The present invention relates to articles and garments with a modified polyvinyl alcohol film fabric having the utility of a material sold by DuPont de Nemours and Company under the trademark TYVEK® which is a non-woven spunbonded polyolefin. More particularly there is provided a modified polyvinyl alcohol fibrous film having the combination of a lower porosity film like layer of coalesced or fused fibers with a fibrous layer attached core layer.
The prior art has recognizes uses for polyvinyl alcohol compositions in the manufacture of water soluble useful articles. For example, U.S. Pat. No. 3,413,229 which is incorporated herein by reference, teaches the production of water soluble bags or pouches for which packets or the like are produced containing such materials as detergents, bleaches, insecticides, medicinals, chemicals, dyes, pigments, industrial additives and other materials. It is taught that the contents of the packets are dispersed merely by dropping the packets into water whereupon the bags dissolve and release their contents into aqueous dispersions. However, the referenced patent teaches the production of such films which are both hot and cold water soluble.
U.S. Pat. No. 3,859,125, which is incorporated herein by reference, teaches the production of layered articles which include coatings of polyvinyl alcohol. The subject reference teaches coating polyvinyl alcohol on a paper membrane whereby it is taught that the coated paper is soluble in either high or low temperature water. Similarly, U.S. Pat. No. 4,343,133 teaches the coating of polyvinyl alcohol onto a non-woven fiber sheet impregnated with latices of polyvinyl acetate in the manufacture of a pre-moistened towelette which can be disposed of by flushing in plain water without danger of clogging a plumbing system.
Both U.K. Patent No. 1,187,690 and Japanese Patent No. 72041741, which are incorporated herein by reference, teach the production of stand alone polyvinyl alcohol films which are water soluble. The U.K. patent teaches the production of hospital bags and packaging material for such products as detergents and agricultural chemicals while the Japanese patent teaches the use of polyvinyl alcohol films to make laundry bags which dissolve releasing soiled garments contained therein. However, neither reference teaches the unique films of the present invention which can be configured into useful garments and like materials.
U.S. Pat. No. 4,272,851 to Goldstein discloses a protective garment of non-woven, spun bonded polyolefin manufactured by DuPont de Nemours & Co. which is coated on one side by a polyethylene film. The film provides tear resistance, and the film prevents chemical penetration. One of the problems is the cost of manufacture and the problem of scorching during manufacture of the film.
None of the prior patents relate to modifying a polyvinyl alcohol breathable non-woven fabric to form a top surface of infinitely controllable porosity and susceptible to thermal transfer in combination with a polyvinyl alcohol fiber layer.
According to one embodiment, the present invention provides a modified a non-woven, fabric or laminate of polyvinyl alcohol (PVOH) to use alone or in a laminate to provide a film or fabric which can be formed into useful breathable films, non-woven fabrics and articles.
More particularly, there is provided a polyvinyl alcohol film wherein at least one surface has been modified to provide a fused substantially lower porous layer that is susceptible to thermal transfer and is attached to a flexible soft fibrous polyvinyl alcohol layer by a transition layer which can be varied as to the amount of pores during manufacture.
The variable or low porosity layer is attached to the fibrous polyvinyl alcohol layer by a transition layer. The transition layer is the combination of coalesced film or fused layer which is formed during processing and the fibrous layer which is composed of the original nonwoven fabric which remains during formation.
Advantageously, the top and bottom surfaces of the polyvinyl alcohol film have lower porosity and breathability.
The variably porous layers can be provided during manufacture with a water repellant layer or an anti-microbial coating.
“Variable” means that the amount of pores produced by controlling the conditions of the polyvinyl alcohol at the time of manufacture of the fabric.
Preferably, the amount of pores formed in the surface layer is from the surface treatment of the nonwoven fabric by steam impinging the surface or occurring by water held by the film or fabric combined with momentary pressure and direct heat application.
The surface layer or layers varies in porosity depending upon the amount of water held by the initial fiber or fabric or the humidity at the time of manufacture so as to be at least slightly porous and breathable.
In accordance with another embodiment of the invention, the modified polyvinyl alcohol is manufactured into films, garments, wraps, fabrics, including pillow covers, linens, etc. where TYVEK® has been found to be useful.
It is therefore a general object of the invention to provide a polyvinyl alcohol film with at least one surface with a breathable selected porous surface bonded to a fibrous polyvinyl alcohol layer.
