Process for producing polypropylene from C3 olefins selectively produced in a fluid catalytic cracking process

Information

  • Patent Grant
  • 6339180
  • Patent Number
    6,339,180
  • Date Filed
    Thursday, March 2, 2000
    24 years ago
  • Date Issued
    Tuesday, January 15, 2002
    22 years ago
Abstract
A process for producing polypropylene from olefins selectively produced from a catalytically cracked or thermally cracked naphtha stream is disclosed herein. The naphtha stream is contacted with a catalyst containing from about 10 to 50 wt. % of a crystalline zeolite having an average pore diameter less than about 0.7 nanometers at reaction conditions which include temperatures from about 500° C. to 650° C. and a hydrocarbon partial pressure from about 10 to 40 psia.
Description




FIELD OF THE INVENTION




The present invention relates to a process for producing polypropylene from C


3


olefins selectively produced from a catalytically cracked or thermally cracked naphtha stream.




BACKGROUND OF THE INVENTION




The need for low-emissions fuels has created an increased demand for light olefins used use in alkylation, oligomerization, MTBE, and ETBE synthesis processes. In addition, a low cost supply of light olefins, particularly propylene, continues to be in demand to serve as feed for polyolefins production, particularly polypropylene production.




Fixed bed processes for light paraffin dehydrogenation have recently attracted renewed interest for increasing olefins production. However, these types of processes typically require relatively large capital investments as well as high operating costs. It is therefore advantageous to increase olefins yield using processes, which require relatively small capital investment. It would be particularly advantageous to increase olefins yield in catalytic cracking processes.




A problem inherent in producing olefins products using FCC units is that the process depends on a specific catalyst balance to maximize production of light olefins while also achieving high conversion of the 650° F.+(˜340° C.+) feed components. In addition, even if a specific catalyst balance can be maintained to maximize overall olefins production, olefins selectivity is generally low because of undesirable side reactions, such as extensive cracking, isomerization, aromatization and hydrogen transfer reactions. Light saturated gases produced from undesirable side reactions result in increased costs to recover the desirable light olefins. Therefore, it is desirable to maximize olefins production in a process that allows a high degree of control over the selectivity to C


2


-C


4


olefins that are processed and polymerized to form products such as polypropylene and polyethylene.




SUMMARY OF THE INVENTION




An embodiment of the present invention comprises a process for producing polypropylene comprising the steps of (a) contacting a naphtha feed containing between about 10 and about 30 wt. % paraffins and between about 15 and about 70 wt. % olefins with a catalyst to form a cracked product, the catalyst comprising about 10 to about 50 wt. % of a crystalline zeolite having an average pore diameter less than about 0.7 nm, the reaction conditions including a temperature from about 500° C. to 650° C., a hydrocarbon partial pressure of 10 to 40 psia (70-280 kPa), a hydrocarbon residence time of 1 to 10 seconds, and a catalyst to feed ratio, by weight, of about 4 to 10, wherein no more than about 20 wt. % of paraffins are converted to olefins and wherein propylene comprises at least 90 mol. % of the total C


3


products; and, (b) separating the propylene from the cracked product and polymerizing the propylene to form polypropylene.




In another preferred embodiment of the present invention the catalyst is a ZSM-5 type catalyst.




In still another preferred embodiment of the present invention the feed contains about 10 to 30 wt. % paraffins, and from about 20 to 70 wt. % olefins.




In yet another preferred embodiment of the present invention the reaction zone is operated at a temperature from about 525° C. to about 600° C.




DETAILED DESCRIPTION OF THE INVENTION




Suitable hydrocarbons feeds for producing the relatively high C


2


, C


3


, and C


4


olefins yields are those streams boiling in the naphtha range and containing from about 5 wt. % to about 35 wt. %, preferably from about 10 wt. % to about 30 wt. %, and more preferably from about 10 to 25 wt. % paraffins, and from about 15 wt. %, preferably from about 20 wt. % to about 70 wt. % olefins. The feed may also contain naphthenes and aromatics. Naphtha boiling range streams are typically those having a boiling range from about 65° F. to about 430° F. (18-225° C.), preferably from about 65° F. to about 300° F. (18-150° C.).




The naphtha feed can be a thermally-cracked or catalytically-cracked naphtha derived from any appropriate source, including fluid catalytic cracking (FCC) of gas oils and resids or delayed- or fluid-coking of resids. Preferably, the naphtha streams used in the present invention derive from the fluid catalytic cracking of gas oils and resids because the product naphthas are typically rich in olefins and/or diolefins and relatively lean in paraffins.




