respectively. Microorganisms which have been “genetically modified” means that these microorganisms have been manipulated such that they have acquired the capability to express the required enzyme NHase, e.g. by way of incorporation of a naturally and/or modified nitrile hydratase gene or gene cluster or the like. Produced products of the microorganisms that can be used in the context of the present invention are also contemplated, e.g. suspensions obtained by partial or complete cell disruption of the microorganisms.
The terms “nitrile hydratase (NHase) producing microorganism” or “microorganism” or “biocatalysts” or the like, include the cells and/or the processed product thereof as such, and/or suspensions containing such microorganisms and/or processed products. It is also envisaged that the microorganisms and/or processed products thereof are further treated before they are employed in the embodiments of the present invention. “Further treated” thereby includes for example washing steps and/or steps to concentrate the microorganism etc. It is also envisaged that the microorganisms that are employed in the embodiments of the present invention have been pre-treated by a for example drying step. Also known methods for cultivating of the microorganisms and how to optimize the cultivation conditions via for example addition of urea or cobalt are described in WO 2005/054456 and are compassed by the embodiments of the present invention. Advantageously, the microorganism can be grown in a medium containing acetonitrile or acrylonitrile as an inducer of the nitrile hydratase.
Preferably, the biocatalyst for converting acrylonitrile to acrylamide may be obtained from culturing the microorganism in a suitable growth medium. The growth medium, also called fermentation (culture) medium, fermentation broth, fermentation mixture, or the like, may comprise typical components like sugars, polysaccharides, which are for example described in WO 2005/054489 and which are suitable to be used for the culturing the microorganism of the present inventions to obtain the biocatalyst. For storage of the microorganism, the fermentation broth preferably is removed in order to prevent putrefaction, which could result in a reduction of nitrile hydratase activity. The methods of storage described in WO 2005/054489 may be applied according to the present invention ensuring sufficient biocatalyst stability during storage. Preferably, the storage does not influence biocatalytic activity or does not lead to a reduction in biocatalytic activity. The biocatalyst may be stored in presence of the fermentations broth components. Preferred in the sense of the present invention is that the biocatalyst may be stored in form of a frozen suspension and may be thawed before use. Further, the biocatalyst may be stored in dried form using freeze-drying, spray drying, heat drying, vacuum drying, fluidized bed drying and/or spray granulation, wherein spray drying and freeze drying are preferred.
Biocatalyst Make-Up
The biocatalysts that are used according to the present invention in the modular, relocatable plant can for example be cultured under any conditions suitable for the purpose in accordance with any of the known methods, for instance as described in the mentioned prior art of this specification. The biocatalyst may be used as a whole cell catalyst for the generation of amide from nitrile. The biocatalyst may be (partly) immobilized for instance entrapped in a gel or it may be used for example as a free cell suspension. For immobilization well known standard methods can be applied like for example entrapment cross linkage such as glutaraldehyde-polyethyleneimine (GA-PEI) crosslinking, cross linking to a matrix and/or carrier binding etc., including variations and/or combinations of the aforementioned methods. Alternatively, the nitrile hydratase enzyme may be extracted and for instance may be used directly in the process for preparing the amide. When using inactivated or partly inactivated cells, such cells may be inactivated by thermal or chemical treatment.
In a preferred embodiment, the microorganisms are whole cells. The whole cells may be pre-treated by a drying step. Suitable drying methods and/or drying conditions are disclosed e.g. in WO 2016/050816 and WO 2016/050861 and the know art can be applied in the context of the present invention for the use in a relocatable bioconversion unit.
The microorganisms that are employed in the context of the present invention are in a preferred embodiment used in an aqueous suspension and in a more preferred embodiment are free whole cells in an aqueous suspension. The term “aqueous suspension” thereby includes all kinds of liquids, such as buffers or culture medium that are suitable to keep microorganisms in suspension. Such liquids are well-known to the skilled person and include for example storage buffers at suitable pH such as storage buffers which are used to deposit microorganisms, TRIS-based buffers, saline based buffers, water in all quality grades such as distilled water, pure water, tap water, or sea water, culture medium, growing medium, nutrient solutions, or fermentation broths, for example the fermentation broth that was used to culture the microorganisms. During storage for example the aqueous suspension is frozen and thawed before use, in particular without loss in activity.
The biocatalyst may be provided as powder or as aqueous suspension. If provided as powder it is frequently advisable to prepare an aqueous suspension before adding the catalyst into the bioconversion unit. In an embodiment, the biocatalyst suspension may be conducted by suspending the biocatalyst powder in water in a vessel comprising at least a mixing device, for example a stirrer, one or more inlets for water, the biocatalyst and optionally further additives and one outlet for the biocatalyst suspension. The volume of the vessel may be for example from 0.1 m3 to 1 m3. The concentration of the biocatalyst in the aqueous biocatalyst suspension may be for example from 1% to 30% by wt., for example from 10 to 20% by wt. relating to the total of all components of the aqueous suspension.
A biocatalyst suspension may be added directly to the bioconversion unit. In another embodiment a concentrated suspension may be diluted before adding it to the bioconversion unit.
Bioconversion
The hydrolysis of acrylonitrile to acryl amide by means of a biocatalyst is performed in a suitable relocatable bioconversion unit.
Particularly, the bioconversion is performed by contacting a mixture comprising water and acrylonitrile with the biocatalyst in the relocatable bioconversion unit. The term “contacting” is not specifically limited and includes for example bringing into contact with, admixing, stirring, shaking, pouring into, flowing into, or incorporating into. It is thus only decisive that the mentioned ingredients come into contact with each other no matter how that contact is achieved.
Therefore, in one embodiment of the present invention step [0] comprises the following steps:
(a) Adding the following components (i) to (iii) to a bioconversion unit to obtain a composition for bioconversion:
(b) performing a bioconversion on the composition obtained in step (a).
The bioconversion can for example be conducted under any conditions suitable for the purpose in accordance with any of the known methods, for instance as described in the mentioned prior art of this specification like e.g. WO 2016/050817, WO 2016/050819, WO 2017/055518.
The conversion of acylonitrile to the acrylamide may be carried out by any of a batch process and a continuous process, and the conversion may be carried out by selecting its reaction system from reaction systems such as suspended bed, a fixed bed, a fluidized bed and the like or by combining different reaction systems according to the form of the catalyst. Particularly, the method of the present invention may be carried out using a semi-batch process. In particular, the term “semi-batch process” as used herein may comprise that an aqueous acrylamide solution is produced in a discontinuous manner.
According to a non-limiting example for carrying out such a semi-batch process water, a certain amount of acrylonitrile and the biocatalyst are placed in the bioconversion unit. Further acrylonitrile is then added during the bioconversion until a desired content of acrylamide of the composition is reached. After such desired content of acrylamide is reached, the obtained composition is for example partly or entirely recovered from the reactor, before new reactants are placed therein. In particular, in any one of the methods of the present invention the acrylonitrile may be fed such that the content of acrylonitrile during step (b) is maintained substantially constant at a predetermined value. In general, in any one of the methods of the present invention the acrylonitrile content and/or the acrylamide content during step (b) may be monitored. Methods of monitoring the acrylonitrile contents are not limited and include Fourier Transform Infrared Spectroscopy (FTIR). In another embodiment, the heat-balance of the reaction may be used for monitoring the process. This means that monitoring via heat-balance method takes place by measuring the heat energy of the system during bioconversion and by calculating the loss of heat energy during the reaction in order to monitor the process.
Although the conversion of acrylonitrile to the acrylamide may preferably be carried out at atmospheric pressure, it may be carried out under pressure in order to increase solubility of acrylonitrile in the aqueous medium. Because biocatalysts are temperature sensitive and the hydrolysis is an exothermic reaction temperature control is important. The reaction temperature is not specifically restricted provided that it is not lower than the ice point of the aqueous medium. However, it is desirable to carry out the conversion at a temperature of usually 0 to 50° C., preferably 10 to 40° C., more preferably 15 to 30° C. Further suitable condition for the bioconversion according to the present invention are for example described in WO 2017/055518 and are preferably applicable for the method in a relocatable bioconversion unit.
Although the amount of biocatalyst may vary depending on the type of biocatalyst to be used, it is preferred that the activity of the biocatalyst, which is introduced to the reactor, preferably the relocatable bioconversion unit, is in the range of about 5 to 500 U per mg of dried cells of microorganism. Methods for determining the ability of a given biocatalyst (e.g. microorganism or enzyme) for catalyzing the conversion of acrylonitrile to acrylamide are known in the art. As an example, in context with the present invention, activity of a given biocatalyst to act as a nitrile hydratase in the sense of the present invention may be determined as follows: First reacting 100 μl of a cell suspension, cell lysate, dissolved enzyme powder or any other preparation containing the supposed nitrile hydratase with 875 μl of a 50 mM potassium phosphate buffer and 25 μl of acrylonitrile at 25° C. on an Eppendorf tube shaker at 1,000 rpm for 10 minutes.
After 10 minutes of reaction time, samples may be drawn and immediately quenched by adding the same volume of 1.4% hydrochloric acid. After mixing of the sample, cells may be removed by centrifugation for 1 minute at 10,000 rpm and the amount of acrylamide formed is determined by analyzing the clear supernatant by HPLC. For affirmation of an enzyme to be a nitrile hydratase in context with the present invention, the concentration of acrylamide shall particularly be between 0.25 and 1.25 mmol/l—if necessary, the sample has to be diluted accordingly and the conversion has to be repeated. The enzyme activity may then be deduced from the concentration of acrylamide by dividing the acrylamide concentration derived from HPLC analysis by the reaction time, which has been 10 minutes and by multiplying this value with the dilution factor between HPLC sample and original sample. Activities >5 U/mg dry cell weight, preferably >25 U/mg dry cell weight, more preferably >50 U/mg dry cell weight, most preferably >100 U/mg dry cell weight indicate the presence of a functionally expressed nitrile hydratase and are considered as nitrile hydratase in context with the present invention.
It is preferred, that the concentration of acrylonitrile during the bioconversion should not exceed 6% by wt. and may for example be in the range from 0.1% by wt. to 6% by wt., preferably from 0.2% by wt. to 5% by wt., more preferably from 0.3% by wt. to 4% by wt., even more preferably from 0.5% by wt. to 3% by wt., still more preferably from 0.8% by wt. to 2% by wt. and most preferably from 1% by wt. to 1.5% by wt., relating to the total of all components of the aqueous mixture. It is possible that the concentration may vary over time during the bioconversion reaction. In order to obtain more concentrated solutions of acrylamide the total amount of acrylonitrile should not be added all at once but it should be added stepwise or even continuously keeping the abovementioned concentration limits in mind. The disclosure of WO 2016/050818 teaches a method of additional dosing of acrylonitrile, which is suitable to be used and applied in the present invention.
The concentration of acrylamide in the obtained solution is in the range from 10% to 80%, preferably in the range from 20% to 70%, more preferably in the range from 30% to 65%, even more preferably in the range from 40% to 60%, most preferably in the range from 45% to 55% by weight of acrylamide monomers. The reaction should be carried out in such a manner that the final concentration of acrylonitrile in the final acrylamide solution obtained does not exceed 0.1% by weight relating to the total of all components of the aqueous solution. Typical reaction times may be from 2 to 20 h, in particular 4 h to 12 h, for example 6 h to 10 h. After completion of the addition of acrylonitrile, the reactor contents is allowed to further circulate for some time to complete the reaction, for example for 1 hour to 3 hours. The remaining contents of acrylonitrile should preferably be less than 100 ppm ACN.
Suitable reactors for performing the bioconversion are known to the skilled artisan. Examples comprise vessels of any shape, for example cylindrical or spherical vessels, or tube reactors. In one embodiment, the continuous tank reactor as disclosed in WO 2016/006556 A1 may be used for bioconversion.
