The present invention relates to a process for producing microfibrillated cellulose by treating cellulosic fibres.
Cellulosic fibres are multi-component structures made from cellulose polymers, i.e. cellulose chains. Lignin, pentosans and other components known in art may also be present. The cellulose chains in the fibres are attached to each other to form elementary fibrils. Several elementary fibrils are bound to each other to form microfibrils and several microfibrils form aggregates. The links between the cellulose chains, elementary- and microfibrils are hydrogen bonds.
Microfibrillated cellulose (MFC) (also known as nanocellulose) is a material made from wood cellulose fibres, where the individual microfibrils have been partly or totally detached from each other. MFC is normally very thin (˜20 nm) and the length is often between 100 nm to 1 μm.
MFC can be produced in a number of different ways. It is possible to mechanically treat cellulosic fibres so that microfibrils are formed. However, it is very energy consuming method to, for example, shred or refine the fibres and it is therefore not often used.
The production of nanocellulose or microfibrillated cellulose with bacteria is another option. In contrast to the above, this is a bio-synthetic process starting from another raw material than wood fibres. However, it is a very expensive process and time consuming.
It is also possible to produce microfibrils from cellulose by the aid of different chemicals which will break or dissolve the fibres. However, it is difficult to control the length of the formed fibrils and the fibrils are often too short.
One example of production of MFC is described in WO2007091942. In the method described in WO20070912942, the MFC is produced by the aid of refining in combination with addition of an enzyme.
One common problem with the techniques according to prior art is that the process conditions are not favourable for scale-up or large industrial applications requiring high quantities.
Thus, there is a need for an improved process for the production of microfibrillated cellulose.
It is an object of the present invention to provide a process for production of microfibrillated cellulose in an improved and energy efficient way.
Another object of the present invention is to produce microfibrillated cellulose with high consistency.
These objects and other advantages are achieved by the process according to claim 1. By alternating enzymatic treatments with mechanical treatments as described in claim 1 it is possible to produce microfibrillated cellulose (MFC) in a very energy efficient way. Furthermore, it is possible to increase the consistency of the produced MFC which provides clear benefits in terms of handling, dosing, drying or delivering the MFC to another user. This is achieved by the independent claim and preferred embodiments of the process are defined in the dependent claims.
The invention relates to a process for treating cellulosic fibres which process comprises pre-treatment of the fibres with an enzyme in a first enzymatic treatment followed by mechanical pre-treatment of the fibres in a first mechanical treatment. Thereafter, the fibres are treated with an enzyme in a second enzymatic treatment followed by a final mechanical treatment of the fibres in a second mechanical treatment to form microfibrillated cellulose. In this way it is possible to produce MFC in an improved and energy efficient way.
The activity of the enzyme during the first enzymatic treatment can be between 0,01-250 nkat/g, however the activity of the first enzymatic treatment is preferably low, preferably between 0,05-50 nkat/g and the activity of the enzyme during the second enzymatic treatment is preferably higher, preferably between 50-300 nkat/g.
The first mechanical treatment and the second mechanical treatment are preferably done by shredding or refining of the fibres. The first mechanical treatment opens the fibre structure before the following treatment with the enzyme. In this way the second enzymatic treatment will be more effective and selective which also will improve the second mechanical treatment and thus also the production of MFC.
The fibres are preferably mechanically treated at a consistency of between 2-40% by total weight. The fibres are preferably mechanically pre-treated in the first mechanical treatment at a high consistency of between 15-40% by total weight. It has been shown that mechanical pre-treatment of the fibres at high consistency reduces the amounts of fines. The fibres are thereafter preferably mechanically treated in the second mechanical treatment at a consistency of between 15-40% by total weight.
The pH during the first and/or second mechanical treatment is preferably above 9. The increase of pH during the mechanical treatment has been shown to decrease the energy needed.
The enzyme used during the first and/or the second enzymatic treatments is preferably affecting hemicellulose, such as xylanase or mannanase or an enzyme affecting cellulose, such as cellulase. The enzyme used in the process will decompose the cellulosic fibres and increase the accessibility and activity of the fibres and thus also the production of microfibrillated cellulose.
The cellulosic fibres are preferably fibres of kraft pulp.
The invention relates to a process for producing microfibrillated cellulose in an improved and energy efficient way. Furthermore, it is possible to produce MFC with a high consistency.
It has been shown that the combination of a first enzymatic treatment followed by a first mechanical treatment and a second enzymatic treatment activates and opens up the fibre structure in an improved way. Moreover, it has been shown that a second mechanical treatment of the treated fibres can be done in order to produce microfibrillated cellulose. By this process it is possible to produce MFC in a controlled and cost efficient way and also to produce MFC with a high consistency.