The process of the present invention is performed in a process unit comprising a reaction zone, a stripping zone, a catalyst regeneration zone, and a fractionation zone. The naphtha feed is fed into the reaction zone where it contacts a source of hot, regenerated catalyst. The hot catalyst vaporizes and cracks the feed at a temperature from about 500° C. to 650° C., preferably from about 525° C. to 600° C. The cracking reaction deposits coke on the catalyst, thereby deactivating the catalyst. The cracked products are separated from the coked catalyst and sent to a fractionator. The coked catalyst is passed through the stripping zone where volatiles are stripped from the catalyst particles with steam. The stripping can be preformed under low severity conditions to retain a greater fraction of adsorbed hydrocarbons for heat balance. The stripped catalyst is then passed to the regeneration zone where it is regenerated by burning coke on the catalyst in the presence of an oxygen containing gas, preferably air. Decoking restores catalyst activity and simultaneously heats the catalyst to between about 650° C. and about 750° C. The hot catalyst is then recycled to the reaction zone to react with fresh naphtha feed. Flue gas formed by burning coke in the regenerator may be treated for removal of particulates and for conversion of carbon monoxide. The cracked products from the reaction zone are sent to a fractionation zone where various products are recovered, particularly a C


3


fraction and a C


4


fraction.




While attempts have been made to increase light olefins yields in the FCC process unit itself, the practice of the present invention uses its own distinct process unit, as previously described, which receives naphtha from a suitable source in the refinery. The reaction zone is operated at process conditions that will maximize C


2


to C


4


olefins, particularly propylene, selectivity with relatively high conversion of C


5


+ olefins. Catalysts suitable for use in the practice of the present invention are those which are comprising a crystalline zeolite having an average pore diameter less than about 0.7 nanometers (nm), said crystalline zeolite comprising from about 10 wt. % to about 50 wt. % of the total fluidized catalyst composition. It is preferred that the crystalline zeolite be selected from the family of medium-pore-size (<0.7 nm) crystalline aluminosilicates, otherwise referred to as zeolites. Of particular interest are the medium-pore zeolites with a silica to alumina molar ratio of less than about 75:1, preferably less than about 50:1, and more preferably less than about 40:1, although some embodiments incorporate silica-to-alumina ratios greater than 40:1. The pore diameter, also referred to as effective pore diameter, is measured using standard adsorption techniques and hydrocarbonaceous compounds of known minimum kinetic diameters. See Breck,


Zeolite Molecular Sieves


, 1974 and Anderson et al., J. Catalysis 58, 114 (1979), both of which are incorporated herein by reference.




Medium-pore-size zeolites that can be used in the practice of the present invention are described in “Atlas of Zeolite Structure Types,” eds. W. H. Meier and D. H. Olson, Butterworth-Heineman, Third Edition, 1992, which is hereby incorporated by reference. The medium-pore-size zeolites generally have a pore size from about 0.5 nm, to about 0.7 nm and include for example, MFI, MFS, MEL, MTW, EUO, MTT, HEU, FER, and TON structure type zeolites (IUPAC Commission of Zeolite Nomenclature). Non-limiting examples of such medium-pore-size zeolites, include ZSM-5, ZSM-12, ZSM-22, ZSM-23, ZSM-34, ZSM-35, ZSM-38, ZSM-48, ZSM-50, silicalite, and silicalite 2. The most preferred is ZSM-5, which is described in U.S. Pat. Nos. 3,702,886 and 3,770,614. ZSM-11 is described in U.S. Pat. No. 3,709,979; ZSM-12 in U.S. Pat. No. 3,832,449; ZSM-21 and ZSM-38 in U.S. Pat. No. 3,948,758; ZSM-23 in U.S. Pat. No. 4,076,842; and ZSM-35 in U.S. Pat. No. 4,016,245. All of the above patents are incorporated herein by reference. Other suitable medium-pore-size zeolites include the silicoaluminophosphates (SAPO), such as SAPO-4 and SAPO-11 which is described in U.S. Pat. No. 4,440,871; chromosilicates; gallium silicates; iron silicates; aluminum phosphates (ALPO), such as ALPO-11 described in U.S. Pat. No. 4,310,440; titanium aluminosilicates (TASO), such as TASO-45 described in EP-A No. 229,295; boron silicates, described in U.S. Pat. No. 4,254,297; titanium aluminophosphates (TAPO), such as TAPO-11 described in U.S. Pat. No. 4,500,651; and iron aluminosilicates.




