Claims
- 1. A process for producing polymer particles from an organic solvent solution consisting essentially of an organic solvent, a poor solvent, and polymer particles being dissolved in said organic solvent solution, the process comprising:
- (a) initially introducing said polymer particles into a particle producing zone, and stirring said polymer particles under conditions in which said organic solvent would be vaporizable,
- (b) introducing said organic solvent solution having a polymer concentration of 3 to 70% by weight, onto said polymer particles which are maintained in said particle producing zone, said particle producing zone not substantially containing steam, said solution being added in an amount of not more than 250% by weight per hour based on the amount of the polymer particles which are initially held in said particle producing zone, said poor solvent being selected from the group consisting of benzene, toluene, xylene, pentane, hexane, heptane, octane, acetone and methyl ethyl ketone, said poor solvent being in an amount of 5 to 50% by weight based on the weight of said polymer in said organic solvent solution, wherein said polymer is not precipitated by said amount of said poor solvent, and
- (c) evaporating said organic solvent, while maintaining said organic solvent solution of said polymer in contact with said polymer particles which are maintained in said particle producing zone, to produce said polymer particles.
- 2. The process as claimed claim 1 wherein the particle producing zone is a complete mixing particle producing vessel.
- 3. A process for producing polymer particles from an organic solvent solution consisting essentially of an organic solvent, a poor solvent, and polymer particles being dissolved in said organic solvent solution, the process comprising:
- (a) initially introducing said polymer particles into a horizontal vessel having a horizontal particle producing zone, and stirring said polymer particles under conditions in which said organic solvent would be vaporizable,
- (b) introducing said organic solvent solution into said horizontal particle producing zone, said organic solvent solution being divided into a plurality of streams for introducing said organic solvent solution through a plurality of points in said horizontal particle producing zoned and onto said polymer particles which are maintained in said horizontal particle producing zone, said organic solvent solution having a polymer concentration of 3 to 70% by weight, said particle producing zone not substantially containing steam, said solution being added in an amount of not more than 250% by weight per hour based on the amount of the polymer particles which are initially held in said horizontal particle producing zone, said poor solvent being selected from the group consisting of benzene, toluene, xylene, pentane, hexane, heptane, octane, acetone and methyl ethyl ketone, said poor solvent being in an amount of 5 to 50% by weight based on the weight of said polymer in said organic solvent solution, wherein said polymer is not precipitated by said amount of said poor solvent and
- (c) evaporating said organic solvent, while maintaining said organic solvent solution of said polymer in contact with said polymer particles which are maintained in said horizontal particle producing zone, to produce said polymer particles.
- 4. The process as claimed in claim 1 wherein the organic solvent is methylene chloride.
- 5. The process as claimed in claim 1 wherein the polymer is selected from the group consisting of polycarbonate and polyarylate.
- 6. The process according to claim 1 wherein the polymer is polyester polycarbonate.
- 7. The process as claimed in claim 5 wherein the organic solvent is methylene chloride.
- 8. The process as claimed in claim 6 wherein the organic solvent is methylene chloride.
- 9. The process as claimed in claim 1 wherein the polymer is selected from the group consisting of polycarbonate, polyarylate and polyamide; the organic solvent is selected from the group consisting of methylene chloride., chloroform, chlorobenzene, dioxane and tetrahydrofuran; and the process is carried out at a temperature of 0 to 200.degree. C., an absolute pressure of 0.1 to 11 kg/cm.sup.2 and with a residence time of polymer in the particle producing zone of 0.01 to 10 hours.
- 10. The process as claimed in claim 9 wherein the polymer is dissolved in the organic solvent in a concentration of 10 to 60% by weight; the temperature is 30 to 150.degree. C. and the pressure is 0.5 to 5 kg/cm.sup.2.
- 11. The process as claimed in claim 10 wherein the polymer is polycarbonate having a particle diameter of 50 .mu.m to 3 mm.
- 12. The process as claimed in claim 1 wherein the organic solvent solution is added in an amount of not more than 100% by weight per hour based on the amount of the polymer particles held in the polymer producing zone.
- 13. The process as claimed in claim 3 wherein the organic solvent solution is added in an amount of not more than 100% by weight per hour based on the amount of the polymer particles held in the polymer producing zone.
- 14. The process as claimed in claim 1 wherein the process is continuous and the polymer particles are stirred homogeneously.
- 15. The process as claimed in claim 3 wherein the process is continuous and the polymer particles are stirred homogeneously.
- 16. The process as claimed in claim 1 wherein part of the polymer particles produced in the particle producing zone is continuously recycled to said particle producing zone.
Priority Claims (2)
Number |
Date |
Country |
Kind |
045554 |
Feb 1991 |
JPX |
|
277621 |
Oct 1991 |
JPX |
|
Parent Case Info
This application is a Continuation of application Ser. No. 08/166,805 filed Dec. 13, 1993, which is a continuation of application Ser. No. 07/927,658 filed Aug. 26, 1992 (abandoned), which is the United States national phase application of International application No. PCT/JP92/00052 filed Jan. 23, 1992.
US Referenced Citations (9)
Foreign Referenced Citations (8)
Number |
Date |
Country |
465967 |
|
EPX |
2286847 |
Apr 1976 |
FRX |
1171155 |
|
DEX |
1291119 |
|
DEX |
49-28642 |
Mar 1974 |
JPX |
57-141427 |
Sep 1982 |
JPX |
2-233733 |
Sep 1990 |
JPX |
1090975 |
Nov 1967 |
GBX |
Non-Patent Literature Citations (1)
Entry |
Toyota, Keizo; Tanaka, Junji, "Polycarbonate Powder", (1974), Chemical Abstracts, 80, No. 4, Abstract No. 15904y, pp. 54, col. 2; of JP-A- 47 041 421. |
Continuations (2)
|
Number |
Date |
Country |
Parent |
166805 |
Dec 1993 |
|
Parent |
927658 |
Aug 1992 |
|