Claims
- 1. A method for producing saline soluble xanthan gum comprising the steps of:
- (a) producing precipitated xanthan gum by mixing, with stirring, an aqueous solution of xanthan gum with a hydrophilic organic solvent in which the xanthan gum is insoluble;
- (b) removing liquid from the precipitated xanthan gum to form a cake having a liquid content of no more than 50 % by weight;
- (c) disintegrating the xanthan gum cake into particles having an average particle size of from 0.3 to 2 cm in diameter; and
- (d) drying the xanthan gum at a temperature not exceeding 80.degree. C.
- 2. The method of claim 1 wherein the liquid is removed by squeezing the precipitated xanthan gum.
- 3. The method of claim 1 wherein the organic solvent is selected from the group consisting of methanol, ethanol, isopropanol, dioxane, acetone, tetrahydrofuran, and combinations thereof.
- 4. The method of claim 1 wherein the average particle size diameter is from 0.6 to 1.5 cm.
- 5. The method of claim 1 wherein the liquid content of the cake is from 40 to 50% by weight.
- 6. The method of claim 1 wherein the xanthan gum particles are dried at a temperature from 40 to 65.degree. C. and a pressure of from 40 to 100 Torr.
- 7. The method of claim 1 wherein the xanthan gum produced exhibits a viscosity of not less than 650 mPa as determined on a 0.5 % by weight solution thereof in a 12 % by weight aqueous sodium chloride solution at 20.degree. C. at 30 rpm using a Brookfield BL viscometer and exhibits a ratio of this viscosity to that determined on a 0.5% by weight solution thereof in distilled water of not less than 1.3.
- 8. The method of claim 1 wherein the liquid removal is carried out in a V-type disk press.
- 9. The method of claim 1 wherein the liquid removal is carried out in a V-type disk press having opposing disk shape screens for pressing the precipitated xanthan gum therebetween.
- 10. The method of claim 9 wherein the screens have openings of not greater than 1 mm.sup.2.
- 11. The method of claim 9 wherein the screens have a diameter of from 0.5 to 1.5 meters and are rotated at a speed of from 1 to 12 rpm.
- 12. The method of claim 1 wherein the mixing is carried out with a rotating stirrer and by repeated cycles of rotation of the stirrer, first in one direction and then in the reverse direction.
- 13. The method of claim 12 wherein the cycle of rotation comprises rotating the stirrer between about 90 to 360 degrees in one direction and then rotating the stirrer in an equal amount in the reverse direction.
- 14. The method of claim 1 wherein the dried xanthan gum is ground to a mesh size of 80 mesh or finer.
- 15. The method of claim 1 wherein the liquid is removed by squeezing the precipitated xanthan gum in a V-type disk press.
- 16. The method of claim 1 wherein the disintegrated xanthan gum is dried in a fluidized air dryer.
- 17. The method of claim 1 wherein the mixing is carried out in a cylindrical tank having an agitator shaft therein provided with upper and lower opposing pairs of agitating blades extending from the agitator shaft and wherein the diameter of the tank to the diameter of a circle defined by the extended blades is at least 0.5.
- 18. The method of claim 1 wherein the xanthan gum cake is disintegrated using a disintegrator comprising a treating tank formed from a cylindrical wall, a portion of said wall being a screen, a rotary cutter disposed essentially in said cylindrical tank for chopping up xanthan gum which has been introduced to the cylindrical tank, the disintegrated xanthan gum being discharged from the cylinder through the screened wall portion.
- 19. The method of claim 1 wherein the precipitated xanthan gum is dried in a dryer comprising a rotatable drying gum rotatable on a driven rotating shaft, the drum having an inlet and an outlet, and having an outer jacket for receiving hot liquid to heat the interior of the drum.
Priority Claims (1)
Number |
Date |
Country |
Kind |
7-174713 |
Jul 1995 |
JPX |
|
CROSS-REFERENCE TO RELATED APPLICATIONS
The priority of prior copending provisional application Ser. No. 60/000,870, filed Jul. 11, 1995, is claimed.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
5416206 |
Nagura et al. |
May 1995 |
|
Non-Patent Literature Citations (1)
Entry |
Database XP 002023564--Derwent Publications AN-94-040055 & JP-A-05 345 801. |