It is another object of the invention to provide a laminate with a polyvinyl alcohol film having a coalesced surface layer that its porosity can be regulated by preconditioning the amount of water held by the polyvinyl alcohol prior to formation of the laminate.
It is a further object of the invention to provide wraps, garments and other useful articles with a film having similar characteristics of TYVEK®.
It is a still further object of the invention to provide protective garments and medical garments which are readily disposable after use.
It is yet another object of the invention to provide polyvinyl alcohol woven or non-woven films or fabrics having a modified surface.
These and other objects and advantages will become more apparent for the Description of Preferred Embodiment and the following drawings.
According to the present invention there is provided a film, fabric, garment or article comprising a breathable polyvinyl alcohol film in which at least one surface layer has been modified so as to possess a tightly controlled porosity.
As shown in
As shown in
As shown in
The non-woven films or fabrics of the invention have a surface layer which is more susceptible to thermal transfer than the interior fiber layer (13). In this way they can be bonded into a near film-like exterior while leaving the inner fibers unbonded. In so doing, one would effectively alter the monolithic fiber structure of a spunlaced PVOH fabric into a fabric with three distinct layers. The two outside layers would be highly compacted and bonded to improve fabric strength and abrasion resistance, while the inner core of the fabric would be highly compacted but would not be bonded together and resulting in a soft flexible fabric.
The film or fabric of the invention can be only polyvinyl alcohol with or without acetyl groups and cross-linked or uncross-linked.
The film or fabric can comprise a laminate formed with polyvinyl alcohol and another thermoplastic, preferably, a polyolefin, i.e. polyethylene to provide added tear strength.
Precursor polymer or sheet materials useful in practicing the present method comprise polyvinyl alcohol with or without acetyl groups, cross-liked or uncross-linked. The garments of the inventional are comprised of a polyvinyl alcohol homopolymer that has been highly oriented by post drawing or heat annealing. Ideal for use in the present invention would be a highly crystallized, at least approximately 98% saponified or hydrolyzed polyvinyl acetate. Commercially, polyvinyl alcohol which is sold under the trademark Vinex 1003™ and 1002™ by Air Products could be used herein. Useful PVOH fibers are typically 0.5 denier to 5.0 denier and are preferably from 1.0-2.0 denier and most preferably sized at 1.2-1.5 denier. A commercially available product for use in the present invention is either type T-B (VEE 1290) or type T-5 (VPB 101) which are each available from Kuralon as its PVA fiber. This material is sold in 44 mm lengths. The T-B product is sized at 1.2 denier while the T-5 product is sold in 38 mm staple lengths of 1.5 denier.
The precursor fabric useful in practicing the present invention can be constructed by any well known technique for making woven, non-woven, knitted or otherwise formed fabric. Such non-woven techniques useful in practicing the present invention include spun bonding, melt blowing or wet laying, hydro entangling with cold water and/or thermally bonding with 30-70% of the surface melted to form essentially a non porous surface. When products are configured of sheets of suitable thermoplastic material, the sheets are approximately 3 to 20 mils in thickness and more preferably 8 to 12 mils in thickness and most preferably approximately 8 mils in thickness. Suitable non-woven fabric or sheets are approximately from 15 g/yd2 to 200 g/yd2 in weight and more preferably from 20 g/yd2 to 70 g/yd2 and most preferably from 25 g/yd2 to 80 g/yd2.
As noted previously, polymer or sheet material useful in practicing the present invention is comprised of polyvinyl alcohol with or without acetyl groups, cross-linked or uncross-linked. It is proposed that the polyvinyl alcohol be substantially fully hydrolyzed, that is, having 98% or greater hydrolyzed acetyl groups.
For the sake of adequate mechanical strength, in some cases the polyvinyl alcohol-based non-woven fabric or sheet material should have a degree of polymerization of at least 700 and no greater than approximately 1500. Ideally, such materials should have a degree of polymerization of approximately 900 and be substantially crystallized.
To enhance the manufacture of suitable polyvinyl alcohol resin-based materials, suitable quantities of a plasticizer may be necessary. It is contemplated that up to 15% (wt.) of a suitable plasticizer such as glycerine or polyethylene glycol may be employed to assist in providing a smooth melt extrusion from the polyvinyl alcohol-based pellets.