In one embodiment of the invention, the relocatable bioconversion unit is similar to the relocatable storage unit for acrylonitrile as described above. Using largely the same equipment for storing acrylonitrile or other monomers and the bioconversion step contributes to an economic process for manufacturing aqueous acrylamide solutions.
The relocatable bioconversion unit comprises a reaction vessel. The volume of the reaction vessel is not specifically limited and may range from 10 m3 to 150 m3, for example it may be about 20 m3 to 50 m3. Preferably, the reaction vessel should be double walled and should be horizontal. Such a construction avoids installing a pit for the collection of any leakage thereby ensuring an easier and quicker relocation of the reaction unit.
The bioconversion unit furthermore comprises means for mixing the reaction mixture and means for controlling the temperature of the contents of the vessel. The hydrolysis of acrylonitrile to acrylamide is an exothermal reaction and therefore heat generated in course of the reaction should be removed in order to maintain an optimum temperature for bioconversion.
The bioconversion unit furthermore usually comprises means for measurement and control, for example means for controlling the temperature or for controlling the pressure in the vessel.
For temperature control, the preferred bioconversion unit comprises an external temperature control cycle comprising a pump which pumps the aqueous reactor contents from the storage vessel through a heat exchanger and back into the storage vessel, preferably via an injection nozzle.
In one embodiment, a separate, relocatable temperature control unit is used comprising pump and heat exchanger and which is connected with the bioconversion unit by pipes or flexible tubes. In a preferred embodiment, the temperature control cycle is integrated into the relocatable bioconversion unit. It may—for example—be located at one end of the unit besides the reaction vessel.
The reaction vessel may furthermore comprise means for mixing the aqueous reaction mixture, for example a stirrer.
Surprisingly, it has been found, that the external temperature control cycle described above may also be used as means for mixing. The stream of the aqueous reaction mixture which passes through the temperature control cycle and which is injected back into the reaction vessel causes a circulation of the aqueous reaction mixture within the reaction vessel which is sufficient to mix the aqueous reaction mixture.
Preferably, no stirrer is used for the mobile bioconversion unit. A stirrer is an additional mechanical device, which increases the technical complexity. When using the external temperature control cycle for mixing instead of a stirrer, the technical complexity can be reduced while still sufficient mixing during bioconversion can be ensured. Advantageously, without a stirrer a transportation step is easier, since no stirrer as additional technical component has to be removed before transportation. Further, a bioconversion unit without a stirrer offers more flexibility in form, shape, mechanical stability requirements and size for the bioconversion unit. In particular, a horizontal set-up for the relocatable bioconversion unit can be realized easier without a stirrer and with mixing just via the external temperature control cycle.
Adding acrylonitrile to the contents of the bioconversion unit may be performed in various ways. It may be added into the reaction vessel or it may be added into the temperature control cycle, for example after the pump and before the heat exchanger or after the heat exchanger. Injecting acrylonitrile into the temperature control cycle ensures good mixing of the reaction mixture with freshly added acrylonitrile. Preferably, acrylonitrile is added between pump and heat exchanger.
The amount of reaction mixture cycled per hour through the temperature control cycle is chosen such that sufficient mixing to the contents of the reactor as well as sufficient temperature control is achieved. In one embodiment, the amount of reaction mixture cycled per hour through the temperature control cycle may be from 100% to 1000% of the total volume of the reaction mixture in the bioconversion unit, in particular from 200% to 1000% and for example from 500% to 800%.
Off-gases of the bioconversion unit may comprise acrylonitrile, acrylic acid and acrylamide. If necessary, according to the applicable rules such off-gases may be treated in a manner known in the art. For example, it may be possible to combust the off-gases.
In one embodiment, all off-gases containing acrylonitrile, acrylic acid and acrylamide may be washed in a scrubber. The scrubber vessel may have a volume of 1 m3 to 100 m3, preferably a volume of 5 m3 to 100 m3, more preferably a volume of 10 m3 to 100 m3. It may be for example an ISO tank or relocatable storage vessel, preferably a double walled vessel. The scrubber water may preferably be collected in a tank and it may be re-used in the next bio-conversion batch.
Biomass Removal
After bioconversion, the reaction vessel comprises an aqueous solution of acrylamide, which still comprises the biocatalyst suspended therein.
The biocatalyst preferably becomes removed completely, essentially completely, or partially before polymerization, however, removing the biocatalyst may not be absolutely necessary in every case. Whether it is necessary to remove the biocatalyst substantially depends on two factors, namely whether remaining biocatalyst negatively affects polymerization and/or the properties of the polyacrylamide obtained and/or the biocatalyst negatively affects the application of the obtained polyacrylamide solution. In one embodiment, at least 75%, preferably at least 90% by weight of the biomass—relating to the total of the biomass present—should be removed.
The method for removing the biocatalyst is not specifically limited. Separation of the biocatalyst may take place by for example filtration or centrifugation. In other embodiments, active carbon may be used for separation purpose.
Procedurally, for removing the biocatalyst there are several options.
In one embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit, passed through a unit for removing the biocatalyst, and thereafter the aqueous acrylamide solution is filled into a suitable storage unit for acrylamide, preferably a relocatable storage unit for acrylamide as described above.
In another embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit, passed through a unit for removing the biocatalyst and thereafter the aqueous acrylamide solution is filled directly into the monomer make-up unit, i.e. without intermediate storing in an acrylamide storage unit.
In another embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit and is filled directly, i.e. without removing the biocatalyst, into the monomer make-up unit. In said embodiment, the biocatalyst is still present in course of monomer make-up and is removed after preparing the aqueous monomer solution (step [1]) as described below.
In another embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit, passed through a unit for removing the biocatalyst and thereafter filled back into the bioconversion unit. In order to ensure complete discharge of the bioconversion unit before re-filling it with the acrylamide solution, the unit for removing the biocatalyst should comprise a buffer vessel having a volume sufficient for absorbing the contents of the bioconversion unit.
The above-mentioned methods for biocatalyst removal are for example applicable for partwise and/or complete removal of the biocatalyst. Further, it is preferred, that the completely or partly removed biocatalyst may be reused for a subsequent bioconversion reaction.
Provision of Acrylic Acid
In the context of the present invention, acrylic acid or salts thereof may be used as comonomer besides acrylamide. Basically, any kind of acrylic acid may be used for the process according to the present invention, for example acrylic acid obtained by catalytic oxidation of propene. In one embodiment of the invention ammonium acrylate available by enzymatic hydrolysis of acrylonitrile may be used for carrying out the process according of the present invention (hereinafter also “bio acrylate”).
In a preferred embodiment of the present invention the manufacture of ammonium acrylate by enzymatic hydrolysis of acrylonitrile is also performed at the site of the modular plant in a modular unit. Suitable enzymes have been disclosed in WO 97/21827 A1 and the literature cited therein, and the publication describes also suitable conditions for carrying out the reaction. The manufacture of bio-acrylate may be carried out using stirred tank reactors or loop reactors, and in particular, the relocatable bioconversion unit described above may also be used.
Manufacturing bio-acrylate on-site also saves transport costs. Although acrylic acid may be provided to the site of the modular plant as pure compound, its molecular weight is −36% higher than that of acrylonitrile.
Step [1]—Preparation of an Aqueous Monomer Solution
In course of step [1] an aqueous monomer solution comprising at least water, acrylamide and optionally further water-soluble, monoethylenically unsaturated monomers is prepared in a relocatable monomer make-up unit.
Monomer Storage
Basically, it is possible to run step [1] as just-in-time-process, i.e. providing the monomers to the relocatable plant when monomers are needed and directly withdrawing the monomers from the transport vessels. However, in order to ensure an uninterrupted operation is preferred to hold available at least some storage capacity for the monomers at the location of the modular, relocatable plant.
Depending on the chemical nature, any water-soluble, monoethylenically unsaturated monomers to be used may be provided as pure monomers or as aqueous solutions to the plant. It is also possible to provide a mixture of two or more water-soluble, monoethylenically unsaturated monomers, in aqueous solution or as pure monomers, to the modular plant. Acrylamide and other water-soluble, monoethylenically unsaturated monomers such as acrylic acid, ATBS, or DM3AQ, or mixtures thereof, preferably may be stored in relocatable storage units. Details of such relocatable storage units for monomers have already been outlined above for acrylonitrile and we refer to the description above.
The monomers may be provided to the plant by road tankers, ISOtanks, or rail cars and pumped into the relocatable storage unit(s).
In one embodiment, a relocatable storage unit with integrated temperature control cycle as depicted in
In another embodiment, a relocatable storage unit with a separate, external temperature control cycle as depicted in
As a rule, the temperature of the monoethylenically unsaturated monomers such as acrylamide, acrylic acid, ATBS or DM3AQ should not exceed 25° C. to 30° C.
Pure associative monomers as described above may be waxy solids and may be stored at room temperature. They may be stored as aqueous solutions, for example as aqueous solutions comprising 25% by weight of the associative monomer. Because the amounts of associative monomers are significantly smaller than the amounts of other monoethylenically unsaturated monomers smaller relocatable storage units than that described above may be used.
Acidic monomers such as acrylic acid or ATBS are often partially or completely neutralized for polymerization using suitable bases.
Bases, such as aqueous solutions of NaOH may also be stored in storage vessels as described above. A cooling cycle is not necessary. To the contrary, depending on the climatic conditions, a heating such as a heating element in the vessel may be necessary because concentrated NaOH freezes at about +15° C.
Monomer Make-up
The aqueous monomer solution for polymerization to be prepared in course of step [1] in the relocatable monomer make-up unit comprises water and 5% to 45% by weight, preferably 15% to 45% by weight of water-soluble, monoethylenically unsaturated monomers, relating to the total of all components of the aqueous monomer solution. The water-soluble, monoethylenically unsaturated monomers comprise at least acrylamide, preferably bio acrylamide which preferably is manufactured in step [0] also at the location of the modular, relocatable plant. The monomer concentration may be selected by the skilled artisan according to his/her needs. Details about adequately selecting the monomer concentration will be provided below.
In one embodiment of the invention, the monomer concentration is from 8% by weight to 24.9% by weight, preferably from 15% by weight to 24.9% by weight, for example from 20 to 24.9% by weight, relating to the total of all components of the aqueous monomer solution.
For preparing the aqueous monomer solution, the water-soluble, monoethylenically unsaturated monomers to be used are mixed with each other. All monomers and optionally additives may be mixed with each other in a single step but it may also be possible to mix some monomers and add further monomers in a second step. Also, water for adjusting the concentration of the monomers may be added. Water eventually used for rinsing lines in course of transferring the monomer solution into the polymerization unit, needs to be taken into consideration when adjusting the concentration.
Further additives and auxiliaries may be added to the aqueous monomer solution.
Examples of such further additives and auxiliaries comprise bases or acids for adjusting the pH value. In certain embodiments of the invention, the pH-value of the aqueous solution is adjusted to values from pH 5 to pH 7, for example pH 6 to pH 7.
Examples of further additives and auxiliaries comprise complexing agents, defoamers surfactants, or stabilizers.
In one embodiment, the aqueous monomer solution comprises at least one stabilizer for the prevention of polymer degradation. The stabilizers for the prevention of polymer degradation are what are called “free-radical scavengers”, i.e. compounds which can react with free radicals (for example free radicals formed by heat, light, redox processes), such that said radicals can no longer attack and hence degrade the polymer. Using such kind of stabilizers for the stabilization of aqueous solutions of polyacrylamides basically is known in the art, as disclosed for example in WO 2015/158517 A1, WO 2016/131940 A1, or WO 2016/131941 A1.