The medium-pore-size zeolites can include “crystalline admixtures” which are thought to be the result of faults occurring within the crystal or crystalline area during the synthesis of the zeolites. Examples of crystalline admixtures of ZSM-5 and ZSM-11 are disclosed in U.S. Pat. No. 4,229,424, which is incorporated herein by reference. The crystalline admixtures are themselves medium-pore-size zeolites and are not to be confused with physical admixtures of zeolites in which distinct crystals of crystallites of different zeolites are physically present in the same catalyst composite or hydrothermal reaction mixtures.




The catalysts of the present invention are held together with an inorganic oxide matrix material component. The inorganic oxide matrix component binds the catalyst components together so that the catalyst product is hard enough to survive interparticle and reactor wall collisions. The inorganic oxide matrix can be made from an inorganic oxide sol or gel which is dried to “bind” the catalyst components together. Preferably, the inorganic oxide matrix is not catalytically active and will be comprising oxides of silicon and aluminum. Preferably, separate alumina phases are incorporated into the inorganic oxide matrix. Species of aluminum oxyhydroxides-γ-alumina, boehmite, diaspore, and transitional aluminas such as α-alumina, β-alumina, γ-alumina, δ-alumina, ε-alumina, κ-alumina, and ρ-alumina can be employed. Preferably, the alumina species is an aluminum trihydroxide such as gibbsite, bayerite, nordstrandite, or doyelite. The matrix material may also contain phosphorous or aluminum phosphate.




Process conditions include temperatures from about 500° C. to about 650° C., preferably from about 525° C. to 600° C., hydrocarbon partial pressures from about 10 to 40 psia (70-280 kPa), preferably from about 20 to 35 psia (140-245 kPa); and a catalyst to naphtha (wt/wt) ratio from about 3 to 12, preferably from about 4 to 10, where catalyst weight is total weight of the catalyst composite. Preferably, steam is concurrently introduced with the naphtha stream into the reaction zone and comprises up to about 50 wt. % of the hydrocarbon feed. Also, it is preferred that the feed residence time in the reaction zone be less than about 10 seconds, for example from about 1 to 10 seconds. These conditions will be such that at least about 60 wt. % of the C


5


+ olefins in the naphtha stream are converted to C


4


− products and less than about 25 wt. %, preferably less than about 20 wt. % of the paraffins are converted to C


4


− products, and that propylene comprises at least about 90 mol. %, preferably greater than about 95 mol. % of the total C


3


reaction products with the weight ratio of propylene/total C


2


− products greater than about 3.5.




Preferably, ethylene comprises at least about 90 mol. % of the C


2


products, with the weight ratio of propylene:ethylene being greater than about 4, and that the “full range” C


5


+ naphtha product is enhanced in both motor and research octanes relative to the naphtha feed. It is within the scope of this invention to pre-coke the catalysts before introducing the feed to further improve the selectivity to propylene. It is also within the scope of this invention to feed an effective amount of single ring aromatics to the reaction zone to also improve the selectivity of propylene versus ethylene. The aromatics may be from an external source such as a reforming process unit or they may consist of heavy naphtha recycle product from the instant process.




The following examples are presented for illustrative purposes only and are not to be taken as limiting the present invention in any way.











EXAMPLES 1-12




The following examples illustrate the criticality of process operating conditions for maintaining chemical grade propylene purity with samples of cat naphtha cracked over ZCAT-40 (a catalyst that contains ZSM-5) which had been steamed at 1500° F. (815° C.) for 16 hrs to simulate commercial equilibrium. Comparison of Examples 1 and 2 show that increasing Cat/Oil ratio improves propylene yield, but sacrifices propylene purity. Comparison of Examples 3 and 4 and 5 and 6 shows reducing oil partial pressure greatly improves propylene purity without compromising propylene yield. Comparison of Examples 7 and 8 and 9 and 10 shows increasing temperature improves both propylene yield and purity. Comparison of Examples 11 and 12 shows decreasing cat residence time improves propylene yield and purity. Example 13 shows an example where both high propylene yield and purity are obtained at a reactor temperature and cat/oil ratio that can be achieved using a conventional FCC reactor/regenerator design for the second stage.





















TABLE 1












Feed




Temp.






Oil Res.




Cat Res.




Wt. %




Wt. %




Propylene






Example




Olefins, wt %




° C.