It has been shown that a first enzymatic treatment of cellulosic fibres followed by a first mechanical treatment, preferably at a high consistency, can increase the cutting of the fibres but while the production of fines is kept low. It is preferred to keep the amount of fines at a minimum after the first mechanical treatment, since enzymes which will be added in the second enzymatic treatment first decomposes fines before they decompose the fibres. Consequently, a low amount of fines increases the efficiency of the second enzymatic treatment.
The first enzymatic treatment as well as the second enzymatic treatment are done in order for the enzymes to decompose the cellulosic fibres and improve the production of MFC. The enzyme will decompose the primary layer of the fibres and thus increase the accessibility of the fibres and is then able to penetrate the fibre structure and get in between the fibrils. By the enzymatic treatments it is possible to reduce the extension of the mechanical treatments. A mechanical treatment of cellulosic fibres might strongly reduce the strength of the fibres and it is therefore advantageous to decrease the extent of such treatment as much as possible. By treating the fibres with enzymes before both mechanical treatments it is possible to avoid any unnecessary decrease in the strength of the fibres since the duration of the mechanical treatments can be decreased and the mechanical treatments can be done in a more gentle way.
The enzyme used in the first and second treatment can be any wood degrading enzymes which decompose cellulosic fibres. Cellulase is preferably used but other enzymes, for example enzymes which break down hemicellulose, such as xylanase and mannanase, may also be used. The same or different enzyme can be used in the two enzymatic treatments. The enzyme is often an enzymatic preparation which can contain small parts of other enzymatic activities than the main enzyme of the preparation.
Enzyme is added to the fibres which are in the form of a slurry which has a concentration of approximately 4-5%. The enzyme is added during stirring either in the beginning of the first and/or second treatment or during the entire reaction time.
The temperature used for the treatments with the enzyme may be between 30-85° C. However, the temperature depends on the enzyme used and the optimal working temperature for that specific enzyme as well as other parameters of the treatment, such as time and pH. If cellulase is used, the temperature during the treatment may be approximately 50° C.
The first and second enzymatic treatments may each last for 30 minutes-5 hours. The time needed depends on the cellulosic fibres which are treated and on the activity of the enzyme as well as the temperature of the treatment.
The enzymatic treatments can be terminated by either rising the temperature or the pH in order to denaturate the enzymes. The pH during the treatment with the enzyme is preferably between 4-6.
The activity of the enzyme during the first treatment can be between 0,01-250 nkat/g, preferably between 0,05-50 nkat/g. The target with the first enzymatic treatment is only to weaken or decompose the top surface of the fibres. Consequently, the activity of the enzyme is preferably low so that the fibres are not decomposed too much. The activity of the enzyme during the second enzymatic treatment is preferably between 50-300 nkat/g. The second enzymatic treatment is done in order to decompose the primary layer of the fibres as previously discussed, i.e. not only the top surface. Consequently, the activity of the enzyme during the second enzymatic treatment needs to be higher than during the first enzymatic treatment.
After the first enzymatic treatment, the cellulosic fibres are mechanically pre-treated in a first mechanical treatment. The fibres are preferably shredded or refined in order to increase the specific surface area of the fibres and in this way facilitate and improve the effect of the second enzymatic treatment. The shredding or refining may be done at a consistency between 2-40% by total weight. However, high consistency, preferably between 15-40%, or between 10-20% by total weight is often preferred. Low consistency, for example 2-6% by total weight or medium consistency, for example 10-20% of total weight can also be used.
The fines after the first mechanical treatment may be separated for example by fractionating the treated fibres, and the longer fibres can thus be further treated in the second enzymatic and mechanical treatments.
The first mechanical treatment is preferably done at a consistency of between 15-40% by total weight. It has been shown that treating cellulosic fibres with a first enzymatic treatment with quite low enzymatic activity followed by mechanical treatment at high consistency may increase fibre cutting, i.e. fibres with reduced fibre length are produced, while the amount of fines is kept at a minimum compared to other mechanical treatments. If large amount of fines are present during an enzymatic treatment the enzymes will first decompose them and not the fibres which are the target for the enzymatic treatment. Consequently, the first enzymatic and mechanical treatments will increase the efficiency of the second enzymatic treatment and thus also the efficiency of the second mechanical treatment and the production of MFC. Furthermore, by reducing the fibre length, the runnability during high consistency mechanical treatments increases. By the possibility to increase the consistency during mechanical treatments, even less fines will be produced and the internal fibrillation, which will make the fibre surface more open for the enzymes to penetrate, is improved.