The stabilizers may be selected from the group of non-polymerizable stabilizers and polymerizable stabilizers. Polymerizable stabilizers comprise a monoethylenically unsaturated group and become incorporated into the polymer chain in course of polymerization. Non-polymerizable stabilizers don't comprise such monoethylenically unsaturated groups and are not incorporated into the polymer chain.
In one embodiment of the invention, stabilizers are non-polymerizable stabilizers selected from the group of sulfur compounds, sterically hindered amines, N-oxides, nitroso compounds, aromatic hydroxyl compounds or ketones.
Examples of sulfur compounds include thiourea, substituted thioureas such as N,N′-dimethylthiourea, N,N′-diethylthiourea, N,N′-diphenylthiourea, thiocyanates, for example ammonium thiocyanate or potassium thiocyanate, tetramethylthiuram disulfide, and mercaptans such as 2-mercaptobenzothiazole or 2-mercaptobenzimidazole or salts thereof, for example the sodium salts, sodium dimethyldithiocarbamate, 2,2′-dithiobis(benzothiazole), 4,4′-thiobis(6-t-butyl-m-cresol).
Further examples include dicyandiamide, guanidine, cyanamide, paramethoxyphenol, 2,6-di-t-butyl-4-methylphenol, butylhydroxyanisole, 8-hydroxyquinoline, 2,5-di(t-amyl)-hydroquinone, 5-hydroxy-1,4-naphthoquinone, 2,5-di(t-amyl)hydroquinone, dimedone, propyl 3,4,5-trihydroxybenzoate, ammonium N-nitrosophenylhydroxylamine, 4-hydroxy-2,2,6,6-tetramethyoxylpiperidine, (N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine and 1,2,2,6,6-pentamethyl-4-piperidinol.
Preference is given to sterically hindered amines such as 1,2,2,6,6-pentamethyl-4-piperidinol and sulfur compounds, preferably mercapto compounds, especially 2-mercaptobenzothiazole or 2-mercaptobenzimidazole or the respective salts thereof, for example the sodium salts, and particular preference is given to 2-mercaptobenzothiazole or salts thereof, for example the sodium salts.
The amount of such non-polymerizable stabilizers—if present—may be from 0.1% to 2.0% by weight, relating to the total of all monomers in the aqueous monomer solution, preferably from 0.15% to 1.0% by weight and more preferably from 0.2% to 0.75% by weight.
In another embodiment of the invention, the stabilizers are polymerizable stabilizers substituted by a monoethylenically unsaturated group. Examples of stabilizers comprising monoethylenically unsaturated groups comprise (meth)acrylic acid esters of 1,2,2,6,-pentamethyl-4-piperidinol or other monoethylenically unsaturated groups comprising 1,2,2,6,6-pentamethyl-piperidin-4-yl groups. Specific examples of suitable polymerizable stabilizers are disclosed in WO 2015/024865 A1, page 22, lines 9 to 19. In one embodiment of the invention, the stabilizer is a (meth)acrylic acid ester of 1,2,2,6,6-pentamethyl-4-piperidinol.
The amount of polymerizable stabilizers—if present—may be from 0.01 to 2% by weight, based on the sum total of all the monomers in the aqueous monomer solution, preferably from 0.02% to 1% by weight, more preferably from 0.05% to 0.5% by weight.
In one embodiment, the aqueous monomer solution comprises at least one non-polymerizable surfactant. Adding such surfactants in particular is advisable when associative monomers are used. For such kind of polyacrylamides the surfactants lead to a distinct improvement of the product properties. Examples of suitable surfactants including preferred amounts have been disclosed in WO 2015/158517 A1, page 19, line, 23 to page 20, line 27. If present, such non-polymerizable surfactant may be used in an amount of 0.1 to 5% by weight, for example 0.5 to 3% by weight based on the amount of all the monomers used.
The relocatable monomer make-up unit may be any kind of equipment for the mixing monomers provided that it is relocatable, for example a stirred, relocatable vessel.
In one embodiment, a relocatable monomer make-up unit is similar to the relocatable bioconversion unit as described above. Using largely the same equipment for storing acrylonitrile or other monomers, the bioconversion step and for monomer make-up contributes to an economic process for manufacturing aqueous acrylamide solutions.
The relocatable monomer make-up unit comprises a monomer make-up vessel in which the monomers, water and optionally further components are mixed.
The volume of the monomer make-up vessel is not specifically limited and may range from 10 m3 to 150 m3, for example it may be about 20 to 90 m3. Preferably, the monomer make-up vessel should be double walled and should be horizontal. Such a construction avoids installing a pit for the collection of any leakage thereby ensuring an easier and quicker relocation of the reaction unit.
The relocatable monomer make-up unit furthermore comprises means for controlling the temperature of the aqueous monomer solution. Usually, the temperature of the aqueous monomer solution should be not more than 5° C., for example from −5° C. to +5° C. The monomer make-up unit furthermore comprises means for measurement and control.
For temperature control, the relocatable monomer make-up unit comprises an external temperature control cycle comprising a pump which pumps the aqueous reactor contents from the storage vessel through a heat exchanger and back into the storage vessel, preferably via an injection nozzle.
The temperature control cycle may be a separate, relocatable temperature control unit comprising pump and heat exchanger which is connected with the monomer make-up vessel by pipes or flexible tubes. In another embodiment, the temperature control cycle may be integrated into relocatable monomer make-up unit. It may—for example—be located at one end of the unit besides the monomer make-up vessel.
The monomer make-up vessel may be equipped with a stirrer for mixing the components of the aqueous monomer solution with each other.
However, in the same manner as with the bioreactor, the external temperature control cycle may be used as means for mixing. The stream of the aqueous monomer mixture which passes through the temperature control cycle and which is injected back into the monomer make-up vessel causes a circulation of the aqueous reaction mixture within the reaction vessel which is sufficient to mix the aqueous reaction mixture.
In another embodiment, a separate temperature control cycle may be used.
The monomers to be mixed with each other and with water are preferably mixed in the monomer make-up vessel, however in another embodiment, it is possible to add the monomers into the temperature control cycle. It is frequently advisable, to first add water to the monomer make-up vessel and then one or more further monomers and/or acids or bases and/or further additives. If acidic monomers such as acrylic acid are used, they should be neutralized before adding acrylamide. For copolymers comprising acrylic acid and acrylamide at first the necessary amount of water may be added into the vessel, followed by NaOH, thereafter acrylic acid and thereafter acrylamide.
Further additives which optionally might be present such as complexing agents, defoamers surfactants, or stabilizers as mentioned above may be dissolved in aqueous solvents, preferably water in suitable dissolution units and the solutions also added into the monomer make-up vessel.
In another embodiment of the invention, the bioconversion unit may also be used for monomer make-up.
In a preferred embodiment, the aqueous acrylamide solution does no longer comprise the biocatalyst. However, in another embodiment the acyl amide solution still comprises the biomass. In said embodiment, the biocatalyst may be removed after preparing the aqueous monomer solution in the same manner as described above or it may not be removed. Criteria for deciding in which cases it may not be necessary to remove the biocatalyst have already been mentioned above.
After mixing the aqueous monomer solution it is transferred from the relocatable monomer make-up unit or any other unit serving as monomer make-up vessel such as the bioconversion unit to the polymerization unit. Such connection for transferring the aqueous monomer solution hereinafter also is referred to as “monomer feed line”.
In one embodiment, associative monomers may also be added into the monomer make-up vessel. However, in a preferred embodiment, aqueous solutions of the associative monomers, in particular associative monomers having the formula (III), (IV), or (V) may be metered into the monomer feed line.
In another embodiment of the invention, the relocatable polymerization unit itself may be used for monomer make-up. As will be detailed below, the relocatable polymerization unit may be connected to a temperature control unit before polymerization, so that the monomer solution may also be cooled in the polymerization unit until directly before the start of polymerization. As will be detailed also below, the polymerization unit may comprise injection nozzles for nitrogen or other inert gases in order to inert the contents of the polymerization unit and such injection of inert gases also efficiently mixes the contents of polymerization unit. Also, combinations are possible, for example providing a monomer concentrate in a separate, relocatable monomer make-up unit and diluting the aqueous monomer solution in the relocatable polymerization unit with additional water. In another example, acids or bases—if necessary—may be added not into a separate monomer make-up unit but directly to the polymerization unit.
Step [2]—Polymerization
In course of step [2] the aqueous monomer solution prepared in step [1] is polymerized in the presence of suitable initiators for radical polymerization under adiabatic conditions thereby obtaining an aqueous polyacrylamide gel.
Such a polymerization technique is also briefly denominated by the skilled artisan as “adiabatic gel polymerization”. Reactors for adiabatic gel polymerization are unstirred. Due to the relatively high monomer concentration the aqueous monomer solution used solidifies in course of polymerization thereby yielding an aqueous polymer gel. The term “polymer gel” has been defined for instance by L. Z. Rogovina et al., Polymer Science, Ser. C, 2008, Vol. 50, No. 1, pp. 85-92.
“Adiabatic” is understood by the person skilled in the art to mean that there is no exchange of heat with the environment. This ideal is naturally difficult to achieve in practical chemical engineering. In the context of this invention, “adiabatic” shall consequently be understood to mean “essentially adiabatic”, meaning that the reactor is not supplied with any heat from the outside during the polymerization, i.e. is not heated, and the reactor is not cooled during the polymerization. However, it will be clear to the person skilled in the art that—according to the internal temperature of the reactor and the ambient temperature—certain amounts of heat can be released or absorbed via the reactor wall because of temperature gradients, but this effect naturally plays an ever lesser role with increasing reactor size.
The polymerization of the aqueous monomer solution generates polymerization heat. Due to the adiabatic reaction conditions the temperature of the polymerization mixture increases in course of polymerization.
The polymerization is performed in a relocatable polymerization unit having a volume of 1 m3 to 100 m3, in particular 1 to 40 m2, preferably from 5 m3 to 40 m3, more preferably 5 to 30 m3 and more preferably 20 m3 to 30 m3.
The transportable polymerization unit may be of cylindrical or conical shape.
Preferably, the polymerization unit is cylindrical having a conical taper at the bottom and a bottom opening for removing the aqueous poly acrylamide gel. In one embodiment, there may be additionally a cylindrical section between the lower end of the conical taper and the bottom opening. The inner wall of the transportable polymerization unit may preferably be coated with an anti-adhesive coating. Basically, anti-adhesive coatings are known in the art. Examples comprise polypropylene, polyethylene, epoxy resins and fluorine containing polymers such as polytetrafluoroethylene or perfluoroalkoxy polymers.
One embodiment of a relocatable polymerization unit for use in the present invention is schematically shown in
The diameter (D) of the polymerization unit P1 in the cylindrical section may in particular be from 1.5 to 2.5 m, preferably from 2 m to 2.5 m and the length (L) of the cylindrical section may be from 4 to 6 m, preferably 5 to 6 m. The conus angle α in the conical part (see also
The relocatable polymerization unit P1 is operated in a vertical position as depicted in
For polymerization, the aqueous monomer solution prepared in course of step [1] is filled into the relocatable polymerization unit, in particular into the polymerization unit P1. For that purpose, the relocatable monomer make-up unit or any other unit serving as monomer make-up unit such as the bioconversion unit is connected with the polymerization unit by a monomer feed line.
As already outlined above, in another embodiment the aqueous monomer solution may be prepared in the polymerization unit itself. In such embodiment, the polymerization unit already is filled with an aqueous monomer solution and it is no longer necessary to fill the monomer solution into the relocatable polymerization unit.
The polymerization is performed in the presence of suitable initiators for radical polymerization. Suitable initiators for radical polymerization, in particular for adiabatic gel polymerization are known to the skilled artisan.