Cat/Oil




Oil psia




Time, sec




Time, sec




C


3




=






C


3











Purity, %









1




38.6




566




4.2




36




0.5




4.3




11.4




0.5




95.8%






2




38.6




569




8.4




32




0.6




4.7




12.8




0.8




94.1%






3




22.2




510




8.8




18




1.2




8.6




8.2




1.1




88.2%






4




22.2




511




9.3




38




I.2




5.6




6.3




1.9




76.8%






5




38.6




632




16.6




20




1.7




9.8




16.7




1.0




94.4%






6




38.6




630




16.6




13




1.3




7.5




16.8




0.6




96.6%






7




22.2




571




5.3




27




0.4




0.3




6.0




0.2




96.8%






8




22.2




586




5.1




27




0.3




0.3




7.3




0.2




97.3%






9




22.2




511




9.3




38




1.2




5.6




6.3




1.9




76.8%






10




22.2




607




9.2




37




1.2




6.0




10.4




2.2




82.5%






11




22.2




576




18.0




32




1.0




9.0




9.6




4.0




70.6%






12




22.2




574




18.3




32




1.0




2.4




10.1




1.9




84.2%






13




38.6




606




8.5




22




1.0




7.4




15.0




0.7




95.5%



















Example




Wt. % C


2




=






Wt. % C


2











Ratio of C


3




=


to C


2




=






Ratio of C


3




=


to C


2











Wt. % C


3




=











1




2.35




2.73




4.9




4.2




11.4






2




3.02




3.58




4.2




3.6




12.8






3




2.32




2.53




3.5




3.2




8.2






4




2.16




2.46




2.9




2.6




6.3






5




6.97




9.95




2.4




1.7




16.7






6




6.21




8.71




2.7




1.9




16.8






7




1.03




1.64




5.8




3.7




6.0






8




1.48




2.02




4.9




3.6




7.3






9




2.16




2.46




2.9




2.6




6.3






10




5.21




6.74




2.0




1.5




10.4






11




4.99




6.67




1.9




1.4




9.6






12




4.43




6.27




2.3




1.6




10.1






13




4.45




5.76




3.3




2.6




15.0











C


2







= CH


4


+ C


2


H


4


+ C


2


H


6















The above examples (1,2,7 and 8) show that C


3




=


/C


2




=


>4 and C


3




=


/C


2







>3.5 an be achieved by selection of suitable reactor conditions.




EXAMPLES 14-17




The cracking of olefins and paraffins contained in naphtha streams (e.g., FCC naphtha, coker naphtha) over small or medium-pore zeolites such as ZSM-5 can produce significant amounts of ethylene and propylene. The selectivity to ethylene or propylene and selectivity of propylene to propane varies as a function of catalyst and process operating conditions. It has been found that propylene yield can be increased by co-feeding steam along with cat naphtha to the reactor. The catalyst may be ZSM-5 or other small or medium-pore zeolites. Table 2 below illustrates the increase in propylene yield when 5 wt. % steam is co-fed with an FCC naphtha containing 38.8 wt % olefins. Although propylene yield increased, the propylene purity is diminished. Thus, other operating conditions may need to be adjusted to maintain the targeted propylene selectivity.





















TABLE 2










Steam




Temp.






Oil Res.




Cat Res.




Wt %




Wt %




Propylene






Example




Co-feed




C




Cat/Oil




Oil psia




Time, sec




Time, sec




Propylene




Propane




Purity, %











14




No




630




8.7




18




0.8




8.0




11.7




0.3




97.5%






15




Yes




631




8.8




22




1.2




6.0




13.9




0.6




95.9%






16




No




631




8.7




18




0.8




7.8




13.6




0.4




97.1%






17




Yes




632




8.4




22




1.1




6.1




14.6




0.8




94.8%














Light olefins resulting from the preferred process may be used as feeds for processes such as oligomerization, polymerization, co-polymerization, ter-polymerization, and related processes (hereinafter “polymerization”) to form macromolecules. Such light olefins may be polymerized both alone and in combination with other species, in accordance with polymerization methods known in the art. In some cases it may be desirable to separate, concentrate, purify, upgrade, or otherwise process the light olefins prior to polymerization. Propylene and ethylene are preferred polymerization feeds. Polypropylene and polyethylene are preferred polymerization products made therefrom.



