Claims
- 1. A process for the preparation of a cast thermoplastic film having a mirrorlike surface for use in the manufacture of reflective signs comprising the steps of:
- (a) applying an aqueous coating composition to at least one surface of a paper substrate, said aqueous coating composition comprising an adhesion primer dispersed in water,
- (b) drying said coated substrate,
- (c) applying a molten film of at least 0.5 mils of a low density polyethylene over said coated surface, said molten film of low density polyethylene having an extrusion melt temperature of from about 425.degree. F. to about 575.degree. F., said low density polyethylene having a density of about 0.917 grams per cubic centimeter to about 0.930 grams per cubic centimeter,
- (d) adhering said low density polyethylene film to said coated surface,
- (e) cooling said low density polyethylene film to a temperature below the melt point of said low density polyethylene to form a release paper having a low density polyethylene surface,
- (f) applying a solution comprising an organic solvent and a thermoplastic resin soluble in said organic solvent to said release paper on said low density polyethylene surface,
- (g) drying said solution to remove said organic solvent and form a thermoplastic resin film on said release paper,
- (h) baking said dried thermoplastic resin film on said release paper to remove traces of said solvent, and thereafter,
- (i) stripping said baked thermoplastic resin film from said release paper,
- whereby a thermoplastic film having a mirrorlike surface is obtained.
- 2. The process of claim 1 wherein said adhesion primer is selected from the group consisting of aluminum oxide particles, colloidal silicas, hydrolyzed organic titanates, polyethylenimines, polyamides and urea-formaldehyde resins.
- 3. The process of claim 1 wherein said low density polyethylene film has a thickness of from about 0.5 mils to about 4 mils.
- 4. The process of claim 1 wherein said molten film of low density polyethylene has an extrusion melt temperature of from about 525.degree. F. to about 550.degree. F.
- 5. The process of claim 1 wherein said low density polyethylene contains from about 1% to about 7% by weight of aluminum metal pigment based on the total weight of said low density polyethylene film.
- 6. The process of claim 1 wherein said baking is accomplished at a temperature of at least 280.degree. F.
- 7. A process for the preparation of a cast thermoplastic film having a mirrorlike surface for use in the manufacture of reflective signs comprising the steps of:
- (a) applying an aqueous coating composition to at least one surface of a paper substrate, said coating composition comprising aluminum oxide particles dispersed in water, said aluminum oxide particles having a particle size of from about 1 millimicron to about 60 millimicrons, said aluminum oxide particles being applied to said surface at a coat weight of from about 0.25 grams per square meter to about 0.60 grams per square meter,
- (b) drying said coated substrate, and calendering said surface of said dried coated substrate to a Sheffield smoothness of from about 60 to about 90,
- (c) treating said coated, calendered surface of said dried substrate with a corona discharge,
- (d) applying a molten film of at least 0.5 mils of a low density polyethylene over said treated coated surface, said molten film of low density polyethylene having a melt temperature from about 525.degree. F. to about 550.degree. F., said low density polyethylene having a density of from about 0.917 grams per cubic centimeter to about 0.930 grams per cubic centimeter, said low density polyethylene containing from about 1% to about 7% by weight of aluminum metal pigment based on the total weight of said low density polyethylene film,
- (e) adhering said low density polyethylene film to said coated surface,
- (f) cooling said low density polyethylene film to a temperature below the melt point of said low density polyethylene to form a release paper having a low density polyethylene surface,
- (g) applying a solution comprising an organic solvent and a thermoplastic resin soluble in said organic solvent to said release paper on said low density polyethylene surface,
- (h) drying said solution to remove said organic solvent and form a thermoplastic resin film on said release paper,
- (i) baking said dried thermoplastic resin film on said release paper to remove traces of said solvent, and thereafter,
- (j) stripping said baked thermoplastic resin film from said release paper, whereby a thermoplastic film having a mirrorlike surface is obtained.
- 8. The process of claim 7 wherein said thermoplastic resin is polyvinylbutyral.
Parent Case Info
This is a continuation of application Ser. No. 742,097, filed Nov. 16, 1976, now abandoned.
US Referenced Citations (13)
Continuations (1)
|
Number |
Date |
Country |
Parent |
742097 |
Nov 1976 |
|