In a preferred embodiment, redox initiators are used for initiating. Redox initiators can initiate a free-radical polymerization even at temperatures of less than +5° C. Examples of redox initiators are known to the skilled artisan and include systems based on Fe2+/Fe3+—H2O2, Fe2+/Fe3+-alkyl hydroperoxides, alkyl hydroperoxides-sulfite, for example t-butyl hydroperoxide-sodium sulfite, peroxides-thiosulfate or alkyl hydroperoxides-sulfinates, for example alkyl hydroperoxides/hydroxymethane-sulfinates, for example t-butyl hydroperoxide-sodium hydroxymethanesulfinate.
Furthermore, water-soluble azo initiators may be used. The azo initiators are preferably fully water-soluble, but it is sufficient that they are soluble in the monomer solution in the desired amount. Preferably, azo initiators having a 10 h t1/2 in water of 40° C. to 70° C. may be used. The 10-hour half-life temperature of azo initiators is a parameter known in the art. It describes the temperature at which, after 10 h in each case, half of the amount of initiator originally present has decomposed.
Examples of suitable azo initiators having a 10 h t1/2 temperature between 40 and 70° C. include 2,2′-azobis[2-(2-imidazolin-2-yl)propane] dihydrochloride (10 h t1/2 (water): 44° C.), 2,2′-azobis(2-methylpropionamidine) dihydrochloride (10 h t1/2 (water): 56° C.), 2,2′-azobis[N-(2-carboxyethyl)-2-methylpropionamidine hydrate (10 h t1/2 (water): 57° C.), 2,2′-azobis{2-[1-(2-hydroxyethyl)-2-imidazolin-2-yl]propane} dihydrochloride (10 h t1/2 (water): 60° C.), 2,2′-azobis(1-imino-1-pyrrolidino-2-ethylpropane) dihydrochloride (10 h t1/2 (water): 67° C.) or azobis(isobutyronitrile) (10 h t1/2 (toluene): 67° C.).
In one embodiment of the invention a combination of at least one redox initiator and at least one azo initiator is used. The redox initiator efficiently starts polymerization already at temperatures below +5° C. When the reaction mixture heats up, also the azo initiators decompose and also start polymerization.
The initiators preferably are added as aqueous solutions to the aqueous monomer solution. The initiator raw material may be stored in a cold storage container. Dissolving the initiators in water may be performed using suitable relocatable initiator make-up vessels. The initiator make-up vessel may comprise a temperature control cycle. Instead of an own temperature control cycle, cold water, for example water having a temperature of less than +5° C. may be used for dissolving the initiators. The initiator make-up vessels furthermore may comprise means for mixing such as a stirrer. However, mixing may also be conducted by bubbling an inert gas through the aqueous mixture thereby simultaneously mixing and inerting the aqueous mixture. The solutions may be filtered before use.
Solutions of azo initiators may be added into the monomer feed line while the aqueous monomer solution is transferred from the relocatable monomer make-up unit to the relocatable polymerization unit. In another embodiment solutions of azo initiators may already be added to the monomer make-up vessel, provided the monomer solution has already been cooled to temperatures below ambient temperature, preferably to less than +5° C. and the 10 h t1/2 temperature of the initiator is high enough so that the initiator doesn't decompose prematurely.
Solutions of redox initiators may be added into the monomer feed line or into the relocatable polymerization unit.
Before polymerization oxygen from the reactor and the reaction mixture to be polymerized needs to be removed. Deoxygenation is also known as inertization.
In one embodiment, inertization is performed in the relocatable polymerization unit. For that purpose, inert gases such as nitrogen or argon are injected into the reactor filled with the monomer solution. Preferably, nozzles for injecting inert gases are located in the bottom of the polymerization unit. In the relocatable polymerization unit P1 they may for example be located in the conical taper. The bubbles of inert gases rising in the reactor remove oxygen and simultaneously mix the contents of the reactor very efficiently. Initiator solutions metered into the reactor are mixed with the aqueous solution by means of the inert gas injection.
In another embodiment, inertization may be performed in the monomer feed line. Inert gases such as nitrogen or argon may be injected into the feed line. In order to ensure effective mixing of the gas injected and the aqueous gases injected it is frequently desirable that the monomer feed line additionally comprises a static mixture. The gas injected into the monomer feed line may be removed before entering into the reactor by means of a suitable degassing unit such as the degassing units described in WO 2003/066190 A1 or in CN 202492486 U. In another embodiment, no separate degassing unit is used, but the solution is degassed after entering into the polymerization unit. In one embodiment, the monomer solution enters into the reactor by means of a spray nozzle for the purpose of removing gas.
Of course, it is possible to combine the two embodiments for degassing, i.e. to purging the relocatable polymerization unit with inert gases and degassing the monomer mixture.
The radical polymerization starts after adding the initiator solutions, preferably solutions of redox initiators, to the aqueous monomer solution thereby forming an aqueous polyacrylamide gel. Due to the polymerization heat generated in course of polymerization and the adiabatic reaction conditions, the temperature in the polymerization unit increases.
In the following, the temperature of the aqueous monomer solution before the onset of polymerization shall be denominated as T1 and the temperature of the aqueous polymer gel directly after polymerization shall be denominated as T2. It goes without saying that T2>T1.
Within the context of the present invention, the temperature T1 should not exceed 30° C., in particular T1 should not exceed 25° C. Preferably, T1 should not exceed 10° C., more preferably not +5° C. In one embodiment, T1 may be from −5° C. to +30° C., for example from −5° C. to +25° C., preferably from −5° C. to +5° C., and more preferably from −5° C. to +5° C. The temperature T1 of the monomer solution may be adjusted as already disclosed above, i.e. already the monomer solution in the monomer make-up vessel may be cooled appropriately. Of course, also the temperature control unit for adjusting T1 may be located in the monomer feed line, or the polymerization unit may be connected to a temperature control unit before polymerization, so that the monomer solution may still be cooled in the polymerization unit until directly before the start of polymerization.
As the polymerization is carried out under adiabatic conditions, the temperature T2 reached in course of polymerization is not influenced by external heating or cooling but only depends on the polymerization parameters chosen. But suitable choice of the polymerization parameters, the skilled artisan can adjust T2. Because the reaction is adiabatic, the temperature increase in course of polymerization basically depends on the heat of polymerization generated in course of polymerization, the heat capacity of contents of the polymerization unit and the temperature T1 of the monomer solution, i.e. the temperature before the onset of polymerization. Due to high water contents of the mixture for polymerization the heat capacity of the mixture for polymerization is dominated by the heat capacity of water and it may of course be measured. The polymerization heat per mole (or per mass) for common monoethylenically unsaturated monomers is known in the art and may therefore be gathered from the scientific literature. Of course, it may also be measured. So, it is possible for the skilled artisan to calculate at least roughly the heat of polymerization for specific monomer compositions and specific monomer concentrations. The higher the concentration of the monoethylenically unsaturated monomers in the aqueous solution the more heat of polymerization is generated. T2 may be roughly calculated from the parameter mentioned above by the formula T2=T1+[(polymerization heat)/(heat capacity)]. The temperature T2 should be at least 45° C., preferably at least 50° C., for example from 50° C. to 100° C., for example from 55° C. to 95° C. In an embodiment of the invention T1 is from −15° C. to +5° C. and T2 is from 50° C. to 95° C.
In one embodiment of the invention, T2 does not exceed 70° C., preferably it does not exceed 65° C. On the other hand, it shouldn't be too low, in order to ensure an essentially complete polymerization. In certain embodiments of the invention, T2 should be from 45° C. to 70° C., in particular from 50° C. to 70° C., preferably from 50° C. for 65° C. For example, it may be from 55° C. to 65° C. In one embodiment, T1 is from −15° C. to +5° C. and T2 is from 50° C. to 70° C., preferably from 50° C. for 65° C. and for example from 55° C. to 65° C.
Limiting T2 to temperatures ≤70° C. may be achieved by the measures mentioned above. In particular, it is advisable to choose a concentration of monomers in the aqueous polymer solution of 5% by weight to 24.9% by weight relating to the total of all components of the aqueous solution, in particular 8% by wt. to 24.9% by weight and for example 20% by weight to 24.9% by weight. In addition, T1 may be −5° C. to +5° C.
The time of polymerization may be from 2 to 24 h, for example from 3 to 6 h.
For lower concentrations, T1 may also be chosen to be more than +5° C. For concentrations around 20% by weight, T1 may be chosen to be around +10° C. to achieve a T2 in the range from 50° C. to 65° C. For concentrations around 15% by weight, T1 may be chosen to be around +25° C. to achieve a T2 in the range from 50° C. to 65° C.
Step [3] Removal of the Aqueous Polyacrylamide Gel
In course of step [3], the aqueous polyacrylamide gel is removed from the relocatable polymerization unit. After removal from the polymerization unit the aqueous polymer gel is further processed by comminuting and dissolving the aqueous polyacrylamide gel in an aqueous fluid.
Basically, removing the aqueous polyacrylamide gel may be performed by any kind of technology. The details depend on the specific design of the polymerization vessel and the connected downstream processing equipment.
Preferably, the aqueous polyacrylamide gel may be removed by applying pressure onto the gel and pressing it through an opening in the relocatable polymerization unit. By the way of example, pressure may be generated by mechanical means such as a piston, by means of gases such as compressed air, nitrogen, argon or by means of aqueous fluids, in particular water. Preferably, gases and/or aqueous fluids are used.
For removing the polyacrylamide gel from the preferred relocatable polymerization unit P1, the relocatable polymerization unit P1 is operated in vertical position. The aqueous polyacrylamide gel is removed through the opening (26) at the bottom which is opened for the purpose of removing by applying pressure onto the gel from the top side of the reactor. Pressure may be applied using gases and/or water. Examples of gases comprise pressurized air, nitrogen or argon. Basically, any kind of gas may be used, provided it does not react with the polyacrylamide gel. In another embodiment, the relocatable polymerization unit may comprise mechanical means, such as a piston for generating pressure. The pressure to be applied for removing the gel may be selected by the skilled artisan. Factors relevant for the selection of the pressure include the viscosity of the polyacrylamide gel, the width of the bottom opening (26), the geometry of the polymerization unit or—if present—the kind of anti-adhesive layer. For example, pressures may range from 110,000 Pa to 1,000,000 Pa, in particular 150,000 Pa to 750,000 Pa, for example 200,000 Pa to 500,000 Pa (absolute pressures). Removing the aqueous polyacrylamide gel may be supported by a thin water-film at the inner walls of the reactor, in particular on the walls of the conical part of the reactor. Such a thin water-film may be generated by injecting water or an aqueous fluid through fine holes in the wall of the reactor into the reactor, in particular holes in the conical part. Should some polymer gel remain in the polymerization unit, the polymerization unit may be rinsed with water to remove the remaining amounts.
The bottom opening (26) of the polymerization unit P1 may be connected with a comminution unit—if present—or directly with a suitable dissolution unit, for instance with a stirred vessel. Said connection may simply be a pipe but it may also comprise means for transporting the gel such as for example screw conveyors or belt conveyors.
In other embodiments, the polyacrylamide gel may be conveyed by the gas pressure from the polymerization reactor into a pump. Such a pump may be helpful in achieving a constant feed rate and a constant pressure for the consecutive step [4] of comminuting and dissolving the polyacrylamide gel. Depending on the nature of the equipment used for step [5] ensuring constant feed rate and a constant pressure may be difficult to achieve by gas pressure alone. A pump may in particular be helpful, if it is the aim to convey the polyacrylamide gel through a comminution unit in course of step [4] causing a significant pressure drop, such as for example conveying the polyacrylamide gel through a hole perforation plate and/or conveying the gel through a relatively long pipe.
Suitable are all pumps capable of transporting the polyacrylamide gel, in particular positive displacement pumps such as a progressive cavity pump or a screw spindle pump.
Steps [4] and [5] Comminution and Dissolution of the Aqueous Polyacrylamide Gel
In course of step [4] the aqueous polyacrylamide gel is comminuted and in course of step [5] dissolved in an aqueous liquid, thereby obtaining an aqueous polyacrylamide solution.