Other mechanical pre-treatments besides refining and shredding, such as beating, steam explosion, defibration, homogenization, ultrasonic treatment, dry cutting or other known mechanical fibre treatments in order to soften the fibres and make them more active and reactive before the following treatments can also be used.
After the first mechanical treatment, an enzyme is once again added to the fibres which are in the form of a slurry which has a concentration of approximately 4-5%. The enzyme is added during stirring either in the beginning of the second enzymatic treatment or during the entire reaction time. The second treatment with the enzyme increases the accessibility and the activity of the fibres and improves the following mechanical treatment to form MFC.
The fibres are thereafter mechanically treated in a second mechanical treatment in order to form microfibrillated cellulose. The time and temperature during such treatment varies depending on the fibres treated as well as on the previous treatments and are controlled in order to receive fibres with the desired fibre length. The second mechanical treatment may be done by a refiner, defibrator, beater, friction grinder, high shear fibrilator (such as cavitron rotor/stator system), disperger, homogenizator (such as micro fluidizer) or other known mechanical fibre treatment apparatus. Usually the consistency of the fibres during treatment in a micro fluidizer can not be too high. However, exposing the fibres to high pressure in narrow capillary at high consistency will also result in high mechanical impact on the fibres and the fibres can be treated at a high consistency in a micro fluidizer according to the process described in claim 1.
The consistency of the fibres during the mechanical treatment is preferably between 2-40% by total weight. It is preferred to have a high consistency during the second mechanical treatment, preferably between 15-40% by total weight. The produced MFC will thus also have high consistency, preferably above 15% by total weight or preferably between 15-40% by total weight or even more preferably between 15-25% by total weight. In this way it is possible to transport the MFC to the site of usage in a very concentrated form. If needed it is possible to add water or chemical in order for the produced MFC to swell and thus make sure that all microfibrils are separated in the water or chemical. Addition of water during the second mechanical treatment should be avoided since the MFC will swell and it might be difficult to remove the produced MFC from the refiner, shredder or other mechanical treatment apparatus.
The pH during the first and/or second mechanical treatment is preferably above 9, even more preferably above 10. The increase of pH during the mechanical treatment has been shown to increase the efficiency of the mechanical treatment and thus decrease the energy needed.
It is also possible to add chemicals which will change the fibre to fibre friction or the swelling of the fibres during the process according to claim 1. Friction decreasing chemicals can for example be carboxymethylcellulose (CMC), starch or different polymers such as poly acrylamide (PAM) or surface active agents. Friction increasing chemicals may be fillers such as talc, calcium carbonate, kaolin or titanium dioxide etc. Chemicals which increases or decreases swelling of fibres can for example be sodium hydroxide, other pH changing chemicals, different salts or charged polymers. These chemicals are preferably added after the second enzymatic treatment before the second mechanical treatment. However, it is also possible to add chemicals before or during the first mechanical treatment. Another reason for adding e.g. polymers is to stabilize the fibrils.
The cellulosic fibres used in the process according to the invention are preferably fibres of kraft pulp, i.e. they have been treated according to the kraft process. It has been shown that the primary wall of the fibres in kraft pulp often prevents the fibres from forming fibrils. Thus, it is necessary to remove the primary wall. The primary wall of the fibres can be removed by increasing the pre-treatment of the fibres. Thus, increased refining, preferably high consistency refining, has been shown to be very effective. Also, enzymes affecting hemicellulose can be used, either alone or in combination with refining, preferably high consistency refining. It has been shown that the combination of enzymatic pre-treatment, mechanical pre-treatment, enzymatic treatment and a mechanical treatment as described in claim 1 is very effective when it comes to removing the primary walls of cellulosic fibres. However, other chemical pulps, mechanical pulps or chemi-mechanical pulps can also be used, one example is sulphite pulp. The fibres can also be bleached or unbleached. Fibres with thin fibre walls are preferably used.
The cellulosic fibres may be hardwood and/or softwood fibres. It has been shown that sulphite pulps and pine kraft pulp disintegrate into smaller fractions when treated according to the invention compared to eucalyptus and birch kraft pulps. Thus, it is preferred to treat softwood fibres with the process according to the invention.
The produced MFC has very good bonding properties, i.e. it bonds well to different material such as glass, aluminium, paper or wood. Thus the MFC can be used for the production of films. Another advantage with the produced MFC is that it can be used as a priming agent between different materials such as bio-barrier and fibre based substrate.
Micro fibrillated cellulose (MFC) is often also referred to as nanocellulose. Fibres that has been fibrillated and which have microfibrills on the surface and microfibrils that are separated and located in a water phase of a slurry are included in the definition MFC.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0950535-5 | Jul 2009 | SE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB10/53044 | 7/2/2010 | WO | 00 | 2/10/2012 |