It was found that the manufactured fabric for use as disposable medical garments displayed nearly identical physical properties similar to fabric manufactured from polyester and polypropylene. However, the fabric manufactured was unaffected by cool or warm water (23°-37° C.) but when exposed to hot water (80°-90° C.), immediately dissolved.
The incorporation of a water repellent to the surface of the modified polyvinyl alcohol film or fabric is quite a useful adjunct to minimize surface attack by liquid moisture at a temperature lower than that at which solubility occurs. It has been found that even with polyvinyl alcohol films and fabrics which become water soluble only at elevated temperatures, when exposed to water, the surface of such material tends to take on a slick “feel” and the use of water repellents tends to minimize this effect. Suitable repellents include fluorocarbons offered by the 3M Co. sold under its trademarks FC 824 and 808. Oleic acid and fatty acids are also useful repellants. These materials are useful in the range of between 0.1 to 2.0% (wt.) based upon the weight of the polyvinyl alcohol polymer.
Antimicrobial agents can be added to the surface particularly for medical applications such as gowns, drapes, etc. Antimicrobials include GERM PATROL® sold by Germ Patrol, LLC, silanes, silver or copper antimicrobials, and the like.
The surface modified polyvinyl alcohol can be produced as disclosed in U.S. patent application Ser. No. 13/135,917 filed Jul. 18, 2011.
The surface can also be modified by utilizing the water retention held by the precursor film or fabric. In this regard the film or fabric can be preconditioned by subjecting the film or fabric to a fixed humidity and temperature for time sufficient for equilibrium between fiber and the atmosphere to occur, 24 to 96 hours, 72 hours beginning preferred and then utilizing heated rollers and pressure rollers to create the steam to melt and compact the surface and form a layer of reduced porosity while leaving the adjoining fibers in tact. The films or fabrics of the present invention are useful in making medical clothing, gowns, drapes, etc. The films or fabrics can be formed into envelopes, building wraps for inert articles.
A variety of modifications to the embodiment described will be apparent to those skilled in the art from the disclosure provided herein. Thus, the present invention can be embodied in other specific forms without departing from the spirit or essential attributes thereof and accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicating the scope of the invention.
This application is a continuation-in-part of U.S. application Ser. No. 13/135,917, filed Jul. 18, 2011, now U.S. Pat. No. 8,293,664 issued Oct. 23, 2012, which application is herein incorporated by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3322593 | Conti | May 1967 | A |
| 3413229 | Bianco et al. | Nov 1968 | A |
| 3856598 | Gregorian et al. | Dec 1974 | A |
| 3859125 | Miller et al. | Jan 1975 | A |
| 3870542 | Ida et al. | Mar 1975 | A |
| 3874964 | Cogliano et al. | Apr 1975 | A |
| 4147844 | Babinsky et al. | Apr 1979 | A |
| 4272851 | Goldstein | Jun 1981 | A |
| 4324827 | Obayashi | Apr 1982 | A |
| 4343133 | Daniels et al. | Aug 1982 | A |
| 4409761 | Bechtel | Oct 1983 | A |
| 4415617 | D'Elia | Nov 1983 | A |
| 4639390 | Shoji | Jan 1987 | A |
| 4713068 | Wang et al. | Dec 1987 | A |
| 4726986 | Cannady et al. | Feb 1988 | A |
| 4731266 | Bonnebat et al. | Mar 1988 | A |
| 4772510 | McClure | Sep 1988 | A |
| 4833010 | Langley | May 1989 | A |
| 4855178 | Langley | Aug 1989 | A |