Comminuting the aqueous polyacrylamide gel before dissolution in an aqueous liquid is helpful, because smaller gel particles dissolve more quickly in the aqueous liquid than larger gel particles. It should be kept in mind that already removing the aqueous polyacyrylamide gel from the polymerization unit (i.e. step [3]) may cause some disintegration of the gel into smaller gel pieces.
Steps [4] and [5] may be separate steps to be conducted consecutively or the steps may be combined with each other. In other embodiments, already some of the polyacrylamide gel may be dissolved in course of step [4] but dissolution mostly takes place in a consecutive step [5]. As will be detailed below, step [4] may comprise adding already some aqueous liquid, preferably water, to the aqueous polyacrylamide gel and a certain amount of the aqueous polyacrylamide gel might already dissolve in course of step [4], thereby yielding aqueous polyacrylamide gel pieces suspended in an aqueous polyacrylamide solution.
The aqueous liquid used for dissolving the aqueous polyacrylamide gel comprises water. The term “water” includes any kind of water such as desalinated water, fresh water or water comprising salts, such as brines, sea water, formation water, produced water or mixtures thereof. Besides water, the aqueous liquid may comprise organic solvents miscible with water, however the amount of water relating to the total of all solvent should be at least 70% by weight, preferably at least 90% by weight, more preferably at least 95% by weight. In one preferred embodiment, the aqueous liquid comprises only water as solvent. Furthermore, the aqueous liquid may optionally also comprise additives such as for example surfactants, complexing agents, bases, acids of the like. Kind and amount of such additives may be selected according to the intended use of the aqueous polyacrylamide solution. Of course, additives may also be added at a later stage, for example after complete dissolution of the aqueous polyacrylamide gel.
The concentration of the aqueous polyacrylamide solution to be obtained in course of step [5] may be selected by the skilled artisan according to the intended use of the solution. The term “aqueous solution” shall not be limited to dilute aqueous solutions but shall also encompass concentrates. It goes without saying, that the polyacrylamide concentration of an aqueous solution obtained after carrying out step [5] necessarily is lower than the concentration of the aqueous polyacrylamide gel before carrying out step [5]. More concentrated solutions may require—depending on the viscosities of such solutions—pressure, for example pressure created by pumps for transport in pumps. The viscosities of polyacrylamide solutions depend as a matter of principle on various factors such as chemical composition, chemical composition of the aqueous solvent, molecular weight, temperature, pH value or concentration.
In particular, the concentrations of the aqueous polyacrylamide solutions may be up to 14.9% by weight, for example from 0.01 to 14.9% by weight, preferably from 0.01 to 7% by weight.
Typically, the concentration of the diluted aqueous polyacrylamide solution may be up to 2% by weight, for instance, from 0.01 to 2%, suitably from 0.05 to 1.5%, often, 0.1% to 1%.
Aqueous polyacrylamide concentrates may have a concentration from 2.1 to 14.9% by weight, in particular from 2.1% to 7% by wt., for example from 3.1% to 6% by weight. It goes without saying, that obtaining a concentrate of 14.9% by weight requires that the concentration of the polyacrylamide gel used as starting material for step 5 is greater than 14.9% by weight.
Step [4] Comminution of the Aqueous Polyacrylamide Gel
In course of step [4] the aqueous polyacrylamide gel is comminuted by conveying the aqueous polyacrylamide gel through at least one relocatable comminuting unit, thereby obtaining aqueous polyacrylamide gel pieces.
The relocatable comminution unit may be a separate, relocatable comminution unit. In another embodiment, the comminution unit may be fixed to the relocatable polymerization unit, so that the relocatable polymerization unit and the comminution unit are one relocatable unit. Such a unit is relocatable in its entirety.
The particle size of the aqueous polyacrylamide gel pieces obtained in course of step [4] is not specifically limited. In an embodiment of the invention, particles of aqueous polyacrylamide gel should conveniently have a size such that at least two dimensions are no more than 1 cm, preferably no more than 0.5 cm. Preferably three dimensions of the aqueous polyacrylamide gel pieces should be no more than 1 cm, preferably no more than 0.5 cm. There is no lower limit necessary for the aqueous polyacrylamide gel pieces, since the smaller the pieces the easier it will be for the polymer to dissolve. Frequently, aqueous polyacrylamide gel pieces may have a size such that three dimensions are as low as 0.1 cm. Often the aqueous polyacrylamide gel pieces tend to have three dimensions each of from 0.1 cm to 0.5 cm.
Basically, any kinds of comminution means maybe used for disintegrating the aqueous polyacrylamide gel into smaller particles. Examples of suitable means for comminuting aqueous polyacrylamide gels include cutting devices such as knives or perforated plates, crushers, kneaders, static mixers or water-jets.
In other embodiments, the relocatable comminution unit may not be directly connected with the polymerization unit but distant from it and the aqueous polyacrylamide gel is transported to the comminution unit, for example by screw conveyors or belt conveyors.
When the preferred polymerization unit P1 is used, preferably, the bottom opening (32) may be connected with the comminution unit, either directly or with a pump as outlined above in between.
Static Cutting Device
In one embodiment of the invention, the aqueous polyacrylamide gel is conveyed through a static cutting device, such as knives or metal grills thereby obtaining smaller gel particles. A static cutting device preferably may belocated directly under the bottom opening (32). In other embodiments, a pump as described above may transport the polyacrylamide gel to a more distant static cutting device. Suitable static cutting devices comprise perforated plates or metal grills, such as disclosed, for instance, in U.S. Pat. No. 4,605,689. In one embodiment, the aqueous gel is conveyed through the static cutting device or into the connection between the pump and the static cutting device together with an aqueous liquid as described above, preferably water, thereby yielding a mixture of particles of an aqueous polyacrylamide gel in an aqueous liquid. The aqueous liquid is metered into the connection between the bottom opening (32) and the static cutting device, i.e. before the gel enters into the static cutting device. Preferably, not the entire amount of the aqueous liquid necessary to dissolve the polyacrylamide gel completely and to achieve the desired concentration is added at this stage but only a portion of it. Surprisingly, already 1% of the total amount of aqueous liquid significantly improves conveying the aqueous polyacrylamide gel through the static cutting device. It goes without saying that already some portion of the polyacrylamide gel may dissolve in the aqueous liquid, thereby obtaining a mixture of an aqueous polyacrylamide gel in a diluted polyacrylamide solution. The mixture comprising aqueous polyacrylamide gel pieces in an aqueous liquid/a diluted acrylamide solution is conveyed to the dissolution unit, for example through a pipe.
Perforated Plate
In another embodiment of the invention, the relocatable comminution unit comprises a perforated plate the aqueous polyacrylamide gel is conveyed through such perforated plate. An extruder or a screw conveyor or a pump may be used to generate the necessary pressure for passing the perforated plate. In course of passing through the perforated plates a number of separate cords of aqueous acrylamide gel are formed. They may be cut by a rotating knife or may be flushed away by means of a water jet and conveyed to the dissolution unit.
Static Mixer
In another embodiment of the invention, the aqueous polyacrylamide gel is conveyed together with an aqueous liquid through a static mixer thereby yielding a mixture of particles of an aqueous polyacrylamide gel in an aqueous liquid. Of course also a plurality of static mixers may be used. The aqueous liquid is metered into the connection between the bottom opening (26) and the static mixer, or into the connection between the pump and the static mixer, i.e. before the gel enters into the static mixer. In an embodiment, not the entire amount of aqueous liquid necessary to dissolve the polyacrylamide gel completely and to achieve the desired concentration is added at this stage but only a portion of it. It goes without saying that already some portion of the polyacrylamide gel may dissolve in the aqueous liquid, i.e. the mixture may be also a mixture of an aqueous polyacrylamide gel in a diluted polyacrylamide solution. The mixture comprising aqueous polyacrylamide gel pieces in an aqueous liquid/a diluted acrylamide solution is conveyed to the dissolution unit, for example through a pipe.
Water-Jet Cutting
In a preferred embodiment of the invention, the aqueous polyacrylamide gel is cut into pieces on aqueous polyacrylamide gel by means of a water-jet cutting unit. The water-jet cutting unit cuts the aqueous polyacrylamide gel by means of at least one water jet at a pressure of at least 150*105 Pa thereby obtaining a mixture of particles of an aqueous polyacrylamide gel in an aqueous liquid. Of course, already some of the aqueous polyacrylamide gel may dissolve in the aqueous liquid in course of water-jet cutting.
Preferably, the surrounding wall section of the water jet cutting unit is a tubular section, a conical section or a combination of tubular and conical sections. The aqueous polyacrylamide gel may then enter into the water jet cutting unit from one end, pass through the cutting stage to reduce the size of the aqueous polyacrylamide gel and desirably the so formed aqueous polyacrylamide gel pieces should exit from the outlet. Aqueous liquid from the cutting stage, desirably should also exit from the outlet. Thus, a mixture of aqueous polyacrylamide gel pieces and water optionally comprising dissolved polymer gel may be formed in the cutting stage.
The surrounding wall section of the water jet cutting unit may be in any suitable orientation. Nevertheless, it is preferred that the surrounding wall section is substantially upright, with the inlet at the upper end and the outlet at the lower end. The upper end may be preferably connected directly with the bottom opening (3) of the polymerization unit by suitable means.
The passage of the aqueous polyacrylamide gel may be by gravity alone or may be fed into the water jet cutting unit under pressure, for instance, by pumping, mechanically feeding, by gas pressure or by the action of a vacuum. Preferably, the aqueous polyacrylamide gel is fed into the water jet cutting unit by means of gas or water pressure exerted on the contents of the polymerization unit P1 forming the aqueous polyacrylamide gel. Alternatively, or additionally, the aqueous polyacrylamide gel is fed into the water jet cutting unit by means of mechanical conveying devices, such as scrolls.
The at least one water-jet has a pressure of at least 150*105 Pa. The pressure may be considerably higher than this, for instance, up to 10,000*105 Pa. However, it is not normally necessary for the pressure to be as high as this and lower pressures, for instance no higher than 7,500*105 Pa are usually adequate. In one embodiment of the invention, the pressure of the water jet in the cutting unit has a pressure of from 150*105 Pa to 5,000*105 Pa, preferably from 200*105 Pa to 2,000*105 Pa, more preferably from 250*105 Pa to 1000*105 Pa.
Typically, the water jet would flow from a nozzle having a nozzle orifice of suitable diameter. By the term nozzle we mean a device which is designed to control the direction or the characteristics of a fluid flow, including to increase the velocity, as it exits. In general, the nozzle orifice diameter should be from 0.1 mm to 3.00 mm, for instance, from 0.25 mm to 2.00, or from 0.25 mm to 1.00 mm, suitably from 0.30 mm to 0.90 mm, desirably from 0.40 mm 0.80 mm. It may be desirable to employ a multiplicity of nozzles on a head in which each nozzle delivers a stream of aqueous liquid at the aforementioned pressures of at least 150″105 Pa. When a multiplicity of nozzles on a head is employed the number of nozzles may be at least 2, for instance, from 2 to 10 nozzles. The nozzles may be arranged in one plane or in different planes and angles. The nozzles may be arranged in such a way, for instance over a domed surface of the head, that the multiplicity of streams radiate out in different axises. Such a multiplicity of nozzles may be arranged such that the streams of aqueous liquid form an array each travelling in different directions.
The at least one nozzle may rotate or oscillate.
In one embodiment, the at least one nozzle oscillates. Such oscillation of the nozzle may produce a fan shaped water stream sweep pattern. In this embodiment of the invention, it may be of particular value to employ a multiplicity of nozzles which can oscillate. Typically, the number of nozzles may be from 2 to 8, preferably from 2 to 6. It may also be desirable that a multiplicity of nozzles are arranged on at least one head, each head containing from 2 to 10 nozzles. It may be desirable for the multiplicity of heads, for instance, from 2 to 10 heads, each head containing the multiplicity of nozzles, to be employed. In this case each of the heads may separately oscillate.
