Claims
- 1. A process for producing a high-strength heat-resistant pipe, the process comprising the steps of:normalizing a steel at a temperature in the range of 1100 to 1250° C., the steel comprising C in an amount of 0.06 to 0.15% by weight, Si in an amount of 1.5% by weight or less, Mn in an amount of 0.5 to 1.5% by weight, V in an amount of 0.05 to 0.3% by weight, and at least one of Nb, Ti, Ta, Hf, and Zr, in an amount of 0.01 to 0.1% by weight, the balance being Fe and unavoidable impurities, piercing the steel to produce a pierced product, and cooling the pierced product to room temperature or to a temperature lower than the temperature at which transformation to bainite is completed, wherein after the cooling the pierced product has microstructure consisting of bainite and at least one carbide of V, Nb, Ti, Ta, Hf or Zr.
- 2. A process for producing a high-strength heat-resistant pipe, the process comprising the steps of:preparing an ingot comprising C in an amount of 0.06 to 0.15% by weight, Si in an amount of 1.5% by weight or less, Mn in an amount of 0.5 to 1.5% by weight, V in an amount of 0.05 to 0.3% by weight, and at least one of Nb, Ti, Ta, Hf, and Zr, in an amount of 0.01 to 0.1% by weight, the balance being Fe and unavoidable impurities, piercing the ingot, during a process of cooling the ingot, at a temperature within the range in which austenite recrystallizes, so as to produce a pierced product, and cooling the pierced product to room temperature or to a temperature lower than the temperature at which transformation to bainite is completed, wherein after the cooling the pierced product has microstructure consisting of bainite and at least one carbide of V, Nb, Ti, Ta, Hf or Zr.
- 3. A process for producing a high-strength heat-resistant pipe according to claim 1, wherein, after the step of cooling to produce a cooled product, the process further comprises the step of tempering the cooled product at the A1 point or a lower temperature.
- 4. A process for producing a high-strength heat-resistant pipe according to claim 2, wherein, after the step of cooling to produce a cooled product, the process further comprises the step of tempering the cooled product at the A1 point or a lower temperature.
- 5. The process according to claim 1, wherein the steel comprises Gin an amount of 0.06 to 0.14% by weight.
- 6. The process according to claim 2, wherein the ingot comprises C in an amount of 0.06 to 0.14% by weight.
- 7. The process according to claim 1, wherein the steel comprises C in an amount of 0.06 to 0.12% by weight.
- 8. The process according to claim 2, wherein the ingot comprises C in an amount of 0.06 to 0.12% by weight.
- 9. The process according to claim 5, further comprising welding the pierced product.
- 10. The process according to claim 6, further comprising welding the pierced product.
Priority Claims (1)
Number |
Date |
Country |
Kind |
10-272202 |
Sep 1998 |
JP |
|
Parent Case Info
This application is a Division of application Ser. No. 09/397,518 Filed on Sep. 17, 1999, now U.S. Pat. No. 6,299,705 issued Oct. 9, 2001.
Foreign Referenced Citations (2)
Number |
Date |
Country |
363096215 |
Apr 1988 |
JP |
407197125 |
Aug 1995 |
JP |