| 4865903 | Adiletta | Sep 1989 | A |
| 4879165 | Smith | Nov 1989 | A |
| 4920575 | Bartasis et al. | May 1990 | A |
| 4924525 | Bartasis | May 1990 | A |
| 4970105 | Smith | Nov 1990 | A |
| 4981738 | Farnworth et al. | Jan 1991 | A |
| 5002820 | Bolton et al. | Mar 1991 | A |
| 5035941 | Blackburn | Jul 1991 | A |
| 5037700 | Davis | Aug 1991 | A |
| 5061748 | Bolton et al. | Oct 1991 | A |
| 5082721 | Smith, Jr. et al. | Jan 1992 | A |
| 5098770 | Paire | Mar 1992 | A |
| 5124208 | Bolton et al. | Jun 1992 | A |
| 5151314 | Brown | Sep 1992 | A |
| 5162148 | Boye et al. | Nov 1992 | A |
| 5166007 | Smith et al. | Nov 1992 | A |
| 5236769 | Paire | Aug 1993 | A |
| 5250350 | Tung | Oct 1993 | A |
| 5266167 | Hess | Nov 1993 | A |
| 5491022 | Smith | Feb 1996 | A |
| 5492108 | Smith et al. | Feb 1996 | A |
| 5494720 | Smith et al. | Feb 1996 | A |
| 5496640 | Bolton et al. | Mar 1996 | A |
| 5554667 | Smith et al. | Sep 1996 | A |
| 5667885 | Nguyen et al. | Sep 1997 | A |
| 5688577 | Smith et al. | Nov 1997 | A |
| 5692935 | Smith | Dec 1997 | A |
| 5763062 | Smith et al. | Jun 1998 | A |
| 5869193 | Langley | Feb 1999 | A |
| 6045900 | Haffner et al. | Apr 2000 | A |
| 6302993 | Smith et al. | Oct 2001 | B1 |
| 6364980 | Smith et al. | Apr 2002 | B1 |
| 6638605 | Ankuda et al. | Oct 2003 | B1 |
| 6671031 | Nishimura | Dec 2003 | B1 |
| 6803034 | Duval et al. | Oct 2004 | B2 |
| 6808791 | Curro et al. | Oct 2004 | B2 |
| 7093307 | Smith | Aug 2006 | B1 |
| 7358295 | Miller et al. | Apr 2008 | B2 |
| 7718555 | Smith et al. | May 2010 | B1 |
| 7937772 | Smith et al. | May 2011 | B1 |
| 8293664 | Smith et al. | Oct 2012 | B1 |
| 20010008695 | Bolton et al. | Jul 2001 | A1 |
| 20020028876 | Jenkines et al. | Mar 2002 | A1 |
| 20020091074 | Wooley et al. | Jul 2002 | A1 |
| 20020115581 | DuVal et al. | Aug 2002 | A1 |
| 20020155302 | Smith et al. | Oct 2002 | A1 |
| 20020164465 | Curro et al. | Nov 2002 | A1 |
| 20030003308 | Kashiba et al. | Jan 2003 | A1 |
| 20030044579 | Bolton | Mar 2003 | A1 |
| 20030082445 | Smith et al. | May 2003 | A1 |
| 20030082972 | Monfalcone et al. | May 2003 | A1 |
| 20040096666 | Knox et al. | May 2004 | A1 |
| 20040121678 | Baldwin et al. | Jun 2004 | A1 |
| 20060046022 | Bader et al. | Mar 2006 | A1 |
| 20070172614 | Lee | Jul 2007 | A1 |
| 20080038975 | Weiss | Feb 2008 | A1 |
| 20090061131 | Monfalcone et al. | Mar 2009 | A1 |
| 20090294294 | Feng et al. | Dec 2009 | A1 |
| 20090325447 | Austin | Dec 2009 | A1 |
| 20100055472 | Bravet et al. | Mar 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 1352710 | Jun 2002 | CN |
| 1187690 | Apr 1970 | GB |
| 9416585 | Aug 1994 | WO |
| 9425189 | Nov 1994 | WO |
| 0058539 | Oct 2000 | WO |
| 03071012 | Aug 2003 | WO |
| 2004052522 | Jun 2004 | WO |
| 2013012854 | Jan 2013 | WO |
| Entry |
|---|
| USPTO; Non-Final Office Action dated Jan. 18, 2012 in U.S. Appl. No. 13/135,917. |
| USPTO; Final Office Action dated Apr. 6, 2012 in U.S. Appl. No. 13/135,917. |
| USPTO; Notice of Allowance dated Jun. 14, 2012 in U.S. Appl. No. 13/135,917. |
| PCT; International Search Report and Written Opinion dated Dec. 7, 2012 in Application No. PCT/US12/047047. |
| EPO; European Search Search Report dated Jul. 20, 2015 in Application No. 12814529.9. |
| USPTO; Non Final Office Action dated Dec. 18, 2015 in U.S. Appl. No. 13/533,392. |
| USPTO; Non Final Office Action dated Jun. 21, 2016 in U.S. Appl. No. 13/533,392. |
| Number | Date | Country | |
|---|---|---|---|
| 20150159322 A1 | Jun 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13135917 | Jul 2011 | US |
| Child | 13317965 | US |