Such multiplicity of nozzles or multiplicity of heads each may be positioned circumferentially with respect to the aqueous polyacrylamide gel, such that the water streams extend inwardly. The multiplicity of nozzles and/or multiplicity of heads may be positioned evenly such that the distance between all adjacent nozzles is equal. Alternatively, they may not to be evenly spaced.
Thus, when the multiplicity of nozzles or multiplicity of heads are arranged circumferentially the aqueous polyacrylamide gel would then pass within the circumferentially positioned nozzles and be cut by the multiplicity of aqueous liquid streams. The at least one oscillating nozzle or head may be moved by a suitable actuator mechanism.
Each oscillating nozzle may have a sweep of up to 180°. Typically, the sweep may be 30° to 180°, for instance from 35° to 75°. The exact range of the sweep will often depend on the exact number of nozzles employed. The oscillation frequency should for instance be up to 50 s−1 (cycles per second), typically from 0.5 s−1 to 50 s−1.
When the at least one nozzle, for instance, multiplicity of nozzles, or at least one head, for instance multiplicity of heads, is/are arranged circumferentially with respect to the aqueous polyacrylamide gel, each of the at least one nozzles or at least one head may rotate circumferentially about the aqueous polyacrylamide gel. When the circumferentially arranged at least one nozzle or at least one head rotates it may be desirable that each nozzle or each head may independently oscillate as given above. Alternatively, it may be desirable that when the circumferentially arranged at least one nozzle or at least one head rotates they may not oscillate. The rotation of the at least one nozzle or at least one head may be achieved by a suitable drive mechanism.
In another preferred embodiment of the invention, the at least one nozzle rotates and the stream of aqueous liquid generated forms a circular sweep pattern. The at least one nozzle may be a multiplicity of nozzles housed on at least one head. Such at least one rotating nozzle may be rotated by the action of a suitable motorized drive mechanism.
It may be desirable to employ more than one rotating nozzle, for instance, a multiplicity of nozzles housed on at least one head. However, it is usually only necessary to employ one rotating nozzle or where more than one nozzle is employed the multiplicity of nozzles are arranged on one head.
In one embodiment of the invention, the at least one rotating nozzle, or at least one head is mounted centrally and the aqueous liquid stream extends substantially perpendicular to the axis of the direction of the incoming aqueous polyacrylamide gel. In this form the aqueous liquid stream sweep pattern is disc shaped. In an adaptation of this preferred aspect the rotating nozzle or head, which is/are mounted centrally, may generate at least one stream of liquid which is not perpendicular to the direction of the incoming aqueous polyacrylamide gel, but instead is angled such that the at least one aqueous liquid stream sweep pattern is a cone shaped, for instance, an upright cone where the at least one aqueous liquid stream is angled downwards, or an inverted cone where the at least one aqueous liquid stream is angled upwards. Where the at least one aqueous liquid stream is angled either upwards or downwards it is preferred that the angle is no more than 50° up or down from the position which is perpendicular to the direction of the incoming aqueous polyacrylamide gel. Preferably this angle should be from 5° to 45°, more preferably from 10° to 35°, particularly from 15° to 25°.
In a further embodiment of the invention, the at least one rotating nozzle or rotating head is not mounted centrally but off center. For instance, where the cutting stage is contained in a surrounding wall section the rotating nozzle may be located at or close to the wall of the surrounding wall section. Typically, the nozzle or head would be orientated such that it generates at least one eccentric aqueous stream sweep pattern.
The rotating nozzle or rotating head may rotate at a frequency of up to 3000 rpm (revolutions per minute (i.e. 50 s−1 cycles per second)). The rotational frequency may be selected by the skilled artisan. A higher rotational frequency, for example a rotational frequency from 500 rpm to 3000 rpm) may by trend tear the aqueous polyacrylamide gel into smaller parts while a smaller rotational frequency, for example from 10 rpm to less than 500 ppm, preferably 20 rpm to 200 rpm more properly cuts the aqueous polyacrylamide gel.
Desirably, the water-jet cutting unit will divide the aqueous polyacrylamide gel into numerous smaller sized pieces. The aqueous polyacrylamide gel pieces should conveniently have a size such that at least two dimensions are no more than 2 cm, preferably no more than 1 cm, more preferably no more than 0.5 cm. Preferably three dimensions of the aqueous polyacrylamide gel pieces should be no more than 2 cm, preferably no more than 1 cm, preferably no more than 0.5 cm. There is no lower limit necessary for the aqueous polyacrylamide gel pieces, since the smaller the pieces the easier it will be for the polymer to dissolve. In one embodiment, the aqueous polyacrylamide gel pieces have three dimensions each of from 0.1 to 1.5 cm.
The water-jet cutting unit may also comprise a sieve tray beneath the at least one stream of aqueous liquid. This is intended to prevent oversized aqueous polyacrylamide gel lumps from passing into the next stage. The sieve tray should have openings of a size corresponding to the maximum size of aqueous polyacrylamide gel pieces which should be allowed to pass to the next stage. Suitably the sieve tray may be a mesh formed by a plurality of inter-meshing wires or bars. Alternatively, the sieve tray may be formed as a surface with a plurality of holes cut therein, for instance, analogous to a colander. Typically, the sieve tray should be a static device. It should extend to cover the whole area below where the aqueous polyacrylamide gel cutting is taking place. Preferably, the sieve tray may be affixed to the surrounding wall section. In embodiments of the present invention additional streams of aqueous liquid are directed at the surface of the sieve tray in order to facilitate the size reduction of the oversized aqueous polyacrylamide gel lumps captured by the tray. It may be desirable to employ one or more aqueous liquid streams of high-pressure, for instance, of at least 150′105 Pa in order to facilitate the cutting of the oversized aqueous polyacrylamide gel lumps such that the aqueous polyacrylamide gel is cut into small enough pieces to pass through.
Desirably, a curtain of aqueous liquid is provided on the inside of the surrounding wall section. This curtain of aqueous liquid may help prevent aqueous polyacrylamide gel from sticking to the wall of the surrounding wall section and reduce friction of the moving polymer thereby reducing necessary static pressure or avoiding additional mechanical means to move the polymer towards the cutting area. Such curtain of aqueous liquid may be produced by providing a secondary aqueous liquid supply. Typically, the pressure of the aqueous liquid should be below 30 bar, for instance, from 3 bar to 20 bar, desirably from 5 bar to 10 bar. The water may be fed to a ring main, in the form of an annulus, and mounted on the inside of the surrounding wall section. In order to be most effective, the ring main or annulus should be mounted at or close to the top of the surrounding wall section to provide the maximum protection by the curtain of water. Desirably the aqueous liquid flows from the ring main or annulus down the inner surface of the wall of the surrounding wall section as a curtain.
Combinations
The described methods of comminuting the aqueous polyacrylamide gel may also combined with each other.
In one embodiment of the invention, the relocatable comminution unit comprises at least a water-jet cutting device and a static cutting member. The at least one static cutting member may for instance be one or more knives, blades, cutting wires or any combination thereof. In one form the at least one cutting member may consist of a multiplicity of knives or blades mounted on the wall of the tubular section circumferentially with the knives or blades extending inwardly. In another form the at least one cutting member may be knives or blades mounted from a central position with the knives or blades extending out radially. In a further form the at least one cutting member may be a mesh of knives, blades or cutting wires. Typically, the static cutting member, where employed, should extend over the whole cross-section of the surrounding wall section. Suitably, the aqueous polyacrylamide gel may be cut by contacting the at least one static cutting member before contacting the at least one stream of aqueous liquid.
In another embodiment, water-jet cutting may be combined with static mixing. For that purpose, the aqueous mixture comprising pieces of polyacrylamide gel leaving the water-jet cutting unit is conveyed through at least one static mixer. Additional aqueous liquid may be added to the mixture, before it enters into the at least one static mixer.
In another embodiment, water-jet cutting is combined with both, static cutting means and a static mixer. The combination with static cutting means has already been described above. Thereafter, the aqueous mixture comprising pieces of polyacrylamide gel leaving the comminution unit comprising a water-jet cutting step and a static cutting step is conveyed through at least one static mixer. Additional aqueous liquid may be added to the mixture, before it enters into the at least one static mixer.
In one embodiment, comminuting the aqueous polyacrylamide gel is carried out by at least one means selected from rotating water-jets, rotating knives or and a hole perforation plate. Preferably, a combination of at least one hole perforation plate and rotating water-jets or at least one hole perforation plate and rotating knives may be used.
In other embodiments, the comminution unit comprises a combination of water-jet cutting and a hole perforation plate. The hole perforation plate comprises holes. The shape of the holes is not specifically limited. Examples comprise circular holes, ellipsoidal holes, triangular holes, quadrangular holes such as quadratic, rectangular, or rhombic holes, pentagonal holes, hexagonal holes or star-like holes but also longitudinal holes such as slots. The holes may be cylindrical holes but they may also be conical.
The dimensions of the holes are not specifically limited. However, preferably at least one dimension of the holes should be from 0.5 to 5 mm. In one embodiment of the invention, the hole perforation plate comprises circular holes having a diameter from 0.5 to 5 mm, for example from 1 mm to 3 mm.
The aqueous polyacrylamide is conveyed from the polymerization unit through the hole perforation plate. One or more rotating nozzles for water-jets are mounted above or below the hole perforation plate.
One embodiment of such a combination is schematically shown in
Step [5] Dissolution
The dissolution of the aqueous polyacrylamide gel pieces generated in course of step [4] in an aqueous liquid is conducted in a relocatable dissolution unit. Basically, any kind of relocatable dissolution unit may be used.
Examples of suitable relocatable dissolution units comprise stirred vessels. A dissolution unit may only comprise one vessels or it may comprise more than one vessel which may be operated in series or in parallel. Mixing may also be achieved by flowing the contents of the dissolution vessel out through a conduit and then recirculating back into the mixing vessel. Other examples comprise relocatable dissolution units comprising a combination of static mixers with unstirred vessels or in-line dispersing such as rotor-stator units.
Unstirred vessels or unstirred vessels in combination with other equipment such as static mixers are in particular useful, when the desired concentration of the polyacrylamide solution is higher, for example when the aqueous polyacrylamide solution is a concentrate as indicated above, for example a concentrate having a concentration of 3.1% to 6% by weight. Dissolution may be performed by conveying the comminuted aqueous polyacrylamide gel through a static mixer or a plurality of static mixers together with sufficient aqueous liquid and thereafter the mixture is filled into an unstirred vessel and allowed to stand in order to finalize dissolution.
In one embodiment of the invention, the aqueous polyacrylamide gel pieces are dissolved in the aqueous liquid by passing the aqueous polyacrylamide gel pieces of step [4], preferably a mixture of aqueous polyacrylamide gel pieces in an aqueous liquid into a relocatable dissolution comprising at least a dissolution vessel and means for mixing the polyacrylamide gel with the aqueous liquid. Aqueous liquid is added to the dissolution vessel. The amount depends on the amount of aqueous liquid already added to the aqueous polyacrylamide gel in the preceding comminution step and the desired concentration of the final polyacrylamide solution.
Examples of means for mixing comprise one or more impellers or stirrers which optionally may be combined with static mixing devices. Mixing may also be achieved by flowing the contents of the dissolution vessel out through a conduit and then recirculating back into the mixing tank. The dissolution unit may also comprise two or more than two dissolution vessels connected in series. The volume of the dissolution vessel is not specifically limited and may range from 10 m3 to 150 m3, for example from 20 m3 to 50 m3 per vessel.