Claims
  • 1. A process for producing polypropylene comprising the steps of:(a) contacting a naphtha feed containing between about 10 and about 30 wt. % paraffins and between about 15 and about 70 wt. % olefins with a catalyst to form a cracked product, the catalyst comprising about 10 to about 50 wt. % of a crystalline zeolite having an average pore diameter less than about 0.7 nm, the reaction conditions including a temperature from about 500° C. to 650° C., a hydrocarbon partial pressure of 10 to 40 psia, a hydrocarbon residence time of 1 to 10 seconds, and a catalyst to feed ratio, by weight, of about 4 to 10, wherein no more than about 20 wt. % of paraffins are converted to olefins and wherein propylene comprises at least 90 mol. % of the total C3 products; and, (b) separating the propylene from the cracked product and polymerizing the propylene to form polypropylene.
  • 2. The process of claim 1 wherein the crystalline zeolite is selected from the ZSM series.
  • 3. The process of claim 2 wherein the crystalline zeolite is ZSM-5.
  • 4. The process of claim 3 wherein propylene comprises at least 95 mol. % of the total C3 products.
  • 5. The process of claim 3 wherein the reaction temperature is from about 500° C. to about 600° C.
  • 6. The process of claim 3 wherein at least about 60 wt. % of the C5 + olefins in the feed are converted to C4− products and less than about 25 wt. % of the paraffins are converted to C4− products.
  • 7. The process of claim 6 wherein propylene comprises at least about 90 mol. % of the total C3 products.
  • 8. The process of claim 7 wherein the weight ratio of propylene to total C2− products is greater than about 3.5.
  • 9. The process of claim 8 wherein the weight ratio of propylene to total C2− products is greater than about 4.0.
  • 10. A process for producing polypropylene comprising the steps of:(a) contacting a naphtha feed containing between about 10 and about 30 wt. % paraffins and between about 15 and about 70 wt. % olefins with a catalyst to form a cracked product, the catalyst comprising a crystalline zeolite having an average pore diameter less than about 0.7 nm, the reaction conditions including a temperature from about 500° C. to 650° C., a hydrocarbon partial pressure of 10 to 40 psia, a hydrocarbon residence time of 1 to 10 seconds, and a catalyst to feed ratio, by weight, of about 4 to 10, wherein no more than about 20 wt. % of paraffins are converted to olefins and wherein propylene comprises at least 90 mol. % of the total C3 products; and, (b) separating the propylene from the cracked product and polymerizing the propylene to form polypropylene.
  • 11. The process of claim 10 wherein the crystalline zeolite is selected from the ZSM series.
  • 12. The process of claim 11 wherein the crystalline zeolite is ZSM-5.
  • 13. The process of claim 10 wherein propylene comprises at least 95 mol. % of the total C3 products.
  • 14. The process of claim 12 wherein the reaction temperature is from about 500° C. to about 600° C.
  • 15. The process of claim 14 wherein at least about 60 wt. % of the C5+ olefins in the feed is converted to C4− products and less than about 25 wt. % of the paraffins are converted to C4− products.
  • 16. The process of claim 15 wherein the weight ratio of propylene to total C2− products is greater than about 3.5.
  • 17. The process of claim 16 wherein the weight ratio of propylene to total C2− products is greater than about 4.0.
CROSS-REFERENCE TO RELATED APPLICATION

This is a continuation-in-part of U.S. application Ser. No. 09/073,085 filed May 5, 1998 now U.S. Pat. No. 6,069,287.

US Referenced Citations (29)
Number Name Date Kind
3442792 Eng et al. May 1969 A
3893905 Fenske et al. Jul 1975 A
3928172 Davis, Jr. et al. Dec 1975 A
4171257 O'Rear et al. Oct 1979 A
4282085 O'Rear et al. Aug 1981 A
4502945 Olbrich et al. Mar 1985 A
4830728 Herbst et al. May 1989 A
4865718 Herbst et al. Sep 1989 A
4950387 Harandi et al. Aug 1990 A
5026935 Leyshon et al. Jun 1991 A
5026936 Leyshon et al. Jun 1991 A
5043522 Leysohn et al. Aug 1991 A
5069776 Biswas et al. Dec 1991 A
5160424 Le et al. Nov 1992 A
5171921 Gaffney et al. Dec 1992 A
5292976 Dessau et al. Mar 1994 A
5372704 Harandi et al. Dec 1994 A
5378352 Degnan et al. Jan 1995 A
5389232 Adewuyi et al. Feb 1995 A
5396010 Harandi et al. Mar 1995 A
5414172 Chin et al. May 1995 A
5472594 Tsang et al. Dec 1995 A
5846403 Swan et al. Dec 1998 A
5865987 Borghard et al. Feb 1999 A
5865988 Collins et al. Feb 1999 A
6069287 Ladwig et al. May 2000 A
6093867 Ladwig et al. Jul 2000 A
6106697 Swan et al. Aug 2000 A
6118035 Fung et al. Sep 2000 A
Foreign Referenced Citations (2)
Number Date Country
0347003 May 1996 EP
WO9856874 Dec 1998 WO
Continuation in Parts (1)
Number Date Country
Parent 09/073085 May 1998 US
Child 09/517503 US