- 1. A process for the production of dense soda ash comprising preheating light soda ash, soda ash fines or a combination thereof to a temperature between about 35.degree. C. and about 200.degree. C., mechanically blending the preheated light soda ash or soda ash fines or combination thereof with sodium carbonate decahydrate, wherein the molar ratio of light soda ash or soda ash fines or combination thereof to sodium carbonate decahydrate is less than about 9:1, reacting at a temperature between about 60.degree. C. and about 150.degree. C. said components to form substantially coarse agglomerates of sodium carbonate monohydrate, and then calcining at a temperature between about 125.degree. C. and 250.degree. C. said sodium carbonate monohydrate to form dense soda ash having an average bulk density of at least about 55 lb/ft.sup.3.
- 2. The process according to claim 1, wherein the molar ratio of light soda ash or soda ash fines or combination thereof to sodium carbonate decahydrate is between about 4.5:1 and about 7.5:1.
- 3. The process according to claim 1, wherein the light soda ash or soda ash fines or combination thereof is preheated to a temperature between about 600.degree. C. and about 150.degree. C.
- 4. The process according to claim 1, further comprising the step of heating the mixture to achieve the reaction temperature.
- 5. The process according to claim 1, further comprising blending the sodium carbonate decahydrate with a first portion of light soda ash or soda ash fines or a combination thereof at a temperature below about 32.degree. C. before blending the sodium carbonate decahydrate with the pre-heated light soda ash or soda ash fines or a combination thereof.
- 6. The process according to claim 1, wherein said sodium carbonate decahydrate is partially dehydrated.
- 7. The process according to claim 1, wherein the sodium carbonate monohydrate has a particle size distribution larger than 100 mesh above about 40 weight percent.
- 8. The process according to claim 1, wherein the reaction is carried out at a temperature less than about 110.degree. C.
- 9. A process for the production of dense soda ash, the process comprising mechanically blending anhydrous sodium carbonate fines pre-heated above 35.degree. C. and sodium carbonate decahydrate crystals, wherein the molar ratio of fines to decahydrate crystals is less than about 9:1, reacting at a temperature between about 60.degree. C. and about 150.degree. C. said fines and crystals to form substantially coarse, fused agglomerates containing sodium carbonate monohydrate and then calcining the fused agglomerates at a temperature between about 125.degree. C. and about 250.degree. C. to produce dense soda ash having an average bulk density of at least about 55 lb/ft.sup.3.
Parent Case Info
This application is a continuation of application Ser. No. 08/438,891, filed May 10, 1995 abandoned.
US Referenced Citations (11)
Foreign Referenced Citations (2)
Number |
Date |
Country |
0 191 512 A1 |
Aug 1986 |
EPX |
0 542 351 A1 |
May 1993 |
EPX |
Non-Patent Literature Citations (1)
Entry |
European Search Report Oct. 27, 1997 for counterpart foreign application No. EP 96 20 1222. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
438891 |
May 1995 |
|