The aqueous polyacrylamide gel pieces, preferably a mixture of aqueous polyacrylamide gel pieces and aqueous liquid/aqueous polyacrylamide solution is filled into the dissolution vessel through an opening (44) and the polyacrylamide solution may be removed through the line (45).
In another embodiment, two or more dissolution units may be connected in series. In embodiments of the invention 2 to 15, for example 5 to 12 dissolution units may be connected in series. The aqueous polyacrylamide gel pieces, preferably the mixture of aqueous polyacrylamide pieces are filled in the first dissolution vessel and mixed with aqueous liquid. The mixture is continuously transported into at least a second dissolution unit for further dissolution. It may be transferred from there into a third dissolution unit. From the last dissolution unit aqueous polyacrylamide solution may be removed.
It is also possible, that not separate relocatable dissolution units are used but that two or more dissolution vessels may be connected in series in just one frame.
In another embodiment, at least two the relocatable dissolution units, preferably at least three relocatable dissolution may be connected in a cyclical manner, i.e. they are connected in series and the last one is connected again with the first one.
In another embodiment, a relocatable dissolution unit is a dissolution unit fixed on a truck.
In another embodiment, the aqueous polyacrylamide solution may be further diluted for application after carrying out step [5] in a second dilution step.
After carrying out step [5], the aqueous polyacrylamide solution may be directly transferred to the site where it is used, i.e. to an oil well for injection. In other embodiments the aqueous may be stored temporarily at location B before using it.
For such temporary storage, a storage vessel or a series of storage vessels may be used. Storing the solution in particular is advantageous to make the necessary analytics and the quality control.
For transporting the aqueous polyacrylamide solution obtained in course of step [5]-either directly from the dissolution unit or temporary storage vessels to the site-of-use several options exist depending on the location of the site-of-use.
In one embodiment, the transfer may simply be carried out by means of piping or any other suitable conduit.
For transporting the aqueous polyacrylamide solution to more distant sites-of-use, also pipelines may be used. In another embodiment, the aqueous solution is transported from the modular plant to the site-of-use using a suitable transport unit. Examples of suitable transport units comprise for instance road tankers or tank containers.
In one embodiment of the invention, step [5] is carried out in such a manner that a concentrate as defined above is obtained, i.e. an aqueous polyacrylamide solution having a concentration from 2.1 to 14.9% by weight, in particular from 2.1% to 7% by wt., for example from 3.1% to 6% by weight. Thereafter, such concentrate is transported to the site-of-use using a suitable transport unit, for instance a transport unit as described above. At the site-of-use, the concentrate is removed from the transport unit, for instance by pumping and either used directly or alternatively diluted with additional aqueous liquid thereby obtaining an aqueous polyacrylamide solution having a lower concentration, for example a concentration from 0.01% by weight to 2% by weight. Transporting a concentrate has the advantage of transporting less water compared to transporting a dilute solution which reduces transport cost. The concentrates as described above may still be viscos fluids or even solid but usually they are still pumpable, so that they can be easily removed from the transport units.
By the way of example, in such an embodiment, the modular plant may be located at a more central point of an oil field and serves a number of different oil wells with polyacrylamide concentrate. The distance between the modular plant and the sites-of-use may for example be from 1 to 500 km or from 10 km to 300 km.
Modification of the Polyacrylamides
In one embodiment of the invention, the polyacrylamides may simultaneously by modified in course of steps [4] and [5].
For that purpose, suitable agents for modifying the polymers may be added to the aqueous liquid used for dissolving the aqueous polyacrylamide gel. In other embodiments, such agents may be added separately, preferably as aqueous solution.
In one embodiment of the invention, the polyacrylamides may be partially hydrolyzed thereby obtaining polyacrylamides comprising also —COOH groups or salts thereof. In certain embodiments, about 30 mol % of the amide groups may be hydrolyzed to carboxylic groups. Partially hydrolyzed polyacrylamides are known in the art. For that purpose, bases such as NaOH are added to the aqueous liquid.
In another embodiment, hydroxylamine and a base may be added to the aqueous liquid thereby obtaining polyacrylamides in which a part of the amide groups are converted to hydroxamic acid groups.
Measurement and Control
In one embodiment, the modular, relocatable plant comprises a central process measuring and control technology unit. Preferably, the process measuring and control technology unit is connected with all units of the modular, relocatable plant, thereby enabling a central process control similar to fixed plants. In one embodiment, all connections with measuring and control instruments of a certain unit, e.g. the dissolution unit, the monomer storage units or the polymerization units are bundled in one cable, for example BUS technology, so that they may be easily plugged together. Of course, also other connecting technologies are possible, for example radio links.
Modular, Relocatable Plant
In a further embodiment, the present invention relates to a modular, relocatable plant for manufacturing aqueous polyacrylamide solutions by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in an aqueous liquid, comprising at least
Details of the individual units of the plant, including preferred embodiments, have already been described above and we refer to the respective passages.
In one preferred embodiment, the relocatable comminution unit comprises at least means selected from rotating water-jets, rotation knives and hole perforation plates.
In another preferred embodiment, the modular, relocatable plant comprises relocatable storage units for water-soluble, monoethylenically unsaturated monomers different from acrylamide.
In a preferred embodiment, acrylamide is also manufactured in the modular, relocatable plant by hydrolyzing acrylonitrile in water in the presence of a biocatalyst capable of converting acrylonitrile to acrylamide.
The present invention therefore furthermore relates to a modular, relocatable plant for manufacturing aqueous polyacrylamide solutions by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water, comprising at least
Details of the individual units of the plant have already been described above and we refer to the respective passages. As outlined above, the comminution unit may be a separate, relocatable comminution unit or it may be fixed to the polymerization unit.
Use of the Aqueous Polyacrylamide Solutions
The aqueous polyacrylamide solutions manufactured according to the present invention may be used for various purposes, for example for mining applications, oilfield applications, water treatment, waste water cleanup, paper making or agricultural applications.
For the application, the aqueous polyacrylamide solutions may be used as such or they may be formulated with further components. The specific composition of aqueous polyacrylamide solutions is selected by the skilled artisan according to the intended use of the polyacrylamide solution.
Oilfield Applications
Examples of oilfield applications in which the aqueous polyacrylamide solutions manufactured according to the present invention may be used include enhanced oil recovery, oil well drilling or the use as friction reducers, for example friction reducers for fracturing fluids.
Enhanced Oil Recovery
In one embodiment of the invention, the aqueous polyacrylamide solutions manufactured according to the present invention are used for enhanced oil recovery.
Accordingly, the present invention also relates a method for producing mineral oil from underground mineral oil deposits by injecting an aqueous fluid comprising at least an aqueous polyacrylamide solution into a mineral oil deposit through at least one injection well and withdrawing crude oil from the deposit through at least one production well, wherein the aqueous polyacrylamide solution is prepared by the process for producing an aqueous polyacrylamide solution as described above. Details of the process have already been disclosed above.
For the method of enhanced oil recovery, at least one production well and at least one injection well are sunk into the mineral oil deposit. In general, a deposit will be provided with a plurality of injection wells and with a plurality of production wells. An aqueous fluid is injected into the mineral oil deposit through the at least one injection well, and mineral oil is withdrawn from the deposit through at least one production well. By virtue of the pressure generated by the aqueous fluid injected, called the “polymer flood”, the mineral oil flows in the direction of the production well and is produced through the production well. In this context, the term “mineral oil” does not of course just mean a single-phase oil; instead, the term also encompasses the customary crude oil-water emulsions.
The aqueous fluid for injection comprises the aqueous poly acrylamide solution prepared by process according to the present invention. Details of the process have been disclosed above.
In one embodiment, the modular plant according to the present invention may be at an injection well to be treated with aqueous polyacrylamide solutions or close to such an injection well. In another embodiment, the modular plant may be in between a plurality of such injection wells or at one of them and the aqueous polyacrylamide solution is distributed from there to all injection wells, for example by means of pipelines.
The aqueous acrylamide solution obtained may be used as such or it may be mixed with further components. Further components for enhanced oil recovery fluids may be selected by the skilled artisan according to his/her needs.
For enhanced oil recovery, a homopolymer of acrylamide may be used, however preferably water-soluble copolymers comprising at least 10%, preferably at least 20%, and more preferably at least 30% by weight of acrylamide and at least one additional water-soluble, monoethylenically unsaturated monomer different from acrylamide are used. Suitable water-soluble comonomers have already been mentioned above and we refer to the disclosure above.
In one embodiment, water-soluble comonomers may be selected from water-soluble, monoethylenically unsaturated monomers comprising at least one acid group, or salts thereof. The acidic groups are preferably selected from the group of —COOH, —SO3H and —PO3H2 or salts thereof. Preference is given to monomers comprising COOH groups and/or —SO3H groups or salts thereof. Suitable counterions have already been mentioned above. Examples of such comonomers comprise acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid, vinylsulfonic acid, allylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid (ATBS), 2-methacrylamido-2-methylpropane-sulfonic acid, 2-acrylamidobutanesulfonic acid, 3-acrylamido-3-methylbutane-sulfonic acid, 2-acrylamido-2,4,4-trimethylpentanesulfonic acid, vinylphosphonic acid, allylphosphonic acid, N-(meth)acrylamidoalkylphosphonic acids and (meth)acryloyloxyalkyl-phosphonic acids.
In a preferred embodiment, acrylic acid and/or ATBS or salts thereof may be used as comonomers.
In such copolymers, the amount of acrylamide usually is from 20% by wt. to 90% by wt. and the amount of acrylic acid and/or ATBS or salts thereof is from 10% by wt. to 80% by wt., relating to the amount of all monomers in the copolymer. Preferably, the amount of acrylamide is from 60% by wt. to 80% by wt. and the amount acrylic acid and/or ATBS or salts thereof is from 20% by wt. to 40% by wt.
In another embodiment, the copolymers to be used for enhanced oil recovery comprise at least one water-soluble, monoethylenically unsaturated monomer comprising at least one acid group, or salts thereof, preferably acrylic acid and/or ATBS or salts thereof, and at least one associative monomer. Examples of associative monomers have already been disclosed above. In one embodiment, at least one associative monomer of the general formula (III), (IV), or (V) is used, preferably at least one associative monomer of the general formula (V). Preferred embodiments of the associative monomers (III), (IV), and (V) have already been disclosed above and it is explicitly referred to that description.
In such polyacrylamides, the amount of acrylamide usually is from 40% by wt. to 89.9% by wt., the amount of acrylic acid and/or ATBS or salts thereof is from 10% by wt. to 59.9%, and the amount of associative monomers is from 0.1 to 5% by wt., relating to the amount of all monomers in the copolymer.
In one embodiment, the polyacrylamides for EOR comprise 45% to 55% by weight of acrylamide, 0.1 to 5%, preferably 0.1 to 2% by weight of at least one associative monomer of the general formula (V) mentioned above, including the preferred embodiments, and 40 to 54.9% by weight of acrylic acid or salts thereof.
The aqueous fluid for injection can be made up in freshwater or else in water comprising salts, such as seawater or formation water. As already outlined above, water comprising salts may already be used for dissolving the aqueous polyacrylamide gel. Alternatively, the polyacrylamide gel may be dissolved in fresh water, and the solution obtained can be diluted to the desired use concentration with water comprising salts.
The aqueous injection fluid may of course optionally comprise further components. Examples of further components include biocides, stabilizers, free-radical scavengers, initiators, surfactants, cosolvents, bases and complexing agents.
The concentration of the copolymer in the injection fluid is fixed such that the aqueous formulation has the desired viscosity for the end use. The viscosity of the formulation should generally be at least 5 mPas (measured at 25° C. and a shear rate of 7 s−1), preferably at least 10 mPas.
In general, the concentration of the polyacrylamide in the injection fluid is 0.02 to 2% by weight based on the sum total of all the components in the aqueous formulation. The amount is preferably 0.05 to 0.5% by weight, more preferably 0.1 to 0.3% by weight and, for example, 0.1 to 0.2% by weight.
Friction Reducers for Hydraulic Fracturing
In another embodiment of the invention, the aqueous polyacrylamide solutions manufactured according to the present invention are used as friction reducers in hydraulic fracturing applications.
Hydraulic fracturing involves injecting fracturing fluid through a wellbore and into a formation under sufficiently high pressure to create fractures, thereby providing channels through which formation fluids such as oil, gas or water, can flow into the wellbore and thereafter be withdrawn. Fracturing fluids are designed to enable the initiation or extension of fractures and the simultaneous transport of suspended proppant (for example, naturally-occurring sand grains, resin-coated sand, sintered bauxite, glass beads, ultra-lightweight polymer beads and the like) into the fracture to keep the fracture open when the pressure is released.
In one embodiment of hydraulic fracturing, fracturing fluids having a high viscosity are used. Such a high viscosity may be achieved by crosslinked polymers, such as crosslinked guar. Such a high viscosity is necessary to ensure that the proppants remain distributed in the fracking fluid and don't sediment, for example already in the wellbore.
In another embodiment of hydraulic fracturing, also known as “slickwater fracturing”, fluids having only a low viscosity are used. Such fluids mainly comprise water. In order to achieve proppant transport into the formation, the pumping rates and the pressures used are significantly higher than for high-viscosity fluids, thereby causing turbulent flow. The turbulent flow of the fracking fluid causes significant energy loss due to friction. In order to avoid or at least minimize such friction losses, high molecular weight polyacrylamides may be used which change turbulent flow to laminar flow.
Accordingly, in another embodiment the present invention relates to a method of fracturing subterranean formations by injecting an aqueous fracturing fluid comprising at least an aqueous base fluid, preferably water, proppants and a friction reducer through a wellbore into a subterranean formation at a pressure sufficient to flow into the formation and to initiate or extend fractures in the formation, wherein the friction reducer comprises an aqueous polyacrylamide solution prepared by the process for producing an aqueous polyacrylamide solution in a modular plant as described above. Details of the manufacturing process have already been disclosed above. Examples of aqueous base fluids comprise fresh water, brines, sea water, formation water treated water or mixtures thereof.
In a preferred embodiment of the present invention, the aqueous polyacrylamide solution has a concentration from 2.1 to 14.9% by weight, preferably from 2.1 to 10% by weight, in particular from 2.1% to 7% by wt., and for example from 3.1% to 6% by weight. The concentrate may be preferably used as such, i.e. without further dilution on-site. For example, it may be feeded into the blenders which are typically used for mixing fracturing fluids. The transport of the concentrate may preferably be carried out by filling the concentrate into a suitable transport unit, transporting the transport unit to the site-of-use and removing the concentrate form the transport unit, for example by pumping. The transport unit may have a volume from 1 m3 to 40 m3, in particular 5 m3 to 40 m3, for example 20 m3 to 30 m3. Examples of suitable transport units comprise vessels comprising at least one opening or tank containers.
Mining Applications
In one embodiment, the method for preparing an aqueous polyacrylamide solution according to the present invention is carried out in areas where mining, mineral processing and/or metallurgy activities takes place. Consequently, the aqueous polyacrylamide solution as product obtained by the method of the present invention is preferably used for applications in the field of mining, mineral processing and/or metallurgy and the method for preparing the aqueous polyacrylamide solution is preferably used at the plant of the respective industry.
Preferably, mining activities comprises extraction of valuable minerals or other geological materials from certain deposits. Such deposits can contain ores, for example metal containing ores, sulfidic ores and/or non-sulfidic ores. The ores may comprise metals, coal, gemstones, limestone or other mineral material. Mining is generally required to obtain any material in particular mineral material that cannot be grown through agricultural processes, or created artificially in a laboratory or factory. The aqueous polyacrylamide solution according to the present invention is preferably used to facilitate the recovery of mineral material, for beneficiation of ores and for further processing of ores to obtain the desired minerals or metals.
Typically, mining industries, mineral processing industries and/or metallurgy industries are active in the processing of ores and in the production of for example alumina, coal, iron, steel, base metals, precious metals, diamonds, non-metallic minerals and/or areas where aggregates play an important role. In such industries, the method of the present invention and the obtained homo- or copolymer of acrylamide can be used for example
Accordingly, the present invention relates to the use of an aqueous polyacrylamide solution for mining, mineral processing and/or metallurgy activities comprising the use for solid liquid separation, for tailings disposal, for polymer modified tailings deposition, for tailings management, as density and/or rheology modifier, as agglomeration aid, as binder and/or for material handling, wherein the aqueous polyacrylamide solution is prepared at the plant of the respective industry, comprising for example the following steps:
hydrolyzing acrylonitrile in water in presence of a biocatalyst capable of converting acrylonitrile to acrylamide so as to obtain an acrylamide solution,
For the mining, mineral processing and/or metallurgy activities a homopolymer of acrylamide for example can be used. Further preferred are also copolymers of acrylamide. Such copolymers of acrylamide can be anionic, cationic or non-ionic. Anionic copolymers are for example co-polymers of acrylamide with increasing proportions of acrylate groups, which give the polymers negative charges, and thus anionic active character, in aqueous solution. Anionic copolymers of acrylamide can in particular be used for waste water treatment in metallurgy like iron ore plants, steel plants, plants for electroplating, for coal washing or as flocculants. Non-ionic polymers and/or copolymers of acrylamide can be used for example as nonionic flocculants suitable as settlement aids in many different mineral processing applications and are particularly effective under very low pH conditions, as encountered for example in acidic leach operations. Cationic copolymers of acrylamide have in particular an increasing proportion of cationic monomers. The cationic groups, which are thus introduced into the polymer, have positive charges in aqueous solution.
It is preferred, that the polymer obtained from the method of the present invention is used as flocculant in a process in which individual particles of a suspension form aggregates. The polymeric materials of the present invention forms for example bridges between individual particles in the way that segments of the polymer chain adsorb on different particles and help particles to aggregate. Consequently, the polymers of the present invention act as agglomeration aid, which may be a flocculant that carries active groups with a charge and which may counterbalance the charge of the individual particles of a suspension. The polymeric flocculant may also adsorb on particles and may cause destabilization either by bridging or by charge neutralization. In case the polymer is an anionic flocculant, it may react against a positively charged suspension (positive zeta potential) in presence of salts and metallic hydroxides as suspension particles, for example. In case the polymer of the present invention is for example a cationic flocculant, it may react against a negatively charged suspension (negative zeta potential) like in presence of for example silica or organic substances as suspension particles. For example, the polymer obtained from the method of the present invention may be an anionic flocculant that agglomerates clays which are electronegative.
Preferably, the method of the present invention and the obtained polymer and/or copolymer of acrylamide (polyacrylamide) is used for example in the Bayer process for alumina production. In particular, the polyacrylamide can be used as flocculant in the first step of the Bayer-Process, where the aluminum ore (bauxite) is washed with NaOH and soluble sodium aluminate as well as red mud is obtained. Advantageously, the flocculation of red mud is enhanced and a faster settling rate is achieved when acrylamide polymers and/or co-polymers are added. As red mud setting flocculants, polyacrylamide may be used for settling aluminum red mud slurries in alumina plants, provides high settling rates, offers better separation performance and reduces suspended solids significantly. Also the liquor filtration operations are improved and with that the processing is made economically more efficient. It is further preferred that the polyacrylamides are used in decanters, in washers, for hydrate thickening, for green liquor filtration, as crystal growth modifiers, as thickener and/or as rheology modifier.
It is further preferred that the method of the present invention and the polymers of acrylamide are used in processes for solid liquid separation as for example flocculant or dewatering aid, which facilitate thickening, clarifying, filtration and centrifugation in order to enhance settling rates, to improve clarities and to reduce underflow volumes. In particular, in filtration processes the polyacrylamide homo- or co-polymer of the present invention increase filtration rates and yields, as well as reducing cake moisture contents.
Further preferred is the use of the method and the obtained polyacrylamide of the present invention in particular for material handling and as binder. In the mining industry, the movement of large volumes of material is required for processing the rock and/or ores which have been extracted from the deposits. The typical rock and/or ore processing for example starts with ore extraction, followed by crushing and grinding the ore, subsequent mineral processing (processing or the desired/valuable mineral material), then for example metal production and finally the disposal of waste material or tailings. It was a surprise that with the method of the present invention and in particular the obtained polyacrylamide the handling of the mineral material can be enhanced by increasing efficiency and yield, by improving product quality and by minimizing operating costs. Particularly, the present invention can be used for a safer working environment at the mine site and for reduction of environmental discharges. Preferably, the method and the obtained polyacrylamide of the present invention can for example be used as thickener, as density and/or rheology modifier, for tailings management. The obtained polyacrylamide polymer can modify the behavior of the tailings for example by rheological adjustment. The obtained polyacrylamide polymers are able to rigidify tailings at the point of disposal by initiating instantaneous water release from the treated slurry. This accelerates the drying time of the tailings, results in a smaller tailings footprint and allows the released water to be returned to the process faster. This treatment is effective in improving tailings properties in industries producing alumina, nickel, gold, iron ore, mineral sands, oil sands or copper for example. Further benefits of the polymers obtained according to the present invention are for example maximized life of disposal area, slurry placement control, no re-working of deposit required, co-disposal of coarse and fine material, faster trafficable surface, reduced evaporative losses, increased volume for recycling, removed fines contamination, reduced fresh water requirement, lower land management cost, less mobile equipment, lower rehabilitation costs, quicker rehabilitation time, lower energy consumption, accelerated and increased overall water release, improved rate of consolidation, reduced rate of rise, reduced amount of post depositional settlement.
Preferably, the obtained product from the method of the present invention is used for agglomeration of fine particulate matter and for the suppression of dust. Particularly, polyacrylamide polymers or copolymers are used as organic binders to agglomerate a wide variety of mineral substrates. For example, the polyacrylamide polymers or copolymers are used for iron ore pelletization as a full or partial replacement for bentonite. The product from the method of the present invention can be used as binder, in particular as solid and liquid organic binders in briquetting, extrusion, pelletization, spheronization and/or granulation applications and gives for example excellent lubrication, molding and/or binding properties for processes such as coal-fines briquetting, carbon extrusion, graphite extrusion and/or nickel briquetting.
It is preferred that the method of the present invention and in particular the aqueous polyacrylamide solution obtained by the method is used for the beneficiation of ores which comprise for example coal, copper, alumina, gold, silver, lead, zinc, phosphate, potassium, nickel, iron, manganese, or other minerals.
Advantages of the Process According to the Invention
The process according to the present invention provides significant advantages as compared to known processes for the manufacture of polyacrylamide powders as well as compared to known processes for manufacturing polyacrylamide solutions on-site.
As already outlined above, drying aqueous polyacrylamide gel thereby obtaining polyacrylamide powders, transporting the powders to the site of use and re-dissolving the dry powders at the site of use is energy extensive and consequently the operational costs for drying are high. Furthermore, also the capital expenditure for the entire post-processing equipment including size reduction, drying, sieving, grinding is significant in relation to the total capital expenditure for the entire plant.
As compared to the known processes of manufacturing aqueous polyacrylamide solutions on-site by polymerizing aqueous acrylamide solutions and dissolving the gels obtained the process according to the present invention has the advantage that is easy to move the entire plant when polyacrylamide solutions are no longer needed at a location, i.e. at an oil well, but at another location, i.e. another oil well.
| Number | Date | Country | Kind |
|---|---|---|---|
| PCT/EP2017/077246 | Oct 2017 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2018/078498 | 10/18/2018 | WO | 00 |